The present invention relates to a method of producing a roll of a laminate strip with a polarizing film. In particular, the present invention relates to a method of producing a roll of a laminate strip formed from an optical film laminate including a polarizing film which consists of a polyvinyl alcohol type resin with a molecularly oriented dichroic material, and has a thickness of 10 μm or less.
There has been widely known a method in which a single layer of a polyvinyl alcohol type resin (hereinafter referred to as “PVA type resin”) formed in a film shape is subjected to dyeing and stretching to produce a polarizing film comprising a PVA type resin layer, wherein molecules of the PVA type resin are oriented in the direction of stretching, and a dichroic material is absorbed (impregnated) in the PVA type resin in a molecularly oriented state. The thickness of a polarizing film to be obtained by the above conventional method using a PVA type resin single-layer film is in the range of about 15 to 35 μm. The conventional method makes it possible to obtain a polarizing film having optical characteristics of a single layer transmittance of 42% or more, and a polarization rate of 99.95% or more. Currently, polarizing films produced by the conventional method are used in optical display devices for televisions, mobile phones, personal digital assistants, and other appliances.
However, since the PVA type resins are hydrophilic and highly hygroscopic, a polarizing film produced using a PVA type resin is sensitive to changes in temperature and humidity, and more likely to expand and contract due to changes in surrounding environments, which is liable to cause the occurrence of crack. Moreover, the expansion and contraction caused by environmental changes during use will produce stress in an adjacent member to which the polarizer film is joined, and thereby cause deformation, such as warp, in the adjacent member.
Thus, in order to suppress expansion and contraction of a polarizer film to reduce the impact of temperature and humidity, it is usual to employ, as a polarizing film for televisions, an optical film laminate prepared by laminating a triacetylcellulose (TAC) film having a thickness of 40 to 80 μm and serving as a protection film, on each of opposite surfaces of a polarizing film. However, even in such a structure, in cases where a single-layer polarizing film is used therein, there is a limit to thinning of the polarizing film. Thus, expansion and contraction forces of the polarizing film become unignorable, and it is difficult to completely suppress the influence of expansion and contraction of the polarizing film, so that a certain level of expansion and contraction will inevitably occur in the optical film laminate including the polarizing film. If expansion or contraction occurs in such an optical film laminate including a polarizing film, stress arising from the expansion or contraction will cause deformation, such as warp, in an adjacent member. This deformation, even if it is small, leads to the occurrence of non-uniformity of display in a liquid-crystal display device. Thus, in order to suppress the occurrence of non-uniformity of display, it is necessary to make design considerations, for example, to carefully select the material for each member to be used in the optical film laminate including the polarizing film. Further, the contraction stress of the polarizing film will cause peeling or the like of the optical film laminate from a liquid-crystal panel. Thus, a high-adhesion adhesive is required to join the optical film laminate to the liquid-crystal display panel. However, the use of such a high-adhesion adhesive gives rise to a problem of difficulty in re-working which is an operation of, when the presence of an optical defect is found in a polarizing film of an optical film laminate laminated to a liquid-crystal display panel through a subsequent inspection, peeling the optical film laminate from the liquid-crystal display panel and laminating another optical film laminate to the liquid-crystal display panel. This is a technical problem in a polarizing film to be obtained by the conventional method using a PVA type resin single-layer formed in a film shape.
Thus, there is a need for a new polarizing film production method, as an alternative to the conventional polarizing film production method using a PVA type resin single-layer, and being incapable of achieving a sufficient level of thinning of a polarizing film due to the above problem. Specifically, it is virtually impossible to produce a polarizing film having a thickness of 10 μm or less by the conventional method using a PVA type resin single-layer formed in a film shape. This is because, in producing a polarizing film using a film-shaped PVA type resin single-layer, if a thickness of the PVA type resin single-layer is excessively reduced, dissolution and/or breaking is likely to occur in a PVA type resin layer in a dyeing step and/or a stretching step, which makes it impossible to form a polarizing film having a uniform thickness.
In order to cope with this problem, there has been proposed a method designed such that a PVA type resin layer is applied and formed on a thermoplastic resin substrate, and the PVA type resin layer formed on the resin substrate is stretched together with the resin substrate, and subjected to dyeing, so as to produce a polarizing film significantly thinner than the polarizing film obtained by the conventional method. This polarizing film production method using a thermoplastic resin substrate is noteworthy in that it provides a possibility of producing a polarizing film more uniformly than the polarizing film production method using a PVA type resin single-layer.
For example, Japanese Patent JP 4279944B (Patent Document 1) discloses a polarizing plate production method which comprises steps of forming a polyvinyl alcohol resin layer having a thickness of 6 μm to 30 μm, on one of opposite surfaces of a thermoplastic resin film by a coating process, stretching the polyvinyl alcohol resin layer at a stretching ratio of 2 to 5 in such a manner that the polyvinyl alcohol resin layer is formed as a transparent coating element layer to thereby form a composite film consisting of two layers including the thermoplastic resin film and the transparent coating element layer, laminating an optical transparent resin film layer on the side of the transparent coating element layer of the composite film consisting of the two layers, through a bonding agent, peeling and removing the thermoplastic resin film, and dyeing and fixing the transparent coating element layer in such a manner that the transparent coating element layer is formed as a polarizing element layer. A polarizing plate to be obtained by this method has a two-layer structure consisting of the optical transparent resin film layer and the polarizing element layer. According to the description of the Patent Document 1, the polarizing element has a thickness of 2 to 4 μm.
The method disclosed in the Patent Document 1 is designed to perform stretching under an elevated temperature by a uniaxial stretching process, wherein the stretching ratio is restricted to the range of 2 to 5, as mentioned above. As for the reason why the stretching ratio is restricted to 5 or less, the Patent Document 1 explains that stretching at a high stretching ratio of greater than 5 makes it extremely difficult to maintain stable production. Specifically, there is described that the atmospheric temperature during stretching is set to 55° C. in cases where ethylene-vinyl acetate copolymer is used as the thermoplastic resin film, to 60° C. in cases where non-stretched polypropylene is used as the thermoplastic resin film, or to 70° C. in cases where non-stretched nylon is used as the thermoplastic resin film. The method disclosed in the Patent Document 1 employs a uniaxial stretching process in air under an elevated temperature. Further, as described in the Patent Document 1, the stretching ratio is restricted to 5 or less. Thus, a polarizing film having an extremely small thickness of 2 to 4 μm, to be obtained by this method, is not enough to satisfy optical characteristics desired for a polarizing film to be used, for example, in an optical display device such as a liquid-crystal television, or an optical display device using an organic EL display element.
The method of forming a polarizing film with steps of forming a PVA type resin layer on a thermoplastic resin substrate by a coating process, and stretching the PVA type resin layer together with the substrate is also disclosed in Japanese Patent Laid-Open Publication JP 2001-343521A (Patent Document 2) and Japanese Patent Laid-Open Publication JP 2003-043257A (Patent Document 3). The methods disclosed in the Patent Documents 2 and 3 are designed such that a laminate consisting of a thermoplastic resin substrate and a PVA type resin layer applied on the substrate is subjected to uniaxial stretching at a temperature of 70° C. to 120° C., in cases where the substrate is made of a non-crystallizable polyester resin. Then, the PVA type resin layer molecularly oriented by the stretching is subjected to dyeing to allow a dichroic material to be impregnated therein. In the Patent Document 2, there is described that the uniaxial stretching may be longitudinal uniaxial stretching or may be transverse uniaxial stretching. Differently, in the Patent Document 3, a method is described in which transverse uniaxial stretching is performed, and, during or after the transverse uniaxial stretching, contracting the length in a direction perpendicular to a direction of the stretching by a specific amount. In both of the Patent Documents 2 and 3, there is described that the stretching ratio is typically set to about 4 to 8. Further, there is described that the thickness of a polarizing film to be obtained is in the range of 1 to 1.6 μm.
In the Patent Documents 2 and 3, although there is described that the stretching ratio is typically set to 4 to 8, since the Patent Documents 2 and 3 adopt an elevated temperature in-air stretching process, it is considered that the stretching ratio will be limited to 5 as described, for example, in the Patent Document 1. None of the Patent Documents 2 and 3 describes a specific technique for achieving a stretching ratio of greater than 5 by the elevated temperature in-air stretching process. In fact, in Examples described in the Patent Documents 2 and 3, only a stretching ratio of 5 and a stretching ratio of 4.5 are described, respectively, in the Patent Document 2 and the Patent Document 3. Through additional tests on the methods disclosed in the Patent Documents 2 and 3, the inventors of the present invention have ascertained that it is impossible to adequately perform stretching at a stretching ratio of greater than 5 by the methods disclosed therein. Therefore, it should be understood that only a stretching ratio of 5 or less is substantially disclosed in the Patent Documents 2 and 3. As with the Patent Document 1, the polarizing film to be obtained by the method disclosed in each of the Patent Documents 2 and 3 is not enough to satisfy optical characteristics desired for a polarizing film to be used, for example, in an optical display device such as a liquid-crystal television.
U.S. Pat. No. 4,659,523 (Patent Document 4) discloses a polarizing film production method which comprises subjecting a PVA type resin layer coated on a polyester film to uniaxial stretching together with the polyester film. This method disclosed in the Patent Document 4 is intended to form the polyester film serving as a substrate of the PVA type resin layer in such a manner as to have optical characteristics allowing the polyester film to be used together with a polarizing film, but it is not intended to produce a polarizing film comprising a PVA type resin layer and having a small thickness and excellent optical characteristic. Specifically, the method disclosed in the Patent Document 4 is no more than a technique of improving optical characteristics of a polyester resin film to be stretched together with a PVA type resin layer to be formed as a polarizing film. A polarizer material production method having the same object is also disclosed in Japanese Patent Publication JP 08-012296B (Patent Document 5).
As disclosed in the Patent Documents 1 to 5, a method has already been known in which a PVA type resin layer is formed on a thermoplastic resin substrate by a coating process, and the PVA type resin layer is stretched together with the thermoplastic resin substrate to produce a thin polarizing film. However, it has not been realized to obtain a highly-functional polarizing film usable in a display device satisfying the optical characteristics of a contrast ratio of 1000:1 or more, and a maximum luminance (brightness) of 500 cd/m2 or more, which are required for a display device, typically, for liquid-crystal televisions, or a polarizing film having optical characteristics usable in an optical display device using an organic EL display element.
Through extensive efforts, the inventors have successfully developed an optical display device comprising a polarizing film which has a significantly small thickness as compared with conventional polarizing films and exhibits required optical characteristics. It is therefore an object of the present invention to provide a method of, using the newly developed polarizing film, producing a roll of a laminate strip with a polarizing film, which is suitable for production of optical display devices.
The inventors have successfully obtained a novel polarizing film by stretching a non-crystallizable ester type thermoplastic resin substrate and a PVA type resin layer applied to and formed on the substrate together through a 2-stage stretching step consisting of preliminary in-air stretching and in-boric-acid-solution stretching, and subjecting the PVA type resin layer to dyeing using a dichroic dyeing material, wherein the polarizing film has a thickness of 10 μm or less, and optical characteristics of the polarizing film represented by a single layer transmittance T and a polarization rate P can satisfy characteristics required for polarizing films for use in optical display devices.
The present invention provides a method of producing a roll of an optical film laminate using such a polarizing film. The method for producing the optical film laminate may comprise steps of forming a continuous web of optical film laminate including a polarizing film which consists of a polyvinyl alcohol type resin layer and has a thickness of 10 μm or less and an absorption axis in a lengthwise direction of the optical film laminate, subjecting the laminate to a 2-stage stretching consisting of a preliminary in-air stretching and an in-boric-acid-solution stretching, to carry out a uniaxial stretching to a stretching ratio of 5 to 8.5 to thereby reduce the thickness of the polyvinyl alcohol type resin layer to 10 μm or less, and impregnating a dichroic material in the polyvinyl alcohol type resin layer. The method further comprises the steps of: cutting the continuous web of optical film laminate along a direction parallel to the lengthwise direction to form at least one continuous web of laminate strip having a given width; and winding the continuous web of laminate strip having the given width into a roll.
The method of the present invention may further comprise a step of, after the step of forming a continuous web of optical film laminate, winding the optical film laminate into a roll to form a roll of the optical film laminate, wherein after the step of winding the optical film laminate, the step of cutting is performed while unrolling the optical film laminate from the roll of the optical film laminate. Further, in the method of the present invention, a plurality of continuous webs of laminate strips having given widths may be formed through the step of cutting. In this case, each of the plurality of continuous webs of laminate strips may have a different given width, or may have the same given width.
Preferably, in the method of the present invention, in a state before the stretching sub-step, the thermoplastic resin substrate has a thickness which is six times or more the thickness of the polyvinyl alcohol type resin layer formed on the substrate. The thermoplastic resin substrate is preferably made of a transparent ester type resin.
In a preferred embodiment of the present invention, the polarizing film is formed to have optical characteristics satisfying the following conditions:
P>−(100.929T-42.4−1)×100 (where T<42.3); and
P≧99.9 (where T≧42.3)
wherein T is a single layer transmittance, and P is a polarization rate.
In another preferred embodiment of the present invention, the polarizing film is formed to have optical characteristics satisfying the following conditions:
T≧42.5; and
P≧99.5
wherein T is a single layer transmittance, and P is a polarization rate.
Preferably, in the method of the present invention, a stretching ratio during the preliminary in-air stretching is 3.5 or less. The impregnation of the dichroic material may be performed by immersing the polyvinyl alcohol type resin layer in a dyeing solution containing iodine in a water solvent in an iodine concentration ranging from 0.12 to 0.30 weight %. The method of the present invention may further include a step of cleaning the optical film laminate by a cleaning solution containing an iodide salt at a solution temperature not higher than 40° C. The method of the present invention may further include a step of laminating a separator film on a surface of the polarizing film on a side opposite to the thermoplastic resin substrate, through an adhesive. Alternatively, the method of the present invention may further include a step of laminating an optically functional film on the surface of the polarizing film opposite to the thermoplastic resin substrate, through a bonding agent. In this case, the method may further include a step of laminating a separator film on a surface of the optically functional film at a side opposite to the polarizing film, through an adhesive. Further, the optically functional film may be a biaxial phase difference film having a three-dimensional refractive index, in which refractive indexes in triaxial directions have the relation of nx>ny>nz. The separator film may be preliminarily subjected to a treatment have an adhesion force to the adhesive layer weaker than an adhesion force of the polarizing film or the optically functional film to the adhesive layer. In this case, when the separator film is peeled, the adhesive layer will be left on the side of the polarizing film or the optically functional film.
