Patent Application
20050205847
Since their discovery in the early 1990s, carbon nanotubes have been the subject of intense scientific research directed toward developing techniques for synthesizing high quality nanotube materials, and evaluating their physical and chemical properties. Carbon nanotubes are allotropes of carbon comprising one or more cylindrically configured graphene sheets. Carbon nanotubes typically have small diameters (≈1-10 nanometers) and large lengths (up to several microns), and therefore may exhibit very large aspect ratios (length to diameter ratio ≈103 to about 105). Nanotube materials are often classified on the basis of structure as either single walled carbon nanotubes (SWNTs) or multiwalled carbon nanotubes (MWNTs). Research over the past decade has demonstrated that carbon nanotube materials exhibit extraordinary mechanical, electrical and chemical properties, which has stimulated substantial interest in developing applied technologies exploiting these properties.
Single walled carbon nanotubes (SWNTs) are one class of carbon nanotubes which have been identified as potentially useful materials for a number of applied technologies. SWNTs are made up of a single, contiguous graphene sheet wrapped around and joined with itself to form a hollow, seamless tube having capped ends similar in structure to smaller fullerenes. SWNTs typically have very small diameters (≈1 nanometer) and are often present in curled and looped configurations. The energy band structure of SWNTs varies considerably, and SWNTs exhibit either metallic or semiconductor electrical behavior depending on their precise molecular structure and diameter. Under some experimental conditions, SWNTs undergo efficient self assembly processes that generate bundles (or ropes) of SWNTs aligned along their lengths and strongly bound together by van der Waals forces. SWNTs are chemically versatile materials which have been demonstrated as capable of functionalization of their exterior surfaces and capable of encapsulation of materials within their hollow cores, such as gases and molten materials.
Research over the last decade has identified a number of unique properties of SWNTs which make these materials particularly promising candidate materials for a variety of device applications ranging from a revolutionary class of new electronic devices to composite materials having enhanced mechanical properties. First, SWNTs are believed to have remarkable mechanical properties suggesting their utility as structural reinforcement additives in high strength, low weight and high performance composite materials. For example, calculations and experimental results suggest that the SWNTs have tensile strengths at least 100 times that of steel or any known other known fiber. In addition, SWNTs are stiffer than conventional reinforcement materials, such as carbon fibers, while also exhibiting a very large Young's Modulus (as large as about 1 TPa) when distorted in some directions. Second, SWNTs exhibit useful electrical properties which may serve the basis of a new class of nanotube based electronic devices. For example, the electron transport behavior in carbon nanotubes is predicted to be essentially that of a quantum wire, which has stimulated interest in fabricating ultrafast nanotube based devices. In addition, the electrical properties of SWNTs have been observed to vary significantly upon charge transfer doping and intercalation, which has opened up new avenues for tuning the electrical properties of these materials. Further, due to their nanometer size diameter, mechanical robustness, chemical stability and high electrical conductivity, SWNTs may provide enhanced field emitters in a range of devices, including flat panel displays, AFM tips and electron microscopes. Finally, SWNTs are also believed to possess useful thermal, magnetic and optical properties which make them suitable materials for a range of emerging applied technologies.
The unique chemical and physical characteristics of carbon nanotubes is often severely attenuated or entirely lost when these materials are present with substantial amounts of impurities. Therefore, the successful development of nanotube based technologies taking full advantage of their extraordinary properties depends critically on the availability of sources of substantially pure nanotube materials. Currently available methods for synthesizing SWNTs, however, do not directly result in substantially pure samples containing these materials. Rather, conventional synthesis processes, such as techniques utilizing arc discharge, laser ablation, and chemical vapor deposition, yield a complex reaction product comprising a mixture of SWNTS, carbonaceous impurities and noncarbonaceous impurities. The impurity component of the reaction product generated using many of these techniques is very significant and SWNTs often comprise less than half of the reaction product by weight. Carbonaceous impurities generated in conventional synthesis processes are present in both single layer and multilayer configurations and include amorphous carbon, graphene sheets, graphite, incomplete and complete fullerenes and multiwalled nanotubes. Noncarbonaceous impurities commonly present in SWNT containing samples include residual metal catalyst particles, such as particles comprising nickel, yttrium, iron, molybdenum, palladium, and cobalt, and catalyst support materials, such as ceramic materials.
As a result of associative intermolecular interactions, such as van der Waals interactions, impurities and SWNTs in samples prepared via conventional synthesis techniques are present in highly coupled physical states. For example, the outer surfaces of SWNTs and bundles of SWNTs are typically heavily coated with a variety of single and multilayer carbonaceous impurities. In addition, metal catalyst particles unavoidably generated in catalytic synthesis methods are often entirely or partially encapsulated in high stable multilayers comprising carbonaceous impurities. Associative intermolecular interactions involving these materials present a unique challenge for purifying and isolating SWNTs in samples prepared by conventional synthesis methods. For example, the carbon multilayers surrounding metal catalyst particles severely reduce the effectiveness of purification via dissolution of the particles in acids provided to the sample. In addition, associative interactions between carbonaceous impurities and SWNTs pose significant problems for positioning, aligning and/or integrating SWNTs into desired device configurations.
Significant research has been direct toward developing methods of isolating and purifying SWNTs, due to the inability of conventional synthesis methods to directly produce substantially pure samples of high quality carbon nanotubes. Effective purification methods are capable of removing the wide range of different impurities that exhibit markedly different chemical and physical properties. In addition, effective purification methods are capable of selectively removing a majority of these impurities without causing significant damage to or destruction of the SWNTs. Furthermore, effective purification methods are capable high throughout processing of significant quantities of SWNTs in a relatively small number of efficient purification steps, thereby avoiding unreasonably long processing times.
