10266442
The present invention relates generally to additive manufacturing of glass, by extrusion of molten glass through a nozzle.
In illustrative implementations of this invention, a crucible kiln heats glass such that the glass becomes or remains molten. A nozzle extrudes the molten glass while one or more actuators actuate movements of the nozzle, a build platform or both. A computer controls these movements such that the extruded molten glass is selectively deposited to form a 3D glass object.
In some implementations, the actuators actuate the crucible kiln and nozzle to move in horizontal x, y directions and actuate the build platform to move in a z-direction. In other implementations, “polar printing” occurs in which motion occurs in linear r, angular theta, and linear z directions: the actuators (a) actuate the crucible kiln and nozzle to move along a single horizontal “r” axis; (b) actuate the build platform to rotate about its center line in an angular theta direction, and (c) actuate the build platform to move up and vertically in a z direction. In yet other implementations, the nozzle and crucible kiln are stationary, and the actuators actuate the build platform to move relative to the nozzle.
In illustrative implementations, the nozzle is independently heated by a nozzle kiln. In some cases, the nozzle kiln is partially housed in the crucible kiln, and partially protrudes below the crucible kiln.
In illustrative implementations, the build platform is located inside an annealing kiln, and the nozzle protrudes into the annealing kiln. Thus, the selective deposition of molten glass occurs inside the annealing kiln. The annealing kiln heats the extruded glass during the selective deposition, and anneals the glass by slowly and progressively lowering the temperature of the extruded glass after the selective deposition.
In some implementations, a fluid flows through a cavity or tubes adjacent to the nozzle tip, in order to cool the nozzle tip and thereby reduce the amount of glass that sticks to the nozzle tip. The lower the temperature of the nozzle tip, the less glass sticks to the nozzle tip or the easier it is to remove it.
In some implementations, one or more refractory metal sheets are press-formed to fit around the exit orifice of the nozzle and thereby protect the nozzle tip from becoming clogged by glass. When glass becomes stuck to a disposable sheet, the disposable sheet is removed.
In some implementations, a valve controls flow of molten glass through the nozzle. For example, in some cases, the valve comprises a pair of refractory shears. When the shears are closed, they cut the filament of molten glass exiting the nozzle and block flow of molten glass through the nozzle. In other cases, a motor raises a rod up and down. When the rod is fully lowered, it extends into the nozzle, touching interior walls of the nozzle tip and blocking flow of molten glass through the nozzle.
In some implementations, the sole impetus for the flow of molten glass through the nozzle is the force of gravity. In other implementations, molten glass is actively pushed out of the nozzle. For example, in some cases, a refractory plunger or compressed air exerts pressure against molten glass in the crucible and thereby pushes the molten glass through the nozzle.
In some cases, a tube extends into the nozzle almost to the tip of the nozzle. Air is blown through the tube, such that a column of air infiltrates the filament of molten glass as it is extruded from the nozzle. The column of air is trapped inside the filament and is co-axial with the filament.
In illustrative implementations, the 3D glass object produced by the selective deposition is optically transparent.
The description of the present invention in the Summary and Abstract sections hereof is just a summary. It is intended only to give a general introduction to some illustrative implementations of this invention. It does not describe all of the details and variations of this invention. Likewise, the descriptions of this invention in the Field of Technology section and Field Of Endeavor section are not limiting; instead they identify, in a general, non-exclusive manner, a field of technology to which exemplary implementations of this invention generally relate. Likewise, the Title of this document does not limit the invention in any way; instead the Title is merely a general, non-exclusive way of referring to this invention. This invention may be implemented in many other ways.
The above Figures show some illustrative implementations of this invention, or provide information that relates to those implementations. However, this invention may be implemented in many other ways.
Prototype
The following is a description of a prototype of this invention. This prototype is a non-limiting example of this invention; this invention may be implemented in many other ways.
In this prototype, a 3D printer fabricates 3D glass objects, such as objects that comprise optically transparent glass. The 3D printer operates at high temperatures, extrudes highly viscous molten glass, and overcomes large inertias during the 3D printing process.
In this prototype, a crucible kiln maintains molten glass at a temperature of 1900-2000 degrees Fahrenheit. The temperature of the feed affects the dimensional accuracy of the print due to the change in viscosity across the temperature range. Electrical specifications of the crucible kiln are: 1800 W, 120V, 15 A, 1 phase, 20 A breaker. The kiln is made of alumina-silica fiber board (Duraboard®) and it is heated through Kanthal® A-1 1.8 mm diameter, 0.57 Resistance Ω·m 20° C. coils. Temperature of the crucible kiln is read by a Type K thermocouple.
In this prototype, a nozzle kiln provides independent heating to the printer nozzle. The electrical specifications of the nozzle kiln are: 300 W, 48V, 6 A, 1 phase, 15 A breaker. The kiln is made of alumina-silica fiber board (Duraboard®) and it is heated through Kanthal® A-1 1 mm diameter, 1.85 Resistance Ω·m 20° C. coils. Temperature of the nozzle kiln is read by a Type S thermocouple. The characteristics of the flow of molten glass are highly temperature dependent. The nozzle kiln is partially housed in a bottom wall of the crucible kiln, and also protrudes below the bottom of the crucible kiln.
In this prototype, the crucible, crucible kiln, nozzle and nozzle kiln together comprise a compact unit, which is sometimes referred to herein as the “print head”. All heating elements and thermocouples exit on the same side of the print head in order not to limit the print head movements.
