Method of producing zinc from chloride solutions which contain chiefly iron, copper and zinc

The invention relates to a method of producing zinc by liquid-liquid extraction from chloride solutions which contain iron, copper and zinc and subsequent electrolysis of zinc from the chloride solution and particularly at removing zinc from those solutions which are formed when complex copper-zinc-lead ores are leached with iron chloride in processes which are known per se. The extraction is carried out on that solution which is formed when the contents of copper possibly has been lowered in known way.
By the method of the invention the lead is, if necessary, precipitated as lead chloride in known way by crystallization at lowered temperature, whereupon the extraction of zinc is carried out on the residual solution, possibly after removal or reduction of the copper contents. The zinc is extracted into the organic phase by means of tri-n-butyl-phosphate (TBP) diluted in an organic solvent, whereupon the organic phase and the lye is separated. The organic phase is before the back-extraction washed with a portion of the product solution in order to remove the chief part of co-extracted copper and iron. Used zinc chloride electrolyte from the subsequent zinc chloride electrolysis is utilized for the back extraction, and the resulting product solution is cleaned for iron and copper and other impurities by known methods and possibly supplied with an organic glazing means of for instance polyacryl type. The zinc chloride electrolysis is preferably carried out in a diaphragm cell. As diaphragm there can be used different qualities of artificial fiber cloth as for instance polypropylene or teflon cloth and there is preferably used DS-anodes and aluminum cathodes. That chlorine which is developed on the anodes is returned to the process, while the zinc is precipitated on the cathodes and removed regularly.
In order to obtain a selective zinc chloride extraction from iron-copper-zinc chloride lye which is formed after the possible reduction of the contents of lead, it is important that the copper concentration does not exceed a certain value, and the inventors have found that the copper concentration should not exceed 50 grams per liter. If the copper concentration in the lye is to be reduced, a part of the copper can be removed in known way, for instance by cementation, electrolysis or hydrogen reduction. The reduction of the copper contents is carried out until the copper concentration has reached the desired value. The feed solution to the zinc extraction step can for instance be taken from the catholyte solution in the copper electrolysis. The zinc concentration in this solution is unaltered.
EXAMPLE I
A bulk concentrate containing iron, copper, zinc and lead with 11% Cu, 25% Fe, 18.4% Zn and 3.7% Pb was leached with a chloride solution containing iron, copper, zinc and lead, and the lead concentration was reduced by crystallization in known way. The lye after the lead crystallization contained 46 grams per liter Cu, 180 grams per liter Fe, 92 grams per liter Zn and 5 grams per liter Pb. In order to reduce the copper concentration to about 25 grams per liter Cu, the solution was first conducted to a diaphragm cell in which it was electrolyzed until the desired concentration was obtained. From the catholyte compartment of the electrolysis cell the solution with the reduced copper contents was conducted to the continuously operating extraction equipment in which the zinc chloride was extracted with TBP diluted by Solvesso 150. The organic phase which contained 22.4 grams per liter Zn was first washed with a part of the product solution from the back extraction step, whereupon it was back extracted with used zinc chloride electrolyte from the zinc electrolysis. This contained 25 grams per liter Zn. The concentration of zinc was hereby increased to 60 grams per liter (g/l hereinafter). Some iron, copper and other impurities was also back extracted, and impurities were as mentioned above removed from the so formed product solution to a content which can be tolerated by the known methods for zinc electrolysis. The product solution was supplied with an organic glazing means in a concentration of 5 parts per million (ppm) and electrolyzed in a diaphragm cell with DS-anodes and aluminum cathodes. The diaphragm consisted of a polypropylene cloth. The ingoing electrolyte (product solution) contained 60 g/l Zn and 4 g/l HCl, while the outgoing contained 25 g/l Zn and 0.5 g/l HCl. The outgoing electrolyte was as mentioned above returned to the back extraction step. The raffinate from the zinc extraction can be used for another leaching of metals after being reoxidized in known way.

FIG. 1 illustrates a preferred closed loop process in a second embodiment of the present invention described in Example II below.
FIG. 2 is a flow diagram of a preferred system for organic extraction of zinc in Example II.
FIG. 3 is a flow diagram of a preferred system for purifying the zinc rich aqueous medium before zinc electrolysis in Example II.