A number of different approaches have been pursued in recent years for purifying SWNT containing samples. First, several techniques have been developed that are based on chemically modifying impurities to enhance their removal, including selective oxidation processes, such as gas phase oxidation, catalytic oxidation and acid oxidation, and nitric acid and hydrogen peroxide reflux methods. Although chemical modification techniques have been demonstrated as capable of enhancing the purity of SWNT containing samples, these treatments invariably destroy a significant portion of the SWNTs present in the sample, and are not effective at removing metal particulate impurities enclosed in carbon multilayers. Second, purification methods have been pursued based on microfiltration and cross flow filtration techniques. These techniques require a relatively large number of repeated filtration and suspension processing steps, however, making the procedures relatively slow and inefficient. Finally, purification of SWNTs via size exclusion chromatography has also been demonstrated. However, this approach requires use of surfactants for suspension of the SWNTs in the sample undergoing chromatographic separation, which can result in residual surfactant in the purified sample that can deleteriously affect the chemical and physical properties of the purified nanotubes.
The following references relate generally to methods of synthesizing and purifying carbon nanotubes: (1) A. M. Cassell, J. A. Raymakers, J. Kong, H. J. Dai, J. Phys. Chem. B 103(31), (1999), pp. 6484-6492; (2) M. Su, B. Zheng, J. Liu, Chem. Phys. Lett. 322(5), (2000), pp. 321-326; (3) B. Kitiyanan, W. E. Alvarez, J. H. Harwell, D. E. Resasco, Chem. Phys. Lett. 317(3-5), (2000), pp. 497-503; (4) J. H. Hafner, M. J. Bronikowski, B. R. Azamian, P. Nicolaev, A. G. Rinzler, D. T. Colbert, K. A. Smith, R. E. Smalley, Chem. Phys. Lett. 296(1-2), (1998) pp. 195-202 (5) H. M. Cheng, F. Li, G. Su, H. P. Pan, L. L. He, X. Sun, M. S. Dresselhaus, Appl. Phys. Lett. 72(25), (1998), pp. 3282-3284; (6) B. Zheng, Y. Li, J. Liu, Applied Physics A 74, 345-348 (2002); (7) C. Journet, W. K. Maser, P. Bernier, A. Loiseau, M. Lamy de la Chapelle, S. Lefrant, R. Lee, J. E. Fischer, Nature 388, 756-758 (1997); (8) A. Thess, R. Lee, P. Nikolaev, H. Dai, P. Petit, J. Robert, C. Xu, Y. H. Lee, S. G. Kim, A. G. Rinzler, D. T. Colbert, G. E. Scuseria, D. Tomanek, J. E. Fischer, R. E. Smalley, Science 273, (1996) 483-487; (9) M. Holzinger, A. Hirsch, P. Bernier, G. S. Duesberg, M. Burghard, Applied Physics A 70, (2000) 599-602; (10) G. S. Duesberg, J. Muster, V. Krstic, M. Burghard, S. Roth, Appl. Phys. A 67, (1998), 117-119; (11) J. Liu, A. G. Rinzler, H. Dai, J. H. Hafner, R. K. Bradley, P. J. Boul, A. Lu, T. Iverson, K. Shelimov, C. B. Huffman, F. Rodriuez-Macias, Y. S. Shon, T. R. Lee, D. T. Colbert, R. E. Smalley, Science 280, (1998) 1253-1256; (12) A. G. Rinzler, J. Liu, H. Dai, P. Nikolaev, C. B. Huffman, F. J. Rodriguez-Macias, P. J. Boul, A. H. Lu, D. Heymann, D. T. Colbert, R. S. Lee, J. E. Fischer, A. M. Rao, P. C. Eklund, R. E. Smalley, Appl. Phys. A 67, (1998) 29-37; (13) Y. Feng, G. Zhou, G. Wang, M. Qu, Z. Yu, Chem, Phys, Lett, 375, (2003) 645-648; (14) T. Takenobu, M. Shiraishi, A. Yamada, M. Ata, H. Kataura, Y. Iwasa, Synthetic Metals 135-136, (2003) 787-788; (15) I. W. Chiang, B. E. Brinson, A. Y. Huang, P. A. Willis, M. J. Bronikowski, J. L. Margrave, R. E. Smalley, R. H. Hauge, J. Phys. Chem. B 105, (2001) 8297-8301.
It will be appreciated from the foregoing that there is currently a need in the art for improved methods for purifying carbon nanotube materials, particularly SWNTs, such that these materials can be effectively integrated into a range of applied technology settings. Specifically, methods are needed for purifying SWNT containing samples generated via conventional SWNT synthesis methods, such as samples comprising mixtures of SWNTS, a range of carbonaceous impurities and metal or metal oxide catalyst particles. In addition, purification methods are needed that provide high yields of high quality nanotube materials, thereby minimizing loss or damage to SWNTs in a sample undergoing purification. Further, low cost and versatile purification methods are needed that are compatible with high throughput processing of large amounts of SWNTs generated by the conventional synthesis techniques.
