The use of split lignocellulosic materials is proposed in order to eliminate toxic heavy metals soluble in wastewaters from household or industrial origin. The proper management of this technology involves defining the solid/liquid ratio or pulp density, the pH value at a constant or variable level and the stirring conditions in the adsorption reactor for each kind of RIL (liquid industrial waste), i.e. according to its chemical composition, which will allow optimizing the process in short periods of operation.
The presence of heavy metals soluble in wastewaters uses to be toxic for the flora and fauna including man. A number of sea plants and animals show a clear trend to bioaccrue metals in its different organs. Due to this, we may note in the bibliography that several methodologies have been developed to eliminate said metals. Among said technologies, chemical or biologic precipitation should be noted, which uses bacteria to reduce anion sulphates. Although precipitation/settlement or filtration are the methodologies mostly used at industrial level, they lose efficacy when dealing with very dilute solutions (U.S. Pat. No. 6,630,071 (2003); U.S. Pat. No. 5,080,806 (1992). Precipitates thus formed may be separated by settlement, filtration or flotation upon flocculation/coagulation if applicable. Since the precipitates formed, such as hydrated oxides or salts, depend on the solubility thereof, the concentrations remaining in the solution after the end of the process do not ensure that all metals may reach the maximum concentrations permitted by the regulations in effect in the different countries. The methods described above incorporate various amounts of new chemical and/or biologic contaminants (microorganisms) to the treated waters. Other methods use activated carbon and ionic exchange resins as adsorbing agents, which are frequently used at lab, pilot plant and industrial level scale, especially in this last case, when waters are to be softened (U.S. Pat. No. 6,878,286 (2005)). Due to its cost, however, regeneration is a necessary process and this increases the cost of the treatment process. A number of artificial chemical products deriving from hidroxyapatites (Bailliez, Doctoral Dissertation 03 ISAL 0007 (2003). Lyon, France) and natural products as bentonites, vermiculite and lignocellulosic materials has been studied to eliminate heavy metals from waters. The latter should be noted since their adsorbing capacity has been proved but under experimental conditions, which are not the most suitable to apply them at industrial level (Gaballah et Kibertus, J. of Geochem. Explor. 62 (1998)241-286). In the present invention this type of vegetal substrate is revalued to be used at lab scale and also at industrial level.
The adsorption processes are one of the few alternatives available in the market to eliminate metallic contaminants present in wastewaters, which concentrations may vary between μg/L and some tenths or hundredths of mg/L (Dubey et Gupta. Separation and Purification Technology. 41(1), 2005, 21-28). A number of investigations have been developed using low-cost natural adsorbing agents (Bailey. et al, Wat.Res. 33(11), 1999, 2469-2479) as tree bark, lignin, tannins, chitin, modified cotton, clays and zeolites among others. Tannins in particular are polyphenols, which are functionally similar to lignin that have been used as adsorbing agents of heavy metals. They are first reacted with aldehydes, such as formalin, and then precipitated with ammonia. Then, they are redissolved in the waters contaminated with heavy metals, which are precipitated again acting as adsorbing agents of heavy metals present in the contaminated water (U.S. Pat. No. 5,158,711; U.S. Pat. No. 5,460,791; U.S. Pat. No. 6,264,840).
Lignocellulosic materials are wide-ranging as to their origin, with the following having to be noted: wastes from the grain agricultural industry (walnuts, almonds, coffee, etc.) and tree bark, such as fir tree, acacia, pine and others, which behaviour has been studied by different researchers (Gaballah et al, WO 9215397; Palma et al, Wat. Res. 37(2003)4974-4980).
Lignocellulosic materials, as tree bark, have been recognized for decades as a material to adsorb heavy metals. The use and behavior of said materials for contaminated waters, however—both synthetic and natural—has become mostly restricted to the field of basic science.
The use of split lignocellulosic materials is proposed in order to eliminate toxic heavy metals soluble in wastewaters from household or industrial origin.
This invention shows several advantages relating to that already known in the state of the art. In this proposal:
1. Pre-treatment of chemical activation widely used in literature to date is eliminated, which incorporates chemicals in the preparation of the adsorbing vegetal substrate. This process increases the treatment cost of contaminated waters.
2. The presence of tannins soluble in treated waters is minimized due to the shortened adsorption times in the reactor. Tannins in fact form part of tree barks and have properties to adsorb heavy metals. Their extraction and use have been described in literature, but it involves additional costs by incorporating new chemicals as aldehydes and ammonia.
