The present invention relates to a method of producing a pneumatic tire. More specifically, the present invention relates to a method of producing a pneumatic tire, the method improving the uniformity and durability of the tire and preventing occurrence of blisters which caused by trapped air, when a thermoplastic resin film is used as an air permeation prevention layer. Particularly, the present invention relates to a method of producing a pneumatic tire suitable for use as a heavy-duty tire.
In a tubeless pneumatic tire, the inner surface of the tire is lined integrally with an air permeation prevention layer (an inner liner), and a butyl rubber excellent in air non-permeability is used as a material for the air permeation prevention layer. However, although there is an increasing demand for a reduction in weight of pneumatic tires, it has been difficult to achieve the reduction in weight when using the butyl rubber because the butyl rubber has a large specific gravity. In this respect, Patent Document 1 proposes the use of a thermoplastic resin film having a small specific gravity as an air permeation prevention layer instead of such butyl rubber so as to enable the reduction in weight of a pneumatic tire.
However, the thermoplastic resin film has no such air absorbability as the butyl rubber has. For this reason, a problem arises in that, if air is trapped in an uncured tire in the forming of the uncured tire, the trapped air leads to occurrence of blisters in an inner surface of the thermoplastic resin film after a curing process.
A green tire before a curing process is formed as follows. A cylindrical thermoplastic resin film 6 is first wrapped around a making drum 20 as shown in Part 5A of
Particularly, consider a case of tires, such as heavy-duty tires, in which a carcass lifting caused during a curing process is so large that an inner liner is likely to bite into carcass cords constituting a carcass layer. In this case, because a tie-rubber sheet needs to be formed with a large thickness in order to prevent the biting, such tires have a problem that the aforementioned failure due to the lap splice of the tie-rubber sheet is more likely to occur. Patent Document 1: Japanese patent application Kokai publication No. Hei 8-258506
An object of the present invention is to provide a method of producing a pneumatic tire, the method improving the uniformity and durability of the tire and preventing occurrence of blisters caused by trapped air, when a thermoplastic resin film is used as an air permeation prevention layer, and particularly, the present invention relates to a method suitable for producing a heavy-duty pneumatic tire.
A method of producing a pneumatic tire according to the present invention for achieving the above-described object includes: wrapping a thermoplastic resin film around a making drum; winding an unvulcanized tie-rubber sheet on the thermoplastic resin film; splicing a winding start portion and a winding end portion of the tie-rubber sheet with each other; and thereafter winding a carcass layer on the tie-rubber sheet. The method is characterized in that a splice of the tie-rubber sheet is made to be a butt-splice, and an unvulcanized auxiliary rubber sheet is interposed between the tie-rubber sheet and the thermoplastic resin film, along a joint of the butt-splice.
The method of producing a pneumatic tire according to the present invention provides the following effects. In the method, when the tie-rubber sheet is wound on the thermoplastic resin film and the end portions of the tie-rubber sheet are spliced, the splice of the end portions of the tie-rubber sheet is made to be the butt-splice. Accordingly, no step is formed, so that the size of a void of trapped air is reduced to the minimum, thus preventing occurrence of blisters. This makes it possible to solve a problem of a reduction in durability of the tire which is caused by an event that the thermoplastic resin film is locally thinned by stress concentration, and also to improve the uniformity of the tire. Moreover, in the method, the unvulcanized auxiliary rubber sheet is interposed between the joint of the butt-splice of tie-rubber sheet and the thermoplastic resin film. Accordingly, the auxiliary rubber sheet prevents the joint from opening, and also absorbs air even if a void is formed at the joint, thus eliminating occurrence of blisters.