The present invention provides processes for purifying samples comprising one or more desired forms of carbon by removing impurities from the sample. Purification methods of the present invention are capable of preferentially removing undesired impurities, thereby increasing the purity a desired carbon material having a selected structure in a sample. Methods of the present invention are capable of effectively removing impurities without substantially damaging or destroying the desired carbon material in a sample undergoing processing. In some embodiments, therefore, the present methods provide a means of purifying a selected carbon material such that the purified selected carbon material has a structure and composition that does not different significantly from its structure and composition in the starting material subject to processing or has a structure that is enhanced after processing via the present methods, such as a structure exhibiting enhanced extent of crystallinity. The present purification methods are versatile and, thus capable of generating a range of substantially pure carbon materials, including carbon nanotubes (SWNTS and MWNTs), fullerenes, and other carbon allotropes such as carbon fibers, carbon films and diamond, from samples generated by a range of synthesis methods, including, catalytic and noncatalytic processes. In one embodiment, the methods of the present invention provide a source of substantially pure, high quality carbon nanotubes, are compatible with high throughput processing of samples comprising large quantities of carbon nanotubes, and require substantially less processing steps than conventional methods of purifying carbon nanotubes.
The present purification methods selectively remove carbonaceous impurities, noncarbonaceous impurities and multiphase impurities having both a carbon-containing portion and a noncarbon-containing portion by exfoliating single and multilayer carbonaceous impurities having structures that differ from the structures of selected carbon materials in the sample. Exfoliation processes useful in the present methods disrupt the structure and arrangement of single and multilayer carbon impurities thereby making these materials more susceptible to removal via subsequent processing steps. Exfoliation of carbon impurities comprising a plurality of layers of graphene, graphite and/or amorphous carbon, for example, makes these materials susceptible to removal by gas phase oxidation at temperatures lower than those corresponding to the gas phase oxidation of thee materials in their unexfoliated forms. In embodiments of the present invention providing high yields of selected carbon materials, exfoliation is carried out under conditions wherein undesired carbonaceous impurities are at least partially exfoliated, while the desired, selected forms of carbon do not undergo substantial exfoliation and/or chemical degradation. Any exfoliation process capable of selectively disrupting the structure and arrangement of single and multilayer carbonaceous impurities may be used in the present purification methods, including methods wherein one or more intercalants are added to the sample and insert into interstitial sites between multilayers of carbonaceous impurities and/or into interstitial sites located between a selected carbon material and a carbonaceous impurities coating its outer surface.
The present invention provides methods that are particularly useful for purifying samples prepared by processes that yield a mixture of a desired carbon material, including carbon nanotubes (SWNTS and/or MWNTs), fullerenes, and/or other selected allotropes of carbon, and impurities comprising residual metal catalyst particles or catalyst support materials, such as transition metal or metal oxide particles partially or completely enclosed in multilayer carbonaceous impurities. In one embodiment, the present invention provides methods for at least partially exfoliating carbonaceous multilayers enclosing metal catalyst particles in a sample. This aspect of the present invention enhances subsequent removal of metal particles because exfoliation ruptures the structure of the carbonaceous layers thereby making the particles susceptible to removal via dissolution. Optionally, methods of this aspect of the present invention may further comprise the step of selectively removing the exfoliated carbonaceous multilayers, for example via wet oxidation, which further exposes the outer surfaces of the metal particles and enhances subsequent removal via dissolution. This aspect of the present invention provides versatile purification methods useful for increasing the purity of a desired carbon material in samples generated by virtually any catalytic synthesis techniques employing metal or metal based catalysts such as metal carbonyls.
In one aspect, the present invention provides a method of purifying a sample containing a carbon material having a selected structure wherein at least partial exfoliation of undesired single and multilayer carbonaceous impurities present in the sample allows for effective removal of impurities having a range of chemical compositions and physical states. A sample is provided containing the carbon material having a selected structure and impurities. The impurities present in the sample comprise carbonaceous impurities comprising one or more carbon layers having structures different than that of the selected carbon material undergoing purification. Optionally, the impurities present in the sample comprise noncarbonaceous impurities, such as metal particles and/or metal derivative particles such as metal oxide particles, and multiphase impurities, such as metal particles and/or metal derivative particles such as metal oxide particles partially or completely enclosed in multilayer carbonaceous impurities.
At least a portion of the carbon layers of the carbonaceous impurities are exfoliated, and the impurities are removed thereby purifying the sample. Exfoliation of at least a portion of the carbon layers in this method of the present invention allows for effective removal of carbonaceous impurities, noncarbonaceous impurities and multiphase impurities. In one embodiment, removal of exfoliated carbonaceous materials directly purifies the sample. Any method of removing exfoliated carbonaceous material may be used in the present methods provided that it does not substantially damage or destroy the selected carbon material undergoing purification, including but not limited to chemical transformation methods (e.g. wet oxidation and dissolution), filtration (e.g. cross flow or microfiltration methods) and chromatographic methods (e.g. size exclusion chromatography).
In another embodiment, exfoliation processing steps exfoliate at least a portion of carbon multilayers enclosing metal particles in the sample undergoing processing. In this embodiment, exfoliation at least partially exposes the surface of the metal particles, thereby allowing for their effective removal by a wide variety of removal methods. Removal of the exposed metal particles may be provided by any technique known in the art including, but not limited to, dissolution in a solution added to the sample, for example by refluxing the sample in a concentrated inorganic and/or organic acid, and/or treatment with an appropriate gas, for example by treatment with a halogen gas, such as chlorine at high temperatures (e.g. at or above about 900 degrees Celsius). Optionally, the purification methods of the present invention may further comprise the step of annealing the sample after the impurities have been removed. This optional step is beneficial in some applications as it may repair any damage to the carbon material having a selected structure that occurs during processing. It also removes residual reactant and solvant(s) and/or enhances the crystalline structure of the selected carbon material.
