The present invention relates to a method of synthesizing composite materials, and particularly, to the in-situ synthesis of metal-matrix nanocomposites utilizing electromagnetic forces, Lorentz forces to control the size and distribution level of ceramic reinforcements in the nanocomposites.
Metal matrix composite materials (MMC) generally exhibit outstanding performance at elevated temperatures and have a high strength-to-weight ratio, which make these materials desirable for advanced applications in aerospace, automotive and marine industries. The size, morphology and the spatial distribution level of the reinforcement determine the final mechanical properties of the MMC. Recently, it has been found that metal matrix nanocomposites (MMNC) exhibit superior mechanical properties when compared to MMC. MMNC is a composite material including a metal matrix and ceramic reinforcements that are a few nanometers in size dispersed throughout the metal matrix. However, due to the nanometric size of ceramic reinforcements, the fabrication of MMNC is quite difficult because of the following challenges: (1) poor wettability between liquid metal and ceramic, (2) high clustering tendency of nano size particles, and (3) high oxidation affinity of liquid metal.
The fabrication of MMNC can be carried out by using in-situ synthesis or ex-situ synthesis techniques. In the in-situ synthesis technique, the reinforcement particles are obtained from a chemical reaction between two or more constituents of the material. However, in the ex-situ synthesis technique, the pre-manufactured reinforcements are added externally. A number of methods are presently recognized in the art of fabrication metal matrix nanocomposite materials. Many of these methods, however, fail to provide distribution homogeneity of the nano-sized reinforcements throughout the manufactured material.
Thus, a method of synthesizing metal matrix nanocomposites solving the aforementioned problems is desired.
A method for synthesizing a metal matrix nanocomposite (MMNC) is an in-situ synthesis technique for preparing a metal matrix with ceramic reinforcements dispersed homogenously therein. The method includes mixing a base metal matrix material with two or more ceramic-forming elements to form a mixture; blending the mixture; drying the mixture; ball milling the mixture with a plurality of milling balls to form a milled mixture; using induction heating to form a melt flow and induce electromagnetic forces; and initiating a plurality of stirring vortexes in the melt flow to form the metal matrix nanocomposite. The metal nanocomposite is in a homogenous phase.
These and other features of the present invention will become readily apparent upon further review of the following specification and drawings.
Similar reference characters denote corresponding features consistently throughout the attached drawings.
A method for synthesizing a metal matrix nanocomposite (MMNC) is an in-situ synthesis technique for preparing a metal matrix with ceramic reinforcements dispersed homogenously therein. The method includes mixing a base metal matrix material with two or more ceramic-forming elements to form a mixture; blending the mixture; drying the mixture; milling the mixture with a plurality of milling balls in a ball mill to form a milled mixture; using induction heating to form a melt flow and induce electromagnetic forces; and initiating a plurality of stirring vortexes in the melt flow to form the metal matrix nanocomposite. The metal nanocomposite is in a homogenous phase.
The mixture can be formed in a degassed organic solvent and blended under ultrasonic conditions at a temperature of, e.g., about 35° C. The organic solvent can be acetone. The mixing process can be carried out by dry mixing and/or wet mixing. In the dry mixing, the targeted materials are mixed using ultrasonic vibrator, mechanical stirrer, and/or barrel mixing with multi-axes movement. For wet mixing, the raw materials are mixed in a liquid bath of volatile solutions have no reaction affinity with the raw materials under ultrasonic stirring effects.
The mixture can be added to a ball-milling container, e.g., stainless steel or tungsten carbide jars, with stainless steel or tungsten carbide balls in a pre-determined ratio and rotated at high speed. The jar rotation can provide a mixture in the form of a granular composite. The ball milling can be performed at a rotation speed of at least 1000 rotations per minute for at least one hour in at least two different axes directions. The plurality of milling balls can include steel balls or tungsten carbide balls or mixtures thereof. The plurality of milling balls may include a first plurality of balls having a first size, a second plurality of balls having a second size, and a third plurality of balls having a third size. The first, second, and third sizes can be different from each other. The first size can be about 10 mm in diameter. The second size can be about 6 mm in diameter. The third size can be about 3 mm in diameter. The ball to mixture weight ratio in the ball mill container can be about 10:1. The milling balls and mixture can be held in a suitable milling container, e.g., a stainless steel jar with a capacity of about 80 ml.
