Patent Grant
11712858
The present application claims priority from Japanese Patent Application No. 2018-040258 filed on Mar. 6, 2018, the entire contents of which are hereby incorporated by reference.
Examples of the present invention relate to a method of shaping a preform and a method of molding a composite material.
Resin transfer molding (RTM) methods have been known as a method of molding a composite material of resin reinforced with fiber, such as glass fiber reinforced plastics (GFRP) and carbon fiber reinforced plastics (CFRP).
The RTM methods are methods of molding a composite material that include laminating fiber sheets, impregnating the fiber sheets with a thermosetting resin, and thermally curing the fiber sheets. Among the RTM methods, a method including evacuation to impregnate fiber with a resin is called vacuum assisted resin transfer molding (VaRTM), and a method including resin impregnation using dies is called matched-die RTM.
In the case of molding a composite material by an RTM method, a dry preform is manufactured prior to resin impregnation. The dry preform is a laminate of fiber sheets that is shaped in accordance with a shape of the composite material after molding. The dry preform is manufactured by laminating fiber sheets. However, in many cases, a thermoplastic binder is interposed between the fiber sheets so that the fiber sheets are provisionally fastened not to slide from one another (see, for instance, Japanese Unexamined Patent Application Publication (JP-A) No. 2010-253873 and JP-A No. 2009-214371).
A tape-shaped fibrous base material is called a dry tape member. A dry tape member on which a thermoplastic nonwoven cloth is superposed and a dry tape member to which thermoplastic fine particles are adhered are available on the market. In laminating dry tape members including a thermoplastic binder, the dry tape members are heat-sealed with the binder in a spotted manner at regular intervals using an exclusive-use heater so as to provisionally fasten each of the dry tape members to an adjacent dry tape member. This makes it possible to prevent the laminated dry tape members from being displaced from one another or coming off.
An aspect of the present invention provides a method of shaping a preform including: laminating a plurality of dry tape members each including a binder and fiber while partly heat-sealing the plurality of dry tape members with the binder to provisionally fasten each of the plurality of dry tape members to an adjacent dry tape member; bending the plurality of dry tape members, which have been provisionally fastened, along a bending line; and heat-sealing the plurality of dry tape members, which have been bent, with the binder to manufacture a shaped dry preform, in which at the laminating, at least one of the followings is satisfied:
(i) an amount of heat-sealing with the binder is changed in an area along the bending line,
(ii) an amount of heat-sealing with the binder is different between portions adjacent to and on opposite sides of the area along the bending line, or
(iii) an amount of heat-sealing with the binder is different between portions adjacent to each other at the bending line as a border.
An aspect of the present invention provides a method of molding a composite material including impregnating the dry preform, which has been manufactured by the above-described method of shaping the preform, with a thermosetting resin, and thermally curing the preform to manufacture the composite material.
In the following, some preferred examples of the present invention are described in detail with reference to the accompanying drawings. Note that the following description is directed to illustrative instances of the disclosure and not to be construed as limiting to the present invention. Factors including, without limitation, numerical values, dimensions, shapes, materials, components, positions of the components, and how the components are coupled to each other are for purposes of illustration to give an easier understanding of the present invention, and are not to be construed as limiting to the present invention, unless otherwise specified. Further, elements in the following instances which are not recited in a most-generic independent claim of the disclosure are optional and may be provided on an as-needed basis. The drawings are schematic and are not intended to be drawn to scale. Throughout the specification and the drawings, elements having substantially the same function and configuration are denoted with the same minerals to avoid redundant description. Illustration of elements that are not directly related to the present invention is omitted.
In the case of manufacturing a dry preform of a complicated shape by drape forming in which a laminate of dry tape members is pressed on a male die, it is necessary to make the dry tape members slide from one another and be deformed after laminating the dry tape members. Consequently, in the case of provisionally fastening the dry tape members by heat-sealing with a thermoplastic binder, the dry tape members may wrinkle or be ripped, thus degrading a shaping quality of the dry preform.
It is therefore desirable to ensure shaping a dry preform of an improved quality even if the dry preform has a complicated shape.