In this prototype, molten glass is contained in a refractory crucible positioned inside the crucible kiln. The molten glass flows out of the crucible, then through an alumina nozzle, and then exits the tip of the nozzle and is deposited. The nozzle kiln has a hole, into which the nozzle is inserted. After the nozzle is inserted, the crucible and the nozzle are assembled with a refractory mortar. The nozzle is machined from bulk alumina rods.
In this prototype, the print head (including nozzle, crucible, crucible kiln and nozzle kiln) is mounted on a carriage that comprises supports mounted on roller bearings that travel on structural tracks. The nozzle kiln and nozzle protrude out of the bottom of the crucible kiln, and thus protrude below the carriage into the annealing chamber. The nozzle deposits molten glass, precisely controlling layer height. The layers of deposited glass adhere to each other.
In this prototype, the molten glass is deposited into an annealing chamber. Thus, the 3D object formed by the deposited glass is created inside the annealing chamber. The annealing chamber reduces the cooling rate of the glass, such that the 3D object being manufactured comprises crack-free glass with strong adhesion between layers.
In this prototype, the annealing chamber operates at 900 degrees Fahrenheit, before slowly cooling during annealing. The annealing chamber remains stationary. A build platform supports the 3D glass object being fabricated. The build platform is positioned inside the annealing chamber. An actuator moves the build platform up and down vertically. The print head moves horizontally in X-Y directions.
In this prototype, the heating elements of the annealing chamber draw 4000 Watts. Power for the heating elements is obtained by plugging into a 208 V wall outlet. The annealing chamber includes two refractory doors. One door provides access to the nozzle. The other door may be opened, in order to remove the 3D printed object from the annealing chamber. In addition, the annealing chamber includes a heat-resistant Neoceram® window, through which a user may look to visually monitor progress of a print job.
In this prototype, the top of the annealing kiln has a hole, into which the nozzle of the print head protrudes in order to deposit molten glass into the annealing chamber. Two light, thin, refractory Duraboard® insulation skirts, together with the carriage for the print head, block this hole and reduce the amount of heat that is lost through this hole. One skirt is mounted on top of the annealing chamber, whereas the other one is mounted to the moving carriage below the crucible kiln.
In this prototype, a frame provides structural support for the printer, and is positioned along the exterior of the printer. The frame is made from 80/20 aluminum 1″ stock and 1018, 1″ square steel tube. Aluminum is used for elements not exposed to high heat, while the heavier steel is reserved for central components that may become hot from the feed kiln, annealing kiln, or radiating molten glass. The print head is mounted on a moveable carriage. The carriage comprises steel supports mounted on shielded roller bearings that travel on structural steel tracks. The entire assembly, including the frame, print head, carriage, and annealing chamber, fits through a standard door frame.
This prototype includes three independent stepper motor-lead screw gantry systems. Out of these three stepper motor-lead screw gantry systems, one actuates x motion of the print head carriage, one actuates y motion of the print head carriage, and one actuates z motion of the build carriage.
In this prototype, each stepper motor is electronically controlled by a driver circuit, which in turn is electronically controlled by an Arduino® PCB and an Arduino® Shield PCB. The stepper motors are NEMA 23 in size and have a rated holding torque of 400 oz-inches. The stepper motors operate in their high-torque range due to the inertia of the crucible kiln and carriage assembly. The driver circuits permit a maximum current of 7.8 Amps to the stepper motors and are powered separately from the electronic controls with a 48 V power supply.
In this prototype, each of the x and y motors are connected to an ACME ½-10 five-start fast travel lead screw with a flexible helical coupling that accommodates slight misalignments during operation. The x and y motors are isolated from axial and radial loads by bearing blocks. Each of the x and y motors is mounted at the corner of the travel range actuated by the motor. The lead screws for the x and y motors, respectively, are attached to the carriage with a brass nut and the far end is not constrained in order to reduce risk of jamming due to substantial vibration when operating at full speeds. Plates and mounts are made of mild steel.
In this prototype, the Z motor is mounted at the base of the frame and drives a standard travel lead screw through radial bearings to the build platform. The build platform support rod extends through a hole at the base of the annealing chamber kiln.
In this prototype, an emergency stop button is wired to cut power to the drivers and motors and mounted to the frame for easy access. Limit switches are mounted at the “zeros” of the X and Y axes both to provide homing information to the control software and to protect the system from mechanical crashes. These prevent the motor from driving when activated and are connected directly to the Arduino® shield. The limit switch cables are bundled separately from the motor cables to prevent interference.
In this prototype, a computer slices a CAD model of the desired three-dimensional glass object. To do so, the computer performs a C# script in Grasshopper Build 0.9.76.0, and imported into an open source printing software, Repetier-Host V1.0.6. Open source Repetier firmware is used to direct the 3D printer. The Repetier firmware is adapted for the acceleration, velocities, and size of the 3D printer.
In this prototype, a computer performs an algorithm that includes the following steps. The slicing script draws a helix around the CAD model structure, providing information for continuous flow and accommodating for the specific filament diameter of extruded glass. This helix is then represented in Cartesian coordinates in the form of g-code. The g-code generator may take two different types of inputs to create the code: a free-form spline/polyline curve or a non-uniform rational basis spline (nurbs) surface. The layer height and curve discretization, as well as the feed rate, may be modified in real-time, while watching the toolpath update live in the preview pane. Users may also define specific velocities for each point. The algorithm for the wrapping toolpath takes the input surface, intersects it based on the layer height, discretizes each intersection curve based on the input resolution, and then incrementally remaps the discretized points with increasing z values. The remapped points are then connected with a polyline to create the continuous wrapping toolpath for any given complex geometry. All remapped points are ordered and formatted to g-code syntax which is then be imported directly into Repetier software.
