The present disclosure is directed to a process to repair erosion coatings.
Gas turbine engines, such as those that power modern commercial and military aircraft, generally include a compressor section to pressurize an airflow, a combustor section to burn a hydrocarbon fuel in the presence of the pressurized air, and a turbine section to extract energy from the resultant combustion gases.
Gas turbine engines have rows of circumferentially spaced airfoils mounted on respective rotor disks for rotation about an engine axis. Advanced configurations feature shroud-less hollow airfoils manufactured of lightweight materials. The airfoils are designed to high tolerances and typically include a coating to accommodate significant operational requirements.
Airfoil coatings erode over time and may be reapplied as part of a repair strategy.
In accordance with the present disclosure, there is provided a method of repairing an erosion coating coupled to a substrate wherein the coating comprises an anodization layer on the substrate, a bond primer layer on the anodization layer, a corrosion-resistant primer on the bond primer, and an erosion coating on the corrosion-resistant primer. The method comprises abrading an erosion coating; abrading a corrosion-resistant primer; creating an abraded surface comprising a bond primer over an anodization layer coupled to the substrate, chemically etching the anodization layer; abrading the bond primer; applying an anodization layer to the substrate; applying a bond primer layer over the anodization layer; applying a corrosion-resistant layer over the bond primer layer; and applying an erosion coating layer over the corrosion-resistant layer.
In another and alternative embodiment, the abraded surface comprises at least one of a bare metal substrate, an anodization layer over the substrate; a portion of a bond primer over the anodization layer over the substrate and an anodization layer over said substrate with a portion of a corrosion-resistant primer over a bond primer over said anodization layer over said substrate.
In another and alternative embodiment, the abrading is selected from the group consisting of mechanical abrasion, abrasive blast, grinding, sanding, and the like.
In another and alternative embodiment, applying the anodization layer to the substrate comprises acid anodization on an assembled blade.
In another and alternative embodiment, the step of chemically etching the anodization layer comprises a chromic-phosphoric acid etch.
In another and alternative embodiment, the chromic-phosphoric acid etch facilitates mechanical removal of the bond primer layer in the absence of the anodization layer.
In another and alternative embodiment, the chromic-phosphoric acid etch comprises removing the anodization layer.
In another and alternative embodiment, a sheath remains coupled to a blade body and a body cover is also attached to a suction side of the blade body.
Other details of the process to repair erosion coatings are set forth in the following detailed description and the accompanying drawings wherein like reference numerals depict like elements.
The engine 20 generally includes a low spool 30 and a high spool 32 mounted for rotation around an engine central longitudinal axis A relative to an engine static structure 36 via several bearing compartments 38. The low spool 30 generally includes an inner shaft 40 that interconnects a fan 42, a low pressure compressor 44 (“LPC”) and a low pressure turbine 46 (“LPT”). The inner shaft 40 drives the fan 42 directly or through a geared architecture 48 to drive the fan 42 at a lower speed than the low spool 30. The high spool 32 includes an outer shaft 50 that interconnects a high pressure compressor 52 (“HPC”) and high pressure turbine 54 (“HPT”). A combustor 56 is arranged between the HPC 52 and the HPT 54. The inner shaft 40 and the outer shaft 50 are concentric and rotate around the engine central longitudinal axis A which is collinear with their longitudinal axes.
Core airflow is compressed by the LPC 44 then the HPC 52, mixed with fuel and burned in the combustor 56, then expanded over the HPT 54 and the LPT 46. The turbines 46, 54 rotationally drive the respective low spool 30 and high spool 32 in response to the expansion. The main engine shafts 40, 50 are supported at a plurality of points by the bearing compartments 38. It should be appreciated that various bearing compartments 38 at various locations may alternatively or additionally be provided.
Referring also to
Each fan blade 58 generally includes an innermost root portion 60, an intermediate platform portion 62, and an outermost airfoil portion 64. In one form, the root portion 60 defines an attachment such as an inverted fir tree, bulb, or dovetail, so the fan blade 58 is slidably received in a complimentary configured recess provided in a fan rotor 59 (
With reference to
The substrate 82, in this embodiment, is the fan blade 58 base metal (e.g., an aluminum alloy). The coating 80 protects the substrate 82 from corrosion, wear and other physical damage.
The anodization layer 84, in this embodiment, is defined as an oxide layer formed through a chemical anodization process. The anodization process changes the surface morphology of the aluminum at the surface and creates an anodization layer up to 0.0001 inches (0.00254 mm) with a microscopic roughness that greatly increases the surface area for bonding and provides for some mechanical retention of bond primers.
The bond layer 86, in this embodiment, is an organic primer layer (e.g., epoxy-based) which may be spray-applied to a thickness of up to 0.0005 inches (0.0127 mm). The bond layer 86 is applied to increase the bond strength between the underlying aluminum/anodization layer 84 and the subsequent primers and coatings.
The corrosion resistant primer 88, in this embodiment, is an epoxy-based material and is loaded with hexavalent chromium as the active corrosion-resistant component. Alternatively, the corrosion resistant primer 88 is a non-hexavalent chromium based corrosion-resistant primer. The corrosion-resistant primer 88 is applied up to a thickness of 0.001 inches (0.0254 mm) to prevent corrosion of the underlying aluminum.
The erosion coating 90, in this embodiment, is an organic erosion coating (e.g., polyurethane) with a thickness of up to 0.030 inches (0.762 mm). The erosion coating 90 protects the underlying primers and metal substrate from damage due to particle and rain impact.
With reference to
The coating 80 to be remanufactured or repaired is initially abraded (102) to leave an abraded surface 104. In an exemplary embodiment, at least the erosion coating layer 90, the corrosion-resistant primer layer 88, and at least a portion of the bond primer 86 can be removed by a variety of surface alteration and material removal techniques, such as for example, mechanical abrasion, abrasive blast, grinding, sanding, abrasion, laser ablation, waterjet stripping, flashlamp/CO2 stripping, and the like. Examples of abrasion media can be aluminum oxide, glass, silicon carbide, sodium bicarbonate, plastic media, steel, walnut shells and the like. The resultant abraded surface 104 can be relatively rough in texture and be a mixed surface containing a bare metal substrate and material remnants of the abraded layers 84, 86, and 88. In an exemplary embodiment only the anodization layer 84 remains over the substrate 82. In other embodiments, portions of the bond primer 86 remain over portions of the anodization layer 84.
In an exemplary embodiment, the process of repair 100 aims to remove the remaining abraded surface 104 layers. As shown in
At step 108 a second mechanical abrasion technique is applied to remove the remainder of the bond layer 86. In an exemplary embodiment, the mechanical abrasion can be done by hand, or other means. A bare substrate surface 92 is the result of the above steps 102 through 108. Steps 106 and 108 may be repeated until a bare substrate is obtained.
At step 110 a new anodization layer 84 is applied to the substrate surface 92. As shown in
At step 112 a new bond primer layer 86 is applied over the anodization layer 84. At step 114 a new corrosion-resistant primer layer 88 is applied over the bond primer layer 86. At step 116 a new erosion coating layer 90 is applied over the corrosion-resistant primer layer 88.
The process of repairing erosion coatings for blades and structural guide vanes coated with erosion coatings provided the advantage of replacing damaged erosion coating with the fan blade assembled.
There has been provided a process to repair erosion coatings. While the process to repair erosion coatings has been described in the context of specific embodiments thereof, other unforeseen alternatives, modifications, and variations may become apparent to those skilled in the art having read the foregoing description. Accordingly, it is intended to embrace those alternatives, modifications, and variations which fall within the broad scope of the appended claims.