The present disclosure relates in general to wind turbine rotor blades, and more particularly to methods for joining blade components of rotor blades using printed grid structures.
Wind power is considered one of the cleanest, most environmentally friendly energy sources presently available, and wind turbines have gained increased attention in this regard. A modern wind turbine typically includes a tower, a generator, a gearbox, a nacelle, and one or more rotor blades. The rotor blades capture kinetic energy of wind using known foil principles. The rotor blades transmit the kinetic energy in the form of rotational energy so as to turn a shaft coupling the rotor blades to a gearbox, or if a gearbox is not used, directly to the generator. The generator then converts the mechanical energy to electrical energy that may be deployed to a utility grid.
The rotor blades generally include a suction side shell and a pressure side shell typically formed using molding processes that are bonded together at bond lines along the leading and trailing edges of the blade. Further, the pressure and suction shells are relatively lightweight and have structural properties (e.g., stiffness, buckling resistance and strength) which are not configured to withstand the bending moments and other loads exerted on the rotor blade during operation. Thus, to increase the stiffness, buckling resistance and strength of the rotor blade, the body shell is typically reinforced using one or more structural components (e.g. opposing spar caps with a shear web configured therebetween) that engage the inner pressure and suction side surfaces of the shell halves.
In addition, conventional rotor blades require a substantial amount of bond paste to provide structure at various blade joints (e.g. at the leading or trailing edges of the rotor blade) to prevent local buckling of the suction and pressure side shells. Due to the complex geometry near these joint areas, it is often difficult to provide this structure in other ways that would be lighter than bond paste. Thus, conventional rotor blades typically utilize excess paste for the structure needed at the joints. Such excess paste, however, is expensive, heavy, and can limit the types of adhesives that can be used. For example, heavy and thick adhesive sections containing fast curing adhesives with high exothermic reactions can generate excess heat and damage the surrounding materials, thereby creating safety hazards.
In view of the foregoing, the art is continually seeking improved methods for joining blade components of rotor blades that use less adhesives.
Aspects and advantages of the invention will be set forth in part in the following description, or may be obvious from the description, or may be learned through practice of the invention.
In one aspect, the present disclosure is directed to a method for joining a first blade component and a second blade component of a rotor blade together. The method includes printing and depositing, via a computer numeric control (CNC) device, at least one three-dimensional (3-D) grid structure at a first joint area of the rotor blade. The first joint area contains the first blade component interfacing with the second blade component. The method also includes providing an adhesive at the first joint area and contacting at least a portion of the grid structure. Further, the method includes securing the first blade component and the second blade component together at the first joint area via the adhesive.
In one embodiment, the adhesive may at least partially fill the grid structure. In another embodiment, the first and second blade components may include first and second outer surfaces of the rotor blade, a shear web, and/or a spar cap. Thus, in one embodiment, the method may include placing the first outer surface into a mold of the rotor blade, printing and depositing, via the CNC device, the grid structure(s) onto an inner surface of the first outer surface at the first joint area, wherein the grid structure bonds to the first outer surface as the grid structure is being deposited, placing the second outer surface atop the first outer surface, and securing the first and second outer surfaces together via the adhesive.
In further embodiments, the first joint area may include a spar cap/shear web connection, a spar cap/blade shell connection, and/or a blade shell/blade shell connection. More specifically, in certain embodiments, the blade shell/blade shell connection may include a trailing edge and/or a leading edge of the rotor blade.
In additional embodiments, the method may include printing and depositing, via the CNC device, a first grid structure onto the inner surface of the first outer surface at the first joint area and a second grid structure onto the inner surface of the first outer surface at a different, second joint area. In such embodiments, the method may also include printing and depositing, via the CNC device, the first grid structure onto the inner surface of the first outer surface and spaced apart from the trailing edge of the rotor blade to provide a first gap. In addition, in several embodiments, the method may further include printing and depositing, via the CNC device, the second grid structure onto the inner surface of the first outer surface and spaced apart from the leading edge of the rotor blade to provide a second gap.