EXAMPLE II
A sulfidic bulk concentrate containing iron, copper, zinc, and lead has been leached with chloride leach liquor by the known red-ox principle. The active oxidized species in the liquor are the ferric ions, and the metal sulfides are attacked according to the equations:
3FeCl.sub.3 +CuFeS.sub.2 =CuCl+4FeCl.sub.2 +S.degree. (1)
ZnS+2FeCl.sub.3 =ZnCl.sub.2 +FeCl.sub.2 =S.degree. (2)
PbS+2FeCl.sub.3 =PbCl.sub.2 +2FeCl.sub.2 +S.degree. (3)
A small amount of the elementary sulfur formed by reactions (1) through (3) is oxidized further to sulfate:
6FeCl.sub.3 +4H.sub.2 O+S.degree.=6FeCl.sub.2 +6HCl+H.sub.2 SO.sub.4 (4)
Pyrite (FeS.sub.2) in the concentrate is not attacked by the ferric ions.
The composition of the leach liquor going into the leach system is (all analyses in g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________150 135 15 25 25 0 48.1 21.1 4.0 5.0______________________________________
To this leach liquor was added a sulfide concentrate with analysis shown below (weight percent):
______________________________________Zn Cu Pb S______________________________________29.0 7.7 8.1 40______________________________________
The leaching was performed in an apparatus described in a copending application. Referring to FIG. 1, the leach liquor to the leaching system is split in two parallel streams. The main (primary) stream 10 is used in a substoichiometric leach with respect to available sulfides in the concentrate, and the secondary stream 12 is used in a superstoichiometric leach on the residue from the primary leach.
With this particular concentrate, the primary leach operation was done at 14 in two tanks, each of 30 liter capacity and made of glassfibre-reinforced polyester (GRP), connected in series. Each tank was equipped with a stirrer of the propeller type, and baffles, to avoid settling of solids in the tanks during operation.
The concentrate was fed to the first leach tank by means of a vibrating screw-feeder and at a rate that gave an amount of leach liquor substoichiometrically to the available metal sulfides in the concentrate.
The ratio of concentrate to leach liquor was 360 grams concentrate per liter of leach liquor added.
The residence time in each tank was one hour, and the temperature 105.degree. C. The slurry from tank No. 1 was fed into tank No. 2 via an overflow connection.
The slurry out of tank No. 2 was pumped to a conventional thickener (not shown) made of rubber-coated steel. The underflow from the thickener, containing the solids, was sent to the secondary leach at 16 for an essentially complete extraction of the remaining metal values.
The remaining solids from the secondary leach, composed mainly of gangue and sulfur, were taken out in a filter press 18 made of polypropylene and operated at 105.degree. C. The fresh leach liquor addition to the secondary stage was, with this particular concentrate, added at a rate that ensured a red/ox potential in the secondary leach tank of 500 mV as measured with the Pt/calomel couple. This ensures essentially complete extraction of the remaining metals in the residue from the primary leach stage.
The leach residue at 20 was washed countercurrently with the HCl solution resulting from the zinc chloride purification (see later).
The overflow from the thickener, containing the metal values as chlorides, and essentially reduced (i.e. no ferric present, and only traces of cupric) was pumped to the lead chloride crystallization stage 22. The analysis of the liquid overflow from the thickener, before entering the crystallizer at 22 was (analysis in g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________153 0 153 38 5 33 104 30 19.5 11.4______________________________________
The crystallizer itself was of the known vacuum-flash type. The temperature of the entering liquid is lowered from the initial 105.degree. C. down to 10.degree. C. by reducing the pressure above the liquid and boiling off water. The lead chloride was collected in a fluidized bed of circulating crystals.
The materials of construction of the crystallizer are titanium and glass in all parts in contact with the liquid. Fluidization of lead chloride crystals was achieved by means of an internal circulation of liquid by a titanium propeller.
The lead chloride particles formed in the circulating liquid grow to a definite size and drop out of the bed and down to the bottom, where they are intermittently removed via a barometric leg.
The liquid leaving the crystallizer has the following composition (analysis in g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________186.3 0 186.3 46.4 6.0 40.4 126.5 12.0 23.7 13.9______________________________________
The increases in iron, copper, zinc, hydrochloric acid, and sulfate concentrations are due to the water evaporation in the vacuum flashing of the hot incoming liquid.
