Patent Grant
9181698
The present disclosure relates to a method of forming a balancing layer on a building panel, a semi-finished product and a building panel.
Traditional laminated panels, intended to be used for e.g. flooring or furniture components, are generally produced by the following steps:
Typical press parameters are 40-60 bar pressure and a temperature of 160-200° C. with a pressing time of 8-45 seconds. The surface layer has generally a thickness of 0.1-0.2 mm, the thickness of the core varies between 6-12 mm and the balancing layer is about 0.1-0.2 mm thick.
This production method and product produced by such methods are generally referred to as the DPL process and DPL products (Direct Pressure Laminate).
Recently, building panels with a wood fibre based surface have been developed. Powder comprising wood fibres, a binder, preferably melamine formaldehyde resin, aluminium oxide particles and colour pigments are scattered on a core of a wood fibre based material such as HDF and pressed under heat and pressure in a continuous or discontinuous press to obtain a product with a paper free and solid surface layer. The press parameters are similar to DPL. A higher pressure of 40-80 bar and a pressing time of 15-45 seconds may be used when the surface is formed with deep embossing and a thickness of, for example, 0.4-0.6 mm. The pressing temperature is generally 150-200° C. Such wood fibre based floors, generally referred to as Wood Fibre Floors (WFF), have considerably better properties than traditional laminate floors since a thicker and more impact-resistant and wear-resistant surface with deep embossing may be produced in a cost efficient way.
Both DPL products and panels having a wood fibre based surface have a balancing layer arranged on the rear face of the core. The balancing layer may be a balancing paper or powder-based balancing layer comprising wood fibres and a binder. The core with the upper and lower layers is moved into a press and pressed under heat and pressure such that the layers are cured and attached to the core.
The layers on the front face and the rear face of the core are exposed to a first shrinking when the thermosetting resin in the upper and lower layer cures during pressing. The balancing layer at the rear face balances the tension that is created by the surface layer of the front face and the panel is substantially flat with a small convex backward bending when it leaves the press. Such first shrinking and balancing of the panel is below referred to as “pressing balancing”. The second temperature shrinking, when the panels is cooled from about 150-200° C. to room temperature, is also balanced by the balancing layer and the panel is essentially flat. The second balancing is below referred to as “cooling balancing”. A small convex backward bending is preferred since this counteracts upward bending of the edges in dry conditions when the relative humidity may go down to 20% or lower during wintertime.
A problem is that this essentially flat panel comprises tension forces caused by the shrinking of the surface and balancing layers during pressing and during cooling to room temperature.
The surface layer and the core will swell in summertime when the indoor humidity is high and shrink in wintertime when the indoor humidity is low. The panels will shrink and expand and a cupping of the edges may take place. The balancing layer is used to counteract such cupping. In the installed floor, the balancing layer is used to work as a diffusion barrier for moisture from the underlying floor, and to minimize the impact of the surrounding climate. Consequently, the balancing layer is adapted balance shrinking and expansion caused by both pressing, cooling and climate changes.
It is known that a balancing layer comprising a powder mix of wood fibres and a thermosetting binder can be used to balance the surface layer. A method for producing such a balancing layer is described in WO 2012/141647.
US 2010/0239820 describes a method of producing a laminated decorative plate wherein an unimpregnated decorative layer is applied onto a layer of glue arranged on the core. A counteracting layer is arranged on the other side of the core, and it is described that neutral paper with solid or liquid resin as a glue is suitable for the counteracting layer. The counteracting layer is adapted to prevent the finished plate from warping or bending as a result of influences of temperature and humidity. WO 2010/084466 discloses a balancing layer substantially consisting of a synthetic material layer, which is free from material sheets. The synthetic material is provided in liquid form.
It is an object of at least certain embodiments of the present invention to provide an improvement or alternative over the above described techniques and prior art.
A further object of at least certain embodiments of the present invention is to provide a method reducing the cost for providing a building panel with a balancing layer.
A further object of at least certain embodiments of the present invention is to reduce the amount of thermosetting binder in the balancing layer.
At least some of these and other objects and advantages that will be apparent from the description have been achieved by a method of producing a building panel. The method comprises:
providing a core,
applying a balancing layer on a first surface of the core, wherein the balancing layer has a first moisture content and comprises a sheet impregnated with a thermosetting binder,
applying a surface layer on a second surface of the core, wherein the surface layer has a second moisture content and comprises a thermosetting binder,
adjusting the first moisture content of the balancing layer such that the first moisture content of the balancing layer is higher than the second moisture content of the surface layer prior to curing by applying heat and pressure, and
curing the surface layer and the balancing layer by applying heat and pressure.
By moisture content is meant water present in any form.
The balancing layer is adapted to counteract shrinking forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing. The shrinking forces formed by the thermosetting binder of the surface layer during pressing and curing are balanced or counteracted by the shrinking forced formed by the thermosetting binder of the balancing layer during pressing. By arranging a balancing layer on the core opposite the surface layer, the shrinking forces formed by the thermosetting binder in the surface layer and by the thermosetting binder in the balancing layer are balanced against each other.
An advantage of at least embodiments of the invention is that by adjusting the moisture content of the balancing layer to be higher than the moisture content of the surface layer prior to curing, for example, by applying water on the core and/or on the balancing layer, the balancing layer can balance larger shrinking forces formed by the surface layer during pressing and cooling. By increasing the moisture content of the balancing layer prior to curing, the amount of thermosetting binder of the balancing layer can be reduced. A thinner paper, i.e. a paper having reduced weight per square meter, can also be used. The reduced amount of the thermosetting binder of the balancing layer is compensated by the effects of the higher moisture content of the balancing layer.
Pressing tests show that a suitable moisture content in a balancing layer comprising a thermosetting binder such as melamine formaldehyde may increase the shrinking forces during curing and cooling and that this may be used to reduce the amount of the thermosetting binder in the balancing layer. It is preferred that the moisture content in the thermosetting binder of the balancing layer prior to pressing is higher than the general moisture content of about 4.5-6% that is the case when conventional impregnated paper is used as a balancing layer. The moisture content of the balancing layer should preferably exceed the moisture content of the surface layer. The moisture content of the balancing layer preferably exceeds 10% of the total weight of the balancing layer. In some application it may be an advantage to use even higher moisture contents, for example, exceeding 20%. The moisture content is measured prior to pressing. The moisture content in a conventional backing paper is usually limited by the fact that the papers are stacked on a pallet and too high moisture content causes sticking and single paper sheets cannot be taken from the pallet.
The moisture in the balancing layer contributes to the increased balancing capacity of the balancing layer in several ways. The moisture in the balancing layer facilitates and improves heat transfer from the heated press plates into the balancing layer, thus accelerating and/or increasing cross-linking of the thermosetting resin. The moisture content also influences curing of the thermosetting resin by increasing or facilitating floating of the thermosetting binder, which may result in a higher degree of cross-linking. The moisture content of the balancing layer may also influence the core of the building panel. The moisture content of the balancing layer may make the core, for example, a core of a wood-based material, more formable during pressing. A small convex backward bending of the core may be achieved, counteracting an upward bending of the edges of the surface layer. The method may comprise adjusting the moisture content of the balancing layer and/or the surface layer such that the moisture content of the balancing layer is higher than the moisture content of the surface layer.
The step of adjusting the first moisture content of the balancing layer may comprise applying water or steam to the first surface of the core prior to applying the balancing layer.
The step of adjusting the first moisture content of the balancing layer comprises applying water or steam to the balancing layer. Adjusting the first moisture content of the balancing layer may also be performed by applying water or steam to both the first surface of the core and to the balancing layer prior to curing by applying heat and pressure.
The first moisture content of the balancing layer may be about 6-30%, preferably 8-20% of the total weight of the balancing layer prior to curing.
The first moisture content of the balancing layer may exceed 10%, preferably exceeds 20%, more preferably exceeds 30%, of the total weight of the balancing layer.
The thermosetting binder may be of the same type in the surface layer and in the balancing layer.
The thermosetting binder of the surface layer and/or the balancing layer may be melamine formaldehyde resin. The thermosetting binder of the surface binder and/or the balancing layer may also be urea melamine formaldehyde or a combination of urea/melamine formaldehyde. Any other amino resin is also possible, such as phenol formaldehyde resin.
The sheet impregnated with the thermosetting binder may be a paper sheet impregnated with the thermosetting binder. The paper sheet is preferably a melamine formaldehyde impregnated paper.
The surface layer may comprise a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper. The surface layer may also comprise an overlay paper, preferably a resin impregnated overlay paper comprising wear resistant particles.
The surface layer may comprise a layer comprising a thermosetting binder and at least one pigment.
The amount of the thermosetting binder in the balancing layer may be lower than the amount of the thermosetting binder in the surface layer.
The core may be wood-based material such as a MDF, HDF, plywood, OSB, Wood Plastic Composite (WPC), etc.
According to a second aspect of the invention, a semi-finished product for forming a building panel after curing is provided. The semi-finished product comprises a core having a first surface and a second surface opposite the first surface, a balancing layer arranged on the first surface of the core, wherein the balancing layer comprises a sheet impregnated with a thermosetting binder, a surface layer arranged on the second surface of the core, wherein the surface layer comprises a thermosetting binder, wherein a first moisture content of the balancing layer is higher than a second moisture content of the surface layer prior to curing.
By curing is meant curing by applying heat and pressure, i.e. reacting the thermosetting binder to C-stage.
