METHODS FOR PRODUCING 2024 AND 7075 ALUMINUM ALLOYS BY RECYCLING WASTE AIRCRAFT ALUMINUM ALLOYS

Abstract

The present invention relates to techniques for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys, which belong to technical fields for circular economy. The present invention develops techniques for obtaining the 2024 and 7075 aluminum alloys by subjecting waste aircraft aluminum alloys as raw materials to pretreatment, smelting, impurity removal, melt ingredient assay, ingredient adjustment, refining, and casting. Through utilizing the waste package aluminum alloys and the waste aluminum pop-top cans to adjust the ingredients, the waste aircraft aluminum alloys would be recycled at a lower cost without downgrading. The present invention has some advantages, such as low cost, and applicability for industrial production, as well as prominent economic benefit.

Description

TECHNICAL FIELD

The invention provides methods for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys, which belong to be technologies for circular economy, and particularly relates to methods for recycling waste aircraft aluminum alloys without downgrading.

BACKGROUND ART

According to the prediction from Aircraft Fleet Recycling Association (AFRA), 6000-8000 aircrafts will be decommissioned in the next 10-20 years. The waste aircrafts contain a great amount of aluminum alloys. For example, the aluminum alloys used in a civil aircraft constitutes about 70% of the total weight, and mainly comprise 2XXX and 7XXX series of aluminum alloys. During long-term placement of the waste aircrafts, the degradation of aluminum alloys would be caused by ultraviolet ray, rainfall, oxidation, and the like, while the environmental issues, such as soil and groundwater pollution, and occupation of massive land resources, will be raised as well. Therefore, recycling of waste aircraft aluminum alloys not only saves energy, but also protects the environment, and would have good economic benefits. The main problem in regenerating 2024 and 7075 aluminum alloys from the waste aircraft aluminum alloys is that: the waste aircraft aluminum alloys contain a large number of riveting components, it is difficult to separate different designations of aluminum alloys from other impurities by sorting; the waste aircraft aluminum alloys contain various alloy elements having high contents, thereby dilution of excessive elements is usually performed by adding a plenty of pure aluminum in the smelting process, leading to a significant increased production cost.

Chinese patent ZL200780023435.6 discloses a process for manufacturing an aluminium-based remelted block intended for producing an aluminum alloy for the aeronautical industry. This method utilizes fractional crystallization to purify the waste aeronautical aluminum alloy melt, which can effectively remove impurities, such as iron and silicon in the aluminum melt, and has a less impact on other alloy elements. However, the method has a very high requirement for the equipment and a higher production cost. Chinese Patent ZL201310018088.5 discloses a method for obtaining a target aluminum alloy by subjecting waste miscellaneous aluminums as raw materials to iron removal by magnetic separation, pretreatment, smelting, molten liquid ingredient assay, calculation, proportioning, and ingredient adjustment. During the process of ingredient adjustment, pure aluminum is added to adjust the elements exceeding the upper limit of range of the target alloy ingredient, which has a disadvantage of higher production cost. Chinese patent ZL201010190753.5 discloses an aluminum alloy ingot having high performance and homogeneity and the method for producing the same, which can effectively remove the non-metallic materials in the waste aluminum materials and reduce the slag produced in the smelting process. However, this method does not relate to proportioning aluminum alloy ingredients.

As described above, the existing techniques for recycling waste aircraft aluminum alloys have some issues to varying degrees, such as higher production cost, incomplete ingredient adjustment, use of aluminum alloy products by downgrading, and the like, and there is an urgent need to develop a technique for recycling waste aircraft aluminum alloys without downgrading.

SUMMARY OF THE DISCLOSURE

The present invention provides a method for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys with respect to the problems encountered in proportioning ingredients in the current processes of recycling waste aircraft aluminum alloys. The particular steps are as follows:

(1) pretreatment: subjecting the waste aircraft aluminum alloys to breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and the like;

(2) smelting: smelting the pretreated waste aircraft aluminum alloys till complete melting at a smelting temperature from 700° C. to 800° C.;

(3) impurity removal: purifying the aluminum liquid using foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;

(4) ingredient adjustment: testing the ingredients in the aluminum liquid, and comparing them with target aluminum alloy ingredients; and adjusting the ingredients in the aluminum liquid using the other waste aluminum alloys and the interalloys, till the ingredients of the aluminum liquid meet the requirement for the target aluminum alloy ingredients;

(5) filtration: purifying the aluminum liquid using foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;

(6) refining and purification: refining the aluminum liquid by adding a refining agent and a degasifier, and placing the refined aluminum liquid for a period; and then purifying the aluminum liquid twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi to separate the substances not molten in the aluminum liquid, respectively;

(7) casting: after refining and removing impurities, casting the aluminum liquid to obtain the aluminum alloys with target ingredients.