Steps of an RTM method illustrated in
In the case of molding a composite material by the RTM method that includes laminating fiber sheets, impregnating the fiber sheets with a thermosetting resin, and thermally curing the fiber sheets, it is necessary to shape a dry preform having a shape in accordance with a shape of the composite material. Because the dry preform has substantially the same shape as the composite material 1, the common die 4 may be used to shape the dry preform. However, other than the die 4 to thermally cure the composite material 1, a die to shape the dry preform may be used.
The dry preform may be manufactured as a laminate of a plurality of fiber sheets. However, mere lamination of fiber sheets may unfortunately cause displacement of the fiber sheets from one another. In view of this, dry tape members including a thermoplastic binder and fiber in the form of tapes have been developed into products. Use of dry tape members as a material of the dry preform makes it possible to laminate the dry tape members while partly heat-sealing the dry tape members with the binder to provisionally fasten the dry tape members not to slide.
As illustrated in
As illustrated in
As illustrated in
The dry preform is manufactured as a laminate of a plurality of dry tape members. Consequently, a dry tape member is cut into a shape of each fiber layer of the dry preform in a developed state.
The dry preform may be manufactured as a bent laminate of dry tape members 22 each having a web surface 20 to form the web 2 of the composite material 1 and flange surfaces 21 to respectively form the two flanges 3, as illustrated in
As a matter of course, in the case of molding a composite material having a curved web and a composite material having flat flanges, a dry preform may be manufactured as a laminate of the dry tape members 22 having curved web surfaces and as a laminate of the dry tape members 22 having flat flange surfaces. That is, a dry preform may be manufactured as a laminate of the dry tape members 22 having a shape in which a curved surface and a flat surface are coupled or a curved surface and a curved surface are coupled at a bending line 23.
In order to manufacture the laminate of the dry tape members 22 having the shape illustrated in
Then, the flat dry tape members 22 are laminated on a desired die. Although the flat dry tape members 22 may be laminated on the die 4 illustrated in
In laminating the dry tape members 22, the dry tape members 22 are partly heat-sealed with the thermoplastic binder by a heater to prevent the laminated dry tape members 22 from sliding and being displaced from one another. That is, adjacent dry tape members 22 in a thickness direction and a lamination direction are partly adhered to one another by heat-sealing with the thermoplastic binder. This prevents the laminated dry tape members 22 from being displaced from one another.
The binder may be heated by an automatic heater or manually heated by an operator using a portable heater. As a heater to weld the binder on the fiber, an ultrasonic welder and a laser welder have been known. Alternatively, an automatic laminator to laminate the dry tape members 22 and weld the binder automatically has been developed into a product.
Use of a heater makes it possible to perform spot welding of the binder. Consequently, adjacent dry tape members 22 may be adhered to one another at a large number of points to provisionally fasten the dry tape members 22 while laminating the dry tape members 22.
As described above, at step S1, which is a step of laminating the fiber sheets in the flowchart of
It should be noted that the laminated flat dry tape members 22 are each to be bent into the shape having the web surface 20 and the flange surfaces 21, as illustrated in
In view of this, an amount of heat-sealing with the thermoplastic binder is changeable in accordance with a shape of the dry preform and each of the dry tape members 22 after shaping. As illustrated in
In view of this, it is appropriate to determine the amount of heat-sealing at such a value that the portions 22A to be bent along the bending lines 23 are made to slide to some extent. For this purpose, the amount of heat-sealing with the thermoplastic binder may be different between the portions 22A and a portion 22B of the dry tape member 22 that are adjacent to each other at the bending line 23 as a border. Specifically, an amount of heat-sealing with the thermoplastic binder in the portions 22A to be bent along the bending lines 23 in a plurality of dry tape members 22 may be made less than an amount of heat-sealing with the thermoplastic binder in the portions 22B adjacent to the portions 22A to be bent.
This makes it possible to limit a range where the portions 22A to be bent along the bending lines 23 are slidable. That is, the portions 22A to be bent along the bending lines 23 may be made to slide in a range required for bending while provisionally fastening the portions 22A to adjacent dry tape members 22.