The method of the present invention may include a step of, before the step of winding the continuous web of laminate strip having the given-width into a roll, subjecting the optical film laminate to defect inspection, and, if a defect is detected, recording the position of the defect. The recording may be performed by applying a mark on the optical film laminate. Alternatively, the recording may be performed by storing defect information including at least positional information about the defect, in a recording medium. In this case, the recording is performed by storing the defect information including at least positional information about the defect, in the recording medium, together with roll identification information for identifying the roll of the continuous web of laminate strip.
As desired characteristics of a polarizing film when it is used in an optical display device such as a liquid-crystal television, the inventors have set conditions represented by the following formulas:
P>−(100.929T-42.4−1)×100 (where T<42.3); and
P≧99.9 (where T≧42.3)
wherein T is a single layer transmittance, and P is a polarization rate.
Differently from the liquid-crystal display device, an organic EL display device typically has a structure using a single polarizing film. Thus, optical characteristics required for such a polarizing film becomes different from optical characteristics required for the polarizing film for use in the liquid-crystal display device. As for the optical characteristics required for the polarizing film for use in the organic EL display device, the inventers have set conditions represented by the following formulas:
T≧42.5; and
P≧99.5
wherein T is a single layer transmittance, and P is a polarization rate.
The present invention makes it possible to realize a polarizing film having a thickness of 10 μm or less and exhibiting optical characteristics represented in terms of the single layer transmittance T and the polarization rate P satisfying the above conditions. In a preferred embodiment, the present invention provides a production method for a roll of an optical film laminate strip including a polarizing film having such desired optical characteristics.
The present invention makes it possible to obtain a roll of an optical film laminate strip using a polarizing film having a thickness which is significantly thin as compared to that of a conventional polarizing film while exhibiting required optical characteristics, e.g., a polarizing film which consists of a polyvinyl alcohol type resin layer with a molecularly oriented dichroic material and has a thickness of 10 μm or less and required optical characteristics.
As mentioned above, any case of using a thermoplastic resin substrate and subjecting a PVA type resin layer formed on the substrate to uniaxial stretching to attain a stretching ratio of 5 or more cannot be found in prior art documents.
Representative examples of a polarizing film production method which may be used in the present invention, and a method of producing a roll of an optical film laminate strip, according to preferred embodiments of the present invention, will be specifically described below with reference to the accompanying drawings.
la is a sectional view illustrating an example of an organic EL display device using an optical film laminate according to the present invention.
b is a sectional view illustrating another example of the organic EL display device using the optical film laminate according to the present invention.
As the background art of polarizing films, descriptions will be made on optical characteristics represented by material characteristics of a thermoplastic resin substrate to be used in the present invention and polarization performance of a polarizing film.
Firstly, descriptions will be made briefly on general material characteristics of a thermoplastic resin suitable for use in the present invention.
Thermoplastic resins are roughly classified into two types, one being the type which is in a state in which polymer molecules are orderly oriented, and the other being the type which is in a state in which molecules are not orderly oriented or only a small portion of polymer molecules are orderly oriented. The former is called “crystallized state”, and the latter is called “amorphous or non-crystallized state. Correspondingly, one type of thermoplastic resin having a property capable of being transformed from a non-crystallized state into a crystallized state depending on conditions is called “crystallizable resin”, and the other type of thermoplastic resin which does not have such a property is called “non-crystallizable resin”. On the other hand, regardless of whether a crystallizable resin or a non-crystallizable resin, a resin which is not in a crystallized state or has not been transformed into a crystallized state, is called “amorphous or non-crystalline resin”. The term “amorphous or non-crystalline” will be used herein in distinction from the term “non-crystallizable” which means a property incapable of transformation into a crystallized state.
For example, the crystallizable resin may include olefin type resins such as polyethylene (PE) and polypropylene (PP), and ester type resins such as polyethylene terephthalate (PET) and polybutylene terephthalate (PBT). One feature of the crystallizable resin is that, based on heating and/or stretching/orienting, polymer molecules are orderly arranged, and crystallization is progressed. Physical properties of the resin vary according to the degree of crystallization. On the other hand, even in the crystallizable resin, such as polypropylene (PP) or polyethylene terephthalate (PET), it is possible to suppress crystallization by inhibiting polymer molecules from being orderly oriented which may otherwise be caused by heating or stretching/orienting. Such crystallization-inhibited polypropylene (PP) and polyethylene terephthalate (PET) will hereinafter be referred respectively as “non-crystallizable polypropylene” and “non-crystallizable polyethylene terephthalate”, and collectively referred as “non-crystallizable olefin type resin” and “non-crystallizable ester type resin”, respectively.
For example, in the case of polypropylene (PP), the resin may be made to have an atactic structure having no stereoscopic regularity to thereby produce a crystallization-inhibited non-crystallizable polypropylene (PP). Further, for example, in the case of polyethylene terephthalate (PET), it is possible to produce a crystallization-inhibited non-crystallizable polyethylene terephthalate (PET) by copolymerizing isophthalic acid or a modifier group such as 1,4-cyclohexanedimethanol, as a polymerizing monomer, or by copolymerizing a molecule which inhibits crystallization of polyethylene terephthalate (PET).
Secondly, brief description will be made on optical characteristics of a polarizing film usable in a large-sized liquid-crystal display element.
Basically, the term “optical characteristic” of a polarizing film is used herein to mean a polarization performance represented by a polarization rate P and a single layer transmittance T. In general, the polarization rate P and the single layer transmittance T of a polarizing film are in a trade-off relationship. The two optical characteristic values can be expressed by a T-P graph. In the T-P graph, it can be interpreted that a polarizing film has a better polarization performance if a plotted line for the polarizing film is located on a higher side in terms of the single layer transmittance and on a higher side in terms of the polarization rate.
Referring to
On the other hand, the polarization rate P can be converted to a contrast ratio (CR) of a polarizing film. For example, a polarization rate P of 99.95% corresponds to a contrast ratio of a polarizing film of 2000:1. In a display device prepared by using this polarizing film in each of opposite sides of a liquid-crystal display panel for a liquid-crystal television, the contrast ratio will be 1050:1. As above, the contrast ratio of the display device is less than that of the polarizing film, because depolarization occurs within the display panel. The depolarization occurs because of a phenomenon wherein, when light transmitted through the polarizing film on a backlight side transmits through the display panel, the light is scattered and/or reflected by pigments in a color filter, a liquid-crystal molecule layer and a thin-film transistor (TFT), so that the polarization state of a part of the light is changed. As the contrast ratio of each of the polarizing film and the display panel becomes larger, the liquid-crystal television has better contrast and better visibility.
Meanwhile, the contrast ratio of a polarizing film is defined as a value obtained by dividing a parallel transmittance (Tp) by a cross transmittance (Tc). On the other hand, the contrast ratio of a display device is defined as a value obtained by dividing a maximum luminance by a minimum luminance. The minimum luminance is a luminance in a black screen. In a liquid-crystal television designed assuming a typical viewing environment, the minimum luminance is set to 0.5 cd/m2 or less as a reference required value. If the minimum luminance is greater than this value, color reproducibility will be deteriorated. The maximum luminance is a luminance in a white screen. In a liquid-crystal television designed for a typical viewing environment, a display having a maximum luminance ranging from 450 to 550 cd/m2 is used. If the maximum luminance is less than this range, visibility of the liquid-crystal television will be decreased because display becomes dark.
Performance required for a display device of a liquid-crystal television using a large-sized display element includes a display contrast ratio of 1000:1 or more and a maximum luminance of 500 cd/m2 or more. This may be considered as a “required performance”. The line 1 (T<42.3%) and the line 2 (T≧42.3%) in
The contrast ratio and the maximum luminance of a display device for a liquid-crystal television can be calculated based on a light intensity of a light source (backlight), transmittances of two polarizing films disposed on backlight and viewing sides, a transmittance of a liquid-crystal display panel, polarization rates of the two backlight-side and viewing-side polarizing films, and a depolarization rate of the liquid-crystal display panel. The lines 1 and 2 in
Formula (1) is used for deriving the contrast ratio of a display device. Formula (2) is used for deriving the maximum luminance of the display device. Formula (3) is used for deriving a dichroic ratio of a polarizing film.
CRD=Lmax/Lmin, Formula (1)
Lmax=(LB×Tp−(LB/2×k1B×DP/100)/2×(k1F−k2F))×Tcell/100, Formula (2)
and
DR=A
k2
/A
k1=log(k2)/log(k1)=log(Ts/100×(1−P/100)/TPVA)/log(Ts/100×(1+P/100)/TPVA), Formula (3)
where:
Lmin=(LB×Tc+(LB/2×k1B×DP/100)/2×(k1F−k2F))×Tcell/100;
Tp=(k1B×k1F+k2B×k2F)/2×TPVA;
Tc=(k1B×k2F+k2B×k1F)/2×TPVA;
k1=Ts/100×(1+P/100)/TPVA; and
k2=Ts/100×(1−P/100)/TPVA,
wherein:
The line 1 in
On the other hand, although the polarizing film A (T=40.6%, P=99.998%), the polarizing film B (T=41.1%, P=99.994%) and the polarizing film C (T=41.6%, P=99.98%) also belong to the group 3, they are located in a region having a lower single layer transmittance (darker). Thus, if one of these polarizing films is used on each of the backlight and viewing sides, the required performance cannot be satisfied. In cases where one of the polarizing films A, B and C is used on either one of the backlight and viewing sides, in order to achieve the required performance, it is necessary to use, as a polarizing film to be used on the other side, a polarizing film having a single layer transmittance greater than that of the polarizing films in the group 3 and excellent polarization performance, specifically, at least a polarization rate of 99.9% or more, such as the polarizing film E in the group 4, the polarizing film F in the group 5 or the polarizing film G in the group 7.
Respective polarization performances of the polarizing films belonging to the groups 1 to 7 are calculated in accordance with the Formula (3). The Formula (3) can be used to calculate the single layer transmittance T and the polarization rate P based on the dichroic ratio (DR) serving as an index of polarization performance of a polarizing film. The term “dichroic ratio” means a value obtained by dividing an absorbance in a direction of an absorption axis of a polarizing film by an absorbance in a direction of a transmission axis thereof. A higher value of the dichroic ratio indicates better polarization performance. For example, each polarizing film in the group 3 is calculated as a polarizing film having polarization performance in which the dichroic ratio is about 94. This means that any polarizing film having a dichroic ratio of less than this value does not achieve the required performance.
Further, in cases where a polarizing film having polarization performance inferior to those of the polarizing films in the group 3, such as the polarizing film H (41.0%, 99.95%) in the group 1 or the polarizing film J (42.0%, 99.9%) in the group 2, is used on either one of the backlight and viewing sides, in order to achieve the required performance, it is necessary to use, as a polarizing film to be used on the other side, a polarizing film having polarization performance better than those of the polarizing films in the group 3, such as the polarizing film I (43.2%, 99.95%) in the group 6 or the polarizing film K (42.0%, 99.998%) in the group 7, as is clear from the Formulas (1) and (2)
In order to achieve the required performance of a display device for a liquid-crystal television, the polarization performance of either one of the backlight-side and viewing-side polarizing films has to be better than those of the polarizing films in the group 3. The line 1 (T<42.3%) in
In conclusion, a desired condition for achieving polarization performance required for a display device of a liquid-crystal television using a large-sized display element is that either one of the backlight-side and viewing-side polarizing films has a polarization performance better than that of the polarizing film in a region beyond at least the threshold represented by the line 1 (T<42.3%) and the line 2 (T≧42.3%), more specifically, a polarization performance better than those of the polarizing films in the group 3, and a polarization rate of 99.9% or more.
A polarizing film for use in an organic EL display device is often utilized for blocking internally reflected light, in such a manner that it is combined mainly with a ¼ wavelength phase difference film to form circularly-polarized light. In this case, a single polarizing film is used. Thus, as mentioned above, optical characteristics required for the polarizing film to be used in the organic EL display device becomes different from that of the transmissive liquid-crystal display device using two polarizing films. Specifically, it is required to meet the following conditions: single layer transmittance T≧42.5, and polarization rate P≧99.5. The required performance of the polarizing film for use in the organic EL display device is indicated by the one-dot chain line in
Examples 1 to 18 will be described as specific examples of a polarizing film for use in an optical film laminate, according to the present invention.
A continuous web of substrate was prepared as a non-crystallizable ester type thermoplastic resin substrate comprising isophthalic acid-copolymerized polyethylene terephthalate copolymerized with 6 mol % of isophthalic acid (hereinafter referred to as “non-crystallizable PET”). The non-crystallizable PET has a glass transition temperature of 75° C. A laminate comprising the continuous web of non-crystallizable PET substrate and a polyvinyl alcohol (hereinafter referred to as “PVA”) layer was prepared in the following manner. By the way, PVA has a glass transition temperature of 80° C.
A non-crystallizable PET substrate having a thickness of 200 nm was prepared, and a PVA aqueous solution having a PVA concentration of 4 to 5 wt % was also prepared by dissolving a PVA powder having a polymerization degree of 1000 or more and a saponification degree of 99% or more in water. Then, the PVA aqueous solution was applied to the 200 nm-thick non-crystallizable PET substrate, and dried at a temperature of 50 to 60° C., to form a PVA layer having a thickness of 7 μm on the non-crystallizable PET substrate. This product will hereinafter be referred to as a “laminate comprising the non-crystallizable PET substrate and the 7 μm-thick PVA layer formed on the non-crystallizable PET substrate”, or as a “laminate including the 7 μm-thick PVA layer”, or simply as a “laminate”.
The laminate including the 7 μm-thick PVA layer was subjected to the following steps including a 2-stage stretching step consisting of preliminary in-air stretching and in-boric-acid-solution stretching, to produce a polarizing film having a thickness of 3 μm. Through the first-stage preliminary in-air stretching, the laminate including the 7 μm-thick PVA layer was stretched together with the non-crystallizable PET substrate to form a stretched laminate including a 5 μm-thick PVA layer. This product will hereinafter be referred to as a “stretched laminate”. Specifically, the stretched laminate was obtained by placing the laminate including the 7 μm-thick PVA layer into a stretching apparatus arranged in an oven set to a stretching temperature environment of 130° C., to stretch the laminate in an end-free uniaxial manner to attain a stretching ratio of 1.8. Through this stretching step, the PVA layer in the stretched laminate was converted into a 5 μm-thick PVA layer in which PVA molecules are oriented.
