Patent Application
20160318252
1. Field of the Invention
The invention relates to methods for producing metallic articles by three-dimensional printing.
2. Background of the Invention
Three dimensional printing was developed in the 1990's at the Massachusetts Institute of Technology and is described in several United States patents, including the following U.S. Pat. No. 5,490,882 to Sachs et al., U.S. Pat. No. 5,490,962 to Cima et al., U.S. Pat. No. 5,518,680 to Cima et al., U.S. Pat. No. 5,660,621 to Bredt et al., U.S. Pat. No. 5,775,402 to Sachs et al., U.S. Pat. No. 5,807,437 to Sachs et al., U.S. Pat. No. 5,814,161 to Sachs et al., U.S. Pat. No. 5,851,465 to Bredt, U.S. Pat. No. 5,869,170 to Cima et al., U.S. Pat. No. 5,940,674 to Sachs et al., U.S. Pat. No. 6,036,777 to Sachs et al., U.S. Pat. No. 6,070,973 to Sachs et al., U.S. Pat. No. 6,109,332 to Sachs et al., U.S. Pat. No. 6,112,804 to Sachs et al., U.S. Pat. No. 6,139,574 to Vacanti et al., U.S. Pat. No. 6,146,567 to Sachs et al., U.S. Pat. No. 6,176,874 to Vacanti et al., U.S. Pat. No. 6,197,575 to Griffith et al., U.S. Pat. No. 6,280,771 to Monkhouse et al., U.S. Pat. No. 6,354,361 to Sachs et al., U.S. Pat. No. 6,397,722 to Sachs et al., U.S. Pat. No. 6,454,811 to Sherwood et al., U.S. Pat. No. 6,471,992 to Yoo et al., U.S. Pat. No. 6,508,980 to Sachs et al., U.S. Pat. No. 6,514,518 to Monkhouse et al., U.S. Pat. No. 6,530,958 to Cima et al., U.S. Pat. No. 6,596,224 to Sachs et al., U.S. Pat. No. 6,629,559 to Sachs et al., U.S. Pat. No. 6,945,638 to Teung et al., U.S. Pat. No. 7,077,334 to Sachs et al., U.S. Pat. No. 7,250,134 to Sachs et al., U.S. Pat. No. 7,276,252 to Payumo et al., U.S. Pat. No. 7,300,668 to Pryce et al., U.S. Pat. No. 7,815,826 to Serdy et al., U.S. Pat. No. 7,820,201 to Pryce et al., U.S. Pat. No. 7,875,290 to Payumo et al., U.S. Pat. No. 7,931,914 to Pryce et al., U.S. Pat. No. 8,088,415 to Wang et al., U.S. Pat. No. 8,211,226 to Bredt et al., and U.S. Pat. No. 8,465,777 to Wang et al.
In essence, three-dimensional printing involves the spreading of a layer of particulate material and then selectively jet-printing a fluid onto that layer to cause selected portions of the particulate layer to bind together. This sequence is repeated for additional layers until the desired part has been constructed. The material making up the particulate layer is often referred as the “build material” and the jetted fluid is often referred to as a “binder”, or in some cases, an “activator”. Post-processing of the three-dimensionally printed part is often required in order to strengthen and/or densify the part.
Various methods are used to supply each new powder layer for three-dimensional printing. For example, some three-dimensional printers have a powder reservoir box which contains powder supported upon a vertically indexable platform and use a counter-rotating roller to transfer a predetermined amount of powder from the top of the powder reservoir box to the top of a build box. Some other three-dimensional printers utilize a traveling dispenser to dispense each new layer of powder.
