Patent Application
20080145570
1. Technical Field
The present invention relates to a method of preparing a carbon-nanotube based composite material and, more particularly, to a method of preparing a carbon nanotube/polymer composite material.
2. Description of Related Art
Since the report of their discovery in 1991 by Iijima, carbon nanotubes (CNTs) have been extensively studied for their interesting structural, physio-chemical, mechanical, electrical, and electromechanical properties. Many potential technological applications have been proposed including hydrogen storage, nanoelectronic devices, field emission display (FED), field emission microscopy (FEM), chemical sensors, and so on. Carbon nanotubes are considered desirable, at least in part, due to their unique electrical and mechanical properties. Currently, the study of carbon nanotube/polymer composite materials is gaining significant attention. Such a nanotube-reinforced composite material has board applications because of good antistatic performance, microwave absorbing capability, electromagnetic shielding ability, and so on.
Generally speaking, a carbon nanotube/polymer composite material has been prepared via an in-situ polymerization process, solution compounding process, and/or a melt compounding process.
However, a carbon nanotube/polymer composite material prepared by the above-mentioned processes tend to have a relatively higher resistance value. Furthermore, relatively poor conductivity network is formed among carbon nanotubes. Such high resistance and poor conductivity is essentially a product of a lack of connectivity between a significant number of proximate carbon nanotubes. Therefore, the good electrical conductivity and thermal conductivity properties of carbon nanotubes has heretofore not, on the whole, been sufficiently utilized in nanotube-based composites.
What is needed, therefore, is a method of preparing a carbon nanotube/polymer composite material, in which carbon nanotubes have desirable interconnection.
In one present embodiment, a method of preparing a carbon nanotube/polymer composite material includes the steps of:
In another present embodiment, a method of preparing a multilayer carbon nanotube/polymer composite material includes the steps of:
Many aspects of the present method can be better understood with reference to the following drawings. The components in the drawings are not necessarily to scale, the emphasis instead being placed upon clearly illustrating the principles of the present method.
Corresponding reference characters indicate corresponding parts throughout the several views. The exemplifications set out herein illustrate at least one preferred embodiment of the present method, in one form, and such exemplifications are not to be construed as limiting the scope of the embodiment in any manner.
Embodiments will now be described in detail below and with reference to the drawings. Referring to
In step (a), the carbon nanotube-based film may be produced, e.g., by a volatilization method or a chemical vapor deposition (CVD) method. The volatilization method includes the following steps of: firstly, mixing carbon nanotubes and dimethyl formamide solution together; secondly, dispersing the carbon nanotubes into the dimethyl formamide solution by an ultrasonic vibration dispersion method, thereby obtaining a mixture; and finally volatilizing the dimethyl formamide from the mixture, thereby obtaining the carbon nanotube-based film.
The pre-polymer solution may, for example, be a polymethyl methacrylate (PMMA) solution. A method of preparing the polymethyl methacrylate (PMMA) solution includes the following steps. Firstly, a pre-polymer such as 93˜99.98 wt % of methyl methacrylate (MMA), a reaction initiator such as 0.02˜2 wt % of azodiisobutyronitrile (AIBN), and a polymerization assistant, such as 0˜5 wt % of dibutyl phthalate (DBP), are mixed together. Secondly, the admixture is pre-polymerized in a water bath of 80° C.˜95° C. and stirred/churned for 5˜30 minutes. The admixture is heated until the admixture looks like glycerin. Finally, the admixture is naturally cooled in ambient air until the pre-polymerization reaction has stopped.
In the present embodiment, the pre-polymer may, beneficially, be selected from the group consisting of ethyl acrylate, butyl acrylate, styrene, butadiene, acrylonitrile, and combinations thereof. The reaction initiator may be selected from the group consisting of benzoperoxide, azodiisobutyronitrile, and combinations thereof. The polymerization assistant may be selected from the group consisting of dibutyl phthalate, cetyl trimethyl ammoniumbromide, polyethylene acid salt, polymethacrylic acid salt, C12-C18 high fatty acid, silane coupling agent, titanate coupling agent, aluminate coupling agent, and combinations thereof.
