Method of reducing distortion in a spray formed rapid tool

Information

  • Patent Grant
  • 6179039
  • Patent Number
    6,179,039
  • Date Filed
    Thursday, March 25, 1999
    25 years ago
  • Date Issued
    Tuesday, January 30, 2001
    23 years ago
Abstract
A method of reducing distortion in a spray formed rapid tool includes the steps of making a model of a desired tool and constructing a ceramic pattern as the inverse of the model. The method also includes the steps of building a thermal model of the desired tool from a solid model of the ceramic pattern and applying thermal boundary conditions to the thermal model based on known conditions. The method also includes the steps of running the thermal model to produce a temperature distribution of the desired tool and determining any temperature deviations in the temperature distribution above a predetermined value. The method further includes thermally spraying a metal material against the ceramic pattern to form the desired tool if there are no temperature deviations in the temperature distribution above the predetermined value.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates generally to spray formed rapid tools and, more specifically, to a method of reducing distortion in a spray formed rapid tool.




2. Description of the Related Art




It is known to make a spray formed rapid tool. In spray forming, a master model of a desired tool is produced using a free form fabrication technique. This master model is then used to create a ceramic pattern, which is the reverse of the desired tool to be produced. The resulting ceramic pattern is the receptor onto which metal is sprayed to form a deposit in the shape of the desired tool. Typically, the spray forming process uses a wire-arc spraying. In wire-arc spraying, electric current is carried by two electrically conductive, consumable wires with an electric arc forming between the wire tips. A high-velocity gas jet blowing from behind the consumable wires strips away the molten metal, which continuously forms as the wires are melted by the electric arc. The high-velocity gas jet breaks up or atomizes the molten metal into finer particles in order to create a fine distribution of molten metal droplets. The atomizing gas then accelerates the droplets away from the wire tips to the ceramic pattern where the molten metal droplets impact the ceramic pattern to incrementally form a deposit in the shape of the desired tool. The completed desired tool is then mounted and used to produce parts in conventional stamping, die casting, or molding process.




During the spray forming process, the spray formed rapid tool may have a varied temperature distribution across the ceramic pattern and each layer thereof. This can result in distortion of the spray formed rapid tool as shrinkage of the sprayed metal occurs. Recently, there has been a need to create the spray formed rapid tool geometrically accurate. To accomplish this, a number of trial spray runs are conducted to determine ideal spray parameters to obtain a uniform temperature distribution.




Although the above process for making a spray formed rapid tool has worked well, it suffers from the disadvantage that trial spray runs have to be conducted to determine the spray parameters for spraying the spray formed rapid tool. Another disadvantage of the above process is that the spray parameters are achieved by trial and error. Yet another disadvantage of the above process is that to scale between different sized tools with different geometric features, estimation occurs which is undesired. Still another disadvantage of the above process is that the trial spray runs and estimation are time consuming and result in significant development costs for a spray formed rapid tool.




SUMMARY OF THE INVENTION




Accordingly, the present invention is a method of reducing distortion in a spray formed rapid tool. The method includes the steps of making a model of a desired tool, constructing a ceramic pattern as the inverse of the model, and building a thermal model of the desired tool from a solid model of the ceramic pattern. The method also includes the steps of applying thermal boundary conditions to the thermal model based on known conditions. The method also includes the steps of running the thermal model to produce a temperature distribution of the desired tool and determining any temperature deviations in the temperature distribution above a predetermined value. The method further includes the steps of thermally spraying a metal material against the ceramic pattern to form the desired tool if there are no temperature deviations in the temperature distribution above the predetermined value.




One advantage of the present invention is that a method is provided of reducing distortion in a spray formed rapid tool. Another advantage of the present invention is that the method has greater probability to create spray formed rapid tools accurately the first time. Yet another advantage of the present invention is that the method eliminates conducting trial spray runs to determine the spray parameters, resulting in a shortened product development cycle time. Still another advantage of the present invention is that the method reduces the estimation required to scale parameters between different sized tools with different geometric features. A further advantage of the present invention is that the method reduces development costs.




Other features and advantages of the present invention will be readily appreciated as the same becomes better understood after reading the subsequent description taken in conjunction with the accompanying drawings.











BRIEF DESCRIPTION OF THE DRAWINGS





FIGS. 1A

,


1


B,


1


C,


1


D and


1


E are a schematic flow diagram of a method of forming a spray formed rapid tool.





FIG. 2

is a flowchart of a method, according to the present invention, of reducing distortion in the spray formed rapid tool formed by the method of FIG.