The ceramic-forming elements can include at least two different elements having a high affinity to form a ceramic reinforcement compound. For example, the ceramic-forming elements can include at least two of the following elements: Ti, C, B, Zr, W, and Si. The ceramic-forming elements can react within the base metal matrix, e.g., liquid Al, to form the ceramic reinforcement. The base metal matrix can include Al, Mg, Zn, or Ti. The ceramic reinforcement can include at least one of TiC, TiB2, ZrC, ZrB2, WC, SiC, and B4C. An exemplary weight percentage of Ti and C to form TiC particles can be about 1 wt % Ti and about 0.5 wt % C. This ratio is variable based on the base alloy, temperature, and required particle size. The ceramic reinforcements have nano-metric sizes and are synthesized in situ during the melting of the mixture using electromagnetic forces. The electromagnetic forces can include Lorentz forces. The electromagnetic forces can control the size and distribution level of the reinforcements.
In the melt processing stage, the milled mixture can be placed in a cylindrical crucible between two punchers made from electrical/thermal conductive material, such as graphite. The charge can be heated up to a targeted temperature range that is predetermined using thermodynamic calculations, and under the effect of the electromagnetic forces that are generated by the induction melting. The induced electromagnetic forces, Lorentz forces, drive the melt flow by initiating a number of micro stirring vortexes that affect the nucleation and growth kinetics of ceramic embryos within the melt. After a certain holding time at the aimed temperature, the charge is left to cool down under the continued effect of electromagnetic forces.
In-situ melting of the metal matrix nanocomposite can occur by induction heating using a commercially available high frequency induction melting unit to homogenize the metal matrix nanocomposite. The induction heating can generate an electromagnetic stirring force and/or Lorentz force. The melting can occur at temperatures ranging from about 1300° C. to about 1500° C. for a time period of about 3 minutes to about 6 minutes. The step of drying the mixture may occur at a temperature of about 50° C. under vacuum for about 12 hours to evaporate the organic solvent.
Preferably, in the melt processing step, a high-frequency induction heating unit (HFIH) is utilized. The main configuration of the HFIH unit is shown in
Nanocomposite refers to a multiphase solid material where one of the phases has one, two or three dimensions of less than 100 nanometers (nm), or structures having nano-scale repeat distances between the different phases that make up the material. As used herein the term “nanoparticle” refers to a particle having at least one dimension sized between 1 and 100 nanometers. As used herein the term, Lorentz force is the electromagnetic stirring force that forms due to the interaction between the induced current and magnetic wave during the induction melting, and is the driving force for the liquid metal stirring in producing the in-situ synthesized nano-metal matrix composite. The term base metal is intended to mean the individual metal matrix of the composite such as Al, Mg, or Zn in which the ceramic compound can form. For example, Zr and C can be added to Al matrix (liquid Al) to form ZrC inside the Al matrix (the base metal), or Zr and C can be added to Mg matrix (liquid Mg) to form ZrC inside the Mg matrix (the base metal).
Pure aluminum and aluminum alloy powder can be prepared by atomization, melt spinning, plasma method, or splat quenching. Preferably, atomization is preferred. In atomization, aluminum droplets are broken down and rapidly solidified into fine particles with an average size range of a few nanometers to a few millimeters. In the present method, pure aluminum and aluminum alloys are used in the form of fine powder or in granular form. These powders or granular particles are then mixed by the targeted elements that can form ceramic compounds at elevated melting temperatures.
The in-situ synthesis of metal matrix nanocomposite materials by melt processing has previously been difficult due to (i) uncontrollable size of the produced reinforcements, (ii) severe agglomeration of the reinforcement particles because of capillary and Van Der Waals attractive forces, (iii) high oxidation affinity of the metals, and (iv) in some cases poor wettability between the reinforced ceramics and the melt. In the inventive method, however, metal matrix nanocomposite materials have been in-situ synthesized under the effects of electromagnetic forces to overcome the abovementioned drawbacks.
Electromagnetic forces are utilized to reach a heightened homogeneity of the melt at which maximized embryos density of ceramic reinforcements is achieved under restricted growth condition. Due to an interaction between the induced current and electromagnetic waves in the melt, powerful forces called the electromagnetic forces, Lorentz forces, are formed. These forces result in intense and localized stirring forces that determine the melt flow pattern. The Lorentz force is able to minimize the Ostwald ripening phenomenon by equalizing the solutes concentration at the surfaces of the formed ceramic particles in the melt, resulting in a significant reduction in their growth and coarsening tendency. The localized stirring effect of Lorentz force results in intensive shearing forces that can break down the particles agglomeration and decrease the clustering tendency. As a result of the intensive and localized stirring effect of the Lorentz forces, any oxide layer formed on the particle surfaces wash out, providing an intimate and clean ceramic/liquid metal interface. This results in the optimized incorporation of ceramic reinforcements within the melt. The intensity of the Lorentz force is controlled by frequency adjustments.