In another embodiment, the method may include filling, at least in part, at least one of the first gap or the second gap with the adhesive. In addition to the adhesive, in certain embodiments, the method may also include forming at least a portion of the grid structure of a foaming agent.
In still further embodiments, the method may include selectively applying cooling air to the grid structure during printing and depositing. In yet another embodiment, the method may also include printing and depositing, via the CNC device, one or more alignment structures into the at least one grid structure.
In additional embodiments, the grid structure(s) may contact the inner surface of the first outer surface and an inner surface of the second outer surface. Thus, in certain embodiments, the grid structure(s) may include a tapered chord-wise cross-section.
In another aspect, the present disclosure is directed to a joint area of a rotor blade of a wind turbine. The joint area includes a first blade component, a second blade component interfacing with the first blade component at a joint, at least one three-dimensional (3-D) grid structure positioned between the first and second blade components adjacent to the joint, and an adhesive provided between the grid structure and the first and second blade components.
In one embodiment, the first and second blade components of the joint area may include first and second outer surfaces of the rotor blade, a shear web, or a spar cap. In another embodiment, the grid structure(s) may be formed, at least in part, via additive manufacturing. Alternatively, or in addition, the grid structure(s) may be formed, at least in part, of a pre-fabricated honeycomb material. It should be understood that the joint area may further include any of the additional features as described herein.
In yet another aspect, the present disclosure is directed to a method for securing a blade add-on component to a rotor blade. The method includes printing and depositing, via a computer numeric control (CNC) device, at least one three-dimensional (3-D) grid structure to form the blade add-on component. The method also includes placing the blade add-on component onto or within the rotor blade. Further, the method includes providing an adhesive to at least partially fill the grid structure. Moreover, the method includes securing the blade add-on component to the rotor blade via the adhesive.
In one embodiment, the blade add-on component may correspond to a reinforcement structure for a leading edge or a trailing edge, a flatback airfoil corner, or a tip extension. It should be understood that the method may further include any of the additional features and/or steps as described herein.
These and other features, aspects and advantages of the present invention will become better understood with reference to the following description and appended claims. The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth in the specification, which makes reference to the appended figures, in which:
Reference now will be made in detail to embodiments of the invention, one or more examples of which are illustrated in the drawings. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment can be used with another embodiment to yield a still further embodiment. Thus, it is intended that the present invention covers such modifications and variations as come within the scope of the appended claims and their equivalents.
Generally, the present disclosure is directed to methods for manufacturing grid structures for wind turbine rotor blades using automated deposition of materials via technologies such as 3-D Printing, additive manufacturing, automated fiber deposition, as well as other techniques that utilize CNC control and multiple degrees of freedom to deposit material. As such, the grid structures of the present disclosure are useful for reinforcing a joint area of the rotor blade (i.e. by providing buckling resistance at the joint area). More specifically, the printed structures described herein may contain one or more gaps and may be shaped to fill the space between two laminate surfaces that require bonding. The tight gaps within the printed structure allow for a significantly reduced amount of adhesive to be used and allow the adhesive to flow between the gaps of the printed structure upon closing. Thus, the adhesive flow between the gaps and the reduced amount of adhesive needed substantially reduces the hydraulic pressure needed to close the joint. In addition, the adhesive can form a mechanical lock when cured into the structure to increase bonding strength and reliability compared to an adhesive-only bond. As such, joints of the present disclosure provide a net weight savings as the bulk of the printed structure gaps remains unfilled after closing of the joint.
In addition, the grid structures described herein allow for faster curing adhesives to be used and reduce the overall process cycle time and weight. Moreover, the grid structures of the present disclosure allow for non-destructive testing (NDT) inspection, as the joint areas no longer require foam. Further, the grid structures of the present disclosure can be directly printed to thermoplastic fiberglass skins, thereby providing a more ideal bonding surface. The printed structures of the present disclosure may also simultaneously be used to align components during the bonding process and can be used to fill difficult gaps, such as the space created when using flat pultrusions in spar caps against a curved airfoil surface.