The present invention has some advantages in that: the ingredients of the waste aircraft aluminum alloy melt are adjusted using paint-removed waste aluminum pop-top cans and the waste package aluminum alloys, which can significantly reduce the production cost and is beneficial for the industrial application.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1. Flow Chart of the process for recycling waste aircraft aluminum alloys.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention will now be further described in detail with reference to the following Examples, but it is not limited to the following Examples.

Example 1

Production of 7075 Aluminum Alloy by Recycling Waste Aircraft Aluminum Alloys

(1) pretreatment: the waste aircraft aluminum alloys are subjected to breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and the like;

(2) smelting: the pretreated waste aircraft aluminum alloys are smelt till complete melting at a smelting temperature of 700° C.;

(3) impurity removal: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;

(4) ingredient adjustment: after the removal of impurities, two samples are taken from different parts of the aluminum melt for the ingredient assay.

The ingredients in the standard 7075 aluminum alloy, the waste package aluminum alloys as ingredient adjustment agents, and the aluminum melt upon the impurity removal in “GB/T3190-2008 deformation aluminum and aluminum alloy ingredients” are shown in Table 1.

TABLE 1
Table for the comparison of the aluminum alloy ingredients prior to
ingredient proportioning and the 7075 aluminum alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 7075	1.2-2.0	5.1-6.1	2.1-2.9	<0.3	0.18-0.3	<0.4	<0.5	<0.2
aluminum alloy
Waste package	<0.15	<0.25	4.0-5.0	0.2-0.5	<0.10	<0.20	<0.35	<0.10
aluminum alloys
Melt ingredients	2.378	2.385	1.286	0.325	0.078	0.26	0.227	0.027

Through the comparison of the aluminum alloy melt ingredients prior to ingredient adjustment and the standard 7075 aluminum alloy ingredients, it can be seen that the contents of Cu and Mn are excessive, while the contents of Zn, Mg, and Cr are insufficient. After calculation, 25% the paint-removed waste package aluminum alloys, 1.6% aluminum-chromium alloy, 3.5% metallic zinc and 1% aluminum-magnesium alloy are added into the melt, and well stirred. After the added materials are completely molten, two samples are taken from different parts of the aluminum melt for the ingredient assay. The comparison of adjusted aluminum melt ingredients and the standard 7075 aluminum alloy ingredients is shown in Table 2, and then the aluminum melt ingredients have already met the requirements for the standard 7075 aluminum alloy.

TABLE 2
Table for the comparison of the melt ingredients upon
adjustment and the standard 7075 alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 7075	1.2-2.0	5.1-6.1	2.1-2.9	<0.3	0.18-0.3	<0.4	<0.5	<0.2
aluminum alloy
Melt ingredients	1.622	5.584	2.498	0.272	0.238	0.22	0.263	0.019

(5) filtration: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;

(6) refining and purification: the aluminum liquid is refined by adding a refining agent and a degasifier, and the refined aluminum liquid is placed for a period; the aluminum liquid is then purified twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi to separate the substances not molten in the aluminum liquid, respectively.

(7) casting: after refining and removing impurities, the aluminum liquid is casted to obtain the 7075 aluminum alloy ingot.

Example 2

Production of 2024 Aluminum Alloy by Recycling Waste Aircraft Aluminum Alloys

(1) pretreatment: the waste aircraft aluminum alloys are subjected to breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and the like;

(2) smelting: the pretreated waste aircraft aluminum alloys are smelt till complete melting at a smelting temperature of 800° C.;

(3) impurity removal: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;

(4) ingredient adjustment: after the removal of impurities, two samples are taken from different parts of the aluminum melt for the ingredient assay.

The ingredients in the standard 2024 aluminum alloy, the waste aluminum pop-top cans as ingredient adjustment agents, and the aluminum melt upon the impurity removal in “GB/T3190-2008 deformation aluminum and aluminum alloy ingredients” are shown in Table 3.