The second aspect incorporates all the advantages of the fifth aspect of the invention, which previously have been discussed in relation to the first aspect, whereby the previous discussion is applicable also for the building panel.
The thermosetting binder of the balancing layer may B-stage.
The balancing layer is adapted to counteract forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing and curing.
The first moisture content of the balancing layer may be about 6-30%, preferably 8-20%, of the total weight of the balancing layer prior to curing.
The first moisture content of the balancing layer may exceed 10%, preferably exceeds 20%, more preferably exceeds 30%, of the total weight of the balancing layer prior to curing.
The thermosetting binder may be of the same type in the surface layer and in the balancing layer.
The thermosetting binder of the surface layer and/or the balancing layer may be melamine formaldehyde resin. The thermosetting binder of the surface binder and/or the balancing layer may also be urea melamine formaldehyde or a combination of urea/melamine formaldehyde.
The sheet impregnated with the thermosetting binder may be a paper impregnated with the thermosetting binder, preferably a melamine formaldehyde impregnated paper.
The surface layer may comprises a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper. The surface layer may also comprise an overlay paper, preferably a resin impregnated paper comprising wear resistant particles.
The surface layer may comprise a layer comprising a thermosetting binder and at least one pigment.
According to third aspect of the invention, a method of producing a building panel is provided. The method comprises providing a core,
applying a balancing layer on a first surface of the core, wherein the balancing layer has a first moisture content and comprises a B-stage thermosetting binder, applying a surface layer on a second surface of the core, wherein the surface layer has a second moisture content and comprises a B-stage thermosetting binder, adjusting the first moisture content of the balancing layer such that the first moisture content of the balancing layer is higher than the second moisture content of the surface layer prior to curing, and
curing the thermosetting binder of the surface layer and the balancing layer to C-stage by applying heat and pressure.
Thermosetting binders may be classified as A-, B-, and C-stage according to their extent of reaction compared to the extent of reaction at gelation. In an A-stage thermosetting binder, the extent of reaction is less than the extent of reaction at gelation, i.e. uncured. A B-stage thermosetting binder is close to the gel point, i.e. semi-cured. A C-stage thermosetting binder is well past the gel point, i.e. cured. The A-stage thermosetting binder is soluble and fusible. The B-stage thermosetting resin is still fusible but is barely soluble. The C-stage thermosetting binder is highly crosslinked and both infusible insoluble. (Principles of Polymerization, George Odian, 3rd edition).
The B-stage thermosetting binder applied for the balancing layer may be reacted to the B-stage in a previous step, such as reacted to the B-stage in a dried thermosetting resin impregnated paper, or as a spray-dried thermosetting resin. By a B-stage thermosetting binder is not meant a thermosetting binder in liquid form. In the B-stage, reactivity of the thermosetting binder remains. In the C-stage, the thermosetting binder has no remaining reactivity, or at least almost no reactivity. Thermosetting binders in the B-stage may have a varying degree of crosslinking, from a low degree of crosslinking being close to A-stage, to a high degree of crosslinking being close to C-stage.
The B stage thermosetting binder of the balancing layer may be present in form of, for example, a sheet impregnated with the thermosetting binder such as a paper sheet impregnated with the thermosetting binder, a thermosetting binder applied in powder form.
The balancing layer is adapted to counteract shrinking forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing. The shrinking forces formed by the thermosetting binder of the surface layer during pressing and curing are balanced or counteracted by the shrinking forced formed by the thermosetting binder of the balancing layer during pressing.
By arranging a balancing layer on the core opposite the surface layer, the shrinking forces formed by the thermosetting binder in the surface layer and by the thermosetting binder in the balancing layer are balanced against each other.
An advantage of at least embodiments of the invention is that by adjusting the moisture content of the balancing layer to be higher than the moisture content of the surface layer prior to curing, for example, by applying water on the core and/or on the balancing layer, the balancing layer can balance larger shrinking forces formed by the surface layer during pressing and cooling. By increasing the moisture content of the balancing layer prior to curing, the amount of thermosetting binder of the balancing layer can be reduced. A thinner paper, i.e. a paper having reduced weight per square meter, can also be used. The reduced amount of the thermosetting binder of the balancing layer is compensated by the effects of the higher moisture content of the balancing layer.
Pressing tests show that a suitable moisture content in a balancing layer comprising a thermosetting binder such as melamine formaldehyde may increase the shrinking forces during curing and cooling and that this may be used to reduce the amount of the thermosetting binder in the balancing layer. It is preferred that the moisture content in the thermosetting binder of the balancing layer prior to pressing is higher than the general moisture content of about 6% that is the case when a conventional impregnated paper is used as a balancing layer. The moisture content of the balancing layer should preferably exceed the moisture content of the surface layer. The moisture content of the balancing layer preferably exceeds 10% of the total weight of the balancing layer. In some application it may be an advantage to use even higher moisture contents, for example, exceeding 20%. The moisture content is measured prior to pressing. The moisture content in a conventional backing paper is usually limited by the fact that the papers are stacked on a pallet and too high moisture content causes sticking and single paper sheets cannot be taken from the pallet.
The moisture in the balancing layer contributes to the increased balancing capacity of the balancing layer in several ways. The moisture in the balancing layer facilitates and improves heat transfer from the heated press plates into the balancing layer, thus accelerating and/or increasing cross-linking of the thermosetting resin. The moisture content also influences curing of the thermosetting resin by increasing or facilitating floating of the thermosetting binder, which may result in a higher degree of cross-linking. The moisture content of the balancing layer may also influence the core of the building panel. The moisture content of the balancing layer may make the core, for example, a core of a wood-based material, more formable during pressing. A small convex backward bending of the core may be achieved, counteracting an upward bending of the edges of the surface layer.
The step of adjusting the first moisture content of the balancing layer may comprise applying a water or steam to the first surface of the core prior to applying the balancing layer.
The step of adjusting the first moisture content of the balancing layer may comprise applying a water or steam to the balancing layer.
The first moisture content of the balancing layer may be about 6-30%, preferably 8-20% of the total weight of the balancing layer prior to curing.
The first moisture content of the balancing layer may exceed 10%, preferably exceeds 20%, more preferably exceeds 30%, of the total weight of the balancing layer. The thermosetting binder may be of the same type in the surface layer and in the balancing layer.
The thermosetting binder of the surface layer and/or the balancing layer may be melamine formaldehyde resin. The thermosetting binder of the surface binder and/or the balancing layer may also be urea melamine formaldehyde or a combination of urea/melamine formaldehyde. Any other amino resin is also possible, such as phenol formaldehyde resin.
The balancing layer may comprise a sheet impregnated with the thermosetting binder, preferably a paper sheet impregnated with thermosetting binder.
The step of applying the balancing layer may comprise applying the thermosetting binder in powder form.
The balancing layer may comprise at least 80 wt % of the thermosetting binder, preferably at least 90 wt % of the thermosetting binder.
The amount of the thermosetting binder in the balancing layer may be lower than the amount of the thermosetting binder in the surface layer. The surface layer may comprises a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper. The surface layer may also comprise an overlay paper, preferably a resin impregnated paper comprising wear resistant particles.
The surface layer may comprise a layer comprising a thermosetting binder and at least one pigment.
The present invention will by way of example be described in more detail with reference to the appended schematic drawings, which show embodiments of the present invention.
a-e illustrates a method of producing a building panel according to an embodiment of the present invention.
a-e illustrates a method of producing a building panel according to an embodiment of the present invention.
a-e illustrates a method of producing a building panel according to an embodiment.
a-e illustrates a method of producing a building panel 1 according to an embodiment of the present invention. The building panel 1 may be a floor panel, a wall panel, a ceiling panel, a furniture component, etc.
The method comprises providing a core 2. The core 2 is preferably a wood-based board such as MDF or HDF. The core 2 may also be a particle board, OSB or plywood. The core may also be a Wood Plastic Composite (WPC). The core 2 comprises a first surface 3 and a second surface 4 opposite the first surface 3. The core 2 may be arranged on a conveyor belt 5 conveying the core 2 between the steps described below with reference to
Steam or water is applied, preferably by spraying, on the first surface 3 of the core 2 by a steam or water application device 17 as shown in
In
Alternatively, or as a complement to applying steam or water on the first surface 3 of the core 2, steam or water may be applied on the balancing layer 6 when arranged on the core 2, as shown in
By applying steam or water on the core 2 and/or on the balancing layer 6, moisture is added to the balancing layer 6 and/or a portion of the core 2 adjacent the balancing layer 6 such that the moisture content of the balancing layer is adjusted. Pressing tests show that a suitable moisture content in the balancing layer 6 comprising a thermosetting binder such as melamine formaldehyde may increase the shrinking forces during curing and cooling and that this may be used to reduce the content of the thermosetting binder in the balancing layer 6. It is preferred that the moisture content in the thermosetting binder of the balancing layer 6 prior to pressing is higher than the general moisture content of about 4.5-6% that is the case when conventional impregnated paper is used as a balancing layer. The moisture content of the balancing layer 6 should preferably exceed the moisture content of the surface layer 12. The moisture content of the balancing layer 6 may be 6-30%, preferably 8-20%, of the total weight of the balancing layer 6. In some application it may be an advantage to use even higher moisture contents, for example, exceeding 20%. The moisture content is measured prior to pressing.
In order to further adjust the moisture content of the balancing layer 6 prior to pressing, the balancing layer 6 may be heated by, for example, IR or hot air to dry the balancing layer 6. The thermosetting binder remains essentially in B-stage.