Referring now to the drawings,
Referring now to
The thermoplastic rotor blade components and/or materials as described herein generally encompass a plastic material or polymer that is reversible in nature. For example, thermoplastic materials typically become pliable or moldable when heated to a certain temperature and returns to a more rigid state upon cooling. Further, thermoplastic materials may include amorphous thermoplastic materials and/or semi-crystalline thermoplastic materials. For example, some amorphous thermoplastic materials may generally include, but are not limited to, styrenes, vinyls, cellulosics, polyesters, acrylics, polysulphones, and/or imides. More specifically, exemplary amorphous thermoplastic materials may include polystyrene, acrylonitrile butadiene styrene (ABS), polymethyl methacrylate (PMMA), glycolised polyethylene terephthalate (PET-G), polycarbonate, polyvinyl acetate, amorphous polyamide, polyvinyl chlorides (PVC), polyvinylidene chloride, polyurethane, or any other suitable amorphous thermoplastic material. In addition, exemplary semi-crystalline thermoplastic materials may generally include, but are not limited to polyolefins, polyamides, fluoropolymer, ethyl-methyl acrylate, polyesters, polycarbonates, and/or acetals. More specifically, exemplary semi-crystalline thermoplastic materials may include polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polypropylene, polyphenyl sulfide, polyethylene, polyamide (nylon), polyetherketone, or any other suitable semi-crystalline thermoplastic material.
Further, the thermoset components and/or materials as described herein generally encompass a plastic material or polymer that is non-reversible in nature. For example, thermoset materials, once cured, cannot be easily remolded or returned to a liquid state. As such, after initial forming, thermoset materials are generally resistant to heat, corrosion, and/or creep. Example thermoset materials may generally include, but are not limited to, some polyesters, some polyurethanes, esters, epoxies, or any other suitable thermoset material.
In addition, as mentioned, the thermoplastic and/or the thermoset material as described herein may optionally be reinforced with a fiber material, including but not limited to glass fibers, carbon fibers, polymer fibers, wood fibers, bamboo fibers, ceramic fibers, nanofibers, metal fibers, or similar or combinations thereof. In addition, the direction of the fibers may include multi-axial, unidirectional, biaxial, triaxial, or any other another suitable direction and/or combinations thereof. Further, the fiber content may vary depending on the stiffness required in the corresponding blade component, the region or location of the blade component in the rotor blade 16, and/or the desired weldability of the component.
More specifically, as shown, the main blade structure 15 may include any one of or a combination of the following: a pre-formed blade root section 20, a pre-formed blade tip section 22, one or more one or more continuous spar caps 48, 50, 51, 53, one or more shear webs 35 (
Referring particularly to
More specifically, as shown in
In specific embodiments, as shown in
In addition, the spar caps 48, 50, 51, 53 may be constructed of any suitable materials, e.g. a thermoplastic or thermoset material or combinations thereof. Further, the spar caps 48, 50, 51, 53 may be pultruded from thermoplastic or thermoset resins. As used herein, the terms “pultruded,” “pultrusions,” or similar generally encompass reinforced materials (e.g. fibers or woven or braided strands) that are impregnated with a resin and pulled through a stationary die such that the resin cures or undergoes polymerization. As such, the process of manufacturing pultruded members is typically characterized by a continuous process of composite materials that produces composite parts having a constant cross-section. Thus, the pre-cured composite materials may include pultrusions constructed of reinforced thermoset or thermoplastic materials. Further, the spar caps 48, 50, 51, 53 may be formed of the same pre-cured composites or different pre-cured composites. In addition, the pultruded components may be produced from rovings, which generally encompass long and narrow bundles of fibers that are not combined until joined by a cured resin.
Referring to
Referring now to
As used herein, 3-D printing is generally understood to encompass processes used to synthesize three-dimensional objects in which successive layers of material are formed under computer control to create the objects. As such, objects of almost any size and/or shape can be produced from digital model data. It should further be understood that the methods of the present disclosure are not limited to 3-D printing, but rather, may also encompass more than three degrees of freedom such that the printing techniques are not limited to printing stacked two-dimensional layers, but are also capable of printing curved shapes.