The main part of the lead carried into the system by the concentrate is removed as lead chloride in this step. The balance is precipitated as lead jarosite in the oxidation step.
The produced lead chloride is washed on a filter at 24 and the used wash-water added to the process stream. This decreases the concentrations somewhat (analysis in g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________185.2 0 185.2 46.2 6.0 40.2 125.8 12.0 23.5 13.8______________________________________
This liquid is fed to the cathode compartment 26 in the known copper electrowinning diaphragm cell 28 and is totally reduced by the influence of the current flowing in the cell. The necessary amount of copper to balance out the amount added in the concentrate feed is deposited on the cathodes as a powder, which falls off and sinks to the bottom of the cell. The bottom of the cell is conical, to achieve good collection of the produced copper powder. The powder is intermittently removed from the bottom through an air-operated valve.
Materials of construction in the copper electro-winning cell 28 are GRP and rubber in all parts that are in contact with the liquid. The cathodes were made of titanium, and the anodes were of the so-called DSA type (dimensionally stable anodes, titanium with a noble metal oxide layer).
The electrolysis temperature was in the range of 40.degree.-90.degree. C.
The catholyte in the copper electrowinning cell is used as feed to the zinc solvent extraction at 30. The produced raffinate is returned to the anode compartment 32 of the copper EW cell 28. The importance and great advantage of using the catholyte as feed to the SX system lies in the very large difference in the distribution coefficients for zinc chloride and iron (III) chloride. The table below gives measured values of these coefficients in the actual chloride solution, with the used tri-n-butyl phosphate extractant:
D.sub.Zn =0.25
D.sub.Fe(III) =10
D.sub.Fe(II) =0.012
D.sub.Cu(I) =0.082
D.sub.Cu(II) =0.008
As one sees, the importance of keeping oxidized species (Cu (II) and Fe (III)) at as low as possible values cannot be stressed enough. The influence of copper (II) is caused by the equilibrium between the oxidized and reduced species in the solution:
Cu.sup.2+ +Fe.sup.2+ =Cu.sup.+ +Fe.sup.3+ (5)
This equilibrium will be disturbed when contacting a solution with essentially no iron (III), but measurable amounts of copper (II), with an extractant with a strong affinity for iron (III), as the case is with TBP: ##STR1##
We therefore run the electrolysis at 28 at a red/ox potential (less than 300 mV) that assures us that no ferric is present in the catholyte, and that all the copper is in the cuprous state. This catholyte, with an analysis as given below (analysis in g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________182.7 0 182.7 25.9 0 25.9 124.7 11.9 23.4 13.7______________________________________
The other important advantage of using the catholyte as fed to the SX stage is that copper is at its lowest concentration in this liquid, and coextraction of copper is therefore minimized.
The drop in copper content reflects the production of the same amount of copper that was dissolved from the concentrate in the leaching operation. The small drop in the concentration of the other elements present is caused by washing of the produced copper powder at 26 with water, and the returning of the wash-water to the process solution.
FIG. 2 illustrates a preferred system of TBP solvent extraction of zinc but it will be understood that any conventional extraction and scrub system may be employed. The catholyte from 26 is fed to the mixer-settlers 34 of solvent extraction at 30 where it is contacted with the organic extractant tri-n-butyl-phosphate (TBP). The extractant was diluted with a commercial available diluent, Exxon Solvesso 150. The concentration of the extractant TBP in the diluent was 40 volume percent. The feed solution was cooled to 30.degree. C. by passing it through a titanium heat exchanger (not shown) before it entered the mixer-settlers.
The mixer-settlers 36 were of the known pump-mix type, made in glassfibre reinforced polyester. The dimensions of the mixer (L.times.W.times.H) were 200.times.200.times.200 mm, and the adjoining settler (L.times.W.times.H) 500.times.200.times.200 mm. The mixer-settlers were equipped with lids. A guiding plate (not shown) was located at the inlet of the settler to lower the linear velocity of the emulsion from mixer and inject it at the interphase of the settler. The impellers, with 6 radial blades on both sides, were made in polypropylene. They had a diameter of 100 mm and were operated at 425 rpm. Connections and piping were mostly made in polypropylene, but some polyethylene and a special brand of rubber hose were also used.