Purification methods of the present invention are capable of enriching the purity of a single selected carbon material or plurality of different selected carbon materials. Selectivity in the present invention is provided by processing steps that are capable of exfoliating a selected set of materials corresponding to undesired impurities, while avoiding exfoliating or damaging to the desired carbon material(s) in the sample undergoing purification. In one embodiment, for example, the present invention provides methods for selectively enriching the purity of single walled carbon materials, such as SWNTs and/or single walled fullerenes, by selectively exfoliating carbonaceous materials that comprise a plurality of carbon multilayers, such as graphene multilayer structures, graphite multilayers, amorphous carbon multilayers, multiwalled fullerenes, MWTNs or any combination of these materials. Selective exfoliation in this aspect of the present invention allows for multilayer carbonaceous impurities to be efficiently removed, for example by selective oxidation, without significant loss of or damage to the desired single walled carbon materials. Alternatively, the present invention provides methods for selectively enriching the purity of one or more selected multilayer carbon structures, such as MWNTs, multiwalled fullerenes, diamond, carbon fibers, carbon films or any combination of these materials. In this embodiment, the exfoliation technique employed and experimental conditions of the sample (e.g. temperature, sample composition, composition of exfoliation initiator added to the sample etc.) are chosen such that undesired multilayered carbonaceous impurities are selectively exfoliated and subsequently removed, resulting in enhancement of the purity of the selected multilayer carbon structures in the sample.
Exfoliation of multilayer carbonaceous impurities can be carried out in any manner which promotes effective removal of impurities, while not substantially damaging or destroying the carbon materials having a selected structure in the sample. Exfoliation processes preferred for some application are rapid exothermic chemical reactions or physical changes that exfoliate carbonaceous materials without damaging desired components of a sample. In some embodiments, exfoliation is carried out by addition of one or more intercalants to the sample that insert into interstitial sites between carbon multilayers of multilayer carbonaceous impurities and/or insert into interstitial sites between a selected carbon material, such as SWNTs or MWNTs, and a carbonaceous impurity coating the outside of the selected carbon material.
In one embodiment of the present invention, addition of an intercalant generates intercalated carbon materials having intercalants present in interstitial sites between carbon multilayers comprising carbonaceous impurities. The presence of intercalants between the multilayers of carbonaceous impurities makes these materials susceptible to various selective exfoliation processes. For example, some intercalants weaken or disrupt the intermolecular or intramolecular forces between adjacent multilayers resulting in more selective and more complete exfoliation. Insertion of some intercalants of the present invention between multilayers results in an expansion of the interlayer distance separating adjacent multilayers and/or may provide a reactant for chemical reactions that initiate selective exfoliation of multilayer carbonaceous impurities.
Alternatively, addition of intercalants in the present invention generates intercalated carbon materials having intercalants present in interstitial sites between a selected carbon material and an impurity comprising a carbonaceous outer layer coating the selected carbon material. This aspect of the present invention is useful for disrupting associative interactions, such as van der Waals interactions, between impurities and desired carbon materials in a sample. In one embodiment, insertion of intercalants into interstitial sites between a selected carbon material and a layer comprising carbonaceous impurity provides a means of separating the selected carbon material from impurities that associatively interact with it. This aspect of the present invention is particularly useful for separating and removing single or multiple layer carbonaceous impurities coating the outer surfaces of SWNTs and MWNTs. This aspect of the present invention is useful for removing coatings of carbonaceous impurities on carbon nanotubes which affect their physical, electrical and chemical properties and present difficulties in integrating these materials into desired device configurations.
In one embodiment of the present invention, exfoliation is achieved by adding an exfoliation initiator to a sample containing one or more intercalants which reacts with intercalants in intercalated carbon layers, thereby initiating selective exfoliation. Exemplary exfoliation initiators react exothermically with intercalants in intercalated carbon layers and, optionally initiate an expansion of material present between carbon layers, for example by generating a gaseous reaction product. In another embodiment, exfoliation is achieved by subsequently raising the temperature of the intercalated carbon layers, for example by heating the sample or exposing the sample to electromagnetic radiation. Rapidly raising the temperature of intercalated samples provides sufficient energy to selectively exfoliate the carbon layers of carbonaceous impurities.
As many carbonaceous impurities are amphoteric in nature, intercalants useful in this aspect of the present invention include, electron donor intercalant, such as alkali metals (e.g. Li, K, Na, Rb and Cs), and electron acceptor intercalants, such as halogens (e.g. fluorine, bromine and iodine), metal chlorides and acids (e.g. lewis acids such as nitric acid, perchloric acid, sulfuric acid; and formic acid). The present invention includes methods wherein more than one type of intercalant is added to the sample undergoing purification, for example methods in which carbon layers are bi-intercalated. The present invention includes intercalation processing of samples via electrochemical methods, including but not limited to, intercalation initiated via chronoamperometric or chronovoltametric methods. Intercalants may be provided as liquids, gases and in solutions added to samples undergoing purification. Preferred intercalants for applications requiring high yields of high quality carbon materials do not significantly damage or disrupt the desired carbon material undergoing purification.