1


.





FIG. 3

is a diagram of a spray plane for the method of FIG.


2


.





FIG. 4

is a diagram of a temperature distribution of a thermal model for the method of FIG.


2


.











DESCRIPTION OF THE PREFERRED EMBODIMENT(S)




Referring to the drawings and in particular

FIGS. 1A through 1E

, one embodiment of a method of forming a spray formed rapid tool is shown. The method begins by creating or making a master model


12


of a desired tool as illustrated in

FIGS. 1A and 1B

. Typically, the master model


12


may be produced by using a CAD/CAM design and a free-form fabrication system such as stereolithography. Such a process is disclosed in U.S. Pat. No. 5,658,506 to White et al., the disclosure of which is hereby incorporated by reference.




The method also includes the step of constructing a ceramic pattern


14


as the inverse of the master model


12


as illustrated in FIG.


1


C. To create the ceramic pattern


14


, the bottom of the master model


12


is adhered to a base plate (not shown) of an open box (not shown); the box is open at its top. A desired ceramic slurry is poured around the master model


12


to form the ceramic pattern


14


and completely covers its geometry to a thickness of greater than one (1) inch at the thinnest wall section. Entrapped air is minimized by vibrating the box and slurry contained therein on a table (not shown) , preferably in a vacuum chamber (not shown). Depending on the character of the ceramic slurry that is employed, the ceramic pattern


14


is either (i) air dried, removed and then fired to finally cure it, or (ii) the ceramic slurry is freeze cast to temperatures around −30 F. and the master model


12


removed prior to the ceramic pattern


14


thawing out, or (iii) the ceramic slurry is dried and, then the master model


12


burned out while the ceramic pattern


14


is undergoing curing. The latter is conventional investment casting and is not desirable because of the possibility of shell cracking, lower shell strength and poor geometric comparability with the spray process. Freeze casting is preferred.




The master model


12


is removed from the cured ceramic pattern


14


by installing screws (not shown) in the back of the master model


12


and pulling the master model


12


out physically. Alternatively, a stationary plate (not shown) may be used through which the extraction screws extend and the master model


12


is removed by turning the screws inward to pull against the stationary plate and also pull the master model


12


away from the ceramic pattern


14


.




The ceramic material for the ceramic pattern


14


is selected to provide a good surface finish (such as 1-4 microns), good thermal shock resistance value at temperatures of 1800≧2400 F., able to withstand up to 2400 F. temperatures, have compressive strengths of about 9,000 psi and possess a low shrinkage (less than 0.3 percent) and possess low thermal expansion (1.0-4.0 E-6/degree F.) and have no reaction to molten metal. The ceramic material is selected to be capable of withstanding a molten metal environment and have a very smooth surface with good dimensional accuracy. The ceramic materials used include aluminum oxide ceramics, dental ceramics, investment casting slurries, fused silica and freeze cast alumina.




The method includes the step of thermally spraying a metal material against the ceramic pattern


14


to form a spray formed rapid tool


16


as the desired tool. Such step is desirably carried out by the wire arc process previously described. Another method to carry out the step of thermally spraying is the osprey process wherein a semi-solid slurry of hardenable metal material is sprayed from an induction heated nozzle supply and is impelled against the ceramic pattern


14


with a high velocity due to the high pressure gases that atomize the molten fluid. Metal droplets are formed from a melt that is atomized by gas (not from wire or powder). Continuous spraying is carried out to build up a layer that exceeds at least one-quarter (¼) inch in thickness, at its thinnest section. As the spray is applied and built up, the spray formed rapid tool


16


is formed as illustrated in FIG.


1


D.




Metals usable for this purpose include metals such as zinc and high temperature high strength carbon steel. These include certain tool steels such as A2 and plain carbon steel with (0.8% carbon by weight) as well as maraging steels. Maraging steels are difficult to machine and are seldom used for tooling, but can be readily spray formed to produce a desirable microstructure.




Once the spray formed rapid tool


16


is formed, the ceramic pattern


14


is removed by chipping, grit blasting, or using a water jet to leave the completed spray formed rapid tool


16


as illustrated in FIG.


1


E. The completed spray formed rapid tool


16


may then be used in a die-set mold mounted in an injection molding machine (not shown) and used to produce molded parts. It should also be appreciated that the completed spray formed rapid tool


16


may be used for stamping, die casting, blow molding or other material forming operations.