In step (b), after the pre-polymer solution is poured in the container, the container is advantageously able to stand for 0.5˜2 hours so that the pre-polymer solution can adequately settle and fill in interspaces of the carbon nanotube-based film to thereby form a mixed layer of the carbon nanotube-based film and pre-polymer solution at the bottom portion of the container.
In step (c), a carbon nanotube/polymer composite film with a single-side electrical conductivity (i.e., one side of the composite film remains covered by a layer of polymerized solution, which acts as an insulating layer) is able to be produced in the present embodiment.
The carbon nanotube-based film begins to be integrated with the pre-polymer solution at the interface therebetween. After the pre-polymer solution is polymerized, the produced polymer is tightly integrated with the carbon nanotubes of the carbon nanotube-based film, thereby forming the carbon nanotube/polymer composite material.
The processes of polymerization and integration are described in detail, as follows. Firstly, the container that contains the pre-polymer solution and the carbon nanotube-based film therein is held at a temperature of 50° C.˜60° C. for 1˜4 hours to urge the pre-polymer solution to polymerize and to simultaneously integrate with the carbon nanotube-based film. The container is further heated to 90° C.˜100° C. for approximate 2 hours, so that the pre-polymer solution continues to polymerize and integrate with the carbon nanotube-based film, thereby forming the carbon nanotube/polymer composite film with single-side electrical conductivity. Carbon nanotube/polymer composite film of different thicknesses, e.g., in the range of 0.02˜2 millimeters, can be produced by controlling the addition of the pre-polymer solution and/or the thickness of the initial carbon nanotube-based film.
In addition, one or more additional layers can be formed on the composite. To do so, an additional (e.g., in this case, second) layer of the carbon nanotube-based film is disposed on the exposed/upper (e.g., in this case, the first) carbon nanotube/polymer composite film, and then a definite amount/volume of the pre-polymer solution is poured in the container. After a while, using a treatment process like that used for the first layer, the pre-polymer solution is polymerized and integrated with the additional (e.g., second) carbon nanotube-based film, thereby forming the next additional (e.g., second) layer of the carbon nanotube/polymer composite film. By analogy, a multilayer carbon nanotube/polymer composite film of a desired number of composite layers can be easily prepared.
One particular embodiment provides a first method of preparing a carbon nanotube/PMMA composite film with single-side electrical conductivity. The first method includes the following steps.
(1). Providing a carbon nanotube-based film and a pre-polymer PMMA solution.
The carbon nanotube-based film may be produced by the volatilization method. The volatilization method includes the following steps of: 2˜4 mg carbon nanotubes and 20 ml dimethyl formamide solution are firstly mixed together. Secondly, the carbon nanotubes are further dispersed into dimethyl formamide solution by 20˜100 Hz ultrasonic vibration for about 0.5˜4 hours (2 hours is quite suitable), thereby obtaining a mixture with carbon nanotubes uniformly dispersed therein. The carbon nanotubes may be single-walled carbon nanotubes (SWCNTs) or multi-walled carbon nanotubes (MWCNTs). The dimethyl formamide solution has shown to be a good dispersant for the carbon nanotubes. A saturation point of the carbon nanotubes in the dimethyl formamide solution is about 0.25 mg/ml. Finally, the mixture is poured in a container, and the container is then disposed in a drying box. The mixture is dried in ambient air at a temperature of 100° C. for about 2 hours until the dimethyl formamide is completely volatilized from the mixture. The carbon nanotube-based film is thus prepared at the bottom of the container.
A method of preparing the polymethyl methacrylate (PMMA) solution includes the following steps. Firstly, the polymer, such as 97 wt % of methyl methacrylate (MMA); the reaction initiator, such as 0.1 wt % of azodiisobutyronitrile (AIBN); and the polymerization assistant, such as 2.9 wt % of dibutyl phthalate (DBP), are mixed together. Secondly, the mixture is pre-polymerized in a water bath of 92° C. while being stirred for 10 minutes. The heating occurs until the mixture looks like glycerin. Finally, the mixture is naturally cooled in an air atmosphere until pre-polymerization reaction has stopped.
(2). The carbon nanotube-based film is placed at a bottom portion of a container, and then the pre-polymer solution is poured in the container.