The following examples will further illustrate the synthetic processes of making metal matrix nanocomposite.
Pre-designated masses of Al-6% Ti alloy and graphite powders providing the stoichiometric ratio of titanium carbide ceramic compound were mixed in acetone solution and stirred by using an ultrasonic bath. In the beginning of the stirring process, the mixture was degassed for about 2 hours to remove any entrapped gases and moisture among the particles. In the next 2 hours, the mixture was vigorously stirred in the acetone solution which was preheated to 35° C. This stirring technique optimized the distribution homogeneity of the constituent materials with lesser oxidation possibility. After stirring, the mixture was placed in an oven at 50° C. under vacuum for 12 hours to evaporate acetone. The mixture was kept under vacuum until the second step was performed.
In the second step, the dried mixture of Al-6% Ti/graphite obtained from the ultrasonic bath mixing in Example 1 was combined with stainless steel balls that were 10 mm, 6 mm, and 3 mm in size. The balls were added to the mixture in a weight ratio of 10/1 (balls/mixture). The ball milling technique was used to prevent clustering tendency between powders due to the Van Der Waals attractive forces, and the formation of oxide layers on the metals. The presence of an oxide layer at metal surface can have negative effects on the in-situ synthesis reactions of the ceramic compounds during the melt processing. In addition, the chemical reactivity can be halted due to the presence of the oxides that prevent an intimate contact among the reactant elements. Further, during the melt stirring process, the oxide films may trap the formed ceramic particles within the melt causing full rejection and poor incorporation of those intermetallic compounds.
The charge was added to a stainless steel jar with 80 ml capacity and rotated at 1000 rpm for about 1 hour in two different axes directions, creating an intensive vibration in a conventional high energy ball mill, e.g., planetary ball mill. After the milling process, the jar was left to cool down to ambient temperatures, and then the milled mixture is removed and kept under vacuum to avoid oxidations until the next step.
The ball milled mixture of Al-6% Ti/graphite was added to the graphite die that is placed in the core of the induction coil at the heating focal point and under applied pressure of 3 MPa. High vacuum was applied on the melting chamber to avoid oxidation and to remove the trapped gases and moistures. Due to the generation of the induced current passing through the assembly, the temperature continued to increase until it reaches the targeted melting temperature. The targeted temperature was decided based on the calculation of the standard Gibbs free energies of TiC formation. In liquid state, the titanium and carbon were considered as diluted solutes in liquid aluminum solution and thus the targeted temperature was defined as the temperature at which the formation reaction of TiC is maximized at the expense of the other reactions. Accordingly, the targeted temperature of TiC in-situ synthesized is determined by calculating the standard Gibbs free energies (ΔG) of the following possible reactions:
Ti(1.0 wt %)+C(s)=TiC(s) (1)
4/3Al(l)+C(s)=1/3Al4C3(s) (3)
ΔG(Jmol−1)=−89.611+32.841T (4)
Ti(l)+3Al(l)=Al3Ti(s) (5)
ΔG(Jmol−1)=−52503+21.483T (6)
The melt processing technique as described can be used for in-situ synthesis of the nano metal matrix composite (NMMC), which includes various ceramic compounds such as TiC, WC, TiB2, ZrC, SiC, B4C, etc. The in-situ synthesized nano-metal matrix composite (NMMC) was characterized by superior thermal stability, mechanical properties and corrosion resistance. The NMMC materials fabricated by the present technique can be used in advanced aerospace, automotive, and marine applications that require materials with high thermal stability. These applications include pistons, cylinder heads, turbines, engines, aircraft parts, and submarine parts.
It is to be understood that the present invention is not limited to the embodiments described above, but encompasses any and all embodiments within the scope of the following claims.
Number | Name | Date | Kind |
---|---|---|---|
9138806 | Nabawy | Sep 2015 | B2 |
20120060648 | Zhao | Mar 2012 | A1 |
20130152739 | Li et al. | Jun 2013 | A1 |
20160260530 | Yue | Sep 2016 | A1 |
Number | Date | Country |
---|---|---|
104690270 | Jun 2015 | CN |
2000-343202 | Dec 2000 | JP |
WO 2015028065 | Mar 2015 | WO |
Entry |
---|
C. Suranarayana, “Mechanical alloying and milling,” Progress in Materials Science, 46, 2001, pp. 1-184. |