Method of producing barium-titanium-based oxide glass using containerless solidification process

Abstract
Disclosed is a method of producing a barium-titanium-based ferroelectric glass using a containerless solidification process, such as an electrostatic levitation process or a gas levitation process, which comprises the steps of levitating a sample 1 of a barium-titanium-based compound by a levitating force of compressed air, heating the sample up to a temperature greater than its melting point (1330° C.) by about 100° C. to allow the sample to be molten, and, after maintaining the molten state for a given time period (at least several second), quenching the sample from a given temperature range (1400 to 1000° C.) at a cooling rate of about 103 K/sec, so as to allow the sample to be solidified while inhibiting nucleation and mixing of impurities from a container. The present invention makes it possible to provide a glass exhibiting an unprecedented, extremely large permittivity.
Description
TECHNICAL FIELD

The present invention relates to a method of producing a BaTi2O5 ferroelectric glass using a containerless process.


BACKGROUND ART

Over 50 years since discovery of a ferroelectric barium titanium oxide BaTi2O5, researches on ferroelectrics with a focus on applications thereof have been carried out energetically around the world.


A ferroelectric material having a high permittivity, a piezoelectric property, a pyroelectric property, an electrooptic effect and a nonlinear optical effect is applied to various fields, such as electrical and optical fields, and used as a capacitor, an amplifying element, a piezoelectric resonant element, a pyroelectric element, a light modulator and a wavelength conversion element. In particular, recent years, great interest has been shown in researches and applications of a transparent ferroelectric oxide glass. The ferroelectric glass can be crystallized to control its optical properties, and therefore expected to be utilized as a high-performance light modulator (electrical signal/light signal conversion), optical switch (change in direction of a light path) and wavelength conversion element (change in wavelength of a laser beam). Further, the ferroelectric glass is suited to mass production at low cost in view of advantageous capability to be produced through short processes. Thus, the research and development of the ferroelectric glass are highly significant from an industrial perspective as well as scientific and engineering perspectives.


While the ferroelectric BaTi2O5 has excellent dielectric characteristics, it is extremely difficult to be formed as bulk glass due to relatively high nucleation frequency and crystal growth rate in its solidification process. In previous reports, only a thin film-shaped glass was obtained even in a roll quenching method at a cooling rate of about 107 to 8 K/s (see the following Non-Patent Publication 1). Further, an addition of a glass forming element is required to obtain a ferroelectric glass (see the following Non-Patent Publication 2).

    • [Patent Publication 1] Japanese Patent Application No. 2003-284855
    • [Patent Publication 2] Japanese Patent Application No. 2004-020798
    • [Non-Patent Publication 1] K. Yoshimaru, Y. Ueda, K. Morinaga, T. Yanagase, Journal of the Ceramic Society of Japan, 1984, 92: p 481
    • [Non-Patent Publication 2] A. Narasaki, K. Tanaka, K. Hirao, Appl. Phys. Lett. 1999; 75: p 3399


DISCLOSURE OF THE INVENTION

It is an object of the present invention to provide a method capable of producing a high-purity barium-titanium-based ferroelectric glass with high efficiency.


With a focus on barium-titanium-based compounds, the inventors have developed a high-purity barium-titanium-based ferroelectric glass production method which comprises melting a sample by a laser beam while inhibiting nucleation and mixing of impurities from a container and then quenching in a given temperature range, based on a containerless solidification process, such as an electrostatic levitation process or a gas levitation process.


Specifically, according to a first aspect of the present invention, there is provided a method of producing a barium-titanium-based ferroelectric glass, which comprises the steps of: levitating a material having a composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.9 to 1.1); heating the material kept in a levitated state up to a temperature greater than its melting point by about 100° C. to allow the material to be molten; and cooling the molten material at a given cooling rate.


According to a second aspect of the present invention, there is provided a method of producing a barium-titanium-based ferroelectric glass, which comprises the steps of levitating a material having a composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr or Ca; y=0 to 0.5); heating the material kept in a levitated state up to a temperature greater than its melting point by about 100° C. to allow the material to be molten; and cooling the molten material at a given cooling rate.


In the above method set forth in the first or second aspect of the present invention, it is preferable that the step of heating the material includes irradiating the material with a laser beam. In this case, the material may be irradiated with the laser beam from both upper and lower sides thereof.


Preferably, the material is a spherical-shaped polycrystalline material.