The present methods are capable of processing samples comprising complex mixtures of materials having a wide range of chemical compositions, structures and physical states. For example, the present methods are useful for purifying sample generated by virtually all catalytic and noncatalytic synthesis methods for making SWNTs, MWNTs, catalytically grown carbon fibers, catalytically grown carbon films and diamond, including but not limited to, arc-discharge methods, chemical vapor deposition methods, plasma enhanced chemical vapor deposition methods, high pressure carbon monoxide disproportionation methods; pyrolytic methods, flame synthesis methods, electrochemical synthesis methods; and laser ablation methods. The versatility with respect to the type of carbon material that is purified in the present methods largely arises from the use of selective exfoliation wherein impurities having structures similar to, but not the same as, a desired carbon material may be exfoliated and removed without substantial loses or damage to the desired carbon material. In addition, this versatility arises from the use of selective exfoliation to render noncarbonaceous impurities in a state susceptible to removal via dissolution.
The present invention provides a method of purifying a sample containing SWNTS by selectively removing graphene layers, graphite, amorphous carbon, incomplete fullerenes, metal particles or any combination of these materials. In one embodiment, methods of this aspect of the present invention are capable of providing purified samples corresponding to a yield of SWNTs selected over the range of about 15% to about 20% and a purity selected from about 90 to about 98% by weight. In the context of this description, the term yield refers to the weight ratio (in percent) of the achieved purified SWNT to the initial amount of carbon material before purification (e.g. 1 gram of carbon will provide 150 milligram of purified SWNT in a process providing a 15% yield). In another embodiment, the present invention provides a method of purifying a sample containing MWNTS by selectively removing graphene layers, graphite, amorphous carbon, incomplete fullerenes, metal particles or any combination of these materials. Further, the methods of the present invention are applicable to purifying nanotubes made from other materials, such as boron nitride nanotubes. The present methods are not limited to purifying carbon nanotube containing samples, and are capable of isolating and purifying other useful allotropes of carbon, such as single walled fullerenes, multiwalled fullerenes, diamond, carbon fibers, carbon films, and carbon whiskers.
The present methods are also suitable for purification of diamond materials. Conventional diamond synthesis methods, such as high temperature-high pressure processing of molten graphite and chemical vapor deposition methods, generate diamond-containing samples having significant carbonaceous impurities, such as graphite. Methods of the present invention are useful for exfoliating these carbonaceous impurities, thereby allowing for more easy removal of the exfoliated carbonaceous impurities.
In another aspect, the present invention provides a method of purifying a sample containing a carbon material having a selected structure comprising the steps of: (1) providing the sample containing the carbon material having a selected structure and impurities comprising carbonaceous impurities, wherein the carbonaceous impurities comprising one or more carbon layers having a structure different than that of the selected structure; (2) exfoliating at least a portion of the carbon layers of the carbonaceous impurities, thereby generating exfoliated carbonaceous material; and (3) removing the impurities, thereby purifying the sample containing a carbon material having a selected structure. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.
In another aspect, the present invention provides a method of exfoliating at least a portion of a plurality of carbon multilayers at least partially enclosing metal particles in a sample generated in the synthesis of carbon nanotubes comprising the steps of: (1) providing the sample generated in the synthesis of carbon nanotubes containing the metal particles, wherein each metal particle is at least partially enclosed by the carbon multilayers; (2) adding an intercalant to the sample, wherein the intercalant inserts between at least a portion of the carbon multilayers, thereby generating intercalated carbon multilayers having intercalant present between the carbon multilayers; and (3) adding an exfoliation initiator to the sample which reacts with intercalant present between the carbon multilayers, thereby exfoliating at least a portion of the carbon multilayers.
In another aspect, the present invention provides a method of removing carbonaceous coatings from the outer surfaces of carbon nanotubes comprising the steps of: (1) providing a sample comprising the carbon nanotubes, wherein at least a portion of the outer surfaces of the nanotubes are partially or completely coated with the carbonaceous coatings, and wherein the carbonaceous coatings have a structure different from that of the nanotubes; (2) adding an intercalant to the sample, wherein the intercalant inserts into interstitial sites between the nanotubes and the carbonaceous coating; and (3) adding an exfoliation initiator to the sample which reacts with the intercalant, wherein the reaction between the intercalant present between the carbon nanotubes and the carbonaceous coating and the exfoliation initiator exfoliates the carbonaceous coating, thereby removing the carbonaceous coatings from the outer surfaces of the carbon nanotubes. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.
In another aspect, the present invention provides a method of purifying a sample containing single walled nanotubes comprising the steps of: (1) providing the sample containing the single walled nanotubes and impurities comprising metal particles, wherein the metal particles are at least partially enclosed by a plurality of carbon multilayers having a structure different from that of the carbon nanotubes; (2) adding an intercalant to the sample, wherein the intercalant inserts between at least a portion of the carbon multilayers enclosing the metal particles, thereby generating intercalated carbon multilayers having intercalant present between the carbon multilayers; and (3) adding an exfoliation initiator which reacts with intercalant present between the carbon multilayers, thereby exfoliating at least a portion of the carbon multilayers and exposing the surface of the metal particles; and (4) refluxing the sample in concentrated hydrochloric acid, thereby dissolving the metal particles and purifying the sample containing single walled nanotubes. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.
