Patent Application
20210171677
The present invention relates to a solution polymerisation process. More specifically, the present invention deals with separating and removing the inert components of the reaction mixture downstream of the polymerisation process.
It is known to produce olefin polymers in solution polymerisation process where the unreacted monomer and comonomer and the solvent are separated from the solution and recycled to the polymerisation process.
WO-A-2009/013217 discloses a process for separating a hydrocarbon-containing feed stream downstream of an olefin polymerisation process. Separation of olefin monomer, comonomer and hydrocarbon diluent is described.
WO-A-2009/090254 discloses a process for recovering unreacted monomer from a slurry or a gas phase polymerisation process.
In spite of the prior art there still remains a need for an efficient process for separating and recovering inert components originating from the comonomer from the polymer solution in a solution polymerisation. For example 1-hexene contains small amount of isomers of hexane and hexene which are not active towards polymerisation. Thus these components start to accumulate in the process making it less efficient. Polymer density control becomes difficult if the inert components are not removed. The present invention provides an efficient process for separating and removing the inert C6 components.
The present invention provides a process for removing hydrocarbons comprising the steps of
characterised in that at least a part of the third bottom stream is withdrawn as a purge stream.
The present invention is directed to a process for polymerising one or more olefins in one or more polymerisation reactors in solution. The solution polymerisation process is typically conducted in a solvent in which the monomer, eventual comonomers, eventual chain transfer agent and the polymer formed in course of the process are dissolved. Such processes are disclosed, among others, in WO-A-1997/036942, WO-A-2006/083515, WO-A-2008/082511, and WO-A-2009/080710.
Polymerisation
The polymerisation may be conducted in one or more polymerisation reactors. It is obvious that where the text refers to one polymerisation reactor it can be equally applied to more than one reactor, and in specific to any one of the reactors.
In the polymerisation reactor olefin monomers having two or more carbon atoms, one or more catalyst systems, optionally one or more comonomers, optionally one or more chain transfer agents, and optionally one or more diluents or solvents are used for conducting a polymerisation. Thus, the polymerisation system is in its dense fluid state and comprises the olefin monomers, any comonomer present, any diluent or solvent present, any chain transfer agent present, and the polymer product.
The olefin monomer is an alpha-olefin having two or more carbon atoms, preferably from 2 to 10 carbon atoms. More preferably the olefin monomer is selected from the group consisting of ethylene, propylene and 1-butene. Especially preferably the olefin monomer is ethylene.
One or more comonomers are optionally and preferably present in the polymerisation reactor. The comonomer is selected from the group consisting of alpha-olefins different from the olefin monomer having from 2 to 10 carbon atoms; polyenes, such as non-conjugated alpha-omega-dienes, having from 4 to 10 carbon atoms, cyclic olefins having from 6 to 20 carbon atoms and cyclic polyenes having from 6 to 20 carbon atoms. Preferably, the comonomer is selected from the group of alpha-olefins different from the olefin monomer having from 2 to 10 carbon atoms, such as 1-butene, 1-hexene and 1-octene when the olefin monomer is ethylene; and ethylene, 1-butene and 1-hexene when the olefin monomer is propylene.
1-hexene is one of the typically used comonomers in solution polymerisation. 1-hexene contains typically 2-3% isomers of hexane and hexene which are not active towards polymerisation, e.g. iso or tertiary hexenes or n-hexane. Since these components are inert to polymerisation they start to accumulate in the process.
The polymerisation catalyst may be any catalyst known in the art which is capable of polymerising the monomer and the optional comonomer. Thus, the polymerisation catalyst may be a Ziegler-Natta catalyst as disclosed in EP-A-280352, EP-A-280353 and EP-A-286148, or it may be a metallocene catalyst as disclosed in WO-A-1993025590, U.S. Pat. No. 5,001,205, WO-A-1987003604 and U.S. Pat. No. 5,001,244, or it may be a combination of these. Also other suitable catalysts, such as late transition metal catalysts, can be used.
A chain transfer agent may be used for controlling the molecular weight of the polymer as it is known in the art. A suitable chain transfer agent is, for instance, hydrogen.
