Patent Application
20100297467
A method of casting metal wherein planar, directional solidification is combined with feeding metal of varying composition to produce an ingot with varying composition through the ingot thickness and substantially uniform composition across the ingot width and thickness.
A method of casting metal, comprising the following steps. Molten metal of a first composition is fed into a mold cavity, via a first control apparatus, wherein the control apparatus is open, wherein the feeding comprises flowing out of a first feed chamber. The first control apparatus is closed. A second control apparatus is opened. Molten metal of a second composition is fed into the mold cavity, via the second control apparatus, wherein at least a portion of the metal of the first composition in the mold cavity is sufficiently molten so that an initial feed of molten metal of the second composition mixes with the molten metal of the first composition in the mold cavity, wherein the feeding comprises flowing out of a second feed chamber, wherein the second composition is different from the first composition. An ingot is removed from the mold cavity, wherein the ingot has a top section, a middle section, and a bottom section, wherein the bottom section is composed of metal of the first composition, wherein the top section is composed of metal of the second composition, wherein the middle section is composed of a mixture of metal of the first composition and the second composition.
A method of casting metal, comprising the following steps. Molten metal of a first composition is fed into a mold cavity, via a first control apparatus, wherein the control apparatus is open, wherein the feeding comprises flowing out of a first feed chamber. The first control apparatus is closed. A second control apparatus is opened. Any molten metal of the first composition between the first feed chamber and the first control apparatus is drained, Molten metal of a second composition is fed into the mold cavity, via the second control apparatus, wherein at least a portion of the metal of the first composition in the mold cavity is sufficiently molten so that an initial feed of molten metal of the second composition mixes with the molten metal of the first composition in the mold cavity, wherein the feeding comprises flowing out of a second feed chamber, wherein the second composition is different from the first composition. A first thickness of metal in the mold cavity is determined. The second control apparatus is closed in response to determining the first thickness. A second thickness of metal in the mold cavity is determined. The first control apparatus is opened in response to determining the second thickness. Molten metal of the first composition is fed into the mold cavity, wherein at least a portion of the metal of the second composition in the mold cavity is sufficiently molten so that an initial feed of molten metal of the first composition mixes with the molten metal of the second composition in the mold cavity. An ingot is removed from the mold cavity, wherein the ingot has a first layer, a second layer, a third layer, a fourth layer, and a fifth layer wherein the first and fifth layers are composed of metal of the first composition, wherein the third layer is composed of metal of the second composition, wherein the second and fourth layers are composed of a mixture of metal of the first composition and the second composition.
As used herein, a solidification front is, for example, the interface between the solid portion and liquid portion of a cast ingot as it cools. A substantially planar solidification front is, for example, a solidification front that is substantially uniform across the plane substantially parallel to the face of the ingot that begins cooling first.
A cast metal ingot is formed, wherein a solidification front remains substantially planar during casting, wherein the ingot has a top section, a middle section, and a bottom section, wherein the bottom section is composed of metal of a first composition, wherein the top section is composed of metal of a second composition, wherein the middle section is composed of a mixture of metal of the first composition and the second composition.
A cast metal ingot is formed, wherein a solidification front remains substantially planar during casting, wherein the ingot has a first layer, a second layer, a third layer, a fourth layer, and a fifth layer wherein the first and fifth layers are composed of metal of a first composition, wherein the third layer is composed of metal of the second composition, wherein the second and fourth layers are composed of a mixture of metal of the first composition and the second composition.
A cast metal ingot is formed, wherein a solidification front remains substantially planar during casting, wherein the ingot has multiple layers comprising two or more compositions separated by layers composed of mixtures of those compositions.
A method of casting metal, comprising the following steps. A specified quantity of molten metal of a first composition is fed into a mixing apparatus. Molten metal is fed from the mixing apparatus into a mold cavity. A molten metal of a second composition is fed into the mixing apparatus, wherein the first composition is different from the second composition. An ingot is removed from the mold cavity, wherein the ingot has a thickness, a top, and a bottom, wherein the ingot composition includes a continuous gradient, wherein the continuous gradient is a gradient of metals of at least the first and second compositions, wherein an amount of metal of the first composition decreases gradually from the bottom of the ingot through the thickness to the top of the ingot, wherein an amount of metal of the second composition in increases gradually from the bottom of the ingot through the thickness to the top of the ingot.