Piston type dosage pump were used for metering all the aqueous flows, except for the two recirculating aqueous scrub phases were centrifugal pumps were used. A pneumatic metering pump completely in teflon and glass for all parts in touch with liquid to be pumped, was employed for the organic phase.
Because of the pulsation created by the piston pumps, these flow rates were controlled simply by measuring the amount of liquid within a certain time. The flow rates in the circuits belonging to the centrifugal pumps were checked by rotameters.
The extraction section consists of three mixer-settler stages 36. A fraction of the feed liquor is fed at 38 directly to the last extraction stage, to avoid crud formation due to low acidity, which is caused by the tendency of TBP to extract hydrochloric acid.
The iron scrub at 40 consists of two stages 42, to scrub out most of the coextracted iron. As ferric is extracted to a much higher extent than ferrous, it is essential that both the extraction and the iron-scrub stages are kept inert, and at a low red/ox potential in the aqueous phases.
The copper-scrub section 44 has one stage only. The section is operated under oxidizing conditions, using air as oxidizing agent in the aqueous phase. The reason is that cuprous is more readily extracted by TBP that cupric. Coextracted copper is thus scrubbed out of the organic phase rather effectively by air oxidized aqueous phase. As indicated on the flowsheet in FIG. 2, air is injected only into the aqueous phase. This is performed in a surge/pump tank for the recirculating aqueous phase.
The strip section 46 consists of four stages.
The storage/surge tank for organic phase is not shown on the flowsheet. The tank was located between the strip and the extraction sections 46 and 34, respectively. Further, a tank (not shown) was installed in the raffinate stream to prevent break-through of organic phase to the copper electrowinning cell in case of improper interphase level in the settler of the third extraction stage 36. The tank was supplied with a baffle to let the underflow only to the copper cell.
The preferred flow of liquids in the extraction, scrub and strip stages is illustrated in FIG. 2. As there shown, the TBP is continuously circulated in a closed loop as shown by the heavy black line 48 of FIG. 2. Preferably the extraction at 34 is effected by countercurrent flow of TBP with respect to the catholyte from 26 and if desired any conventional solvent extraction may be employed in place of the mixer-settlers 36.
The aqueous medium used in the stripping and scrub stages is preferably the spent electrolyte from the zinc electrolysis (later described) and the flow of this aqueous medium is shown in the lighter line 50 of FIG. 2. Stripping of the TBP at 46 is carried out in conventional apparatus and preferably mixer-settlers 36 are employed in which the aqueous medium and TBP flow countercurrently. A portion (approximately 10%) of the aqueous medium rich in zinc is bled off at 51 for use in the iron and copper scrub steps at 40 and 44 respectively. Scrubbing is carried out in conventional apparatus such as mixer-settlers 36 and the aqueous scrub solution from 40 and 44 is fed back into the closed loop of the main circuit after the copper electrowinning cell 28 for oxidation and precipitation of iron. The aqueous medium rich in zinc from the strip stage 46 if necessary is pumped to a solution purification at 52 (FIG. 1) to remove any remaining iron and copper and other impurities prior to zinc electrolysis.
The raffinate from the extraction step 34 is returned to the copper electrowinning cell, and purged into the anode compartment 32 of the cell 28.
The analysis of the raffinate to 32 is as follows (g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________188.2 0 188.2 23.3 0 23.3 18.8 13.5 24.6 15.5______________________________________
The necessary amount of ZnCl.sub.2 in the catholyte from 26 is extracted at 34 into the organic phase together with small amounts of copper and iron. The phase volume ratio of aqueous feed flow/organic flow was 0.146.