In
In the present invention, in the method of producing a pneumatic tire having the above-described structure, a green tire before a curing process is formed as follows. As shown in Part 2A of
In the method of winding the tie-rubber sheet 7 shown as an example in
In the butt-splicing of the tie-rubber sheet 7, if the tie-rubber sheet 7 has been cut to have a circumferential length that coincides with the circumferential length of the thermoplastic resin film 6 with the thickness of the auxiliary rubber sheet 9 taken into account, a void of trapped air is scarcely formed in the butt-spliced portion. In actual practice, however, the circumferential length of the tie-rubber sheet 7 may vary due to a dimensional error at the time of cutting both end portions thereof. Moreover, the tie-rubber sheet itself may extend because stitching is performed on the joint in order to press and bond the end surfaces of the tie-rubber sheet to each other at the butt-splicing process, or because the tie-rubber sheet is hauled for the butt-splicing. Since the joint 7c is forced to thrust up as shown in
In the present invention, stitching is preferably performed on an upper portion of the butt-spliced portion after the tie-rubber sheet is wound and butt-spliced. The stitching makes it possible to further reduce in size or even almost eliminate the void. After the tie-rubber sheet is wound, a carcass layer is wound therearound according to an ordinary method in the same manner as the conventional case. Then, bead cores are fitted thereon, and then, side rubbers are wound therearound to form a first green tire. Further, a tread rubber is wound around the outer periphery of the first green tire so as to form a second green tire. The second green tire is cured in the curing process, so that a product tire is produced.
In the present invention, the splice of the tie-rubber sheet is made to be the butt-splice as described above, so that no step is formed in the spliced portion. Accordingly, since a void of trapped air is small in size or is hardly formed, occurrence of blisters can be prevented. In addition, since no step is formed, it is possible to avoid the thinning of the thermoplastic resin film in a vicinity of the spliced portion due to stress concentration caused by the lifting up during the curing process, and also to prevent the uniformity of the tire from being deteriorated. Moreover, interposing the auxiliary rubber sheet between the thermoplastic resin film and the joint of the butt-splice prevents the joint from opening, and also prevents occurrence of blisters because the auxiliary rubber sheet absorbs air even when a void of trapped air is formed.
In the present invention, the thickness (tg) of the tie-rubber sheet is preferably in a range from 1.0 mm to 4.0 mm, and more preferably 1.2 mm to 3.5 mm. In particular, if the thickness (tg) of the tie-rubber sheet is set at 1.2 mm or more, the thermoplastic resin film can be prevented from biting into carcass cords of the carcass layer during the curing process even in a heavy-duty tire. Moreover, the angle of an edge surface of the tie-rubber sheet to the thickness direction thereof is preferably in a range of ±5°. Setting the angle of the edge surface in such a range makes it possible to further enhance the effect obtained by the interposing of the auxiliary rubber sheet.
The thickness (tm) of the auxiliary rubber sheet is preferably in a range from 0.1 mm to 0.5 mm, and more preferably in a range from 0.2 mm to 0.4 mm. Setting the thickness (tm) of the auxiliary rubber sheet at 0.1 mm or more makes it possible to sufficiently obtain the effect of absorbing air during the curing process, thereby securing the reinforcement of the joint. Setting the thickness (tm) of the auxiliary rubber sheet at 0.5 mm or less makes it possible to reduce the amount of air trapped due to the step on the end portion of the auxiliary rubber sheet and thus to prevent occurrence of blisters, thereby reducing an influence on the weight and uniformity of the tire.
The circumferential length (L) of the auxiliary rubber sheet is preferably in a range from 10 mm to 20 mm. Setting the circumferential length (L) of the auxiliary rubber sheet at 10 mm or more makes it possible to sufficiently obtain the effect of absorbing air during the curing process and the effect of preventing the opening failure of the joint of the tie-rubber sheet. Setting the circumferential length (L) of the auxiliary rubber sheet at 20 mm or less makes it possible to suppress an increase in weight of the tire.