Referring particularly to
Further, as shown, the method of the present disclosure further includes forming one or more fiber-reinforced outer skin surfaces 56 in the mold 58 of the rotor blade 16. In certain embodiments, the outer skin surface(s) 56 (which form the pressure and/or suction side surfaces 31, 33) may include one or more continuous, multi-axial (e.g. biaxial) fiber-reinforced thermoplastic or thermoset outer skins. Further, in particular embodiments, the method of forming the fiber-reinforced outer skin surfaces 56 may include at least one of injection molding, 3-D printing, 2-D pultrusion, 3-D pultrusion, thermoforming, vacuum forming, pressure forming, bladder forming, automated fiber deposition, automated fiber tape deposition, or vacuum infusion.
For example, in one embodiment, a thermoset material may be infused into the fiber material on the mold 58 to form the outer skin surface 56 using vacuum infusion. As such, the vacuum bag is removed after curing and the grid structures 66, 70 described herein can then be printed onto the inner surface of the outer skin surfaces 56. Alternatively, the vacuum bag may be left in place after curing. In such embodiments, the vacuum bag material can be chosen such that the material would not easily release from the cured thermoset fiber material. Such materials, for example, may include a thermoplastic material such as polymethyl methacrylate (PMMA) or polycarbonate film. Thus, the thermoplastic film that is left in place allows for bonding of thermoplastic grid structures 66 to the thermoset skins with the film in between.
In still further embodiments, the outer skin surface(s) 56 may be formed of a reinforced thermoplastic resin with the grid structures 66, 70 being formed of a thermoset-based resin with optional fiber reinforcement. In such embodiments, depending on the thermoset chemistry involved—the grid structures 66, 70 may be printed to the outer skin surfaces 56 while the surfaces 56 are still hot, warm, partially cooled, or completely cooled.
In addition, the outer skin surfaces 56 may be further treated to promote bonding between the outer skin surfaces s56 and the grid structure 66, 70. More specifically, in certain embodiments, the outer skin surfaces 56 may be treated using flame treating, plasma treating, chemical treating, chemical etching, mechanical abrading, embossing, elevating a temperature of at least areas to be printed on the outer skin surfaces 56, and/or any other suitable treatment method to promote said bonding. In additional embodiments, the method may include forming the outer skin surfaces 56 with more (or even less) matrix resin material on the inside surface to promote said bonding. In additional embodiments, the method may include varying the outer skin thickness and/or fiber content, as well as the fiber orientation.
In addition, as shown, the outer skin surface(s) 56 of the rotor blade 16 may be curved. In such embodiments, the method may include forming the curvature of the outer skin surfaces 56. Such forming may include providing one or more generally flat fiber-reinforced outer skin surfaces, forcing the outer skin surfaces 56 into a desired shape corresponding to a desired contour, and maintaining the outer skin surfaces 56 in the desired shape during printing and depositing. As such, the outer skin surfaces 56 generally retain their desired shape when the outer skin surfaces 56 and the grid structures 66, 70 printed thereto are released. In addition, the CNC device 60 may be adapted to include a tooling path that follows the contour of the rotor blade 16.
Thus, as shown in
It should be understood that any suitable shape of grid structures 66, 70 described herein can be printed and deposited as desired. As such, in certain embodiments, the grid structures 66, 70 may bond to the outer skin(s) 56 as the grid structures 66, 70 are being deposited, which reduces the amount of adhesive and/or curing time needed for the first and second joint areas 68, 72, respectively. For example, as shown in
For example, in one embodiment, the CNC device 60 is configured to print and deposit the grid structures 66, 70 after the formed skin surface 56 reaches a desired state that enables bonding of the grid structures 66, 70 thereto, i.e. based on one or more parameters of temperature, time, and/or hardness. Therefore, in certain embodiments, wherein the skin surfaces 56 and grid structures 66, 70 are formed of a thermoplastic matrix, the CNC device 60 may immediately print the grid structures 66, 70 thereto as the forming temperature of the skin surface(s) 56 and the desired printing temperature to enable thermoplastic welding/bonding can be the same).