A metal ingot is cast from at least two different metals, including a first composition and a second composition, wherein a solidification front remains substantially planar during casting, wherein the ingot has a thickness, a top, and a bottom, wherein the ingot composition includes a continuous gradient, wherein the continuous gradient is a gradient of metals of at least the first and second compositions, wherein an amount of metal of the second composition decreases gradually from the bottom of the ingot through the thickness to the top of the ingot, wherein an amount of metal of the first composition in increases gradually from the bottom of the ingot through the thickness to the top of the ingot.
A method of casting metal, comprising the following steps. Molten metal of a first composition is fed into a mold cavity via a first programmable control apparatus, wherein the feeding comprises flowing out of a first feed chamber. Molten metal of a second composition is fed into the mold cavity via a second programmable control apparatus, wherein the feeding comprises flowing out of a second feed chamber, wherein the second composition is different from the first composition. The first control apparatus is programmed to permit molten metal of the first composition to flow out of the first feed chamber at a desired rate that decreases to 0 lbs/minute during a desired first casting period. The second control apparatus is programmed to permit molten metal of the second composition to flow out of the second feed chamber at a rate increasing from 0 lbs/minute to the desired rate. The first control apparatus is also programmed to permit molten metal to flow out of the first feed chamber at a rate increasing from 0 lbs/minute to the desired rate, during a desired second casting period. The second control apparatus is also programmed to permit molten metal to flow out of the second feed chamber at a rate decreasing from the desired rate to 0 lbs/minute during the second casting period. An ingot is removed from the mold cavity, wherein the ingot has a thickness, a top, a bottom, and a mid-point, wherein the ingot composition includes a continuous gradient, wherein the continuous gradient is a gradient of metals of the first and second composition, wherein an amount of metal of the first composition decreases gradually from the bottom of the ingot through the thickness to the mid-point of the ingot, wherein an amount of metal of the first composition increases gradually from the mid-point of the ingot through the thickness to the top of the ingot.
A metal ingot is cast from at least two different metals, including a first composition and a second composition, wherein a solidification front remains substantially planar during casting, wherein the ingot has a thickness, a top, a bottom, and a mid-point, wherein the ingot composition includes a continuous gradient, wherein the continuous gradient is a gradient of metals of at least the first and the second composition, wherein an amount of metal of the first composition decreases gradually from the bottom of the ingot through the thickness to the mid-point of the ingot, wherein an amount of metal of the first composition increases gradually from the mid-point of the ingot through the thickness to the top of the ingot.
Other variations, embodiments and features of the present disclosure will become evident from the following detailed description, drawings and claims.
a is a top view of an illustration of a further embodiment of the casting system of the present invention.
It will be appreciated by those of ordinary skill in the art that the embodiments disclosed herein can be embodied in other specific forms without departing from the spirit or essential character thereof. The presently disclosed embodiments are therefore considered in all respects to be illustrative and not restrictive.
In one embodiment of the present invention, a cast ingot is formed by a method of unidirectional solidification wherein the composition is varied through the thickness, either gradually or in steps or any combination of the two. For purposes of this description, thickness is defined as the thinnest dimension of the casting. A casting system used to produce the ingot includes, in one embodiment, a casting apparatus including a mold cavity oriented substantially horizontally, having a plurality of sides and a bottom that may be structured to selectively permit or resist the effects of a coolant sprayed thereon. One example of a bottom configuration is a substrate having holes of a size that allow coolants to enter but resist the exit of molten metal. Such holes are, in one example, at least about 1/64 inch in diameter, but not more than about one inch in diameter. Another example of a bottom configuration is a conveyor having a solid section and a mesh section. One example of a casting apparatus that may be used is described in U.S. Pat. Nos. 7,377,304 and 7,264,038. By this reference, the contents of these patents are deemed to be incorporated into the present application.
