Method to produce a thermoplastic wear resistant foil

Description

FIELD OF THE DISCLOSURE

The present disclosure relates to a method to produce a thermoplastic wear resistant foil, a method to produce a building panel including such a thermoplastic wear resistant foil and a building panel.

TECHNICAL BACKGROUND

In recent years, so-called Luxury Vinyl Tiles and Planks (LVT) have gained increasing success. These types of floor panels usually comprise a thermoplastic core, a thermoplastic décor layer arranged on the core, a transparent wear layer on the décor layer, and a coating applied on the wear layer. The thermoplastic material is often PVC. The wear layer is conventionally a PVC foil, for example, having a thickness of 0.2-0.7 mm. The coating applied on the wear layer is conventionally a UV curing polyurethane coating. The wear layer together with the coating provides the wear resistance of the floor panel and protects the décor layer.

However, when subjecting floor panels to wear, it has been shown that the coating and the wear layer are relatively easily worn down, or at least worn such that the appearance of the wear layer is affected, such as having scratches and/or not being transparent any longer. Compared to a conventional laminate floor panel, the wear resistance of a LVT floor panel is inferior. However, LVT floors offer several advantages over, for example, laminate floors, such as deep embossing, dimensional stability related to humidity, moisture resistance and sound absorbing properties.

It is therefore desirable to provide a LVT product having improved wear resistance. It is also desirable to simplify the build up of LVT product.

It is known from US 2008/0063844 to apply a surface coating including aluminum oxide on a resilient floor covering. The coating is a wet coating.

WO 2013/079950 discloses an anti-skid floor covering comprising at least two transparent polymer layers, wherein particles of an aggregate material having an average particle size of between about 0.05 mm to about 0.8 mm are located between and/or within the two or more polymer layers. The particles improve the slip resistance of the floor covering.

SUMMARY

It is an object of at least embodiments of the present disclosure to provide an improvement over the above described techniques and known art.

A further object of at least embodiments of the present disclosure is to improve the wear resistance of LVT floorings.

A further object of at least embodiments of the present disclosure is to simplify the build up of LVT floorings.

At least some of these and other objects and advantages that will be apparent from the description have been achieved by a method to produce a wear resistant foil according to a first aspect. The method includes a first foil comprising a first thermoplastic material, applying wear resistant particles and a second thermoplastic material on the first foil, and adhering the first foil to the second thermoplastic material and the wear resistant particles to form a wear resistant foil.

The first and the second thermoplastic material may be thermoplastic materials of different type, or may be thermoplastic material of the same type.

An advantage of at least embodiments of the present disclosure is that a wear resistant foil having improved wear resistance is provided. By including wear resistant particles in the wear resistant foil, the wear resistant particles provide additional wear resistance to the thermoplastic materials of the first and the second foil. The wear resistance of the foil is improved compared to a conventional wear layer of LVT products.

Furthermore, conventional coatings, for example, a UV curable PU coating conventionally applied on the wear layer, may be replaced by using the wear resistant foil according to the disclosure instead. A conventional coating step may be replaced by arranging a single foil. Thereby, the production process is simplified and the number of steps in the production process is reduced by arranging a wear resistant foil having improved wear resistant properties instead of several layers or coatings.

By using different thermoplastic material in the first foil and the second thermoplastic material applied on the first foil, it is possible to benefit from different thermoplastic material having different properties. The desired properties of the material of the first foil may differ from the desired properties of the thermoplastic material applied on the first foil. For the layer formed by the second thermoplastic material and the wear resistant particles arranged on the first foil, properties such as stain resistance and scratch resistance are important, and the choice of the thermoplastic material can be chosen to match these criteria. Usually, suitable thermoplastic material for forming the layer applied on the first foil may be more expensive compared to thermoplastic material used as, for example, in printed film or as core material. By only using such thermoplastic material in the layer arranged on the first foil, the cost of the wear resistant foil can be controlled. Further, the layer formed by the second thermoplastic material can have a layer thickness being less than a layer thickness of the first foil. By choosing different thermoplastic materials for the first foil and the overlying layer, the thermoplastic materials can be used in an efficient and cost effective manner. By adjusting the layer thicknesses, the materials can be used in an even more efficient manner.

The object of the wear resistant particles is to provide wear resistance of the foil when being worn, not to provide slip resistance.

The second thermoplastic material may be in powder form when applied on the first foil.

The second thermoplastic material may be in powder form when adhered to the first foil, such as, for example, when being pressed to the first foil.

The first foil, the second thermoplastic material and the wear resistant particles may be adhered to each other by pressing the first foil, the wear resistant particles and the second thermoplastic material together.

The wear resistant foil is preferably transparent, or at least substantially transparent, for example, having a light transmittance index exceeding 80%, preferably exceeding 90%.

Thereby, any decorative layer or decorative print is visible through the wear resistant foil. Preferably, the wear resistant foil does not influence of the impression of any decorative layer or decorative print arranged beneath the wear resistant foil. The wear resistant foil is preferably non-pigmented.

The wear resistant particles may be enclosed by the first foil and the second thermoplastic material after being adhered to each other. The wear resistant particles may be encapsulated by the second foil. Preferably, the wear resistant particles do not protrude from a surface of a layer formed by the second thermoplastic material after being adhered to the first layer. If the wear resistant particles protrude beyond the surface of the layer formed by the second thermoplastic material, the wear resistance foil will cause wear on items placed on the wear resistance foil. For example, when the wear resistant foil is used a top surface of a flooring, protruding wear resistant particles will cause wear on socks, shoes, etc. Further, protruding wear resistant particles would cause a rough and/or harsh surface of the wear resistant foil, as provided by a slip resistant surface. The aim of the wear resistant particles enclosed by the thermoplastic material is to provide wear resistance when the second foil is worn, not to provide slip resistance.

The wear resistant particles and the second thermoplastic material may be applied as a mix. As an alternative or complement, the wear resistant particles and the second thermoplastic material may be applied separately.

The second thermoplastic material may be applied in molten form. The second thermoplastic material may be applied in an extrusion process such as extrusion lamination or extrusion coating on the first foil.

The first thermoplastic material may be or comprise polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

The second thermoplastic material may be or comprise polyvinyl chloride (PVC) or polyurethane (PU). The second thermoplastic material may be or comprise polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

The first foil may substantially consist of the thermoplastic material, preferably polyvinyl chloride, and optionally additives.

Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

The first foil may be a decorative foil. The first foil may be printed, for example by digital printing, direct printing, rotogravure printing, etc.

The second thermoplastic material may be or comprise polyvinyl chloride (PVC) or polyurethane (PU).

By arranging the second thermoplastic material being or comprising polyurethane, no additional polyurethane containing coating has to be provided on top of the wear resistant foil. Thereby, the layered structure of a LVT product may be simplified. Furthermore, compared to for example a conventional wear layer substantially consisting of PVC, a wear resistant foil comprising an upper portion of polyurethane (PU) obtains improved chemical resistance. Its scratch resistance and micro-scratch resistance are also improved. An upper layer of polyurethane (PU) also provides improved resistance against black heel mark. An additional advantage is that curable polyurethane, such as UV curable polyurethane, shrinks when curing. By pressing a thermoplastic polyurethane (PU) material, no, or at least reduced, such shrinking occurs.

In one embodiment, the first thermoplastic material may be or comprises polyvinyl chloride (PVC) and the second thermoplastic material comprises polyurethane (PU). Thereby, a wear resistant foil having the properties of both polyvinyl chloride (PVC) and polyurethane (PU) is provided.

The wear resistant particles comprise aluminum oxide. The wear resistant may comprise carborundum, quartz, silica, glass, glass beads, glass spheres, silicon carbide, diamond particles, hard plastics, reinforced polymers and organics.

The wear resistant particles may have an average particle size of less than 45 μm.

The wear resistant particles may have a refractive index similar to the refractive index of the second thermoplastic material. The wear resistant particles may have a refractive index of 1.4-1.7. In one embodiment, the wear resistant particle may have a refractive index of 1.4-1.9, preferably 1.5-1.8, for example, 1.7-1.8. The refractive index of the wear resistant particles may not differ from the refractive index of the second thermoplastic material more than ±20%.

A layer formed by the second thermoplastic material and the wear resistant particles may have a thickness being less than 75 μm, for example, such as about 50 μm, after being adhered to the first foil, for example, by pressing.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. The wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. However, during pressing, the wear resistant particles are pressed into the first foil such that the wear resistant particles do not protrude beyond an upper surface of the layer formed by the second thermoplastic material and the wear resistant particles after pressing, although the wear resistant particles having an average particle size exceeding the thickness of the layer formed by the second thermoplastic material and the wear resistant particles.

The ratio between the size of the wear resistant particles and the thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than 1.5:1.

The thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than the thickness of the first foil.

The method may further comprise applying scratch resistant particles on the first foil, or together with the second thermoplastic material. The scratch resistant particles may be or comprise nano-sized silica particles, preferably fused silica particles. The scratch resistant particles may be or comprise aluminum oxide.

According to a second aspect, a method of forming a building panel is provided. The method comprises applying a wear resistant foil produced according to the first aspect on a core, and applying pressure to the wear resistant foil and the core for forming a building panel.

The core may be provided with a decorative layer. The core may be provided with a print on a surface of the core. The wear resistant foil may be arranged on the decorative layer, or on the print. Alternatively, the first foil of the wear resistant foil may be a decorative layer.

The core may comprise a third thermoplastic material.

The first, second and third thermoplastic material may be thermoplastic materials of different types, or may be the same type of thermoplastic material. The first, second and third thermoplastic material may be or comprise any one of the follow group: polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The core may be a thermoplastic core, a WPC (Wood Plastic Composite), etc. The core may be provided with several layers. The core may be foamed.

The core may be a wood-based board or a mineral board. The core may in embodiments be HDF, MDF, particleboard, OSB, Wood Plastic Composite (WPC).

The decorative layer may be a thermoplastic foil. The decorative layer may comprise any of the thermoplastic material listed above.