In this prototype, the 3D printer selectively deposits molten glass with a spatial precision of about 2 mm. The crucible kiln, nozzle kiln and annealing kiln are able to heat up to 2300° F., and the maximum build volume is 0.7 cubic feet.
This invention is not limited to the prototype described above. Instead, this invention may be implemented in many different ways.
Drawings
Turning now to the drawings,
In
In
In
In
In
In
As used herein, “x, y motion” means motion in two horizontal axes that are perpendicular to each other. As used herein, “z motion” means vertical motion. Likewise, as used herein, “x” and “y” directions means two directions that are horizontal and are perpendicular to each other, and “z” direction means a vertical direction. Likewise, as used herein, “x” and “y” axes mean two axes that are horizontal and are perpendicular to each other, and a “z” axis means a vertical axis.
In
In
In
In
In
In some cases, x, y and z motions are actuated by three lead screw gantry systems that include motors 211, 221 and 201, respectively. In some cases, motors 201, 211, and 221 comprise stepper motors or servo motors. In some cases, the motors are controlled by driver circuits that are controlled by one or more microcontrollers (e.g., an Arduino® board and shield). The microcontrollers are in turn controlled by another computer.
In some cases, the molten glass comprises a soft, flexible filament of molten glass as it exits the nozzle.
In the example shown in
Alternatively or in addition, in some cases, at least a portion of the deposition of glass is not layer-by-layer. For example, in some cases, molten glass is deposited at a position such that the glass dribbles down the edge of one or more previously deposited layers and stops at a level lower than the layer most recently deposited.
In the example shown in
In some implementations of this inventions, cool fluid flows through tubes or cavities near the tip of the nozzle and cools the nozzle tip, in order to reduce the amount of glass that sticks to the nozzle tip, and thus to reduce fouling of the nozzle. As used herein, to “foul” means to build up glass on a surface of the nozzle tip. For example, in some cases, glass is heated to approximately 1850° Fahrenheit in the nozzle, and it is desirable that the nozzle tip be at a lower temperature than the glass. This is because lowering the temperature of the nozzle tip tends to reduce the amount of glass that sticks to the nozzle tip—that is, the lower the temperature of the nozzle tip, the less amount of molten glass that sticks to the nozzle tip.
In the examples shown in
In
In
In each of
In some implementations of this inventions, one or more disposable sheets of refractory material cover the nozzle tip, except the nozzle orifice, in order to reduce fouling of the nozzle. After solidified glass builds up on a disposable sheet, the sheet is removed and replaced with a new disposable sheet. In some cases, the refractory sheets comprise metal, such as stainless steel, or an Inconel® austenite nickel-chromium-based superalloy, or tungsten carbide.
In the example shown in
In the example shown in
In some implementations, it is advantageous to immobilize the print head (including nozzle 125, crucible 105, crucible kiln 107, and nozzle kiln 109). For example, immobilizing the print head allows the crucible to be larger and heavier and to contain more glass.
In
Thus, in
In
In
In
In
In the example shown in
In the example shown in
In
In
In some cases, valve driver circuit 923 controls a valve motor 924. The valve motor 924 actuates a valve. For example, in some cases, valve motor 924 opens and shuts a pair of shears 511, as shown in
In some cases, a plunger driver circuit 925 controls a plunger motor 926. The plunger motor 926 actuates a plunger (e.g., 1103) that creates pressure to actively extrude molten glass, as shown in
In some cases, an air driver circuit 927 controls an air pump 929. The air pump 929 pumps compressed air that is used to created pressure to actively extrude molten glass, as shown in
In some cases, a feeder driver circuit 930 controls a feeder motor 931. The feeder motor 931 actuates a feeder mechanism for feeding materials into crucible 105. For example, in some cases, the feeder mechanism loads one or more of the following materials into the crucible 105: glass nuggets, glass ingots, glass powder, a glass rod or filament, or raw materials for manufacturing glass.
In some cases, instructions for one or more movements of a plunger, valve or tube are embedded in g-codes that are generated by computer 900.
In the example shown in
In
In some implementations of this invention, the extrusion of molten glass through the nozzle is actuated only by gravitational force, and the rate of extrusion is controlled by factors such as the temperature and material composition of the glass.
However, in some implementations, it is advantageous to actively exert pressure against the molten glass, in order to increase the extrusion rate for a given temperature or material composition of glass. Furthermore, by varying the pressure exerted against the molten glass, the rate of extrusion of the molten glass may be controlled, while (in some cases) holding other factors (such as temperature or material composition of glass) constant.
In some cases, the materials are inserted manually. Alternatively, in some cases, a feeder motor 931 actuates a feeder mechanism that feeds the materials into the crucible or nozzle. For example, in some cases, the feeder mechanism comprises any material handling system, including any vibrating feeder, rotary feeder, rotary screw feeder, variable rate feeder, or volumetric feeder.