In one embodiment of the casting system, a trough for transporting material from each of at least two reservoirs leads to a mixer or a standard degassing unit, each trough having a flow control valve to vary the flow of material from the reservoir into a mixer or standard degassing unit. In one example, at least one trough leads from the mixer to a degassing unit and a filter, from which the trough terminates at a side of the mold cavity, and is structured to introduce material to the mold cavity in a level fashion. In another embodiment, the material is delivered vertically to the top of the mold cavity in a controlled manner. In either of these embodiments, the material may be delivered at a single point or multiple points around the mold cavity.
The sides of the mold cavity are in one embodiment insulated. A plurality of cooling jets, for example air/water jets, are located below the bottom, and are structured to spray coolant against the bottom surface of the substrate. In one embodiment, the substrate is perforated allowing the cooling media to directly contact the solidifying ingot.
In one embodiment, molten metal is introduced substantially uniformly through the mold cavity. At the same time, for example, a cooling medium is applied uniformly over the bottom side of the substrate. In another embodiment, the rate at which molten metal flows into the mold cavity, and the rate at which coolant is applied to the bottom are both controlled to provide unidirectional solidification. The coolant may begin as air, for example, and then gradually be changed from air to an air-water mist, and then to water but any cooling media or delivery method that achieves the desired heat transfer can be used.
Accordingly, one embodiment of the present invention provides an improved method of directionally solidifying castings during cooling where the solidification front remains substantially planar. Hence, in one example, as composition of the metal fed into the mold cavity varies, the composition of the resultant ingot varies in a consistent way through the thickness. In this example, the composition varies through the thickness but not across the width or length of the ingot.
In one embodiment, by varying the flow of material from each reservoir, the composition of the ingot can be varied gradually or in a layered manner. The following examples result in an ingot having layers of different compositions, with an interface between the layers that is relatively sharp, compared to the next group of examples. In one example, material of a first composition flows out of the first reservoir and then is halted at the same time that the flow of material having a second composition is initiated from the second reservoir. In this example the resultant ingot consists of a layer of the first composition combined with a layer of the second composition.
In another example, molten metal of the first composition flows from a first reservoir into a first degasser or other means for removing hydrogen or other undesirable elements from the molten metal, including, for example, sodium, potassium, or calcium. The degasser can be located in the casting line, such as a porous trough degasser or a compact degasser. Alternatively, the degasser can treat the molten metal outside of the casting line and the molten metal is transferred back into the casting line.
In a further example molten metal of the first composition next flows from the degasser into a filter, such as for example a ceramic foam filter or other means for removing nonmetallic inclusions, for example oxides.
In another example, molten metal of the first composition flows into the mold cavity through a trough including a first control apparatus or similar device that regulates the flow rate of the molten metal. The control apparatus may be, for example, a pneumatic gate or dam, and can be computer-controlled and/or programmable. In another example, the trough leading to the mold cavity contains a second control apparatus or similar device, through which molten metal of the second composition flows into the mold cavity.
In a further example, the mold cavity is vertically moveable, and can move downward during casting at a controllable or programmable rate. In one embodiment, this rate is about 0.5 inches/minute. In another example, the troughs are vertically moveable, and can move upward during casting at a controllable or programmable rate.
In another example, flow from each reservoir is alternated repeatedly and in any pattern desired, resulting in a multi-layered ingot. The flows are started and stopped by opening and closing the first and second control apparatuses as needed. The control apparatuses may be opened and closed, for example, by computer-controlled pneumatics. In yet another example, flow from each reservoir is varied, resulting in a variable composition in a first increment of thickness and then flow is stopped from one of the reservoirs to produce a layer of constant composition in the next increment of thickness. In a further example, molten metal of the first composition is drained from any trough between the first feed chamber and the first control apparatus before the second control apparatus is opened to permit the flow of molten metal of the second composition into the mold cavity. In another example, molten metal of the second composition is drained from any trough between the second feed chamber and the second control apparatus before the first control apparatus is re-opened, re-feeding molten metal of the first composition into the mold cavity.