According to a third aspect, a method to produce a building panel is provided. The method includes providing a core, applying a first foil comprising a first thermoplastic material on the core, applying wear resistant particles and a second thermoplastic material on the first foil, and adhering the core to the first foil to the second thermoplastic material and the wear resistant particles to each other to form a building panel.

The first and the second thermoplastic material may be thermoplastic materials of different type, or may be thermoplastic material of the same type.

In one embodiment, the wear resistant foil is produced in connection with forming the building panel. The wear resistant foil may be laminated together when laminating any other layer, for example a decorative layer, a balancing layer, etc., to the core.

Furthermore, conventional coatings, for example a UV curable PU coating conventionally applied on the wear layer, may be replaced by using the wear resistant foil according to the disclosure instead. A conventional coating step may be replaced by arranging a single foil. Thereby, the production process is simplified and the number of steps in the production process is reduced by arranging a wear resistant foil having improved wear resistant properties instead of several layers or coatings.

By using different thermoplastic material in the first foil and in the second thermoplastic material applied on the first foil, it is possible to benefit from different thermoplastic material having different properties. The desired properties of the thermoplastic material of the first foil may differ from the desired properties of the second thermoplastic material applied on the first foil. For the layer formed by the second thermoplastic material and the wear resistant particles arranged on the first foil, properties such as stain resistance and scratch resistance are important, and the choice of the thermoplastic material can be chosen to match these criteria. Usually, suitable thermoplastic material for forming the layer applied on the first foil may be more expensive compared to thermoplastic material used as, for example, in printed film or as core material. By only using such thermoplastic material in the layer arranged on the first foil, the cost of the wear resistant foil can be controlled. Further, the layer formed by the second thermoplastic material can have a layer thickness being less than a layer thickness of the first foil. By choosing different thermoplastic materials for the first foil and the overlying layer, the thermoplastic materials can be used in an efficient and cost effective manner. By adjusting the layer thicknesses, the materials can be used in an even more efficient manner.

The object of the wear resistant particles is to provide wear resistance of the foil when being worn, not to provide slip resistance.

The second thermoplastic material may be in powder form when applied on the first foil.

The wear second thermoplastic material may be in powder form when adhered to the first foil, such as, for example, when pressed to the first foil.

The first foil together with the wear resistant particles and the second thermoplastic material form a wear resistant foil, preferably being transparent, or at least substantially transparent, for example, having a light transmittance index exceeding 80%, preferably exceeding 90%. Thereby, any decorative layer or decorative print is visible through the wear resistant foil. Preferably, the wear resistant foil does not influence of the impression of any decorative layer or decorative print arranged beneath the wear resistant foil. The wear resistant foil is preferably non-pigmented.

The wear resistant particles may be enclosed by the first foil and the second thermoplastic material after being adhered to each other.

Preferably, the wear resistant particles do not protrude from a surface of a layer formed by the second thermoplastic material opposite the first foil after pressing. If the wear resistant particles protrude beyond the surface of the second thermoplastic material, the wear resistance foil will cause wear on items placed on the wear resistance foil. For example, when the wear resistant foil is used a top surface of a flooring, protruding wear resistant particles will cause wear on socks, shoes, etc. Further, protruding wear resistant particles would cause a rough and/or harsh surface of the wear resistant foil, as provided by a slip resistant surface. The aim of the wear resistant particles enclosed by the thermoplastic material is to provide wear resistance when the second thermoplastic material is worn, not to provide slip resistance.

In one embodiment, the first thermoplastic material comprises polyvinyl chloride (PVC) and the second thermoplastic material comprises polyurethane (PU).

The wear resistant particles may preferably comprise aluminum oxide. The wear resistant particles may comprise aluminum oxide such as corundum, carborundum, quartz, silica, glass, glass beads, glass spheres, silicon carbide, diamond particles, hard plastics, reinforced polymers and organics, or combinations thereof.

The wear resistant particles may have an average particle size of less than 45 μm. The wear resistant particles may have a refractive index similar to the refractive index of the second thermoplastic material. The wear resistant particles may have a refractive index of 1.4-1.7. In one embodiment, the wear resistant particle may have a refractive index of 1.4-1.9, preferably 1.5-1.8, for example, 1.7-1.8. The refractive index of the wear resistant particles may not differ from the refractive index of the second thermoplastic material more than ±20%.

A layer formed by the second thermoplastic material and the wear resistant particles may have a thickness being less than 75 μm, for example, such as about 50 μm, after being adhered to each other.

The ratio between the size of the wear resistant particles and the thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than 1.5:1.

The thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than the thickness of the first foil.

The method may further comprise applying scratch resistant particles on the first foil. Alternatively, or as a complement, the scratch particles may be applied together with the second thermoplastic material. The scratch resistant particles may be or comprise nano-sized silica particles, preferably fused silica particles. The scratch resistant particles may be or comprise aluminum oxide.

The core may comprise a third thermoplastic material.

The first, second and third thermoplastic material may be thermoplastic materials of different types, or may be the same type of thermoplastic material.

The third thermoplastic material may be or comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The core may be a thermoplastic core, a WPC (Wood Plastic Composite), etc. The core may be provided with several layers. The core may be foamed.

The core may be a wood-based board or a mineral board. The core may in embodiments be HDF, MDF, particleboard, OSB, Wood Plastic Composite (WPC).

A decorative layer may be arranged on the core. In one embodiment, the method may comprise applying a decorative layer prior to applying the first foil. The decorative layer may be a thermoplastic layer. The decorative layer may be a wood powder layer comprising a thermosetting binder and lignocellulosic or cellulosic particles. The decorative layer may be a thermoplastic layer applied as a powder, preferably comprising a print printed into the thermoplastic material in powder form. The decorative layer may be a wood veneer layer, a cork layer or a decorative paper.

In one embodiment, the first foil is arranged directly on the core. The core may be provided with a print, and the first foil is arranged on the print. Alternatively, or as a complement, the first foil may be a decorative foil. The first foil may be printed, for example by digital printing, direct printing, rotogravure, etc. Preferably, the print is provided on a surface of the first foil facing the core.

The method may further comprise applying a coating on the wear resistant foil. The coating may comprise acrylate or methacrylate monomer or acrylate or methacrylate oligomer. The coating may be radiation curing, such as UV curing or electron beam curing.

According a fourth aspect, a method to produce a wear resistant foil is provided. The method comprises providing a carrier, applying wear resistant particles and a second thermoplastic material on the carrier, and adhering the wear resistant particles and the second thermoplastic material to each other to form a wear resistant foil.

Embodiments of the fourth aspect all the advantages of the first aspect, which previously has been discussed, whereby the previous discussion is applicable also for the building panel.

The second thermoplastic material may be in powder form when applied on the carrier.

The wear second thermoplastic material may be in powder form when adhered to the carrier, such as, for example, when pressed to the carrier.

The wear resistant foil is preferably transparent, or at least substantially transparent, for example, having a light transmittance index exceeding 80%, preferably exceeding 90%. Thereby, any decorative layer or decorative print is visible through the wear resistant foil. Preferably, the wear resistant foil does not influence of the impression of any decorative layer or decorative print arranged beneath the wear resistant foil. The wear resistant foil is preferably non-pigmented.

The wear resistant particles may be enclosed by the first foil and the second thermoplastic material after being adhered to each other.

Preferably, the wear resistant particles do not protrude from a surface of a layer formed by the second thermoplastic material after being adhered to the first foil. If the wear resistant particles protrude beyond the surface of the layer formed by the second thermoplastic material, the wear resistance foil will cause wear on items placed on the wear resistance foil. For example, when the wear resistant foil is used a top surface of a flooring, protruding wear resistant particles will cause wear on socks, shoes, etc. Further, protruding wear resistant particles would cause a rough and/or harsh surface of the wear resistant foil, as provided by a slip resistant surface. The aim of the wear resistant particles enclosed by the second thermoplastic material is to provide wear resistance when the second foil is worn, not to provide slip resistance.

In one embodiment, the carrier may be a first foil comprising a first thermoplastic material as discussed above in respect of the third aspect.

The carrier may be a substrate.

In one embodiment, the carrier may be a temporary carrier such as a release foil or conveyor means.

In one embodiment, the carrier may be a core. The core may be a thermoplastic core, a Wood Plastic Composite (WPC), a wood-based board or a mineral board. The step of adhering may comprise adhering the carrier to the second thermoplastic material and the wear resistant particles.

The second thermoplastic material may be or comprise polyvinyl chloride (PVC) or polyurethane (PU).

The method may further comprise releasing the wear resistant foil from the carrier. The wear resistant particles may comprise aluminum oxide. The wear resistant may comprise carborundum, quartz, silica, glass, glass beads, glass spheres, silicon carbide, diamond particles, hard plastics, reinforced polymers and organics.

The wear resistant particles may have an average particle size of less than 45 μm.

A layer formed by the second thermoplastic material and the wear resistant particles may have a thickness being less than 75 μm, for example, such as about 50 μm, after being adhered to each other.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. The wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. However, during pressing, the wear resistant particles are pressed into the carrier such that the wear resistant particles do not protrude beyond an upper surface of the layer formed by the second thermoplastic material and the wear resistant particles after pressing, although the wear resistant particles having an average particle size exceeding the thickness of the layer formed by the second thermoplastic material and the wear resistant particles.

The ratio between the size of the wear resistant particles and the thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than 1.5:1.

According a fifth aspect, a building panel is provided. The building panel comprises a core, a wear resistant foil arranged on a surface of the core, wherein the wear resistant foil comprises a second thermoplastic material and wear resistant particles substantially homogenously distributed in said second thermoplastic material.

Embodiments of the fifth aspect incorporate all the advantages of the first, which previously has been discussed, whereby the previous discussion is applicable also for the building panel.

The wear resistant particles may be enclosed by the second thermoplastic material.

