Method of preparing a xylene product

Abstract

A method of modifying a zeolite catalyst to increase para-xylene selectivity of the zeolite catalyst in toluene methylation reactions is provided. The method includes forming a slurry of a ZSM-5-type zeolite and an aqueous solution of a phosphorus compound. Water is removed from the slurry to provide a non-steamed, phosphorus treated ZSM-5 zeolite catalyst without deposition of phosphorus onto the catalyst by organophosphorus vapor deposition. The resulting non-steamed, phosphorus treated ZSM-5 zeolite catalyst has a pore volume of from 0.2 ml/g or less and provides greater than 80% para-xylene selectivity of mixed xylenes when used in toluene methylation.

Description

TECHNICAL FIELD

The invention relates generally to the alkylation of aromatic compounds and catalysts used for such reactions.

BACKGROUND

Para-xylene is a valuable substituted aromatic compound due to its great demand for production of terephthalic acid, a major component in forming polyester fibers and resins. It can be commercially produced from hydrotreating of naphtha (catalytic reforming), steam cracking of naphtha or gas oil, and toluene disproportionation.

Alkylation of toluene with methanol, which is also known as toluene methylation, has been used in laboratory studies to produce para-xylene. Toluene methylation has been known to occur over acidic catalyst, particularly over zeolite or zeolite-type catalyst. In particular, ZSM-5-type zeolite, zeolite Beta and silicaaluminophosphate (SAPO) catalysts have been used for this process. Generally, a thermodynamic equilibrium mixture of ortho (o)-, meta (m)- and para (p)-xylenes can be formed from the methylation of toluene, as is illustrated by the reaction below.

Thermodynamic equilibrium compositions of o-, m-, and p-xylenes may be around 25, 50 and 25 mole %, respectively, at a reaction temperature of about 500° C. Such toluene methylation may occur over a wide range of temperatures, however. Para-xylene can be separated from mixed xylenes by a cycle of adsorption and isomerization. Byproducts such as C9+ and other aromatic products can be produced by secondary alkylation of the xylene product.

A significantly higher amount of p-xylene can be obtained in toluene methylation reaction if the catalyst has shape selective properties. Shape selective properties can be obtained in modified zeolite catalysts by modifying zeolite pore opening size, inactivation of the external surface of the zeolite or controlling zeolite acidity. Toluene methylation may occur over modified ZSM-5 or ZSM-5-type zeolite catalyst giving xylene products containing significantly greater amounts of p-xylene than the thermodynamic concentration.

Phosphoric acid and other phosphorus-containing compounds have been used to modify ZSM-5 zeolite catalysts to provide shape selective properties. U.S. Pat. No. 6,504,072, for instance, discloses the treatment of ZSM-5 zeolite catalyst with phosphorus to control the reduction of diffusivity and pore volume prior to severe steaming to provide a para-selective catalyst. U.S. Pat. No. 4,554,394 discusses the treatment of ZSM-5 zeolites with a vapor phase organophosphorus reagent to provide para-selective properties.

Unfortunately, there are a number of technical hurdles for toluene methylation to be commercially successful and improvements are needed.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention, reference is now made to the following descriptions taken in conjunction with the accompanying figures, in which:

FIG. 1 is a plot of BET surface area of different H₃PO₄ modified ZSM-5 zeolite catalysts as a function of the amount of phosphorus used in the modification;

FIG. 2 is a plot of total pore volume of different H₃PO₄ modified ZSM-5 zeolite catalysts as a function of the amount of phosphorus used in the modification;

FIG. 3 shows ²⁷Al MAS-NMR spectra of (a) NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio 280, and of (b) phosphorus modified ZSM-5 zeolite catalyst;

FIG. 4 is a plot of wt % total xylenes and selectivity to total xylenes and p-xylene for a liquid product stream obtained from toluene methylation over H₃PO₄ modified ZSM-5 zeolite catalysts having a starting SiO₂/Al₂O₃ mole ratio of 30 as a function of amount of phosphorus used in the modification; and

FIG. 5 is a plot of wt % total xylenes and selectivity to total xylenes and p-xylene for a liquid product stream obtained from toluene methylation over H₃PO₄ modified ZSM-5 zeolite catalysts having a starting SiO₂/Al₂O₃ mole ratio of 280 as a function of amount of phosphorus used in the modification.

