Method of providing flow control of heat activated sealant using a combination sealant/flow control agent

Abstract

A method of controlling the flow of a heat activated expandable sealant is provided in which a heat activated sealant is coated with a flow control agent having a melt flow rate which is lower than that of the sealant. The combination sealant/flow control agent is preferably used to seal gaps or cavities in parts such as components in automotive vehicles with minimal sagging.

Description

BACKGROUND OF THE INVENTION

[0002] This invention is directed to a method for providing flow control of heat activated expandable or non-expandable sealants which are used to seal gaps or cavities in parts such as components in automotive vehicles, and more particularly, to such a method which utilizes a sealant in combination with a flow control agent to modulate the flow of the sealant upon heating.

[0003] In the manufacture of automotive vehicles, many body components include cavities which require sealing in order to block the passage of dust, moisture, and air (fumes) which can cause corrosion of the body parts. Such sealants are also used to block the passage of noise through the openings. Heat activated sealants are known in the automotive industry for the purpose of filling such gaps and voids. For example, expandable sealants may be formed into a desired configuration which is adapted to be placed within a body cavity or between two parts so that when the part is subjected to a paint baking operation or other process at elevated temperatures, the shaped sealant expands to an extent that the cavity or area between the parts is filled or sealed. Such heat activated sealants are typically comprised of thermoplastic or thermosetting materials which may contain a blowing agent which is activated upon heating such that the sealant expands and flows into the gaps.

[0004] Heat activated expandable sealants currently in use are typically used to bridge or seal gaps which are less than about 8 to 10 mm. However, when such gaps are greater than about 10 mm (up to 100 mm), it is difficult to achieve proper flow as the adhesive tends to flow excessively, causing unsightly “stalactites”. In addition, the sealant is often unable to expand or flow sufficiently to bridge the larger gaps without excess thinning or blow-out in the gap being sealed.

[0005] It would be desirable to be able to better control the flow of heat activated sealants to eliminate the problems of excessive flow or sag. Accordingly, there is a need in the art for a method of controlling flow of heat activated sealants.

SUMMARY OF THE INVENTION

[0006] The present invention meets that need by providing a flow control agent for use in combination with a heat activated expandable sealant for the purpose of controlling the flow of the sealant upon heating. The sealant/flow control agent combination may be used to seal cavities or gaps in parts such as automotive components with minimal sagging.

[0007] In accordance with one aspect of the present invention, a method for controlling the flow of a heat activated expandable sealant is provided which comprises providing a heat activated expandable sealant, applying a flow control agent to at least a portion of the sealant, and heating the sealant with the flow control agent to cause the sealant to flow. The sealant has a higher melt flow rate than the flow control agent, i.e., the flow control agent is more resistant to flow than the sealant, which allows the flow to be controlled upon heating. By “melt flow rate” (also referred to as melt flow index or melt flow number), it is meant the output rate (flow) of molten resin in grams which would occur in 10 minutes through a standard die of 2.095 mm in diameter and 8.0 mm in length under the action of a standard weight of 2.16 kg at a temperature of 190° C. (see ASTM Standard 1238).

[0008] The melt flow rate of the sealant is greater than the melt flow rate of the flow control agent.

[0009] The expandable sealant of the present invention is preferably in the form of a tack-free, rubber/plastic extruded sheet or thermoformed (shaped) part. The sealant may be thermoformed prior to or after applying the flow control agent.

[0010] The flow control agent is preferably in the form of a liquid coating which is coated on one side of the shaped sealant. In an alternative embodiment, the flow control agent may be in the form of a mesh, film or any other material which controls the amount of flow of the sealant as described above.

[0011] A number of sealants and flow control coatings may be used in the present invention as long as they satisfy the above-described melt flow rate relationship. Accordingly, it should be appreciated that both the sealant and flow control coating may be selected from the group consisting of acrylic resins, styrene-butadiene block copolymers, isoprene butadiene block copolymers, ester gums, ethylene propylene diene rubber, ethylene vinyl acetate, hydrocarbon resins, phenolic resins, polyamides, polyethylene, polyesters, polyolefins, polypropylene, polyvinyl acetate, polyvinylidene chloride, polyvinyl chloride, styrene butadiene, terpolymers, and vinyl acetate.