Preferably, the wear resistant particles do not protrude from a surface of a layer formed by the second thermoplastic material. If the wear resistant particles protrude beyond the surface of the second foil, the wear resistance foil will cause wear on items placed on the wear resistance foil. For example, when the wear resistant foil is used a top surface of a flooring, protruding wear resistant particles will cause wear on socks, shoes, etc. Further, protruding wear resistant particles would cause a rough and/or harsh surface of the wear resistant foil, as provided by a slip resistant surface. The aim of the wear resistant particles enclosed by the thermoplastic material is to provide wear resistance when the second foil is worn, not to provide slip resistance.

The wear resistant foil may further comprise a first foil comprising a first thermoplastic material.

The first thermoplastic material may be or comprise polyvinyl chloride (PVC). The first thermoplastic material may be or comprise polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

The wear resistant particles may preferably comprise aluminum oxide. The wear resistant particles may comprise aluminum oxide, carborundum, quartz, silica, glass, glass beads, glass spheres, silicon carbide, diamond particles, hard plastics, reinforced polymers and organics, or a combination thereof.

The wear resistant particles may have an average particle size of less than 45 μm.

A layer formed by the second thermoplastic material and the wear resistant particles may have a thickness being less than 75 μm, for example, such as about 50 μm, after being adhered.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. The wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the second thermoplastic material and the wear resistant particles. However, during pressing, the wear resistant particles are pressed into the core or any intermediate layer such as a first foil such that the wear resistant particles do not protrude beyond an upper surface of the layer formed by the second thermoplastic material and the wear resistant particles after pressing, although the wear resistant particles having an average particle size exceeding the thickness of the layer formed by the second thermoplastic material and the wear resistant particles.

The ratio between the size of the wear resistant particles and the thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than 1.5:1.

The thickness of the layer formed by the second thermoplastic material and the wear resistant particles may be less than the thickness of the first foil.

The building panel may further comprise a decorative layer arranged on the core, wherein the wear resistant foil is arranged on the decorative layer.

The core may comprise a third thermoplastic material. The third thermoplastic material may be or comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

The core may be a thermoplastic core, a Wood Plastic Composite (WPC), a wood-based board or a mineral board.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure will by way of example be described in more detail with reference to the appended schematic drawings, which show embodiments of the present disclosure.

FIG. 1 shows a method to produce a wear resistant foil according a first embodiment.

FIG. 2 shows a method to produce a wear resistant foil according to a second embodiment.

FIG. 3 shows a building panel.

FIG. 4 shows a method to produce a building panel.

FIGS. 5A-B show embodiments of a building panel.

FIG. 6A shows a method to produce a wear resistant foil.

FIG. 6B shows a method to produce a building panel.

DETAILED DESCRIPTION

A method to produce a wear resistant foil 10 according to an embodiment will now be described with reference to FIG. 1. FIG. 1 shows a production line for producing a wear resistant foil 10.

The first foil 1 comprises a first thermoplastic material. The first thermoplastic material may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

In FIG. 1, the first foil 1 is provided as a continuous web. In other embodiments, the first foil 1 may also be cut into sheets. The first foil 1 may also be formed by an extrusion process. The first foil 1 may also be formed of a powder layer comprising the first thermoplastic material in powder form.

Preferably, the first foil 1 is formed of the thermoplastic material. The first foil 1 may substantially consist of the thermoplastic material, and optionally additives. Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

In one embodiment, the first foil 1 is a PVC foil.

The first foil 1 may have a thickness of 0.1-1 mm.

In one embodiment, the first foil 1 is a decorative foil. The first foil 1 may be printed, for example by digital printing, direct printing, rotogravure, etc.

As shown in FIG. 1, an applying device 3 applies, preferably scatters, a second thermoplastic material 5 in powder form and wear resistant particles 4 on the first foil 1. In FIG. 1, the thermoplastic material 5 and the wear resistant particles 4 are applied as a mix.

The thermoplastic material 5 and the wear resistant particles 4 may also be applied separately. Preferably, if applied separately, the wear resistant particles 4 are applied first, and the second thermoplastic material 5 is applied on the wear resistant particles 4.

The second thermoplastic material 5 may be the same as in the first foil 1, or being different from the thermoplastic material of the first foil 1. The second thermoplastic material 5 may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

In the embodiment shown in FIG. 1, the second thermoplastic material 5 is applied as a powder. By powder is also meant powder that has formed granules of the thermoplastic material, dry blends of the thermoplastic material, or agglomerates of the thermoplastic material. The granules may comprise both the thermoplastic material 5 and the wear resistant particles 4. The agglomerates may comprise both the thermoplastic material 5 and the wear resistant particles 4.

The average particle size of the thermoplastic material 5 may be less than 500 μm, preferably 50-250 μm. The thermoplastic material 5 in a dry blend may have size of less than 500 μm. Granules of the thermoplastic material 5 may have an average particle size of 200-4000 μm, preferably less than 1000 μm.

In the embodiment shown in FIG. 1, the wear resistant particles 4 and the second thermoplastic material 5 is applied as a mix.

In embodiments, the second thermoplastic material 5 may be applied in molten form, which is described in more detail with reference to FIG. 6A. The wear resistant particles 4 may be mixed with the second thermoplastic material 5 in molten form or applied separately. The second thermoplastic 5 in molten form may be applied in an extrusion process such as extrusion lamination and extrusion coating on the first foil 1.

The wear resistant particles 4 may be aluminum oxide particles such as corundum. Alternatively, or as a complement, the wear resistant particles 4 may be carborundum, quartz, silica, glass, glass beads, glass spheres, silicon carbide, diamond particles, hard plastics, reinforced polymers and organics.

The wear resistant particles 4 preferably have an average particle size within the range of 10-200 μm, preferably within the range of 50-120 μm such as 50-100 μm. The wear resistant particles 4 may have an average particle size of less than 50 μm, preferably less than 45 μm. The wear resistant particles 4 may have a spherical shape or an irregular shape. The wear resistant particles 4 may be surface treated. The wear resistant particles 4 may be silane-treated particles.

The wear resistant particles 4 may have a refractive index similar to the refractive index of the second thermoplastic material 5. The wear resistant particles may have a refractive index of 1.4-1.7. In one embodiment, the wear resistant particle may have a refractive index of 1.4-1.9, preferably 1.5-1.8, for example, 1.7-1.8. The refractive index of the wear resistant particles may not differ from the refractive index of the second thermoplastic material more than ±20%.

The wear resistant particles may be applied in an amount of 20-100 g/m2, preferably in an amount of 40-60 g/m2.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing. However, the wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material 5 after pressing. During pressing, the wear resistant particles are pressed into the first foil such that the wear resistant particles do not protrude beyond an upper surface of the layer formed by the second thermoplastic material 5, although the wear resistant particles having an average particle size exceeding the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing.

The ratio between the size of the wear resistant particles and the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing may be less than 1.5:1.

Scratch resistant particles (not shown) may also be applied on the first foil 1, as a mix together with the thermoplastic material 5 and the wear resistant particles 4 or separately. By scratch resistant particles are meant particles improving the scratch or scratch resistant properties of the foil. The scratch resistant particles may be applied together with the wear resistant particles 4, for example as a mix, or may be applied separately. Preferably, the scratch particles are arranged on an upper part of the layer formed by the thermoplastic material 5 and the wear resistant particles 4. The scratch resistant particles may be may be or comprise nano-sized silica particles, preferably fused silica particles. The scratch resistant particles may be or comprise aluminum oxide.

The scratch resistant particles may be disc shaped particles, preferably having a width/thickness ratio being equal or exceeding 3:1, more preferably being equal or exceeding 5:1. Such disc-shaped particles orientate along the surface of the foil, thereby improving the scratch resistance of the foil. The scratch resistant particles may have an average particle size of 1-50 μm, preferably 10-20 μm.

Additives may also be applied on the first foil 1, or together with the second thermoplastic material. Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

In one embodiment, the first foil 1 is a PVC foil and the second thermoplastic material 5 is polyurethane (PU) in powder form. In one embodiment, the first foil 1 is a PVC foil and the second thermoplastic material 5 is PVC in powder form.

The first foil 1 and the second thermoplastic material 5 in powder form are thereafter adhered to each other, for example, being pressed together, to form a wear resistant foil 10 comprising the first foil 1, the second thermoplastic material 5 and the wear resistant particles 4.

The first foil 1 and the second thermoplastic material 5 in powder form may be pressed together in a calendering process. As shown in FIG. 1, the first foil 1 and the second thermoplastic material 5 in powder form are pressed together in continuous press 6. The first and second thermoplastic material may be adhered together by pressure alone, by heat and pressure, by pressure and adhesive, or by heat, pressure, and adhesive.

Preferably, both pressure and heat is applied in order to adhere the first foil and the second thermoplastic material together. As alternative or complements to a calendering process, a continuous or static press may also be used. The pressing operation may for example be made as a hot-hot process, a hot-cold process, etc. The pressing may be made with an embossed press matrix or press roller, such that an embossed structure is formed in the wear resistant foil.

Depending on the thermoplastic materials and process used, the pressure applied may be 5-100 bar, applied for example during 5-500 seconds. The temperature may be 80-300° C., such as 100-250° C., such as 150-200° C.

By the process described above with reference to FIG. 1, a wear resistant foil 10 is formed. The wear resistant foil 10 may be formed as a continuous foil, or be cut into sheets. The second thermoplastic material 5 and the wear resistant particles 4 form an upper part of the wear resistant foil 10. Preferably, the wear resistant particles 4 may be substantially homogenous distributed in the upper part of the wear resistant foil 10. The first foil 1 forms a lower part of the wear resistant foil 10. As seen in a cross-section of the wear resistant foil, the wear resistant particles 4 are heterogeneously distributed through the wear resistant foil 10. There is a higher concentration of the wear resistant particles 4 in the upper parts of the wear resistant foil 10 than in the lower parts of the wear resistant foil 10.