Suitable alloy compositions include, but are not limited to, alloys of the AA series 1000, 2000, 3000, 4000, 5000, 6000, 7000, or 8000. Other suitable metals may include magnesium base alloys, iron base alloys, titanium base alloys, nickel base alloys, and copper base alloys. New Suitable alloy compositions further include but are not limited to aluminum alloys containing copper, magnesium, silicon, zinc, lithium, manganese, zirconium, hafnium, scandium, iron, all of which may have varying weight-percents of the non-aluminum element.
In one example, the first composition is a 5456 alloy. About 5000 lbs of the first composition is held in a furnace at about 1370° Fahrenheit. The second composition is a 7085 alloy. About 6000 lbs of the second composition is held in a furnace at about 1370° Fahrenheit. The molten metal of the first composition flows from the first furnace-reservoir to the first degasser at a rate of about 80 lbs/minute. The degasser rotates at a constant speed as molten metal is transferred out of the furnace-reservoir. The molten metal of the second composition flows from the second furnace-reservoir to the second degasser, and the second filter, then stops at the closed second control apparatus. After a thickness of solidified metal of the first composition is in the mold cavity, the first control apparatus is closed. The flow out of a feed chamber such as a furnace-reservoir may be stopped, for example, by using a refractory-type plug or similar device to plug the opening in the feed chamber through which the molten metal is flowing. Alternatively, the flow out of a feed chamber such as a tilt furnace may be stopped, for example, by tilting the reservoir. The molten metal of the first composition that has flowed out of the first furnace-reservoir but did not flow into the mold cavity is drained out, and the first filter replaced. Next, the second control apparatus is opened, and molten metal of the second composition flows into the mold cavity at a rate of about 80 lbs/minute. After a thickness of solidified metal of the second composition is in the mold cavity, the second control apparatus is closed, and the flow of molten metal out of the second furnace-reservoir is stopped. Concomitant with closing the second control apparatus and stopping the flow out of the second furnace-reservoir, the first furnace-reservoir is re-opened and molten metal of the first composition flows to the first degasser, then through the first filter that is replaced, then stops at the closed first control apparatus. When the thickness of the solidified metal in the mold box is sufficient, the first control apparatus is opened and molten metal of the first composition flows into the mold cavity. Casting continues until a desired thickness of metal is in the mold cavity. The resulting ingot has a composition alternating between metal of the first and second compositions.
The following examples result in an ingot having layers of different compositions, with an interface between the layers that is relatively diffuse, compared to the preceding group of examples. In one example, material is fed from both reservoirs, simultaneously, resulting in a composition that is a mix of the compositions in each reservoir related to the material flow rates from each reservoir. In another example, the flow from each reservoir is varied continuously to create any desired mixture at any given position through the thickness of the solidified ingot. In yet another example, flow from each reservoir is varied resulting in a variable composition in a first increment of thickness and then flow is stopped from one of the reservoirs to produce a layer of constant composition in the next increment of thickness. Such a procedure could be varied, in other examples, in any way desired to produce alternating layers of gradient compositions, constant compositions or any combination, therein.
Another embodiment of the invention provides a method of maintaining a relatively constant solidification rate through the thickness of the casting by varying application of the cooling media.
In one example, molten metal of a first composition is an aluminum alloy that is 6 weight percent magnesium. About 6000 lbs of molten metal of the first composition is in a furnace-reservoir at about 1370° Fahrenheit. Molten metal of the second composition is an aluminum alloy that is 2.5 weight percent magnesium. About 700 lbs of molten metal of the second composition is in a mixing apparatus at about 1350° Fahrenheit. The furnace-reservoir is opened, permitting molten metal of the first composition to flow into the mixing apparatus at a rate of about 80 lbs/minute. Molten metal flows out of the mixing apparatus into a filter, and into the mold cavity. Casting continues with molten metal flowing from the furnace-reservoir into the mixing apparatus, from the mixing apparatus into the filter, and from the filter into the mold cavity until metal in the mold cavity reaches the desired thickness. The resulting ingot has a single composition gradient through the thickness, for example the magnesium content. In another example, the mixing apparatus is a degasser that rotates at a constant speed.