In some cases, raw materials for glass 1205 are fed into crucible 105. For example, in some cases, the raw materials comprise a combination of materials selected from: oxides (e.g., SiO2, B2O3, or P2O3), silicate sands, feldspars (e.g. albite, anorthite, aplite), borax, dolomite, limestone, nepheline, kyanite, sand, soda ash, or recycled glass. In some cases, the raw materials also include one or more (a) fluxes to reduce melting temperature (e.g., Na2O, PbO, K2O, Li2O), (b) property modifiers to control material properties such as durability, expansion, or viscosity (e.g., CaO, Al2O3), (c) colorants, or (d) fining agents (such as As-oxides, Sb-oxides, KNO3, NaNO3, NaCl, fluorides, or sulfates).
In some cases, it is advantageous to quickly refill the crucible or nozzle with already molten and fined glass, as shown in
In some cases, it is advantageous for the printer (a) to extrude a molten glass filament that surrounds an air-filled cavity, where the cavity extends for at least a portion of the length of the filament, or (b) to otherwise extrude blown glass. In illustrative implementations, coaxial infiltration of air into a molten glass filament facilitates hollow object fabrication.
In the example shown in
In illustrative implementations of this invention, the printer produces optically transparent glass. In some implementations, the production of optically transparent glass includes one of more of the following features: (a) starting from large (and, in some cases, pre-fined) glass chunks to limit bubble amount; (b) fining glass for at least 2 hours (and in some cases, between 3 or 4 hours) to reduce bubble content; (c) extruding viscous molten glass, instead of sintering a powder; (d) depositing a molten glass filament with no vertical offset between the top of the layer of glass being deposited and the nozzle (instead of positioning the nozzle above the layer being deposited, and thereby causing the extruded filament to drop before reaching the level of the layer being deposited); (e) annealing the extruded glass in an annealing chamber; and (f) polishing the exterior surface (including base and walls) of the 3D printed glass object, after the glass cools to room temperature.
In illustrative implementations, the 3D printer selectively deposits molten glass. This allows the 3D printer to create shapes that cannot be fabricated by conventional glassblowing or by a conventional manufacturing technique in which a parison is blow molded.
In
Crucible and nozzle materials and shapes may be varied, depending on the particular implementation of this invention. For example, in some cases, a wide elongated crucible allows refilling farther from the nozzle with less impact on pressure head and consequently on flow rate.
In some implementations, the skirt insulation system (e.g., 701, 703) is replaced by a bellow system.
In illustrative implementations of this invention, the glass comprises a glass material, as that term is defined herein. Thus, in illustrative implementations of this invention, glass material is melted in a crucible 105, extruded through a nozzle 125, and selectively deposited (layer-by-layer or otherwise) to form a 3D object that comprises glass material.
In illustrative implementations of this invention, the glass comprises an amorphous material, as that term is defined herein. Thus, in illustrative implementations of this invention, an amorphous material is melted in a crucible 105, extruded through a nozzle 125, and selectively deposited (layer-by-layer or otherwise) to form a 3D object that comprises amorphous material.
Field of Endeavor
The field of endeavor of this invention is additive manufacturing of glass, by extrusion of molten glass through a nozzle.
The inventors confronted at least the following two problems: (1) how to additively manufacture a glass object by selective deposition of molten glass by extrusion through a nozzle; and (2) how to additively manufacture an optically transparent glass object, by selective deposition of molten glass by extrusion through a nozzle.
Computers
In exemplary implementations of this invention, one or more electronic computers (e.g. 900, 904) are programmed and specially adapted: (1) to control the operation of, or interface with, hardware components of an apparatus for additive manufacture of glass, including any heating elements, motors, actuators, valves, thermocouples or other sensors; (2) to control movement of a print head or build platform; (3) to control temperature in the interior of a kiln, including a crucible kiln, nozzle kiln or annealing kiln, (4) to perform any other calculation, computation, program, algorithm, computer function or computer task described or implied above; (5) to receive signals indicative of human input; (6) to output signals for controlling transducers for outputting information in human perceivable format; and (7) to process data, to perform computations, to execute any algorithm or software, and to control the read or write of data to and from memory devices. The one or more computers may be in any position or positions within or outside of the additive manufacturing apparatus. For example, in some cases (a) at least one computer is housed in or together with other components of the additive manufacturing apparatus, and (b) at least one computer is remote from other components of the additive manufacturing apparatus. The one or more computers are connected to each other or to other components of the additive manufacturing apparatus either: (a) wirelessly, (b) by wired connection, or (c) by a combination of wired and wireless links.
In exemplary implementations, one or more computers are programmed to perform any and all calculations, computations, programs, algorithms, computer functions and computer tasks described or implied above. For example, in some cases: (a) a machine-accessible medium has instructions encoded thereon that specify steps in a software program; and (b) the computer accesses the instructions encoded on the machine-accessible medium, in order to determine steps to execute in the program. In exemplary implementations, the machine-accessible medium comprises a tangible non-transitory medium. In some cases, the machine-accessible medium comprises (a) a memory unit or (b) an auxiliary memory storage device. For example, in some cases, a control unit in a computer fetches the instructions from memory.