After adhering the layers, the wear resistant particles are enclosed by the first foil and the second thermoplastic material. Although the wear resistant particles and the second thermoplastic material may be applied as mix, during the pressing, the second thermoplastic material fuses and encloses the wear resistant particles. Preferably, the wear resistant particles do not protrude beyond the surface of the layer formed the second thermoplastic material facing away from the first foil. Thereby, a wear resistant foil having a smooth surface can be formed.

The wear resistant foil 10 is preferably transparent, or substantially transparent.

The second thermoplastic material 5 and the wear resistant particles 4 may be formed into a layer, which may have a thickness of 0.01-1 mm, preferably as measured in the final product, for example, after pressing or extruding. Preferably, the layer formed by the second thermoplastic material 5 and the wear resistant particles 4 has a thickness less than 0.5 mm, more preferably less than 75 μm such as about 50 μm, preferably as measured in the final product, for example, after pressing or extruding.

Different additives may be included to the first foil 1 compared to the second thermoplastic material 5 in powder form in order to obtain different properties in different layers of the wear resistant foil 10.

A wear resistant foil 10′ may also be produced in accordance with the embodiment described with reference to FIG. 2. In the embodiment shown in FIG. 2, a second thermoplastic material 5 in powder form and wear resistant particles 4 are applied, preferably scattered, by an applying device 3 on a carrier 7. The carrier 7 may be a substrate. The carrier 7 may for example be a release foil or Teflon® treated press plate. It is also contemplated that the carrier 7 may be a core 21, for example, provided with a print. The core 21 may a thermoplastic core, a WPC (Wood Plastic Composite), a wood-based board such as HDF or MDF, a mineral board, etc. It is also contemplated that a first thermoplastic material in powder form may be applied on the carrier.

The second thermoplastic material 5 may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

By powder is also meant powder that has formed granules of the thermoplastic material 5, dry blends of the thermoplastic material 5, or agglomerates of the thermoplastic material 5. The granules may comprise both the thermoplastic material 5 and the wear resistant particles 4. The agglomerates may comprise both the thermoplastic material 5 and the wear resistant particles 4.

A layer of the second thermoplastic material 5 is applied on the carrier 7. Preferably, the second thermoplastic material 5 and the wear resistant particles 4 are applied as a mix. The second thermoplastic material 5 and the wear resistant particles 4 may also be applied separately. Preferably, if applied separately, the wear resistant particles 4 are applied first, and the second thermoplastic material 5 is applied on the wear resistant particles 4.

In the embodiment shown in FIG. 2, the second thermoplastic material 5 is applied in powder form. In embodiments, the second thermoplastic material 5 may be applied in molten form, which is described in more detail with reference to FIG. 6A. The wear resistant particles 4 may be mixed with the second thermoplastic material 5 in molten form or applied separately. The second thermoplastic 5 in molten form may be applied in an extrusion process such as extrusion lamination and extrusion coating on the carrier 7.

More than one type of thermoplastic material 5 may be applied on the carrier 7. Thermoplastic materials having different properties may be applied. As an example, a PVC powder may be applied, and a PU powder may be applied on the PVC powder for forming a wear resistant foil 10′ having different properties. The wear resistant particles 4 may be applied in between the PVC powder and the PU powder. Different types of additives may also be added to the different thermoplastic materials in order to form a wear resistant foil 10′ having different properties in different layers.

The wear resistant particles 4 preferably have an average particle size within the range of 10-200 μm, preferably within the range of 50-120 μm, such as 50-100 μm. The wear resistant particles 4 preferably have an average particle size of less than 50 μm, preferably less than 45 μm. The wear resistant particles 4 may have a spherical shape or an irregular shape. The wear resistant particles 4 may be surface treated. The wear resistant particles 4 may be silane-treated particles.

The wear resistant particles may be applied in an amount of 20-100 g/m2, preferably in an amount of 40-60 g/m2.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing. However, the wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing. During pressing, the wear resistant particles are pressed into the carrier such that the wear resistant particles do not protrude beyond an upper surface of the layer, although the wear resistant particles have an average particle size exceeding the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing.

Scratch resistant particles (not shown) may also be applied on the carrier 7, or as a mix together with the thermoplastic material 5 and the wear resistant particles 4 or separately. By scratch resistant particles are meant particles improving the scratch or scratch resistant properties of the foil. The scratch resistant particles may be applied together with the wear resistant particles 4, for example as a mix, or may be applied separately. Preferably, the scratch particles are arranged on an upper part of the layer formed by the thermoplastic material 5 and the wear resistant particles 4. The scratch resistant particles may be may be or comprise nano-sized silica particles, preferably fused silica particles. The scratch resistant particles may be or comprise aluminum oxide.

Additives may also be applied on the carrier 7. Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

The additives may also be applied together with the second thermoplastic material 5.

The second thermoplastic material 5 in powder form and the wear resistant particles 4 are thereafter adhered to each other such as fused together, preferably pressed together to form a wear resistant foil 10′.

The second thermoplastic material 5 in powder form and the wear resistant particles 4 may be pressed together in a calendering process. As shown in FIG. 2, the second thermoplastic material 5 and the wear resistant particles 4 are pressed together in a continuous press 6. Preferably, both pressure and heat is applied in order to form a wear resistant foil 10′ of the second thermoplastic material 5 and the wear resistant particles 4. As alternative or complements to a calendaring process, a continuous or static press may also be used. The pressing may for example be made as a hot-hot process, a hot-cold process, etc. The pressing may be made with an embossed press matrix or press roller, such that an embossed structure is formed in the wear resistant foil 10′. As described above, the second thermoplastic material 5 may also be extruded on the carrier 7, such as extrusion coated or extrusion laminated to the carrier.

By the process described above with reference to FIG. 2, a wear resistant foil 10′ is formed, comprising the second thermoplastic material and the wear resistant particles. The wear resistant foil 10′ is preferably transparent, or substantially transparent.

The wear resistant foil may have a thickness of 0.01-1 mm, preferably as measured in the final product, for example, after pressing or extruding. Preferably, the wear resistant foil has a thickness less than 0.5 mm, more preferably less than 0.1 mm, preferably as measured in the final product, for example, after pressing or extruding.

The wear resistant foil 10, 10′ produced accordance with the embodiments described when referring to FIG. 1 and FIG. 2, may in a subsequent step be adhered to a core 21 to form a building panel 20, as shown in FIG. 3. The building panel 20 may be a floor panel, a wall panel, a ceiling panel, a furniture component, etc.

The core 21 may comprise a third thermoplastic material. The third thermoplastic material may be the same as the first and/or second material, or be different from the first and/or the second material.

The third thermoplastic material may comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The core may be formed of several layers. The core may be foamed.

In one embodiment, the core 21 comprises the third thermoplastic material and fillers. The fillers may comprise calcium carbonate, such as chalk and/or limestone, or sand.

In one embodiment, the core 21 is a Wood Plastic Composite (WPC), comprising the third thermoplastic material and wood particles as fillers.

The core 21 may be provided with a decorative layer 22 arranged on a top surface of the core 21, as shown in FIG. 3. The wear resistant foil 10, 10′ is then arranged on the decorative layer 22. The decorative layer 22 may be a decorative foil comprising a thermoplastic material. The thermoplastic material of the decorative layer may be or comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The decorative layer 22 is preferably printed, for example by direct printing, rotogravure, or digital printing.

The core 21 may also be provided with a balancing layer (not shown) arranged on a lower surface of the core 21, opposite the decorative layer 22. Any intermediate layer may also be arranged between the core 21 and the decorative layer 22.

The wear resistant foil 10, 10′ produced according to the method described above with reference to FIG. 1 or FIG. 2, is arranged on the decorative layer. The core 21, the decorative layer 22, and the wear resistant foil 10, 10′ are pressed together to form a building panel 20. Heat may also be applied when applying pressure. The core, the decorative layer and the wear resistant foil may be pressed together in a continuous or static press, or in a calendering operation. As alternatively, the wear resistant foil 10, 10′, optionally comprising the decorative layer 22, may be adhered to the core 21 by an adhesive, such as hot melt.

The wear resistant foil 10, 10′ is preferably transparent, or substantially transparent, for example, having a light transmittance index exceeding 80%, preferably exceeding 90%.

A coating (not shown) may be applied on the wear resistant foil 10, 10′. The coating may comprise acrylate or methacrylate monomer or acrylate or methacrylate oligomer. The coating may be radiation curing, such as UV curing or electron beam curing.

As an alternative to a separate decorative layer 22, a print may be printed directly on the top surface of core 21. The wear resistant foil 10, 10′ is thereby arranged directly on the core 21.

In one embodiment, when the wear resistant foil 10 is produced according to the embodiment described with reference to FIG. 1, the first foil 1 forms a decorative layer. A separate decorative layer 22 may then be excluded. The first foil 1 may be printed, for example by digital printing, direct printing, rotogravure, etc. Preferably, the print is provided on side of the first foil 1 adapted to face the core 21. The wear resistant foil 10 is in this embodiment arranged directly on the core 21 of the above described type.

An embodiment of the building panel 20 comprises a core 21 comprising PVC, a decorative foil 22 comprising PVC, a wear resistant foil 10 comprising PVC in the first foil 1 and PU applied as the second thermoplastic material 5.

In other embodiments, the core 21 may be a wood-based board or a mineral board. The core may, for example, be a HDF, MDF, particleboard, plywood, OSB, etc.

As an alternative to the decorative foil, the decorative layer 22 may be formed of a thermoplastic material applied as a powder on the core. A print may be printed in the powder thermoplastic material. The thermoplastic material in powder form may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The wear resistant foil 10, 10′ is arranged on the powder layer and pressed together. The core 21 may be of the above described type.

Another alternative to the decorative foil is to apply a thermosetting binder, preferably an amino resin and in powder form, and lignocellulosic or cellulosic particles for forming the decorative layer 22 on the core 21. A print is may be printed in the powder layer, or pigments may be included. The core may be of the above described type. The wear resistant foil 10, 10′ is arranged on the powder layer and pressed together under heat, such that the thermosetting binder of the decorative layer is cured.