The core 2 with the balancing layer 6 may be handled. For example, the core may be turned such that the balancing layer 6 faces the conveyor belt 5 as shown in
Alternatively, the surface layer 12 may be a wood fibre based powder comprising wood fibres, a thermosetting resin and wear resistant particles. It is also contemplated that the surface layer 12 may be of any other type, for example, a veneer layer, or a combination of a décor paper and a wood fibre based surface. The surface layer 12 may also be a layer of a thermosetting binder such as melamine formaldehyde or urea formaldehyde. The layer may consist essentially of the thermosetting binder but may also comprise decorative elements such as pigments and wear resistant particles such as aluminium oxide. The surface layer 12 comprises in this embodiment no paper.
In a preferred embodiment, the binder of the balancing layer 6 and the binder of the surface layer 12 is of the same type. Preferably, melamine formaldehyde resin is used both in the surface layer 12 and in the balancing layer 6.
A semi-finished product as shown in
The moisture content of the balancing layer 6 prior to curing may be about 6-30%, preferably 8-20%, of the total weight of the balancing layer prior to curing. The balancing layer 6 and the surface layer 12 is thereafter cured by applying heat and pressure in a press. The thermosetting binder of the balancing layer 6 and the surface layer 12 is cured to its C stage. By curing and pressing the surface layer 12 and the balancing layer 6 to the core 2, the surface layer 12 and the balancing layer 6 are adhered to the core 2. Thereby, a building panel 1 comprising the core 2, the surface layer 12 and the balancing layer 6 is obtained, which is shown in
After pressing, the balancing layer 6 balances the tension created by the surface layer 12 during curing such that the building panel 1 remains essentially flat after pressing and cooling (“pressing balancing” and “cooling balancing”). By essentially flat is meant a cupping less than 2 mm/m. A small convex backward bending being less than 2 mm/m is preferred. The thermosetting binder of the balancing layer 6 balances forces created by the thermosetting binder of the surface layer 12. By applying water on the core 2 and/or on the balancing layer 6, the balancing layer 6 may balance larger shrinking forces formed by the surface layer 12 during pressing and cooling. Thereby, the amount of the thermosetting binder of the balancing layer 6 can be reduced. As an example, the amount of the thermosetting binder in the balancing layer 6 may about 75% of the amount of the thermosetting binder in the surface layer
a-e illustrates a method of producing a building panel 1 according to an embodiment of the present invention. The building panel 1 may be a floor panel, a wall panel, a ceiling panel, a furniture component, etc.
The method comprises providing a core 2. The core 2 is preferably a wood-based board such as MDF or HDF. The core 2 may also be a particle board, OSB or plywood. The core may also be a Wood Plastic Composite (WPC). The core 2 comprises a first surface 3 and a second surface 4 opposite the first surface 3. The core 2 may be arranged on a conveyor belt 5 conveying the core 2 between the steps described below with reference to
Steam or water is applied, preferably by spraying, on the first surface 3 of the core 2 by a steam or water application device 17 as shown in
In
In
The thermosetting powder 7 is preferably scattered on the first surface 3 of the core 2 by a scattering unit 8. The thermosetting binder in powder form is applied on the first surface 3 of the core 2 such as a layer forming a balancing layer 6 is formed. The scattered layer comprises preferably 50-150 g/m2, such as 50-100 g/m2, of spray dried thermosetting binder such as spray dried melamine formaldehyde particles. The scattered layer preferably corresponds to a thickness of about 0.1-0.5 mm of powder or about 0.1-0.2 mm of a pressed and cured thermosetting binder layer such as a melamine formaldehyde layer.
Since water or steam has been applied to the first side 3 of the core 2 prior to applying the thermosetting binder, the thermosetting binder gets tacky and sticks together such that a layer of the thermosetting binder is formed and such that the layer of the thermosetting binder adheres to the core. Thereby, it is possible to handle the core without the thermosetting binder falling off the core.
Alternatively, or as a complement to applying steam or water on the first surface 3 of the core 2, steam or water may be applied on the balancing layer 6 when arranged on the core 2, as shown in
By applying steam or water on the core 2 and/or on the balancing layer 6, moisture is added to the balancing layer 6 and/or a portion of the core 2 adjacent the balancing layer 6 such that the moisture content of the balancing layer is adjusted. Pressing tests show that a suitable moisture content in the balancing layer 6 comprising a thermosetting binder such as melamine formaldehyde may increase the shrinking forces during curing and cooling and that this may be used to reduce the content of the thermosetting binder in the balancing layer 6. It is preferred that the moisture content in the thermosetting binder of the balancing layer 6 prior to pressing is higher than the general moisture content of about 4.5-6% that is the case when conventional impregnated paper is used as a balancing layer. The moisture content of the balancing layer 6 should preferably exceed the moisture content of the surface layer 12. The moisture content of the balancing layer 6 may be 6-30%, more preferably 8-20%, of the total weight of the balancing layer 6. In some application it may be an advantage to use even higher moisture contents, for example, exceeding 20%. The moisture content is measured prior to pressing. In order to further adjust the moisture content of the balancing layer 6 prior to pressing, the balancing layer 6 may be heated by, for example, IR or hot air to dry the balancing layer 6. The balancing layer 6 remains essentially in B-stage, or at least not completely in C-stage.
The core 2 with the balancing layer 6 may be handled, for example, turned such that the balancing layer 6 faces the conveyor belt 5 as shown in
When the semi-finished product has been turned, a surface layer 12 is applied to the second surface 4 of the core 2 as shown in
Alternatively, the surface layer 12 may be a wood fibre based powder comprising wood fibres, a thermosetting resin and wear resistant particles. It is also contemplated that the surface layer 12 may be of any other type, for example, a veneer layer, or a combination of a décor paper and a wood fibre based surface.
The surface layer 12 may also be a layer of a thermosetting binder such as melamine formaldehyde or urea formaldehyde. The layer may consist essentially of the thermosetting binder. A layer consisting essentially of the thermosetting binder may also include decorative elements, such as pigments, and wear resistant particles, such as aluminium oxide. The surface layer 12 comprises, in this embodiment, no paper.
In a preferred embodiment, the binder of the balancing layer 6 and the binder of the surface layer 12 is of the same type. Preferably, melamine formaldehyde resin is used both in the surface layer 12 and in the balancing layer 6.
A semi-finished product as shown in
The moisture content of the balancing layer 6 prior to curing preferably may be 6-30%, more preferably 8-20%, of the total weight of the balancing layer 6.
The balancing layer 6 and the surface layer 12 is thereafter cured by applying heat and pressure in a press. The thermosetting binder of the balancing layer 6 and the surface layer 12 is cured to its C stage. By curing and pressing the surface layer 12 and the balancing layer 6 to the core 2, the surface layer 12 and the balancing layer 6 are adhered to the core 2. Thereby, a building panel 1 comprising the core 2, the surface layer 12 and the balancing layer 6 is obtained, which is shown in
After pressing, the balancing layer 6 balances the tension created by the surface layer 12 during curing such that the building panel 1 remains essentially flat after pressing and cooling (“pressing balancing” and “cooling balancing”). By essentially flat is meant a cupping less than 2 mm/m. A small convex backward bending being less than 2 mm/m is preferred. The thermosetting binder of the balancing layer 6 balances forces created by the thermosetting binder of the surface layer 12. By applying water on the core 2 and/or on the balancing layer 6, the balancing layer 6 may balance larger shrinking forces formed by the surface layer 12 during pressing and cooling. Thereby, the amount of the thermosetting binder of the balancing layer 6 can be reduced.
The balancing layer 6 described above with reference to
It is also contemplated that the water or steam may be applied to the balancing layer 6 just before pressing. The semi-finished product comprising the core 2 and the balancing layer 6 as described above with reference to
The building panel 1 as described above may be a floor panel, a wall panel, a ceiling panel, a furniture component, etc. In the embodiment wherein the building panel is a floor panel, the floor panel 1′ may be provided with a mechanical locking system as shown in
Another embodiment of a method of producing a building panel 1 will now be described with reference to
a illustrates that a thermosetting binder is applied on the first surface 3 of the core 3 for forming a balancing layer 6. The thermosetting binder is applied as a liquid. The thermosetting binder is dissolved in a solvent, preferably a water based solvent, thus forming a liquid. The thermosetting binder is preferably melamine formaldehyde resin. Additives such as wetting and release agents, catalyst may be added to the solvent.
A layer of the liquid thermosetting binder 7′ is applied to the first surface 3 of the core 2 for forming the balancing layer 6. Thereafter, the layer of the thermosetting binder is preferably dried as shown in
Preferably, several layers of the thermosetting binder are applied to the first surface 3 of the core 2 for forming the balancing layer 6. Preferably, a drying step is provided between application of each layer.
The layer or layers of the thermosetting binder is adapted to form a balancing layer 6 of the building panel 1.
Drying of the layer or layers of the thermosetting binder is performed at a temperature wherein the thermosetting binder remains essentially in B-stage. The object of the heating step is to obtain a layer which is touch dry such that the core with the thermosetting layer can be handled.
The core 2 having the thermosetting binder arranged thereon for forming the balancing layer 6 forms a semi-finished product, which is shown in
The semi-finished product may be handled as a separate product due to the balancing layer being dried and adhered to the core 2. For example, the semi-finished may be stacked on a pallet for intermediate storage, or may be stored and transported to another plant. Thereby, the core 2 having the layer of thermosetting binder for forming the balancing layer 6 attached thereto may be produced in a different process than the subsequent application of the surface layer 12, and at a different location.
