Claims
- 1. An improved process for removing low molecular weight organosilicon volatiles in the mixing of an uncured heat vulcanizable silicone rubber composition consisting essentially of:
- (A) mixing:
- (a) a diorganopolysiloxane polymer having a viscosity varying from 1,000,000 to 300,000,000 centipoise at 25.degree. C. where the organo groups are monovalent hydrocarbon radicals;
- (b) a filler selected from the class consisting of fumed silica and precipitated silica and
- (c) a process aid in a Banbury-type mixing vessel which encloses the mixture; said Banbury-type mixing vessel having an external heating jacket, means for adding additional ingredients and means for removing volatile ingredients; and
- (B) heating and continually mixing the mixture at 140.degree. to 170.degree. C. for 5 minutes to 30 minutes, the improvement consisting essentially of the additional steps of:
- (C) continuously removing the low molecular weight organosilicon volatiles from said mixture by the utilization of aspirator means, said aspirator means being operated by passing effluent through an eductor wherein the suction end of said eductor is connected to the area of said Banbury-type mixing vessel above said mixture;
- (D) condensing volatiles entrained in said effluent by cooling said effluent to about room temperature in a condenser means;
- (E) separating the condensed volatiles from said effluent by collecting the volatiles in a decantor vessel wherein the condensed volatiles are collected by means of a weir arrangement in the decantor vessel and wherein effluent is recycled to said eductor and new effluent being passed to the decantor vessel as needed; and
- (F) removing said condensed volatiles from said decantor vessel for disposal or reuse.
- 2. The process of claim 1 wherein there is added liquid CO.sub.2 to said devolatilized mixture after the heating step is terminated so as to rapidly cool the mixer.
- 3. The process of claim 1 wherein a nitrogen atmosphere is maintained in the overhead area of said enclosed mixing vessel.
- 4. The process of claim 1 wherein the decantor vessel is vented to remove uncondensed volatiles.
- 5. The process of claim 1 wherein there is present in said mixing vessel a dust collector for removing filler particles from the atmosphere above the mixing vessel when said filler is mixed into said diorganopolysiloxane polymer.
- 6. The process of claim 1 wherein after said heating steps further comprising extruding the devolatilized mixture and passing said mixture through a screen to remove impurities thereby providing a purified devolatilized mixture and thereafter packaging said cured devolatilized mixture.
Parent Case Info
This application is a continuation of application Ser. No. 155,690, filed June 6, 1980 and now abandoned.