Methods for preparation from carbonate precursors the compounds of lithium transition metals oxide

Abstract
A method for preparing lithium transitional metal oxides, comprises the steps of: preparing a carbonate precursor using the following substeps: forming a first aqueous solution containing a mixture of at least two of the ions of the following metal elements (“Men+”): cobalt (Co), nickel (Ni), and manganese (Mn); forming a second aqueous solution containing ions of CO32−; and mixing and reacting the first solution and the second solution to produce the carbonate precursor, Ni1-x-yCoxMnyCO3; and preparing the lithium transition metals oxide from the carbonate precursors using the following substeps: evenly mixing Li2CO3 and the carbonate precursor; calcinating the mixed material in high temperature; and cooling and pulverizing the calcinated material to obtain the lithium transition metal oxide, Li Ni1-x-yCoxMnyO2.
Description
CROSS REFERENCE

This application claims priority to a Chinese patent application entitled “Methods for Preparation from Carbonate Precursors the Compounds of Lithium Transition Metals Oxide” filed on Nov. 19, 2002, having a Chinese Patent Application No. 02151991.9.


FIELD OF INVENTION

This invention relates to methods for preparing compounds of lithium transitional metal oxide. In particular, it relates to methods for preparing carbonate precursors and, from the carbonate precursors, compounds of lithium transitional metal oxide that has excellent electrochemical properties.


BACKGROUND

Known commercialized lithium ion batteries use several types of transition metal oxide compounds such as lithium cobalt dioxide (LiCoO2), lithium nickel dioxide (LiNiO2), and lithium manganese dioxide (LiMn2O4) etc. as the material for the positive electrode. LiCoO2 is the most commonly used material. Although the overall properties of LiCoO2 are the best, its cost is high and, due to its scarcity, the cost is likely to rise even higher. Its supply could even dry up. Therefore, many countries are researching the use of at least two of the following transition metals: Cobalt (Co), Nickel (Ni), and Manganese (Mn) as the basic ingredient for compounds of lithium transition metal oxide to be used for electrodes in batteries. Representative relevant work includes: Reference 1: Zhaolin Lin et al. in J. Power Sources, 88-82 (1999) 416-419 which discloses the synthesizing method for the lithium transition oxide compound, Li Ni1-x-yCoxMnyO2; and Reference 2: Chinese Patent No. CN1271185A, Oct. 25, 2000, which discloses a method of preparation for an additive ingredient, LiCoO2, LiNiO2, and LiMn2O4.


The inventors of this invention found that, when compared with oxidized compounds prepared by thermally decomposing the mixture made by combining the salts or hydroxide compounds of transition metal elements such as cobalt, nickel, and manganese and with salt of lithium, the compounds prepared by the method described by Zhaolin, Lin, et al. in reference 1 have better distribution of grain diameter, density, and electrochemical capacity. However, in order to have said excellent properties, the range of the distribution of the diameter for the spherical intermediate products formed using method reported by Zhaolin, Lin, et al in reference 1, Ni1-x-yCoxMny(OH)2, has to be narrow. This can only occur by strictly controlling the precipitation conditions which is difficult to accomplish in practice. The method described in Chinese Patent No. CN1271185A (reference 2) spray mixes soluble salts, carbonates, or alkaline solutions of lithium and transition metals such as of cobalt, nickel, or manganese, and alkaline carbonates to obtain a crystal compound; then decompose thermally to obtain LiCoO2, LiNiO2, and LiMn2O4 as the additive ingredient. However, this method is not easy to implement as the Li2CO3 produced has a large solubility, and some of it is dissolved and removed during the rinsing process to remove the negative ions. This decreases the lithium content of the final product and results in the inability to obtain the amount calculated from the formulas of LiCoO2, LiNiO2, and LiMn2O4.


Due to the limitation of the prior art, it is therefore desirable to have novel and innovative methods for the preparation of compounds of lithium transitional metal oxide.


SUMMARY OF THE INVENTION

A method for preparation from carbonate precursors the compounds of lithium and transition metal oxides that includes first, the preparation of the carbonate precursors and then the preparation of the compounds of lithium transition metals oxide from the carbonate precursors.


