Patent Application
20120096989
The invention relates to alloyed zinc powders, a key component for the manufacture of the anode of alkaline batteries.
Battery manufacturers are confronted with the well-known problem of the formation and accumulation of hydrogen gas within the battery, which is caused by the corrosion of the zinc powder by the alkaline electrolyte. Generation of gas increases the internal pressure in the cell. Safety systems are provided to prevent the explosion of the battery, but the risk of damage due to electrolyte leakage remains. Gassing may occur before use of the battery, i.e. during its shelf life; it typically also occurs after partial discharge, a phenomenon further on referred to as “PD gassing.”
The capacity of a battery depends on the capability of the zinc powder to generate zinc ions and electrons according to:
Zn+2(OH)−→Zn(OH)2+2e− (1).
However, if the reaction medium is depleted in OH-, an irreversible reaction is induced, leading to the precipitation of ZnO on the surface of the zinc particles, passivating their surface. The end result is that part of the metallic zinc will not be available for the electrochemical reaction (1), thereby limiting the effective battery capacity to a fraction of its theoretical value. This phenomenon of passivation occurs mainly at high discharge rates, i.e. when the zinc particles release a high flux of zinc ions, while only a limited amount of hydroxide ions is available at the reaction sites.
Several patents, such as U.S. Pat. No. 6,284,410, claim good high drain discharge performances by using a fine zinc powder, as such, or in a blend with a coarse zinc powder. The high specific surface of the fine powder tends to enhance high drain discharge, but it unfortunately also limits the shelf life and increases the PD gassing.
The use of large flaky particles also tends to improve the high drain service and the shock resistance of the alkaline battery, as mentioned in U.S. Pat. No. 6,022,639. Other shapes like spheres, teardrops and strands were studied in WO 2004/012886. Unfortunately, these shapes greatly increase the gel viscosity, which leads to processing problems during the manufacture of batteries.
Low gassing, good process ability and high drain capability thus create conflicting demands. It is the aim of the present invention to solve this conflict.
To this end, a new alloyed zinc powder for alkaline batteries comprising particles pierced with at least one hole in an amount of more than, either one or more, of: 10% by count in the sieving fraction 250 to 425 μm; and 3% by count in the sieving fraction 150 to 250 μm; and 2% by count in the sieving fraction 105 to 150 μm is presented. The zinc alloy powder in the sieving fraction 250 to 425 μm preferably comprises particles pierced with at least one hole in an amount of more than 20% by count, more preferably more than 30% by count, and still more preferably at least 31% by count, and even at least 36% by count. The above mentioned ‘particles pierced with at least one hole’ will in the remainder of the text be referred to as ‘pierced particles.’
In a more specific embodiment, the powder comprises one or more of bismuth, indium and aluminum as alloying elements. Preferably, the alloy consists of either of: 0.001-0.05% by weight aluminum and 0.001-2% indium; 0.002-0.2% by weight bismuth and 0.001-2% indium; 0.002-0.2% by weight bismuth, 0.001-2% indium and 0.001-0.05% aluminum; and 0.002-0.2% by weight bismuth; and, optionally, up to 0.5% by weight of either one or both of lead and calcium, the remainder being zinc. Furthermore, a zinc powder consisting of 0.005-0.05% by weight Pb, the remainder being zinc, is also suitable. Said zinc may, as a matter of fact, also contain unavoidable impurities, such as those allowed in so-called Special High Grade (SHG) zinc.
As a further embodiment, this invention concerns alkaline batteries comprising an alloyed zinc powder according to anyone of the above criteria.
Alloyed zinc powders suitable for alkaline batteries can be produced by centrifugal atomization (CA), a process described in EP 1155464B1. Liquid zinc is hereby poured onto a disk, rotating rapidly in a protective oxygen-depleted atmosphere. This process results in the production of classical CA powders. For obtaining pierced particles according to this invention, it is however necessary to cool the atomization atmosphere to a temperature of less than 110° C., and preferable at a temperature of less than 100° C. This can be done by applying forced air cooling on the external walls of the atomization chamber. Advantageously, the atomization is performed in an atmosphere having an oxygen content of less than 8% by volume, and more preferably of more than 4% by volume.