Referring to the drawings, like numerals indicate like elements and the same number appearing in more than one drawing refers to the same element. In addition, hereinafter, the following definitions apply:
“Carbon material” and “carbonaceous materials” are used synonymously in the present description and refer to a class of compounds comprising carbon atoms. Carbon materials include allotropes of carbon such as SWNTs, MWNTs, single walled and multiwalled fullerenes, graphite, graphene, amorphous carbon, carbon fibers, carbon films, carbon whiskers, and diamond, and all derivatives thereof. Carbon materials in the present invention may be entirely comprised of carbon atoms or may include carbon in combination with other elements, such as dopants, intercalants and functional groups conjugated to the carbon structures. Depending on the composition of the sample and intended outcome of the purification method, carbon materials may be classified as desired carbon materials or undesired carbonaceous impurities. Desired carbon materials have a selected structure (which depends on the precise application of the method) and are purified by the present methods. Carbonaceous impurities, in contrast, have a structure different from that of the desired carbon materials and are subject to removal by the present methods. Carbon materials, including both desired carbon materials and carbonaceous impurities, may exist in single or multilayer forms.
The term “carbon layer” refers to a structure of wherein certain atoms are held together by directed covalent, ionic or other strong intramolecular forces. Layers may be planar or contoured. Interactions between different carbon layers may be via intermolecular forces, such as van der Waals interactions. Examples of carbon layers include, but are not limited to, graphite layers, graphene sheets, walls of a multiwalled or single walled fullerenes, MWNTs, SWNTs, layers comprising carbon fiber and carbon films. Carbon layer may also refer to a carbonaceous impurity coating the outer surface of a particle, such as a residual metal catalyst particle, metal derivative particles such as metal oxide particles or particle comprising catalyst support material, and a carbonaceous impurity coating the outer surface of desired a carbon material, such as a carbon nanotube (SWNT and MWNT), a fullerene, other desired carbon allotrope. The terms “carbon layer” and “carbon layers” does not limit the size, shape or orientation of the layers.
“Exfoliation” refers to a process whereby adjacent layers are separated by a distance such that the strength of associative interactions between adjacent layers is decreased. Exfoliation of a multilayer material, such as a plurality of graphene sheets or graphite layers, includes separation of a single layer comprising a multilayer structure and includes involve separation of a plurality of layers comprising a multilayer structure. Exfoliation may involve separation of two different materials or separation of different layers of a multilayer material by disruption of associative interactions, such as van der Waals interactions, that hold the materials together. For example, the present invention provides methods of exfoliating carbonaceous impurities that coat a desired carbon material such as a carbon nanotube (SWNT or MWNT), fullerene, carbon fiber, diamond, and carbon film. In addition, the present invention provides methods of exfoliating carbonaceous impurities that coat particles, such as metal catalyst particles, metal derivative particles such as metal oxide particles, and particles comprising catalyst support materials. The present invention provides methods wherein carbon layers comprising carbonaceous impurities are either partially or entirely exfoliated.
“Intercalant” refers to a material that inserts into interstitial sites and/or endohedral sites in a single or multilayer receiving material. Addition of an intercalant to a receiving material comprising a carbon material (e.g. graphite, graphene, amorphous carbon, MWNTs etc.), generates intercalated carbonaceous material. In some cases, the intercalated carbonaceous material has a well defined stoichiometry with respect to the amount of intercalant associated with the carbon material. In one embodiment of the present invention, intercalant is added to a sample and inserts into interstitial sites between carbon layers in multilayer carbonaceous impurities and/or inserts into interstitial sites between a desired carbon material and a carbonaceous impurity coating its outer surface.
“Exfoliation initiator” refers to a material that reacts with intercalant in intercalated carbonaceous material, thereby causing at least partial exfoliation of the intercalated carbonaceous material. Exfoliation initiators may comprise molecules, ions, atoms or complexes thereof, and may be in solid, gas, liquid or solution phases.
“Metal catalyst particles” refer to metal particles generated by catalytic synthesis methods for generating carbon materials. Metal catalyst particles typically comprise transition metals and mixtures thereof including, but not limited to, nickel, molybdenum, palladium, yttrium, iron, copper, molybdenum; and cobalt.
“Purification” refers to a process whereby the percentage (or fraction) of a desired material in a sample is increased via processing. Purification methods of the present invention may increase the percentage by mass, percentage by weight, percentage by volume and/or mole fraction of one or more selected carbon materials in a sample undergoing processing. Purification methods of the present invention useful for some applications are capable of providing a purified selected carbon material having a structure and composition that does not vary significant from its structure and composition in the starting material subject to processing or has a structure that is enhanced after processing via the present methods, such as a structure exhibiting an enhanced extent of crystallinity. For example, methods of the present invention are capable of purifying a SWNT-containing sample such that the purified SWNTs are not present in derivatized (i.e. oxidized) or functionalized forms.
In the following description, numerous specific details of the devices, device components and methods of the present invention are set forth in order to provide a thorough explanation of the precise nature of the invention. It will be apparent, however, to those of skill in the art that the invention can be practiced without these specific details.
This invention provides methods of purifying samples containing a carbon material having a selected structure by removing carbonaceous, noncarbonaceous and multiphase impurities from the sample. Particularly, the present invention provides purification methods for samples containing selected carbon materials, such as carbon nanotubes (SWNTs and MWNTs), wherein carbonaceous impurities comprising carbon layers having a different structure than the selected carbon material are exfoliated, thereby facilitating subsequent removal of impurities via chemical transformation, for example by selective oxidation and/or dissolution processes.