Another alternatives for forming the decorative layer 22 are providing a veneer layer, such as a wood veneer layer or a cork veneer layer or a paper layer for forming the decorative layer.

The different layers, i.e., the core 21, the decorative layer 22, the wear resistant foil 10, 10′, may be provided as continuous layers or being cut into sheets for the embodiment described with reference to FIG. 3.

FIG. 4 shows a method to produce a building panel 20 including forming a wear resistant foil 10 integrated into the production of the building panel 20. The building panel 20 may be a floor panel, a wall panel, a ceiling panel, a furniture component, etc.

A core 21 is provided. The core 21 may comprise a third thermoplastic material. The third thermoplastic material may be the same as the first and/or second material, or be different from the first and/or the second material.

The third thermoplastic material may comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The core 21 may be formed of several layers. The core may be foamed.

In one embodiment, the core 21 comprises the third thermoplastic material and fillers. The fillers may comprise calcium carbonate, such as chalk and/or limestone, or sand. In one embodiment, the core 21 is a Wood Plastic Composite (WPC), comprising the third thermoplastic material and wood particles as fillers.

The core 21 may be provided with a decorative layer 22 arranged on a top surface of the core 21. The wear resistant foil 10 is then arranged on the decorative surface 22. The decorative layer 22 may be a decorative foil comprising a thermoplastic material. The thermoplastic material of the decorative layer may be or comprise polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The decorative layer 22 is preferably printed, for example by direct printing, rotogravure, or digital printing.

The core 21 may also be provided with a balancing layer (not shown) arranged on a lower surface of the core 21, opposite the decorative layer 22. Any intermediate layer or layers may be arranged between the core 21 and the decorative layer 22.

A first foil 1 is arranged on the core 12. The first foil 1 comprises a first thermoplastic material. The first thermoplastic material may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

A first foil 1 is provided, preferably as a continuous web. The first foil 1 may also be cut into sheets. The first foil 1 may also be formed by an extrusion process in connection with producing the building panel. The first foil 1 may also be formed of a powder layer comprising the first thermoplastic material in powder form.

Preferably, the first foil 1 is formed of the thermoplastic material. The first foil may substantially consist of the thermoplastic material, and optionally additives. Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

In one embodiment, the first foil 1 is a PVC foil.

The first foil 1 may have a thickness of 0.1-1 mm.

As shown in FIG. 4, an applying device 3 applies, preferably scatters, a second thermoplastic material 5 in powder form and wear resistant particles 4 on the first foil 1. In FIG. 1, the second thermoplastic material 5 and the wear resistant particles 4 are applied as a mix. The thermoplastic material 5 and the wear resistant particles 4 may also be applied separately. Preferably, if applied separately, the wear resistant particles 4 are applied first and the second thermoplastic material 5 is applied on the wear resistant particles 4.

The second thermoplastic material 5 may be the same as in the first foil 1, or being different from the thermoplastic material of the first foil 1. The second thermoplastic may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.

In the embodiment shown in FIG. 4, the second material 5 is applied as a powder. By powder is also meant powder that has formed granules of the thermoplastic material 5, dry blends of the thermoplastic material 5, or agglomerates of the thermoplastic material 5. The granules may comprise both the thermoplastic material 5 and the wear resistant particles 4. The agglomerates may comprise both the thermoplastic material 5 and the wear resistant particles 4.

In the embodiment shown in FIG. 4, the wear resistant particles 4 and the second thermoplastic material is applied as a mix.

In the embodiment shown in FIG. 4, the second thermoplastic material 5 is applied in powder form. In embodiments, the second thermoplastic material 5 may be applied in molten form, which is described in more detail with reference to FIG. 6B. The wear resistant particles 4 may be mixed with the second thermoplastic material 5 in molten form or applied separately. The second thermoplastic 5 in molten form may be applied in an extrusion process such as extrusion lamination and extrusion coating on the first foil 1.

The wear resistant particles 4 preferably have an average particle size within the range of 10-200 μm, preferably within the range of 50-120 μm, such as 50-100 μm. The wear resistant particles 4 may have an average particle size of less than 50 μm, preferably less than 45 μm. The wear resistant particles 4 may have a spherical shape or an irregular shape. The wear resistant particles 4 may be surface treated. The wear resistant particles 4 may be silane-treated particles.

The wear resistant particles may be applied in an amount of 20-100 g/m2, preferably in an amount of 40-60 g/m2.

The wear resistant particles may have an average particle size being less than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing. However, the wear resistant particles may have an average particle size being larger than the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing. During pressing, the wear resistant particles are pressed into the first foil such that the wear resistant particles do not protrude beyond an upper surface of the layer, although the wear resistant particles having an average particle size exceeding the thickness of the layer formed by the wear resistant particles and the second thermoplastic material after pressing.

Scratch resistant particles (not shown) may also be applied on the first foil 1. By scratch resistant particles are meant particles improving the scratch or scratch resistant properties of the first foil 1. The scratch resistant particles may be applied together with the wear resistant particles, for example as a mix, or may be applied separately. Preferably, the scratch particles are arranged on an upper part of the layer formed by the thermoplastic material 5 and the wear resistant particles 4. The scratch resistant particles may be may be or comprise nano-sized silica particles, preferably fused silica particles. The scratch resistant particles may be or comprise aluminum oxide.

Additives may also be applied on the first foil 1, preferably together with the second thermoplastic material 5. Additives may be plasticizers, stabilizers, lubricants, degassing agents, coupling agents, compatibilizers, crosslinking agents, etc.

In one embodiment, the first foil 1 is a PVC foil and the second thermoplastic material 5 is PU. In one embodiment, the first foil 1 is a PVC foil and the second thermoplastic material 5 is PVC.

The different layers, i.e., the core 21, the decorative layer 22, the first foil 1, may be provided as continuous layers or being cut into sheets.

The core 21, the first foil 1 and the second thermoplastic material 5 in powder form with the wear resistant particles 4 are thereafter adhered to each other, for example, pressed together, to form a building panel 20. The first foil 1 and the second thermoplastic material 5 with the wear resistant particles 4 form a wear resistant foil 10 of the building panel 20.

The wear resistant foil 10 is preferably transparent, or substantially transparent, for example, having a light transmittance index exceeding 80%, preferably exceeding 90%.

The core 21, the first foil 1 and the second thermoplastic material 5 are preferably pressed together in a pressing station 6. The press may be a continuous or static press. The first and second foil may be adhered together by pressure alone, by heat and pressure, by pressure and adhesive, or by heat, pressure, and adhesive. Preferably, both pressure and heat is applied in order to adhere the first and the second foil to each other. The pressing operation may for example be made as a hot-hot process, a hot-cold process, etc. Depending on the thermoplastic materials and process used, the pressure applied may be 5-100 bar, applied for example during 5-500 seconds. The temperature may be 80-300° C., such as 100-250° C., such as 150-200° C. The pressing may be made with an embossed press matrix or press roller, such that an embossed structure is formed in the wear resistant foil. As an alternative, the layers may be adhered to each other by an adhesive such as glue, for example, hot melt.

The second thermoplastic material 5 and the wear resistant particles 4 form a layer, which may have a thickness of 0.01-1 mm, preferably as measured in the final product, for example, after pressing or extruding. Preferably, the layer formed by the second thermoplastic material 5 and the wear resistant particles 4 has a thickness less than 0.5 mm, more preferably less than 75 μm such as about 50 μm, preferably as measured in the final product, for example, after pressing or extruding.

After adhering, the wear resistant particles are enclosed by the first foil and the second thermoplastic material. Although the wear resistant particles and the second thermoplastic material may be applied as mix, during the pressing, the second thermoplastic material fuses and encloses the wear resistant particles. Preferably, the wear resistant particles do not protrude beyond the surface of the layer formed the second thermoplastic material facing away from the first foil. Thereby, a wear resistant foil having a smooth surface can be formed.

A coating (not shown) may be applied on the wear resistant foil 10. The coating may comprise acrylate or methacrylate monomer or acrylate or methacrylate oligomer. The coating may be radiation curing, such as UV curing or electron beam curing.

As an alternative to a separate decorative layer 22, a print may be printed directly on the top surface of core 21. The first foil 1 is thereby arranged directly on the core 21.

As an alternative to a separate decorative layer 22, the first foil 1 may be a decorative foil. The first foil 1 may be printed, for example by digital printing, direct printing, rotogravure, etc. Preferably, the print is provided on a side of the first foil 1 adapted to face the core 21. The first foil 1 is thereby arranged directly on the core 21.

As an alternative to the decorative foil described above, the decorative layer 22 may be formed of a thermoplastic material applied as a powder on the core. A print may be printed in the powder thermoplastic material. The thermoplastic material in powder form may be polyvinyl chloride (PVC), polyester, polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof. The first foil 1 is arranged on the powder layer and pressed together, as described above. The core 21 may be of the above described type.

Another alternative to the decorative foil described above is to apply a thermosetting binder, preferably an amino resin and in powder form, and lignocellulosic or cellulosic particles for forming the decorative layer 22 on the core 21. A print is may be printed in the powder layer, or pigments may be included. The core may be of the above described type. The first foil 1 is arranged on the powder layer are pressed together under heat as described above, such that the thermosetting binder of the decorative layer is cured.

Another alternatives for forming the decorative layer 22 are providing a wood veneer layer, a cork layer, or a paper layer for forming the decorative layer.

In one embodiment, the first foil 1 may be a decorative foil. The first foil 1 may be provided with a print, for example by digital printing, direct printing or rotogravure.

In one embodiment, both the decorative layer 22 and the first foil 1 are excluded. The second thermoplastic material 5 in powder form and the wear resistant particles 4 are applied directly on the core. The second thermoplastic material 5 is of the above described type. The core 21 is of the above described type. An upper surface of the core 21 may be provided with a print, preferably a digital print. The wear resistant particles 4 of the above described type may be applied together with the second thermoplastic material 5 as a mix or separately. Scratch resistant particles of the above described type may also be applied.