TABLE 3
Table for the comparison of the aluminum alloy ingredients prior to
ingredient proportioning and the 2024 aluminum alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 2024	3.8-4.9	<0.25	1.2-1.8	0.3-0.9	<0.1	<0.5	<0.5	<0.15
aluminum alloy
the waste	0.05-0.25	<0.25	0.8-1.3	0.8-1.4	—	<0.60	<0.80	<0.10
aluminum
pop-top cans
Melt ingredients	3.752	1.543	1.368	0.532	0.043	0.20	0.213	0.028

Through the comparison of the aluminum alloy melt ingredients prior to ingredient adjustment and the standard 2024 aluminum alloy ingredients, it can be seen that the content of Zn is excessive, while the content of Cu is insufficient. After calculation, 650% paint-removed waste aluminum pop-top can sheets, 1.6% aluminum-chromium alloy, 22.5% metallic copper and 10% aluminum-magnesium alloy are added into the melt, and well stirred. After the added materials are completely molten, two samples are taken from different parts of the aluminum melt for the ingredient assay. The comparison of adjusted aluminum melt ingredients and the standard 2024 aluminum alloy ingredients is shown in Table 4, and then the aluminum melt ingredients have already met the requirements for the standard 2024 aluminum alloy.

TABLE 4
Table for the comparison of the melt ingredients upon
adjustment and the standard 2024 alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 2024	3.8-4.9	<0.25	1.2-1.8	0.3-0.9	<0.1	<0.5	<0.5	<0.15
aluminum alloy
Melt ingredients	4.298	0.224	1.512	0.638	0.032	0.23	0.403	0.032

(5) filtration: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;

(6) refining and purification: the aluminum liquid is refined by adding a refining agent and a degasifier, and the refined aluminum liquid is placed for a period; the aluminum liquid is then purified twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi to separate the substances not molten in the aluminum liquid, respectively.

(7) casting: after refining and removing impurities, the aluminum liquid is casted to obtain the 2024 aluminum alloy ingot.

Example 3

Production of 7075 Aluminum Alloy by Recycling Waste Aircraft Aluminum Alloys

(1) pretreatment: the waste aircraft aluminum alloys are subjected to breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and the like;

(2) smelting: the pretreated waste aircraft aluminum alloys are smelt till complete melting at a smelting temperature of 750° C.;

(3) impurity removal: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;

(4) ingredient adjustment: after the removal of impurities, two samples are taken from different parts of the aluminum melt for the ingredient assay.

The ingredients in the standard 7075 aluminum alloy, the waste package aluminum alloys as ingredient adjustment agents, and the aluminum melt upon the impurity removal in “GB/T3190-2008 deformation aluminum and aluminum alloy ingredients” are shown in Table 5.

TABLE 5
Table for the comparison of the aluminum alloy ingredients prior to
ingredient proportioning and the 7075 aluminum alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 7075	1.2-2.0	5.1-6.1	2.1-2.9	<0.3	0.18-0.3	<0.4	<0.5	<0.2
aluminum alloy
Melt ingredients	2.138	3.012	1.375	0.295	0.094	0.25	0.245	0.025
Waste package	<0.15	<0.25	4.0-5.0	<0.15	<0.15	<0.20	<0.35	<0.10
aluminum alloys

Through the comparison of the aluminum alloy melt ingredients prior to ingredient adjustment and the standard 7075 aluminum alloy ingredients, it can be seen that the contents of Cu and Mn are excessive, while the contents of Zn, Mg, and Cr are insufficient. After calculation, 25% the paint-removed waste package aluminum alloys, 2% aluminum-chromium alloy, 4% metallic zinc and 1% aluminum-magnesium alloy are added into the melt, and well stirred. After the added materials are completely molten, two samples are taken from different parts of the aluminum melt for the ingredient assay. The comparison of adjusted aluminum melt ingredients and the standard 7075 aluminum alloy ingredients is shown in Table 6, and then the aluminum melt ingredients have already met the requirements for the standard 7075 aluminum alloy.

TABLE 6
Table for the comparison of the melt ingredients upon
adjustment and the standard 7075 alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 7075	1.2-2.0	5.1-6.1	2.1-2.9	<0.3	0.18-0.3	<0.4	<0.5	<0.2
aluminum alloy
Melt ingredients	1.596	5.828	2.597	0.268	0.257	0.25	0.295	0.021

(5) filtration: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;

(6) refining and purification: the aluminum liquid is refined by adding a refining agent and a degasifier, and the refined aluminum liquid is placed for a period; the aluminum liquid is then purified twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi to separate the substances not molten in the aluminum liquid, respectively.

(7) casting: after refining and removing impurities, the aluminum liquid is casted to obtain the 7075 aluminum alloy ingot.

Example 4

Production of 2024 Aluminum Alloy by Recycling Waste Aircraft Aluminum Alloys

(1) pretreatment: the waste aircraft aluminum alloys are subjected to breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and the like;

(2) smelting: the pretreated waste aircraft aluminum alloys are smelt till complete melting at a smelting temperature of 750° C.;

(3) impurity removal: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;

(4) ingredient adjustment: after the removal of impurities, two samples are taken from different parts of the aluminum melt for the ingredient assay.