The semi-finished product may also be turned 180° such that the balancing layer 6 of the thermosetting binder is directed downwards, for example, towards the conveyor belt 5 as shown in
When the semi-finished product has been turned, a surface layer 12 may be applied on the second surface 4 of the core 2 as shown in
In a preferred embodiment, the binder of the balancing layer 6 and the binder of the surface layer 12 is of the same type. Preferably, melamine formaldehyde resin is used both in the surface layer 12 and in the balancing layer 6.
Alternatively, the surface layer 12 may be a wood fibre based powder comprising wood fibres, a thermosetting binder, preferably melamine formaldehyde resin, and wear resistant particles, such as aluminium oxide. It is also contemplated that the surface layer may be of any other type, for example, a veneer layer, or a combination of a décor paper and a wood fibre based surface or a combination of a veneer layer and a wood fiber based surface.
The thermosetting binder of the layer for forming the balancing layer 6 and of the surface layer 12 is thereafter cured by applying heat and pressure in a press. Thereby, the balancing layer 6 is formed. By curing and pressing the surface layer 12 and the balancing layer 6 to the core 2, the surface layer 12 and the balancing layer 6 are adhered to the core 2. Thereby, a building panel 1 having the core 2, the surface layer 12 and the balancing layer 6 is formed, which is shown in
After pressing, the balancing layer 6 balances the tension created by the surface layer 12 such that the building panel 1 remains essentially flat after pressing and cooling (“pressing balancing” and “cooling balancing”). By essentially flat is meant a cupping less than 2 mm/m. A small convex backward bending being less than 2 mm/m is preferred. The thermosetting binder of the balancing layer 6 balances forces created by the thermosetting binder of the surface layer 12. By using the same type of binder in the balancing layer 6 as in the surface layer 12, the forces created by the binder in the surface layer 12 are matched and counteracted by the forces created by the binder in the balancing layer 6 on the opposite surface of the core.
In addition to the thermosetting binder, the balancing layer 6 may comprise various additives. The balancing layer 6 is in this embodiment paper free, i.e. comprises no paper. In a preferred embodiment, the balancing layer 6 comprises only the thermosetting binder and optional additives. The balancing layer may consist of, or essentially consist of, the thermosetting binder. It is also contemplated that filler particles may be applied to the balancing layer 6, preferably in an amount lower than 50% by weight of the balancing layer 6, more preferably in an amount lower than 20% by weight of the balancing layer 6. Filler particles may include wood fibres, sand, mineral particles, aluminium oxide, etc. The filler particles may be scattered onto the layer of the thermosetting binder such that the balancing layer comprises the thermosetting binder and filler particles. Alternatively, the filler particles may be mixed with the thermosetting binder in liquid form. If a large amount of thermosetting binder is required to balance the surface layer 12, filler particles may be included in the balancing layer 6 to obtain necessary tension of the balancing layer 6.
The methods result in a building panel 1 comprising a core 2, a surface layer 12 and a balancing layer 6 as shown in
In alternative embodiments, the surface layer 12 may be a wood fibre based powder comprising wood fibres, a thermosetting resin and wear resistant particles. The surface layer 12 may also be a layer of a thermosetting binder such as melamine formaldehyde or urea formaldehyde. The surface layer 12 may consist essentially of the thermosetting binder but may also comprise decorative elements such as pigments and wear resistant particles such as aluminium oxide. The surface layer 12 comprises in this embodiment no paper. It is contemplated that there are numerous modifications of the embodiments described herein, which are still within the scope of the invention as defined by the appended claims.
The balancing layer is referred to as a layer. However, during pressing, the thermosetting binder may in some embodiments at least partly impregnate the core such that the layer becomes less distinct. Thereby, the balancing layer may be at least partly integrated into the core. After pressing, the balancing layer may at least partly form part of the core.
It is also contemplated that pre-pressing of the balancing layer may be performed prior to curing the balancing layer and the surface layer. During pre-pressing step, the balancing layer remains in B-stage, or is at least not completely in C-stage. Cooling of the balancing layer may be performed after the pre-pressing step.
Furthermore, it is also contemplated that an overlay paper such as a resin impregnated overlay paper may be included in the surface layer and that the balancing layer balances both the décor layer and the overlay paper.
Embodiments may also be defined as:
A method of producing a building comprises providing a core, applying a thermosetting binder on a first surface of the core for forming a balancing layer, wherein the balancing layer comprises at least 80% by weight of a thermosetting binder, preferably at least 90% by weight of a thermosetting binder, applying a surface layer on a second surface of the core, wherein the surface layer comprises a thermosetting binder, and curing the surface layer and the balancing layer by applying heat and pressure.
The balancing layer is adapted to counteract shrinking forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing and cooling.
The amount of the thermosetting binder applied on the first surface is chosen such that the balancing layer balances shrinking forces formed by the surface layer during pressing and cooling.
Also the chemical composition of the balancing layer, including, for example, additives applied to the thermosetting binder, affects properties such as tension of the balancing layer.
An advantage of the method is that the balancing layer that consists essentially of a thermosetting resin, counteracts and balances the tension created by the surface layer during pressing (“pressing balancing”). The balancing layer keeps the building panel essentially flat after pressing. Thereafter, the balancing layer counteracts and balances temperature shrinking of the surface layer when the panel is cooled from the present temperature to room temperature (“cooling balancing”) such that the building panel remains essentially flat. Finally, the balancing layer counteracts and balances cupping of the edges of the floor panel due to shrinkage and expansion caused by changes in temperature and humidity of the indoor climate (“climate balancing”).
By applying essentially only a thermosetting binder as a balancing layer, the cost for the balancing layer is reduced, for example, compared to using an impregnated paper as a balancing layer. Furthermore, the overall production of the building panel is simplified by removing the step of impregnating a paper for forming a balancing paper layer. The production process is simplified by applying the thermosetting binder directly on the core for forming a balancing layer.
The tension of the balancing layer counteracting shrinking forces formed by the surface layer during pressing and cooling may be varied by the amount of thermosetting resin applied, additives applied, for example, additives changing the reactivity of the thermosetting binder, water applied, and the type of thermosetting binder. For example, a lower amount of thermosetting binder may be compensated by adding an additive, applying water, or choosing a thermosetting binder creating larger tension forces such as melamine formaldehyde resin.
The balancing layer is referred to as a layer. However, during pressing, the thermosetting binder may at least partly impregnate the core such that the layer becomes less distinct. Thereby, the balancing layer may be at least partly integrated into the core. After pressing, the balancing layer may at least partly form part of the core.
The balancing layer may consist essentially of a thermosetting binder. Additives such as, for example, wetting agents, release agents, catalysts, etc., may be included in the balancing layer that consists essentially of the thermosetting binder. Catalyst may influence how large tension forces that may be formed by the balancing layer adapted to counteract shrinking forces of the surface layer.
The pressing temperature may exceed 140° C., for example, 140-210° C.
The amount of the thermosetting binder in the balancing layer may exceed 50 g/m2. The amount of the thermosetting binder in the balancing layer 6 may about 75% of the amount of the thermosetting binder in the surface layer.
The thermosetting binder is preferably an amino resin such as urea formaldehyde or melamine formaldehyde.
The thermosetting binder may include pigments. The thermosetting binder may include wear resistant particles such as aluminium oxide.
In one embodiment, the balancing layer consists of, or consists essentially of the thermosetting binder. In this embodiment, the balancing layer comprises no paper and no wood fibres. However, a balancing layer consisting essentially of the thermosetting binder may include additives.
The thermosetting binder may be of the same type in the surface layer and in the balancing layer. By the expression same type is meant binder belong to the same group of resin, such as melamine formaldehyde, urea formaldehyde, etc. By using the same type of binder in both the surface layer and the balancing layer, the balancing layer matches the behavior of the surface layer The balancing layer balances shrinkage and/or expansion of the balancing layer by counteracting the movements of the surface layer in a similar way when using the same type of thermosetting binder.
The thermosetting binder of the surface layer may be melamine formaldehyde resin. Direct Pressure Laminate (DPL) and High Pressure Laminate (HPL) are conventionally impregnated with melamine formaldehyde resin.
The thermosetting binder of the surface layer and/or the balancing layer may also be urea melamine formaldehyde or a combination of urea/melamine formaldehyde.
The thermosetting binder of the balancing layer may be melamine formaldehyde resin. A balancing layer comprising melamine formaldehyde resin creates greater tension compared to, for example, urea formaldehyde. Therefore, a balancing layer comprising melamine formaldehyde can counteract/balance greater tension formed by the surface layer.
The surface layer may be arranged directly on the core. The balancing layer can balance a surface layer arranged directly on the core. The surface layer may comprise a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper. The décor paper may be arranged directly on the core. It has been shown that the balancing layer consisting essentially of a thermosetting binder can be used to balance a surface layer of décor paper. Thus, a balancing layer consisting essentially of a thermosetting binder can be used to balance a DPL.
The surface layer may comprise a layer of a thermosetting binder, preferably melamine formaldehyde resin, and at least one pigment. The surface may in this embodiment consist essentially of the thermosetting binder with optional additives, such as pigments, wear resistant particles, etc.
The amount of the thermosetting binder in the balancing layer may essentially correspond to the amount of the thermosetting binder in the surface layer. Thereby, balancing of the surface layer is further improved.