As illustrated in
In a more specific instance, while the intervals between heat-sealing points to be locally heated may be made as narrow as approximately 3 inches in the portions 22B to be the web 2 shaped as a flat surface, the intervals between heat-sealing points to be locally heated may be made as wide as approximately 5 inches to 10 inches in the portions 22A to be the flanges 3 shaped as curved surfaces of a large curvature.
This makes it possible to make the amount of heat-sealing with the thermoplastic binder in the portions 22A to be each of the flanges 3 less than the amount of heat-sealing with the thermoplastic binder in the portions 22B to be the web 2. It becomes also possible to provisionally fasten the portions 22B to be the web 2 to sufficiently decrease a sliding amount. Meanwhile, it becomes possible to provisionally fasten the portions 22A to be the flanges 3 to prevent the portions 22A from being largely detached while making the portions 22A slide to some extent to avoid wrinkling and being ripped when bent. As a matter of course, the same applies to the portions 22B to be the web 2 that are not flat surfaces but curved surfaces of a small curvature.
Local heating at irregular intervals between heat-sealing points may be manually performed by an operator using a portable heater. Alternatively, local heating may be automatically performed using an automatic heater with a three-axis movement mechanism and a robot arm. In the case of automatically performing local heating at irregular intervals between heat-sealing points using an automatic heater, positioning of the heat-sealing points may be determined by numerical control (NC) using NC programs.
As illustrated in
When lamination including provisional fastening of the developed dry tape members 22 is completed, the plurality of dry tape members 22 provisionally fastened to each other are bent along the bending lines 23 at step S2. For this purpose, in the case where the plurality of dry tape members 22 provisionally fastened are laminated on a lamination die of a flat plate shape, the laminate of the dry tape members 22 provisionally fastened is placed on the die 4 for molding the composite material 1 as illustrated in
This makes it possible to form a laminate of the dry tape members 22 that has a shape having (i) a curved surface and a flat surface that are coupled at each of the bending lines 23 or (ii) a curved surface and a curved surface that are coupled at each of the bending lines 23, which shape is similar to the shape of the laminate of the dry tape members 22 including the web surface 20 and the flange surfaces 21 as illustrated in
Next, at step S3, the bent laminate of the dry tape members 22 is wholly heated by a heater. Practically, as described later, the die 4 for molding the composite material 1 or the die for shaping the dry preform is heated by the heater. Thus, the fiber sheets in the plurality of dry tape members 22 after bending may be heat-sealed with the thermoplastic binder therein to manufacture the shaped dry preform. That is, it becomes possible to manufacture, as the dry preform, the laminate of the dry tape members 22 that has a shape in which a curved surface and a flat surface are coupled or a curved surface and a curved surface are coupled at each of the bending lines 23, which shape is similar to the shape of the laminate of the dry tape members 22 including the web 2 and the flanges 3.
Next, at step S4, the fiber that constitutes the dry preform is impregnated with a thermosetting resin. For this purpose, a space where the dry preform is placed is hermetically sealed and evacuated.
In the case of manufacturing the composite material 1 by the VaRTM method, the dry preform 30 placed on the die 4 for molding the composite material 1 or the dry preform 30 transferred from the shaping die to the die 4 for molding the composite material 1 is covered with a bagging film 31, and edges of the bagging film 31 are adhered to the die 4 with a sealant 32. Then, a region hermetically sealed by the bagging film 31 is decreased in pressure by a vacuum device 33. That is, the dry preform 30 is bagged by evacuation by the vacuum device 33.
In the case of manufacturing the composite material 1 by the RTM method using the upper die 40 of a rigid body, the dry preform 30 is disposed in a space defined between the die 4 for molding the composite material 1, which serves as a lower die, and the upper die 40. Then, the space defined between the die 4 and the upper die 40 is evacuated by the vacuum device 33.