Subsequently, the stretched laminate was subjected to a dyeing step to form a dyed laminate in which iodine is absorbed (impregnated) in the 5 μm-thick PVA layer having the oriented PVA molecules. This product will hereinafter be referred to as a “dyed laminate”. Specifically, the dyed laminate was obtained by immersing the stretched laminate in a dyeing solution having a temperature of 30° C. and containing iodine and potassium iodide, for an arbitrary time, to cause iodine to be absorbed in the PVA layer included in the stretched laminate, so as to allow the PVA layer for making up a target polarizing film (to a polarizing film to be finally formed) to have a single layer transmittance of 40 to 44%. In this step, the dyeing solution was prepared by adjusting a concentration of iodine and a concentration of potassium iodide to fall within the range of 0.12 to 0.30 wt % and the range of 0.7 to 2.1 wt %, respectively, using water as a solvent. A ratio of the concentration of iodine to the concentration of potassium iodide is 1:7.
By the way, it is necessary to use potassium iodide to allow iodine to be dissolved in water. More specifically, the stretched laminate was immersed in a dyeing solution having an iodine concentration of 0.30 wt % and a potassium iodide concentration of 2.1 wt %, for 60 seconds, to form a dyed laminate in which iodine is absorbed in the 5 μm-thick PVA layer having the oriented PVA molecules. In the Example 1, various dyed laminates different in single layer transmittance and polarization rate were formed by changing an immersion time of the stretched laminate in the dyeing solution having an iodine concentration of 0.30 wt % and a potassium iodide concentration of 2.1 wt %, to adjust an amount of iodine to be absorbed, so as to allow a target polarizing film to have a single layer transmittance of 40 to 44%.
Further, through the second-stage in-boric-acid-solution stretching, the dyed laminate was further stretched together with the non-crystallizable PET substrate to form an optical film laminate including a PVA layer making up a 3 μm-thick polarizing film. This product will hereinafter be referred to as an “optical film laminate”. Specifically, the optical film laminate was obtained by feeding the dyed laminate through a stretching apparatus arranged in treatment equipment having a boric acid aqueous solution containing boric acid and potassium iodide and having a temperature of 60 to 85° C., to subject the dyed laminate to an end-free uniaxial stretching to attain a stretching ratio of 3.3. More specifically, the temperature of the boric acid aqueous solution was 65° C. Further, the boric acid aqueous solution was set to contain 4 weight parts of boric acid with respect to 100 weight parts of water, and 5 weight parts of potassium iodide with respect to 100 weight parts of water.
In this step, the dyed laminate having iodine impregnated therein in an adjusted amount was first immersed in the boric acid aqueous solution for 5 to 10 seconds. Then, the dyed laminate was fed to directly pass between each of a plurality of set of rolls having different circumferential speeds and serving as the stretching apparatus arranged in the treatment equipment, and subjected to an end-free uniaxial stretching to attain a stretching ratio of 3.3 by taking a time of 30 to 90 seconds. Through this stretching, the PVA layer included in the dyed laminate is changed into a 3 μm-thick PVA layer in which absorbed iodine is highly oriented in one direction in the form of a polyiodide ion complex. This PVA layer makes up a polarizing film of an optical film laminate.
As above, in the Example 1, a laminate comprising a non-crystallizable PET substrate and a 7 μm-thick PVA layer formed on the substrate is first subjected to preliminarily in-air stretching at a stretching temperature of 130° C. to form a stretched laminate. Then, the stretched laminate is subjected to dyeing to form a dyed laminate. Then, the dyed laminate is subjected to in-boric-acid-solution stretching at a stretching temperature of 65° C., to form an optical film laminate including a 3 μm-thick PVA layer stretched together with the non-crystallizable PET substrate to attain a total stretching ratio of 5.94. Through the 2-stage stretching, it becomes possible to form an optical film laminate including a 3 μm-thick PVA layer in which PVA molecules in the PVA layer formed on the non-crystallizable PET substrate are highly oriented, and iodine absorbed through the dyeing is highly oriented in one direction in the form of a polyiodide ion complex.
Then, in a cleaning step although it is not essential in a production process of an optical film laminate, the optical film laminate was taken out of the boric acid aqueous solution, and boric acid deposited on a surface of the 3 μm-thick PVA layer formed on the non-crystallizable PET substrate was cleaned by a potassium iodide aqueous solution. Subsequently, in a drying step, the cleaned optical film laminate was dried by warm air at a temperature of 60° C. The cleaning step is designed to solve defective appearance due to deposition of boric acid.
Subsequently, in a lamination and/or transfer step, an 80 μm-thick triacetylcellulose (TAC) film was laminated to a surface of the 3 μm-thick PVA layer formed on the non-crystallizable PET substrate, while applying a bonding agent onto the surface of the 3 μm-thick PVA layer. Then, the non-crystallizable PET substrate was peeled to allow the 3 μm-thick PVA layer to be transferred to the 80 μm-thick triacetylcellulose (TAC) film.
In the Example 2, as with the Example 1, a 7 μm-thick PVA layer was formed on a non-crystallizable PET substrate to form a laminate, and then the laminate including the 7 μm-thick PVA layer was subjected to preliminary in-air stretching and stretched at a stretching ratio of 1.8 to form a stretched laminate, whereafter the stretched laminate was immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate including an iodine-absorbed PVA layer. Differently from the Example 1, a process in the Example 2 additionally comprises a cross-linking step. The cross-linking step is designed to immerse the dyed laminate in a cross-linking boric acid aqueous solution at a temperature of 40° C., for 60 seconds, so as to allow PVA molecules of the iodine-absorbed PVA layer to be subjected to cross-linking. The cross-linking boric acid aqueous solution in this step was set to contain 3 weight parts of boric acid with respect to 100 weight parts of water, and 3 weight parts of potassium iodide with respect to 100 weight parts of water.
The cross-linking step in the Example 2 is intended to expect at least three technical effects. The first is an insolubilization effect of preventing a thinned PVA layer included in the dyed laminate from being dissolved during subsequent in-boric-acid-solution stretching. The second is a dyeing stabilization effect of preventing elution of iodine absorbed in the PVA layer. The third is a node formation effect of forming nodes by cross-linking molecules of the PVA layer together.
In the Example 2, the cross-linked dyed laminate was immersed in an in-boric-acid-solution stretching bath at 75° C. which is higher than a stretching temperature of 65° C. in the Example 1, and stretched at a stretching ratio of 3.3 to form an optical film laminate, as with the Example 1. The process in the Example 2 further comprises a cleaning step, a drying step and a lamination and/or transfer step each of which is the same as that in the Example 1.
In order to further clarify the technical effects expected of the cross-linking step in advance of the in-boric-acid-solution stretching, a non-cross-linked dyed laminate in the Example 1 was immersed in the in-boric-acid-solution stretching bath at a stretching temperature of 70 to 75° C. In this case, the PVA layer included in the dyed laminate was dissolved in the in-boric-acid-solution stretching bath to preclude the stretching.
In the Example 3, as with the Example 1, a 7 μm-thick PVA layer was formed on a non-crystallizable PET substrate to form a laminate, and then the laminate including the 7 μm-thick PVA layer was subjected to preliminary in-air stretching and stretched at a stretching ratio of 1.8 to form a stretched laminate. Differently from the Example 1, a process in the Example 3 additionally comprises an insolubilization step. The insolubilization step is designed to immerse the stretched laminate in a boric acid insolubilizing aqueous solution at a solution temperature of 30° C., for 30 seconds, so as to insolubilize a PVA layer included in the stretched laminate and having oriented PVA molecules. The boric acid insolubilizing aqueous solution in this step was set to contain 3 weight parts of boric acid with respect to 100 weight parts of water. A technical effect expected of the insolubilization step in the Example 3 is to prevent the PVA layer included in the stretched laminate from being dissolved at least during a subsequent dyeing step.
In the Example 3, as with the Example 1, the insolubilized stretched laminate was immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate including an iodine-absorbed PVA layer. Subsequently, the dyed laminate was immersed in the in-boric-acid-solution stretching bath at 65° C. which is equal to the stretching temperature in the Example 1, and stretched at a stretching ratio of 3.3 in the same manner as that in the Example 1 to form an optical film laminate. The process in the Example 3 further comprises a cleaning step, a drying step and a lamination and/or transfer step each of which is the same as that in the Example 1.
In order to further clarify the technical effects expected of the insolubilization step in advance of the dyeing step, a non-insolubilized stretched laminate in the Example 1 was subjected to dyeing to form a dyed laminate, and the formed dyed laminate was immersed in the in-boric-acid-solution stretching bath at a stretching temperature of 70 to 75° C. In this case, the PVA layer included in the dyed laminate was dissolved in the in-boric-acid-solution stretching bath to preclude the stretching, as with the Example 2.
In another test, in place of the dyeing solution in the Example 1 where a concentration of iodine is set to 0.30 wt % using water as a solvent, a dyeing solution was prepared to set an iodine concentration in the range of 0.12 to 0.25 wt %, while keeping the remaining conditions unchanged. Then, the non-insolubilized stretched laminate in the Example 1 was immersed in the prepared dyeing solution. In this case, the PVA layer included in the stretched laminate was dissolved in the dyeing bath to preclude the dyeing. In contrast, when the insolubilized stretched laminate in the Example 3 was used, the dyeing to the PVA layer could be performed without dissolution of the PVA layer, even if the iodine concentration of the dyeing solution was in the range of 0.12 to 0.25 wt %.
In the Example 3 where the dyeing to the PVA layer can be performed even if the iodine concentration of the dyeing solution is in the range of 0.12 to 0.25 wt %, various dyed laminates different in single layer transmittance and polarization rate were formed by changing the iodine concentration and the potassium iodide concentration of the dyeing solution in the certain range in the Example 1, while keeping an immersion time of the stretched laminate in the dyeing solution constant, to adjust an amount of iodine to be absorbed, so as to allow a target polarizing film to have a single layer transmittance of 40 to 44%.
In the Example 4, an optical film laminate was formed by a production process in which the insolubilization step in the Example 3 and the cross-linking step in the Example 2 are added to the production process in the Example 1. Firstly, a 7 μm-thick PVA layer was formed on a non-crystallizable PET substrate to form a laminate, and then the laminate including the 7 μm-thick PVA layer was subjected to preliminary in-air stretching based on an end-free uniaxial stretching process to attain a stretching ratio of 1.8 to thereby form a stretched laminate. In the Example 4, as with the Example 3, through the insolubilization step of immersing the formed stretched laminate in a boric acid insolubilizing solution at a temperature of 30° C. for 30 seconds, the PVA layer included in the stretched laminate and having oriented PVA molecules was insolubilized. Then, in the Example 4, as with the Example 3, the stretched laminate including the insolubilized PVA layer was immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate including an iodine-absorbed PVA layer.
In the Example 4, as with the Example 2, through the cross-linking step of immersing the formed dyed laminate in a boric acid cross-linking solution at 40° C. for 60 seconds, PVA molecules of the iodine-absorbed PVA layer are cross-linked together. Then, in the Example 4, the cross-linked dyed laminate was immersed in an in-boric-acid-solution stretching bath at 75° C. which is higher than a stretching temperature of 65° C. in the Example 1, for 5 to 10 seconds, and subjected to an end-free uniaxial stretching to attain a stretching ratio of 3.3, in the same manner as that in the Example 2, to thereby form an optical film laminate. The process in the Example 4 further comprises a cleaning step, a drying step and a lamination and/or transfer step each of which is the same as that in each of the Examples 1 to 3.
As with the Example 3, the PVA layer in the Example 4 is never dissolved even if the iodine concentration of the dyeing solution is in the range of 0.12 to 0.25 wt %. In the Example 4, various dyed laminates different in single layer transmittance and polarization rate were formed by changing the iodine concentration and the potassium iodide concentration of the dyeing solution in the certain range in the Example 1, while keeping an immersion time of the stretched laminate in the dyeing solution constant, to adjust an amount of iodine to be absorbed, so as to allow a target polarizing film to have a single layer transmittance of 40 to 44%.
As above, in the Example 4, a 7 μm-thick PVA layer is formed on a non-crystallizable PET substrate to form a laminate, and then the laminate including the 7 μm-thick PVA layer is subjected to preliminarily in-air stretching based on an end-free uniaxial stretching process to attain a stretching ratio of 1.8 to thereby form a stretched laminate. The formed stretched laminate is immersed in a boric acid insolubilizing solution at a solution temperature of 30° C. for 30 seconds to insolubilize the PVA layer included in the stretched laminate. The stretched laminate including the insolubilized PVA layer is immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate in which iodine is absorbed in the insolubilized PVA layer. The dyed laminate including the iodine-absorbed PVA layer is immersed in a boric acid cross-linking solution at 40° C. for 60 seconds to cross-link PVA molecules of the iodine-absorbed PVA layer together. The dyed laminate including the cross-linked PVA layer is immersed in an in-boric-acid-solution stretching bath containing iodine and potassium iodide and having a temperature of 75° C., for 5 to 10 seconds, and then subjected to in-boric-acid-solution stretching based on an end-free uniaxial stretching process to attain a stretching ratio of 3.3 to thereby form an optical film laminate.
In the Example 4, based on the 2-stage stretching consisting of the elevated temperature in-air stretching and the in-boric-acid-solution stretching, and pre-treatments consisting of the insolubilization in advance of the immersion into a dyeing bath and the cross-linking in advance of the in-boric-acid-solution stretching, it becomes possible to stably form an optical film laminate including a 3 μm-thick PVA layer making up a polarizing film, in which PVA molecules of the PVA layer formed on the non-crystallizable PET substrate are highly oriented, and iodine reliably absorbed in the PVA molecules through the dyeing is highly oriented in one direction in the form of a polyiodide ion complex.
In the Example 5, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is a thickness of the PVA layer formed on the non-crystallizable PET substrate. In the Example 4, the PVA layer initially had a thickness of 7 μm, and the PVA layer finally included in the optical film laminate had a thickness of 3 μm, whereas, in the Example 5, the PVA layer initially had a thickness of 12 μm, and the PVA layer finally included in the optical film laminate had a thickness of 5 μm.
In the Example 6, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is a polymerizing monomer used in the non-crystallizable PET substrate. In the Example 4, the non-crystallizable PET substrate was prepared by copolymerizing PET and isophthalic acid, whereas, in the Example 6, the non-crystallizable PET substrate was prepared by copolymerizing PET and 1,4-cyclohexanedimethanol serving as a modifier group.
In the Example 7, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that a stretching ratio for each of the preliminary in-air stretching and the in-boric-acid-solution stretching was changed to allow a total stretching ratio to become equal to or close to 6.0. In the Example 4, the stretching ratios for the preliminary in-air stretching and the in-boric-acid-solution stretching were set, respectively, to 1.8 and 3.3, whereas, in the Example 7, the two stretching ratios were set, respectively, to 1.2 and 4.9. Meanwhile, the total stretching ratio in the Example 4 was 5.94, whereas the total stretching ratio in the Example 7 was 5.88. The reason is that, in the in-boric-acid-solution stretching, it was unable to perform the stretching at a stretching ratio of 4.9 or more.