The amount of the thermosetting binder in the balancing layer may be lower than the amount of the thermosetting binder in the surface layer. The amount of the thermosetting binder in the balancing layer may, for example, be about 80% of the amount of the thermosetting binder in the surface layer.
Thermosetting binder of the balancing layer may be applied in liquid form. Thereby, the balancing layer may be applied as a coating to the core. The balancing layer may be applied as one or several layers of the thermosetting binder. By using a liquid thermosetting binder, no extra off-line drying of the binder is necessary, for example, spray drying or drying of an impregnated paper.
The method may further comprise drying the thermosetting binder. Preferably, the balancing layer remains essentially in B-stage. The balancing layer may be applied as several layers of a thermosetting binder, wherein each layer preferably is dried before application of a subsequent layer.
The step of applying the thermosetting binder forming the balancing layer may comprise applying, preferably by scattering, the thermosetting binder in powder form. The thermosetting binder may be a dry powder. By applying the thermosetting binder in powder form, the balancing layer may be applied in a single step, preferably as a single layer. The thermosetting binder may be spray dried.
The method may further comprise applying water or steam, on the first surface of the core prior to applying to the thermosetting binder. Alternatively, the method may further comprise applying preferably water, or steam, on the thermosetting binder. The aqueous solution or steam is used to stabilize the balancing layer such that the core with the balancing layer can be handled in the production line, for example, be turned around. The aqueous solution or steam makes the thermosetting binder tacky and thereby the thermosetting binder in powder form sticks together. The aqueous solution may comprise release and wetting agents and catalysts. The aqueous solution may include pigments. The thermosetting binder remains essentially in B-stage.
The moisture content of the balancing layer may be higher than the moisture content of the surface layer as measured prior to pressing. The moisture content may be 3-30%, such as 8-20%, of the total weight of the balancing layer. The moisture content of the balancing layer may exceed 10%, preferably 20%, more preferably 30%, of the total weight of the balancing layer. Water or steam may be applied to the thermosetting binder or to the first surface of the core prior to applying the thermosetting binder in order to adjust the moisture content of the balancing layer to be formed.
Pressing test show that a suitable moisture content in a balancing layer comprising a thermosetting binder such as melamine formaldehyde may increase the shrinking forces during curing and cooling and that this may be used to reduce the content of the thermosetting binder in the balancing layer. It is preferred that the moisture content in the thermosetting binder of the balancing layer prior to pressing is higher than the general moisture content of about 6% that is the case when conventional impregnated paper is used as a balancing layer. The moisture content in liquid or spray dried thermosetting binder such as melamine should preferably exceed the moisture content of the surface layer. The moisture content should preferably exceed 10% of the total weight of the balancing layer. In some application it may be an advantage to use even higher moisture contents, for example, exceeding 20%.
According to another embodiment, a building panel is provided. The building panel comprises a core having a first and second surface, a balancing layer arranged on the first surface of the core, wherein the balancing layer comprises at least 80% by weight of a thermosetting binder, preferably at least 90% by weight of a thermosetting binder, a surface layer arranged on the second surface of the core, wherein the surface layer comprises a thermosetting binder.
The balancing layer is adapted to counteract shrinking forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing.
The balancing layer is referred to as a layer. However, during pressing, the thermosetting binder may at least partly impregnate the core such that the layer becomes less distinct. Thereby, the balancing layer may be at least partly integrated into the core. After pressing, the balancing layer may at least partly form part of the core.
The thermosetting binder may be of the same type in the surface layer and in the balancing layer.
The thermosetting binder of the surface layer may be melamine formaldehyde resin.
The thermosetting binder of the balancing layer may be melamine formaldehyde resin.
The surface layer may be arranged directly on the core.
The surface layer may comprise a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper.
The amount of the thermosetting binder in the balancing layer may essentially correspond to the amount of the thermosetting binder in the surface layer. The amount of the thermosetting binder in the balancing layer may be lower than to the amount of the thermosetting binder in the surface layer. The amount of the thermosetting binder in the balancing layer may, for example, be about 80% of the amount of the thermosetting binder in the surface layer.
The moisture content of the balancing layer may be higher than the moisture content of the surface layer as measured prior to pressing. The moisture content may be 6-30%, such as 8-20%, of the total weight of the balancing layer prior to curing.
The moisture content of the balancing layer may exceed 10%, preferably 20%, more preferably 30%, of the total weight of the balancing layer prior to curing.
The surface layer may comprise a layer of a thermosetting binder and at least one pigment. The surface layer may in one embodiment consist of, or consist essentially of a thermosetting binder and optional additives.
According to another embodiment, a semi-finished product is provided. The semi-finished product comprises a core having a first surface, and a balancing layer arranged on the first surface of the core, the balancing layer comprising at least 80% by weight of a thermosetting binder, preferably at least 90% of a thermosetting binder.
The semi-finished product is already provided with a balancing layer. A surface layer can in a separate process be applied to the semi-finished product to form a building panel. The semi-finished product may, for example, be stored and transported.
The thermosetting binder may be essentially B-stage. For example, the balancing layer may only be dried without curing, or if the thermosetting binder is in powder form, liquid or steam may be applied in order to get the binder tacky and stick the powder together and attach to the core.
The thermosetting binder may be melamine formaldehyde resin.
According to another embodiment, a method of producing a building panel is provided. The method comprises: providing a core, applying a thermosetting binder in a liquid form on a first surface of the core for forming a balancing layer, applying a surface layer on a second surface of the core, wherein the surface layer comprises a thermosetting binder, and curing the surface layer and the balancing layer by applying heat and pressure.
The balancing layer is adapted to counteract shrinking forces formed by the surface layer during pressing and cooling such that the building panel remains essentially flat in room temperature after pressing.
Furthermore, by applying the thermosetting binder as a liquid, no extra off-line drying of the binder is necessary, for example, spray drying or drying of an impregnated paper.
The balancing layer is referred to as a layer. However, during pressing, the thermosetting binder may at least partly impregnate the core such that the layer becomes less distinct. Thereby, the balancing layer may be at least partly integrated into the core. After pressing, the balancing layer may at least partly form part of the core.
The balancing layer may be paper free.
The method may further comprise drying the thermosetting binder prior to applying heat and pressure.
The method may further comprise applying filler particles on the thermosetting binder. The filler particles may be wood fibres, sand, mineral particles, aluminium oxide, etc. Alternatively, the filler particles may be mixed with the thermosetting binder.
The balancing layer may comprise at least 80% by weight of the thermosetting binder, preferably at least 90% by weight of the thermosetting binder.
The building panel may be pressed at a temperature of at least 120° C.
The thermosetting binder may be present with the balancing layer with an amount of at least 50 g/m2.
The thermosetting binder may be of the same type in the surface layer and in the balancing layer.
The thermosetting binder of the surface layer and/or the balancing layer is melamine formaldehyde resin. The thermosetting binder of the surface binder and/or the balancing layer may also be urea melamine formaldehyde or a combination of urea/melamine formaldehyde.
The surface layer may be arranged directly on the core.
The surface layer may comprise a décor paper, preferably a resin impregnated décor paper, more preferably a melamine formaldehyde impregnated décor paper.
The surface layer may comprise a layer of a thermosetting binder and at least one pigment.
The amount of the thermosetting binder in the balancing layer may essentially correspond to the amount of the thermosetting binder in the surface layer.
The amount of the thermosetting binder in the balancing layer may be lower than the amount of the thermosetting binder in the surface layer.
The moisture content of the balancing layer may be higher than the moisture content of the surface layer.
The moisture content may be 6-30%, such as 8-20%, of the total weight of the balancing layer prior to curing.
The moisture content of the balancing layer may exceed 10%, preferably 20%, more preferably 30%, of the total weight of the balancing layer prior to curing.
A water solution was sprayed on one surface of a standard HDF board, Sonae 9.7 mm. Then 100 g/m2 melamine formaldehyde powder resin—773 from BASF—was applied with a scattering device on the wet HDF board.
The HDF board was then turned upside down and a surface layer containing 100 g/m2 melamine formaldehyde resin was applied on the other side of the board.
The HDF board containing a clean dry melamine formaldehyde resin on one side for forming a balancing layer and on the other side a surface layer containing 100 g/m2 melamine, then was put into a press where heat and pressure was applied.
Pressing conditions:
Temperature: 160° C. on the upper and under heating plates.
Pressing time: 20 sec
Pressure: 40 bar
During the pressing operation the melamine formaldehyde resins cured and a laminate board was obtained.
In order to investigate the cupping behavior of this product we placed the above flooring laminate into different climates. After 3 days in 50% RH climate the cupping was +0.83 mm (convex cupping). After 2 days in 25% RH climate the cupping was −0.07 mm (slightly concave).
300 g/m2 wet melamine formaldehyde resin with a solid content of 50% was applied with a roller device one surface of a standard HDF board, Sonae 9.7 mm, and then dried in an oven so the surface was dry which gives the possibility to turn the HDF board upside down. A surface layer containing 300 g/m2 melamine formaldehyde resin was applied on the other side of the board.
The HDF board containing a wet melamine resin on one side for forming a balancing layer and on the other side a surface layer containing 300 g/m2 melamine resin was then put into a press where heat and pressure was applied.
Pressing conditions:
Temperature: 170° C. on the upper and under heating plates.