After completing evacuation, both in the case of bagging with the bagging film 31 as illustrated in
It should be noted that to make the resin fluid as necessary, the resin is heated to approximately 100° C. in the resin injector 50. In the case of injecting the resin in a heated state, the die 4 may incorporate a heater to heat the resin not to decrease a temperature of the resin. In the case of incorporating the heater in the die 4, for instance, the die 4 may incorporate a pipe in which a heated fluid such as heated steam, heated air, and heated water flows. Alternatively, an electric heater may be incorporated in the die 4. In the case of using the upper die 40 as illustrated in
Next, at step S5, the resin impregnated in the dry preform 30 is thermally cured. Specifically, as illustrated in FIG. 9 or
It should be noted that the composite material 1 is not limited to the shape illustrated in
As illustrated in
As illustrated in
The above-described method is likewise applicable to manufacturing not only the dry preform and the composite material 1 including the web 2 and the flanges 3 but also a dry preform and a composite material having a shape of two plate-shaped portions coupled at a bending line, and a dry preform and a composite material having a shape of a plate-shaped portion bent a plurality of times at a plurality of bending lines in an identical direction. In the case of bending the dry tape members 22 at a plurality of bending lines, heat-sealing may be performed at intervals of three or more different distances.
A laminate of the dry tape members 22 may be bent along a bending line to make the laminate of the dry tape members 22 have a surface with a sharp edge or a curved surface such as a round-chamfered surface. In the case of forming a curved surface such as a round-chamfered surface along a bending line, at the time of provisional fastening of the dry tape members 22, the amount of heat-sealing with the binder may be different between portions adjacent to and on opposite sides of an area chamfered along the bending line, instead of the amount of heat-sealing with the binder being different between each portion 22A and the portion 22B which are adjacent to each other at the corresponding bending lines 23 as the border, as illustrated in
Depending on a shape of the dry preform and the composite material 1, the amount of heat-sealing with the binder may be different between a plurality of dry tape members 22 to be laminated, that is, the amount of heat-sealing with the binder may be changed in a direction of lamination of the dry tape members 22. In a specific instance, in the case where the dry preform and the composite material 1 are so thick that a difference between a radius of chamfering on the inside and a radius of chamfering on the outside that is formed by bending at the bending line is large, a difference between a sliding amount of the dry tape member 22 on the inside and a sliding amount of the dry tape member 22 on the outside is also large. In view of this, amounts of heat-sealing with the binder may be adjusted in accordance with sliding amounts of the respective dry tape members 22 for bending the laminate of the dry tape members 22.
In the method of shaping the preform and the method of molding the composite material described above, in the case of manufacturing the dry preform and the composite material 1 by taking steps including a step of bending the laminate of the dry tape members 22, an amount of heat-sealing with the binder in the portions 22A to be bent of the dry tape members 22 is made small to facilitate bending of the dry tape members 22.
Consequently, the method of shaping the preform and the method of molding the composite material make it possible to easily deform the dry tape members 22 in shaping the dry tape members 22 while provisionally fastening the dry tape members 22 at the time of laminating the dry tape members 22. As a result, circumstances of the dry tape members 22 wrinkling or being ripped may be avoided to manufacture the dry preform of an improved quality. Particularly, optimizing the intervals between heat-sealing points in accordance with the shape of the dry preform and the composite material 1 makes it possible to manufacture the dry preform and the composite material 1 of an improved quality even if the dry preform and the composite material 1 have a complicated shape.
The method of shaping a preform and the method of molding a composite material according to the second example illustrated in
As illustrated in
Then, partial heat-sealing may be performed with the thermoplastic binders for provisionally fastening the dry tape members 22 at a temperature T (T2<T<T1) lower than the first melting point representative value T1 and higher than the second melting point representative value T2.
Consequently, even if intervals between heat-sealing points for provisional fastening are constant in the portions 22A and 22B that are adjacent to each other at the bending lines 23 as borders in the dry tape members 22, an amount of heat-sealing with the binders may be different between the portions 22A and 22B adjacent to each other at the bending lines 23 as the borders. That is, an amount of heat-sealing with the binder in the portions 22A to be bent along each of the bending lines 23 in the dry tape members 22 may be made smaller than an amount of heat-sealing with the binder in the portions 22B adjacent to the portions 22A to be bent.
As a matter of course, in the case where a chamfering area is wide, a melting point representative value of the thermoplastic binder is different between portions adjacent to and on opposite sides of an area along each of the bending lines 23. In this case, the amount of heat-sealing with the binder may be different between the portions adjacent to and on opposite sides of an area along the bending line 23.