In the Example 8, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that a stretching ratio for each of the preliminary in-air stretching and the in-boric-acid-solution stretching was changed to allow a total stretching ratio to become equal to 6.0. In the Example 8, the stretching ratios for the preliminary in-air stretching and the in-boric-acid-solution stretching were set to 1.5 and 4.0, respectively.
In the Example 9, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that a stretching ratio for each of the preliminary in-air stretching and the in-boric-acid-solution stretching was changed to allow a total stretching ratio to become equal to 6.0. In the Example 9, the stretching ratios for the preliminary in-air stretching and the in-boric-acid-solution stretching were set to 2.5 and 2.4, respectively.
In the Example 10, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. In the Example 4, a stretching temperature for the preliminary in-air stretching was set to 130° C., whereas, in the Example 10, the stretching temperature for the preliminary in-air stretching was set to 95° C.
In the Example 11, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. In the Example 4, the stretching temperature for the preliminary in-air stretching was set to 130° C., whereas, in the Example 11, the stretching temperature for the preliminary in-air stretching was set to 110° C.
In the Example 12, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. In the Example 4, the stretching temperature for the preliminary in-air stretching was set to 130° C., whereas, in the Example 12, the stretching temperature for the preliminary in-air stretching was set to 150° C.
In the Example 13, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that the stretching ratio for the preliminary in-air stretching was set to 1.8, and the stretching ratio for the in-boric-acid-solution stretching was changed to 2.8. As a result, in the Example 13, the total stretching ratio was about 5.0 (accurately, 5.04), whereas, in the Example 4, the total stretching ratio was about 6.0 (accurately, 5.94).
In the Example 14, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that the stretching ratio for the preliminary in-air stretching was set to 1.8, and the stretching ratio for the in-boric-acid-solution stretching was changed to 3.1. As a result, in the Example 14, the total stretching ratio was about 5.5 (accurately, 5.58), whereas, in the Example 4, the total stretching ratio was about 6.0 (accurately, 5.94).
In the Example 15, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is that the stretching ratio for the preliminary in-air stretching was set to 1.8, and the stretching ratio for the in-boric-acid-solution stretching was changed to 3.6. As a result, in the Example 15, the total stretching ratio was about 6.5 (accurately, 6.48), whereas, in the Example 4, the total stretching ratio was about 6.0 (accurately, 5.94).
In the Example 16, an optical film laminate was produced under the same conditions as those in the Example 4, except the following difference. The difference is a stretching scheme in the preliminary in-air stretching. In the Example 4, the preliminary in-air stretching was performed based on an end-free uniaxial stretching process to attain a stretching ratio of 1.8 times, whereas, in the Example 16, the preliminary in-air stretching was performed based on an end-fixed uniaxial stretching process to attain a stretching ratio of 1.8 times.
In the Example 17, an optical film laminate was produced under the same conditions as those in the Example 16, except the following difference. The difference is that the stretching ratio for the preliminary in-air stretching was set to 1.8, and the stretching ratio for the in-boric-acid-solution stretching was changed to 3.9. As a result, in the Example 17, the total stretching ratio was about 7 (accurately, 7.02), whereas, in the Example 16, the total stretching ratio was about 6.0 (accurately, 5.94).
In the Example 18, an optical film laminate was produced under the same conditions as those in the Example 16, except the following difference. The difference is that the stretching ratio for the preliminary in-air stretching was set to 1.8, and the stretching ratio for the in-boric-acid-solution stretching was changed to 4.4. As a result, in the Example 18, the total stretching ratio was about 8 (accurately, 7.92), whereas, in the Example 16, the total stretching ratio was about 6.0 (accurately, 5.94).
The comparative example 1 has been prepared, under the same conditions as those in the Example 4, by applying a PVA solution to a 200 μm-thick non-crystallizable PET substrate, and drying to form a laminate comprising the non-crystallizable PET substrate and a 7 μm-thick PVA layer formed on the substrate. Then, the laminate including the 7 μm-thick PVA layer was subjected to elevated temperature in-air stretching at a stretching temperature of 130° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 4.0 to thereby form a stretched laminate. Through the stretching, the PVA layer included in the stretched laminate was changed to a 3.5 μm-thick PVA layer having oriented PVA molecules.
Then, the stretched laminate was subjected to dyeing to form a dyed laminate in which iodine is absorbed in the 3.5 μm-thick PVA layer having the oriented PVA molecules. Specifically, the dyed laminate was obtained by immersing the stretched laminate in a dyeing solution having a temperature of 30° C. and containing iodine and potassium iodide, for an arbitrary time, to cause iodine to be absorbed in the PVA layer included in the stretched laminate, so as to allow the PVA layer for making up a target polarizing film to have a single layer transmittance of 40 to 44%. Various dyed laminates different in single layer transmittance and polarization rate were formed by adjusting an amount of iodine to be absorbed in the PVA layer having the oriented PVA molecules, in the above manner
Further, the dyed laminated was subjected to cross-linking. Specifically, the dyed laminated was cross-linked in such a manner that it is immersed in a boric acid cross-linking solution containing 3 weight parts of boric acid with respect to 100 weight pars of water and 3 weight parts of potassium iodide with respect to 100 weight pars of water and having a temperature of 40° C., for 60 seconds. The cross-linked dyed laminate in the comparative example 1 corresponds to the optical film laminate in the Example 4. Thus, a cleaning step, a drying step and a lamination and/or transfer step in the comparative example 1 are the same as those in the Example 4.
In the comparative example 2, the laminates in accordance with the comparative examples 1 have been stretched to a stretching ratio of 4.5, 5.0 and 6.0, respectively. The following comparative table illustrates phenomena experienced in a 200 μm-thick non-crystallizable PET substrate and a PVA layer formed on the non-crystallizable PET substrate, including the comparative examples 1 and 2. Based on the data, it has been verified that the stretching ratio during the elevated temperature in-air stretching at a stretching temperature of 130° C. has an upper limit of 4.0.
In
As is clear from
Referring to
An example in which a laminate prepared by coating a PVA type resin layer on a non-crystallizable PET substrate is subjected to an end-free uniaxial stretching in air under elevated temperature is shown as comparative examples 1 and 2 in the following Table 1. In the non-crystallizable PET substrate, there is no constraint of stretching temperature. In the comparative example 1, a polarizing film was produced by forming a 7 μm-thick PVA type resin layer on a 200 μm-thick non-crystallizable PET substrate to form a laminate, and subjecting the laminate to the elevated temperature in-air end-free uniaxial stretching at a stretching temperature of 130° C. The stretching ratio in the comparative example 1 was 4.0.
Referring to Table 1, in the comparative example 2, as with the comparative example 1, polarizing films were prepared by forming a 7 μm-thick PVA type resin layer on a 200 μm-thick non-crystallizable PET substrate to form laminates, and stretching the laminates to the stretching ratio of 4.5, 5.0 and 6.0, respectively. As illustrated in Table 1, in each of the polarizing films, there have been observed non-uniform stretching or breaking in the film surfaces of the non-crystalline PET substrates, and breaking of the PVA type resin layer at a stretching ratio of 4.5. Based on the data, it has been verified that the stretching ratio of the PVA type resin layer during the elevated temperature in-air end-free uniaxial stretching at a stretching temperature of 130° C. is limited to 4.0.
In each of the reference samples 1 to 3, although there is a difference in stretching temperature, a dyed laminate was produced by steps of forming a PVA type resin layer on a crystallizable PET substrate to form a laminate, subjecting the laminate to stretching at a stretching ratio of 4.0 to 4.5 to allow PVA molecules to be oriented, and causing iodine to be absorbed in the thinned PVA type resin layer. Specifically, the stretched laminate was immersed in a dyeing solution containing iodine and potassium iodide under a temperature of 30° C., for an arbitrary time, to cause iodine to be impregnated in the PVA type resin layer included in the stretched laminate, so that the PVA type resin layer constituting a target polarizing film has a single layer transmittance of 40 to 44%. In addition, the amount of iodine to be absorbed in the thinned PVA type resin layers was adjusted to produce various polarizing films having different single layer transmittance T and polarization rate P.
Referring to
Therefore, prior to the present invention, the inventors have developed a polarizing film and a production method therefor disclosed in the international application PCT/JP 2010/001460. This is based on findings with a focus on a plasticizing function of water in which a laminate comprising a PET substrate and a PVA type resin layer formed on the substrate can be stretched even at a stretching temperature below a glass transition temperature Tg thereof. An example of a polarizing film produced by this process is shown as a comparative example 3 herein. In accordance with this method, the laminate comprising the PET substrate and the PVA type resin layer formed on the substrate can be stretched at a stretching ratio of up to 5.0.
Through subsequent researches, the inventors have ascertained that the stretching ratio is limited to 5.0 because the PET substrate is made of crystallizable PET. Previously, the inventors have considered that the stretching function would not largely be affected by the crystallizing property of the PET substrate, since a laminate comprising a PET substrate and a PVA type resin layer formed on the substrate was stretched in a boric acid aqueous solution at a temperature below a glass transition temperature Tg. However, it was found that, in cases where the PET substrate is made of non-crystallizable PET, the laminate can be stretched at a stretching ratio of up to 5.5. It is assumed that, in a polarizing film production method equivalent to the comparative example 3, the stretching ratio is limited to 5.5, due to the non-crystallizable PET substrate which poses a limit on the stretching ratio.
In the comparative example 1, various polarizing films having different single layer transmittance T and polarization rate P were prepared. Respective optical characteristics of the polarizing films are illustrated in
The solid line in
On the other hand, the dotted line in
Referring now to
The method of producing a polarizing film which can be used in the present invention comprises a combination of 2-stage stretching steps consisting of elevated temperature in-air stretching and in-boric-acid-solution stretching, as will be described later. The combination of 2-stage stretching steps is not the one which is simply conceivable. Through various long-term researches, the inventors have finally reached a surprising conclusion that the following two technical problems can be simultaneously solved only by the combination. In an attempt to produce a polarizing film by forming a PVA type resin layer on a thermoplastic resin substrate to form a laminate, and subjecting the laminate to stretching and dyeing, there are two technical problems which have been considered to be impossible to overcome.
The first technical problem is that the stretching ratio and the stretching temperature each having an impact on improvement in molecular orientation of a PVA type resin are largely restricted by the thermoplastic resin substrate on which the PVA type resin layer is formed.
The second technical problem is that, for example, even if the problem on restrictions to the stretching ratio and the stretching temperature can be overcome, stretching of the PVA type resin is restricted due to its crystallization because crystallization and stretchability of a crystallizable resin such as the PVA type resin and PET used for the thermoplastic resin substrate are incompatible physical properties.
The first technical problem will further be discussed as follows. One of the restrictions in producing a polarizing film using a thermoplastic resin substrate is caused by the property of the PVA type resin wherein the stretching temperature is above the glass transition temperature Tg (about 75 to 80° C.) thereof and its attainable stretching ratio is in the range of 4.5 to 5.0. If a crystallizable PET is used as a material for the thermoplastic resin substrate, the stretching temperature is further restricted to 90 to 110° C. It has been considered that any polarizing film cannot be free from the above restriction as long as it is produced by a process of forming a PVA type rein layer on a thermoplastic resin substrate to form a laminate and subjecting the laminate to the elevated temperature in-air stretching to have the PVA type rein layer included in the laminate decreased in thickness.
Therefore, with a focus on a plasticizing function of water, the inventors have proposed in-boric-acid-solution stretching capable of serving as an alternative to the elevated temperature in-air stretching. However, even in the in-boric-acid-solution stretching at a stretching temperature of 60 to 85° C., it has been difficult to overcome the restriction caused by the thermoplastic resin substrate, specifically, a restriction that the stretching ratio attainable in a crystallizable PET is limited to 5.0, and the stretching ratio attainable in a non-crystallizable PET is limited to 5.5. These facts cause a restriction on improvement in orientation of PVA molecules, which leads to a restriction to optical characteristics of the polarizing film of a decreased thickness. This is the first technical problem.
A solution to the first technical problem can be explained based on
On the other hand, the solid lines in
The relationship between the molecular orientation and the extent of crystallization of the PET used as a material for the thermoplastic resin substrate, illustrated in
By solving the first technical problem, it has become possible to eliminate restrictions to the stretching ratio which would otherwise be caused by the PET substrate, and increase the total stretching ratio to improve the molecular orientation of the PVA type resin. Thus, optical characteristics of the polarizing film can be significantly improved. However, an improvement in the optical characteristics achieved by the inventors is not limited thereto. Further improvement will be achieved by solving the second technical problem.
The second technical problem will further be discussed in the followings. One of the features inherent to a PVA type resin and a crystallizable resin such as PET as a material for the thermoplastic resin substrate is that, in general, polymer molecules are orderly arranged by heating and stretching/orienting and thereby crystallization is progressed. Stretching of the PVA type resin is restricted by crystallization of the PVA type resin which is a crystallizable resin. Crystallization and stretchability are mutually incompatible physical properties, and it has been commonly recognized that progress in crystallization of the PVA type resin hinders the molecular orientation of the PVA type resin. This is the second technical problem. Means for solving the second technical problem can be explained based on
The solid line in
Similarly, the dotted line in
The solid line in
As above, it has been possible to attain an unanticipated remarkable result in that the orientation of PVA molecules in the PVA type resin layer formed by the second-stage in-boric-acid-solution stretching can be further improved by setting the stretching temperature or the stretching ratio during the first-stage elevated temperature in-air stretching to a higher value.
Reference will now made to the crystallization degree or extent of crystallization (horizontal axis) of the PVA type resin illustrated in
On the other hand, if the crystallization degree of the PVA type resin layer is 37% or more, dyeability of the PVA type resin layer will be deteriorated, and thereby it is necessary to increase a concentration of the dyeing aqueous solution, so that an amount of material to be used, and a required time for the dyeing, will be increased, which is likely to cause deterioration in productivity. If the crystallization degree of the PVA type resin layer is 40% or more, another problem, such as breaking of the PVA type resin layer during the in-boric-acid-solution stretching, is likely to occur. Therefore, the extent of crystallization or the crystallization degree of the PVA type resin is preferably determined in the range of 27% to 40%, more preferably in the range of 30% to 37%.