The preparation of the carbonate precursors from transition metals nickel, cobalt, and manganese include the following steps: (1) Formulate a solution which combines a solution that contains a mixture of ions of cobalt, nickel, and manganese with another solution that contains CO32− ions; (2) Combine the two solutions together to react and form the carbonate precursor, Ni1-x-yCoxMnyCO3.


The preparation of the compounds of lithium transition metal compound with transitional metal nickel, cobalt, and manganese include the following steps: (1) Mix Li2CO3 with the Ni1-x-yCoxMnyCO3 precursor uniformly, calcine the mixture in air at 500-800° C. for 2 to 20 hours; (2) Cool and pulverize said calcined material; (3) Calcine again said pulverized calcined material in air at 700 to 950° C. for 2 to 30 hours; and (4) Cool, ballmill, and sift to obtain the compound of lithium transition metal oxide, LiNi1-x-yCoxMnyO2.


The LiNi0.4Co0.2Mn0.4CO3 that is prepared by the method of this invention has a narrow range of grain size distribution where the average grain size is 10 μm. A battery with an electrode made from this compound has a long cycle life and its electrical capacity reaching 150 mAh/g, long cycle life making it suitable of use in lithium ion batteries.





BRIEF DESCRIPTION OF THE FIGURES


FIG. 1 illustrates a photograph at 1000× magnification of an example of the Ni1-x-yCoxMnyCO3 precursor made from using a method of the present invention.



FIG. 2 is an example of the grain size distribution of the Ni1-x-yCoxMnyCO3 precursor made from using a method of the present invention.



FIG. 3 shows the electrical discharge curves of a lithium ion battery made with Li Ni00.4Co0.2Mn0.4O2 by using a method of the present invention.



FIG. 4 is a curve of the cycle characteristics of a lithium ion battery made with LiNi00.4Co0.2Mn0.4O2 by an example of an embodiment of the present invention.





DETAILED DESCRIPTION OF THE PRESENT INVENTION

One of the objectives of this invention is to eliminate the defects in prior art methods, and to provide a method for preparing a compound from the carbonate precursors of lithium transitional metal oxide with excellent electrochemical properties. If nickel, cobalt, and manganese are used as the transition metals, then the carbonate precursor is Ni1-x-yCoxMnyCO3 or its hydroxide carbonate compound. The final product LiNi1-x-yCoxMnyO2 is formed after the precursor is thermally decomposed with a lithium salt.


If nickel, cobalt, and manganese are chosen as the transition metals, one of the characteristics of this invention, a method to prepare from carbonate precursors the compounds of lithium transition metals oxide, include the following steps:


(1) Preparation of Carbonate Precursor

    • a. Formulate a solution with an aqueous solution (hereinafter referred to as “solution A”) containing a mixture of at least two of the ions of the following metal elements (hereinafter “Men+”): Cobalt (Co), Nickel (Ni), and manganese (Mn); and an aqueous solution containing ions of CO32− (hereinafter “solution B”);
    • b. Mix, stir, and react solution A and solution B for several hours to obtain the Ni1-x-yCoxMnyCO3 precursor (including its hydroxide carbonate compound);
    •  The specifications for reactions are: PH: 5 to 10, reaction temperature: 30to 90° C., stirring speed: 20 to 120 revolutions, per minute, and reaction time: 2 to 30 hours;


(2) Formation of Compound of Lithium Transition Metal Oxide

    • a. Mix said Li2CO3 and said Ni1-x-yCoxMnyCO3evenly. Then calcine in air at 500 to 800° C. for 2 to 20 hours;
    • b. Cool and pulverize of said material that has been calcined;
    • c. Again calcine said pulverized calcined material in air at 700 to 950° C. for 2 to 30 hours; and
    • d. Cool, ballmill, and sift to obtain the compound of lithium transition metal oxide Li Ni1-x-yCoxMnyO2.