It is known to produce a dense part by using three-dimensional printing to create a particulate skeleton of a metal or metal alloy and then to infiltrating a metal or metal alloy into the porosity contained within that skeleton. For example, U. S. Pat. No. 5,775,402 to Sachs et al. discloses creating a stainless steel skeleton by three-dimensional printing an article from 50 micron diameter stainless steel build powder and then presintering the printed article. The presintered article is about 60% dense by volume. Bronze is then infiltrated into the stainless steel skeleton at 1100° C. using porous stainless steel stilts to conduct the molten bronze from a reservoir up into the stainless steel skeleton. The ability of the bronze to dissolve the stainless steel is satisfied by erosion of the stilts. U. S. Pat. No. 6,585,930 B2 to Liu et al. describes the use of a one-step infiltration method in which a single heat treatment is used to sinter and infiltrate the three-dimensionally printed article.
Despite its advantages, the aforementioned prior art method of infiltrating a metal skeleton to create a dense article has its drawbacks. Among these disadvantages are the necessities of providing a reservoir of the infiltrant and of providing a stilting configuration to conduct the infiltrant from the reservoir to the metal skeleton. The use of stilting results in a significant amount of work. The work includes designing and creating the stilts and the reservoirs, setting up the stilts and filling the reservoirs, connecting the article or articles to the stilts, cutting the infiltrated articles away from the stilts, scrapping the stilts, and surface conditioning the articles to eliminate the stilts stubs that remain attached to articles and to blend these attachment areas into the articles' contours. The use of stilts also results in a large amount of scrap generation. For small articles, the weight of the amount of scrapped stilts can exceed that of the articles, even when a large number of articles are processed at the same time. The use of stilts also impacts on the size and type of furnace for infiltrating the printed article into a dense article.
The present invention provides methods of producing dense three-dimensionally printed articles in manners which overcome the aforementioned disadvantages of the prior art. The methods of the present invention utilize a multiple-component build powder which is used to three-dimensionally print the article. This multiple-component build powder comprises a mixture of a first material powder and a second material powder. The first material powder has a melting temperature, melting temperature range, or dissociation temperature which is higher than the melting temperature or melting temperature range of the second material powder and the first material powder has no more than a limited amount of solubility in the second material powder. The methods of the present invention comprise using the multiple-component build powder to three-dimensionally print an article of a desired geometry and heating the printed article to a temperature at which a sufficient amount of the second material powder melts to enable it to infiltrate throughout the interstices between the first material powder particles so that the article achieves a room temperature relative density of at least 85 percent of its theoretical density, the theoretical density being the density the article would have if it contained no porosity.
The criticality of the features and merits of the present invention will be better understood by reference to the attached drawings. It is to be understood, however, that the drawings are designed for the purpose of illustration only and not as a definition of the limits of the present invention.
In this section, some preferred embodiments of the present invention are described in detail sufficient for one skilled in the art to practice the present invention without undue experimentation. It is to be understood, however, that the fact that a limited number of preferred embodiments are described herein does not in any way limit the scope of the present invention as set forth in the appended claims. It is to be understood that whenever a range of values is described herein or in the appended claims that the range includes the end points and every point therebetween as if each and every such point had been expressly described. Unless otherwise stated, the word “about” as used herein and in the appended claims is to be construed as meaning the normal measuring and/or fabrication limitations related to the value which the word “about” modifies. Unless expressly stated otherwise, the term “embodiment” is used herein to mean an embodiment of the present invention.
The methods of the present invention comprise a step of three dimensional printing a multi-component build powder, i.e. a build powder mixture, which comprises a first material powder and a second material powder to form a printed article and subsequently heating the printed article to a temperature at which a sufficient amount of the second material powder melts to enable it to infiltrate throughout the interstices between the first material powder particles so that the article achieves a room temperature relative density of at least 85 percent of its theoretical density, the theoretical density being the density the article would have if it contained no porosity. The first material powder has a melting temperature, melting temperature range, or dissociation temperature which is higher than the melting temperature or melting temperature range of the second material powder and the first material powder has no more than a limited amount of solubility in the second material powder.
