Claims
- 1. A method of preventing the formation of segregations in continuous casting of steel and metal alloys in a strand cast from molten metal, where the cast strand is formed from a molten metal introduced, through a casting chill and undergoing solidification to a solid strand, characterized by physically deforming the cast strand plastically, by action on its external surface, in successive steps from immediately below the chill prior to any other treatment of the strand to a point where the strand is fully solidified, controlling said deforming so that the cross-section area of the strand is reduced to an extent in each of said steps corresponding to the solidification shrinkage and cooling shrinkage of the strand at the position of said step, said deforming steps substantially avoiding upward and downward transport of melt in the strand from the chill to the point where the strand is fully solidified.
- 2. A method according to claim 1, characterized in that said deforming is carried out in order to provide a fully solidified strand in a vertical direction.
- 3. A method according to claim 1, characterized in that said deforming is carried out to provide a fully solidified strand disposed in a horizontal direction.
- 4. A method according to claim 1, characterized in that the cast strand, by a corresponding design of the casting chill, is initially given a substantially rectangular cross-section with convex broad sides, and the deforming is carried out by means of plane rolls in at least one rolling step.
- 5. A method according to claim 1, at which a cast strand with rectangular cross-section is deformed plastically, characterized in that this is carried out by at least one rolling step with rolls, each having a diameter decreasing from the center to both ends.
- 6. A method according to claim 1, characterized in that, said reduction in cross-section is carried out at a deformation rate calculated from the following equations:
- 1=X.sub.C +X.sub.S +X.sub.P +X.sub.Fe +X.sub.other elements
- where,
- X.sub.C =molar fraction of element C,
- X.sub.S =molar fraction of element S,
- X.sub.P =molar fraction of element P,
- X.sub.Fe =molar fraction of element Fe, and
- X.sub.other elements =molar fraction of other elements; ##EQU4## where, M=molar weight of each of the designated elements identified by periodic chart subscripts and E=other alloying or non-metallic elements which are present in the melt such as Si and Mn; and further that, ##EQU5## where, y.multidot.A=volume of the solid phase of a solid/liquid domain having a length .lambda. and an area A wherein the solid phase length is y;
- (.lambda.-y).multidot.A=volume of the liquid phase of solid/liquid domain wherein the liquid phase length is (.lambda.-y);
- dy=the incremental volume of said domain solidifying during a given time period;
- X.sub.s =molar fraction of E in the solid phase volume y.multidot.A;
- V.sub.m.sup.s =molar volume of the solid phase y.multidot.A;
- X.sub.L =molar fraction of E in the liquid phase volume (.lambda.-y).multidot.A;
- V.sub.m.sup.L =molar volume of the liquid phase (.lambda.-y).multidot.A;
- V.sub.in =volume of liquid entering the domain volume .lambda..multidot.A;
- V.sub.out =volume of liquid leaving the domain volume .lambda..multidot.A;
- then summarizing:
- I+II+III-IV=V+VI
- where, the symbolized terms are as above defined; and further wherein, ##EQU6## where, S.sub.sh =the solidification shrinkage when incremental volume dy.multidot.A solidifies;
- and wherein,
- deformation rate=solidification shrinkage+cooling shrinkage in the semi-solidified area-cooling shrinkage in the surrounding solid area; and
- at the condition
- V.sub.in =V.sub.out =0.
- 7. A method according to claim 1, characterized in that, said reduction in cross-section area is in the range of from 1% to 10% and is carried out in 20 to 40 successive steps.
- 8. A method according to claim 1, characterized in that said controlling step is carried out according to the following equation:
- deformation rate=solidification shrinkage and cooling shrinkage in the semi-solidified area-cooling shrinkage in the surrounding solid area.
RELATED APPLICATIONS
This application is a continuation-in-part of Ser. No. 819,214, filed July 26, 1977. The entire disclosure of Ser. No. 819,214 is hereby included by reference as though fully set forth herein.
US Referenced Citations (5)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
819214 |
Jul 1977 |
|