Motors, particularly gas powered motors or automobile engines, create a significant amount of vibration. For example, the action of the cam shaft creates torsional vibration. Torsional vibration can be reduced by using a vibration dampener. Typically the dampener mounts to the drive shaft and includes an annular weight fixed to a hub by an elastomeric member. A pulley may ride on the exterior surface of annular weight. Regardless, it is important that the weight not slip relative to the hub.
The elastomeric member or ring can be formed in a number of different ways. The elastomer can be injection molded between the annular weight and the hub and cured in place. This is by far the strongest bond that can be achieved in the torsional vibration dampener. Alternately a pre-formed or pre-cured elastomeric ring can be forced between the annular weight and the hub. Adhesive can be pre-applied to either surface to improve the bond between the metal weight and the metal hub.
The least expensive torsional vibration dampener simply uses a pre-cured elastomeric member which is compressed and force-fitted between the annular ring and hub. The resulting compression provides a strong bond between the annular ring and hub and prevents relative slippage. However, as this heats, the elastomeric member softens and slipping is a more significant problem.
The concern with relative movement between a elastomeric member and a metal member can be found in other applications such as the rubber bushing on a shock absorber.
The present invention is premised on the realization that the bond between a previously cured elastomeric member and a metal surface can be significantly enhanced by phosphating the metal surface prior to compression fitting the elastomeric member to the metal member.
Further with certain elastomeric members the bond strength between the metal surface and the elastomeric member can increase as the composite structure is heat aged as might occur during use. The phosphated surface actually promotes a bond between the metal surface and the elastomeric member particularly with respect to pre-cured EPDM and pre-cured ethylene acrylates.
The objects and advantages of the present invention will be further appreciated in light of the following detailed description and drawings in which:
According to the present invention, the bond strength between a metal surface and a compression fitted rubber surface is improved by phosphating the metal surface prior to compression fitting the rubber member against the metal surface. As described below, the present invention is particularly useful in the formation of torsional vibration dampeners. The same invention can also be used in other applications such a rubber bushings attached to shock absorbers and the like. However, the invention will be particularly described with respect to a torsional vibration dampener.
There are a vast number of different designs of torsional vibration dampeners. Exemplary vibration dampeners are disclosed in U.S. Pat. No. 4,710,152 and U.S. Pat. No. 5,231,893. The vibration dampener 10 shown in
The elastomeric member can be a wide variety of different elastomers and is cured prior to assembly. The elastomeric member can be for example natural rubber or synthetic elastomer. Suitable elastomers include EPDM, styrene butadiene rubber, isoprene rubber, nitrile rubber, ethylene propylene copolymer and ethylene acrylic copolymer. The selection of the particular elastomeric member simply depends on the particular application. With respect to torsional vibration dampeners, the elastomer and its formulation are dictated by customer demand and performance requirements. An exemplary EPDM formula is shown below.
One skilled in the art can vary this widely or use different elastomer formulations to achieve the desired result.
The hub itself and the weight are both metal. Generally these will be formed from automotive ductile cast iron, automotive gray cast iron, steel or aluminum. The hub preferably will use automotive ductile cast iron whereas the weight is preferably automotive gray cast iron although this is not essential for use in the present invention.
Both the annular weight, particularly its inner surface, and the hub, particularly its outer annular surface, are subjected to a phosphatizing treatment. In such a treatment the surfaces are first subjected to an alkaline wash by immersing or spraying the metal with an aqueous alkaline solution having a pH of 9–13. The pH is established by a sodium hydroxide solution. This can be heated if necessary depending upon how dirty the metal surface is. Generally this would take a matter of a few seconds to several minutes to accomplish. The metal is then rinsed with tap water.
The phosphatizing agent is an acidic aqueous solution of phosphate ion. The phosphate may be any soluble phosphate including zinc phosphate, iron phosphate, calcium phosphate and mixed calcium zinc phosphate. Iron phosphate is preferred. The concentration of the phosphate ion should be 1 to 4% and the pH of the bath should be 2 to 6.