The concentration profiles over the extraction-, scrub- and strip stages in the SX sequence shown in FIG. 2 were (all values in g/l):
______________________________________Zinc Copper Iron Or- Aque-Stage ganic ous Organic Aqueous Organic Aqueous______________________________________Extrac- 9.80 13.8 1.80 21.8 2.10 175.0tion 3Extrac- 15.40 57.5 2.18 25.3 2.40 180.2tion 2Extrac- 18.00 101.1 2.60 25.9 2.66 182.6tion 1Iron 18.40 83 1.72 36.0 0.96 80.1scrub 2Iron 19.20 84 1.60 34.5 0.74 80.2scrub 1Copper 19.40 83 0.24 89.0 0.70 13.7scrubStrip 4 11.0 75.0 0.0031 0.53 0.0302 2.5Strip 3 6.14 49.1 0.0016 0.013 0.0060 0.092Strip 2 3.36 33.6 0.00084 <0.002 0.0018 0.010Strip 1 1.80 25.6 0.0068 <0.002 0.001 <0.005Strip in -- 22.0 -- 0 -- --Extrac- -- 124.7 -- 25.9 -- 182.7tionfeed in______________________________________
The iron scrub at 40 was 7.6 volume percent of strip in, and the copper scrub at 44 was 3.6 volume percent of strip in.
The strip solution out of mixer-settler 46 No. 4 (strip 4) was approximately equal to the amount of feed solution to the extraction step.
This solution from 46 was submitted to a purification treatment at 52 to decrease the concentrations of iron and copper to acceptable levels. The procedure for the iron removal is shown schematically in FIG. 3. A part of the solution from strip stage 4 (approximately 10%) is treated with lime at 54 to achieve a precipitation of the zinc in the solution as zinc hydroxide.
CaO+ZnCl.sub.2 +H.sub.2 O=Zn(OH).sub.2 (s)+CaCl.sub.2 (7)
The other metals contained in this stream is similarly precipitated as hydroxides. The pH of the resulting solution is around 7.
The produced zinc hydroxide, (eq. 7), also containing the copper and iron precipitate, was separated in conventional manner at 56 from the resulting calcium chloride solution and used as a base to treat the main amount of strip solution at 58.
The calcium chloride solution from the zinc hydroxide precipitation was treated with sulfuric acid at 60 to generate HCl and deposit calcium as gypsum:
CaCl.sub.2 +H.sub.2 SO.sub.4 +2H.sub.2 O=CaSO.sub.4 .multidot.2H.sub.2 O(s)+2HCl (8)
After filtering of the gypsum at 62, the HCl solution was concentrated at 64 and the resulting HCl solution was utilized in the main leaching circuit for washing purposes, to maintain the chloride and red/ox balance in the process as desired.
The zinc hydroxide was added to the main strip solution at 58 to adjust the pH in this solution to 2-2.5, and at the same time air was injected into the solution to oxidize ferrous ions to ferric, and precipitate ferric hydroxide:
Zn(OH).sub.2 (s)+FeCl.sub.2 +1/2H.sub.2 O+1/4O.sub.2 =ZnCl.sub.2 +Fe(OH).sub.3 (s) (9)
The precipitation reaction was done in a stirred GPR vessel at 80.degree. C. and the resulting iron precipitate was taken out by filtration at 66.
The filtrate was pumped to a second GRP tank 68 equipped with stirrer, and here zinc dust was added to precipitate copper:
Zn(s)+CuCl.sub.2 =Cu(s)+ZnCl.sub.2 (10)
Copper cement was removed in a small rubber-lined steel thickener. The purified solution was then re-adjusted to pH 1 at 70 before entering the zinc electrowinning cell 72 (FIG. 1). The analysis of the feed solution to the zinc cell 72 is (g/l):
______________________________________Zn HCl______________________________________78 3.5 No iron, copper, lead or sulfate.______________________________________
The electrolysis was done in a conventional diaphragm cell 72 made from GRP with aluminum cathodes (0.5 m.sup.2 each) and DSA. Diaphragms were made of polypropylene fabric. In this cell, zinc chloride was decomposed:
ZnCl.sub.2 =Zn(s)+Cl.sub.2 (g) (11)
Zinc is deposited on the aluminum cathodes as a solid layer, and the cathodes were stripped every 24 hours. The chlorine gas evolved on the DSA's were returned to the oxidation stage at 74 in the main process to achieve chlorine as well as red/ox balance.
The cathodic current density used in cell 72 was 400 Am.sup.-2, and the anodic current density somewhat higher.