Reference is now made to the orientation function (vertical axis) of the PVA type resin layer illustrated in
On the other hand, if the orientation function of the PVA type resin layer is set to 0.30 or more, the dyeability will be deteriorated, and thereby it is necessary to increase the concentration of the dyeing aqueous solution, so that an amount of material to be used, and a required time for the dyeing, will be increased, which is likely to cause deterioration in productivity. If the orientation function of the PVA type resin layer is set to 0.35 or more, another problem, such as breaking of the PVA type resin layer during the in-boric-acid-solution stretching, is likely to occur. Therefore, the orientation function of the PVA type resin is preferably set in the range of 0.05 to 0.35, more preferably in the range of 0.15 to 0.30.
Means for solving the first technical problem is to auxiliarily or preliminarily stretch a laminate comprising a non-crystallizable PET substrate and a PVA type resin layer formed on the substrate by the first-stage elevated temperature in-air stretching, whereby the PVA type resin layer can be stretched at a higher stretching ratio by the second-stage in-boric-acid-solution stretching without being restricted by the stretching ratio of the non-crystallizable PET substrate, so that the molecular orientation of the PVA is sufficiently improved.
Means for solving the second technical problem is to auxiliarily or preliminarily set the stretching temperature during the first-stage elevated temperature in-air stretching to a higher value, or auxiliarily or preliminarily set the stretching ratio during the first-stage elevated temperature in-air stretching to a higher value, whereby an unanticipated result has been provided that the orientation of PVA molecules in the PVA type resin layer formed by the second-stage in-boric-acid-solution stretching is further improved. In either case, the first-stage elevated temperature in-air stretching can be regarded as auxiliary or preliminary in-air stretching means for the second-stage in-boric-acid-solution stretching. The “first-stage elevated temperature in-air stretching” will hereinafter be referred to as “preliminary in-air stretching”, in contrast to the second-stage in-boric-acid-solution stretching.
In particular, a mechanism for solving the second technical problem by performing the “preliminary in-air stretching” can be assumed as follows. As is ascertained in
Considering all the above factors together, a polarizing film having a thickness of 10 nm or less and optical characteristics satisfying the following condition (1) or (2) can be obtained by performing stretching based on the 2-stage stretching consisting of a preliminary in-air stretching and an in-boric-acid-solution stretching:
P>−(100.929T-42.4−1)×100 (where T<42.3); and
P≧99.9 (where T≧42.3), Condition (1)
or
T≧42.5; and
P≧99.5 Condition (2)
wherein T is a single layer transmittance, and P is a polarization rate. The dichroic material may be iodine or a mixture of iodine and an organic dye.
A polarizing film having optical characteristics in which the single layer transmittance T and the polarization rate P fall within the ranges represented by the above conditions fundamentally has a performance required for use in a display device for a liquid-crystal television using a large-sized display element, or a performance required for use in an organic EL display device. Specifically, for liquid-crystal televisions, it is possible to produce an optical display device having a contrast ratio of 1000:1 or more, and, a maximum luminance of 500 cd/m2 or more. In this specification, this performance will be referred to as “required performance”. This polarizing film can also be used in an optically functional film laminate to be laminated to a viewing side of an organic EL display panel.
When used with a liquid-crystal display panel, a polarizing film to be disposed on one of a backlight and viewing sides of the liquid-crystal display panel must have polarization performance satisfying at least the above optical characteristics. Further, in cases where a polarizing film having a polarization rate of 99.9% or less is disposed on one of the backlight and viewing sides, it will become difficult to achieve the required performance, even if a polarizing film having highest possible polarization performance is disposed on the other side.
Reference will now be made to
As a material for the thermoplastic resin substrate, it is preferable to use a non-crystallizable ester type resin. This type of thermoplastic resin may include isophthalic acid-copolymerized polyethylene terephthalate, cyclohexanedimethanol-copolymerized polyethylene terephthalate, and non-crystal polyethylene terephthalate including other copolymerized polyethylene terephthalate. The substrate may be made of a transparent resin. Although the above description has been made based on an example in which a non-crystallizable resin material is used as the thermoplastic resin substrate, a crystallizable resin material may also be used.
Preferably, a dichroic material for dyeing a polyvinyl alcohol type resin is iodine, or a mixture of iodine and an organic dye.
In the present invention, an optically functional film may be bonded to a polarizing film made of the PVA type resin layer on the thermoplastic resin substrate. Further, after peeling the resin substrate from the polarizing film, a separator film may be releasably laminated to a surface of the polarizing film from which the resin substrate is peeled, through an adhesive layer. The separator film is treated to allow the adhesion force thereof to the adhesive layer to become weaker than the adhesion force of the polarizing film to the adhesive layer, so that, when the separator film is peeled from the polarizing film, the adhesive layer is left on the side of the polarizing film. In cases where a roll of an optical film laminate to be produced according to the present invention is used for manufacturing display devices, the separator film may be used as a carrier film. Alternatively, the separator may be used only as a medium for giving an adhesive layer to the polarizing film.
In another embodiment of the present invention, an optically functional film laminate may be formed by attaching an optically functional film to a surface of the thermoplastic resin substrate, such as a non-crystallizable ester type thermoplastic resin substrate, on which the polarizing film is not formed, and releasably laminating a separator film onto the optically functional film through an adhesive layer. In this case, the optically functional film may be one of a plurality of conventional optically functional films incorporated in display devices so as to achieve various optical functions. The optically functional film may include the aforementioned ¼ wavelength phase difference film. There have also been known various optically functional film used for viewing angle compensation. In another embodiment, after attaching an optically functional film to a surface of the polarizing film on a side opposite to the thermoplastic resin substrate, a film, such as a protective film, may be attached onto the optically functional film through an adhesive layer. Then, after peeling the thermoplastic resin substrate, a separator film may be attached to a surface of the polarizing film from which the substrate is peeled, through an adhesive layer. A defect inspection may be performed after peeling the separator film. Then, after completion of the inspection, the peeled separator film or a newly prepared separator film may be bonded to the polarizing film through an adhesive layer.
As is evidenced from
Preferably, the non-crystallizable ester type thermoplastic resin substrate is made of a material selected from the group consisting of isophthalic acid-copolymerized polyethylene terephthalate, cyclohexanedimethanol-copolymerized polyethylene terephthalate and non-crystallizable polyethylene terephthalate comprising another copolymerized polyethylene terephthalate, wherein the resin has an orientation function of 0.10 or less, and is subjected to the elevated temperature in-air stretching. The substrate may be made of a transparent resin.
In implementation of the method of the present invention, wherein a polarizing film comprising a PVA type resin, using a thermoplastic resin substrate, an insolubilization process for insolubilizing the PVA type resin is regarded as a key technical problem as will be specifically described below.
In cases where the PVA type resin layer formed on the thermoplastic resin substrate is subjected to stretching, it is not easy to cause iodine to be impregnated in the PVA type resin layer, while preventing the PVA type resin layer included in a stretched intermediate product or a stretched laminate from being dissolved in a dyeing solution. In a production process of a polarizing film, a step of causing iodine to be absorbed in a thinned PVA type resin layer is essential. In a conventional dyeing step, an amount of iodine to be absorbed in the PVA type resin layer is adjusted by using a plurality of dyeing solutions having different iodine concentrations ranging from 0.12 to 0.25 wt %, and keeping an immersion time constant. In such a conventional dyeing step, dissolution of the PVA type resin layer will occur during production of a polarizing film to preclude dyeing. As used here, the term “concentration” means a mixing ratio with respect to a total amount of the solution. Further, the term “iodine concentration” means a mixing ratio of iodine to a total amount of the solution, wherein an amount of iodine added as an iodide such as potassium iodide is not included therein. In the following description, the terms “concentration” and “iodine concentration” will be used as the same meanings.
As is clear from the test result illustrated in
Reference will now be made to
Referring to
The Example 1 indicates optical characteristics of polarizing films produced without conducting the first and the second insolubilization steps. The Example 2 indicates optical characteristics of polarizing films produced by performing only the second insolubilization step without performing the first insolubilization step, and the Example 3 indicates optical characteristics of polarizing films produced by performed only the first insolubilization step without performing the second insolubilization step. The Example 4 indicates optical characteristics of polarizing films produced by performing both the first and second insolubilization steps.
In the present invention, a polarizing film satisfying the required performance can be produced without conducting the first and the second insolubilization steps which will be described later. However, as is clear from
As is clear from
In one embodiment of the present invention, the first insolubilization is designed to prevent dissolution of the thinned PVA type resin layer included in the stretched intermediate product (or stretched laminate). On the other hand, the second insolubilization included in the cross-linking step is designed to stabilize dyeing so as to prevent iodine absorbed in the PVA type resin layer included in the dyed intermediate product (or a dyed laminate) from being eluted during the in-boric-acid-solution stretching at a solution temperature of 75° C. in a subsequent step, and prevent dissolution of the thinned PVA type resin layer.
If the second insolubilization is omitted, elution of the iodine impregnated in the PVA type resin layer will be progressed during the in-boric-acid-solution stretching at a solution temperature of 75° C., so that the PVA resin layer will be acceleratedly dissolved. The elution of iodine and dissolution of the PVA type resin layer can be avoided by lowering a temperature of the boric acid aqueous solution. For example, it is necessary to stretch a dyed intermediate product (or dyed laminate) while immersing it in the boric acid aqueous solution at a solution temperature of less than 65° C. However, this reduces the effect of the plasticizing function of water, so that softening of the PVA type resin layer included in the dyed intermediate product (or dyed laminate) is not sufficiently obtained. This results in deterioration in stretching performance, so that the dyed intermediate product (or dyed laminate) is likely to break during the course of the in-boric-acid-solution stretching. It should be understood that an intended total stretching ratio of the PVA type resin layer cannot be attained.
With reference to the drawings, one example of a process of producing a polarizing film for use in the present invention will be described below.
Referring to
As a thermoplastic resin substrate, there has been prepared a continuous web of substrate made of isophthalic acid-copolymerized polyethylene terephthalate copolymerized with isophthalic acid in an amount of 6 mol % (hereinafter referred to as “non-crystallizable PET”). A laminate 7 comprising a continuous web of non-crystallizable PET substrate 1 having a glass transition temperature Tg of 75° C., and a PVA layer 2 having a glass transition temperature Tg of 80° C. was prepared in the following manner.
(Laminate Preparation Step (A))
Firstly, a non-crystallizable PET substrate 1 having a thickness of 200 μm, and a PVA solution prepared by dissolving a PVA powder having a polymerization degree of 1000 or more and a saponification degree of 99% or more, in water to have a concentration of 4 to 5 wt % were prepared. Then, in a laminate forming apparatus 20 equipped with a coating unit 21, a drying unit 22 and a surface modifying unit 23, the PVA solution was applied to the non-crystallizable PET substrate 1 having a thickness of 200 μm, and dried at a temperature of 50 to 60° C., to form a 7 μm-thick PVA layer 2 on the non-crystallizable PET substrate 1. The thickness of the PVA layer can be appropriately changed, as described later. The laminate obtained in the above manner will hereinafter be referred to as a “laminate 7 comprising a non-crystallizable PET substrate and a PVA layer formed on the substrate”, or as a “PVA layer-including laminate 7”, or simply as a “laminate 7”.
A laminate 7 including a PVA layer will be produced in the form of a polarizing film 3 having a final thickness of 3 μm through the following processes including a 2-stage stretching step consisting of preliminary in-air stretching and in-boric-acid-solution stretching. While the present invention is intended to use a polarizing film having a thickness of 10 μm or less, any polarizing film having an arbitrary thickness of 10 μm or less can be formed by appropriately changing a thickness of the PVA type resin layer to be formed on the PET substrate 1.
(Preliminary in-Air Stretching Step (B))
In a first-stage preliminary in-air stretching step (B), the laminate 7 including the 7 μm-thick PVA layer 2 was stretched together with the non-crystallizable PET substrate 1 to form a “stretched laminate 8” including a 5 μm-thick PVA layer 2. Specifically, in a preliminary in-air stretching apparatus 30 having stretching means 31 provided within an oven 33, the laminate 7 including the 7 μm-thick PVA layer 2 was fed to pass through the stretching means 31 within the oven 33 set to a temperature environment of 130° C., so that it was subjected to end-free uniaxial stretching to attain a stretching ratio of 1.8 to thereby form a stretched laminate 8. At this stage, the stretched laminate 8 may be wound on a take-up unit 32 provided in side-by-side relation to the oven 33, to produce a roll 8′ of the stretched laminate 8.
Now, “end-free stretching” and “end-fixed stretching” will be generally described. When a film of substantial length is stretched in a transportation or feeding direction, the film is reduced in size in a direction perpendicular to the direction of the stretching, i.e. in a width direction of the film. The end-free stretching means a technique of performing stretching without suppressing such reduction in width. “Longitudinal uniaxial stretching” is a technique of performing stretching only in a longitudinal direction of the film. The end-free uniaxial stretching is generally used in contrast with the end-fixed uniaxial stretching which is a technique of performing stretching while suppressing the shrinkage which would otherwise occur in a direction perpendicular to the stretching direction. Through the end-free uniaxial stretching, the 7 μm-thick PVA layer 2 included in the laminate 7 is converted into a 5 μm-thick PVA layer 2 in which PVA molecules are oriented in the stretching direction.
(Dyeing Step (C))
Then, in a dyeing step (C), a dyed laminate 9 was formed in which iodine as a dichroic material is absorbed in the 5 μm-thick PVA layer 2 having the oriented PVA molecules. Specifically, in a dyeing apparatus 40 equipped with a dyeing bath 42 of a dyeing solution 41 containing iodine and potassium iodide, the stretched laminate 8 unrolled from a feeding unit 43 provided in side-by-side relation to the dyeing apparatus 40 and loaded with the roll 8′ was immersed in the dyeing solution 41 at a solution temperature of 30° C., for an appropriate time, to allow a PVA layer making up a target polarizing film 3 (to be finally formed) to have a single layer transmittance of 40 to 44%. In this manner, a dyed laminate 9 was formed in which iodine is absorbed in the molecularly oriented PVA layer 2 of the stretched laminate 8.
In the above step, in order to prevent dissolution of the PVA layer 2 included in the stretched laminate 8, the dyeing solution 41 was formed as an aqueous solvent having an iodine concentration of 0.30 wt %. Further, the dyeing solution 41 was adjusted to allow a concentration of potassium iodide for allowing iodine to be dissolved in water to become 2.1 wt %. A ratio of the iodine concentration to the potassium iodide concentration was 1:7. More specifically, the laminate 8 was immersed in the dyeing solution 41 having an iodine concentration of 0.30 wt % and a potassium iodide concentration of 2.1 wt %, for 60 seconds, to form a dyed laminate 9 having iodine absorbed in the 5 μm-thick PVA layer 2 having the oriented PVA molecules. In the Example 1, the immersion time of the stretched laminate 8 in the dyeing solution 41 having an iodine concentration of 0.30 wt % and a potassium iodide concentration of 2.1 wt % was changed to adjust an amount of iodine to be absorbed, so as to allow a target polarizing film 3 to have a single layer transmittance of 40 to 44%, to form various dyed laminates 9 different in single layer transmittance and polarization rate.