The given cooling rate is preferably about 500 K/sec or more, more preferably, about 800 K/sec or more, particularly preferably about 1000 K/sec or more.


The heating temperature of the material is preferably in the range of about 1200 to 1500° C., more preferably, in the range of about 1300 to 1400° C.


Preferably, the method set forth in the first or second aspect of the present invention further includes the step of, prior to the start of the step of cooling the molten material, maintaining the melting temperature for a given time period. In this case, the given time period is preferably at least several seconds.


According to a third aspect of the present invention, there is provided an apparatus for melting and solidifying a material while keeping the material in a levitated state, which comprises: a gas levitation furnace having a nozzle for injecting gas upward to levitate the material; a fixed base disposed below the gas levitation furnace to support the gas levitation furnace; a gas supply device for supplying the gas to the gas levitation furnace through the fixed base; a laser device for irradiating the material with a laser beam serving as a heating source for heating the material; a flow regulator device for regulating a flow volume of the gas; a temperature measurement device for measuring a temperature of the material; and a control device for controlling the laser beam irradiation based on a temperature of the material measured by the temperature measurement device, so as to control the temperature of the material. The gas to be introduced in the gas levitation furnace may include air, Ar, O2 and N2.


Preferably, the apparatus set forth in the third aspect of the present invention is provided with a beam splitting device for splitting a laser beam from the laser device into at least two split beams, and designed to irradiate the material with the split beams, respectively, from upper and lower sides of the material.


Preferably, the temperature measurement device is a radiation thermometer oriented toward the material. Preferably, the apparatus set forth in the third aspect of the present invention further includes a camera device for monitoring the levitated state of the material, and the flow regulator device is designed to regulate a flow volume of the gas to the gas levitation furnace based on the levitated state of the material shot by the camera device.


According to the present invention, a barium-titanium-based ferroelectric glass can be produced with high efficiency while effectively preventing crystallization and crystal growth during solidification. The obtained barium-titanium-based ferroelectric glass is suitable for use in a light modulator, an optical switch and a wavelength conversion element, and can be widely used in electrical and optical fields. Further, in transition temperatures from a glass phase to a crystal phase, the material exhibits an extremely large relative permittivity of 10,000,000 or more. The material having such an extremely large permittivity can be used, for example, as a material of a high-temperature, large-capacity, small-size electronic device.




BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 is an overall block diagram showing a gas levitation apparatus.



FIG. 2 is a graph showing a cooling curve in a production method for a BaTi2O5 glass.



FIG. 3 is an optical-microscopic photograph showing the BaTi2O5 glass.



FIG. 4 is a graph showing X-ray diffraction patterns of BaTi2O5 glasses, respectively, in a room temperature environment and after being heated up to a given temperature.



FIG. 5 is a graph showing the result of differential scanning calorimetric (DSC) analysis of the BaTi2O5 glass.



FIG. 6 is a graph showing a measurement result of permittivity of the BaTi2O5 glass.



FIG. 7 is a graph showing the result of differential scanning calorimetric (DSC) analysis of a glass having a composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92 to 1.13).



FIG. 8 is a graph showing a measurement result of permittivity of the glass having the composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92).



FIG. 9 is a graph showing the result of differential scanning calorimetric (DSC) analysis of a glass having a composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr; y=0.05 to 0.15).



FIG. 10 is a graph showing a measurement result of permittivity of the glass having the composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr; y=0.1).




BEST MODE FOR CARRYING OUT THE INVENTION

With reference to the drawings, an embodiment of the present invention will now be described.


[Gas Levitation Furnace & Control Device]


Referring to FIG. 1, in a gas levitation apparatus according to this embodiment, a gas levitation furnace 2 is used for levitating a sample 1. As shown in FIG. 1, a fixed base 3 is provided as a means to supply levitating gas to the gas levitation furnace 2 therethrough and prevent movement of the gas levitation furnace 2, and the gas levitation furnace 2 is fixedly mounted on the fixed base 3 using an anchoring wire 4. The sample 1 is placed in a vertically-extending through-hole of the gas levitation furnace 2, and the gas is injected upward from a nozzle disposed below the through-hole of the gas levitation furnace 2 in such a manner to levitate the sample 1. A flow regulator device 13 is provided as a means to control a flow volume of the gas so as to allow the sample 1 to be levitated. A levitated state of the sample 1 is monitored by an image pickup device. In this embodiment, a CCD camera 11 is used as the image pickup device. The CCD camera 11 is electrically connected to a monitor 15 to visually check a position of the sample 1. The flow regulator device 13 may be designed to regulate the flow volume of the gas based on an output of the CCD camera 11. A radiation thermometer 12 is disposed oriented toward the sample 1 to measure being heated up to 730° C. and in a state after being heated up to 1280° C. The X-ray diffraction pattern in the room temperature environment exhibits only a wide range of gentle peak peculiar to a glassy or vitreous material, without any steep or sharp peak. If a crystal structure resides in the transparent sample, a sharp peak caused by a crystal lattice will be observed. Thus, as seen in FIG. 4, the transparent sample placed in the room temperature environment is a glass. Each of the X-ray diffraction patterns of the BaTi2O5 transparent samples in a state after being heated up to 730° C. and 1280° C. exhibits a sharp peak peculiar to a crystal material. This proves that when the transparent sample is heated up to 700° C. or more, a glass phase is transformed to a crystal phase.