DETAILED DESCRIPTION

As used herein, the expression “ZSM-5-type” is meant to refer to those zeolites that are isostructurally the same as ZSM-5 zeolites. Additionally, the expressions “ZSM-5” and “ZSM-5-type” may be used herein interchangeably to encompass one another and should not be construed in any limiting sense. The ZSM-5 zeolite catalysts and their preparation are described in U.S. Pat. No. 3,702,886, which is herein incorporated by reference.

As used herein, catalytic activity can be defined as the production of total xylenes as measured by the weight % of total xylenes in the liquid product stream obtained at a given toluene methylation reaction conditions. As used herein, the total xylenes selectivity can be defined as:% Total Xylenes Selectivity=(X_tx/X_tap)×100  (2)where, X_tx is the weight % of total xylenes and X_tap is the weight % of total aromatic products in the liquid product stream. As used herein, selectivity for p-xylene may be expressed as:% p-Xylene Selectivity=(X_p/X_tx)×100  (3)where, X_p is the weight % p-xylene in the liquid product stream.

By modifying ZSM-5 zeolite catalysts with phosphorus containing compound to provide a selected pore volume, increased para-selectivity may be achieved without the need for subsequent steaming or additional treatment of the catalyst. Furthermore, increased catalyst activity and total xylenes selectivity may be achieved during use in toluene methylation for particular ZSM-5 zeolite catalysts, while still providing high p-xylene selectivity.

The starting ZSM-5 zeolite may be an NH₄- or H-form zeolite, which may be in the form of a powder or any other form. In the present invention, the ZSM-5 zeolite catalyst may include those having a silica/alumina molar ratio of greater than 25 prior to modification with a phosphorus-containing compound. As is discussed below, the silica/alumina ratio of the initial ZSM-5 zeolite catalyst may have an effect on catalyst activity and xylene selectivity of the subsequently treated catalyst in toluene methylation. In certain instances, the SiO₂/Al₂O₃ mole ratio of starting ZSM-5 may be from 250, 280, 300 to 1000 or more to achieve higher activity with increased p-xylene selectivity.

The phosphorus compound may be a phosphorus-containing acid, such as phosphoric acid (H₃PO₄) and phosphorus acid (H₃PO₃). For phosphorus-containing acids, the acid may be used at a concentration of greater than 50 wt %. The phosphorus compound may also include other non-acid phosphorus-containing compounds, such as ammonium hydrogen phosphate ((NH₄)₂HPO₄). The amount of phosphorus used may provide a phosphorus content of the treated catalyst of from 0.04 g P/g zeolite or more. In certain applications, phosphorus may be incorporated into the catalyst in amounts of from 0.09 g P/g zeolite or more, with from about 0.09 g P/g zeolite to about 0.15 g P/g zeolite being suitable in such applications.

The phosphorus may be incorporated into the catalyst by preparing a slurry of the zeolite and an aqueous solution of the phosphorus compound. Heating of the slurry may be used to facilitate treatment of the zeolite catalyst and to evaporate liquids. Heating of the slurry to temperatures of from 70° C. to about 100° C. is suitable in most instances. The slurry may also be stirred or agitated during this step to ensure uniform treatment.

The phosphorus-modified zeolite catalyst may be used unbound or be bound with a binder. Examples of suitable binders include such materials as alumina, clay, and silica. Those techniques used for preparing the bound catalyst are well known in the art. The catalyst, bound or unbound, may be calcined at a temperature between 400° C. and 570° C. in an environment containing oxygen, typically air.