In another example, molten metal of a first composition is an aluminum alloy that is 2 weight percent magnesium. About 5000 lbs of molten metal of the first composition is in a first furnace-reservoir at about 1370° Fahrenheit. Molten metal of a second composition is an aluminum alloy that is 5 weight percent magnesium. About 5000 lbs of molten metal of the second composition is in a second furnace-reservoir at about 1370° Fahrenheit. A first programmable control apparatus between the first furnace-reservoir and a degasser located in the casting line is programmed to permit molten metal of the first composition to flow out of the first furnace-reservoir into the degasser at a rate decreasing from, for example, 80 lbs/minute to 0 lbs/minute during a first casting period, for example 16 minutes. The first casting period is determined by determining a first desired thickness of metal to flow into the mold cavity, for example 8 inches. The rate may decrease, for example, linearly, exponentially, or parabolically. The first control apparatus is also programmed to permit molten metal of the first composition to flow out of the first furnace-reservoir into the degasser at a rate increasing from 0 lbs/minute to the original rate at which molten metal of the first composition flowed out of the first furnace-reservoir, for example 80 lbs/minute, during a second casting period, for example, 16 minutes. The second casting period is determined by determining a second desired thickness of metal to flow into the mold cavity, for example 8 inches. The rate may increase, for example, linearly, exponentially, or parabolically. The second control apparatus is programmed to permit molten metal of the second composition to flow out of the second furnace-reservoir into the degasser at a rate increasing from 0 lbs/minute to, for example, the maximum rate at which molten metal of the first composition is permitted to flow, for example 80 lbs/minute, during the first casting period. The rate may increase, for example, linearly, exponentially, or parabolically. The second control apparatus is also programmed to permit molten metal of the second composition to flow out of the second furnace-reservoir into the degasser at a rate decreasing from the maximum rate attained, for example 80 lbs/minute, to 0 lbs/minute during the second casting period. The rate may decrease, for example, linearly, exponentially, or parabolically. When casting begins, the control apparatuses function as programmed, and molten metal flows out of the furnace-reservoirs, into a degasser, into a filter, and into the mold cavity. Casting continues until the metal in the mold cavity reaches a total desired thickness, for example 16 inches. The resulting ingot has a continuous gradient composition across the thickness, for example the magnesium content.
In a further example, molten metal of a first composition is a 5456 alloy or another aluminum alloy that is approximately 4-5 weight percent magnesium. Molten metal of the second composition is a 7055 aluminum alloy. Casting begins with molten metal of the first composition flowing from a furnace-reservoir through the casting system to the mold cavity. Casting continues with molten metal of the second composition flowing from a furnace-reservoir through the casting system to the mold cavity. The resulting ingot has a single composition gradient through the thickness, for example the magnesium content.