In step (1), the preferred ion concentration of solution A is 0.1 to 3.0 mol/l. Men+ derives from at least one of the compounds from the following groups of materials: sulfates, nitrates, chlorides, acetates, other water soluble inorganic salts, and, other water soluble salts of organic acid.


In step (1), a further preference is for solution A to contain at least one type of additive ingredient from the group containing the ions of the following elements: Ca, Mg, Zn, Y, Ga, and In. The molar concentration of the additive component consists of 0 to 10% of the basic ingredients.


In step (1), the preferred Co32− ion concentration of solution B is 0.1 to 3.0 mol/l. The Co32− derives from at least one of the compounds from the following group of materials: Na2Co3, K2CO3, (NH4)2CO3, other aqueous solution of carbonates, and other compatible water soluble salt containing HCO3.


In step (1), the preferred PH level is adjusted by 1.0-6.0 mol/l of at least one aqueous solution (hereinafter “solution”) from the following groups: NaOH, KOH, and NH3, and other alkaline aqueous solutions. Solutions A, B, and C are combined in a reactor which is continuously stirred.


In step (1), a further preference is for solution A to be a combination of the solutions of the salts of cobalt, nickel, and manganese; solution B is a Na2CO3 solution; and solution C is a NaOH solution. The rate of flow is adjusted for the reaction to proceed at PH between 8 to 9 and the temperature between 30-90° C.


A further preference for step (1) is for solution A to be an aqueous solution of the combination of the sulfates salts of cobalt, nickel, and manganese; solution B to be (NH4)2CO3; and solution C be NH3.H2O solution. The rate of flow is adjusted for the reaction to proceed at the PH level between 8 to 9 and the temperature between 30 to 90° C.


A preference for step (2) is to first dry mix the Li2CO3 with said Ni1-x-yCoxMnyCO3, then wet mix with water or an organic solvent such as ethanol. The mixture is fully stirred and uniformly mixed. For step (2)a, calcine instead at 550 to 700° C., for 6 to 10 hours. For step (2)c, calcine instead at 750 to 900° C. for 10 to 25 hours.


This invention is a method for preparing compounds of lithium transitional metal oxide through the formation of the transition metal carbonate precursor. The preparation method described above is for a particular embodiment using nickel cobalt and manganese as the transition metal. If other transition metals are chosen instead of the three above, this above described embodiment can be tailored by using the appropriate initial ingredients and customizing the reaction specifications.


Implementation Details


If nickel, colbalt, and manganese are used as the transition metal, the following, together with the attached figures explains the methods of this invention in detail.


To form the precursor chemical Ni00.4Co0.2Mn0.4CO3, combine 1.0 mol/l of an aqueous solution of sulfate solution of a combination of cobalt, nickel, and manganese, 1.00 mol/l of aqueous solution of NaOH, and 1.0 mol/l of aqueous solution of NA2CO3 and add into reactor. The reaction temperature is kept at 45° C., and the PH level is kept between 8.5 to 9. The mixture is stirred at 40 revolutions per minute for the 10 hours of reaction time. The Ni00.4Co0.2Mn0.4CO3 precursor is obtained after filtering, washing, and drying. The scanning electron micrograph in FIG. (1) shows that this precursor is not spherically shaped, of even size and distributed and not clustered. FIG. (2) shows that the range of grain size distribution is narrow with average grain size as 10 μm.


To form the compound of lithium transition metal oxide, LiNi00.4Co0.2Mn0.4O2, a pre-determined amount of Ni00.4Co0.2Mn0.4CO3 precursor and Li2CO3 are added in. The dry materials are first mixed together, then water is added and the mixture is fully stirred to combine the ingredients uniformly before transferring to the reactor. The mixture is calcined at 550° for 6 hours. It is then cooled and pulverized. The material is then again calcined at 850° C. for 20 hours, then cooled, and ballmill to make LiNi00.4Co0.2Mn0.4O2. In the resulting product, the range of the distribution of grain size is narrow where the average grain size is 10 μm.