3. A rational use of the vegetal substrates already mentioned is made, which generally form part of agricultural industry wastes. This is achieved by applying certain operation conditions, which allows this kind of substrates to be revalued as adsorbing agents of heavy metals.
4. A restricted use of reactive chemicals is made, which makes the method ecologically and environmentally sustainable.
5. The treatment time in the adsorption reactor is significantly reduced with high efficiency in the elimination of heavy metals present in the water to be treated.
6. This can be applied to a multi-metallic system that may contain such metals as copper, zinc, nickel, lead, cadmium, cobalt, platinum, palladium, chromium, mercury, uranium and mixtures if the process is performed with proper solid-liquid ratio and pH values for the composition of waters.
7. The vegetal substrate obtained at the end of the process allows recycling in order to recover the heavy metals present in non-treated waters. This is an environment-friendly method.
A more detailed description of the invention is provided in the following description and appended claims taken in conjunction with the accompanying drawings.
(1) drying of lignocellulosic material
(2) grinding of lignocellulosic material
(3) filtering the heavy metals solution
(4) charging the reactor
(5) pH adjustment
(6) stirring
(7) filtering
(8) Are specifications met?
(9) reprocessing of metals and/or disposal of the lignocellulosic material used
(10) reuse of water or disposal at local level.
The following is a detailed description and explanation of the preferred embodiments and best modes contemplated by the inventors of carrying the invention along with some examples thereof.
The methodology proposed considers the use of natural renewable adsorbing agents without chemical treatment and defined as lignocellulosic, such as wastes from the grain industry (walnuts, almonds, peanuts, pistachio nut and coconut, among others), tree bark (pines in its different varieties as radiata, Douglas fir, eucalyptus, acacia, holm oak, rauli, oak tree, beech tree, among others). The method proposed optimizes the use of a vegetal substrate, which makes it possible the recycling process of the adsorbing agent and metals eliminated from wastewater, such as copper, zinc, nickel, lead, cadmium, cobalt, platinum, palladium, chromium, mercury, uranium and mixtures among others. The vegetal substrate with moisture equal to or below 10% should be reduced by grading to a size below 1 mm in a grinder prior to its use, so that to increase the solid-liquid interphase area in the reactor, which favors the efficacy of the adsorbing material. A proper solid-liquid ratio should be defined in the reactor within an interval between 3 and 50 g/L according to the initial metallic composition of wastewater. The process is conducted at room temperature. Prior to the batch process start-up, the working pH value should be adjusted, where said pH should range between pH 3 and pH 8, with this value depending on the metallic composition in the liquid residue. The vegetal substrate in the reactor may be found suspending or enclosed in containers permeable to the flow of liquid located inside the reactor. The vegetal material should be kept for the whole adsorption process under turbulent stirring where time—according to the composition of the original liquid residue—is within an interval of 0.5 and 2.0 hours—with a Reynolds value not below 4000 while the process is in progress. The concentration of heavy metals in the water should be monitored by using analysis techniques consistent with the concentrations of metals in the wastewater to be treated.
The different parameters characterizing the methodology proposed (pH, solid-liquid ratio, stirring, permanence times in the adsorption reactor, grading distribution of the raw material, temperature) should be simultaneously applied, which is not evident from the prior studies performed with lignocellulosic substrates.
One liter of an aqueous solution of copper sulphates (II) of 100 mg Cu(II) concentration/liter was treated with 10 grams of radiata pine bark, 10% moisture, and a grading distribution below 1 mm of diameter.
Ten liters of an aqueous solution of copper nitrate (II) of 50 mg Cu(II) concentration/liter, zinc sulphate (II) at 50 mg concentration Zn(II)/liter and cadmium nitrate (II) at 50 mg concentration Cd(II)/liter, were treated with 100 grams of radiata pine bark, 10% moisture, and a grading distribution below 1 mm of diameter.
Although embodiments and examples of the invention have been shown and described, it is to be understood that various modifications, substitutions, and rearrangements of components, parts, materials, and method steps, as well as other uses of the invention, and other processes, can be made by those skilled in the art without departing from the novel spirit and scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
2702-2008 | Sep 2008 | CL | national |
This application is a national phase application based upon priority International PCT Patent Application No. PCT/CL2009/000014 filed Sep. 11, 2009, which is based upon priority Chilean Patent Application No. 2702-2008 filed Sep. 11, 2008.