Patent Grant
10774471
This application claims priority to Korean Patent Application No. 10-2018-0012374 filed on Jan. 31, 2018, and all the benefits accruing therefrom under 35 U.S.C. § 119, the contents of which is incorporated by reference in its entirety.
The present disclosure relates to a method of recycling a by-product generated in a papermaking process.
In general, activities for conserving energy and resource are tasks that should be continuously carried out at individual, enterprise, national and global levels. Among these, in the paper industry, which consumes a large amount of resources and energy such as water and natural wood, the conservation of energy through saving resources by recycling waste paper and reducing water as well as through development of new processes is being regarded as a challenge the paper industry should pursue. Also, the development of technology for improving the physical properties of recycled paper through the use of appropriate fillers is being recognized as a very important research field domestically and internationally. In particular, the recycling of waste paper protects forests through the reduction of natural wood used for pulp and thereby it is possible to obtain reduction of greenhouse gas emissions. The recycling of 1 ton of general waste paper can protect 20 trees, reduce the waste energy used for drying paper and slurry of about 1550 Btu, and reduce 100 kg of waste and 50 kg of carbon dioxide emissions. The amount of waste paper recycled of some domestic enterprise reaches up to 500,000 tons per year, which results to saving about 10 million trees and 2.32×1011 Btu/year and reducing 135×105 tons/year of waste and 6.8 million ton/year of carbon dioxide emissions. In other words, the recycling of waste paper is an industry that has a very high environmental-friendly effect of reducing waste and carbon dioxide emissions as well as saving energy and natural forest resources.
However, there has been a problem in that by-products such as lime mud and lime kiln CaO are produced and they need to be treated.
As a prior art related thereto, Korean Granted Patent Publication No. 10-1585312 B1 and Korean Granted Patent Publication No. 10-0997254 B1.
The present disclosure is directed to providing a method of recycling a by-product generated in a papermaking process that treats the by-product generated in the papermaking process so as to enable it to be reused in a papermaking process.
The problems to be solved by the present disclosure are not limited to the above-mentioned problem(s), and other problem(s) not mentioned can be clearly understood by those skilled in the art from the following description.
According to an aspect of the present disclosure, a method of recycling a by-product generated in a papermaking process may include, pulverizing a by-product produced in a papermaking process to prepare a pulverized product, burning the pulverized product to prepare a burned product, hydrating the burned product to prepare a hydrate, and manufacturing paper from the hydrate and a paper slurry.
In one embodiment, the by-product generated in the papermaking process may include one or more of lime mud and lime kiln CaO.
In one embodiment, burning the pulverized product may be performed at a temperature of 900 to 1,300° C. for 0.5 to 3 hours.
In one embodiment, hydrating the burned product may be performed at a temperature of 20 to 90° C. for 3 to 12 hours after adding water.
In one embodiment, the hydrate may be Ca(OH)2.
In one embodiment, manufacturing the paper may include, adding the paper slurry into a reaction tank, adding the hydrate into the reaction tank and mixing to form a mixture, injecting CO2 gas into the mixture, and adding the CO2 gas-injected mixture to a sheet former for molding into paper.
In one embodiment, the CO2 gas may be injected into the mixture at an injection rate of 50 cc/min.
The paper slurry may be deinked pulp slurry.
According to an aspect of the present disclosure, a paper may be molded by adding a by-product generated in a papermaking process and a paper slurry into a sheet former, and the by-product generated in the papermaking process may include one or more of lime mud and lime kiln CaO.
In one embodiment, the by-product may be a hydrate that was hydrated after being burned.
In one embodiment, a whiteness of the paper may be 80 to 90.
When a method of recycling a by-product generated in a papermaking process according to the present disclosure is used, it is possible to reuse by-products generated in conventional papermaking processes such as lime mud and lime kiln CaO, which is environmentally friendly as well as cost-effective.
Further, the level of whiteness of lime mud and lime kiln CaO which are by-products generated in a papermaking process can be improved to that of an high-grade raw material, and thereby it is possible to also improve the whiteness of paper.