The treated ZSM-5 zeolite catalyst should provide a total pore volume of from about 0.2 ml/g or less. More particularly, the total pore volume may range from about 0.18 ml/g to about 0.07 ml/g. The BET surface area of the ZSM-5 zeolite catalyst may range from less than 300 m²/g to about 10 m²/g.

The phosphorus-modified catalyst contains an insignificant amount of tetrahedral/structural Al in the zeolite framework showing a weak ²⁷Al-NMR peak at around 50 ppm, but the catalyst contains “debris” or extra framework aluminum (EFAl) inside zeolite pores showing a strong ²⁷Al-NMR peak at −14 ppm. The ratio of framework aluminum over extra-framework aluminum for the treated zeolite catalyst may range from about 0.12 to 0.25.

The treated catalyst may be used as a non-steamed catalyst in toluene methylation. As used herein, “non-steamed,” as it refers to the zeolite catalyst, is meant to include zeolite catalyst that has not been treated or subjected to high temperature steam (i.e. greater than 950° C.) to effect structural changes of the catalyst prior to its use in any alkylation or methylation reactions.

The modified catalyst may be contacted with an appropriate feed of toluene and methanol under methylation reaction conditions to carry out toluene methylation. A hydrogen cofeed may also be used. The hydrogen may be used in an amount of at least 0.1 mole per mole of toluene/methanol feed.

Water or steam may also be introduced into the reactor as cofeed along with the toluene/methanol feed. The water or steam used for the methylation reaction may be introduced with or without hydrogen as cofeed with the hydrocarbon feed to the reactor during the start up of the methylation reaction or it may be introduced subsequent to initial start up. In either case, liquid water may be added and vaporized prior to its mixing with hydrogen cofeed (if any) and hydrocarbon feed.

The reactor pressure for toluene methylation or other aromatic alkylation may vary, but typically ranges from about 10 to about 1000 psig. Reactor temperatures may range from 400 to 700° C.

The reaction may be carried in a variety of different reactors that are commonly used for carrying out aromatic alkylation reactions. Single or multi reactors in series and/or parallel are suitable for carrying out the toluene methylation.

The modified catalyst is useful in toluene methylation for preparing a xylene product from a feed of toluene and methanol that has increased selectivity for p-xylene. In particular, the catalyst may provide greater than 80%, 85% and 90% para-xylene selectivity when used in toluene methylation. Additionally, in certain instances, greater than 90% of total xylene selectivity may be achieved.

The following examples further illustrate the invention.

EXAMPLES

Catalyst Preparation

Catalyst A-H

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 30. An aqueous slurry containing 11.63 g of NH₄-ZSM-5 zeolite and 50 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 1.08 g phosphoric acid (85 wt % in aqueous) was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The phosphoric-acid modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of catalysts A-H (see Table 1) were prepared by varying the amount of phosphoric acid with respect to the amount of starting NH₄-ZSM-5 powder. BET surface area and total pore volume (measured by N₂ adsorption) for catalysts A-H are shown in Table 1 and in FIGS. 1 and 2.

TABLE 1
	Water,	Zeolite	H3PO4	P, g/g	SA,
Catalyst	ml	Powder, g	Content, ga	zeolitea	m2/g	PV, ml/g
A	100	46.50	4.00	0.023	266.4	0.483
B	50	11.63	1.08	0.025	259.0	0.340
C	50	11.63	2.52	0.058	157.8	0.212
D	50	11.64	4.04	0.093	66.9	0.189
E	50	11.63	6.01	0.139	24.0	0.183
F	50	11.63	8.05	0.186	18.6	0.179
G	50	11.64	12.51	0.279	14.2	0.077
H	50	11.64	16.01	0.370	9.7	0.079
I			0	0	357.2	0.579
aTotal amount of phosphoric acid (85% in aqueous) or P used in the preparation

As can be seen from Table 1 and FIGS. 1 and 2, a sharp decrease in BET surface area (SA) and total pore volume (PV) of the zeolite catalysts A-H prepared by using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio of 30 with increasing amounts of phosphoric acid or P was observed.