(In-Boric-Acid-Solution Stretching Step (D))
In a second-stage in-boric-acid-solution stretching step (D), the dyed laminate 9 including the PVA layer 2 which was already dyed with molecularly oriented iodine was further stretched to form an optical film laminate 10 which includes the PVA layer having molecularly oriented iodine and making up a 3 μm-thick polarizing film 3. Specifically, in an in-boric-acid-solution stretching apparatus 50 equipped with stretching means 53 and a bath 52 of a boric acid aqueous solution 51 containing boric acid and potassium iodide, the dyed laminate 9 continuously fed from the dyeing apparatus 40 was immersed in the boric acid aqueous solution 51 set to a solution temperature environment of 65° C., and then fed to pass through the stretching means 53 provided in the in-boric-acid-solution stretching apparatus 50, so that it was subjected to an end-free uniaxial stretching to attain a stretching ratio of 3.3 to thereby form the optical film laminate 10.
More specifically, the boric acid aqueous solution 51 was adjusted to contain 4 weight parts of boric acid with respect to 100 weight parts of water, and 5 weight parts of potassium iodide with respect to 100 weight parts of water. In this step, the dyed laminate 9 having the absorbed iodine in an adjusted amount was first immersed in the boric acid aqueous solution 51 for 5 to 10 seconds. Then, the dyed laminate 9 was fed to directly pass through between a plurality of sets of rolls different in circumferential speed, as the stretching means 53 of the in-boric-acid-solution stretching apparatus 50, so that it was subjected to an end-free uniaxial stretching to attain a stretching ratio of 3.3 while taking a time of 30 to 90 seconds. Through this stretching, the PVA layer included in the dyed laminate 9 was changed into a 3 μm-thick PVA layer in which the absorbed iodine is highly oriented in one direction in the form of a polyiodide ion complex. This PVA layer makes up a polarizing film 3 of the optical film laminate 10.
As described above, in the Example 1, the laminate 7 comprising a non-crystallizable PET substrate 1 and a 7 μm-thick PVA layer 2 formed on the substrate 1 is subjected to a preliminarily in-air stretching at a stretching temperature of 130° C. to form a stretched laminate 8, and then the stretched laminate 8 is subjected to dyeing to form a dyed laminate 9. Further, the dyed laminate 9 is subjected to in-boric-acid-solution stretching at a stretching temperature of 65° C. to form an optical film laminate 10 including a 3 μm-thick PVA layer stretched integrally with the non-crystallizable PET substrate to attain a total stretching ratio of 5.94. Through the above 2-stage stretching, it becomes possible to form an optical film laminate 10 including a 3 μm-thick PVA layer making up a polarizing film 3 in which iodine absorbed therein through dyeing is highly oriented in the form of a polyiodide ion complex. Preferably, the optical film laminate 10 will be completed through subsequent cleaning, drying and transfer steps. Details of the cleaning step (G), the drying step (H) and the transfer step (I) will be described in connection with a production process based on the Example 4 incorporating an insolubilization step.
Referring to
(First Insolubilization Step (E))
The first insolubilization step is an insolubilization step (E) prior to the dyeing step (C). As with the production process based on the Example 1, in the laminate preparation step (A), a laminate 7 comprising a non-crystallizable PET substrate and a 7 μm-thick PVA layer 2 formed on the substrate is produced. Then, in the preliminary in-air stretching step (B), the laminate 7 including the 7 μm-thick PVA layer 2 is subjected to preliminary in-air stretching to form a stretched laminate 8 including a 5 μm-thick PVA layer 2. Subsequently, in the first insolubilization step (E), the stretched laminate 8 unrolled from the feeding unit 43 loaded with the roll 8′ is subjected to insolubilization to form the insolubilized stretched laminate 8″. It should be understood that the stretched laminate 8″ insolubilized in this step includes an insolubilized PVA layer 2. This laminate 8″ will hereinafter be referred to as an “insolubilized stretched laminate 8″”.
Specifically, in an insolubilization apparatus 60 containing an insolubilizing boric acid aqueous solution 61, the stretched laminate 8 is immersed in the insolubilizing boric acid aqueous solution 61 at a solution temperature of 30° C., for 30 seconds. The insolubilizing boric acid solution 61 used in this step contains 3 weight parts of boric acid with respect to 100 weight parts of water (hereinafter referred to as “insolubilizing boric acid aqueous solution”). This step is intended to subject the stretched laminate 8 to insolubilization so as to prevent the 5 μm-thick PVA layer included in the stretched laminate 8 from being dissolved at least during the subsequent dyeing step (C).
After the insolubilization, the insolubilized stretched laminate 8 is transported to the dyeing step (C). Differently from the Example 1, in this dyeing step (C), a plurality of dyeing solutions are prepared by changing the iodine concentration in the range of 0.12 to 0.25 wt %. Then, various dyed laminates 9 different in single layer transmittance and polarization rate are formed by using the dyeing solutions while keeping the immersion time of the insolubilized stretched laminate 8″ in each of the dyeing solutions constant, to adjust an amount of iodine to be absorbed, so as to allow a target polarizing film to have a single layer transmittance of 40 to 44%. Even after the immersion in the dyeing solutions having an iodine concentration of 0.12 to 0.25 wt %, the PVA layer in the insolubilized stretched laminate 8″ is never dissolved.
(Cross-Linking Step Including Second Insolubilization (F))
The following cross-linking step may be considered as including the second insolubilization step, in view of the following purpose. The cross-linking step is intended to achieve firstly insolubilization for preventing dissolution of the PVA layer included in the dyed laminate 9 during the subsequent in-boric-acid-solution stretching step (D), secondly stabilization in dyeing for preventing elution of iodine absorbed in the PVA layer; and thirdly formation of nodes by cross-linking of molecules in the PVA layer. The second insolubilization is intended to accomplish the results of the aforementioned first and second aims.
The cross-linking step (F) is performed as a pretreatment for the in-boric-acid-solution stretching step (D). The dyed laminate 9 formed in the dyeing step (C) is subjected to cross-linking to form a cross-linked dyed laminate 9′. The cross-linked dyed laminate 9′ includes a cross-linked PVA layer 2. Specifically, in a cross-linking apparatus 70 containing an aqueous solution 71 comprising iodine and potassium iodide (hereinafter referred to as “cross-linking boric acid aqueous solution”), the dyed laminate 9 is immersed in the cross-linking boric acid solution 71 at 40° C., for 60 seconds, so as to cross-link the PVA molecules of the PVA layer having the absorbed iodine, to form a cross-linked dyed laminate 9′. The cross-linking boric acid aqueous solution 71 used in this step contains 3 weight parts of boric acid with respect to 100 weight parts of water, and 3 weight parts of potassium iodide with respect to 100 weight parts of water.
In the in-boric-acid-solution stretching step (D), the cross-linked dyed laminate 9′ is immersed in the boric acid aqueous solution at 75° C., and subjected to an end-free uniaxial stretching to attain a stretching ratio of 3.3 to thereby form an optical film laminate 10. Through this stretching, the PVA layer 2 included in the dyed laminate 9′ and having absorbed iodine is changed into a 3 μm-thick PVA layer 2 in which the absorbed iodine is highly oriented in one direction in the form of a polyiodide ion complex. This PVA layer makes up a polarizing film 3 of the optical film laminate 10.
In the Example 4, a 7 μm-thick PVA layer 2 is first formed on a non-crystallizable PET substrate 1 to form a laminate 7, and then the laminate 7 is subjected to preliminary in-air stretching at a stretching temperature of 130° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 1.8 to thereby form a stretched laminate 8. Then, the formed stretched laminate 8 is immersed in the insolubilizing boric acid aqueous solution 61 at a solution temperature of 30° C. to insolubilize the PVA layer included in the stretched laminate. The resulting product is an insolubilized stretched laminate 8″. The insolubilized stretched laminate 8″ is immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate 9 in which iodine is absorbed in the insolubilized PVA layer. Then, the dyed laminate 9 including the PVA layer with the absorbed iodine is immersed in the cross-linking boric acid aqueous solution 71 under a solution temperature of 40° C., for 60 seconds, to cross-link PVA molecules of the PVA layer with the absorbed iodine. The resulting product is a cross-linked dyed laminate 9′. The cross-linked dyed laminate 9′ is immersed in an in-boric-acid-solution stretching bath 51 containing boric acid and potassium iodide and having a temperature of 75° C., for 5 to 10 seconds, and then subjected to in-boric-acid-solution stretching based on an end-free uniaxial stretching process to attain a stretching ratio of 3.3 to thereby form an optical film laminate 10.
As described above, based on the 2-stage stretching consisting of the elevated temperature in-air stretching and the in-boric-acid-solution stretching, and the pre-treatments consisting of the insolubilization before immersion in the dyeing bath and the cross-linking before the in-boric-acid-solution stretching, the process in the Example 4 makes it possible to stably form an optical film laminate 10 including a 3 μm-thick PVA layer making up a polarizing film in which PVA molecules in a PVA layer 2 formed on a non-crystallizable PET substrate 1 are highly oriented, and iodine reliably absorbed in the PVA molecules through dyeing is highly oriented in one direction in the form of an polyiodide ion complex.
(Cleaning Step (G))
The dyed laminate 9 or the cross-linked dyed laminate 9′ in the Example 1 or 4 is subjected to stretching in the in-boric-acid-solution stretching step (D), and then taken out of the boric acid aqueous solution 51. Preferably, the taken-out optical film 10 including the polarizing film 3 is directly fed to a cleaning step (G). The cleaning step (G) is intended to wash out unnecessary residuals adhered on a surface of the polarizing film 3. Alternatively, the cleaning step (G) may be omitted, and the optical film 10 including the polarizing film 3 may be directly fed to a drying step (H). However, if the cleaning is in sufficient, boric acid is likely to precipitate from the polarizing film 3 after drying of the optical film laminate 10. Specifically, the optical film laminate 10 is fed to a cleaning apparatus 80 and immersed in a cleaning solution 81 containing potassium iodide having a temperature of 30° C., for 1 to 10 seconds, so as to prevent dissolution of PVA of the polarizing film 3. A potassium iodide concentration of the cleaning solution 81 may be in the range of about 0.5 to 10 weight %.
(Drying Step (H))
The cleaned optical film laminate 10 is fed to a drying step (H) and dried therein. Then, the dried optical film laminate 10 is wound on a take-up unit 91 provided in side-by-side relation to the drying apparatus 90, as a continuous web of optical film laminate 10, to form a roll of the optical film laminate 10 including the polarizing film 3. Any appropriate process, such as natural drying, blow drying and thermal drying, may be employed as the drying step (H). In each of the Examples 1 and 4, the drying was performed by warm air at 60° C., for 240 seconds in an oven type drying apparatus 90.
[Lamination and Transfer Step (I))
As mentioned above, in a preferred embodiment of the present invention, there is provided a method of producing a roll of an optical film laminate using a polarizing film which comprises a polyvinyl alcohol type resin having a molecularly oriented dichroic material, wherein the polarizing film is formed to have optical characteristics satisfying the aforementioned required conditions, through 2-stage stretching consisting of preliminary in-air stretching and in-boric-acid-solution stretching.
In order to form this optical film laminate, an optical film laminate 10 including a polarizing film having a thickness of 10 μm or less (e.g., the above 3 μm-thick polarizing film 3) and formed on a non-crystallizable PET substrate such as a non-crystallizable PET substrate, is subjected to a defect inspection, and then wound into a roll to form a roll of the optical film laminate 10. For example, a roll of an optical film laminate to be formed by the method of the present invention is used in a lamination/transfer step (I) illustrated in
The polarizing film 3 to be produced has a thickness of 10 μm, typically only about 2 to 5 μm through the stretching which reduces the thickness. Thus, it is difficult to handle such a thin polarizing film 3 in the form of a single layer. For this reason, the polarizing film 3 is handled, for example, in the form of an optical film laminate 10, i.e., under a condition that it is left on the non-crystallizable PET substrate, or, in the form of an optically functional film laminate 11 obtained by laminating or transferring the polarizing film to another optically functional film 4.
In the lamination/transfer step (I) illustrated in
The optical film laminate 10 taken up into a roll by the take-up unit 91 in the drying step (H) or the optically functional film laminate 11 formed in the lamination/transfer step (I) may take various other structures or mechanisms.
(1) Improvement in Optical Characteristics of Polarizing Film by Insolubilization (Examples 1 to 4)
As already described with reference to
(2) Impact of Thickness of PVA Type Resin Layer on Optical Characteristics of Polarizing Film (Example 5)
In the Example 4, the 3 μm-thick polarizing film was formed by stretching the 7 nm-thick PVA layer. On the other hand, in the Example 5, the 12 μm-thick PVA layer was first formed, and the 5 μm-thick polarizing film was formed by stretching this PVA layer. The remaining conditions for producing these polarizing films was the same.
(3) Impact of Difference in Material of Non-Crystallizable PET Substrate on Optical Characteristics of Polarizing Film (Example 6)
In the Example 4, a non-crystallizable PET substrate copolymerized with isophthalic acid was used, whereas, in the Example 6, a non-crystallizable PET substrate copolymerized with 1,4-cyclohexanedimethanol as a modifier group was used. In the Example 6, a polarizing film was produced under the same conditions as those in the Example 4, except the above difference.
Referring to
(4) Improvement in Optical Characteristics of Polarizing Film by Stretching Ratio During Preliminary in-Air (Examples 7 to 9)
In the Example 4, the stretching ratio during the first-stage preliminary in-air stretching and the stretching ratio during the second-stage in-boric-acid-solution stretching were set to 1.8 and 3.3, respectively, whereas, in the Examples 7 to 9, the two stretching ratios were set to 1.2 and 4.9 for the Example 7, 1.5 and 4.0 for the Example 8, and 2.5 and 2.4 for the Example 9. In the Example 7 to 9, the polarizing film was produced under the same conditions as those in the Example 4, except the above difference. For example, the stretching temperature during the preliminary in-air stretching was 130° C., and the in-boric-acid-solution stretching was performed using a boric acid aqueous solution at a solution temperature of 75° C. The total stretching ratio in each of the Examples 8 and 9 was 6.0 which is similar to 5.94 as a total stretching ratio obtained when the stretching ratio during the preliminary in-air stretching in the Example 4 is set to 1.8. Differently, the total stretching ratio of the Example 7 was limited to up to 5.88. This is because the stretching ratio during the in-boric-acid-solution stretching could be set to 4.9 or more, which would be caused by the attainable stretching ratio of non-crystallizable PET having an impact on the relationship between the stretching ratio during the first-stage preliminary in-air stretching and the total stretching ratio, as described based on
Referring to
(5) Improvement in Optical Characteristics of Polarizing Film by Stretching Temperature during Preliminary In-Air Stretching (Examples 10 to 12)
In the Example 4, the stretching temperature during the preliminary in-air stretching was set to 130° C., whereas in the Examples 10 to 12, the stretching temperature during the preliminary in-air stretching was set, respectively, to 95° C., 110° C., and 150° C., which are higher than the glass transition temperature Tg of PVA. In these Examples, the polarizing film was produced under the same conditions as those in the Example 4, except the above difference. For example, the stretching ratio during the preliminary in-air stretching was set to 1.8, and the stretching ratio during the in-boric-acid-solution stretching was set to 3.3. The stretching temperature during the preliminary in-air stretching in the Example 4 is 130° C. In these Examples including the Example 4, the production conditions are the same except that the stretching temperature is set to 95° C. for the Example 10, 110° C. for the Example 11, 130° C. for the Example 4 and 150° C. for the Example 12.