After the pre-polymer solution is poured in the container, the container is beneficially able to stand for 0.5˜2 hours so that the pre-polymer solution can adequately settle and fill in interspaces of the carbon nanotube-based film to thereby form a mixed layer of the carbon nanotube-based film and pre-polymer solution at the bottom portion of the container.
(3). The pre-polymer solution is polymerized, and the pre-polymer solution simultaneously integrates with the carbon nanotube-based film, thereby forming a carbon nanotube/polymer composite material. A carbon nanotube/polymer composite film with single-side electrical conductivity may be produced in the first embodiment.
The processes of polymerization and integration are described in detail as follows. Firstly, the container that has the pre-polymer solution and the carbon nanotube-based film therein, is held at a temperature of 50° C.˜60° C. for 14 hours to urge the pre-polymer solution to polymerize, and to simultaneously integrate with the carbon nanotube-based film. The container is further heated to 90° C.˜100° C. for approximate 2 hours, so that the pre-polymer solution continues to polymerize and integrate with the carbon nanotube-based film, thereby forming the carbon nanotube/PMMA composite film with single-side electrical conductivity.
Referring to
Referring to
A second particular embodiment provides a method of preparing a carbon nanotubes array/PMMA composite film with single-side electrical conductivity. The method includes the following steps.
(1). Providing a carbon nanotubes array and a pre-polymer PMMA solution.
The carbon nanotubes array may be produced by the chemical vapor deposition (CVD) method. The chemical vapor deposition (CVD) method includes the following steps. A substrate is first provided. Secondly, a layer of catalyzer, selected from the group consisting of Fe, Co, Ni, or an alloy thereof, is deposited on the substrate. The substrate with the layer of catalyzer deposited, is heat-treated at 300° C.˜500° C. for 0.2˜12 hours in an air atmosphere. The layer of catalyzer changes into oxidized particles after such annealing. Then, the substrate is disposed in a reaction apparatus with a protection gas and heated to a predetermined temperature in the approximate range of 400° C.˜750° C. Protection gas may be any inert gas, nitrogen gas, or combination thereof. Preferably, the protection gas is argon gas. Finally, a mixed gas containing protection gas and carbon source is introduced in the reaction apparatus. When the reaction apparatus is heated to 400° C.˜750° C., a carbon nanotube array is produced therein. The carbon source may be a hydrocarbon such as ethyne or ethane. Preferably, the carbon source is ethyne.
A method of preparing a polymethyl methacrylate (PMMA) solution includes the following steps. Firstly, a pre-polymer such as 95 wt % of methyl methacrylate (MMA), a reaction initiator such as 1 wt % of azodiisobutyronitrile (AIBN), and a polymerization assistant such as 4 wt % of dibutyl phthalate (DBP), are mixed together. Secondly, the admixture is pre-polymerized in a water bath of 95° C. and stirred/churned for 10 minutes. The admixture is heated until the admixture looks like glycerin. Finally, the admixture is naturally cooled in air atmosphere until the pre-polymerization reaction has stopped.
(2). The carbon nanotube array is placed at a bottom portion of a container, and then the pre-polymer solution is poured in the container.
After the pre-polymer solution is poured in the container, the container is advantageously able to stand for 0.5˜2 hours so that the pre-polymer solution can adequately settle and fill in interspaces of the carbon nanotube array to thereby form a mixed layer of the carbon nanotube array and pre-polymer solution at the bottom portion of the container.
(3). The pre-polymer solution is polymerized, and the pre-polymer solution is simultaneously integrated with the carbon nanotube array, thereby obtaining a carbon nanotube array/polymer composite material.
The processes of polymerization and integration are described in detail as follows. Firstly, the container that contains the pre-polymer solution and the carbon nanotube array therein, is held at a temperature of 50° C.˜60° C. for 2.5 hours to urge the pre-polymer solution to polymerize, and to simultaneously integrate with the carbon nanotube array. The container is further heated to 90° C.˜100° C. for approximate 2 hours, so that the pre-polymer solution continues to polymerize and integrate with the carbon nanotube array, thereby forming the carbon nanotube array/ PMMA composite film with single-side electrical conductivity.