The dry tape members 22 may include two kinds of binders having different melting points or may include three or more kinds of binders having different melting points. While the thermoplastic binder in the portions 22A to be bent along the bending lines 23 in the dry tape members 22 may be made of one kind of material having a relatively high melting point, the thermoplastic binder in the portions 22B adjacent to the portions 22A to be bent may be made of one kind of material having a relatively low melting point. A plurality of kinds of materials having different melting points may be blended at different ratios to make two kinds of thermoplastic binders having different representative values, such as average values, intermediate values, minimum values, and maximum values, of melting points.
Therefore, in the case where two kinds of binders having different representative values of melting points are each made of one kind of material, the first melting point representative value T1 is a melting point of a first material, and the second melting point representative value T2 is a melting point of a second material when a deviation of melting point of an identical material is ignored. In a specific instance, nylon 12 (abbreviated as PA12), which is a polyamide including the aliphatic skeleton, may be used as a material of the binder, and has a melting point of 176° C. Meanwhile, nylon 1010 (abbreviated as PA1010) may be also used as a material of the binder, and has a melting point of 202° C., which is higher than the melting point of nylon 12.
In view of this, while the thermoplastic binder in the portions 22B that are adjacent to the portions 22A to be bent along the bending lines 23 in the dry tape members 22, such as the portions to form the web surface 20, may be made of nylon 12 having a relatively low melting point, the thermoplastic binder in the portions 22A to be bent along the bending lines 23 in the dry tape members 22, such as the portions to form the flange surfaces 21, may be made of nylon 1010 having a relatively high melting point. Then, spot heating may be performed at constant intervals at a temperature higher than 176° C., which is the melting point of nylon 12, and lower than 202° C., which is the melting point of nylon 1010.
As a result, although the portions 22B, such as the web surface 20, that are not to be bent along the bending lines 23 in the dry tape members 22 and that include the binder made of nylon 12 are heat-sealed at constant intervals, the portions 22A, such as the flange surfaces 21, that are to be bent along the bending lines 23 in the dry tape members 22 and that include the binder made of nylon 1010 are not heat-sealed even if a heating terminal of a heater is pressed on the portions 22A.
That is, the dry tape members 22 are laminated while the dry tape members 22 are heat-sealed at constant intervals at a temperature at which only the thermoplastic binder having a lower melting point melts. As a result, while only the portions 22B that are not to be bent along the bending lines 23 in the dry tape members 22 may be heat-sealed in a spotted manner and provisionally fastened, the portions 22A that are to be bent along the bending lines 23 in the dry tape members 22 may not be provisionally fastened but be made freely slidable. That is, amounts of heat-sealing the dry tape members 22 may be changed at the bending lines 23 as borders.
It should be noted that dependent on the shape of the dry preform and the composite material 1, it is desirable in many cases to provisionally fasten the portions 22A to be bent along the bending lines 23 in the dry tape members 22 to some degree. In view of this, a plurality of kinds of thermoplastic binders having different melting points may be blended to thereby heat-seal the portions 22A to be bent along each of the bending lines 23 with a smaller amount of heat-sealing than an amount of heat-sealing with which the portions 22B adjacent to the portions 22A to be bent is heat-sealed.
In other words, representative values, such as average values, of melting points of the binders may be adjusted to control secureness of heat-sealing. In a specific instance, blending ratios of nylon 12 and nylon 1010 may be changed to prepare two kinds of binders with which heat-sealing amounts are different when the two binders are heated at a predetermined temperature.
In the above-described second example, the melting points of the thermoplastic binders are optimized so that the amount of heat-sealing with the binder in the portions 22A to be bent in the dry tape members 22 is made small. According to the second example, therefore, bending of the dry tape members 22 is facilitated in a similar manner to the first example so as to prevent the dry tape members 22 from wrinkling and being ripped, thereby manufacturing the dry preform of an improved quality.
Moreover, in the second example, even if the pressure terminal of the heater is pressed on and heats the dry tape members 22, the amounts of heat-sealing are adjustable. Consequently, even in the case of automatically fastening the dry tape members 22 provisionally by spot welding at a plurality of positions simultaneously using an automatic heater, such as an automatic heating robot, including a plurality of pressure terminals, secureness of provisional fastening of the dry tape members 22 is changeable at different positions.