Some phosphatizing baths include certain accelerators. These are all well known in the art. Accelerators that are acceptable for use in the present invention include sodium chlorate, sodium molybdate, sodium nitrobenzene sulfonate, sodium nitrate, sodium nitrite, hydroxyl amine sulphate, sodium borate, plus other metal or amine salts of the above. Particular phosphatizing agents can be purchased from Parker, DuBois Chemical and Betz Dearborn. These are used per the manufacturer's instructions.
Preferably the parts are simply immersed in the phosphatizing bath at a temperature of 110 to about 150° F. for a period of about 50 to about 150 seconds. The parts are then removed and dried.
The torsional vibration dampener is assembled by holding the hub and the annular weight in a jig or fixture leaving an annular space between the two. The elastomeric member is then placed in an appropriate fixture or annular space and hydraulic or pneumatic pressure is applied to force the elastomeric member into the annular space. Adhesive is not applied to either surface of the annular weight or the hub.
For use in the present invention, two preferred elastomeric members are ethylene propylene diene monomer rubber and ethylene acrylate polymers. The present invention improves the grip strength between any elastomeric member and the inner surface of the annular weight or the outer surface of the hub. When EPDM or ethylene acrylate copolymer are used, the bond strength between the elastomeric member and the phosphated metal surfaces actually increases as surfaces are heated overtime. This heating typically occurs during use. For example an automobile's torsional vibration dampener is subject to elevated temperatures (in excess of 100° C.) for extended periods of time. This heat aging increases bond strength.
This has been a description of the present invention along with the preferred method of practicing the invention. However, the invention itself should only be defined by the appended claims.
This application is a division of application Ser. No. 09/345,977, filed Jul. 1, 1999.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3175636 | Winkelmann | Mar 1965 | A |
| 3287197 | Errede | Nov 1966 | A |
| 3634146 | Wystrach et al. | Jan 1972 | A |
| 3799838 | Shaw et al. | Mar 1974 | A |
| 3858925 | Gaydecki | Jan 1975 | A |
| 3955861 | Orain | May 1976 | A |
| 3976624 | Inouye et al. | Aug 1976 | A |
| 4073047 | Fishbaugh et al. | Feb 1978 | A |
| 4102046 | Downing et al. | Jul 1978 | A |
| 4297159 | Dobias et al. | Oct 1981 | A |
| 4536225 | Cayless et al. | Aug 1985 | A |
| 5036943 | Kashiwagi | Aug 1991 | A |
| 5093204 | Watanabe et al. | Mar 1992 | A |
| 5145025 | Damian | Sep 1992 | A |
| 5185916 | Maeno et al. | Feb 1993 | A |
| 5300158 | Chen et al. | Apr 1994 | A |
| 5316810 | Rogerson | May 1994 | A |
| 5401334 | O'Melia et al. | Mar 1995 | A |
| 5506059 | Robbins et al. | Apr 1996 | A |
| 5531841 | O'Melia et al. | Jul 1996 | A |
| 5578680 | Ando et al. | Nov 1996 | A |
| 5579661 | Yarnell et al. | Dec 1996 | A |
| 5884902 | Hamada et al. | Mar 1999 | A |
| 5884959 | Hillen | Mar 1999 | A |
| 5919331 | Smith et al. | Jul 1999 | A |
| 6080268 | Smith et al. | Jun 2000 | A |
| 6082721 | Kingsley | Jul 2000 | A |
| 6292995 | Corbin et al. | Sep 2001 | B1 |
| 6358349 | Christenson et al. | Mar 2002 | B1 |
| 6361592 | Song et al. | Mar 2002 | B1 |
| 6440231 | Beiersdorf et al. | Aug 2002 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20020096245 A1 | Jul 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09345977 | Jul 1999 | US |
| Child | 10057474 | US |