Catalyst J-N

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. A slurry containing 12.09 g of NH₄-ZSM-5 zeolite and 50 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 1.08 g phosphoric acid (85 wt % in aqueous) was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The phosphoric-acid modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of catalysts J-N (see Table 2) were prepared by varying the amount of phosphoric acid with respect to the amount of starting NH₄-ZSM-5 powder. BET surface area and total pore volume (measured by N₂ adsorption) for catalysts J-N are shown in Table 2 and FIGS. 1 and 2. The decrease in SA and PV for catalyst made using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio 280 is not as prominent compared to that for catalysts A-J prepared by using starting NH₄-ZSM-5 having SiO₂/Al₂O₃ mole ratio 30.

TABLE 2
	Water,	Zeolite	H3PO4	P, g/g	SA,
Catalyst	ml	Powder, g	Content, ga	zeolitea	m2/g	PV, ml/g
J	50	12.09	1.08	0.024	330.7	0.208
K	50	24.09	3.95	0.044	299.4	0.182
L	100	48.38	15.8	0.088	183.2	0.138
M	100	48.39	23.7	0.123	156.2	0.113
N	50	12.09	7.75	0.172	163.7	0.120
O			0	0	375.0	0.244
aTotal amount of phosphoric acid (85% in aqueous) or P used in the preparation.

Catalyst P-S

The starting material was an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. A slurry containing 51.66 g of NH₄-ZSM-5 zeolite and 200 ml of deionized water was prepared in a 400 ml beaker. The beaker was placed on a hot plate and the zeolite suspension was stirred using a magnetic stir bar. The temperature of the suspension was maintained around 90° C. 9.07 g ammonium hydrogen phosphate, (NH₄)₂HPO₄, was dissolved in 50 ml water and the salt solution was added drop wise into the beaker. Heating was continued until all liquid was evaporated. The ammonium hydrogen phosphate modified zeolite was dried at 90° C. to 120° C. for at least four hours and at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined zeolite was then crushed and sized using 20 and 40 mesh screens. A series of catalysts P-S (see Table 3) were prepared by varying the amount of ammonium hydrogen phosphate with respect to the amount of starting NH₄-ZSM-5 powder. BET surface area and total pore volume (measured by N₂ adsorption) for catalysts P-S are shown in Table 3.

TABLE 3
	Water,	Zeolite	(NH4)2HPO4,	P, g/g	SA,	PV,
Catalyst#	ml	Powder, g	ga	zeolitea	m2/g	ml/g
P	200	30.09	2.49	0.018	317.2	0.208
Q	200	51.66	9.07	0.039	278.3	0.179
R	200	51.66	12.85	0.055	241.0	0.155
S	200	48.38	18.14	0.082	216.2	0.131
aTotal amount of ammonium hydrogen phosphate or P used in the preparation

There was little or no difference in surface area and pore volume between the catalyst series J-N using phosphoric acid and P-S using ammonium hydrogen phosphate at a given amount of phosphorus. Thus the use of phosphoric acid or ammonium hydrogen phosphate as a phosphorus-containing compound for preparing p-xylene selective catalysts may not make a significant difference.

Comparative Catalysts I & O

Non-phosphorus containing ZSM-5 zeolite catalysts were prepared for comparison purposes. The starting material was either an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 30 or an NH₄-ZSM-5 zeolite powder having a SiO₂/Al₂O₃ mole ratio of 280. The zeolite powder was dried at 340° C. to 360° C. for three hours and then calcined at 510° C. to 530° C. under air for 10 hours. The calcined sample was then pressed and sized using 20 and 40 mesh screens for use in a reactor for toluene methylation reaction. Properties for catalysts I and O are presented in Tables 1 and 2, respectively.

