Claims
- 1. In a method of purifying a bearing steel consisting essentially of carbon, silicon, manganese, phosphorus, sulfur, chromium, aluminum, oxygen, nitrogen and titanium, the remainder being iron together with impurities, the method comprising:
- (i) smelting the bearing steel in a smelting furnace in order to oxidatively scour the steel;
- (ii) pouring the smelted steel into a separate container, performing dephosphorization of the smelted steel and absorbing and removing slag which contains oxide from the steel which floats on top of the smelted steel with a vacuum slag cleaner;
- (iii) conducting reducing refinement of the steel by strongly agitating the smelted steel in the presence of a highly basic slag which has a basicity of not less than 3 while adjusting the temperature of the steel bath, said refinement occurring under an inert atmosphere which is under a pressure greater than normal pressure;
- (iv) performing vacuum degassing of the steel with a circulating vacuum degassing apparatus which imparts strong circulation during two-thirds of the treatment, and weak circulation during one-third of the treatment; and
- (v) performing a reducing refinement on the steel by weakly agitating the smelted steel in a reducing atmosphere at normal pressure, said treatment thereby reducing the amounts of phosphorus, sulfur, aluminum, oxygen, nitrogen and titanium to not more than 0.01%, not more than 0.002%, not more than 0.015%, not more than 0.0006%, not more than 0.005% and not more than 0.0015% by weight respectively.
- 2. The method according to claim 1, wherein said first step (i) comprises smelting said bearing steel in an electric furnace thereby oxidatively refining the steel, and wherein the highly basic slag employed in step (iii) contains a total amount of FeO and MnO which is not more than 0.5% by weight and contains a composition of CaO/SiO.sub.2 /Al.sub.2 O.sub.3 of 0.3 to 0.4.
- 3. The method of claim 1, wherein said bearing steel consists essentially of 0.70 to 1.10% by weight carbon, 0.15 to 1.6% by weight silicon, 0.15 to 1.15% by weight manganese, not more than 0.010% by weight phosphorus, not more than 0.002% by weight sulfur, 0.50 to 1.60% by weight chromium, not more than 0.015% aluminum, not more than 0.0006% by weight oxygen, not more than 0.0050% by weight nitrogen and not more than 0.0015% by weight titanium.
Priority Claims (1)
Number |
Date |
Country |
Kind |
59-50073 |
Mar 1984 |
JPX |
|
Parent Case Info
This is a division of application Ser. No. 707,820, filed Mar. 4, 1985, now U.S. Pat. No. 4,642,219.
US Referenced Citations (3)
Divisions (1)
|
Number |
Date |
Country |
Parent |
707820 |
Mar 1985 |
|