The solvent is suitably present in the polymerisation process. The solvent may be any suitable straight-chain or branched alkyl having from 7 to 20 carbon atoms, a cyclic alkyl, optionally having alkyl substituents, or an aryl, optionally having alkyl substituents, or a mixture of two or more of the above-listed compounds. The solvent must be inert towards the polymerisation catalyst and the monomers. Further, it should be stable in the polymerisation conditions. It further must be able to dissolve the monomer, the eventual comonomers, the eventual chain transfer agent and the polymer in the polymerisation conditions.
The temperature in the polymerisation reactor is such that the polymer formed in the polymerisation reaction is completely dissolved in the reaction mixture comprising the solvent, the comonomer(s), the chain transfer agent and the polymer. The temperature is suitably greater than the melting temperature of the polymer. Thus, when the polymer is a homo- or copolymer of ethylene the temperature is suitably from 120° C. to 220° C., such as from 150° C. to 200° C., depending on the content of comonomer units in the polymer. When the polymer is a homo- or copolymer of propylene the temperature is suitably from 165° C. to 250° C., such as from 170° C. to 220° C., depending on the content of comonomer units in the polymer.
The pressure in the polymerisation reactor depends on the temperature, on one hand, and the type and the amount of the comonomer, on the other hand. The pressure is suitably from 50 to 300 bar, preferably from 50 to 250 bar and more preferably from 70 to 200 bar.
The residence time is short, typically less than 10 minutes.
The process is suitably operated continuously. Thereby streams of monomer, catalyst, and when present streams of comonomer, chain transfer agent and solvent are passed to the polymerisation reactor. A product stream, comprising the unreacted monomer, dissolved polymer and eventual unreacted comonomer and chain transfer agent as well as the eventual solvent is withdrawn from the reactor.
Recovery of Components
The product stream is continuously or intermittently, preferably continuously, withdrawn from the polymerisation reactor. The product stream is then passed to a separation step where a liquid phase comprising the polymer and a vapour phase coexist.
The product stream may be separated in any process step where volatile compounds can be withdrawn from solution. Typically such a process step involves pressure reduction and preferably also heating of the solution. One typical example of such a process step is flashing. For instance, the product stream is heated and then passed along a pipe to a receiving vessel which is operated at a pressure which is substantially lower than the pressure in the polymerisation reactor. Thereby a part of the fluid contained in the solution evaporates and is withdrawn as a vapour stream. The part remaining in the solution with the polymer forms a first concentrated product stream.
Preferably the product stream is heated so that a heated stream is produced. Typically, the temperature of the heated stream is from 200° C. to 300° C., preferably from 210° C. to 270° C. and more preferably from 210° C. to 250° C. Preferably the temperature of the heated stream is from 10° C. to 120° C., more preferably from 20° C. to 100° C. greater than the temperature of the solution in the polymerisation reactor.
The pressure of the product stream is reduced so that the pressure is within the range of from 1 to 15 bar, preferably from 2 to 12 bar and more preferably from 5 to 10 bar. The pressure is preferably reduced so that it is at least from about 40 bar to about 295 bar lower than the pressure in the polymerisation reactor.
In a preferred embodiment the separating step is a flashing step. Thereby a liquid phase and a vapour phase are present in the separating step. The flashing step is suitably conducted in a flash vessel which is a vertical vessel preferably having a generally cylindrical shape. Thereby the flash vessel has a section which has approximately a circular cross-section. Preferably the flash vessel has a cylindrical section which has a shape of a circular cylinder. In addition to the cylindrical section the flash vessel may have additional sections, such as a bottom section, which may be conical, and a top section which may be hemispherical. Alternatively, the flash vessel may also have a generally conical shape.
The temperature in the flash vessel is typically from 130 to 250° C. The temperature should be sufficiently high to keep the viscosity of the solution at a suitable level but less than the temperature where the polymer is degraded. The pressure in the flash vessel is typically from 15 bar to atmospheric, or even less than atmospheric.
The product stream enters the flash vessel at the top. The solution travels downwards in the flash vessel while the gases which evaporate from the solution travel upwards. According to this preferred embodiment the polymer solution forms a thin film which falls downwards in the flash vessel. This facilitates the removal of hydrocarbons from the polymer solution. The gases are typically withdrawn from the top of the flash vessel while the solution is withdrawn from the bottom.
According to an especially preferred embodiment the product stream is sprayed in the flash vessel. The spraying can be done by using one or more suitable nozzles which disperse the solution stream into droplets. Such nozzles are well known in the industry and include air atomising nozzles, flat fan nozzles, hollow cone nozzles and full cone nozzles. Preferably the nozzles break the stream into droplets having the size of not more than about 1 mm.
The nozzle forms a stream of droplets in the flash vessel. The stream of droplets then coagulates within the flash vessel and forms a falling film having a relatively high surface area. This enhances the mass transfer of the volatile components from the solution.
As described above the flash vessel can have a vertical generally cylindrical shape. Then the stream of droplets is directed tangentially with the wall of the flash vessel by a suitable position of the nozzle. Thus, the nozzle is suitably located relatively near to the wall so that its outlet is directed tangentially with the wall. When the stream of the droplets exits the nozzle it moves in the direction of the wall forming a downwards falling film. It is also possible that the flash vessel has a vertical generally conical shape. In such embodiment it is possible to direct the stream of the droplets tangentially with the wall of the flash vessel, as described above. However, it is also possible direct the droplets axially towards the wall of the flash vessel. The nozzle or the nozzles are then arranged eccentrically within the flash vessel. In both arrangements the polymer solution forms a falling film within the flash vessel.
The polymer content in a first concentrated product stream withdrawn from the flashing stage is typically from 35 to 99% by weight. In other words, the first concentrated product stream withdrawn from the first flashing stage contains from 1 to 65% by weight of residual hydrocarbons.
When viewed from a different angle, the hydrocarbon stream withdrawn from the flash vessel is from 35 to 80% by weight from the total material streams withdrawn from the flash vessel. The hydrocarbon stream typically comprises unreacted monomer and also solvent and unreacted comonomer.
By using the flash as described above it is possible to achieve high separation efficiency. For instance, separation efficiency for hydrocarbons containing 6 carbon atoms is at least 75 and preferably at least 80%. Additionally still, separation efficiency for hydrocarbons containing 8 carbon atoms is at least 60% and preferably at least 65%. The separation efficiency is defined as the mass flow of the component withdrawn in the vapour stream divided by the (theoretical) mass flow rate of the component in the vapour stream in equilibrium conditions.
The first concentrated product stream contains the polymer, dissolved in solvent and unreacted comonomer. It may also contain residual monomer which still remains in the solution. Typically the polymer concentration in the first concentrated product stream is from 40% by weight to 90% by weight, preferably from 50 to 80% by weight and most preferably from 60 to 75 by weight, based on the total weight content of the first concentrated product stream. The first concentrated product stream is then typically in liquid phase. The first concentrated product stream may, however, contain a minor amount of vapour, such as vapour bubbles. The amount of vapour in the first concentrated product stream is typically not more than 40 by volume, preferably not more than 30% by volume and especially preferably not more than 20% by volume, such as not more than 10% by volume or not more than 5% by volume.
The vapour stream contains unreacted monomer and other volatile compounds, such as hydrogen. The vapour stream may also contain some of the solvent and comonomer. The vapour stream can optionally comprise a small amount of liquid droplets. The amount of such droplets is typically not more than 40% by volume, preferably not more than 30% by volume and especially preferably not more than 20% by volume.
The first concentrated product stream is then passed to subsequent process steps. Preferably the subsequent process steps include at least one further separation step, more preferably at least two further separation steps. Such further separation steps can be performed, for instance, in a similar way as in the separation step described above. Further vapour streams are withdrawn from the further separation steps.
In a preferred embodiment of the invention the product stream is passed to three subsequent flashing steps.
From any of the separation and further separation steps a part of the vapour or further vapour streams can be directed to a fractionation step, preferably to a first fractionator.
A stream of a solution denotes hereinafter the product stream withdrawn from the polymerisation reactor, the first concentrated product stream withdrawn from a first separator, a second concentrated product stream withdrawn from a second separator or any other concentrated product stream withdrawn from any subsequent separator.
A separator denotes hereinafter the first separator, the second separator, a third separator or any subsequent separator.
A concentrated solution stream denotes hereinafter the solution stream withdrawn from the separator.
A vapour stream denotes hereinafter any of the vapour or further vapour streams or a combination of them.
In the present invention, a stream of a solution preferably comprising 1-hexene and a solvent comprising 7 or more carbon atoms, such as n-octane, is passed to a separator. In the separator a liquid phase comprising the polymer and a vapour phase coexist. A concentrated solution stream and a vapour stream are withdrawn from the separator. At least a part of the vapour stream is passed to a first fractionator. A part of the vapour streams from any of the preceding separation steps can also be passed to the first fractionator.
A first overhead stream and a first bottom stream are withdrawn from the first fractionator. The first fractionator may be any device where the first overhead steam can be separated from the first bottom stream. It is suitably a distillation column or a stripping column. The first bottom stream comprises solvent and hydrocarbons having 9 or more carbon atoms. The first overhead stream comprises solvent, monomer and nitrogen.
The first overhead stream from the first fractionator is passed to a second fractionator. The second fractionator may be any device suitable for separating a second overhead stream from a second bottom stream, for example a distillation column, a stripping column, a multi-phase separator, an extractor or a liquid-liquid separator. The second overhead stream comprising monomer and 1-hexene and the second bottom stream are withdrawn from the second fractionator.
The second overhead stream from the second fractionator is passed to a third fractionator. The third fractionator may be any device suitable for separating a third overhead stream from a third bottom stream. The third fractionator is suitably a distillation column or a stripping column. The third overhead stream comprising monomer and the third bottom stream comprising 1-hexene are withdrawn from the third fractionator. A part of the third bottom stream may be passed to the polymerisation reactor via a feed vessel. A part of the third overhead stream may be passed to the polymerisation reactor via the feed vessel. The third bottom and overhead streams may be subjected to extra steps, such as a purification step, before entering the feed vessel.
A part of the third bottom stream is withdrawn as a purge stream. Inert C6 components, such as isomers of 1-hexene and n-hexane, are removed in the purge stream. The purge stream can be recovered and further used as a gasoline. It is possible to use it also as a fuel additive.
The value of the purge stream can be increased by isomerisation and/or hydrogenation. In a preferred aspect of the invention, the purge stream is recovered and further used. In a more preferred aspect of the invention, the purge stream is recovered, subjected to an isomerisation and/or hydrogenation treatment and further used.
The first bottom stream from the first fractionator is passed to a fourth fractionator. The fourth fractionator may be any device suitable for separating a fourth overhead stream from a fourth bottom stream. The fourth fractionator is suitably a distillation column or a stripping column.
The fourth overhead stream comprising solvent and the fourth bottom stream comprising hydrocarbons having 9 or more carbon atoms are withdrawn from the fourth fractionator. A part of the fourth overhead stream may be passed to the polymerisation reactor via the feed vessel. The fourth overhead stream may be subjected to extra steps, such as a purification step, before entering the feed vessel.
Since inert C6 components are separated and removed from the process, they don't accumulate in the process. When the inert components are removed, the energy consumption of the process and the cost of operation are reduced due to the decreased recycle amounts. These components can be further used as such or they can be treated for instance by isomerising or hydrogenating.
In
Computer simulations were performed using Aspen 8.8 computer software. In the simulation ethylene and 1-hexene were polymerised in n-octane in a polymerisation reactor. A product stream was withdrawn from the polymerisation reactor. The product stream was subjected to three subsequent flashing steps. From each flashing step a part of a vapour stream was directed to a first fractionator. An overhead stream from the first fractionator was passed to a second fractionator. An overhead stream from the second fractionator was passed to a third fractionator. In Inventive Example a part of a bottom stream from the third fractionator was recovered as a purge stream from line (40). In Comparative Example a part of the overhead stream from the first fractionator was recovered as purge stream from line (36). The purge streams in different positions are compared in Table 1.
From the comparison it can be seen that the C6 and C8 flows are almost similar in IE and CE. However, ethylene and ethane are absent in IE. This is beneficial since no separation of C2 is needed if the purge stream is recovered from line (40).
| Number | Date | Country | Kind |
|---|---|---|---|
| 17205096.5 | Dec 2017 | EP | regional |