As a matter of course, provisional fastening of the dry tape members 22 may be performed using an automatic heater with a single pressure terminal or using a portable heater. In this case, the first example may be combined with the second example. That is, both of the intervals between the heat-sealing points and the melting points of the binders may be adjusted to optimize the amounts of heat-sealing the dry tape members 22.
The method of shaping a preform and the method of molding a composite material according to the third example illustrated in
As typically observed in the case of bending the dry tape members 22 along the bending lines 23 to form the web surface 20 and the flange surfaces 21, in the case of bending the dry tape members 22 at the bending lines 23 to form a plurality of surfaces, chamfered portions 22C, such as round-chamfered portions, are often formed in portions that couple the surfaces. The chamfered portions 22C are apt to wrinkle because the dry tape members 22 are bent in a curved state.
In view of this, an area of the chamfered portions 22C along the bending lines 23 may be continuously heat-sealed. Specifically, an amount of heat-sealing with the thermoplastic binder in the chamfered portions 22C formed in a plurality of dry tape members 22 when bent along the bending lines 23 may be made larger than an amount of heat-sealing with the thermoplastic binder in the portions adjacent to the chamfered portions 22C. For instance, in the case of shaping each of the dry tape members 22 in such a manner that the web surface 20 and the flange surfaces 21 are coupled with the chamfered portions 22C, an amount of heat-sealing with the binder in an area from a border between the web surface 20 and the chamfered portion 22C to a border between the flange surface 21 and the chamfered portion 22C may be made large. This makes it possible to prevent the chamfered portions 22C from wrinkling.
As illustrated in
Moreover, the chamfered portions 22C of each of the dry tape members 22 are heat-sealed at constant intervals so that heat-sealing with the binder does not hinder permeation of a thermosetting resin when the fiber is impregnated with the thermosetting resin. This makes it possible to prevent defective permeation of the resin from generating voids, for instance. As a result, the quality of the composite material 1 may be improved.
In either one of cases of heat-sealing the dry tape members 22 along the bending lines 23 continuously or intermittently, the dry tape members 22 may be heat-sealed manually by an operator using a heater or by automatic control (such as NC control) using an automatic heater such as a robot. In the case where heat-sealing is performed continuously along the bending lines 23 as illustrated in
In the above-described third example, in provisional fastening of the dry tape members 22, heat-sealing is performed along the bending lines 23 continuously or intermittently. According to the third example, therefore, bending of the dry tape members 22 is facilitated in a similar manner to the first example and the second example so as to prevent the dry tape members 22 from wrinkling and being ripped, thereby manufacturing the dry preform of an improved quality.
As a matter of course, at least one of the first example or the second example may be combined with the third example. That is, an amount of heat-sealing with the binder in the area along each of the bending lines 23 may be made large, and at the same time, the amount of heat-sealing with the binder may be different between the portions adjacent to and on opposite sides of the area along the bending line 23. In this case, it is appropriate that an amount of heat-sealing with the binder in the portion that is adjacent to the area along the bending line 23 and that is to be bent is made small, and that an amount of heat-sealing with the binder in the portion that is adjacent to the area along the bending line 23 and that is not to be bent is made large.
The method of shaping a preform and the method of molding a composite material according to the fourth example illustrated in
As illustrated in
With this configuration, the portions 22A, such as the flange surfaces 21, to be bent along the bending lines 23 in the plurality of dry tape members 22 may be kept not heat-sealed with the thermoplastic binder, and the portions 22B, such as the web surface 20, adjacent to the portions 22A to be bent may be heat-sealed with the thermoplastic binder. That is, the sheets 60 to prevent heat-sealing with the binder are interposed between the portions 22A to be bent along the bending line 23 in the dry tape members 22 so that adjacent dry tape members 22 in the lamination direction may not be adhered to each other even if the heating terminal of the heater is pressed on the portions 22A.
The sheets 60 are drawn out of the laminate of the dry tape members 22 after provisional fastening of the dry tape members 22. For this purpose, end portions of the sheets 60 are made to protrude from the laminate of the dry tape members 22 to facilitate drawing out the sheets 60. The sheets 60 may be placed and removed every time the dry tape members 22 are laminated and provisionally fastened.