Referring to

FIG. 2

, a method, according to the present invention, of reducing distortion in the spray formed rapid tool


16


is shown. The method begins in bubble


20


and advances to block


22


. In block


22


, the method includes the step of making the master model


12


of a desired tool as previously described. The method then advances to block


24


and includes the step of constructing the ceramic pattern


14


as previously described. The method advances to block


26


and includes the step of building a thermal model of the desired tool from a solid model of the geometry of the ceramic pattern


14


.




In block


26


, the thermal model is built as a computer program. To build the thermal model, computational fluid dynamics are used to model the heat transfer properties of the ceramic pattern


14


and thermal spray pattern. The geometry of the ceramic pattern


14


and thermal properties of the ceramic pattern


14


are inputted into the thermal model. The thermal properties of the ceramic pattern


14


and spray material such as thermal conductivity and specific heat are input into the thermal model. Measured values are used whenever possible. As illustrated in

FIG. 3

, a thermal spray pattern


28


having a generally trapezoidal shape is shown disposed over the ceramic pattern


14


mounted to an aluminum plate


30


. The thermal spray pattern


28


is also input into the thermal model as the pattern of the thermal spray gun tool.




Next, the method advances to block


32


and includes the step of applying thermal boundary conditions to the thermal model. In this step, the thermal boundary conditions include preheat of the ceramic pattern such as 200° C., cooling such as airflow in the spray booth for the thermal spray gun tool, and thermal loads such as from the thermal spray gun tool. These thermal conditions are inputted into the thermal model based on existing known conditions of thermal spray gun tool paths and thermal spray parameters. The method then advances to block


34


.




In block


34


, the method includes the step of running the thermal model to produce a uniform temperature distribution (

FIG. 4

) of the spray formed rapid tool


16


based on the proposed spray gun travel path. The computer program is executed on a conventional computer and the results of the thermal model are analyzed. The method includes determining any temperature deviations in the temperature distribution as illustrated in FIG.


4


. The determination is made by looking for large deviations in temperature profiles, for example, above a predetermined value such as twenty degrees centigrade (20° C.). Additionally, the thermal model can be run and analyzed for high thermal stress levels in the spray formed rapid tool.




After block


34


, the method advances to block


36


and includes the step of adjusting the spray parameters and the spray gun tool path to ensure uniform temperature distribution while the spray formed rapid tool


16


is being formed. For example, the power to the thermal spray gun tool can be adjusted and how close the thermal spray gun tool is to the ceramic pattern. It should be appreciated that adjusting the spray parameters and thermal spray gun tool path before spraying takes place saves time and cost.




The method advances to block


38


and includes the step of adjusting supplemental heating or cooling as required. In this step, if heating is required, a non-thermal spray torch may be used to add heat to a portion of the spray formed rapid tool


16


as it is being formed. Also, if cooling is required, a cooling sink such as a jet of air may be used to add cooling to a portion of the spray formed rapid tool


16


as it is being formed.




After block


38


, the method advances to block


40


and includes the step of thermal spraying the metal material against the ceramic pattern


14


and forming the spray formed rapid tool


16


as previously described. The method then advances to bubble


42


and ends.




Accordingly, the method reduces distortion in the spray formed rapid tool


16


by maintaining a uniform temperature distribution across the ceramic pattern


14


and thermal spray layer during spraying and the shrinkage will be uniform regardless of phase transformation. The spray formed rapid tool


16


may be stress uniform, i.e. have residual stresses distributed relatively equally, but will accurately match the ceramic pattern


14


with less distortion. By adjusting the spray parameters and the thermal spray gun tool paths, the method produces a uniform temperature distribution while spraying on low melt alloys used as a pattern or as wall stock. The method also allows spraying other materials, which do or do not undergo martensite phase transformations. The method controls the shrinkage of the spray formed rapid tool


16


one layer at a time as the spray formed rapid tool


16


is built up. Regardless of the spray materials used, the spray formed rapid tool


16


will shrink uniformly as it cools to room temperature because each thermal spray layer deposited on a previous layer had a uniform temperature distribution.




The present invention has been described in an illustrative manner. It is to be understood that the terminology, which has been used, is intended to be in the nature of words of description rather than of limitation.




Many modifications and variations of the present invention are possible in light of the above teachings. Therefore, within the scope of the appended claims, the present invention may be practiced other than as specifically described.