²⁷Al MAS-NMR

Magic angle spinning (MAS) solid state NMR studies were performed on the starting NH₄-ZSM-5 zeolite having SiO₂/Al₂O₃ mole ratio 280 and the phosphorus modified catalyst samples. Measurements used 400 MHz spectrometer (²⁷Al at 104.5 MHz), room temperature, silicon nitride rotors (Si₃N₄), 13 to 14 KHz sample spinning (about 800000 rpm), 10 degree tip to avoid saturation and 4000-10000 scans signal averaging. Proton decoupling was not employed. All spectra were referenced to aluminum chloride hexahydrate (run separately in a tube) at 0.0 ppm on the chemical shift scale. This leads to an internal reference of 104.85 ppm on the aluminum nitride (small impurity in the silicon nitride rotors).

The starting NH₄-ZSM-5 zeolite sample showed a strong ²⁷Al MAS-NMR peak at around 55 ppm attributing to framework tetrahedral (4 coordinated) aluminum (spectrum a, FIG. 3). The sharpness of the resonance and the symmetry indicate the zeolite is relatively crystalline with very few lattice defects. The framework Al is responsible for zeolite acidity and the starting zeolite sample showed strong acidity. The P-modified sample shows a weak peak at 55-50 ppm region assigned to structural tetrahedral aluminum (spectrum b, FIG. 3). The tetrahedral aluminum peak is severely distorted indicating presence of nested silanols caused by holes in the structure upon removal of some of the framework aluminum. The adjacent peak (30-40 ppm) peak is due to severely distorted but still in the framework aluminum atoms probably either in the 3 or 5 coordination with oxygens. The biggest peak in the spectrum at −14 ppm is from octahedrally coordinated aluminum atoms that are formed when tetrahedrally coordinated framework aluminum is removed from the zeolite framework by the phosphate modification process as mentioned above.

Examples 1-19

The catalysts A-I, J-O and P-S described above and in Tables 1-3, were used in toluene methylation reactions. The reactions were each carried out in a fixed bed, continuous flow type reactor. In each case, a catalyst was dried by slowly raising the catalyst bed temperature (about 5° C./min) to 200° C. under hydrogen (H₂) flow for at least one hour. A premixed toluene and methanol feed (molar ratio 2/1) was added to the reactor at 200° C. and the catalyst bed inlet temperature was increased to about 500° C. The liquid hourly space velocity (LHSV) (based on toluene/methanol feed) was maintained at about 31 hr⁻¹ and a cofeed of H₂ gas was fed and maintained to provide a H₂/HC molar ratio of about 0.1. Water was added to the hydrocarbon (HC) feed and was vaporized prior to introduction to reactor. The H₂O/HC molar ratio was about 0.65 and reactor pressure was about 20 psig. Liquid products were collected at about 3-4 hours of run time and were analyzed. The following results, as presented in Tables 4-6. FIG. 4 is a plot of para-xylene selectivity and selectivity for total xylenes for catalysts A-I. FIG. 5 is a plot of para-xylene selectivity and selectivity for total xylenes for catalysts J-O.