A customary method is used to make a lithium ion battery with said LiNi00.4Co0.2Mn0.4O2. The electrical properties of that battery are then compared with a battery made from Li2CoO2. In FIG. 3, Curve 2 and Curve 1 shows the discharge characteristics of an example of a battery made from an embodiment of this invention and a Li2CoO2 battery, respectively. The graphs show that the discharge capacity of the battery made from the compound of lithium transition metal oxide prepared from an embodiment of this invention is high, reaching to 720 minutes. The electrical capacity is calculated to be 150 mAh/g. Also, the midpoint voltage of the discharge platform is near that of the Li2CoO2 battery. Its cycling life also reaches 500 times. Since the amount of cobalt used is low but the properties of the battery is not reduced, the compounds of lithium transition metals oxide from carbonate precursors made from this invention is new, innovative, has distinctive characteristics, and has widespread application.


When compared with existing methods, this invention has the following advantages:

    • 1. The final product obtained by using this invention has a stable chemical composition and structure. Using the materials as stated, the Ni1-x-yCoxMnyCO3 precursor or the hydroxide compounds of carbonates is formed, which, when decompose thermally with Li2O3 can produce said oxidized compound, Li Ni1-x-yCoxMnyO2. This is possibly due to the fact that lithium is fully mobile and nickel, cobalt, and manganese can be rearranged.
    • 2. The technology is easy to control. Inlike the method used by Zhaolin, Lin, et al in reference 1, it does not require the strict control of reaction conditions. In Zhaolin, Lin et al., the intermediate bi-products, the hydroxides of compounds of nickel, cobalt and manganese, have to be spherically shaped in order for the final product to have good electrochemical properties. The controlling of conditions to achieve this result is difficult in practice.
    • 3. Strictly speaking, under alkaline conditions, the precursor product is the hydroxide salt of Ni1-x-yCoxMnyCO3. When this product decomposes at high temperature, since its outward appearance is not spherical, and carbonates and hydroxide chemicals have different decomposition characteristics, the decomposition matter has crystalline defects and a large number of minute internal holes. Therefore its excellent qualities include: a comparatively larger volume, a long useable lifespan, and a narrow range for the distribution of grain diameter.


While the present invention has been described with reference to certain preferred embodiments, it is to be understood that the present invention is not to be limited to such specific embodiments. Rather, it is the inventor's contention that the invention be understood and construed in its broadest meaning as reflected by the following claims. Thus, these claims are to be understood as incorporating and not only the preferred embodiment described herein but all those other and further alterations and modifications as would be apparent to those of ordinary skilled in the art.