FIG. 5 shows differential scanning calorimetric (DSC) analysis data about the BaTi2O5 transparent sample. As seen in this data, the transparent sample has three phase transition temperatures (690° C., 728° C. and 765° C.). Specifically, the result in FIG. 5 shows that a glass transition occurs at about 690° C., and then the transition from the glass phase to the crystal phase occurs at two temperatures of 728° C. and 765° C.



FIG. 6 shows a measurement result of permittivity of the BaTi2O5 transparent sample. As seen in FIG. 6, the formed glass has an extremely large relative permittivity of about 10,000,000 or more at a temperature (723° C.) close to the crystallization temperature.


EXAMPLE 2

Plural types of samples were prepared by varying ratios of Ba and Ti in a composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92 to 1.13). A glass was formed using each of the samples, and properties of the formed glass were measured.


Specifically, in the same manner as that in Example 1, each of the samples was prepared using about 20 mg of spherical-shaped polycrystalline material having the composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92 to 1.13). Then, by use of the gas levitation apparatus illustrated in FIG. 1, the sample was levitated, and heated up to a given temperature using the laser device 5. After the sample was molten, it was held in the molten state for a given time period. Then, the sample was cooled in the same cooling curve as that in Example, and solidified. More specifically, each of the samples was levitated a temperature of the sample 1 in a non-contact manner. The temperature of the sample 1 measured by the radiation thermometer 12 is acquired by a computer 14. In this embodiment, a carbon dioxide gas laser device 5 is provided as a means to generate a laser beam for heating the sample 1. The computer 14 is electrically connected to the carbon dioxide gas laser device 5 to control a power or intensity of the laser beam. Specifically, the computer 14 is operable, in response to receiving temperature data about the sample 1 detected by the radiation thermometer 12, to control the power of the laser beam serving as a heating source of the sample 1 so as to control the temperature of the sample 1. The laser beam from the carbon dioxide gas laser device 5 is split by a beam splitter 6 into two split beams each having an even power. Then, the sample 1 kept in the levitated state is irradiated with the split beams incident, respectively, from lower and upper sides of the sample 1 through two reflectors 9, 10, and heated up to a given temperature. The above apparatus illustrated in FIG. 1 is designed to heat the sample 1 up to a temperature of about 1300 to 1400° C. so as to allow the sample 1 to be molten, and then cool the molten material at a cooling rate of about 500 to 1500 K/sec so as to solidify the material to form a glass.


[Gas Levitation/Solidification Process]


In the apparatus illustrated in FIG. 1, the gas (e.g. air, Ar, O2 or N2) is introduced into the gas levitation furnace 2 at a flow volume of about 0.7 liter/minute. The two laser beams are emitted, respectively, from above and below the sample 1 to heat the sample 1. A temperature of the sample 1 is measured from above the sample 1 by the radiation thermometer 12. In a process of levitating the sample 1, the gas is injected in such a manner as to blow out of the gas levitation furnace 2 to levitate the sample 1. Then, the sample 1 kept in the levitated state is heated and molten by the laser beams incident thereon from above and below. The levitated state is continuously monitored by the CCD camera 11, and a video image can also be recorded according to need. Further, the state of the sample 1 is visually checked using the monitor 15, and an operator can appropriately adjust the flow regulator device to regulate the flow volume of the gas in such a manner as to prevent the sample 1 from being wrongly vibrated or brought into contact with the gas levitation furnace 2. In this embodiment, the radiation thermometer 12 for measuring a temperature of the sample 1 is disposed at approximately the same height as and at a different angle from those of the CCD camera 11. The radiation thermometer 12 is operable to analyze emission of light from the sample 1 and measure a temperature of the sample 1 based on the emission. The detected temperature is sent to the computer 14, and used for controlling the temperature of the sample 1 through adjustment of the laser beam power. The molten material is cooled at a given cooling rate, and solidified without occurrence of crystallization to form a glass of a barium-titanium-based material.