The second thermoplastic material 5 is fused, preferably by applying heat and pressure, into a wear resistant foil 10′ comprising the wear resistant particles 4 arranged on the core 12 in a pressing operation as described above.

It is contemplated that the core 21 may be excluded in the embodiments described with reference to FIG. 4. By adhering, for example, pressing, the decorative layer 22 and the second thermoplastic material 5 of the above described type with the wear resistant particles 4, a decorative substrate having wear resistant properties is provided.

In addition to the building panel 20 described above with reference to FIG. 3, building panels 20 having another structure may also be provided by the methods described above.

According to one embodiment, which is shown in FIG. 5A, a building panel 20 comprising a core 21 of the above described type and a wear resistant foil 10′ manufactured according to the embodiment described with reference to FIG. 2. An upper surface of the core 21 may be provided with a print 23, for example printed by for example by digital printing, direct printing or rotogravure. The wear resistant foil 10′ is arranged directly on the core 21. The wear resistant foil 10′ is formed of the second thermoplastic material 5 of the above described type applied in powder form and the wear resistant particles 4 of the above described type. The wear resistant particles 4 are preferably substantially homogenously distributed in the wear resistant foil 10′.

According to one embodiment, which is shown in FIG. 5B, a building panel 20 comprising a core 21 of the above described type and a wear resistant foil 10 manufactured according to the embodiment described with reference to FIG. 1. Alternatively, the building panel 20 is manufactured according to the embodiment described with reference to FIG. 4 wherein the decorative layer 20 is excluded. The wear resistant foil 10 is arranged directly on the core 12. The wear resistant foil 10 comprises the first foil 1 of the above described type and the second thermoplastic material 5 of the above described type applied with the wear resistant particles 4 of the above described type. The first foil 1 may be a decorative foil. The first foil 1 may be provided with a print 23, for example printed by digital printing, direct printing or rotogravure. Alternatively, or as a complement, an upper surface of the core 21 is provided with a print 23. The wear resistant foil 10 is arranged directly on the core 21. The wear resistant foil 10 may be produced integrated with the method of producing the building panel, as described with reference to FIG. 4, or as a separate process as described with reference to FIG. 1.

According to one embodiment, the building panel 20 comprises a core 21 of the above described type and a wear resistant foil 10′ formed of the second thermoplastic material 5 of the above described type and the wear resistant particles 4 the above described type applied directly on an upper surface of the core 21. The upper surface of the core 21 may be provided with a print 23, for example printed by for example by digital printing, direct printing or rotogravure.

Any of the above described building panels may be provided with a mechanical locking system. The mechanical locking system may be of the type described in WO 2007/015669, WO 2008/004960, WO 2009/116926, or WO 2010/087752, the entire contents of each is expressly incorporated by reference herein.

In all embodiments, the second thermoplastic material of the above type may be applied in an extrusion process, which is shown in FIGS. 6A-B. In FIG. 6A, a first foil 1 is provided. The first foil 1 is of the type described above with reference to FIGS. 1, 3, 5, 5A-B. In the embodiment shown FIG. 6A, the second thermoplastic material 5 of the above described type is mixed with the wear resistant particles 4 of the above described type. The second thermoplastic material 5 is preferably provided as granulates. The second thermoplastic material 5 in molten form is applied on the first foil 1 comprising the first thermoplastic material by an extruder 8. For example, the second thermoplastic material 5 is applied on the first foil 1 by an extrusion process such as extrusion lamination or extrusion coating.

As an alternative to mix the second thermoplastic material 5 with the wear resistant particles 4, the wear resistant particles 4 may be applied separately form the second thermoplastic material 5 (not shown). The wear resistant particles 4 may be applied on the first foil 1 prior to applying the second thermoplastic material 5 by the extrusion process such as extrusion lamination or extrusions coating on the first foil 1.

The method to produce a wear resistant foil 10 by using an extrusion technique as described above with reference to FIG. 6A is also applicable when forming a building panel corresponding to the embodiment shown in FIG. 4, which is shown in FIG. 6B.

In FIG. 6B, a first foil 1 and a core 21 are provided. The first foil 1 and the core 21 are of the type described above with reference to FIGS. 3, 4, and 5A-B. In the embodiment shown FIG. 6B, the second thermoplastic material 5 of the above described type is mixed with the wear resistant particles 4 of the above described type. The second thermoplastic material 5 is preferably provided as granulates. The second thermoplastic material 5 in molten form is applied on the first foil 1 comprising the first thermoplastic material by an extruder 8. For example, the second thermoplastic material 5 is applied on the first foil 1 by an extrusion process such as extrusion lamination or extrusion coating.

The core 21, the first foil 1 provided with the wear resistant particles 4 and the second thermoplastic material 5 are adhered together for forming a building panel 20, for example, by pressing such as calendaring as shown in FIG. 6B. Alternatively, the layers may be adhered to each other by means of an adhesive, such as hot melt.

It is also contemplated that the co-extruding may be used to form the wear resistant foil. The first foil comprising the first thermoplastic material and a second foil comprising the second thermoplastic material may be formed by co-extruding the first and the second foil. The wear resistant particles may be mixed with the second thermoplastic material, or applied separately on the first and/or the second foil.

It is contemplated that there are numerous modifications of the embodiments described herein, which are still within the scope of the disclosure. For example, it is contemplated that more than one wear resistant foil may be arranged on a core for forming a building panel.

For example, it is contemplated that after pressing, the boundaries between the first foil 1 and the layer formed of the second thermoplastic material 5 in powder and the wear resistant particles 4 may be less distinct.

EXAMPLES
Example 1: Comparative Example

A PVC wear layer foil with a thickness of 0.3 mm was positioned on a decorative foil with a thickness of 0.1 mm. The two foils were laminated on to a PVC core material using a temperature of 160° C., a pressure of 20 bars and a pressing time of 40 seconds. The resulting product was a LVT product. The LVT product was found to have a wear resistance of 3200 revolutions as tested in a Taber abrader.

Example 2: PVC Powder Composition on Foil

A PVC wear layer foil with a thickness of 0.3 mm was positioned on a decorative foil with a thickness of 0.1 mm. 150 g/m2 of a powder composition comprising 90 wt-% PVC and 10 wt-% Al₂O₃was scattered on the wear layer foil. The PVC powder composition and the two foils were laminated on to a PVC core material using a temperature of 160° C., a pressure of 20 bars and a pressing time of 40 seconds. The resulting product was a LVT product. The LVT product was found to have a wear resistance higher than 8000 revolutions as tested in a Taber abrader.

Example 3: PU Powder Composition on Foil

A PVC wear layer foil with a thickness of 0.3 mm was positioned on a decorative foil with a thickness of 0.1 mm. 150 g/m2 of a powder composition comprising 90 wt-% PU powder and 10 wt-% Al₂O₃was scattered on the wear layer foil. The PU powder composition and the two foils were laminated on to a PVC core material using a temperature of 160° C., a pressure of 20 bars and a pressing time of 40 seconds. The resulting product was a LVT product. The LVT product was found to have a wear resistance higher than 8000 revolutions as tested in a Taber abrader.

Example 4: PU Foil on PVC Foil

A printed decorative PVC foil having a thickness of 0.08 mm was arranged on a core comprising three layers and having a thickness of 4 mm. A PVC wear layer having a thickness of 0.25 mm was arranged on the decorative PVC foil. Wear resistant particles in form of aluminum oxide were applied in an amount of 40 g/m2 on the PVC wear layer. A PU foil having a thickness of 0.05 mm was arranged on the wear resistant particles and the PVC wear layer. The different layers were pressed together in a cold-hot-cold process. The pressure applied was 10 bar. The temperatures applied in the cold-hot-cold process were 50° C., 140° C., and 50° C. The product was pressed at 140° C. during 4 minutes. The total pressing time was approximately 55 minutes. The resulting product was a LVT product. The LVT product was found to have a wear resistance higher than 8000 revolutions as tested in a Taber abrader.

Claims

1. A method to produce a wear resistant foil, comprising: providing a first foil comprising a first thermoplastic material,applying wear resistant particles and a second thermoplastic material on the first foil, the second thermoplastic material being applied in powder form; andadhering the first foil to the second thermoplastic material and the wear resistant particles and adhering the wear resistant particles to the second thermoplastic material to form the wear resistant foil,wherein the adhering of first foil to the second thermoplastic material and the wear resistant particles and the adhering of the wear resistant particles to the second thermoplastic material are by pressing, andwherein the wear resistant particles are enclosed by the first and second thermoplastic material and do not protrude from a surface of the second thermoplastic material after being adhered to the first foil.
2. The method according to claim 1, wherein the wear resistant particles are enclosed by the first foil and the second thermoplastic material after the first foil is adhered to the second thermoplastic material and the wear resistant particles.
3. The method according to claim 1, wherein the wear resistant particles and the second thermoplastic material are applied as a mix.
4. The method according to claim 1, wherein the first thermoplastic material comprises polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylates, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.
5. The method according to claim 1, wherein the second thermoplastic material comprises polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylates, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.
6. The method according to claim 1, wherein the wear resistant particles comprise aluminium oxide.
7. The method according to claim 1, wherein the wear resistant foil is substantially transparent.
8. The method according to claim 1, wherein the adhering of the first foil to the second thermoplastic material and the wear resistant particles and the adhering of the wear resistant particles to the second thermoplastic material is by pressing without an adhesive.
9. The method according to claim 1, wherein the first thermoplastic material is polyvinyl chloride and the second thermoplastic material is polyurethane.
10. A method to produce a building panel, comprising: providing a core,applying a first foil comprising a first thermoplastic material on the core,applying wear resistant particles and a second thermoplastic material on the first foil, the second thermoplastic material being applied in powder form, andadhering the core, the first foil, the second thermoplastic material and the wear resistant particles collectively to one another to form a building panel by pressing the core, the first foil, the wear resistant particles, and the second thermoplastic material together,wherein the wear resistant particles are enclosed by the first and second thermoplastic material and do not protrude from a surface of the second thermoplastic material after being adhered to the first foil.
11. The method according to claim 10, wherein the wear resistant particles are enclosed by the first foil and the second thermoplastic material after the first foil is adhered to the second thermoplastic material and the wear resistant particles.
12. The method according to claim 10, wherein the wear resistant particles and the second thermoplastic material are applied as a mix.
13. The method according to claim 10, wherein the first thermoplastic material comprises polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.
14. The method according to claim 10, wherein the second thermoplastic material comprises polyvinyl chloride (PVC), polyester (PE), polypropylene (PP), polyethylene (PE), polystyrene (PS), polyurethane (PU), polyethylene terephthalate (PET), polyacrylate, methacrylate, polycarbonate, polyvinyl butyral, polybutylene terephthalate, or a combination thereof.
15. The method according to claim 10, wherein the wear resistant particles comprise aluminium oxide.
16. The method according to claim 10, further comprising arranging a decorative layer on the core.
17. The method according to claim 10, wherein the collective adhering of the core, the first foil, the wear resistant particles, and the second thermoplastic material is by pressing without an adhesive.
18. A method to produce a wear resistant foil, comprising providing a carrier,applying wear resistant particles and a second thermoplastic material on the carrier, the second thermoplastic material being applied in powder form,adhering the wear resistant particles and the second thermoplastic material to each other to form the wear resistant foil by pressing, andreleasing the wear resistant foil from the carrier,wherein the wear resistant particles are enclosed by the second thermoplastic material and do not protrude from a surface of the second thermoplastic material.
19. A method to produce a wear resistant foil, comprising providing a first foil comprising a first thermoplastic material,applying wear resistant particles and a second thermoplastic material on the first foil, andadhering the first foil to the second thermoplastic material and the wear resistant particles and adhering the wear resistant particles to the second thermoplastic material to form the wear resistant foil,wherein the second thermoplastic material is applied in molten form,wherein the wear resistant particles are enclosed by the first and second thermoplastic material and do not protrude from a surface of the second thermoplastic material after being adhered to the first foil.