In illustrative implementations, one or more computers execute programs according to instructions encoded in one or more tangible, non-transitory, computer-readable media. For example, in some cases, these instructions comprise instructions for a computer to perform any calculation, computation, program, algorithm, computer function or computer task described or implied above. For example, in some cases, instructions encoded in a tangible, non-transitory, computer-accessible medium comprise instructions for a computer to: (1) to control the operation of, or interface with, hardware components of an apparatus for additive manufacturing of glass, including any heating elements, motors, actuators, valves, thermocouples or other sensors; (2) to control movement of a print head or build platform; (3) to control temperature in the interior of a kiln, including a crucible kiln, nozzle kiln or annealing kiln, (4) to perform any other calculation, computation, program, algorithm, computer function or computer task described or implied above; (5) to receive signals indicative of human input; (6) to output signals for controlling transducers for outputting information in human perceivable format; and (7) to process data, to perform computations, to execute any algorithm or software, and to control the read or write of data to and from memory devices.
Network Communication
In illustrative implementations of this invention, one or more electronic devices (e.g., 900, 904, 914, 917, 920, 925, 927, 930) are configured for wireless or wired communication with other electronic devices in a network.
In some cases, one or more of the following hardware components are used for network communication: a computer bus, a computer port, network connection, network interface device, host adapter, wireless module, wireless card, signal processor, modem, router, computer port, cables or wiring.
In some cases, one or more computers (e.g., 900, 904) are programmed for communication over a network. For example, in some cases, one or more computers are programmed for network communication: (a) in accordance with the Internet Protocol Suite, or (b) in accordance with any other industry standard for communication, including any USB standard, ethernet standard (e.g., IEEE 802.3), token ring standard (e.g., IEEE 802.5), wireless standard (including IEEE 802.11 (wi-fi), IEEE 802.15 (bluetooth/zigbee), IEEE 802.16, IEEE 802.20 and including any mobile phone standard, including GSM (global system for mobile communications), UMTS (universal mobile telecommunication system), CDMA (code division multiple access, including IS-95, IS-2000, and WCDMA), or LTS (long term evolution)), or other IEEE communication standard.
In some cases, one or more electronic devices in the additive manufacturing apparatus include a wireless communication module for wireless communication with other electronic devices in a network. Each wireless communication module includes (a) one or more antennas, (b) one or more wireless transceivers, transmitters or receivers, and (c) signal processing circuitry. The wireless communication module receives and transmits data in accordance with one or more wireless standards.
Definitions:
The terms “a” and “an”, when modifying a noun, do not imply that only one of the noun exists.
“Amorphous material” means a material that (a) has a non-crystalline atomic structure when solid and (b) exhibits a glass transition when cooling toward the amorphous material's glass transition temperature. As used herein, an “amorphous material” remains an amorphous material, regardless of temperature (e.g., above or below glass transition temperature) or phase (e.g., solid or liquid).
The term “comprise” (and grammatical variations thereof) shall be construed as if followed by “without limitation”. If A comprises B, then A includes B and may include other things.
The term “computer” includes any computational device that performs logical and arithmetic operations. For example, in some cases, a “computer” comprises an electronic computational device, such as an integrated circuit, a microprocessor, a mobile computing device, a laptop computer, a tablet computer, a personal computer, or a mainframe computer. In some cases, a “computer” comprises: (a) a central processing unit, (b) an ALU (arithmetic logic unit), (c) a memory unit, and (d) a control unit that controls actions of other components of the computer so that encoded steps of a program are executed in a sequence. In some cases, a “computer” also includes peripheral units including an auxiliary memory storage device (e.g., a disk drive or flash memory), or includes signal processing circuitry. However, a human is not a “computer”, as that term is used herein.
“Contain” shall be construed as if followed by “without limitation”. If A contains B, then A contains B and may contain other things. To “contain” does not require total enclosure. For example, a container “contains” a fluid within a cavity formed by the container's walls, even if hole in a container wall creates an orifice connecting the cavity and the external environment.
“Defined Term” means a term or phrase that is set forth in quotation marks in this Definitions section.
For an event to occur “during” a time period, it is not necessary that the event occur throughout the entire time period. For example, an event that occurs during only a portion of a given time period occurs “during” the given time period.
The term “e.g.” means for example.
The fact that an “example” or multiple examples of something are given does not imply that they are the only instances of that thing. An example (or a group of examples) is merely a non-exhaustive and non-limiting illustration.
An “exit orifice” of a nozzle means an orifice through which a fluid or other material exits the nozzle.
A non-limiting example of “extrusion” is flow of molten glass through a nozzle, which flow is actuated only by gravitational force.
Unless the context clearly indicates otherwise: (1) a phrase that includes “a first” thing and “a second” thing does not imply an order of the two things (or that there are only two of the things); and (2) such a phrase is simply a way of identifying the two things, respectively, so that they each may be referred to later with specificity (e.g., by referring to “the first” thing and “the second” thing later). For example, unless the context clearly indicates otherwise, if an equation has a first term and a second term, then the equation may (or may not) have more than two terms, and the first term may occur before or after the second term in the equation. A phrase that includes a “third” thing, a “fourth” thing and so on shall be construed in like manner.
“Fluid” means a gas or a liquid.
The term “for instance” means for example.
“Glass material” means a material that comprises, when solid: (a) silicate glass, (b) borate glass, (c) phosphate glass, (d) fluoride glass, or (e) chalcogenide glass. As used herein, “glass material” remains glass material, regardless of temperature (e.g., above or below glass transition temperature) or phase (e.g., solid or liquid).
Non-limiting examples of a “heating element” include a resistive heating element and an inductive heater.
“Herein” means in this document, including text, specification, claims, abstract, and drawings.
The term “hole” means a hole, cavity, gap, opening or orifice.