In one embodiment of the present invention, the casting apparatus comprising a plurality of sides and a bottom defining a mold cavity, wherein the bottom has at least two surfaces, including a first surface and a second surface. The casting system further includes at least two metal feed chambers, including a first and a second feed chamber, each feed chamber adjacent to a different degasser, each degasser adjacent to a different filter. The casting system also includes at least one trough into which each filter leads, that is adjacent to the mold cavity, wherein the trough includes at least one control apparatus between each filter and the mold cavity, the control apparatuses being structured to control the flow rates of molten metal being fed into the mold cavity. In this embodiment, the bottom of the mold cavity comprises a substrate having (a) sufficient dimensions, and (b) a plurality of apertures, such that the bottom: (i) allows cooling mediums to flow through the apertures and directly contact the metal, wherein a direction of the flow of the cooling medium is from the first surface of the bottom into the mold cavity, and (ii) simultaneously resists the metal initially poured directly onto the second surface of the bottom from exiting through the apertures to the first surface of the bottom. Each feed chamber contains molten metal of different compositions. Molten metal from the first feed chamber is fed into a first degasser adjacent the first feed chamber. The molten metal from the first degasser is fed to a first filter adjacent the first degasser. The molten metal from the first filter is fed into the mold cavity through the trough, wherein the control apparatus between the first filter and the mold cavity is open. Before a desired thickness is reached in the mold cavity, molten metal from the second feed chamber is fed into a second degasser adjacent the second feed chamber. The molten metal from the second degasser is fed to a second filter adjacent the second degasser. The molten metal from the second filter is fed into the trough, wherein the control apparatus between the second filter and the mold cavity is closed. The control apparatus in the trough between the first filter and the mold cavity is then closed. The flow of molten metal out of the first feed chamber into the first degasser is halted. Any metal between the feed chamber and the first control apparatus is drained. The control apparatus in the trough between the second filter and the mold cavity is opened thereby feeding the molten metal from the second filter into the mold cavity. Before a desired thickness is reached in the mold cavity, the control apparatus in the trough between the second filter and the mold cavity is closed. The flow of molten metal out of the second feed chamber into the second degasser is halted, and the control apparatus in the trough between the second filter and the mold cavity is closed. Any metal between the feed chamber and the second control apparatus is drained. Molten metal from the first feed chamber is re-fed into the first degasser, and flows from the first degasser into an renewed first filter, and from the first filter into the trough. After a desired thickness is reached in the mold cavity, the control apparatus between the renewed first filter and the mold cavity is opened, thereby re-feeding molten metal from the renewed first filter into the mold cavity. Simultaneously a cooling medium is directed against the bottom of the mold cavity, whereby the molten metal is cooled unidirectionally through its thickness.
In another embodiment of the present invention the casting apparatus comprises a plurality of sides and a bottom defining a mold cavity, wherein the bottom has at least two surfaces, including a first surface and a second surface. The casting system further comprises at least one metal feed chamber adjacent to a mixing apparatus and at least one control apparatus between the feed chamber and the mixing apparatus, the control apparatus being structured to control the flow rates of molten metal being fed into the mixing apparatus. The casting system also includes at least one filter between the mixing apparatus and the mold cavity and at least one control apparatus between the filter and the mold cavity, the control apparatus being structured to control the flow rates of molten metal being fed into the mold cavity. The bottom of the mold cavity comprises a substrate having (a) sufficient dimensions, and (b) a plurality of apertures, such that the bottom: (i) allows cooling mediums to flow through the apertures and directly contact the metal, wherein a direction of the flow of the cooling medium is from the first surface of the bottom into the mold cavity, and (ii) simultaneously resists the metal initially poured directly onto the second surface of the bottom from exiting through the apertures to the first surface of the bottom. The feed chamber and mixing apparatus each contain molten metal of different compositions. Molten metal is fed from the feed chamber to the mixing apparatus. Molten metal is fed from the mixing apparatus into the filter. Molten metal is fed from the filter into the mold cavity. Simultaneously a cooling medium is directed against the bottom of the mold cavity, whereby the molten metal is cooled unidirectionally through its thickness. In another embodiment, the mixing apparatus is a degasser that rotates at a constant speed. In yet another embodiment, the casting system includes a degasser between the mixing apparatus and the filter.