Claims
  • 1. A method of reducing distortion in a spray formed rapid tool comprising the steps of:making a model of a desired tool; constructing a ceramic pattern as the inverse of the model; building a thermal model of the desired tool from a solid model of the ceramic pattern; applying thermal boundary conditions to the thermal model based on known conditions; running the thermal model to produce a temperature distribution of the desired tool and determining any temperature deviations in the temperature distribution above a predetermined value; and thermally spraying a metal material against the ceramic pattern to form the desired tool if there are no temperature deviations in the temperature distribution above the predetermined value.
  • 2. A method as set forth in claim 1 including the step of separating the ceramic pattern from the model.
  • 3. A method as set forth in claim 1 including the step of separating the ceramic pattern from the desired tool.
  • 4. A method as set forth in claim 1 including the step of adjusting spray parameters to ensure uniform temperature distribution before said step of thermally spraying.
  • 5. A method as set forth in claim 1 including the step of adjusting either supplemental heating or cooling to eliminate any deviations before said step of thermally spraying.
  • 6. A method as set forth in claim 1 wherein the predetermined value is less than 20° C.
  • 7. A method as set forth in claim 1 wherein the thermal boundary conditions comprise preheat of the ceramic pattern.
  • 8. A method as set forth in claim 1 wherein the thermal boundary conditions comprise cooling during said step of thermally spraying.
  • 9. A method as set forth in claim 1 wherein the thermal boundary conditions comprise thermal loads.
  • 10. A method of reducing distortion in a spray formed rapid tool comprising the steps of:making a model of a desired tool; constructing a ceramic pattern as the inverse of the model; separating the ceramic pattern from the mold; building a thermal model of the desired tool from a solid model of the ceramic pattern; applying thermal boundary conditions to the thermal model based on known conditions; running the thermal model to produce a temperature distribution of the desired tool and determining any temperature deviations in the temperature distribution above a predetermined value; thermally spraying a metal material against the ceramic pattern to form the desired tool if there are no temperature deviations in the temperature distribution above the predetermined value; and separating the ceramic pattern from the desired tool.
  • 11. A method as set forth in claim 10 including the step of adjusting spray parameters to ensure uniform temperature distribution before said step of thermally spraying.
  • 12. A method as set forth in claim 10 including the step of adjusting either supplemental heating or cooling to eliminate any deviations before said step of thermally spraying.
  • 13. A method as set forth in claim 10 wherein the predetermined value is less than 20° C.
  • 14. A method as set forth in claim 10 wherein the thermal boundary conditions comprise preheat of the ceramic pattern.
  • 15. A method as set forth in claim 10 wherein the thermal boundary conditions comprise cooling during said step of spraying.
  • 16. A method as set forth in claim 10 wherein the thermal boundary conditions comprise thermal loads.
  • 17. A method of reducing distortion in a spray formed rapid tool comprising the steps of:making a model of a desired tool; constructing a ceramic pattern as the inverse of the model; building a thermal model of the desired tool from a solid model of the ceramic pattern; applying thermal boundary conditions to the thermal model based on known conditions; running the thermal model to produce a temperature distribution of the desired tool and determining any temperature deviations in the temperature distribution above a predetermined value; adjusting either supplemental heating or cooling to eliminate any deviations if there are any temperature deviations in the temperature distribution above the predetermined value; and thermally spraying a metal material against the ceramic pattern to form the desired tool.
  • 18. A method as set forth in claim 17 including the step of separating the ceramic pattern from the model.
  • 19. A method as set forth in claim 17 including the step of separating the ceramic pattern from the desired tool.
  • 20. A method as set forth in claim 17 wherein the predetermined value is less than 20 C.
US Referenced Citations (18)
Number Name Date Kind
4087568 Fay et al. May 1978
4172020 Tisone et al. Oct 1979
4593360 Cocks Jun 1986
4736304 Doehler Apr 1988
4843576 Smith et al. Jun 1989
4902398 Homstad Feb 1990
5009367 Nielsen Apr 1991
5009485 Hall Apr 1991
5047612 Savkar et al. Sep 1991
5189781 Weiss et al. Mar 1993
5319568 Bezaire Jun 1994
5370902 Vigneron et al. Dec 1994
5529809 Glovan et al. Jun 1996
5612887 Laube et al. Mar 1997
5689415 Calotychos et al. Nov 1997
5751607 Ohta May 1998
5770273 Offer et al. Jun 1998
5967218 Pergande et al. Oct 1999
Foreign Referenced Citations (4)
Number Date Country
195 45 005 A1 Jun 1997 DE
198 37 400 C1 Nov 1999 DE
0 781 625 A1 Jul 1997 EP
8089859 Apr 1996 JP