The terms “horizontal” and “vertical” shall be construed broadly. For example, in some cases, the terms “horizontal” and “vertical” refer to two arbitrarily chosen coordinate axes in a Euclidian two dimensional space, regardless of whether the “vertical” axis is aligned with the orientation of the local gravitational field.
As used herein: (1) “implementation” means an implementation of this invention; (2) “embodiment” means an embodiment of this invention; (3) “case” means an implementation of this invention; and (4) “use scenario” means a use scenario of this invention.
The term “include” (and grammatical variations thereof) shall be construed as if followed by “without limitation”.
“I/O device” means an input/output device. For example, an I/O device includes any device for (a) receiving input from a human, (b) providing output to a human, or (c) both. For example, an I/O device includes a user interface, graphical user interface, keyboard, mouse, touch screen, microphone, handheld controller, display screen, speaker, or projector for projecting a visual display. Also, for example, an I/O device includes any device (e.g., button, dial, knob, slider or haptic transducer) for receiving input from, or providing output to, a human.
A non-limiting example of “layer-by-layer” deposition is to deposit flat, separate layers, one on top of another. A non-limiting example of “layer-by-layer” deposition is to deposit a filament in a spiral as shown in
As used herein: (a) to say that a glass material is “molten” means that the temperature of the glass material is above the glass transition temperature of the glass material; (b) to say that an amorphous material is “molten” means that the temperature of the amorphous material is above the glass transition temperature of the amorphous material; and (c) to say that glass is “molten” means that the temperature of the glass is above the glass transition temperature of the glass. As used herein: (a) to say that a glass material “melts” means that the glass material undergoes a glass transition as the temperature of the glass material increases; (b) to say that an amorphous material “melts” means that the amorphous material undergoes a glass transition as the temperature of the amorphous material increases; and (c) to say that glass “melts” means that the glass undergoes a glass transition as the temperature of the glass increases.
As used herein, “nozzle” means any orifice through which material (such as molten glass, gas, liquid, fluid, or solid) passes. A nozzle may have any shape. For example, in some cases, a nozzle may have a shape that does not accelerate material the as the material exits the nozzle.
To say that glass material is “optically transparent” means that the glass material is transparent to light in the visible light spectrum. To say that amorphous material is “optically transparent” means that the amorphous material is transparent to light in the visible light spectrum. To say that glass is “optically transparent” means that the glass is transparent to light in the visible light spectrum.
The term “or” is inclusive, not exclusive. For example A or B is true if A is true, or B is true, or both A or B are true. Also, for example, a calculation of A or B means a calculation of A, or a calculation of B, or a calculation of A and B.
A parenthesis is simply to make text easier to read, by indicating a grouping of words. A parenthesis does not mean that the parenthetical material is optional or may be ignored.
To say that a nozzle “selectively deposits” material does not have any implication regarding whether the rate of flow of the material varies over time.
As used herein, the term “set” does not include a group with no elements. Mentioning a first set and a second set does not, in and of itself, create any implication regarding whether or not the first and second sets overlap (that is, intersect).
Non-limiting examples of “silicate glass” include fused quartz glass, soda-lime-silica glass, sodium borosilicate glass (including Pyrex® glass), lead-oxide glass, and aluminosilicate glass.
“Some” means one or more.
As used herein, a “subset” of a set consists of less than all of the elements of the set.
“Substantially” means at least ten percent. For example: (a) 112 is substantially larger than 100; and (b) 108 is not substantially larger than 100.
The term “such as” means for example.
To say that a machine-readable medium is “transitory” means that the medium is a transitory signal, such as an electromagnetic wave.
Except to the extent that the context clearly requires otherwise, if steps in a method are described herein, then the method includes variations in which: (1) steps in the method occur in any order or sequence, including any order or sequence different than that described; (2) any step or steps in the method occurs more than once; (3) different steps, out of the steps in the method, occur a different number of times during the method, (4) any combination of steps in the method is done in parallel or serially; (5) any step or steps in the method is performed iteratively; (6) a given step in the method is applied to the same thing each time that the given step occurs or is applied to different things each time that the given step occurs; or (7) the method includes other steps, in addition to the steps described.
This Definitions section shall, in all cases, control over and override any other definition of the Defined Terms. For example, the definitions of Defined Terms set forth in this Definitions section override common usage or any external dictionary. If a given term is explicitly or implicitly defined in this document, then that definition shall be controlling, and shall override any definition of the given term arising from any source (e.g., a dictionary or common usage) that is external to this document. If this document provides clarification regarding the meaning of a particular term, then that clarification shall, to the extent applicable, override any definition of the given term arising from any source (e.g., a dictionary or common usage) that is external to this document. To the extent that any term or phrase is defined or clarified herein, such definition or clarification applies to any grammatical variation of such term or phrase, taking into account the difference in grammatical form. For example, the grammatical variations include noun, verb, participle, adjective, and possessive forms, and different declensions, and different tenses. In each case described in this paragraph, Applicant is acting as Applicant's own lexicographer.