The phrase “limited amount of solubility” is to be construed as meaning that the amount of dissolution of the first material powder in the second material powder at the preselected infiltration temperature is insufficient to reduce the diameter of a particle of the first material powder which had a starting diameter of about that of the mean diameter of the first material powder by more than about 25 percent during the infiltration heat treatment of the inventive process. For example, if the first material powder has a mean diameter of 50 microns, then the first material powder would be said to have a limited amount of solubility in the second material powder if the diameter of a first material powder particle having an initial diameter of 50 microns has a diameter of no less than 37.5 microns after the infiltration heat treatment.
The mean powder size and the particle size distribution of the first material powder and the second material powder are selected to be compatible with the three-dimensional printing process. The mixture comprising the first material powder and the second material powder may be prepared by any means known in the art for mixing powders to achieve a compositionally homogeneous mixture. In order to obtain a homogenous mixture, care must be taken in preparing the mixture when the first material powder and second material powder differ in density or particle size by more than about fifteen percent. A level of homogeneity sufficient to result in the printed part having substantially the same distribution of the first material powder and the second material powder on each printed layer is preferred.
The composition of a particular build powder mixture in terms of the relative amounts of the first material powder and the second material powder is chosen such that the amount of second material powder is just sufficient to fully infiltrate interstices the first material powder taking into consideration any dissolution that may occur of one of these materials by the other. Preferably, the volume portion of the first material powder in the build powder mixture is in the range of about 50% to about 95%, and more preferably in the range of about 50% to about 85%.
The compositions of the first material powder and the second material powder are chosen to provide the article with the desired physical properties while taking into consideration that these materials must also be compatible with the three-dimensional printing process and the heat treatment process that will transform the printed article into the dense article. The first material powder is selected so as to have a melting temperature, a melting temperature range, or a dissociation temperature that is above the melting temperature or the melting temperature range of the second material powder. The second material powder is selected such that it is capable of infiltrating into the interparticle interstices between the first material powder particles at a preselected temperature or temperature range so that the article achieves a room temperature relative density of at least 85 percent of its theoretical density. The first material powder may be a ceramic, metal, or metal alloy. The second material powder may be a metal or metal alloy. For example, in one embodiment, the first material powder is a stainless steel and the second material powder is a bronze. In another embodiment, the first material powder is a copper and the second material powder is a bronze.
A 420 grade stainless steel powder was selected for use as a first material powder and a bronze powder (90 weight percent copper and 10 weight percent tin) was selected for use as a second material powder. The first material powder had a mean particle size of about 30 microns and the second material powder had a mean particle size of about 30 microns. A build powder mixture was created by blending together 70 volume percent of the first material powder with 30 volume percent of the second material powder. The blending was done using a Turbula mixer model number T2F available from Glen Mills Inc, Clifton, N.J. 07014 United States in which 1.4 liter batches of the components were mixed for 30 minutes each in a 2 liter mixing container.
An impeller design was chosen as the article to be made. The fully dense impeller 2 after heat treatment made in this example is shown in
The density of the heat treated impeller was measured using the Archimedes method to be 89%.
A stator design was chosen as the article to be made. The fully dense stator 10 after heat treatment made in this example is shown in
Four tensile test bars were chosen as the articles to be made. Each of the bars was approximately 15.24 centimeters long and 1.27 centimeters in diameter. These bars, Samples A-D, were processed as described in Example 1, except that two of the bars, Samples C and D, were heat treated at a hold temperature of 1100° C. The bars were then tensile tested and the measured properties are reported in Table 1.
A Mobius strip-like art object was chosen as the article to be made. The fully dense art object 20 after heat treatment made in this example is shown in
A medallion was chosen as the article to be made. The fully dense medallion 30 after heat treatment made in this example is shown
While only a few embodiments of the present invention have been shown and described, it will be obvious to those skilled in the art that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention as described in the following claims. All United States patents and patent applications, all foreign patents and patent applications, and all other documents identified herein are incorporated herein by reference as if set forth in full herein to the full extent permitted under the law.
This patent application claims priority to U.S. Provisional Application Ser. No. 61/919845, filed Dec. 23, 2013, and incorporates the provisional application by reference in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US14/70732 | 12/17/2014 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61919845 | Dec 2013 | US |