More specifically, in particular embodiments, before the skin surface(s) 56 have cooled from forming, (i.e. while the skins are still hot or warm), the CNC device 60 is configured to print and deposit the grid structures 66, 70 onto the inner surface of the outer skin surfaces 56. For example, in one embodiment, the CNC device 60 is configured to print and deposit the grid structures 66, 70 onto the inner surface of the outer skin surfaces 56 before the surfaces 56 have completely cooled. In addition, in another embodiment, the CNC device 60 is configured to print and deposit the grid structures 66, 70 onto the inner surface of the outer skin surfaces 56 when the surfaces 56 have partially cooled. Thus, suitable materials for the grid structures 66, 70 and the outer skin surfaces 56 can be chosen such that the grid structures 66, 70 bonds to the outer skin surfaces 56 during deposition. Accordingly, the grid structures 66, 70 described herein may be printed using the same materials or different materials.
It should be understood that the grid structures 66, 70 of the present disclosure may include varying shapes and/or designs (e.g. materials, width, height, thickness, shapes, etc., or combinations thereof). As such, the grid structures 66, 70 may define any suitable shape so as to form any suitable structure that can be used at any joint connection within the rotor blade 16 such that adhesives can be reduced in such joints. Thus, the CNC device 60 can be designed having one or more extruders 62 that generate any suitable thickness or width so as to disperse a desired amount of resin material to create the grid structures 66, 70 with varying heights and/or thicknesses. For example, many rotor blade joints include tight angles and/or tapered cross-sections that are conventionally filled with adhesives. Thus, as shown particularly in
In yet another embodiment, the CNC device 60 may also print and deposit one or more alignment structures 82 into the grid structure(s) 66, 70. For example, as shown in
When the grid structures 66, 70 are printed using extruded thermoplastics with tighter gaps, the structures 66, 70 can retain heat as the printed structure gets taller. Additional heat can be further retained as the shape of many rotor blade joints are tapered or angled, thereby requiring grid structures 66, 70 within a tapered or angled cross-section. As such, the printed layer times get shorter as the part is built. As a result, taller structures and those portions with shorter layer times (i.e. the time it takes to print a layer before starting the next layer) can begin to sag and puddle as there is not enough cooling time to sufficiently solidify the previous layer. Thus, the method of the present disclosure is configured to slow down the print speeds as needed, alter the formulation of the resin system to use a faster solidifying resin matrix (e.g. a more semi crystalline/less amorphous formulation), and/or selectively apply cooling air to the grid structures 66, 70 during printing and depositing. For example, in one embodiment, as shown in
In addition to additive manufacturing, the grid structures 66, 70 of the present disclosure may also be formed, at least in part, of one or more pre-fabricated sections of a honeycomb material. For example, in one embodiment, honeycomb prefabricated material can be CNC machined to fit the desired shape needed at the joint and adhesive can be applied to both inner surfaces of the outer skin surfaces 56 to bond the honeycomb material in place. In another embodiment, a thermoplastic honeycomb material may be crushed into shape under pressure and/or heated along with adhesives.
After the grid structures 66, 70 are printed on the outer skin surface 56, as shown in
In such embodiments, as shown in
Thus, the method may also include filling, at least in part, the first and/or second gaps 76, 78 with the adhesive 74. For example, as shown in
In another embodiment, the method may include forming at least a portion of the grid structure 62 of a foaming agent 80. For example, as shown in
The methods of the present disclosure can also be useful for certain types of blade add-on components, where certain aerodynamic features are desired to be added to the exterior surface of a rotor blade either after production and/or to existing rotor blades in the field. Thus, referring now to
Examples of the blade add-on component may include flatback airfoil corner sections, tip extensions (i.e. a grid structure used to fill thin sections between a sock tip and the rotor blade 16, and allow for bonding using this grid technique), or a reinforcement structure for a leading edge or a trailing edge.
This written description uses examples to disclose the invention, including the best mode, and to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they include structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims.