Claims
- 1. A method for molding an article of heat-fusing material in a mold having first and second groups of fluid passages disposed adjacent the mold surface for controlling the temperature over respective first and second areas of the mold surface, said method comprising the steps of: supplying all of the passages with liquid for maintaining the temperature of the first and second areas of the mold surface at a non-gelling temperature below that required to gel any appreciable thickness of the heat-fusing material, disposing liquid heat-fusing material over the first and second areas of the mold surface, supplying the first group of passages with liquid at a temperature sufficient to raise the temperature of the first area to a higher temperature than the second area for gelling a predetermined thickness of the heat-fusing material over the first area while maintaining said second area at a lower temperature, removing non-gelled liquid heat-fusing material from the mold, and supplying the first and second passages with liquid at a temperature sufficient to raise the temperature of the first and second areas to a cure temperature for curing the heat-fusing material disposed thereover.
- 2. A method as set forth in claim 1 including applying a coating of liquid heat-fusing material to the first and second areas while the first and second areas are at said non-gelling temperature and prior to disposing the additional liquid heat-fusing material over said first and second areas for the gelling thereof over the first area.
- 3. A method as set forth in claim 2 further defined as maintaining the temperature of the liquid in the second group of passages to inhibit the gelling of the liquid heat-fusing material over the second area until the first and second passages are supplied liquid for raising the first and second areas to a cure temperature.
- 4. A method as set forth in claim 3 wherein applying a coating is further defined as filling the mold with liquid heat-fusing material and emptying the mold to leave the coating in the mold.
- 5. A method as set forth in claim 4 wherein disposing liquid heat-fusing material is further defined as filling the mold a second time with the additional heat-fusing material, and including emptying the mold a second time of non-gelled heat-fusing material subsequent to the gelling of the material to the predetermined thickness over the first area.
- 6. A method as set forth in claim 5 further defined as maintaining the mold surface at a non-gelling temperature in the range of 130.degree. F. to 180.degree. F. prior to filling the mold the second time for disposing the additional heat-fusing material over the first and second areas, heating the first area of the mold surface with liquid in the first group of passages to a temperature in the range of 250.degree. F. to 290.degree. F. for gelling the heat-fusing material over the first area of the mold surface, and thereafter heating the first and second areas of the mold surface with liquid in the passages to a temperature in the range of 350.degree. F. to 400.degree. F. for the curing of the heat-fusing material.
RELATED APPLICATION
The subject application is a continuation-in-part of the copending application Ser. No. 789,410, filed Apr. 21, 1977, now abandoned.