EXAMPLE 1

A sample 1 was prepared using about 20 mg of spherical-shaped polycrystalline material having a composition of BaTi2O5, and molten and solidified using the gas levitation apparatus illustrated in FIG. 1. Specifically, the sample 1 was levitated based on a levitating force of compressed air used as levitating gas. In the levitated state, the sample 1 was heated up to a temperature greater than a melting point (1330° C.) of the sample 1 by about 100° C., through means of laser beam irradiation, and molten. After being held in the molten state for a given time period (at least several seconds), the sample 1 was rapidly cooled or quenched from a given temperature (1400 to 1000° C.) at a cooling rate of about 103 K/sec, and solidified. FIG. 2(a) shows a cooling curve for quenching the sample 1 from 1400° C., and FIG. 2(b) shows a cooling curve for quenching the sample 1 from 1000° C. An exothermic peak to be caused by crystallization during solidification is not observed in both the cooling curves. If crystallization occurs during the course of continuously cooling and solidifying the sample 1, a peak caused by exothermic heat will appear on the cooling curve. The above cooling curves having no exothermic peak prove that no crystallization occurs during solidification. In other words, it is verified that the sample 1 is solidified in a non-crystallized state or in a glass state. FIG. 3 is an optical-microscopic photograph showing the obtained spherical-shaped transparent sample.



FIG. 4 shows three X-ray diffraction patterns of the BaTi2O5 transparent samples, respectively, in a state when being placed in a room temperature environment, in a state after based on a levitating force of compressed air used as levitating gas. In the levitated state, the sample was heated up to a temperature greater than its melting point by about 100° C., through means of laser beam irradiation. After being held in the molten state for a given time period, the sample was quenched from a given temperature (1400 to 1000° C.) at a cooling rate of about 103 K/sec. An exothermic peak to be caused by crystallization during solidification was not observed in all cooling curves of the samples. Through X-ray diffraction analysis, it was verified that each of the obtained spherical-shaped transparent glasses is a glass.



FIG. 7 shows the result of differential scanning calorimetric analysis of the four transparent samples having the composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92, 1.0, 1.05 and 1.13). As seen in FIG. 7, a glass transition temperature and a crystallization temperature exist in each of the transparent samples. This means that each of the four transparent samples is kept in a vitreous state at a room temperature.



FIG. 8 shows a measurement result of permittivity of the transparent sample having the composition represented by the general formula: Bax Ti3−x O6−x (wherein x=0.92). As seen in FIG. 8, the transparent sample has an extremely large relative permittivity of about 10,000,000 or more at a temperature (730° C.) close to the crystallization temperature, as with the BaTi2O5 transparent sample in Example 1.


EXAMPLE 3

In the same manner as that in Example 1, each of plural types of samples was prepared using about 20 mg of spherical-shaped polycrystalline material having the composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr or Ca; y=0.05 to 0.15), and molten and solidified using the gas levitation apparatus illustrated in FIG. 1. Specifically, each of the samples was levitated based on a levitating force of compressed air used as levitating gas. In the levitated state, the sample was heated up to a temperature greater than its melting point by about 100° C., through means of laser beam irradiation. After being held in the molten state for a given time period, the sample was quenched from a given temperature (1400 to 1000° C.) at a cooling rate of about 10 K/sec. An exothermic peak to be caused by crystallization during solidification was not observed in all cooling curves of the samples. Through X-ray diffraction analysis, it was verified that each of the obtained spherical-shaped transparent glasses is a glass.



FIG. 9 shows the result of differential scanning calorimetric analysis of the three transparent samples having the composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr; y=0.05, 0.1, 0.15). As seen in FIG. 9, a glass transition temperature and a crystallization temperature exist in each of the transparent samples.



FIG. 10 shows a measurement result of permittivity of the transparent sample having the composition represented by the general formula: Ba(1−y) My Ti2 O5 (wherein M=Sr; y=0.1). As seen in FIG. 10, the transparent sample has an extremely large relative permittivity of about 10,000,000 or more at a temperature (730° C.) close to the crystallization temperature, as with the BaTi2O5 transparent sample in Example 1.