Referring again to
As shown in process steps 3, 4 and 5 of
Referring to process step 6 of
Referring to process step 4 in
2C2H5OH+2K→2C2H5O−K++H2
In one embodiment, the sample is reacted with ethanol until a neutral pH is observed, indicating that substantially all the intercalated potassium has undergoing reaction. Exfoliation generates exfoliated carbonaceous material and also ruptures the multilayer structure of carbonaceous impurities enclosing the residual metal catalyst particles. Exfoliation provided by this processing step can disrupt and/or fracture the shell-like multilayer structure of carbonaceous impurities enclosing the residual metal catalyst particles resulting in at least partial exposure of their outer surfaces.
As shown in process steps 5 and 6 in
The methods of the present invention may be realized using a wide variety of instrumentation and reagents well known in the art. Use of a two bulb glass reactor and a two zone furnace is beneficial for adding gas phase potassium to the sample in a manner which minimizes the likelihood of condensing potassium on the sample undergoing processing. In this embodiment, the sample undergoing processing is held in a first bulb maintained at a slightly larger temperature and in fluid communication with a second bulb containing the potassium intercalant. Manipulation of samples undergoing purification in a glove box filled with any inert gas, such as argon, is helpful for avoiding inadvertent premature oxidation of intercalants comprising highly reactive alkali metals (e.g. K and Na) during intercalation of the sample. A variety of methods and instrumentation well known in the art may be used for electrochemically intercalating samples including voltammetric intercalation and electrolysis. Any intercalants and/or exfoliation initiators can be used in the present methods including electron donor intercalants, electron acceptor intercalants and combinations of both electron donor intercalants and electron acceptor intercalants. Exemplary intercalants useful for preparing intercalated carbon layers include, but are not limited to, Li, Na, K, Rb, Cs, F2, Cl2, Br2, I2, chromium oxides such as CrO3, metal chlorides such as CdCl2, YCl3, AlCl3, MOCl5, ZnCl2, FeCl3, sulfuric acid, nitric acid, perchloric acid, formic acid.
The terms and expressions which have been employed herein are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims. The specific embodiments provided herein are examples of useful embodiments of the present invention and it will be apparent to one skilled in the art that the present invention may be carried out using a large number of variations and additional processing steps including, but not limited to, sample transfer steps, temperature variation steps and cycles, product purity analysis, additional separations including phase separations, chromatographic separation, separation by filtration techniques such as microfiltration, removal of excess reagents such as process steps removing intercalants and/or exfoliation initiators added to the sample undergoing processing, and solution phase oxidation of carbonaceous impurities.
The following references relate generally to methods of exfoliating carbon materials: (1) “Exfoliation of carbon fibers”, M. Toyoda and M. Inagaki, Journal of Physics and Chemistry of solids, 65 (2004) 109-117; (2) Review of the doping of carbon nanotubes (multiwalled and single-walled)”, L. Duclaux, Carbon, 40 (2002), 1751-1764; (3) “Exfoliation process of graphite via intercalation compounds with sulfuric acid”, M. Inagaki, R. Tashiro, Y. Reactino and M. Toyoda, Journal of Physics and Chemistry of solids, 65 (2004) 133-137; (4) “Graphite exfoliated at room temperature and its structural annealing” M. Inagaki and M. Nakashima, Carbon, Vol. 32, No. 7 (1994), 1253-1257; (5) “Exfoliation process and elaboration of new carbonaceous materials”, Fuel, Vol 77, No. 6, (1998) 479-485; and (6) “Electrochemical intercalation of ZnCl2—CrO3GIC (graphite intercalation compound) with sulphuric acid”, J. M. Skowronski and J. Urbaniak, Polish J. Chem. 78 (2004) 1339-1344.
All references cited in this application and all references cited in these references are hereby incorporated in their entireties by reference herein to the extent that they are not inconsistent with the disclosure in this application. It will be apparent to one of ordinary skill in the art that methods, devices, device elements, materials, procedures and techniques other than those specifically described herein can be applied to the practice of the invention as broadly disclosed herein without resort to undue experimentation. All art-known functional equivalents of methods, devices, device elements, materials, procedures and techniques specifically described herein are intended to be encompassed by this invention.
The ability of methods of the present invention using potassium intercalation to purify SWNTs was experimentally verified by purifying SWNT containing samples generated using arc discharge synthesis methods. Thermogravimetric analysis (TGA), Raman spectrometry, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to characterize the results of each processing step, and to evaluate the effectiveness of the purification treatment. The purified SWNT products generated by the present methods were compared to SWNT samples purified via conventional acid reflux purification methods. This potassium intercalation step was found to be particularly useful for exfoliating the graphitic shell structure that typically surround residual metal catalyst particles present in samples prepared by many catalytic synthesis methods. By exfoliating the shell structure, subsequent treatments are more efficacious for removing the metal catalyst particles.
1.a Introduction
There have been many investigations of single-wall carbon nanotubes (SWNTS) since these materials were first reported in the early Nineties. The unique physical, chemical and mechanical properties of SWNTs make them candidate materials for service in electronic devices, energy storage systems and structural composites, for example. To obtain behavior in these applications that can be unambiguously and solely attributed to nanotubes, purification of the SWNTs is an essential step, since raw materials are typically composed of less than half SWNTs. The efficiency of any purification method is strongly dependent on the raw materials, which differ for the three methods typically used for the production of SWNTs: chemical vapor deposition (CVD), electric arc-discharge and laser ablation.