Referring to
(6) Improvement of Optical Characteristics of Polarizing Film by Total Stretching Ratio (Examples 13 to 15)
In the Example 4, the stretching ratio during the first-stage preliminary in-air stretching was 1.8, and the stretching ratio during the second-stage in-boric acid solution stretching was 3.3. On the other hand, in the Examples 13 to 15, only the stretching ratio during the second-stage in-boric acid solution stretching was changed to 2.1, 3.1 and 3.6, respectively. This means that the total stretching ratios in the Examples 13 to 15 are 5.04 (about 5.0), 5.58 (about 5.5) and 6.48 (about 6.5), respectively. The total stretching ratio in the Example 4 is 5.94 (about 6). In these Examples including the Example 4, the production conditions are the same except that the total stretching ratio is set to 5 for the Example 13, 5.5 for the Example 14, 6.0 for the Example 4 and 6.5 for the Example 15.
Referring to
(7) Improvement of Optical Characteristics of Polarizing Film by Total Stretching Ratio in End-Fixed Uniaxial Stretching (Examples 16 to 18)
In the Examples 16 to 18, optical film laminates were produced under the same conditions as those in the Example 4, except the following difference. The difference is a stretching scheme in the preliminary in-air stretching. In the example 4, an end-free uniaxial stretching process is employed, whereas in each of the Examples 16 to 18, an end-fixed uniaxial stretching process is employed. In each of these Examples, the stretching ratio during the first-stage preliminary in-air stretching was fixedly set to 1.8, and only the stretching ratio during the second-stage in-boric-acid-solution stretching was changed to 3.3, 3.9, 4.4, respectively. This means that the total stretching ratio was 5.94 (about 6) for the Example 16, 7.02 (about 7) for the Example 17 and 7.92 (about 8) for the Example 18, respectively. In the Examples 16 to 18, the production conditions are the same except the above difference.
Referring to
In the comparative example 3, under the same conditions as those in the comparative example 1, a PVA aqueous solution was applied on a 200 μm-thick PET substrate and dried to form a laminate including a 7 μm-thick PVA layer formed on the PET substrate. Then, the laminate was immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C. to form a dyed laminate including a PVA layer having iodine absorbed therein. Specifically, the dyed laminate is formed by immersing the laminate in a dyeing solution containing 0.30 wt % of iodine and 2.1 wt % of potassium iodide at a solution temperature of 30° C., for an arbitrary time, to allow the PVA layer making up a target polarizing film (to be finally obtained) to have a single layer transmittance of 40 to 44%. Then, the dyed laminate including the PVA layer having the absorbed iodine was subjected to in-boric-acid-solution stretching at a stretching temperature of 60° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 5.0. In this manner, various optical film laminates each including a 3 μm-thick PVA layer integrally stretched with the PET resin substrate were formed.
(Reference Sample 1)
In the reference sample 1, a continuous web of crystallizable polyethylene terephthalate (hereinafter referred to as “crystallizable PET”) was used as a resin substrate, and a PVA aqueous solution was applied on a 200 μm-thick crystallizable PET substrate and dried to form a laminate including a 7 μm-thick PVA layer formed on the crystallizable PET substrate. A glass transition temperature of the crystallizable PET is 80° C. Then, the formed laminate was subjected to an elevated temperature in-air stretching at a stretching temperature of 110° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 4.0 to thereby form a stretched laminate. Through the stretching, the PVA layer included in the stretched laminate was changed into a 3.3 nm-thick PVA layer having oriented PVA molecules. In the reference sample 1, the laminate could not be stretched at a stretching ratio of 4.0 or more in the elevated temperature in-air stretching at a stretching temperature of 110° C.
In a subsequent dyeing step, the stretched laminate was formed as a dyed laminate in which iodine is absorbed in the 3.3 μm-thick PVA layer having oriented PVA molecules. Specifically, the dyed laminate was formed by immersing the stretched laminate in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C., for an arbitrary time to cause iodine to be absorbed in the PVA layer included in the stretched laminate, so as to allow the PVA layer making up a target polarizing film to have a single layer transmittance of 40 to 44%. An amount of iodine to be absorbed in the PVA layer having oriented PVA molecules was adjusted to produce various dyed laminates different in single layer transmittance and polarization rate. Then, the formed dyed laminate was subjected to cross-linking. Specifically, the dyed laminate was cross-linked by immersing it in a cross-linking boric acid aqueous solution containing 3 weight parts of boric acid with respect to 100 weight parts of water and 3 weight parts of potassium iodide with respect to 100 weight parts of water, at a solution temperature of 40° C. for 60 seconds. The cross-linked dyed laminate in the comparative example 1 corresponds to the optical film laminate in the Example 4. Thus, cleaning, drying and lamination and/or transfer steps in the comparative example 1 are the same as those in the Example 4.
(Reference Sample 2)
In the reference sample 2, a crystallizable PET was used as a resin substrate, and a laminate including a 7 μm-thick PVA layer formed on the crystallizable PET substrate was formed in the same manner as that in the reference sample 1. Then, the formed laminate was subjected to elevated temperature in-air stretching at a stretching temperature of 100° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 4.5 to thereby form a stretched laminate. Through the stretching, the PVA layer included in the stretched laminate was changed into a 3.3 μm-thick PVA layer having oriented PVA molecules. In the reference sample 2, the laminate could not be stretched at a stretching ratio of 4.5 or more in the elevated temperature in-air stretching at a stretching temperature of 100° C.
Then, a dyed laminate was formed from the stretched laminate. The dyed laminate was formed by immersing the stretched laminate in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C., for an arbitrary time to cause iodine to be absorbed in the PVA layer included in the stretched laminate, so as to allow the PVA layer making up a target polarizing film to have a single layer transmittance of 40 to 44%. In the reference sample 2, an amount of iodine to be absorbed in the PVA layer having oriented PVA molecules was adjusted to produce various dyed laminates different in single layer transmittance and polarization rate, as with the reference sample 1.
(Reference Sample 3)
In the reference sample 3, a crystallizable PET was used as a resin substrate, and a laminate including a 7 μm-thick PVA layer formed on the crystallizable PET substrate was formed in the same manner as that in the reference sample 1 or 2. Then, the formed laminate was immersed in a dyeing solution containing iodine and potassium iodide and having a temperature of 30° C., for an arbitrary time to cause iodine to be absorbed in the PVA layer included in the laminate, so as to allow the PVA layer making up a target polarizing film to have a single layer transmittance of 40 to 44%, to form various dyed laminates each including the PVA layer having iodine absorbed therein. Subsequently, the formed dyed laminate was subjected to elevated temperature in-air stretching at a stretching temperature of 90° C. based on an end-free uniaxial stretching process to attain a stretching ratio of 4.5 to thereby form a stretched laminate. Through the stretching, the PVA layer included in the stretched laminate was changed into a 3.3 μm-thick PVA layer having oriented PVA molecules. In the reference sample 3, the laminate could not be stretched at a stretching ratio of 4.5 or more in the elevated temperature in-air stretching at a stretching temperature of 90° C.
(Thickness Measurement)
A thickness of each of the non-crystallizable PET substrate, the crystallizable PET substrate and the PVA layer was measured using a digital micrometer (KC-351C from Anritsu Electric Co., Ltd.).
(Measurement of Transmittance and Polarization Rate)
Each of the single layer transmittance T, the parallel transmittance Tp and the cross transmittance Tc of the polarizing film was measured using a UV-visible spectrophotometer (V7100 from JASCO Corporation). Each value of T, Tp and Tc is presented by a Y value measured according to JIS Z8701 (visual field of 2 degrees, C light source) and corrected for spectral luminous efficacy. The polarization rate P was calculated in accordance with the following formula using the above transmittance.
Polarization rate P={(Tp−Tc)/(Tp+Tc)}1/2×100
(Evaluation of Orientation Function of PET)
A Fourier Transform Infrared Spectrometer (FT-IR) (SPECTRUM 2000 from PerkinElmer, Inc.) was used as the measurement device. Attenuated total reflection (ATR) of polarizing light was measured to evaluate the surface of a PET resin layer. The orientation function was calculated in the following manner. Measurements were made on the polarizing light in the directions of 0° and 90° with respect to the stretching direction. Absorption intensity of the obtained spectral at 1340 cm−1 was used to calculate the orientation function according to the Formula 4 (refer to the non-patent document 1) described below. The condition of f=1 indicates a complete or perfect orientation, whereas the condition f=0 indicates a random orientation. The peak observed at 1340 cm−1 is considered as indicating the absorption induced by a methylene in an ethylene glycol unit of PET.
(Evaluation of Orientation Function of PVA)
A Fourier Transform Infrared Spectrometer (FT-IR) (SPECTRUM 2000 from PerkinElmer, Inc.) was used as the measurement device. Attenuated total reflection (ATR) of polarizing light was measured to evaluate the surface of the PVA resin layer. The orientation function was calculated in the following manner. Measurements were made on the polarizing light in the directions of 0° and 90° with respect to the stretching direction. Absorption Intensity of the obtained spectral at 2941 cm−1 was used to calculate the orientation function according to the above Formula 4. Intensity at 3330 cm−1 was used as a reference peak, intensity at 2941 cm−1/intensity at 3330 cm−1 was calculated as the intensity I. The condition of f=1 indicates the complete or perfect orientation, whereas the condition f=0 indicates a random orientation. The peak observed at 2941 cm−1 is considered to be absorption induced by vibration of the main chain of PVA (—CH2—).
(Evaluation of Crystallization Degree of PVA)
A Fourier Transform Infrared Spectrometer (FT-IR) (SPECTRUM 2000 from PerkinElmer, Inc.) was used as the measurement device. Attenuated total reflection (ATR) of polarizing light was measured to evaluate the surface of the PVA resin layer. The crystallization degree was calculated in the following manner. Measurements were made on the polarizing light in the directions of 0° and 90° with respect to the stretching direction. Intensities of the obtained spectral at 1141 cm−1 and at 1440 cm−1 were used to calculate the crystallization degree. It was preliminarily ascertained that a level of the intensity at 1141 cm−1 is correlated with an amount of crystal, and calculations were made using the intensity at 1440 cm−1 as a reference peak to determine a crystallization index with the following equation (Formula 6). Further, a sample of PVA having a known crystallization degree was used to create a crystallization index and a calibration curve in advance, and the calibration curve was used to calculate the crystallization decree from the crystallization index (Formula 5).
Crystallization degree=63.8×(crystallization index)−44.8 (Formula 5)
Crystallization index=((I(1141 cm−1) 0°+2×I(1141 cm−1))90°/3)/((I(1440 cm−1) 0°+2×I(1440 cm−1))90°/3) (Formula 6)
a, 11b and 12 illustrate examples of optical display devices using the above polarizing film.
a is a sectional view illustrating one example of a fundamental structure of an organic EL display device. This display device 200 comprises an optical display panel 201 in the form of an organic EL display panel, and a polarizing film 203 joined to one surface of the display panel 201 through an optically transparent adhesive layer 202. A ¼ wavelength phase difference film 204 is bonded to an outer surface of the polarizing film 203. Optionally, a transparent window 205 as indicated by the dotted line may be disposed on an outer side of the ¼ wavelength phase difference film 204. This structure is useful when a polarized sunglass is used.
b is a sectional view illustrating another example of the structure of the organic EL display device. This display device 200a comprises an optical display panel 201a in the form of an organic EL display panel, and a ¼ wavelength phase difference film 204a joined to one surface of the display panel 201a through an optically transparent adhesive layer 202a. A polarizing film 203a is bonded to an outer surface of the ¼ wavelength phase difference film 204a. Further, a protective layer 206 is bonded to an outer surface of the polarizing film 203a. Optionally, a transparent window 205a as indicated by the dotted line may be disposed on an outer side of the protective layer 206, i.e., on a viewing side of the optical display device 200a. In this example, outside light is converted to linearly-polarized light through the polarizing film 203a and further converted to circularly-polarized light through the ¼ wavelength phase difference film 204a. This structure is capable of blocking outside light from returning to the viewing side of the optical display device due to reflection by front surface and back surface electrodes, other internal reflection surface of the optical display panel 201a, etc., and effective to prevent internal reflection of outside light.
As a material for joining or bonding together layers or films, it is possible to use, as a base polymer, at least one appropriately selected from the group consisting of acrylic-based polymer, silicone-based polymer, polyester, polyurethane, polyamide, polyether, fluorine or rubber-based polymer, isocyanate-based polymer, polyvinyl alcohol-based polymer, gelatin-based polymer, vinyl or latex-based polymer, and waterborne polyester.
As mentioned above, the polarizing film 203 is formed to have a thickness of 10 μm or less, and satisfy the aforementioned optical characteristics. This polarizing film 203 is extremely thin as compared to polarizing films used in this type of conventional optical display device, so that stress arising from expansion/contraction occurring depending on conditions of temperature or humidity becomes significantly smaller. Thus, it becomes possible to considerably reduce a risk that stress arising from expansion/contraction of the polarizing film causes deformation, such as warp, in the display panel 201 adjacent thereto, and drastically suppress deterioration in quality of display due to the deformation. In this structure, as the adhesive layer 202, a material having a diffusing function may be used, or a two-layer structure of an adhesive layer and a diffusion layer may be employed.
As a material for improving adhesion force of the adhesive layer 202, an anchor layer as disclosed, for example, in JP 2002-258269A (Patent Document 6), JP 2004-078143A (Patent Document 7) and JP 2007-171892A (Patent Document 8), may be provided. A binder resin is not limited to a particular type, as long as it is capable of improving anchoring force of the adhesive layer. Specifically, it is possible to use resin (polymer) having an organic reactive group, such as epoxy-based resins, polyurethane-based resins, polyester-based resins, polymers including an amino group in molecules, ester urethane-based resins, or acrylic-based resins including an oxazoline group.