INDUSTRIAL APPLICABILITY

It has been proven that the method of the present invention can provide a glass exhibiting an extremely large permittivity which could not be achieved by conventional methods. This glass having unprecedented features is expected to be applied, for example, to optical devices (optical switches and optical sensors).

Claims
  • 1. A method of producing a barium-titanium-based ferroelectric glass, comprising the steps of: levitating a material having a composition represented by the general formula: Bax Ti3−x O6−x, wherein x=0.9 to 1.1; heating said material kept in a levitated state up to a temperature greater than the melting point of said material by about 100° C. to allow said material to be molten; and cooling said molten material at a given cooling rate.
  • 2. The method as defined in claim 1, wherein the step of heating the material includes irradiating said material with a laser beam.
  • 3. The method as defined in claim 2, wherein said material is irradiated with said laser beam from both upper and lower sides thereof.
  • 4. The method as defined in claim 1, wherein said material is a spherical-shaped polycrystalline material.
  • 5. The method as defined in claim 1, wherein said given cooling rate is about 500 K/sec or more.
  • 6. The method as defined in claim 5, wherein said given cooling rate is about 800 K/sec or more.
  • 7. The method as defined in claim 6, wherein said given cooling rate is about 1000 K/sec or more.
  • 8. The method as defined in claim 7, wherein the heating temperature of said material is in the range of about 1200 to 1500° C.
  • 9. The method as defined in claim 8, wherein the heating temperature of said material is in the range of about 1300 to 1400° C.
  • 10. The method as defined in claim 1, which further includes the step of, prior to the start of the step of cooling said molten material, maintaining said melting temperature for a given time period.
  • 11. The method as defined in claim 10, wherein said given time period is at least several seconds.
  • 12. A method of producing a barium-titanium-based ferroelectric glass, comprising the steps of: levitating a material having a composition represented by the general formula: Ba(1−y) My Ti2 O5, wherein M=Sr or Ca; y=0 to 0.5; heating said material kept in a levitated state up to a temperature greater than the melting point of said material by about 100° C. to allow said material to be molten; and cooling said molten material at a given cooling rate.
  • 13. The method as defined in claim 12, wherein the step of heating the material includes irradiating said material with a laser beam.
  • 14. The method as defined in claim 12, wherein said material is a spherical-shaped polycrystalline material.
  • 15. The method as defined in claim 14, wherein said material is irradiated with said laser beam from both upper and lower sides thereof.
  • 16. The method as defined in claim 12, wherein said given cooling rate is about 500 K/sec or more.
  • 17. The method as defined in claim 16, wherein said given cooling rate is about 1000 K/sec or more.
  • 18. The method as defined in claim 12, wherein the heating temperature of said material is about 1200° C. or more.
  • 19. The method as defined in claim 18, wherein the heating temperature of said material is in the range of about 1300 to 1400° C.
  • 20. The method as defined in claim 12, which further includes the step of, prior to the start of the step of cooling said molten material, maintaining said melting temperature for a given time period.
  • 21. The method as defined in claim 20, wherein said given time period is at least several seconds.
  • 22. An apparatus for melting and solidifying a material while keeping said material in a levitated state, comprising: a gas levitation furnace having a nozzle for injecting gas upward to levitate said material; a fixed base disposed below said gas levitation furnace to support said gas levitation furnace; a gas supply device for supplying said gas to said gas levitation furnace through said fixed base; a laser device for irradiating said material with a laser beam serving as a heating source for heating said material; a flow regulator device for regulating a flow volume of said gas; a temperature measurement device for measuring a temperature of said material; and a control device for controlling the laser beam irradiation based on a temperature of said material measured by said temperature measurement device, so as to control the temperature of said material.
  • 23. The apparatus as defined in claim 22, which further includes a beam splitting device for splitting a laser beam from said laser device into at least two split beams, wherein said apparatus is designed to irradiate said material with said split beams, respectively, from upper and lower sides of said material.
  • 24. The apparatus as defined in claim 22, wherein said temperature measurement device is a radiation thermometer oriented toward said material.
  • 25. The apparatus as defined in claim 22, which further includes a camera device for monitoring the levitated state of said material, wherein said flow regulator device is designed to regulate a flow volume of said gas to said gas levitation furnace based on the levitated state of said material shot by said camera device.
Priority Claims (1)
Number Date Country Kind
2005/064055 Mar 2005 JP national