Pressing time: 30 sec
Pressure: 40 bar
During the pressing operation the melamine formaldehyde resins cured and a laminate board was obtained.
In order to investigate the cupping behavior of this product we placed the above flooring laminate into different climates. After 3 days in 50% RH climate the cupping was −0.7 mm (concave cupping). After 16 days in 25% RH climate the cupping was −0.47 mm (concave cupping).
In order to investigate the influence of water, water was added to a top surface layer. A top surface layer containing 100 g/m2 melamine formaldehyde resin was applied on a surface of a standard HDF board, Sonae 9.7 mm. On top of this a layer 15 g/m2 of water was applied with a spraying device. On the opposite surface of the board a surface layer containing 100 g/m2 melamine was applied.
The board was then put into a press where heat and pressure was applied.
Pressing conditions:
Temperature: 170° C. on the upper and under heating plates.
Pressing time: 30 sec
Pressure: 40 bar
During the pressing operation the melamine formaldehyde resins cured and a laminate board was obtained.
In order to investigate the cupping behavior of this product we placed the above board into different climates. After 3 days in 50% RH climate the cupping was −1.33 mm (concave cupping). After 3 days in 25% RH Climate the cupping was −2.11 mm (concave cupping).
The above trial was repeated with higher water amounts added on a top surface of a HDF board, in increased steps:
30 g/m2 of water applied was applied on the HDF board giving the following cupping:
After 3 days in 50% RH climate the cupping was −1.64 mm (concave cupping). After 3 days in 25% RH Climate the cupping was −2.51 mm (concave cupping).
45 g/m2 of water applied giving the following cupping:
After 3 days in 50% RH climate the cupping was −3.17 mm (concave cupping). After 3 days in 25% RH Climate the cupping was −4.30 mm (concave cupping). 60 g/m2 giving the following cupping:
After 3 days in 50% RH climate the cupping was −3.24 mm (concave cupping). After 3 days in 25% RH Climate the cupping was −4.55 mm (concave cupping).
As can be seen in the above examples, the more water added, the more concave cupping is created on the side where water is added, i.e. in this example on the top surface.
Five different examples were tested. The examples had the following build-up:
The water applied also contained about 1 wt % of a catalyst, about 3-6 wt % of a release agent, and about 2.5 wt % of a wetting agent.
The different layers had the following composition:
The core was a 7.6 mm HDF board.
The examples were pressed with the following press conditions:
Temperature: Oil temperature on upper heating plate 190° C. and 208° C. on the lower heating plate.
Pressing time: 12 sec
Pressure: 35 bar
After pressing, the impact of the water applied can be studied by comparing the shape of the panels. The counteracting forces formed by the melamine formaldehyde resin of the balancing layer, adapted to counteract and balance the tension formed by the melamine formaldehyde resin of the oppositely arranged overlay and décor layers during curing, increased in the following order:
Example D was more convex in shape than example C, which was equal to example B. Example B was more convex in shape than example A. Consequently, the higher amount of water applied, the larger counteracting forces were formed, thus resulting in a more convex shape of the panel after pressing and curing. Example E was equal to example A in its convex shape.
Example E shows that by spraying the balancing layer and the surface on the core on which the balancing layer is arranged with water, an overlay paper can replace a standard backing paper resulting in an equal convex shape. In example 5, the amount of melamine formaldehyde resin has been reduced from 112 g/m2 to 67 g/m2, corresponding to a reduction of 40%, by replacing the standard backing paper with an overlay paper. The paper weight has been reduced from 61 g/m2 to approximately 22 g/m2. However, the resulting counteracting forces essentially equal a standard backing paper.
1. A method of producing a building panel (1), comprising:
providing a core (2),
applying a balancing layer (6) on a first surface (3) of the core (2), wherein the balancing layer (6) has a first moisture content and comprises a B-stage thermosetting binder,
applying a surface layer (12) on a second surface (4) of the core (2), wherein the surface layer (12) has a second moisture content and comprises a B-stage thermosetting binder,
adjusting the first moisture content of the balancing layer (6) such that the first moisture content of the balancing layer (6) is higher than the second moisture content of the surface layer (12) prior to curing by applying heat and pressure, and curing the thermosetting binder of the surface layer (12) and the balancing layer (6) to C-stage by applying heat and pressure.
2. A method according to embodiment 1, wherein the step of adjusting the first moisture content of the balancing layer comprises applying water or steam to the first surface (3) of the core (2) prior to applying the balancing layer (6).
3. A method according to embodiment 1 or 2, wherein the step of adjusting the first moisture content of the balancing layer comprises applying water or steam to the balancing layer (6).
4. A method according to any one of embodiment 1-3, wherein the first moisture content of the balancing layer (6) is 6-30%, preferably 8-20%, of the total weight of the balancing layer (6) prior to curing by applying heat and pressure.
5. A method according to any one of embodiment 1-4, wherein the balancing layer (6) comprises a resin impregnated sheet, preferably a resin impregnated paper.
6. A method according to any one of embodiment 1-4, wherein the step of applying the balancing layer (6) comprises applying the thermosetting binder in powder form.
7. A method according to any one of embodiment 1-6, wherein the amount of the thermosetting binder in the balancing layer (6) is lower than the amount of the thermosetting binder in the surface layer (12).
The present application claims the benefit of U.S. Provisional Application No. 61/751,393, filed on Jan. 11, 2013. The entire contents of U.S. Provisional Application No. 61/751,393 are hereby incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2587064 | Rapson | Feb 1952 | A |
| 2831793 | Elmendorf | Apr 1958 | A |
| 2962081 | Dobry et al. | Nov 1960 | A |
| 3032820 | Johnson | May 1962 | A |
| 3135643 | Michl | Jun 1964 | A |
| 3286006 | Annand | Nov 1966 | A |
| 3308013 | Bryant | Mar 1967 | A |
| 3325302 | Hosfeld | Jun 1967 | A |
| 3342621 | Point et al. | Sep 1967 | A |
| 3345234 | Jecker et al. | Oct 1967 | A |
| 3426730 | Lawson et al. | Feb 1969 | A |
| 3463653 | Letter | Aug 1969 | A |
| 3486484 | Bullough | Dec 1969 | A |
| 3533725 | Bridgeford | Oct 1970 | A |
| 3540978 | Ames | Nov 1970 | A |
| 3565665 | Stranch et al. | Feb 1971 | A |
| 3673020 | De Jaeger | Jun 1972 | A |
| 3846219 | Kunz | Nov 1974 | A |
| 3880687 | Elmendorf et al. | Apr 1975 | A |
| 3897185 | Beyer | Jul 1975 | A |
| 3897588 | Nohtomi | Jul 1975 | A |
| 3914359 | Bevan | Oct 1975 | A |
| 3961108 | Rosner et al. | Jun 1976 | A |
| 4052739 | Wada et al. | Oct 1977 | A |
| 4093766 | Scher et al. | Jun 1978 | A |