[0012] The expandable sealant also preferably includes a blowing agent which causes the sealant to expand during heating. The sealant may also include fillers, plasticizers, and curing agents. In a preferred embodiment, the heat activated expandable sealant comprises modified polyethylene, a styrene-butadiene copolymer, a hydrocarbon resin, ethylene vinyl acetate, and a blowing agent.

[0013] The flow control agent preferably comprises a polyvinyl acetate.

[0014] In use, the sealant with the flow control agent is positioned or secured over the cavity of a component and heated to a temperature of between about 250° F. to 400° F. (121° C. to 204° C.) to cause the sealant to flow into and seal the cavity. The use of the flow control agent in combination with the sealant allows the sealant, upon heating, to bridge gaps or cavities in parts that are up to 100 mm and with less sagging than the use of a sealant alone.

[0015] Accordingly, it is a feature of the invention to provide a method for controlling the flow of an expandable sealant. This, and other features and advantages of the present invention, will become apparent from the following detailed description, accompanying drawings, and appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] FIG. 1 illustrates a shaped sealant in accordance with the present invention;

[0017] FIG. 2 illustrates the shaped sealant coated with a flow control coating which has been secured to an automotive part and subjected to a paint bake cycle;

[0018] FIG. 3 illustrates the sag which occurs during heating of the sealant without the use of a flow control agent (scale is in centimeters); and

[0019] FIG. 4 illustrates the minimal sag which occurs with the use of a flow control agent (scale is in centimeters).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0020] The present invention provides a number of advantages over previously used heat activated sealants. By utilizing a flow control agent in combination with the sealant which has a greater resistance to flow than the sealant, the amount of flow of the sealant is minimized and controlled such that no excessive flow or thinning occurs.

[0021] In a preferred embodiment of the invention, the sealant is an expandable sealant comprising a modified polyethylene, a styrene-butadiene copolymer, a hydrocarbon resin, and ethylene vinyl acetate. Examples of such preferred expandable sealants for use in the present invention include RV7172-3, RV7076-3, RV7113-3, and RV7168-3, all commercially available from RuVan Inc. Additional sealants suitable for use in the present invention are also commercially available from RuVan Inc.

[0022] While the invention has been described herein primarily with reference to expandable sealants, it should be appreciated that the flow control agent may also be used in combination with non-expandable sealants. An example of a non-expandable sealant is RV7148-3, commercially available from RuVan Inc.

[0023] Preferred flow control coatings for use in the present invention include latex vinyl chloride house paint, modified (compounded) vinyl-acetate polymers and copolymers, natural rubber latex, synthetic elastomeric polymers such as styrene-butadiene, chloroprene, or nitrile rubbers. More preferred flow control coatings are ethylene-acetate/ethylene vinyl acetate copolymers available from Air Products under the designations Airflex 300 and 400.

[0024] In the preferred method of the present invention in which the sealant is used in an automotive application, the flow control coating is coated over the shaped sealant on at least one side (preferably the side which will be exposed to air) and allowed to dry at ambient temperature or by warm forced air drying. The coating is preferably applied at a dry coating weight of greater than 1.5 g/m2 but less than 50 g/m2 of dry coating (with about 1.5-3 mm sheet thickness of the sealant material).

[0025] The shaped sealant with the flow control coating on its surface is then secured to the desired automotive part as desired by mechanical fixing, by the use of a pressure sensitive adhesive, or by simply placing the sealant in the desired position. The shaped sealant positioned on the part is then processed through a paint bake cycle at a temperature of between about 250° F. to 400° F. (121° C. to 204° C.) for between about 10 to 60 minutes.

[0026] While the preferred method of the invention is to apply the flow control coating after the sealant has been extruded or thermoformed to the desired shape, it should also be appreciated that the coating may also be easily applied prior to the thermoforming operation. In this method, the heat from the thermoforming operation aids in adhering the flow control coating to the sealant and to dry or cure it so that the resulting shaped sealant components may be stacked prior to use.

[0027] In a preferred application, the sealant is shaped to form a pocket sealer for use in sealing holes in the body components of vehicles. FIGS. 1 and 2 illustrate this use of the invention. FIG. 1 is a photograph illustrating the shaped pocket sealer comprised of the expandable sealant. FIG. 2 illustrates the pocket sealer with the flow control coating on its surface after it has been secured to a cavity on the body of the vehicle and baked for 20 minutes at 325° F. (163° C.).