Variations:
This invention may be implemented in many different ways. Here are some non-limiting examples:
In one aspect, this invention is a method that comprises, in combination: (a) heating of glass material such that the glass material becomes or remains molten; and (b) deposition of the molten glass material, in which the molten glass material is extruded through a nozzle to form an object; wherein during at least part of the deposition, (i) the object being formed rests on a build platform, (ii) the molten glass material is deposited layer-by-layer; and (iii) one or more computers control where in each layer the molten glass material is deposited, by controlling a set of actuators that actuate movement of one or both of the nozzle and build platform. In some cases, at least one actuator, out of the set of actuators, directly or indirectly actuates the nozzle to move along at least one horizontal axis. In some cases: (a) the heating occurs in a kiln; (b) during the deposition, a first actuator, out of the set of actuators, actuates the kiln and the nozzle to move along a first horizontal axis; and (c) during the deposition, a second actuator, out of the set of actuators, actuates the kiln and the nozzle to move along a second horizontal axis, the first and second horizontal axes being perpendicular to each other. In some cases, during the deposition: (a) a first actuator, out of the set of actuators, actuates the nozzle to move along a horizontal axis; and (b) a second actuator, out of the set of actuators, actuates the build platform to rotate. In some cases: (a) during the deposition, the build platform is positioned inside an annealing kiln; and (b) after the deposition, the annealing kiln anneals extruded glass material. In some cases, extrusion of the molten glass material through the nozzle is actuated by gravitational force and is not actuated by any other net mechanical force. In some cases, during the deposition: (a) the nozzle is stationary relative to a wall of the annealing kiln; and (b) at least one actuator, out of the set of actuators, actuates the build platform to cause the build platform to move relative to the nozzle and the wall. In some cases: (a) an exit portion of the nozzle surrounds or is adjacent to an exit orifice of the nozzle; (b) the method further comprises cooling the exit portion of the nozzle by causing fluid to flow through a region that adjoins the exit portion; and (c) the fluid is cooler than molten glass material exiting the exit orifice. Each of the cases described above in this paragraph is an example of the method described in the first sentence of this paragraph, and is also an example of an embodiment of this invention that may be combined with other embodiments of this invention.
In another aspect, this invention is an apparatus comprising, in combination: (a) a build platform; (b) one or more heating elements for heating of glass material, such that the glass material becomes or remains molten; (c) a nozzle for deposition of the molten glass material, such that the molten glass material is extruded through the nozzle to form an object that rests on the build platform; (d) a set of actuators; and (e) one or more computers for controlling the deposition, such that, during at least a portion of the deposition (i) the molten glass material is deposited layer-by-layer; and (ii) the one or more computers control where in each layer the molten glass material is deposited, by causing the set of actuators to actuate movement of one or both of the nozzle and build platform. In some cases, at least one actuator, out of the set of actuators, is configured to actuate the nozzle to move along at least one horizontal axis. In some cases: (a) a first actuator, out of the set of actuators, is configured to actuate the nozzle and at least some of the heating elements to move parallel to a first horizontal axis; and (b) a second actuator, out of the set of actuators, is configured to actuate the nozzle and at least some of the heating elements to move parallel to a second horizontal axis, the first and second horizontal axes being perpendicular to each other. In some cases: (a) a first actuator, out of the set of actuators, is configured to actuate the nozzle to move parallel to a horizontal axis; and (b) a second actuator, out of the set of actuators, is configured to actuate the build platform to rotate. In some cases: (a) the build platform is positioned inside a kiln; and (b) the kiln is configured to anneal extruded glass material. In some cases, the apparatus includes a valve for controlling flow of molten glass material through the nozzle. In some cases: (a) the nozzle is stationary relative to a wall of the kiln; and (b) at least one actuator, out of the set of actuators, is configured to actuate the build platform such that the build platform moves relative to the nozzle and the wall. In some cases: (a) an exit portion of the nozzle surrounds or is adjacent to an exit orifice of the nozzle; and (b) the apparatus further comprises one or more tubes or cavities adjacent to the exit portion, which tubes or cavities are configured to cool the exit portion when fluid cooler than the molten glass material flows through the tubes or cavities. Each of the cases described above in this paragraph is an example of the apparatus described in the first sentence of this paragraph, and is also an example of an embodiment of this invention that may be combined with other embodiments of this invention.
In another aspect, this invention is an apparatus comprising: (a) heating elements for heating glass material, such that the glass material becomes or remains molten; (b) a nozzle for extruding the molten glass material; (c) tubes or chambers that are adjacent to a tip of the nozzle; (d) a pump for pumping fluid through the tubes or chamber to cool the tip of the nozzle to a temperature that is less than temperature of the molten glass material; (e) a set of actuators; and (f) a set of computers that is programmed to control the set of actuators such that the set of actuators actuate movement of one or both of the nozzle and build platform during the extruding, such that extruded molten glass material forms an object in accordance with digital instructions accessed or generated by at least one computer, out of the set of computers. In some cases, the apparatus further comprises a kiln for annealing the molten glass material. In some cases: (a) a first actuator, out of the set of actuators, is configured to actuate the nozzle and at least some of the heating elements to move parallel to a first horizontal axis; and (b) a second actuator, out of the set of actuators, is configured to actuate the nozzle and at least some of the heating elements to move parallel to a second horizontal axis, the first and second horizontal axes being perpendicular to each other. In some cases: (a) a first actuator, out of the set of actuators, is configured to actuate the nozzle to move parallel to a horizontal axis; and (b) a second actuator, out of the set of actuators, is configured to actuate the build platform to rotate. Each of the cases described above in this paragraph is an example of the apparatus described in the first sentence of this paragraph, and is also an example of an embodiment of this invention that may be combined with other embodiments of this invention.