Further, an antistatic agent as disclosed, for example, in JP 2004-338379A (Patent Document 9) may be added to the anchor layer to provide an antistatic capability thereto. The antistatic agent for providing an antistatic capability may includes an ionic surfactant-based material, a conductive polymer-based material such as polyaniline, polythiophene, polypyrrole or polyquinoxaline, and a metal oxide-based material such as tin oxide, antimony oxide or indium oxide. Particularly in view of optical characteristics, appearance, antistatic effect and stability of antistatic effects during heating or humidification, it is preferable to use the conductive polymer-based material. Among the conductive polymer-based materials, it is particularly preferable to use a water-soluble conductive polymer such as polyaniline or polythiophene, or a water-dispersible conductive polymer. When the water-soluble conductive polymer or the water-dispersible conductive polymer is used as a material for forming an antistatic layer, it becomes possible to suppress transformation of an optical film substrate due to an organic solvent during coating.
The present invention will be specifically described in accordance with a first embodiment taking reference to
The optical film laminate 10 is unrolled from a roll 91 (not illustrated in
The optical film laminate 10 is further fed to a separator-film attaching station 230. In the separator-film attaching station 230, a separator film 231 unrolled from a roll 231a is fed to a nip between a pair of attaching rollers 233, 234 via a guide roller 232, in a posture where it is superimposed on a lower surface of the optical film laminate 10. Just before the separator film 231 is entered into the nip between the rollers 233, 234, an adhesive 235 is supplied between the separator film 231 and the optical film laminate 10 to form a layer, so that the separator film 231 is attached to the optical film laminate 10 through the adhesive layer 235 while passing through between the attaching rollers 233, 234, to form a separator film-attached optical film laminate 240. The separator film-attached optical film laminate 240 is fed via second defect detection means 250, and wound into a roll 260. The second defect detection means 250 comprises second reference-point reading means 251, a light source 252 and a light-receiving device 253. The light-receiving device 253 is adapted to receive light emitted from the light source 252 and reflected by the separator film 231 of the separator film-attached optical film laminate 240 and detect a defect. The second defect detection means 250 is operable to detect any defect existing in the separator film-attached optical film laminate 240, and, when the defect is detected, send information about a feed amount of the separator film-attached optical film laminate 240 in a time period between a time when the reference point is read by the second reference-point reading means 251 (i.e., a time when the reference point passes through the second reference-point reading means 251) and a time when the defect is subsequently detected, to a control section 300a of a second control unit 300. The control section 300a is operable to calculate a length of the separator film-attached optical film laminate 240 between the reference point and the detected defect, based on the information about the feed amount of the laminate 240, and store information about the calculated length in a storage section 300b of the second control unit 300. The information indicative of a defect position may be used to allow the control section 300a to instruct defect-mark printing means 270 to print a defect mark at the defect position on the laminate 240. Alternatively, identification information for identifying the roll 260 of the laminate 240 may be printed on the laminate 240 according to information from the control section 300a. In this case, the defect position information is stored in a storage section 300b of the second control unit 300 in association with the identification information of the roll 260.
The adhesive layer-including optical film laminate 10a is further fed to pass through a reference-point printing section 311. The reference-point printing section 311 is operable to print a reference point on the substrate 1 according to a drive signal from a control section 200a of a control unit 200. Then, the adhesive layer-including optical film laminate 10a is fed to pass through a defect detection section 310. The defect detection section 310 comprises reference-point reading means 312 disposed downstream of the reference-point printing section 311, a light source 313, and a light-receiving device 314 for detecting light emitted from the light source 313 and transmitted through the adhesive layer-including optical film laminate 10a. The defect detection section 310 is operable to detect any defect existing in the adhesive layer-including optical film laminate 10a, and, when the defect is detected, send information about a feed amount of the adhesive layer-including optical film laminate 10a in a time period between a time when the reference point is read by the reference-point reading means 311 (i.e., a time when the reference point passes through the reference-point reading means 311) and a time when the defect is subsequently detected, to the control section 200a of the control unit 200. The control section 200a is operable to calculate a length of the adhesive layer-including optical film laminate 10a between the reference point and the detected defect, based on the information about the feed amount of the laminate 10a, and store information about the calculated length in a storage section 200b of the control unit 200.
As with the first embodiment illustrated in
Then, a separator film 231 is re-attached to the laminate 10a. This separator film 231 may be the separator film previously peeled from the separator film-attached optical film laminate 240, or may be a separator film unrolled from an additional roll. The same element or component of the attaching station In
In the illustrated embodiment, a cutting unit 500 is provided as a means to cut the polarizing film 3 of the laminate 240 into an appropriate size, in connection with a production process for an optical display device, wherein a polarizing film is laminated to a rectangular-shaped liquid-crystal display panel having a long side and a short side. Specifically, the cutting unit 500 is designed to cut a wide separator film-attached optical film laminate 240 into two optical film laminate strips having widths corresponding to respective ones of the long side and the short side of the liquid-crystal display panel.
In
Thus, a first laminate strip 510a having a width corresponding to the short side of the liquid-crystal display panel is formed by the first cutting blade 503a and the second cutting blade 503b, and a second laminate strip 510b having a width corresponding to the long side of the liquid-crystal display panel is formed by the second cutting blade 503b and the third cutting blade 503c. The second laminate strip 510b having a width corresponding to the long side is fed by a pair of feed rollers 511, 512, and directly wound into a roll 520. The first laminate strip 510a having a width corresponding to the short side is guided to a position higher than the second laminate strip 510b by a guide roller 513. Then, the first laminate strip 510a is fed in the lengthwise direction by a pair of feed rollers 514, 515, and wound into a roll 521.
In the present invention, as can be understood from the above embodiment, a continuous web of optical film laminate, i.e., the separator film-attached optical film laminate, is cut along a direction parallel to the length direction as the stretching direction of the polarizing film 3, to form a continuous web of laminate strip having a given width, so that a direction of the absorption axis of the polarizing film 3 conforms to a length direction of the laminate strip with a high degree of accuracy. Heretofore, a wide optical film laminate has been cut to a given width in a state after being wound into a roll. However, this technique is incapable of allowing the absorption axis of the polarizing plate to conform to the length direction of the laminate strip with a high degree of accuracy. As compared to the conventional technique of cutting the laminate in the form of a roll, the technique of the present invention described based on the above embodiment provides remarkably high accuracy. In the above embodiment, the first and third cutting blades 503a, 503b, 503c may be arranged at even intervals to obtain two laminate strips each having the same width. Alternatively, two cutting blades may be used to form a single laminate strip.
The second laminate strip 510b having the slits 621 formed therein is fed to a first polarizing-film lamination station 650. Each of a plurality of the liquid-crystal display panels 600 is fed from a side opposite to the laminate strip 510b to the first polarizing-film lamination station 650 in synchronous relation to a respective one of the polarizing film laminate sheets 622 of the second laminate strip 510b, and the polarizing film laminate sheets 622 are sequentially peeled from the separator film 231, and laminated to respective upper surfaces of corresponding ones of the liquid-crystal display panels 600. The liquid-crystal display panel 600 having the polarizing film 3 laminated to the upper surface thereof is conveyed to a reversing/turning section 660 in a direction perpendicular to a direction along which the liquid-crystal display panel 600 is fed to the first lamination station 650.
On the other hand, the first laminate strip 510a having a width corresponding to the short side is unrolled from the roll 521, and fed in the length direction. The first laminate strip 510a unrolled from the roll 521 is fed to pass under defect-mark reading means 623. The defect-mark reading means 623 is operable to read the defect mark. If no defect mark is detected, it is determined that no defect exists in the first laminate strip 510a, and a plurality of slits 624 are formed at lengthwise intervals corresponding to the long side of the liquid-crystal display panel 600 to extend from a surface of the substrate 1 through the polarizing film 3 and the adhesive layer 235 in a width direction perpendicular to the length direction, up to a depth reaching a surface of the separator film 231, in a half-cut manner. According to the half-cut, a polarizing film laminate sheet 625 comprising the substrate 1, the polarizing film 3 and the adhesive layer 235 is formed between two of the slits 624 located adjacent to each other in the length direction of the first laminate strip 510a. Each of the polarizing film laminate sheets 625 is maintained to adhere on the separate film 231 through the adhesive layer 235.
The first laminate strip 510a having the slits 624 formed therein is fed to a second polarizing-film lamination station 651. After the liquid-crystal display panel 600 having the polarizing film laminate sheet 622 laminated on the upper surface thereof is reversed and turned by 90 degrees in the reversing/turning section 660, the liquid-crystal display panel 600 is conveyed to the second polarizing-film lamination station 651 in a direction perpendicular to the first laminate strip 510a, in synchronous relation with a corresponding one of the polarizing film laminate sheets 625 of the first laminate strip 510a. In the second polarizing-film lamination station 651, the polarizing film laminate sheet 625 is peeled from the separator film 231, and laminated to the other surface of the liquid-crystal display panel 600 facing upwardly after the reversing. Through the above process, the two polarizing films 3 are laminated on respective ones of the opposite surfaces of the liquid-crystal display panel 600 while allowing the absorption axes thereof to orthogonally intersect each other.
When the defect mark is detected on the first laminate strip 510a, two slits 624a, 624b are formed in the first laminate strip 510a in a half-cut manner, respectively, at two positions: one position spaced apart from a downstream edge of the defect mark toward the downstream side by a given distance; and the other position spaced apart from an upstream edge of the defect mark toward the upstream side by a given distance. According to a non-illustrated defective-sheet eject mechanism, a polarizing film laminate sheet 625a formed between the slits 624a, 624b is ejected as a defective sheet to a defective-sheet discharge path, without being fed to the second polarizing film lamination station. Generally, the polarizing film laminate sheet 625a formed between the slits 624a, 624b has a length less than that of the normal polarizing film laminate sheet 625 to be formed between the two adjacent slits 624. Thus, it is possible to reduce a material to be discarded as the defective sheet. However, if a defect has a large size extending in the length direction of the first laminate strip 510a, or a plurality of defects successively exist in the length direction of the first laminate strip 510a, the defective polarizing film laminate sheet 625a will become longer than the normal polarizing film laminate sheet 625. In this case, in order to facilitate ejection of the defective sheet, an additional slit may be formed in an intermediate portion of the long defective polarizing film laminate sheet 625a to reduce a length of one defective polarizing film laminate sheet.
When the defect mark is also detected on the second laminate strip 510b, two slits 621a, 621b are formed in the second laminate strip 510b in a half-cut manner, respectively, at two positions: one position spaced apart from a downstream edge of the defect mark toward the downstream side by a given distance; and the other position spaced apart from an upstream edge of the defect mark toward the upstream side by a given distance. According to a non-illustrated defective-sheet eject mechanism, a polarizing film laminate sheet 622a formed between the slits 621a, 621b is ejected as a defective sheet to a defective-sheet discharge path, without being fed to the first polarizing film lamination station.
Differently from the first and second embodiments illustrated in
In the separator film-attached optical film intermediate laminate 240c formed by peeling the substrate 1 from the optical film laminate, a mark M indicative of a reference point is printed on a surface of the separator film 231 by reference-point printing means 710. Then, the separator film-attached optical film intermediate laminate 240c is fed to a second separator-film attaching station 700 via a length measuring roller 711. The length measuring roller 711 is adapted to measure a feed amount of the laminate 240c and send a measurement signal to laminate-feed-amount calculation means 720a of a storage/calculation unit 720.
In the second separator film attaching station 700, a second separator film 703 unrolled from a roll 703a is fed to be superimposed on a surface of the separator film-attached optical film intermediate laminate 240c from which the substrate 1 is peeled, so that it is attached to the polarizing film 3 by a pair of attaching rollers 701, 702, through an adhesive layer 704, to form a second separator film-attached optical film intermediate laminate 240d.
When the optical film laminate 240d passes through a pair of peeling rollers 910, 911, the separator film 703 is peeled therefrom to form a laminate 240e having a structure in which the adhesive layer 704 adheres to the polarizing film 3 of the separator film-attached optical film intermediate laminate 240c. The peeled separator film 703 is taken up into a roll 703a. On the other hand, the laminate 240e is fed to a protective-film attaching station 740 via a defect inspection station 730. In the protective-film attaching station 740, a protective film 741 is joined to the laminate 240e by a pair of attaching roller 742, 743 through the adhesive layer 704 on the surface of the polarizing film 3 of the laminate 240e, to form a protective film-attached optical film laminate 240f. The protective film-attached optical film laminate 240f formed in the above manner is wound into a roll 260A.
In the third embodiment, the defect inspection station 730 comprises reference-point reading means 731, and transmitted-light detection type optical-defect detection means composed of a light source 732 and a light sensing element 733. A read signal from the reference-point reading means 731 is sent to reference-point-read-time storage means 720b of the storage/calculation unit 720, and the reference-point-read-time storage means 720b is operable to store a clock time when the reference point is detected. A defect detection signal from the optical-defect detection means is sent to defect-detection-time calculation means 720c of the storage/calculation unit 720, and the defect-detection-time calculation means 720c is operable to calculate a clock time when the defect is detected and store the calculated clock time. Respective signals from the laminate-feed-amount calculation means 720a, the reference-point-read-time storage means 720b and the defect-detection-time calculation means 720c are input into a defect-position calculation section 772 of a control unit 770 provided in an optical film laminate forming apparatus. The defect-position calculation section 772 is operable, in response to receiving the input of the above signals, to calculate a defect position as measured from the reference point mark M, and send a signal indicative of the defect position to a defect-position storage section 720d of the storage/calculation unit 720. The defect position information stored in the defect-position storage section 720d is stored in another information storage medium 790 separate from the control unit 770.
Identification information conversion means 773a provided in the control unit 770 is operable to instruct roll-identification-information printing means 762a to print identification information I on the separator film 231 of the optical film laminate 240f to identify the laminate 240f. The information storage medium 790 is adapted to store the identification information in association with the defect position information. Thus, in a subsequent station using the roll 260A of the optical film laminate, the defect position of the roll 260A can be read from the information storage medium 790.
Although the present invention has been described in term of specific exemplary embodiments, it is to be understood that various changes and modifications will be apparent to those skilled in the art. Therefore, the present invention is not limited by the description contained herein or by the drawings, but only by the appended claims and their legal equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-197413 | Sep 2010 | JP | national |
| 2011-108629 | May 2011 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13224000 | Sep 2011 | US |
| Child | 13728473 | US |