Priority Claims (3)

Number	Date	Country	Kind
1450894-9	Jul 2014	SE	national
1450895-6	Jul 2014	SE	national
1550455-8	Apr 2015	SE	national

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. application Ser. No. 14/790,850, filed on Jul. 2, 2015, which claims the benefit of Swedish Application No. 1550455-8, filed on Apr. 16, 2015, Swedish Application No. 1450895-6, filed on Jul. 16, 2014, and Swedish Application No. 1450894-9, filed on Jul. 16, 2014. The entire contents of each of U.S. application Ser. No. 14/790,850, Swedish Application No. 1550455-8, Swedish Application No. 1450895-6, and Swedish Application No. 1450894-9 are hereby incorporated herein by reference in their entirety.

US Referenced Citations (219)

Number	Name	Date	Kind
2861372	Hunt	Nov 1958	A
3135643	Michl	Jun 1964	A
3286006	Annand	Nov 1966	A
3308013	Bryant	Mar 1967	A
3887678	Lewicki, Jr.	Jun 1975	A
4092198	Scher	May 1978	A
4093766	Scher	Jun 1978	A
4255480	Scher	Mar 1981	A
4256793	Cannady, Jr. et al.	Mar 1981	A
4376147	Byrne et al.	Mar 1983	A
4430375	Scher	Feb 1984	A
4450194	Kauffman et al.	May 1984	A
4615090	Baus	Oct 1986	A
4756856	Choinski	Jul 1988	A
4916007	Manning	Apr 1990	A
5112671	Diamond	May 1992	A
5188876	Hensel et al.	Feb 1993	A
5266384	O'Dell	Nov 1993	A
5466511	O'Dell et al.	Nov 1995	A
5543193	Tesch	Aug 1996	A
5547741	Wilson	Aug 1996	A
5604025	Tesch	Feb 1997	A
5662977	Spain	Sep 1997	A
5670237	Shultz et al.	Sep 1997	A
5766522	Daly et al.	Jun 1998	A
5787655	Saylor, Jr.	Aug 1998	A
5855832	Clausi	Jan 1999	A
6013222	Douglas et al.	Jan 2000	A
6103377	Clausi	Aug 2000	A
6218001	Chen	Apr 2001	B1
6423167	Palmer et al.	Jul 2002	B1
6444075	Schneider et al.	Sep 2002	B1
6468645	Clausi	Oct 2002	B1
6579610	Shortland	Jun 2003	B1
6617009	Chen et al.	Sep 2003	B1
6666951	Kostiw	Dec 2003	B1
6675545	Chen et al.	Jan 2004	B2
6761008	Chen et al.	Jul 2004	B2
6803110	Drees et al.	Oct 2004	B2
6926954	Schuren et al.	Aug 2005	B2
6986934	Chen et al.	Jan 2006	B2
7169460	Chen et al.	Jan 2007	B1
7211310	Chen et al.	May 2007	B2
7276265	Sigel et al.	Oct 2007	B2
7419717	Chen et al.	Sep 2008	B2
7568322	Pervan et al.	Aug 2009	B2
7576140	Tamaki et al.	Aug 2009	B2
7584583	Bergelin et al.	Sep 2009	B2
7763345	Chen et al.	Jul 2010	B2
7802415	Pervan	Sep 2010	B2
7816000	Sparks et al.	Oct 2010	B2
7886497	Pervan et al.	Feb 2011	B2
7930862	Bergelin et al.	Apr 2011	B2
8021741	Chen et al.	Sep 2011	B2
8028486	Pervan	Oct 2011	B2
8043661	Linnemann	Oct 2011	B2
8112891	Pervan	Feb 2012	B2
8245478	Bergelin et al.	Aug 2012	B2
8293058	Pervan et al.	Oct 2012	B2
8365499	Nilsson et al.	Feb 2013	B2
8480841	Pervan et al.	Jul 2013	B2
8511031	Bergelin et al.	Aug 2013	B2
8584423	Pervan et al.	Nov 2013	B2
8613826	Pervan et al.	Dec 2013	B2
8658274	Chen et al.	Feb 2014	B2
8756899	Nilsson et al.	Jun 2014	B2
8800150	Pervan	Aug 2014	B2
8833028	Whispell et al.	Sep 2014	B2
8834992	Chen et al.	Sep 2014	B2
8973270	Siebert et al.	Mar 2015	B2
9194133	Thiers	Nov 2015	B2
9200460	Cappelle	Dec 2015	B2
9222267	Bergelin et al.	Dec 2015	B2
9249581	Nilsson et al.	Feb 2016	B2
9296191	Pervan et al.	Mar 2016	B2
9314936	Pervan	Apr 2016	B2
9410328	Pervan	Aug 2016	B2
9670371	Pervan et al.	Jun 2017	B2
9695601	Whispell et al.	Jul 2017	B2
9714515	Pervan	Jul 2017	B2
9765530	Bergelin et al.	Sep 2017	B2
10047527	Nilsson et al.	Aug 2018	B2
10059084	Lundblad et al.	Aug 2018	B2
10137659	Pervan	Nov 2018	B2
10287777	Boo et al.	May 2019	B2
10301830	Boo	May 2019	B2
10316526	Kell	Jun 2019	B2
10344379	Pervan et al.	Jul 2019	B2
10407919	Boo	Sep 2019	B2
10450760	Bergelin et al.	Oct 2019	B2
10486399	Chen et al.	Nov 2019	B2
10493731	Lundblad	Dec 2019	B2
10526793	Nilsson et al.	Jan 2020	B2
10704269	Whispell et al.	Jul 2020	B2
10780676	Lundblad et al.	Sep 2020	B2
10808410	Boo et al.	Oct 2020	B2
10837181	Josefsson et al.	Nov 2020	B2
10844612	Boo	Nov 2020	B2
10851549	Boo	Dec 2020	B2
10865571	Kell	Dec 2020	B2
20010021431	Chen	Sep 2001	A1
20020031646	Chen	Mar 2002	A1
20020142135	Chen et al.	Oct 2002	A1
20020146568	Ho et al.	Oct 2002	A1
20030024199	Pervan	Feb 2003	A1
20030055145	Safta et al.	Mar 2003	A1
20030059639	Worsley	Mar 2003	A1
20030072919	Watts, Jr. et al.	Apr 2003	A1
20040048044	Schneider	Mar 2004	A1
20040206036	Pervan	Oct 2004	A1
20040241416	Tian	Dec 2004	A1
20050003160	Chen et al.	Jan 2005	A1
20050107006	Makino	May 2005	A1
20050021081	Pervan	Sep 2005	A1
20060130421	Nollet et al.	Jun 2006	A1
20060191861	Mitterhofer	Aug 2006	A1
20070175148	Bergelin et al.	Aug 2007	A1
20070196624	Chen et al.	Aug 2007	A1
20080000183	Bergelin et al.	Jan 2008	A1
20080000188	Pervan	Jan 2008	A1
20080010924	Pietruczynik	Jan 2008	A1
20080032120	Braun	Feb 2008	A1
20080063844	Chen et al.	Mar 2008	A1
20080075882	Hayata	Mar 2008	A1
20080172971	Pervan	Jul 2008	A1
20080256890	Pervan	Oct 2008	A1
20080311355	Chen et al.	Dec 2008	A1
20090078129	Cappelle	Mar 2009	A1
20090120731	Thompson et al.	May 2009	A1
20090151866	Endert	Jun 2009	A1
20090155612	Pervan	Jun 2009	A1
20090208646	Kreuder et al.	Aug 2009	A1
20100092731	Pervan et al.	Apr 2010	A1
20100152361	Weaver et al.	Jun 2010	A1
20100166967	Chisaka	Jul 2010	A1
20100223881	Kalwa	Sep 2010	A1
20100260962	Chen et al.	Oct 2010	A1
20100300030	Pervan	Dec 2010	A1
20100319282	Ruland	Dec 2010	A1
20100323187	Kalwa	Dec 2010	A1
20110041996	Pervan	Feb 2011	A1
20110056167	Nilsson et al.	Mar 2011	A1
20110104431	Niedermaier	May 2011	A1
20110131901	Pervan et al.	Jun 2011	A1
20110154763	Bergelin et al.	Jun 2011	A1
20110167744	Whispell et al.	Jul 2011	A1
20110177354	Ziegler et al.	Jul 2011	A1
20110223342	Iyer et al.	Sep 2011	A1
20110247748	Pervan et al.	Oct 2011	A1
20110287237	Riebel	Nov 2011	A1
20110300393	Iio et al.	Dec 2011	A1
20110318507	Meersseman	Dec 2011	A1
20120003439	Chen et al.	Jan 2012	A1
20120040149	Chen et al.	Feb 2012	A1
20120137617	Pervan	Jun 2012	A1
20120216947	Huber	Aug 2012	A1
20120279154	Bergelin et al.	Nov 2012	A1
20130014890	Pervan et al.	Jan 2013	A1
20130014891	Vandevoorde	Jan 2013	A1
20130047536	Pervan	Feb 2013	A1
20130052437	Barth	Feb 2013	A1
20130095343	Arsene	Apr 2013	A1
20130111758	Nilsson et al.	May 2013	A1
20130269863	Pervan et al.	Oct 2013	A1
20130298487	Bergelin et al.	Nov 2013	A1
20130299454	Marxen et al.	Nov 2013	A1
20140017452	Pervan et al.	Jan 2014	A1
20140023832	Pervan	Jan 2014	A1
20140033635	Pervan et al.	Feb 2014	A1
20140115994	Pervan	May 2014	A1
20140141239	Ilfrey	May 2014	A1
20140144583	Hakansson et al.	May 2014	A1
20140147585	Smith	May 2014	A1
20140196618	Pervan	Jul 2014	A1
20140220318	Pervan	Aug 2014	A1
20140237924	Nilsson et al.	Aug 2014	A1
20140283466	Boo	Sep 2014	A1
20140290171	Vermeulen	Oct 2014	A1
20140318061	Pervan	Oct 2014	A1
20140352248	Whispell	Dec 2014	A1
20140356594	Chen et al.	Dec 2014	A1
20150056416	Maesen	Feb 2015	A1
20150072111	Rischer et al.	Mar 2015	A1
20150158330	Stoffel	Jun 2015	A1
20150225964	Chen et al.	Aug 2015	A1
20150251486	Hannig	Sep 2015	A1
20150258716	Hannig	Sep 2015	A1
20160016390	Lundblad et al.	Jan 2016	A1
20160016391	Lundblad et al.	Jan 2016	A1
20160052245	Chen et al.	Feb 2016	A1
20160069089	Bergelin et al.	Mar 2016	A1
20160082625	Luukko et al.	Mar 2016	A1
20160108624	Nilsson et al.	Apr 2016	A1
20160144433	Stoffel	May 2016	A1
20160186318	Pervan et al.	Jun 2016	A1
20160194883	Pervan	Jul 2016	A1
20160194885	Whispell et al.	Jul 2016	A1
20160201324	Håkansson et al.	Jul 2016	A1
20160265234	Pervan	Sep 2016	A1
20170037642	Boo	Feb 2017	A1
20170037645	Pervan	Feb 2017	A1
20170175400	Joseffson et al.	Jun 2017	A1
20170232761	Pervan	Aug 2017	A1
20170241136	Kell	Aug 2017	A1
20170348984	Pervan	Dec 2017	A1
20170350140	Bergelin et al.	Dec 2017	A1
20180094441	Boo	Apr 2018	A1
20180313093	Nilsson et al.	Nov 2018	A1
20180339504	Ziegler	Nov 2018	A1
20190091977	Lundblad et al.	Mar 2019	A1
20190211569	Boo et al.	Jul 2019	A1
20190249444	Kell	Aug 2019	A1
20190277041	Pervan	Sep 2019	A1
20200056379	Boo	Feb 2020	A1
20200063441	Boo	Feb 2020	A1
20200208409	Kell	Jul 2020	A1
20200248462	Bergelin et al.	Aug 2020	A1
20200362567	Nilsson et al.	Nov 2020	A1
20200407981	Boo et al.	Dec 2020	A1