| 4131705 | Kubinsky | Dec 1978 | A |
| 4313857 | Blount | Feb 1982 | A |
| 4337290 | Kelly et al. | Jun 1982 | A |
| 4420525 | Parks | Dec 1983 | A |
| 4430375 | Scher et al. | Feb 1984 | A |
| 4474920 | Kyminas et al. | Oct 1984 | A |
| 4890656 | Ohsumi et al. | Jan 1990 | A |
| 5034272 | Lindgren et al. | Jul 1991 | A |
| 5040582 | Hsu | Aug 1991 | A |
| 5206066 | Horacek | Apr 1993 | A |
| 5246765 | Lussi et al. | Sep 1993 | A |
| 5258216 | Von Bonin et al. | Nov 1993 | A |
| 5314554 | Owens | May 1994 | A |
| 5422170 | Iwata et al. | Jun 1995 | A |
| 5466511 | O'Dell et al. | Nov 1995 | A |
| 5543193 | Tesch | Aug 1996 | A |
| 5569424 | Amour | Oct 1996 | A |
| 5601930 | Mehta et al. | Feb 1997 | A |
| 5604025 | Tesch | Feb 1997 | A |
| 5609966 | Perrin et al. | Mar 1997 | A |
| 5766522 | Daly et al. | Jun 1998 | A |
| 5827788 | Miyakoshi | Oct 1998 | A |
| 5855832 | Clausi | Jan 1999 | A |
| 5891564 | Shultz et al. | Apr 1999 | A |
| 5925296 | Leese | Jul 1999 | A |
| 5942072 | McKinnon | Aug 1999 | A |
| 6036137 | Myren | Mar 2000 | A |
| 6103377 | Clausi | Aug 2000 | A |
| 6238750 | Correll et al. | May 2001 | B1 |
| 6468645 | Clausi | Oct 2002 | B1 |
| 6521326 | Fischer et al. | Feb 2003 | B1 |
| 6537610 | Springer et al. | Mar 2003 | B1 |
| 6620349 | Lopez | Sep 2003 | B1 |
| 6769217 | Nelson | Aug 2004 | B2 |
| 6773799 | Persson et al. | Aug 2004 | B1 |
| 6803110 | Drees et al. | Oct 2004 | B2 |
| 6926954 | Shuren et al. | Aug 2005 | B2 |
| 6991830 | Hansson et al. | Jan 2006 | B1 |
| 7022756 | Singer | Apr 2006 | B2 |
| 7485693 | Matsuda et al. | Feb 2009 | B2 |
| 7811489 | Pervan | Oct 2010 | B2 |
| 8349234 | Ziegler et al. | Jan 2013 | B2 |
| 8349235 | Pervan et al. | Jan 2013 | B2 |
| 8419877 | Pervan et al. | Apr 2013 | B2 |
| 8431054 | Pervan et al. | Apr 2013 | B2 |
| 8480841 | Pervan et al. | Jul 2013 | B2 |
| 8481111 | Ziegler et al. | Jul 2013 | B2 |
| 8617439 | Pervan et al. | Dec 2013 | B2 |
| 8663785 | Ziegler et al. | Mar 2014 | B2 |
| 8728564 | Ziegler et al. | May 2014 | B2 |
| 8784587 | Lindgren et al. | Jul 2014 | B2 |
| 8920874 | Ziegler et al. | Dec 2014 | B2 |
| 8920876 | Vetter et al. | Dec 2014 | B2 |
| 20010006704 | Chen et al. | Jul 2001 | A1 |
| 20010009309 | Taguchi et al. | Jul 2001 | A1 |
| 20020054994 | Dupre et al. | May 2002 | A1 |
| 20020100231 | Miller | Aug 2002 | A1 |
| 20030056873 | Nakos et al. | Mar 2003 | A1 |
| 20030059639 | Worsley | Mar 2003 | A1 |
| 20030102094 | Tirri et al. | Jun 2003 | A1 |
| 20030208980 | Miller et al. | Nov 2003 | A1 |
| 20040123542 | Grafenauer | Jul 2004 | A1 |
| 20040191547 | Oldorff | Sep 2004 | A1 |
| 20040202857 | Singer | Oct 2004 | A1 |
| 20040206036 | Pervan | Oct 2004 | A1 |
| 20040237436 | Zuber et al. | Dec 2004 | A1 |
| 20040250911 | Vogel | Dec 2004 | A1 |
| 20050003099 | Quist | Jan 2005 | A1 |
| 20050079780 | Rowe et al. | Apr 2005 | A1 |
| 20050193677 | Vogel | Sep 2005 | A1 |
| 20050252130 | Martensson | Nov 2005 | A1 |
| 20060008630 | Thiers et al. | Jan 2006 | A1 |
| 20060024465 | Briere | Feb 2006 | A1 |
| 20060032175 | Chen et al. | Feb 2006 | A1 |
| 20060070321 | Au | Apr 2006 | A1 |
| 20060145384 | Singer | Jul 2006 | A1 |
| 20060182938 | Oldorff | Aug 2006 | A1 |
| 20060183853 | Sczepan | Aug 2006 | A1 |
| 20070055012 | Caldwell | Mar 2007 | A1 |
| 20070066176 | Wenstrup et al. | Mar 2007 | A1 |
| 20070166516 | Kim et al. | Jul 2007 | A1 |
| 20070184244 | Dohring | Aug 2007 | A1 |
| 20070207296 | Eisermann | Sep 2007 | A1 |
| 20070218260 | Miclo et al. | Sep 2007 | A1 |
| 20070224438 | Van Benthem et al. | Sep 2007 | A1 |
| 20070256804 | Espino et al. | Nov 2007 | A1 |
| 20080000417 | Pervan et al. | Jan 2008 | A1 |
| 20080032120 | Braun | Feb 2008 | A1 |
| 20080090032 | Perrin et al. | Apr 2008 | A1 |
| 20080176039 | Chen et al. | Jul 2008 | A1 |
| 20080263985 | Hasch et al. | Oct 2008 | A1 |
| 20090056257 | Mollinger et al. | Mar 2009 | A1 |
| 20090124704 | Jenkins | May 2009 | A1 |
| 20090135356 | Ando | May 2009 | A1 |
| 20090145066 | Pervan | Jun 2009 | A1 |
| 20090155612 | Pervan et al. | Jun 2009 | A1 |
| 20090208646 | Kreuder et al. | Aug 2009 | A1 |
| 20090294037 | Oldorff | Dec 2009 | A1 |
| 20090311433 | Wittmann | Dec 2009 | A1 |
| 20100092731 | Pervan et al. | Apr 2010 | A1 |
| 20100196678 | Vermeulen | Aug 2010 | A1 |
| 20100223881 | Kalwa | Sep 2010 | A1 |
| 20100239820 | Buhlmann | Sep 2010 | A1 |
| 20100291397 | Pervan et al. | Nov 2010 | A1 |
| 20100300030 | Pervan et al. | Dec 2010 | A1 |
| 20100307675 | Buhlmann | Dec 2010 | A1 |
| 20100307677 | Buhlmann | Dec 2010 | A1 |
| 20100319282 | Ruland | Dec 2010 | A1 |
| 20100323187 | Kalwa | Dec 2010 | A1 |
| 20100330376 | Trksak | Dec 2010 | A1 |
| 20110175251 | Ziegler et al. | Jul 2011 | A1 |
| 20110177319 | Ziegler et al. | Jul 2011 | A1 |
| 20110177354 | Ziegler et al. | Jul 2011 | A1 |
| 20110189448 | Lindgren et al. | Aug 2011 | A1 |
| 20110247748 | Pervan et al. | Oct 2011 | A1 |
| 20110250404 | Pervan et al. | Oct 2011 | A1 |
| 20110262720 | Riebel et al. | Oct 2011 | A1 |
| 20110283642 | Meirlaen et al. | Nov 2011 | A1 |
| 20110283650 | Pervan et al. | Nov 2011 | A1 |
| 20110293823 | Bruderer et al. | Dec 2011 | A1 |
| 20110293906 | Jacobsson | Dec 2011 | A1 |
| 20120263878 | Ziegler et al. | Oct 2012 | A1 |
| 20120263965 | Persson et al. | Oct 2012 | A1 |
| 20120264853 | Ziegler et al. | Oct 2012 | A1 |
| 20120288689 | Hansson et al. | Nov 2012 | A1 |
| 20120308774 | Persson et al. | Dec 2012 | A1 |
| 20130092314 | Ziegler et al. | Apr 2013 | A1 |
| 20130095315 | Pervan et al. | Apr 2013 | A1 |
| 20130111845 | Pervan et al. | May 2013 | A1 |
| 20130189534 | Pervan et al. | Jul 2013 | A1 |
| 20130269863 | Pervan et al. | Oct 2013 | A1 |
| 20130273244 | Vetter et al. | Oct 2013 | A1 |
| 20130273245 | Ziegler et al. | Oct 2013 | A1 |
| 20140044872 | Pervan | Feb 2014 | A1 |
| 20140075874 | Pervan et al. | Mar 2014 | A1 |
| 20140171554 | Ziegler et al. | Jun 2014 | A1 |
| 20140178630 | Pervan et al. | Jun 2014 | A1 |
| 20140186610 | Pervan | Jul 2014 | A1 |
| 20140234531 | Ziegler et al. | Aug 2014 | A1 |
| 20150017461 | Lindgren et al. | Jan 2015 | A1 |
| 20150079280 | Vetter et al. | Mar 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 8028475 | Jun 1975 | AU |
| 2 557 096 | Jul 2005 | CA |
| 2 852 656 | Apr 2013 | CA |
| 298894 | May 1954 | CH |
| 1 815 312 | Jul 1969 | DE |
| 7148789 | Apr 1972 | DE |
| 29 39 828 | Apr 1981 | DE |
| 33 34 921 | Apr 1985 | DE |
| 42 36 266 | May 1993 | DE |
| 202 14 532 | Feb 2004 | DE |
| 103 31 657 | Feb 2005 | DE |
| 20 2004 003 061 | Jul 2005 | DE |
| 10 2004 050 278 | Apr 2006 | DE |
| 20 2006 007 797 | Aug 2006 | DE |
| 10 2005 046 264 | Apr 2007 | DE |
| 10 2006 024 593 | Dec 2007 | DE |
| 10 2010 045 266 | Mar 2012 | DE |
| 0 129 430 | Dec 1984 | EP |
| 0 129 430 | Jan 1990 | EP |
| 0 355 829 | Feb 1990 | EP |
| 0 611 408 | Dec 1993 | EP |
| 0 592 013 | Apr 1994 | EP |
| 0 656 443 | Jun 1995 | EP |
| 0 611 408 | Sep 1996 | EP |
| 0 732 449 | Sep 1996 | EP |
| 0 744 477 | Nov 1996 | EP |
| 0 914 914 | May 1999 | EP |
| 0 732 449 | Aug 1999 | EP |
| 0 744 477 | Jan 2000 | EP |
| 1 035 255 | Sep 2000 | EP |
| 1 125 971 | Aug 2001 | EP |
| 1 136 251 | Sep 2001 | EP |
| 1 193 288 | Apr 2002 | EP |
| 1 209 199 | May 2002 | EP |
| 1 242 702 | Sep 2002 | EP |