Claims
  • 1. A method for preparing lithium transitional metal oxides, comprising the steps of: preparing a carbonate precursor using the following substeps: forming a first aqueous solution containing a mixture of at least two of the ions of the following metal elements (“Men+”): cobalt (Co), nickel (Ni), and manganese (Mn);forming a second aqueous solution containing ions of CO32−; andmixing and reacting said first solution and said second solution to produce the carbonate precursor, Ni1-x-yCoxMnyCO3; andpreparing said lithium transition metals oxide from said carbonate precursors using the following substeps: evenly mixing Li2CO3 and said carbonate precursor;calcinating the mixed material in high temperature; andcooling and pulverizing the calcinated material to obtain said lithium transition metal oxide, LiNi1-x-yCoxMnyO2.
  • 2. The method of claim 1 wherein the calcinating step is performed in air.
  • 3. The method of claim 1 further comprising a step after the cooling step, again calcinating said cooled and pulverized material in air at high temperature.
  • 4. The method of claim 3 further comprising a step after the again calcinating step, cooling, ballmilling, and sifting the again calcinated material to obtain the compound of lithium transition metal oxide, LiNi1-x-yCoxMnyO2.
  • 5. The method of claim 1 wherein the mixing and reacting substep is performed under the condition where the PH is between 5 to 10.
  • 6. The method of claim 1 wherein the mixing and reacting substep is performed under the condition where the reaction temperature is between 30 degrees to 90 degrees Celsius.
  • 7. The method of claim 1 wherein the mixing and reacting substep is performed under the condition where the stirring speed is between 20 to 120 revolutions per minute.
  • 8. The method of claim 1 wherein the mixing Li2CO3 substep is performed under the condition where the calcination is at 500 to 800° C.
  • 9. The method of claim 3 wherein the again calcinating step is performed under the condition where the calcination is at 700 to 950° C.
  • 10. The method of claim 1 wherein the ion concentration of the first solution is 0.1 to 3.0 mol/l.
  • 11. The method of claim 10 wherein the Men+derives from at least one of the compounds from the following groups of materials: sulfates, nitrates, chlorides, acetates, other water soluble inorganic salts, and, other water soluble salts of organic acid.
  • 12. The method of claim 1 wherein the first solution contains at least one type of additive ingredient from the group containing the ions of the following elements: Ca, Mg, Zn, Y, Ga, and In.
  • 13. The method of claim 12 wherein the molar concentration of the additive ingredient is of 0 to 10% of the overall solution.
  • 14. The method of claim 1 wherein the CO32− ion concentration of the second solution is 0.1 to 3.0 mol/l.
  • 15. The method of claim 1 further including a third solution in the preparation of the carbonate precursor wherein the third solution is a NaOH solution; and wherein the condition for preparing said carbonate precursor is where the flow rate is adjusted for the reaction to proceed at PH between 8 to 9 and the temperature is between 30-90° C.
  • 16. The method of claim 1 wherein said first solution is an aqueous solution of the combination of the sulfates salts of cobalt, nickel, and manganese; and said second solution is (NH4)2CO3; and further including a third solution that is a NH3.H2O solution in the preparation of said carbonate precursor where the flow rate is adjusted for the reaction to proceed at the PH level between 8 to 9 and the temperature is between 30 to 90° C.
  • 17. The method of claim 1 wherein the mixing the Li2CO3 step is to first wet mixing with an organic solvent such as ethanol.
  • 18. A method for preparing lithium transitional metal oxides, comprising the steps of: preparing a carbonate precursor using the following substeps: forming a first aqueous solution containing a mixture of at least two of the ions of the following metal elements (“Men+”): cobalt (Co), nickel (Ni), and manganese (Mn), wherein the ion concentration of the first solution is 0.1 to 3.0 mol/l; wherein the first solution contains at least one type of additive ingredient from the group containing the ions of the following elements: Ca, Mg, Zn, Y, Ga, and In; and wherein the molar concentration of the additive ingredient is of 0 to 10% of the overall solution;forming a second aqueous solution containing ions of CO32−; andmixing and reacting said first solution and said second solution to produce the carbonate precursor, Ni1-x-yCoxMnyCO3, under the conditions where the PH is between 5 to 10, the reaction temperature is between 30 degrees to 90 degrees Celsius, and the stirring speed is between 20 to 120 revolutions per minute; andpreparing said lithium transition metals oxide from said carbonate precursors using the following substeps: evenly mixing Li2CO3 and said carbonate precursor;calcinating the mixed material in air in high temperature of 500 to 800° C.; andcooling and pulverizing the calcinated material;again calcinating said cooled and pulverized material in air at high temperature of 700 to 950° C.; andcooling, ballmilling, and sifting the again calcinated material to obtain the compound of lithium transition metal oxide, Li Ni1-x-yCoxMnyO2.
  • 19. The method of claim 18 wherein the Men+derives from at least one of the compounds from the following groups of materials: sulfates, nitrates, chlorides, acetates, other water soluble inorganic salts, and, other water soluble salts of organic acid.
  • 20. The method of claim 18 wherein the CO32− ion concentration of the second solution is 0.1 to 3.0 mol/l.
Priority Claims (1)
Number Date Country Kind
02 1 51991 Nov 2002 CN national
US Referenced Citations (6)
Number Name Date Kind
5160712 Thackeray et al. Nov 1992 A
5631104 Zhong et al. May 1997 A
5783333 Mayer Jul 1998 A
6660432 Paulsen et al. Dec 2003 B2
20040179993 Dahn et al. Sep 2004 A1
20040223906 Wang et al. Nov 2004 A1
Related Publications (1)
Number Date Country
20050053545 A1 Mar 2005 US