The ingredients in the standard 2024 aluminum alloy, the waste aluminum pop-top cans as ingredient adjustment agents, and the aluminum melt upon the impurity removal in “GB/T3190-2008 deformation aluminum and aluminum alloy ingredients” are shown in Table 7.

TABLE 7
Table for the comparison of the aluminum alloy ingredients prior to
ingredient proportioning and the 2024 aluminum alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
Standard 2024	3.8-4.9	<0.25	1.2-1.8	0.3-0.9	<0.1	<0.5	<0.5	<0.15
aluminum alloy
the aluminum	<0.25	<0.25	0.8-1.3	1.0-1.5	—	<0.30	<0.70	<0.10
waste
pop-top cans
Melt ingredients	4.312	0.22	1.498	0.641	0.036	0.20	0.385	0.028

Through the comparison of the aluminum alloy melt ingredients and the standard 2024 aluminum alloy ingredients prior to ingredient adjustment, it can be seen that the content of Zn is excessive, while the content of Cu is insufficient. After calculation, 650% paint-removed waste aluminum pop-top can sheets, 1.5% aluminum-chromium alloy, 23% metallic copper and 10% aluminum-magnesium alloy are added into the melt, and well stirred. After the added materials are completely molten, two samples are taken from different parts of the aluminum melt for the ingredient assay. The comparison of adjusted aluminum melt ingredients and the standard 2024 aluminum alloy ingredients is shown in Table 8, and then the aluminum melt ingredients have already met the requirements for the standard 2024 aluminum alloy.

TABLE 8
Table for the comparison of the melt ingredients upon
adjustment and the standard 2024 alloy ingredients
	Cu	Zn	Mg	Mn	Cr	Si	Fe	Ti
2024	3.8-4.9	<0.25	1.2-1.8	0.3-0.9	<0.1	<0.5	<0.5	<0.15
aluminum alloy
Melt ingredients	4.312	0.22	1.498	0.641	0.036	0.20	0.385	0.028

(5) filtration: the aluminum liquid is purified using foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;

(6) refining and purification: the aluminum liquid is refined by adding a refining agent and a degasifier, and the refined aluminum liquid is placed for a period; the aluminum liquid is then purified twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi to separate the substances not molten in the aluminum liquid, respectively.

(7) casting: after refining and removing impurities, the aluminum liquid is casted to obtain the 2024 aluminum alloy ingot.

Claims

1. A method for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys, comprising: subjecting the waste aircraft aluminum alloys to a pretreatment selected from the group consisting of breaking, iron removal by magnetic separation, removal of heavy metals by flotation, removal of polymers and composite materials by air elutriation, removal of glass by eddy current sorting, and combination(s) thereof;smelting the pretreated waste aircraft aluminum alloys till complete melting at a smelting temperature from 700° C. to 800° C.;purifying aluminum liquid using a foam ceramic filter plate having a pore diameter of 10 ppi to separate the impurities not molten in the aluminum liquid;testing the ingredients in the aluminum liquid, and comparing the ingredients with target aluminum alloy ingredients; and adjusting the ingredients in the aluminum liquid using other waste aluminum alloys and interalloys, till the ingredients thereof meet requirement for the target aluminum alloy ingredients;purifying the aluminum liquid using a foam ceramic filter plate having a pore diameter of 20 ppi to separate the impurities not molten in the aluminum liquid;refining the aluminum liquid by adding a refining agent and a degasifier to form a refined aluminum liquid, and placing the refined aluminum liquid for a period; and then purifying the refined aluminum liquid twice using foam ceramic filter plates having pore diameters of 40 ppi and 60 ppi, respectively, to separate substances not molten in the refined aluminum liquid; andcasting the refined aluminum liquid to obtain the aluminum alloys with target ingredients.

2. The method for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys according to claim 1, characterized in that: while purifying the aluminum liquid using the foam ceramic filter plate having a pore diameter of 10 ppi, the impurities not molten comprise iron alloy, titanium alloy, and carbon fiber.

3. The method for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys according to claim 1, characterized in that: the other waste aluminum alloys comprise paint-removed waste aluminum pop-top cans and waste package aluminum alloys.

4. The method for producing 2024 and 7075 aluminum alloys by recycling waste aircraft aluminum alloys according to claim 1, characterized in that: filtered substances not molten while purifying the refined aluminum liquid using the foam ceramic filter plate having pore diameter of 60 ppi are waste aircraft aluminum alloy raw materials and inorganic coating materials adhered on the waste aluminum alloy raw materials.