In another aspect, this invention comprises an article of manufacture that comprises an integral structure, which integral structure has multiple, separate internal cavities, such that each of the cavities has a volume of at least 40 milliliters and is entirely enclosed by the glass material. In some cases, the integral structure includes layers of optically transparent glass material, such that adjacent layers partially merge into each other. In some cases, the integral structure further comprises an elongated protuberance, which protuberance: (a) is located on an exterior surface of the structure; and (b) comprises a solidified drip of glass material. In some cases, the protuberance is elongated along an axis that is aligned vertically. Each of the cases described above in this paragraph is an example of the article of manufacture described in the first sentence of this paragraph, and is also an example of an embodiment of this invention that may be combined with other embodiments of this invention.
In another aspect, this invention comprises an article of manufacture that comprises a unitary structure, wherein: (a) the unitary structure includes a spiral filament of optically transparent glass material; (b) the spiral filament forms multiple layers, one layer on top of another, which layers are part of the spiral filament and partially merge into each other vertically; and (c) the spiral filament has an elongated cavity that is entirely enclosed by the filament and extends for at least half of a revolution of a spiral formed by the filament. The article of manufacture described in the first sentence of this paragraph may be combined with other embodiments of this invention.
The above description (including without limitation any attached drawings and figures) describes illustrative implementations of the invention. However, the invention may be implemented in other ways. The methods and apparatus which are described above are merely illustrative applications of the principles of the invention. Other arrangements, methods, modifications, and substitutions by one of ordinary skill in the art are therefore also within the scope of the present invention. Numerous modifications may be made by those skilled in the art without departing from the scope of the invention. Also, this invention includes without limitation each combination and permutation of one or more of the abovementioned implementations, embodiments and features.
This application is a continuation of U.S. patent application Ser. No. 15/365,577 filed Nov. 30, 2016, which is a continuation of U.S. patent application Ser. No. 14/697,564 filed Apr. 27, 2015, which claims the benefit of U.S. Provisional Application No. 61/984,137 filed Apr. 25, 2014.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2047173 | Bates | Jul 1936 | A |
| 3293017 | Jenkins | Dec 1966 | A |
| 4682995 | Clasen | Jul 1987 | A |
| 4684385 | Clasen | Aug 1987 | A |
| 4816051 | Clasen | Mar 1989 | A |
| 4888036 | Clasen | Dec 1989 | A |
| 5121329 | Crump | Jun 1992 | A |
| 5402351 | Batchelder et al. | Mar 1995 | A |
| 5741557 | Corbin et al. | Apr 1998 | A |
| 6722872 | Swanson et al. | Apr 2004 | B1 |
| 8070473 | Kozlak | Dec 2011 | B2 |
| 8215371 | Batchelder | Jul 2012 | B2 |
| 20020002843 | Gotoh et al. | Jan 2002 | A1 |
| 20090314391 | Crump et al. | Dec 2009 | A1 |
| 20130000549 | Hartmann | Jan 2013 | A1 |
| 20130306198 | Prest et al. | Nov 2013 | A1 |
| 20140265034 | Dudley | Sep 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 103073174 | May 2013 | CN |
| 103395973 | Nov 2013 | CN |
| 103524022 | Jan 2014 | CN |
| 203419844 | Feb 2014 | CN |
| 203513482 | Apr 2014 | CN |
| Entry |
|---|
| Fateri, M., et al., 2012, On-Site Additive Manufacturing by Selective Laser Melting of Composite Objects. Concepts and Approaches for Mars Exploration, held Jun. 12-14, 2012 in Houston, Texas. LPI Contribution No. 1679, id.4368. |
| Joris, Apr. 14, 2010, You can now 3D print in glass with Shapeways. Posted on Apr. 14, 2010 on Shapeways, What's Hot. Accessed on Jun. 3, 2015 at http://www.shapeways.com/blog/archives/401-you-can-now-3D-print-in-glass-with-Shapeways.html. |
| Klein, S., et al., 2012, 3D Printing of Transparent Glass. HP Laboratories, HPL-2012-198. |
| Luo, J., et al., Oct. 24, 2014, Additive Manufacturing of Glass. Journal of Manufacturing Science and Engineering, vol. 136, Issue 6, 061024, six pages (Oct. 24, 2014). |
| Author Unknown, 2005, The Glass Transition. Polymer Science Learning Center, Department of Polymer Science, The University of Southern Mississippi, 2005. Accessed on Jun. 3, 2015 at http://pslc.ws/macrog/tg.htm. |
| Trevarthan, et al., 2012, Molten Glass. RepRap Forum, Dec. 21, 2012. Accessed on Jun. 3, 2015 at http://forums.reprap.org/read.php?1,172516,172520. |
| Ganter, et al., Vitraglyphic—3D Printing in Glass. Date: Jun. 2010 or earlier. Accessed on Jun. 3, 2015 at http://depts.washington.edu/open3dp/2009/10/vitraglyphic-3d-printing-in-glass/. |
| Whisnant, D., 2000, Polymer Chemistry the Glass Transition. Last updated Jul. 11, 2000. Accessed on Jun. 3, 2015 at http://faculty.uscupstate.edu/llever/Polymer%20Resources/GlassTrans.htm. |
| Number | Date | Country | |
|---|---|---|---|
| 20180148364 A1 | May 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61984137 | Apr 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15365577 | Nov 2016 | US |
| Child | 15878167 | US | |
| Parent | 14697564 | Apr 2015 | US |
| Child | 15365577 | US |