	TABLE 4
	Catalyst
	A	B	C	D	E	F	G	H	I
	Example
Product Analysis, wt %1	1	2	3	4	5	6	7	8	9
Water	21.06	21.50	21.61	21.90	19.02	18.21	16.54	17.27	21.72
Methanol	0	0.10	0.15	0.75	4.05	4.64	5.37	6.48	0.08
Dimethylether	0	0	0	0	0	0	0	0	0
Benzene	1.39	1.18	0	0	0	0	0	0	0.43
Toluene	43.82	44.77	50.54	54.86	70.21	72.00	75.33	74.11	49.63
Ethylbenzene	0	0	0	0	0	0	0	0	0
p-Xylene (PX)	7.11	6.85	12.35	14.30	5.58	4.49	2.65	2.03	5.86
m-Xylene (MX)	15.44	14.88	8.94	4.20	0.47	0.26	0.11	0.11	12.48
o-Xylene (OX)	6.86	6.58	3.46	1.82	0.30	0.17	0	0	5.38
Ethyltoluenes	1.01	0.95	0.42	0.26	0.14	0.11	0	0	1.18
Trimethylbenzenes	2.94	2.84	2.33	1.75	0.22	0.12	0	0	2.81
C10+	0.36	0.36	0.20	0.16	0	0	0	0	0.41
Total Aromatic Products, wt %	35.11	33.64	27.70	22.49	6.71	5.15	2.76	2.14	28.55
Total Xylenes, wt %	29.41	28.31	24.75	20.32	6.35	4.92	2.76	2.14	23.72
Total Xylenes Selectivity, wt %	83.77	84.16	89.35	90.35	94.63	95.53	100	100	83.08
p-Xylene Selectivity, wt %	24.17	24.20	49.90	70.37	87.87	91.26	96.01	94.86	24.70
1Liquid product stream analysis

	TABLE 5
	Catalyst
	J	K	L	M	N	O
	Example
Product Analysis, wt %1	10	11	12	13	14	15
Water	16.33	16.80	19.73	16.38	15.79	16.12
Methanol	0.54	0.50	2.39	1.72	2.13	0.45
Dimethylether	0	0	0	0	0	0
Benzene	0	0	0	0	0	0.39
Toluene	57.02	57.76	60.57	64.47	66.10	52.37
Ethylbenzene	0	0	0	0	0	0
p-Xylene (PX)	19.55	20.18	15.05	15.24	13.37	8.54
m-Xylene (MX)	3.12	2.04	0.76	0.84	0.96	13.70
o-Xylene (OX)	1.56	1.07	0.48	0.53	0.68	5.50
Ethyltoluenes	0.35	0.36	0.32	0.35	0.33	0.67
Trimethylbenzenes	1.39	1.17	0.45	0.47	0.55	2.05
C10+	0.12	0.11	0.25	0	0.09	0.20
Total Aromatic Products,	26.09	24.93	17.31	17.43	15.98	31.05
wt %
Total Xylenes, wt %	24.23	23.29	16.29	16.61	15.01	27.74
Total Xylenes Selectivity,	92.87	93.42	94.11	95.30	93.93	89.34
wt %
p-Xylene Selectivity, wt %	80.69	86.65	92.39	91.75	89.07	30.79
1Liquid product stream analysis

	TABLE 6
	Catalyst
	P	Q	R	S
	Example
Product Analysis, wt %1	16	17	18	19
Water	17.65	16.46	16.22	16.58
Methanol	0.57	0.85	0.98	2.27
Dimethylether	0	0	0	0
Benzene	0	0	0	0
Toluene	56.17	60.21	61.74	66.50
Ethylbenzene	0	0	0	0
p-Xylene (PX)	19.87	18.17	18.34	13.34
m-Xylene (MX)	2.53	1.76	1.05	1.06
o-Xylene (OX)	1.47	0.98	0.58	0.25
Ethyltoluenes	0.35	0.36	0.41	0
Trimethylbenzenes	1.25	1.08	0.68	0
C10+	0.13	0.12	0	0
Total Aromatic Products, wt %	25.60	22.47	21.06	14.65
Total Xylenes, wt %	23.87	20.91	19.97	14.65
Total Xylenes Selectivity, wt %	93.24	93.06	94.82	100
p-Xylene Selectivity, wt %	83.24	86.90	91.84	91.06
1Liquid product stream analysis

While the invention has been shown in only some of its forms, it should be apparent to those skilled in the art that it is not so limited, but is susceptible to various changes and modifications without departing from the scope of the invention. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the scope of the invention.