In yet another embodiment of the present invention, the casting apparatus comprises a plurality of sides and a bottom defining a mold cavity, wherein the bottom has at least two surfaces, including a first surface and a second surface. The casting system further comprises at least two metal feed chambers, including a first and a second feed chamber and at least one trough into which each feed chamber leads, wherein the trough includes at least one programmable control apparatus between each feed chamber and a degasser located in the casting line, the control apparatuses being structured to control the flow rates of molten metal being fed into the degasser. The casting system also includes at least one filter between the degasser and the mold cavity. The bottom of the mold cavity comprises a substrate having (a) sufficient dimensions, and (b) a plurality of apertures, such that the bottom: (i) allows cooling mediums to flow through the apertures and directly contact the metal, wherein a direction of the flow of the cooling medium is from the first surface of the bottom into the mold cavity, and (ii) simultaneously resists the metal initially poured directly onto the second surface of the bottom from exiting through the apertures to the first surface of the bottom. The feed chambers each contain molten metal of different composition. A first control apparatus between the first feed chamber and the degasser is programmed to permit molten metal to flow into the degasser at a rate decreasing linearly from a desired flow rate to 0 lbs/minute during a desired first casting period. A second control apparatus is programmed between the second feed chamber and the degasser to permit molten metal to flow into the degasser at a rate increasing linearly from 0 lbs/minute to the same rate at which molten metal began flowing into the degasser from the first feed chamber during the first casting period. The first control apparatus is also programmed to permit molten metal to flow into the degasser at a rate increasing linearly from 0 lbs/minute to the rate at which molten metal began flowing into the degasser during the first casting period, during a desired second casting period. The second control apparatus is also programmed to permit molten metal to flow into the degasser from the second feed chamber at a rate decreasing linearly to 0 lbs/minute from the rate at which molten metal began flowing into the degasser from the first feed chamber during the first casting period, during the second casting period. Molten metal is fed from the feed chambers into the degasser through the trough, wherein the control apparatuses control the flow as programmed. Simultaneously a cooling medium is directed against the bottom of the mold cavity, whereby the molten metal is cooled uni-directionally through its thickness.
In a further embodiment, the sources of material (1, 2, 3) are furnace-reservoirs.
Although the embodiments described in
a is an illustration of an embodiment of the casting system of the present invention. In this embodiment, the composition of the ingot formed by the system is varied by flowing material from the first metal source (1) through a trough (22) into another metal source (2), and then through a trough (26) to the casting apparatus (14). The material may optionally flow from the second metal source (2) through a trough (23) to a degasser (16), then through a trough (24) to the casting apparatus (14); the material may flow from the degasser (16) through a trough (13) to a filter (12) and then to the casting apparatus (14) through a trough (15); the material may also flow from the second metal source (2) through a trough (25) to the filter (12) and then to the casting apparatus (14) through trough (15). In this embodiment, the ingot would start with the composition in the second metal source and gradually transition to the composition in the first metal source as the second metal source is diluted. The rate of change in composition can be changed by varying the volume of metal in metal source (2).
A coolant manifold is disposed below the bottom (20) in one embodiment. The coolant manifold preferably is configured to selectively spray air, water, or a mixture of air and water against the bottom (20).
In a further embodiment, a laser sensor may be disposed above the mold cavity, and is preferably structured to monitor the level of material within the mold cavity.
The application of coolant to the bottom of the mold cavity, along with, in some preferred embodiments, the insulation on the sides results in directional solidification of the casting from the bottom to the top of the mold cavity. Preferably, the rate of introduction of material into the mold cavity, combined with the cooling rate, will be controlled to maintain about 0.1 inch (2.54 mm) to about 1 inch (25.4 mm) of molten material within the mold cavity 19 at any given time. In some embodiments, the mushy zone between the molten metal and solidified metal may also be kept at a substantially uniform thickness.
In a further embodiment, the metal source (1), degasser (16), filter (12), and casting apparatus (14) are connected by feed troughs.
In yet another embodiment, the metal source (1) is a furnace-reservoir.
In a further embodiment, the metal sources (1, 2), degassers (16), filters (12), and casting apparatus (14) are connected by feed troughs.
In yet another embodiment, the metal sources (1, 2) are furnace-reservoirs.
In a further embodiment, the metal sources (1, 2), degasser (16), filter (12), and casting apparatus (14) are connected by feed troughs.
In yet another embodiment, the metal sources (1, 2) are furnace-reservoirs.
Although the embodiments described in
In one embodiment, and with reference to
In one embodiment, and with reference to
In one embodiment, and with reference to
Although the methods of producing ingot have been described in detail with reference to several embodiments, additional variations and modifications exist within the scope and spirit of the disclosure.
This application claims priority to U.S. Provisional Patent Application Ser. No. 61/180,391 filed May 21, 2009, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61180391 | May 2009 | US |