| 1 249 322 | Oct 2002 | EP |
| 1 454 763 | Sep 2004 | EP |
| 1 242 702 | Nov 2004 | EP |
| 1 498 241 | Jan 2005 | EP |
| 1 507 664 | Feb 2005 | EP |
| 1 507 664 | Feb 2005 | EP |
| 1 584 378 | Oct 2005 | EP |
| 1 681 103 | Jul 2006 | EP |
| 1 690 603 | Aug 2006 | EP |
| 1 847 385 | Oct 2007 | EP |
| 1 961 556 | Aug 2008 | EP |
| 1 985 464 | Oct 2008 | EP |
| 1 997 623 | Dec 2008 | EP |
| 2 025 484 | Feb 2009 | EP |
| 1 454 763 | Aug 2009 | EP |
| 2 105 320 | Sep 2009 | EP |
| 2 213 476 | Aug 2010 | EP |
| 2 226 201 | Sep 2010 | EP |
| 2 246 500 | Nov 2010 | EP |
| 2 264 259 | Dec 2010 | EP |
| 2 272 667 | Jan 2011 | EP |
| 2 272 668 | Jan 2011 | EP |
| 2 305 462 | Apr 2011 | EP |
| 1 847 385 | Sep 2011 | EP |
| 2 873 953 | Feb 2006 | FR |
| 984 170 | Feb 1965 | GB |
| 1090450 | Nov 1967 | GB |
| 2 248 246 | Apr 1992 | GB |
| 2-229002 | Sep 1990 | JP |
| 11-291203 | Oct 1999 | JP |
| 4162799 | Oct 2000 | JP |
| 2001-287208 | Oct 2001 | JP |
| 2003-311717 | Nov 2003 | JP |
| 2003-311718 | Nov 2003 | JP |
| 2005-034815 | Feb 2005 | JP |
| 2005-074682 | Mar 2005 | JP |
| 2005-170016 | Jun 2005 | JP |
| 2005-219215 | Aug 2005 | JP |
| 3705482 | Oct 2005 | JP |
| 2005-307582 | Nov 2005 | JP |
| 2007-216692 | Aug 2007 | JP |
| 2007-268843 | Oct 2007 | JP |
| 2008-188826 | Aug 2008 | JP |
| 2002-0019815 | Mar 2002 | KR |
| 469 326 | Jun 1993 | SE |
| WO 9206832 | Apr 1992 | WO |
| WO 9400280 | Jan 1994 | WO |
| WO 9506568 | Mar 1995 | WO |
| WO 0022225 | Apr 2000 | WO |
| WO 0044576 | Aug 2000 | WO |
| WO 0148333 | Jul 2001 | WO |
| WO 0164408 | Sep 2001 | WO |
| WO 0168367 | Sep 2001 | WO |
| WO 0192037 | Dec 2001 | WO |
| WO 0242167 | May 2002 | WO |
| WO 0242373 | May 2002 | WO |
| WO 03078761 | Sep 2003 | WO |
| WO 03095202 | Nov 2003 | WO |
| WO 2004042168 | May 2004 | WO |
| WO 2004050359 | Jun 2004 | WO |
| WO 2005054600 | Jun 2005 | WO |
| WO 2005066431 | Jul 2005 | WO |
| WO 2005097874 | Oct 2005 | WO |
| WO 2006007413 | Jan 2006 | WO |
| WO 2006013469 | Feb 2006 | WO |
| WO 2006015313 | Feb 2006 | WO |
| WO 2006043893 | Apr 2006 | WO |
| WO 2006126930 | Nov 2006 | WO |
| WO 2007015669 | Feb 2007 | WO |
| WO 2007042258 | Apr 2007 | WO |
| WO 2007059294 | May 2007 | WO |
| WO 2008004960 | Jan 2008 | WO |
| WO 2008004960 | Jan 2008 | WO |
| WO 2008148771 | Dec 2008 | WO |
| WO 2009065768 | May 2009 | WO |
| WO 2009065769 | May 2009 | WO |
| WO 2009065769 | May 2009 | WO |
| WO 2009080772 | Jul 2009 | WO |
| WO 2009080813 | Jul 2009 | WO |
| WO 2009116926 | Sep 2009 | WO |
| WO 2009124704 | Oct 2009 | WO |
| WO 2010084466 | Jul 2010 | WO |
| WO 2010087752 | Aug 2010 | WO |
| WO 2010094500 | Aug 2010 | WO |
| WO 2011087422 | Jul 2011 | WO |
| WO 2011087423 | Jul 2011 | WO |
| WO 2011129757 | Oct 2011 | WO |
| WO 2011141851 | Nov 2011 | WO |
| WO 2012004699 | Jan 2012 | WO |
| WO 2012141647 | Oct 2012 | WO |
| WO 2013056745 | Apr 2013 | WO |
| Entry |
|---|
| U.S. Appl. No. 14/089,928, Pervan, et al. |
| Pervan, Darko, et al., U.S. Appl. No. 14/089,928, entitled “Recycling of Laminate Floorings,” filed in the U.S. Patent and Trademark Office on Nov. 26, 2013. |
| Parquet International, “Digital Printing is still an expensive process,” Mar. 2008, cover page/pp. 78-79, www.parkettmagazin.com. |
| Floor Daily, “Shaw Laminates: Green by Design,” Aug. 13, 2007, 1 pg, Dalton, GA. |
| BTLSR Toledo, Inc. website. http://www.bltresins.com/more.html. “Advantages to Using Powdered Resins,” May 26, 2007, 2 pages, per the Internet Archive WayBackMachine. |
| Nimz, H.H., “Wood,” Ullmann's Encyclopedia of Industrial Chemistry, published online Jun. 15, 2000, pp. 453-505, vol. 39, Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim, DE. |
| Engstrand, Ola (Contact)/Valinge Innovation, Technical Disclosure entitled “Fibre Based Panels With a Wear Resistance Surface,” Nov. 17, 2008, IP.com No. IPCOM000176590D, IP.com PriorArtDatabase, 76 pages. |
| Engstrand, Ola (Contact)/Valinge Innovation, Technical Disclosure entitled “WFF Embossing,” May 15, 2009, IP.com No. IPCOM000183105D, IP.com PriorArtDatabase, 36 pages. |
| Engstrand, Ola (Contact)/Valinge Innovation, Technical Disclosure entitled “VA063 VA064 Scattering and Powder Backing,” Nov. 11, 2011, IP.com No. IPCOM000212422D, IP.com PriorArtDatabase, 34 pages. |
| U.S. Appl. No. 14/237,617, Pervan. |
| U.S. Appl. No. 14/184,299, Ziegler, et al. |
| U.S. Appl. No. 14/192,169, Pervan, et al. |
| U.S. Appl. No. 14/247,839, Ziegler, et al. |
| Pervan, Darko, U.S. Appl. No. 14/237,617, entitled “Panel Coating,” filed in the U.S. Patent and Trademark Office on Feb. 7, 2014. |
| Ziegler, Göran, et al., U.S. Appl. No. 14/184,299, entitled “Heat and Pressure Generated Design”, filed in the U.S. Patent and Trademark Office on Feb. 19, 2014. |
| Pervan, Darko, et al., U.S. Appl. No. 14/192,169, entitled “Fibre Based Panels with a Wear Resistance Surface”, filed in the U.S. Patent and Trademark Office on Feb. 27, 2014. |
| Ziegler, Göran, et al., U.S. Appl. No. 14/247,839, entitled a Powder Mix and a Method for Producing a Building Panel, filed in the U.S. Patent and Trademark Office on Apr. 8, 2014. |
| U.S. Appl. No. 14/516,957, Persson, et al. |
| U.S. Appl. No. 14/553,196, Vetter, et al. |
| U.S. Appl. No. 14/563,167, Ziegler, et al. |
| Le Fur, X., et al., “Recycling melamine-impregnated paper waste as board adhesives,” published online Oct. 26, 2004, pp. 419-423, vol. 62, Springer-Verlag, DE. |
| Odian, George, “Principles of Polymerization,” 1991, 3rd Edition, 5 pages incl. pp. 122-123, John Wiley & Sons, Inc., New York, NY, USA. |
| Persson, Hans, et al., U.S. Appl. No. 14/516,957, entitled “Method of Manufacturing a Building Panel,” filed in the U.S. Patent and Trademark Office on Oct. 17, 2014. |
| Vetter, Georg, et al., U.S. Appl. No. 14/553,196, entitled “Method for Producing a Building Panel,” filed in the U.S. Patent and Trademark Office on Nov. 25, 2014. |
| Ziegler, Göran, et al., U.S. Appl. No. 14/563,167, entitled “Bright Coloured Surface Layer,” filed in the U.S. Patent and Trademark office on Dec. 8, 2014. |
| Ayrilmis, Nadir, “Enhancement of dimensional stability and mechanical properties of light MDF by adding melamine resin impregnated paper waste,” International Journal of Adhesion & Adhesives, 2012, pp. 45-49, vol. 33, ISSN 0143-7496, (article available online Nov. 10, 2011), Elsevier Ltd, NL. |
| Cavdar, A.D., et al., “Effect of waste melamine impregnated paper on properties of oriented strand board”, Materials and Design, 2013, pp. 751-755, vol. 51, ISSN 0261-306, Elsevier Ltd., NL. |
| U.S. Appl. No. 14/321,288, Lindgren, et al. |
| International Search Report issued in corresponding PCT/SE2014/050015, mailed Apr. 7, 2014, ISA/SE, Patent-och registreringsverket, Stockholm, SE, 6 pages. |
| Lindgren, Kent, et al., U.S. Appl. No. 14/321,288, entitled “A Method of Manufacturing Panel and a Building Panel,” filed in the U.S. Patent and Trademark Office on Jul. 1, 2014. |
| U.S. Appl. No. 14/738,274, Persson, et al. |
| Persson, Hans, et al., U.S. Appl. No. 14/738,274 entitled “Powder Based Balancing Layer,” filed in the U.S. Patent and Trademark Office on Jun. 12, 2015. |
| Number | Date | Country | |
|---|---|---|---|
| 20140199558 A1 | Jul 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61751393 | Jan 2013 | US |