Method of preparing tetrarhodium dodecacarbonyl

Abstract

An improved process for making tetrarhodium dodecacarbonyl, Rh.sub.4 (CO).sub.12, reacts RhCl.sub.3.xH.sub.2 O with CO under about 200 psig (14.06 kg/cm.sup.2) at a temperature of about 50.degree. C. in the presence of copper metal and an alkali metal halide, e.g. NaCl. The product mixture is contacted with a chlorinated solvent, e.g. CH.sub.2 Cl.sub.2, which dissolves the desired product and is subsequently recovered by evaporating the solvent.

Description

BACKGROUND OF THE INVENTION

Tetrarhodium dodecacarbonyl (RH.sub.4 (CO).sub.12) is a useful organometallic compound. It can be used as a catalyst or catalyst precursor in such processes as hydroformylation, hydrosilylation and carboxylation. While Rh.sub.4 (CO).sub.12 is a commercially available product, it is very expensive partly because of the difficulty of preparation.

A number of preparations of Rh.sub.4 (CO).sub.12 have been given in the literature. One is based on high pressure (3000 psig, 210.9 kg/cm.sup.2) starting from RhCl.sub.3 or Rh.sub.2 (CO).sub.4 Cl.sub.2 ; other procedures employing atmospheric pressure CO have been taught starting from Rh.sub.2 (CO).sub.4 Cl.sub.2, K.sub.3 (RhCl.sub.6) and RhCl.sub.3.xH.sub.2 O. The compounds Rh.sub.2 (CO).sub.4 Cl.sub.2 and K.sub.3 (RhCl.sub.6) would not be considered good starting materials from an economic standpoint. RhCl.sub.3.xH.sub.2 O is the most readily available starting material. The literature preparations* involve the use of specially treated solvents and the use of inert atmosphere e.g. CO gas padding of the reaction mixture during the product isolation.

*Martinengo, S.; Giordano, G. and P. Chini, Inorg. Synth. 1980, 20, 209.

It would be desirable if a simpler, less complicated and less time consuming process for the preparation of the tetrarhodium dodecacarbonyl could be found.

The present invention is such a process run at low pressures, requiring less time (ca. 2 hours) and does not require specially dried, purified, or deaerated solvents or CO atmosphere handling during the product isolation.

SUMMARY OF THE INVENTION

A simpler, faster process for making tetrarhodium dodecacarbonyl, Rh.sub.4 (CO).sub.12, using as starting material RhCl.sub.3.xH.sub.2 O and reacting with CO under a pressure of about 200 psig, at a temperature of about 50.degree. C. in the presence of copper metal and an alkali metal halide, e.g. NaCl. The product, Rh.sub.4 (CO).sub.12, is separated from the reaction mixture by dissolving in a chlorinated solvent, e.g. methylene chloride, and recovering therefrom by evaporating the solvent.

DETAILED DESCRIPTION OF THE INVENTION

The starting material, RhCl.sub.3.xH.sub.2 O, is dissolved in water and placed in a reactor to which is added an alkali metal halide, e.g. NaCl, and activated copper metal. The reactor is pressured with carbon monoxide from about 25 to about 2500 psig (1.76 to 176 kg/cm.sup.2), preferably from about 50 to about 500 (3.52 to 35.2 kg/cm.sup.2) and heated to a temperature 25.degree.-75.degree. C., preferably 45.degree. to 55.degree. C.

The alkali metal halide and copper metal can be used, within a wide range of from sub-stoichiometric up to perhaps three times stoichiometric, but preferably in about stoichiometric quantities. Pressures above 200 psig (14.06 kg/cm.sup.2) are operable but provide no advantage, but an increase from atmospheric pressure to 200 psig (14.06 kg/cm.sup.2) decreases the time for reaction from 30 hours to <2 hours.

Temperatures above 75.degree. C. cause a decrease in yield, presumably because of the formation of a different product. Temperatures below room temperature cause the reaction to be too slow.

In a representative method the reactants were charged to a 300 cc stirred autoclave with 100-150 cc H.sub.2 O. The autoclave was purged of air and charged to 200 psig (14.06 kg/cm.sup.2) CO then heated to 40.degree.-50.degree. C. Samples were taken to monitor the course of the reaction. After 15 minutes, there was a faint, yellow color (due to RhCl.sub.3.xH.sub.2 O) in the aqueous mixture (red Rh.sub.4 (CO).sub.12 had precipitated); after 30 minutes, the reaction mixture was colorless. To insure completion, the reaction was run for 1 hour. The reactor was cooled, depressurized, and the contents transferred to a beaker with deionized H.sub.2 O. The solid material from the reaction was collected by filtration and the filtrate discarded. The solid should be a mixture of Rh.sub.4 (CO).sub.12, copper, and copper salts. Changing to a clean filtration flask, the solid on the filter was washed with CH.sub.2 Cl.sub.2 to dissolve the Rh.sub.4 (CO).sub.12 and to leave the copper. The Rh.sub.4 (CO).sub.12 and copper was stirred continuously until all of the Rh.sub.4 (CO).sub.12 was dissolved. This treatment was continued until the CH.sub.2 Cl.sub.2 was colorless. The CH.sub.2 Cl.sub.2 solution contained a small amount of water from washing the solid. The water was separated by transferring the liquid to a separatory funnel and adding more water to get a definitive water layer. The water layer was washed one time with more CH.sub.2 Cl.sub.2. The CH.sub.2 Cl.sub.2 was transferred to a round-bottom flask and the CH.sub.2 Cl.sub.2 removed on a rotary evaporator. The Rh.sub.4 (CO).sub.12 was placed in a small bottle and stored in the freezer to retard the slow decomposition it undergoes in the air.

Results of several experiments are shown in the following Table, employing RhCl.sub.3.xH.sub.2 O as the source of rhodium.

TABLE______________________________________ Pressure Rh cpd NaCl Cu Rh.sub.4 (CO).sub.12 % YieldEx. psig (g) (g) (g) (g) Rh.sub.4 (CO.sub.12______________________________________1 200 5 1.2 1.2 3.06 83 (14.06 kg/cm.sup.2)2 200 1.3 0.3 0.3 0.77 80 (14.06 kg/cm.sup.2)3 1000 2.6 0.6 1.5 1.48 77 (70.3 kg/cm.sup.2)______________________________________

The RhCl.sub.3.xH.sub.2 O was a commercially available product. The copper powder used was activated by washing it with an equal mixture of concentrated HCl and acetone and then rinsing with acetone and drying in vacuo. The water used for the reaction was degassed by boiling and sparging with N.sub.2. The methylene chloride was technical grade from a 55-gallon drum and used without purification or deaerating. Contrary to other literature preparations of Rh.sub.4 (CO).sub.12, no precautions were taken to use a CO or inert atmosphere during the isolation of the product.

Claims

1. In a process for preparing tetrarhodium dodecacarbonyl by reacting rhodium trichloride with carbon monoxide in the presence of activated copper metal and an alkali metal halide under a pressure greater than atmospheric, the improvement which comprises conducting the reaction at a pressure of from about 50 to about 500 psig (3.52 to 35.2 kg/cm.sup.2) and at a temperature of 25.degree.-75.degree. C. for a time of less than about two hours.

2. The process of claim 1 wherein the pressure is about 200 psig (14.06 kg/cm.sup.2) and the temperature is from about 45.degree. to about 55.degree. C.

3. The process of claim 2 wherein the copper and alkali metal halide are used in an amount of about stoichiometric with respect to rhodium.

4. The process of claim 3 wherein the alkali metal halide is sodium chloride.