[0028] FIGS. 3 and 4 illustrate the improved flow control obtained by using the flow control agent of the present invention. FIG. 3 illustrates the sag which occurs when the expandable sealant is heated without the use of a flow control agent. FIG. 4 illustrates the sag which occurs when a flow control agent is used in combination with the expandable sealant. As can be seen, minimal sag occurs with the use of the flow control agent.

[0029] While certain representative embodiments and details have been shown for purposes of illustrating the invention, it will be apparent to those skilled in the art that various changes in the methods and apparatus disclosed herein may be made without departing from the scope of the invention, which is defined in the appended claims.

Claims

1. A method for controlling the flow of a heat activated expandable sealant comprising: providing a heat activated expandable sealant; applying a flow control agent to at least a portion of said sealant, said sealant having a higher melt flow rate than said flow control agent; and heating said sealant with said flow control agent to cause said sealant to flow in a controlled manner.

2. The method of claim 1 wherein the melt flow rate of said sealant is greater than the melt flow rate of said flow control agent.

3. The method of claim 1 including thermoforming said sealant into a shape prior to applying said flow control agent.

4. The method of claim 1 including thermoforming said sealant into a shape after applying said flow control agent.

5. The method of claim 1 including securing said sealant with said flow control agent to a component containing a gap or cavity prior to heating.

6. The method of claim 1 wherein said sealant with said flow control agent applied thereto is heated to a temperature of between about 250° F. to 400° F.

7. The method of claim 1 wherein said heat activated expandable sealant and said flow control agent are selected from the group consisting of acrylic resins, styrene-butadiene block copolymers, isoprene butadiene block copolymers, ester gums, ethylene propylene diamene rubber, ethylene vinyl acetate, hydrocarbon resins, phenolic resins, polyamides, polyethylene, polyesters, polyolefins, polypropylene, polyvinyl acetate, polyvinylidene chloride, polyvinyl chloride, styrene butadiene, terpolymers, and vinyl acetate.

8. The method of claim 1 wherein said heat activated expandable sealant includes a blowing agent.

9. The method of claim 1 wherein said heat activated expandable sealant comprises modified polyethylene, a styrene-butadiene copolymer, a hydrocarbon resin, ethylene vinyl acetate, and a blowing agent.

10. The method of claim 1 wherein said flow control agent is selected from the group consisting of latex vinyl chloride paint, modified vinyl-acetate polymers and copolymers, natural rubber latex, synthetic elastomeric polymers, and nitrile rubbers.

11. The method of claim 1 wherein said flow control agent comprises a polyvinyl acetate.

12. The method of claim 1 wherein said flow control agent is in the form of a mesh or film.

13. The method of claim 1 wherein said flow control agent is in the form of a liquid coating.

14. A method for controlling the flow of a non-expandable sealant comprising: providing a non-expandable sealant; applying a flow control agent over at least a portion of the sealant, said sealant having a higher melt flow rate than said flow control agent; and heating said sealant to cause said sealant to flow.

15. In combination, a heat activated expandable sealant and a flow control agent on at least a portion of said sealant, said combination adapted to seal a gap or cavity in a component; said heat activated expandable sealant having a melt flow rate which is higher than the melt flow rate of said flow control agent.

16. The combination of claim 15 wherein said heat activated expandable sealant comprises modified polyethylene, a styrene-butadiene copolymer, a hydrocarbon resin, and ethylene vinyl acetate.

17. The combination of claim 15 wherein said flow control agent coating comprises a polyvinyl acetate.

18. The combination of claim 15 wherein said heat activated expandable sealant is in the form of an extruded sheet or thermoformed part.

19. The combination of claim 15 wherein, upon heating, said heat activated expandable sealant with said flow control agent exhibits less sagging than a heat activated expandable sealant without said flow control agent.

20. A method of sealing a cavity in a component comprising: providing a heat activated expandable sealant; applying a flow control agent to at least a portion of said sealant, said sealant having a higher melt flow rate than said flow control agent; and positioning said heat activated expandable sealant with said flow control agent over said cavity of said component; and heating said sealant and flow control agent to cause said sealant to flow into and seal said cavity.