Pierced particles allow for the use of coarser powders without penalizing the high drain capacity of the battery, while preserving the shelf life, limiting the PD gassing, and ensuring good processing capabilities. Conversely, pierced particles enhance the high drain behavior compared to classical powders with the same particle size distribution.
Hydroxide ions are produced at the cathode of the alkaline battery according to the reaction:
MnO2+H2O+e−→MnOOH+OH−.
As explained above, these hydroxide ions are needed at the zinc at the anode, to avoid the passivating the surface of the zinc particles. It is assumed that pierced particles improve the diffusion of the hydroxide ion from cathode to anode, enhancing the so-called chemical homogeneity of the alkaline battery. This important property can be evaluated by a fast paced intermittent discharge test, where the battery can rest and homogenize for only a short period of time between high current discharge bursts.
Pierced particles can be detected and counted by direct visual observation under a microscope, or by using a shape analyzer like the ALPAGA® system of Occhio SA, Belgium.
The zinc powder of the invention shows particles pierced with at least one hole. The general shape of the zinc powder particle is typically a microscopic flake, which can e.g. be curved, hollow or cuplike.
In metal melt atomization, some authors, like A. J. Yule and J. J. Dunkley in the book “Atomization of melts for Powder Production and Spray Deposition”, pp. 15-46, Clarendon Press, Oxford, 1994, refer to the possible existence of a atomization in two steps. The primary atomization is the formation of a droplet from the liquid metal. The secondary atomization is the further atomization of this droplet by air friction: the high relative velocity breaks up the droplet into smaller particles. This phenomenon is illustrated in
The process of the invention consists in applying proper atomization conditions to freeze the zinc particles early during the secondary atomization step in order to obtain a substantial fraction of pierced particles. This implies means to cool the atomization atmosphere.
Alloyed zinc powders were produced by centrifugal atomization: liquid zinc alloy at 480° C. was hereto poured onto a disk of 170 mm diameter rotating at 13000 rpm in a protective, oxygen-depleted atmosphere.
Table 1 compares the percentage by count of pierced particles observed in each sieving class in a classical CA zinc powder, i.e., without temperature control, to a powder produced according to the invention. Both powders were made using the same alloy consisting of zinc with 200 ppm In, 100 ppm Bi and 100 ppm Al. Both were atomized in an atmosphere containing 6.25% by volume of oxygen. The classical CA powder was manufactured without cooling the atomization atmosphere, resulting in an ambient temperature of about 160° C., whilst the powder according to the invention was manufactured with proper cooling, at 100° C. It is clear that the zinc powder according to the present invention has a much higher count of pierced particles, in particular in the coarser sieving fractions.
Electrochemical cells containing a cathode, an anode and a separator, as shown in
The alkaline batteries were tested in 2 high drain discharge tests:
a 1 A continuous drainage test, with cut off at 1.0 V; and
a 1 A intermittent drainage test with 10 seconds of discharge followed by 50 seconds of rest, with cut off at 0.9 V.
The total discharge times, normalized at 100% using the classical CA powder as a reference, are shown in Table 2.
These experiments confirm that the presence of pierced particles leads to very good results in high drain capacity, in comparison to a classical CA powder made with the same alloy. An oxygen content of more than 4% by volume is advantageous; it is however preferred to remain below 8%, as gassing of the powders otherwise tends to increase to an unacceptable level.
| Number | Date | Country | Kind |
|---|---|---|---|
| 05076173.3 | May 2005 | EP | regional |
This application is a divisional of U.S. application Ser. No. 11/914,501, filed Apr. 18, 2008, which is a national stage application of PCT/EP2006/003657, filed Apr. 21, 2006, which claims priority to U.S. Provisional Application No. 60/683,317, filed May 23, 2005, and European Patent Application No. 050761732.3, filed May 19, 2005, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60683317 | May 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11914501 | Apr 2008 | US |
| Child | 13306071 | US |