The advantages and features of the present disclosure and the manner of accomplishing it will become apparent with reference to the embodiments described in detail below with reference to the accompanying drawings. The present disclosure may, however, be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art, and the invention is only defined by the scope of the claims.
The shapes, sizes, ratios, angles, numbers and the like disclosed in the drawings for describing the embodiments of the present disclosure are illustrative, and thus the present invention is not limited thereto. Like reference numerals refer to like elements throughout the specification.
In the following description of the present disclosure, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present disclosure rather unclear.
In the following description of the present disclosure, a detailed description of known related arts will be omitted when it is determined that the gist of the present invention may be unnecessarily obscured.
In the case where the word ‘includes’, ‘having’, ‘consists’, etc. are used in this specification, other parts may be added unless ‘only˜’ is used. Unless the context clearly dictates otherwise, in a case where a configuration is expressed in singular form, a case of including the same in plurality may be included.
In the case of describing positional relationship, for example, if the positional relationship between two parts is described as ‘on’, ‘on an upper part’, ‘on a lower part’, ‘next to’, and so on, unless ‘immediately’ or ‘directly’ is used, one or more other parts may be positioned between the two parts.
In the case of describing temporal relationship, for example, if a temporal posterior relationship is described by ‘after’, ‘following’, ‘and then’, ‘before’, and so on, unless ‘immediately’ or ‘directly’ is used, a case of being non-continuous may be included.
It is to be understood that each of the features of the various embodiments of the present disclosure may be coupled or combined with each other, partially or entirely, and technically various interlocking and driving are possible, and that the embodiments may be practiced independently of each other as well as practiced together in association.
The present disclosure is characterized in that it is configured to include pulverizing a by-product produced in a papermaking process to prepare a pulverized product in step S100, burning the pulverized product to prepare a burned product in step S200, hydrating the burned product to prepare a hydrate in step S300, and manufacturing paper from the hydrate and a paper slurry in step S400.
The present disclosure is directed to provide a method of recycling a by-product generated in a papermaking process that treats the by-product generated in the papermaking process so as to enable it to be reused in a papermaking process.
When a method of recycling a by-product generated in a papermaking process according to the present disclosure is used, it is possible to reuse by-products generated in conventional papermaking processes such as lime mud and lime kiln CaO, which is environmentally friendly as well as cost-effective. Further, the level of whiteness of lime mud and lime kiln CaO which are by-products generated in a papermaking process can be improved to that of a high-grade raw material, and thereby it is possible to also improve the whiteness of paper.
Hereinafter, referring to
A method of recycling a by-product generated in a papermaking process according to an embodiment of the present disclosure is characterized in that it includes pulverizing a by-product produced in a papermaking process to prepare a pulverized product in step S100, burning the pulverized product to prepare a burned product in step S200, hydrating the burned product to prepare a hydrate in step S300, and manufacturing paper from the hydrate and a paper slurry in step S400.
In the method of recycling a by-product generated in a papermaking process according to an embodiment of the present disclosure, a by-product produced in a papermaking process is pulverized to prepare a pulverized product in step S100.
The method of pulverizing the by-product to prepare the pulverized product is not limited.
The by-product of step S100 generated in the papermaking process may include one or more of lime mud and lime kiln CaO.
The lime mud may be a by-product having a greenish powder form, and the lime kiln CaO may be in a yellowish clinker form.
The reason for pulverizing of the by-product in step S100 is to increase the surface area of the by-product, such as lime mud and lime kiln CaO, to improve reaction.
In the method of recycling a by-product generated in a papermaking process according to an embodiment of the present disclosure, the pulverized product of step S100 is burned to prepare a burned product in step S200.
The burning of the pulverized product in step S200 may be performed at a temperature of 900 to 1,300° C. for 0.5 to 3 hours, and more particularly, at a temperature of 1,000 to 1,200° C. for 1 to 2 hours
When the temperature is 900° C. or less, the whiteness of the by-product decreases and thus causes a problem of lowering the quality of paper which the final product. When the temperature is 1,300° C. or more, it is not cost-effective due to high energy consumption, and so the above-mentioned range is preferable.
In the method of recycling a by-product generated in a papermaking process according to an embodiment of the present disclosure, the burned product of step S200 is hydrated to prepare a hydrate in step S300.
The hydrate prepared in step S300 may be Ca(OH)2.
Hydrating the burned product in step S300 may be performed at a temperature of 20 to 90° C. for 3 to 12 hours after adding water to the burned product of step S200, and more particularly at a temperature of 30 to 80° C. for 3 to 12 hours.
When the temperature is 20° C. or less, the whiteness of the by-product decreases and thus causes a problem of lowering the quality of paper which is the final product. When the temperature is 90° C. or more, it causes degeneration of the by-product, and so the above-mentioned range is preferable.
Likewise, when the reaction time is out of range of the 3 to 12 hours, it causes the problem of the whiteness of the by-product decreasing, and so the above-mentioned range is preferable.
In the method of recycling a by-product generated in a papermaking process according to an embodiment of the present disclosure, paper is manufactured from the hydrate of step S300 and a paper slurry in step S400.
Manufacturing paper in step S400 may include processes of, adding the paper slurry of step into a reaction tank, adding the hydrate of step S300 into the reaction tank and mixing to form a mixture, injecting CO2 gas into the mixture, and adding the CO2 gas-injected mixture to a sheet former for molding into paper.
The CO2 gas may be injected into the mixture at an injection rate of 50 cc/min.
The paper slurry may be deinked pulp slurry.
Paper according to an embodiment of the present disclosure may be molded by adding a by-product generated in a papermaking process and paper slurry into a sheet former, and the by-product generated in the papermaking process may include one or more of lime mud and lime kiln CaO.
The by-product may be a hydrate that was hydrated after being burned.
The whiteness of the paper may be 80 to 90.
Hereinafter, referring to examples and experimental examples, the present disclosure will be described in further detail. However, the following examples and experimental examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
The lime kiln CaO generated as a by-product in a papermaking process was pulverized to be prepared.
Then, the pulverized lime kiln CaO was hydrated at a temperature of 80° C. for 6 hours to prepare a hydrate.
The same procedure as Example 1 was followed except that the pulverized lime kiln CaO was hydrated at 30° C. for 6 hours to prepare a hydrate.
The same procedure as Example 1 was followed except that the pulverized lime kiln CaO was hydrated at 80° C. for 3 hours to prepare a hydrate.
The same procedure as Example 1 was followed except that the pulverized lime kiln CaO was hydrated at 80° C. for 6 hours to prepare a hydrate.
The same procedure as Example 1 was followed except that the pulverized lime kiln CaO was hydrated at 80° C. for 12 hours to prepare a hydrate.
The lime kiln CaO generated as a by-product in a papermaking process was pulverized to be prepared.
Then, the pulverized lime kiln CaO was burned at a temperature of 1,200° C. for 2 hours to prepare a burned product.
The lime kiln CaO generated as a by-product in a papermaking process was pulverized to be prepared.
Next, the pulverized lime kiln CaO was burned at a temperature of 1,200° C. for 2 hours and then was hydrated at 80° C. for 6 hours to prepare a hydrate.
The same procedure as Example 7 was followed except that the burned lime kiln CaO was hydrated at 80° C. for 12 hours to prepare a hydrate.
The lime mud generated as a by-product in a papermaking process was pulverized to be prepared.
Then, the pulverized lime mud was hydrated at 80° C. for 6 hours to prepare a hydrate.
The lime mud generated as a by-product in a papermaking process was pulverized to be prepared.
Next, the pulverized lime mud was burned at a temperature of 1,200° C. for 2 hours and then was hydrated at 80° C. for 3 hours to prepare a hydrate.
The same procedure as Example 10 was followed except that pulverized lime mud was burned at a temperature of 1,000° C.
The same procedure as Example 11 was followed except that the burned product was hydrated at 80° C. for 6 hours to prepare a hydrate.
The same procedure as Example 10 was followed except that the burned product was hydrated at 80° C. for 6 hours to prepare a hydrate.
The same procedure as Example 10 was followed except that the burned product was hydrated at 80° C. for 12 hours to prepare a hydrate.
The lime mud generated as a by-product in a papermaking process was pulverized to be prepared.
The pulverized lime mud was burned at a temperature of 1,200° C. for 2 hours to prepare a burned product.
The quicklime of company B (Comparative Example 1), quicklime of company P (Comparative Example 2), limestone of company D (Comparative Example 3), and quicklime of company W (Comparative Example 4), which are sold on the market were purchased and prepared.
<Analysis>
1. Property Analysis of By-Products Lime Mud and Lime Kiln CaO
Lime mud and lime kiln CaO are by-products generated in the process of making pulp in Moorim P&P CO., LTD. as shown in
The lime mud is a by-product having a slightly greenish powder form and the lime kiln CaO is in a yellowish clinker form.
Tables 1 and 2 below show the chemical composition (XRF analysis) of lime mud, lime kiln CaO, mined high-grade limestone and Comparative Examples 1 to 3.
As can be seen from Tables 1 and 2, there is a difference in impurities such as SiO2 and Al2O3 components of lime mud and lime kiln CaO as compared with Comparative Examples 1 to 3, but it can be confirmed that the component of CaO is an excellent by-product.
Tables 3 and 4 below show mineral analysis (XRD analysis) of limestone mud, lime kiln CaO, mined high-grade limestone and Comparative Examples 3 and 4.
Referring to Tables 3, 4, and
2. Characteristic Analysis of Burning and Hydrating Reactions of Lime Kiln CaO
Referring to
From this, it can be seen that the color of the hydrated substance becomes brighter as the temperature is higher.
3. FT-IR Analysis of Lime Kiln CaO and Measurement of Whiteness
Referring to
Table 5 below shows the results of the measurement of whiteness of lime kiln CaO, Example 1, Example 6, Example 7 and Example 8. (Whiteness is set as a maximum of 100, the standard of a general A4 paper)
As shown in Table 5, lime kiln CaO as a by-product, has a whiteness of about 70.33 and is a yellow-greenish raw material. However, after hydration at 80° C. (Example 1), the whiteness increased 27% to 89.43. In particular, Example 7, where the by-product was hydrated after burning, also showed similar values of 88.18, indicating that the degree of whiteness was increased by hydrating the by-product, lime kiln CaO.
4. Characteristic Analysis of Burning and Hydrating Reactions of Lime Mud
Referring to
5. FT-IR Analysis of Lime Mud and Measurement of Whiteness
Referring to
Table 6 below shows the results of the measurement of whiteness of lime mud, Example 9, Example 13, Example 14 and Example 15. (Whiteness is set as a maximum of 100, the standard of a general A4 paper)
As shown in Table 6, lime mud as a by-product, has a whiteness of about 78.88 and is a greenish raw material, but after hydration at 80° C. (Example 9), the whiteness increased slightly to 80.53. However, Example 14 wherein hydration after burning was performed, the whiteness increased 13%. As a result, it was found that the whiteness increases when the lime mud is hydrated after burning.
On the basis of the above analysis, Examples 9 and 14 were used to prepare a hand-sheet using a laboratory scale sheet former.
Tables 7 and 8 chart the whiteness and experimental conditions of the manufactured paper.
Examples 9 and 14 were used as fillers in the paper manufacturing, and waste paper generated in a papermaking process in Moorim P&P CO., LTD was reused as pulp.
As shown in Table 7, it can be seen that the whiteness of the hand-sheet using Example 9 alone was 82.03, which was usable as a recycled paper. In the case of using Example 9 and a reagent grade Ca(OH), it can be seen that the whiteness of the hand-sheet is improved to 85 to 86. Based thereon, it was found that it could be fully utilized in waste paper recycling.
As shown in Table 8, it can be seen that the whiteness of the hand-sheet using Example 14 alone was 77.97, which was usable as a recycled paper and had a lower whiteness than when lime mud was used. In the case of adding and using Example 14 and a reagent grade Ca(OH) at the same time, it can be seen that the whiteness of the hand-sheet is improved to 90. Based thereon, it was found that it could be fully utilized in waste paper recycling.
Pulp slurry was prepared by setting the weight ratio of deinked pulp to 3% (where the weight ratio is the weight ratio of the dried deinked pulp when the mixed weight ratio of dried deinking pulp and water is 100%), and then 10%, 20%, 30% of Example 9 and Example 14 were added. Each of Examples 9 and 14 was added to the slurry, thoroughly stirred and then ground.
The final basis weight was maintained at 80 g/m2 and a round sheet machine was used. The wetted wet sheet was dewatered sufficiently and then press dried through a drum type dryer.
The present disclosure is directed to providing a method of recycling a by-product generated in a papermaking process that treats the by-product generated in the papermaking process so as to enable it to be reused in a papermaking process.
When a method of recycling a by-product generated in a papermaking process according to the present disclosure is used, it is possible to reuse by-products generated in conventional papermaking processes such as lime mud and lime kiln CaO, which is environmentally friendly as well as cost-effective. Further, the level of whiteness of lime mud and lime kiln CaO which are by-products generated in a papermaking process can be improved to that of a high-grade raw material, and thereby it is possible to also improve the whiteness of paper.
Although detailed embodiments of a method of recycling a by-product generated in a papermaking process according to the present disclosure have been described above, it is apparent that various modifications can be made without departing from the scope of the present disclosure.
Therefore, the scope of the present invention should not be limited to the embodiments described, but should be determined by the equivalents of the claims, as well as the following claims.
It is to be understood that the above-mentioned embodiments are illustrative and not restrictive in all respects and that the scope of the present invention is indicated by the appended claims rather than the above-mentioned description, and all changes or modifications derived from the equivalents thereof should be construed as being included within the scope of the present invention.
S100: Preparing a pulverized product
S200: Preparing a burned product
S300: Preparing a hydrate
S400: Manufacturing into paper
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2018-0012374 | Jan 2018 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5075017 | Hossain | Dec 1991 | A |
| 5665205 | Srivatsa | Sep 1997 | A |
| 5711802 | Theil | Jan 1998 | A |
| 5897700 | Manning | Apr 1999 | A |
| 9637404 | Minnich | May 2017 | B2 |
| 20070062652 | Doelle | Mar 2007 | A1 |
| 20090294083 | Nanba et al. | Dec 2009 | A1 |
| 20120328497 | Higgs | Dec 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| H06073690 | Mar 1994 | JP |
| 2008-207173 | Sep 2008 | JP |
| 100997254 | Nov 2010 | KR |
| 101232633 | Feb 2013 | KR |
| 101585312 | Jan 2016 | KR |
| WO-2012002324 | Jan 2012 | WO |
| Entry |
|---|
| Machine translation of KR20100032545,European Patent Office,[online], retr. Oct. 19, 2019,[retr. from the Internet],<URL:https://worldwide.espacenet.com/publicationDetails/description?CC=KR&NR=20100032545A&KC=A&FT=D&ND=3&date=20100326&DB=&locale=en_EP#>. (Year: 2010). |
| Korean Office Action for corresponding Korean Application No. 10-2018-0012374 dated Mar. 27, 2018. |
| Australian Office Action dated Jun. 26, 2018 for Australian Application No. 2018201033. |
| Office Action issued by the Intellectual Property Office of the Philippines dated Jul. 2, 2018 for Philippine Application No. 1/2018/000050. |
| Hassan Z. Harraz, “Beneficiation and Mineral Processing of Calcium Carbonate and Calcium Sulphate” Aug. 3, 2017, pp. 10-28. |
| Hazem S. Ahmed et al., “Utilization of Lime-mud as a Filler in Paper Making”, Chemistry Department, Faculty of Science, Assiut University, Assuit Egypt, Quena Paper Industry Comp., Nov. 11, 2014. |
| Number | Date | Country | |
|---|---|---|---|
| 20190234018 A1 | Aug 2019 | US |