Claims

1. A method of preparing a xylene product comprising: forming a slurry of a binder-free ZSM-5 zeolite having a SiO2/Al2O3 mole ratio of from about 250 to about 3000 and an aqueous solution of a phosphorus compound;removing water from the slurry to provide a non-steamed, phosphorus treated ZSM-5 zeolite catalyst without deposition of phosphorus onto the catalyst by organophosphorus vapor deposition, and wherein the resulting non-steamed, phosphorus treated ZSM-5 zeolite catalyst has a pore volume of from 0.2 ml/g or less; andcontacting the treated zeolite catalyst with an aromatic feed of toluene and methanol under reaction conditions suitable for toluene methylation to provide a xylene product having greater than 80% para-xylene by total mixed xylenes.

2. The method of claim 1, wherein: the zeolite catalyst has a pore volume of less than 0.18 ml/g.

3. The method of claim 1, wherein: the phosphorus compound includes at least one of phosphoric acid (H3PO4), phosphorus acid (H3PO3) and ammonium hydrogen phosphate ((NH4)2HPO4).

4. The method of claim 1, wherein: the phosphorus content of the treated ZSM-5 zeolite catalyst is from 0.04 g P/g zeolite or more.

5. The method of claim 1, wherein; contacting the treated zeolite catalyst with an aromatic feed of toluene and methanol under reaction conditions suitable for toluene methylation provides greater than 90% total xylene selectivity and greater than 85% para-xylene selectivity of the xylene product.

6. The method of claim 1, wherein: the phosphorus content of the treated ZSM-5 zeolite catalyst is greater than 0.09 g P/g zeolite.

7. The method of claim 1, wherein: the phosphorus compound is a phosphorus-containing acid.

8. The method of claim 1, wherein: the zeolite catalyst has a ratio of framework aluminum to extra-framework aluminum as measured by 27Al MAS-NMR of 0.12 to 0.25.

9. The method of claim 1, wherein: the zeolite catalyst had a SiO2/Al2O3 mole ratio of from about 300 to about 3000 prior to phosphorus treatment.

10. The method of claim 1, wherein: the pore volume is reduced from about 30% to less than about 60% from that of the untreated zeolite.

11. A method of preparing a xylene product comprising: forming a slurry of a binder-free ZSM-5 zeolite having a SiO2/Al2O3 mole ratio of from about 250 to about 3000 and an aqueous solution of a phosphorus compound;removing water from the slurry to provide a non-steamed, phosphorus treated ZSM-5 zeolite catalyst without deposition of phosphorus onto the catalyst by organophosphorus vapor deposition, and wherein the resulting non-steamed, phosphorus treated ZSM-5 zeolite catalyst has a phosphorus content of from 0.04 g P/g zeolite or more and a pore volume of from 0.2 ml/g or less; andcontacting the treated zeolite catalyst with an aromatic feed of toluene and methanol under reaction conditions suitable for toluene methylation to provide a xylene product having greater than 80% para-xylene by total mixed xylenes.

12. The method of claim 11, wherein: the phosphorus content is from 0.09 g P/g zeolite to 0.15 g P/g zeolite.

13. The method of claim 11, wherein: the phosphorus compound is a phosphorus-containing acid.

14. The method of claim 11, wherein: the zeolite catalyst has a pore volume of less than 0.18 ml/g.

15. The method of claim 11, wherein: the zeolite catalyst has a SiO2/Al2O3 mole ratio of from about 250 to 1000 prior to phosphorus treatment.

16. The method of claim 11, wherein: the zeolite catalyst provides greater than 90% para-xylene selectivity of mixed xylenes when used in toluene methylation.

17. The method of claim 11, wherein: the zeolite catalyst had a SiO2/Al2O3 mole ratio of from about 300 to about 3000 prior to phosphorus treatment.

18. The method of claim 11, wherein: the zeolite catalyst has a ratio of framework aluminum to extra-framework aluminum as measured by 27Al MAS-NMR of 0.12 to 0.25.

19. The method of claim 11, wherein: the pore volume is reduced from about 30% to less than about 60% from that of the untreated zeolite.