Foreign Referenced Citations (55)

Number	Date	Country
2 406 991	Nov 2001	CA
104177817	Dec 2014	CN
1 815 312	Jul 1969	DE
103 16 886	Oct 2004	DE
10 2007 046 532	Oct 2008	DE
0 732 449	Sep 1996	EP
0 865 351	Sep 1998	EP
0 732 449	Aug 1999	EP
1 209 199	May 2002	EP
0 865 351	Feb 2003	EP
1 847 385	Oct 2007	EP
1 961 556	Aug 2008	EP
2 123 476	Nov 2009	EP
2 246 500	Nov 2010	EP
2 263 867	Dec 2010	EP
2 264 259	Dec 2010	EP
2 272 667	Jan 2011	EP
2 272 668	Jan 2011	EP
2 305 462	Apr 2011	EP
1 847 385	Sep 2011	EP
2 263 867	Mar 2012	EP
2 789 501	Oct 2014	EP
984 170	Feb 1965	GB
1 090 450	Nov 1967	GB
2 262 940	Jul 1993	GB
2001-113664	Apr 2001	JP
2001-328210	Nov 2001	JP
225556	Feb 1992	NZ
WO 9006970	Jun 1990	WO
WO 9206832	Apr 1992	WO
WO 9400280	Jan 1994	WO
WO 0192037	Dec 2001	WO
WO 2006013469	Feb 2006	WO
WO 2007015669	Feb 2007	WO
WO 2007015669	Feb 2007	WO
WO 2008004960	Jan 2008	WO
WO 2008004960	Jan 2008	WO
WO 2008004960	Jan 2008	WO
WO 2009065769	May 2009	WO
WO 2009065769	May 2009	WO
WO 2009116926	Sep 2009	WO
WO 2009124704	Oct 2009	WO
WO 2010087752	Aug 2010	WO
WO 2011033956	Mar 2011	WO
WO 2011082491	Jul 2011	WO
WO 2011087422	Jul 2011	WO
WO 2011129755	Oct 2011	WO
WO 2011129757	Oct 2011	WO
WO-2011129755	Oct 2011	WO
WO 2011141849	Nov 2011	WO
WO 2011141849	Nov 2011	WO
WO 2013079950	Jun 2013	WO
WO-2013079950	Jun 2013	WO
WO 2016010471	Jan 2016	WO
WO 2016010472	Jan 2016	WO

Non-Patent Literature Citations (15)

Entry
U.S. Appl. No. 14/994,593, Niclas Håkansson, Göran Ziegler and Christer Lundblad, filed Jan. 13, 2016, (Cited herein as US Patent Application Publication No. 2016/0201324 A1 of Jul. 14, 2016).
U.S. Appl. No. 16/113,333, Christer Lundbland, Niclas Håkansson and Göran Ziegler, filed Aug. 27, 2018, (Cited herein as US Patent Application Publication No. 2019/0091977 A1 of Mar. 28, 2019).
International Search Report issued in PCT/SE2015/050782, dated Oct. 20, 2015, ISA/SE Patent-och registreringsverket, Stockholm, SE, 6 pages.
Extended European Search Report issued in EP 15822018.6, dated Nov. 17, 2017, European Patent Office, Munich, DE, 8 pages.
International Search Report issued in PCT/SE2015/050783, dated Oct. 20, 2015, ISA/SE Patent-och registreringsverket, Stockholm, SE, 6 pages.
Extended European Search Report issued in EP 15822782.7, dated Nov. 17, 2017, European Patent Office, Munich, DE, 8 pages.
BTLSR Toledo, Inc. website. http://www.btlresins.com/more.html. “Advantages to Using Powdered Resins,” May 26, 2007, 2 pages, per the Internet Archive WayBackMachine.
Floor Daily, “Shaw Laminates: Green by Design,” Aug. 13, 2007, 1 pg, Dalton, GA.
Le Fur, X., et al., “Recycling melamine-impregnated paper waste as board adhesives,” published online Oct. 26, 2004, pp. 419-423, vol. 62, Springer-Verlag, DE.
Nimz, H.H., “Wood,” Ullmann's Encyclopedia of Industrial Chemistry, published online Jun. 15, 2000, pp. 453-505, vol. 39, Wiley-VCH Verlag GmbH & Co. KgaA, Weinheim, DE.
Odian, George, “Principles of Polymerization,” 1991, 3rd Edition, 5 pages incl. pp. 122-123, John Wiley & Sons, Inc., New York, NY, USA.
Parquet International, “Digital Printing is still an expensive process,” Mar. 2008, cover page/pp. 78-79, www.parkettmagazin.com.
Sichuan Jieyang Building Materials Co., Ltd., “PVC Flooring Planks With Good Quality,” China PVC Flooring; 2013 (retrieved Jun. 26, 2014), 3 pages, http://harjorflooring.en.made-in-china.com/product/vXFxYDICmks/China-PVC-Flooring-Planks-with-Good-Quality.html.
U.S. Appl. No. 16/992,215, filed Aug. 13, 2020, Lundblad, et al.
Lundblad, Christer, et al., U.S. Appl. No. 16/992,215 entitled “Method to Produce a Thermoplastic Wear Resistant Foil,” filed in the U.S. Patent and Trademark Office on Aug. 13, 2020.

Related Publications (1)

	Number	Date	Country
	20200180282 A1	Jun 2020	US

Continuations (1)

	Number	Date	Country
Parent	14790850	Jul 2015	US
Child	16697565		US

Method to produce a thermoplastic wear resistant foil

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

Field of Search

US

International Classifications

Disclaimer

Term Extension

Abstract

Description

Claims

Priority Claims (3)

CROSS REFERENCE TO RELATED APPLICATIONS

US Referenced Citations (219)

Foreign Referenced Citations (55)

Non-Patent Literature Citations (15)

Related Publications (1)

Continuations (1)