Anolyte from the zinc electrowinning cell, now depleted down to 20 g/l zinc, was returned to the strip stage 46 via a chlorine strip tower (not shown) to remove dissolved chlorine gas. In this tower, made of polypropylene and filled with ceramic saddles, and with a height of 4 m and a diameter of 20 cm, the dissolved chlorine was stripped with compressed air. The resulting air/chlorine mixture was also returned to the oxidation stage at 74 in the main hydrometallurgical circuit.
The liquor from the secondary leach stage 16, 18 and the anolyte from the copper electrowinning operation at 28 may be combined at 76 to enter the air oxidation equipment 78. The analysis of this solution was (g/l):
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.+ Zn Pb HCl SO.sub.4.sup.2-______________________________________155.2 58.3 96.9 25.2 8.0 17.2 48.4 21.6 14.0 9.5______________________________________
Equipment 78 consisted of a GRP tank with effective volume 60 liters, with air distribution in the bottom and an impeller-type air disperger operated at 550 rpm. The temperature was maintained at 80.degree. C. in this tank by means of electric heating elements.
In the air oxidation stage, the iron dissolved in the leach stages is precipitated, partially as sodium jarosite, partially as goethite, and excess acid produced in the leaching of sulfur is used up. Sodium for the jarosite precipitation is added as NaCl. The sulfur oxidized to sulfate in the leaching is also taken care of:
Jarosite formation and sulfate removal at 78:
NaCl+3/4O.sub.2 +6FeCl.sub.2 +2H.sub.2 SO.sub.4 +3H.sub.2 O=NaFe.sub.3 (SO.sub.4).sub.2 (OH).sub.6 (s)+3FeCl.sub.3 +4HCl (12)
A small part of the solubilized lead is precipitated as lead jarosite.
Excess acid removal:
HCl+1/4O.sub.2 +FeCl.sub.2 =FeCl.sub.3 +1/2H.sub.2 O (13)
Goethite precipitation:
3FeCl.sub.2 +3/4O.sub.2 +1/2H.sub.2 O=FeO.OH(s)+2FeCl.sub.3 (14)
HCl and sulfate is consumed, and the red/ox potential partly restored. The jarosite/goethite precipitate amounts to 18 g/l solution. This precipitate is taken out in a polypropylene filter press at 80.
The residue collected in the filter press was washed countercurrently in three stages with water, and the washwater from the last stage added to the main process stream.
The partially oxidized solution, with analysis (g/l) as given below, enters the chlorine oxidation stage at 82.
______________________________________Fe.sub.tot Fe.sup.3+ Fe.sup.2+ Cu.sub.tot Cu.sup.2+ Cu.sup.30 Zn Pb HCl SO.sub.4.sup.2-______________________________________150 63 87 25 25 0 48.4 21.6 4.0 5.0______________________________________
The chlorine oxidation stage 82 is made of a chlorination tower, with height 1.5 m and 20 cm diameter. The tower is filled with ceramic saddles. The partially oxidized solution with the above-mentioned composition was introduced at the top of this tower at a temperature of 80.degree. C., and the chlorine/air gas mixture at the bottom. In its passage down the length of the tower, the solution was oxidized back to its original strength with the chlorine gas coming from the zinc electrowinning operation. The exhaust gas from the oxidation tower was free from chlorine and could be released to the atmosphere. The reason for this is that a residual concentration of 15-25 g/l of ferrous ions is always maintained in the outgoing liquid from the chlorine oxidation tower. The oxidation reaction is:
FeCl+1/2Cl.sub.2 (g)=FeCl.sub.3
The regenerated liquid is now again pumped to the leach section, thus making the process cycle a closed loop.
If desired, the liquor from secondary leaching 16, 18 which has not gone through the metal recovery loop may be fed directly to the chlorine oxidation stage at 84.
About 5 to 10 percent of leach liquor is preferably bled off at 86 for separation of solid impurities as by filtration at 88. The filtrate is recycled back to the main stream of leach liquor.
It will be understood that all changes and modifications of the preferred embodiments of the invention herein chosen for the purpose of illustration which do not depart from the spirit and scope of the invention are intended to be covered.

Number	Name	Date	Kind
3441372	Pegler et al.	Apr 1969
4288304	De Marthe et al.	Sep 1981

Method of producing zinc from chloride solutions which contain chiefly iron, copper and zinc

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

US Referenced Citations (2)

Continuations (1)

Continuation in Parts (1)