More specifically, on a dry tape member 22 on which the sheet 60 is placed, another dry tape member 22 is placed and provisionally fastened by partial heat-sealing with the binder. Then, the sheet 60 is drawn out, and the sheet 60 is placed again on the uppermost dry tape member 22 provisionally fastened. Similarly, the following steps are repeated: lamination of a dry tape member 22; provisional fastening by partial heat-sealing; and drawing out the sheet 60. This makes it possible to manufacture the laminate of the dry tape members 22 with only the portions 22B, such as the web surface 20, adjacent to the portions 22A to be bent along the bending lines 23 being provisionally fastened.
Alternatively, a plurality of dry tape members 22 and a plurality of sheets 60 may be alternately superposed on one another and laminated while provisionally fastened, and after provisional fastening of all of the dry tape members 22 is completed, each of the sheets 60 may be drawn out.
In the laminate of the dry tape members 22 provisionally fastened and laminated in this manner, the portions 22A, such as the flange surfaces 21, to be bent along the bending lines 23 in the plurality of dry tape members 22 are not fastened provisionally, and the portions 22B, such as the web surface 20, adjacent to the portions 22A to be bent are partly heat-sealed with the binder and provisionally fastened. This facilitates bending of the laminate of the dry tape members 22.
In the above-described fourth example, instead of making irregular the intervals between the heat-sealing points and the melting points of the binders in provisionally fastening the dry tape members 22, the sheets 60 to prevent heat-sealing with the binder and provisional fastening are interposed between each adjacent pair of the portions 22A, such as the flange surfaces 21, to be bent along the bending lines 23 in the plurality of dry tape members 22. According to the fourth example, therefore, bending of the dry tape members 22 is facilitated in a similar manner to the first example and the second example so as to prevent the dry tape members 22 from wrinkling and being ripped, thereby manufacturing the dry preform of an improved quality.
Particularly, even in the case of using one kind of binder, amounts of heat-sealing with the binder are adjustable. Moreover, even in the case where heat-sealing intervals are constant, amounts of heat-sealing with the binder are adjustable. This makes it possible to form portions not to be easily heat-sealed even in the case of automatic heat-sealing with the binder using a heater such as a robot including a plurality of heating terminals.
Furthermore, the fourth example may be combined with the third example. That is, an amount of heat-sealing with the binder in the area along each of the bending lines 23 in the dry tape members 22 may be made large, and at the same time, the sheets 60 to prevent heat-sealing with the binder and provisional fastening may be interposed between each adjacent pair of the portions that are adjacent to the area along the bending lines 23 and that are to be bent.
Although particular examples have been described above, the described examples are only instances and do not restrict the scope of claims. The novel methods and devices described here may be practiced in various other forms. In addition, in the forms of the methods and devices described here, various omissions, replacements, and changes may be made without departing from the spirit of the present invention. The appended claims and the equivalents thereof include such various forms and modified examples, which are included in the scope and the spirit of the present invention.
For instance, as described above, part or all of each of the examples may be combined. That is, at least one of the followings is satisfied. That is, (i) an amount of heat-sealing with the thermoplastic binder is changed in an area along each of the bending lines 23 in the dry tape members 22, (ii) an amount of heat-sealing with the thermoplastic binder is different between portions adjacent to and on opposite sides of the area along each bending line 23, or (iii) an amount of heat-sealing with the thermoplastic binder is different between the portions 22A and 22B adjacent to each other at each of the bending lines 23 as a border.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-040258 | Mar 2018 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5418035 | Iguchi | May 1995 | A |
| 20140349167 | Wakai | Nov 2014 | A1 |
| 20180229452 | Ogale | Aug 2018 | A1 |
| 20190084214 | Drexler | Mar 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 2009-214371 | Sep 2009 | JP |
| 2010-253873 | Nov 2010 | JP |
| Entry |
|---|
| Bhatt, Sanjiv, “Influence of molecular weight on the properties of poly(ether ether ketone)”, 2010, Society of Plastics Engineers (Year: 2010). |
| Number | Date | Country | |
|---|---|---|---|
| 20190275749 A1 | Sep 2019 | US |