The rubber composition constituting the auxiliary rubber sheet may be the same as or different from that of the tie-rubber sheet, and is not particularly limited as long as being any of those conventionally used as tire materials. For example, the rubber composition used for the auxiliary rubber sheet may be one formed by adding a compounding ingredient such as carbon black, a process oil, or a curing agent to a diene rubber, such as NR, IR, BR, or SBR; an ethylene-propylene copolymer rubber; styrene elastomer; or the like.
The rubber composition constituting the auxiliary rubber sheet preferably includes short fibers, which can enhance the effect of reinforcing the joint of the tie-rubber sheet. The amount of short fibers to be compounded is preferably in a range from 0.1 to 2.0 parts by weight per 100 parts by weight of the rubber component. Setting the amount of short fibers to be compounded in such range makes it possible to further enhance the reinforcement of the interface of the joint. The kind of short fibers is not particularly limited, and at least one of organic fibers and inorganic fibers may be used.
The thermoplastic resin film is preferably a single-layer or multi-layer cylindrical thermoplastic resin film prepared from a thermoplastic resin composition by a general extrusion molding, for example, by an inflation molding. The resin for the thermoplastic resin film is not particularly limited as long as can be subjected to a melt molding. The thermoplastic resin film is preferably made of, for example, a thermoplastic resin, such as a polyamide resin, a polyester resin, a polynitrile resin, a polymethacrylate resin, or a polyvinyl resin; a copolymer composed mainly of one of those resins; or a resin composition containing one of these resin components as a main component. The resin composition is preferably a thermoplastic resin composition containing one of the above thermoplastic resins as a matrix and any elastomer component as a domain. Such elastomer is preferably an olefin elastomer, a styrene elastomer, or the like.
The method of producing a pneumatic tire according to the present invention exhibits its effects particularly in the production of a heavy-duty tire that requires a thick tie-rubber sheet. The method according to the present invention makes it possible to join both end portions of the tie-rubber sheet to each other by the butt-splicing method which has heretofore not been able to be employed, and is useful for a prevention of an opening failure of a butting portion and for a reduction of
Hereinafter, the present invention will be described by giving examples; however, the scope of the present invention is not limited by these examples.
Four types of green tires (Examples 1 and 2, Conventional Example, and Comparative Example) each having a tire size of 11R22.5 and a tire structure shown in
The same rubber composition as that of the tie-rubber sheet was used for constituting the auxiliary rubber sheet. The rubber composition used in Example 2 was one in which 1.0 part by weight of vinylon short fiber is compounded per 100 parts by weight of the rubber component.
Each of the green tires of these four types was cured. Then, the weight of the tire, as well as, blisters, whether or not the tie-rubber sheet was opened, a variation in liner gauge, and the uniformity, after the curing process, were evaluated by the following methods.
Whether or not blisters had occurred was visually checked in the inner surface of a pneumatic tire obtained by curing the green tire of each type.
A pneumatic tire obtained by curing the green tire of each type was disassembled, and whether or not an opening had occurred at the joint in the spliced portion of the tie-rubber sheet was visually checked.
A pneumatic tire obtained by curing the green tire of each type was disassembled, and the thickness of a thinned part of the thermoplastic resin film in a vicinity of the spliced portion of the tie-rubber sheet was measured. Then, the pneumatic tires were evaluated by indices where the thickness of the thermoplastic resin film in a region having a uniform thickness was taken as 100. The closer to 100 the index is, the smaller the variation in liner gauge is.
The RFV of the pneumatic tire obtained by curing the green tire of each type was measured according to JASO C607. Then, the pneumatic tires were evaluated by indices where the measured value of the tire of Conventional Example was taken as 100. The smaller the index is, the more excellent the pneumatic tire is in the uniformity.
The pneumatic tire of Comparative Example was not able to be evaluated in the variation in liner gauge because an opening had occurred at the joint of the tie-rubber sheet during the curing process.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-146631 | May 2006 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2007/060400 | 5/22/2007 | WO | 00 | 11/14/2008 |