Referring to
A third embodiment provides a method of preparing multilayer carbon nanotube array/polymer composite films. The method includes the following steps:
(1). A first carbon nanotube-based film prepared, for example, in the first embodiment or carbon nanotube array prepared in the second embodiment is placed at a bottom portion of a container, and then the pre-polymer solution prepared, e.g., as in the first or second embodiment, is poured in the container.
(2). After the pre-polymer solution is poured in the container, the container is advantageously able to stand for 0.5˜2 hours (one hour is quite suitable) so that the pre-polymer solution can adequately settle and fill in interspaces of the first carbon nanotube-based film or carbon nanotube array to thereby form a mixed layer of the first carbon nanotube-based film or carbon nanotube array and pre-polymer solution at the bottom portion of the container.
(3). The pre-polymer solution is polymerized, and the pre-polymer solution is simultaneously integrated with the first carbon nanotube-based film or carbon nanotubes array, thereby obtaining a carbon nanotubes /polymer composite material.
The processes of polymerization and integration are described in detail as follows. Firstly, the container that contains the pre-polymer solution and the first carbon nanotube-based film or the carbon nanotubes array therein, is held at a temperature of 50° C.˜60° C. for 2 hours to urge the pre-polymer solution to polymerize, and to simultaneously integrate with the first carbon nanotube-based film or carbon nanotube array. The container is further heated to 90° C.˜100° C. for approximate 2 hours, so that the pre-polymer solution continues to polymerize and integrate with the first carbon nanotube-based film or carbon nanotube array, thereby forming a first layer of carbon nanotube-based film or carbon nanotube array/ polymer composite film.
(4). One or more additional layers can be formed on the composite. To do so, an additional (e.g., in this case, the second) layer of the carbon nanotube-based film or carbon nanotube array is disposed on the exposed/upper (e.g., in the case, the first) layer of carbon nanotube/polymer composite film, and then a definite amount/volume of the pre-polymer solution is poured in the container. After a while, using a treatment process like that used for the first layer, the pre-polymer solution is polymerized and integrated with the additional (e.g., second) carbon nanotube-based film or carbon nanotube array, thereby forming the next additional (e.g., second) layer of carbon nanotube/polymer composite film.
Repeating the step (4), a multilayer carbon nanotube/polymer composite film of a desired number of composite layers can be easily prepared.
Referring to
Referring to
The carbon nanotube/polymer composite material prepared according to the embodiments has good electrical conductivity and thermal conduction. The electrical conductivity of the carbon nanotube/polymer composite material is improved by a factor of two (2) over that of a carbon nanotube/polymer composite material prepared by a conventional method. In particular, the electrical conductivity can reach 120 siemens/meter. In addition, the interspaces between the carbon nanotubes are filled with polymer to obtain a stable mechanical connection of the carbon nanotubes. Furthermore, the layer of carbon nanotubes stably connects with the layer of polymer via that same interspace-filling polymer. Therefore, the carbon nanotube/polymer composite material has generally good mechanical properties.
Carbon nanotubes have a stable connection with PMMA in the carbon nanotubes/PMMA composite film prepared according to the first embodiment and in the carbon nanotubes array/PMMA composite film prepared according to the second embodiment. Both the carbon nanotubes/PMMA composite film and the carbon nanotubes array/PMMA composite film can be used as an antistatic material or thermal interface material, due to the good electrical conductivity and thermal conduction of the carbon nanotubes.
The process of preparing multilayer carbon nanotube/polymer composite according to the third embodiment is comparatively simple. It is easy to create an insulative barrier between the two adjacent layers of carbon nanotube/polymer composite films, by using a desired excess amount of pre-polymer material. The multilayer carbon nanotubes/composite can be used, for example, as a capacitor or an electromagnetic shielding material, due to the good electrical conductivity and thermal conduction of the carbon nanotubes.
While certain embodiment has been described and exemplified above, various other embodiments will be apparent to those skilled in the art from the foregoing disclosure. The present invention is not limited to the particular embodiments described and exemplified but is capable of considerable variation and modification without departure from the scope of the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 200610062034.9 | Aug 2006 | CN | national |
This application is related to commonly-assigned, co-pending application: entitled, “CARBON NANOTUBE COMPOSITE”, filed ______ (Atty. Docket No. US11267). The disclosure of the above-identified application is incorporated herein by reference.