Claims
- 1. A method of producing a zirconium-containing alloy by melting copper, together with other alloying ingredients, in an air atmosphere, and adding the zirconium in two separate steps to assure uniform dispersion within the melt, said method comprising the successive steps of:
- (a) melting from about 85 to about 95% by weight of copper of the total copper content in a crucible in air;
- (b) introducing only zirconium in at least a deoxidizing amount to the copper melt; thereafter
- (c) introducing an alloying amount of zirconium to the substantially deoxidizing melt of step (b), thereby dispersing the thus added zirconium uniformly throughout the melt; and
- (d) adding the remaining amount of copper of about 5 to about 15% by weight to the melt, thereby rapidly cooling the melt to a casting temperature and minimizing the loss of zirconium added in step (b), the melt being substantially exposed to an air atmosphere during steps (a), (b), (c) and (d).
- 2. The method according to claim 1 wherein the alloy produced is a chrome-zirconium-copper alloy.
- 3. The method according to claim 1 wherein the alloy contains 0.3 to 1% by weight of Cr and 0.1 to 0.5% by weight of Zr.
- 4. The method according to claim 1 wherein the melting is conducted in a carbon crucible.
- 5. The method of claim 1 wherein there is added after step (b) from 0.005 to 0.1% by weight of at least one additive selected from the group consisting of silicon, germanium, magnesium and boron.
- 6. The method according to claim 1 wherein the alloy is Zr-Cu.
- 7. The method according to claim 6 wherein the Zr-Cu alloy contains about 0.05 to about 0.5% by weight Zr.
Priority Claims (1)
Number |
Date |
Country |
Kind |
54-99884 |
Aug 1979 |
JPX |
|
Parent Case Info
This is a continuation of application Ser. No. 374,910 filed May 4, 1982; which is a continuation of Ser. No. 175,014 filed Aug. 7, 1980 both now abandoned.
US Referenced Citations (7)
Non-Patent Literature Citations (1)
Entry |
Copper-Base Alloys Foundry Practice, Third Edition, 1965, American Foundrymen's Society, Des Plaines, Ill., pp. 8-14. |
Continuations (2)
|
Number |
Date |
Country |
Parent |
374910 |
May 1982 |
|
Parent |
175014 |
Aug 1980 |
|