It has proved a serious challenge to remove multiwalled nanotubes and shells, incomplete fullerenes, graphites, and disordered carbon impurities in the raw materials without also destroying the SWNTs, since all these components are similar chemically. In this example, we concentrate on the purification of SWNTs prepared by arc-discharge and laser oven/ablation because these methods produce SWNTs with a narrow distribution of tube diameters. Important impurities in materials prepared by arc-discharge and laser oven/ablation methods also include metal catalyst particles, which are typically surrounded by shells of polyaromatic carbons. The shell structure protects the metal particles from dissolution in inorganic acids.
Many procedures for purifying SWNTs are based on chromatography and filtration methods, or on selective oxidation processes (i.e. acid oxidation and/or gas oxidation), or a combination of these methods. For any method of purification, a compromise is typically made between impurity removal and the final yield of SWNTs. Another concern is that some purification processes can damage the nanotubes. Refluxing in nitric acid, for example, is effective for removing metallic impurities, but also produces defects in the tubes.
Method of the present invention using a potassium intercalation processing step was used to purify arc-derived carbon SWNTs, which are generally recognized as the most challenging to purify. The present purification methods procedure comprise the steps of: (a) intercalating the SWNT containing sample with potassium (b) reacting/exfoliating the resulting powder with ethanol and (c) wet air oxidation at successively higher temperatures, with each step followed by a reflux in concentrated hydrochloric acid. Low temperature wet air oxidation has generally been thought to remove the more disordered carbon layer coatings on metal catalyst particles, allowing the dissolution of the metal in an acid. Oxidation treatments at higher temperatures remove the more stable carbon layer graphitic shells surrounding the catalyst metal particles. During these wet air oxidation treatments, the metal is converted to an oxide and/or hydroxide. The expansion of the metal due to the lower density of the oxide (densities for Ni and NiO are respectively 8.90 and 6.67) cracks the carbon shells and the metal oxide, thus is exposed and is subsequently dissolved by the proper acid.
The step of potassium intercalation followed by reacting with ethanol causes more complete exfoliation of the intercalated layers, weakening the carbon shell structure covering the metallic particles. These structures are therefore more easily cracked by wet air oxidation, more completely exposing the metal catalyst. Each of these steps contributes to the purification, and the combination of potassium intercalation, wet air oxidation and hydrochloric acid treatments produces a high-purity SWNT containing purified sample. By using transmission electron microscopy, Raman spectrometry, x-ray diffractometry, and thermogravimetric analysis, we show that the methods of the present invention provide better yields and purities than another process involving a more established purification process involving a combination of refluxing in HNO3, centrifugations, refluxing in H2O2 and wet oxidations in air at different temperatures (350 to 520° C.).
1.b Experimental
Single-wall carbon nanotube materials produced by the arc-discharge method with a Ni—Y catalyst (5 at. %) were obtained from Carbolex Inc. According to the manufacturer the as-received sample purity may vary from 70 to 90 vol. %, and it contains residual catalyst impurities.
The as-received SWNT-containing sample was first evacuated and heated to 300° C. to remove any trace of moisture and O2. Using an argon-filled glove box, samples were then loaded into a two-bulb reactor of the type used to synthesize graphitic potassium intercalation compounds. The carbon material and the potassium metal intercalant are put into each bulb of a glass reactor, evacuated, and then placed into a two-zone furnace. The potassium zone temperature was maintained at 250° C., whereas the nanotube zone temperature was adjusted to higher temperature to minimize the possibility that potassium metal might condense on the sample. The masses of potassium and carbon material were chosen to allow the formation of the most potassium-rich intercalation compound, KC8. After reaction for two days, the potassium-doped nanotubes were reacted with ethanol until a neutral pH was obtained. The sample was then refluxed in concentrated hydrochloric acid (37%) for 24 hours: a typically green acid color was observed due to the dissolved Ni2+. The materials were then subjected to a low temperature oxidation (350° C. during 24 hours) under flow of wet air, and again refluxed with HCl to further remove exposed catalyst particles. A final wet air oxidation at 450° C. with a shortened oxidation time of 2.5 hours was subsequently performed, followed by an HCl treatment. As a final step, to repair possible damage to the tube walls, the sample was annealed in nitrogen forming gas at 750° C. for 2 hours.
Thermogravimetric analysis (TGA), Raman spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to evaluate the effectiveness of the purification treatments and to determine the relative purity of the SWNTs.
For TGA analysis, the nanotube samples were loaded into an alumina crucible, and a flow of argon was maintained at 40 mL/min while heating at 10° C./min from room temperature to 200° C. This temperature was held for 20 minutes under the argon flow and then for another 20 minutes under a 50:50 Ar/O2 mixture. The chamber was then maintained under a continuous Ar/O2 flow while the temperature was incrementally raised at 5° C./min to 700° C. or 1000° C. The time (t) dependence of the sample mass (m) was recorded.
To investigate possible SWNT damage from the steps of the purification process, Raman spectra were acquired at room temperature with a Renishaw Micro Raman spectrometer using a 514.5 nm argon ion laser with spectral resolution of 1 cm−1. The samples were encapsulated in argon-filled glass ampoules, and to prevent the loss of potassium from the samples or other instabilities, Raman measurements were made with low laser power.
The crystallinity of the nanotube rope structure and the evolution of the impurity phases during purification were studied by x-ray diffractometry (XRD) and transmission electron microscopy (TEM). X-ray powder diffraction was performed with a Cu Kα X-ray source (Philips PW3040, λ Cu=1.54056 Å, 45 kV, 40 mA). Morphological observations of the as-received SWNTs were obtained by TEM measurements using a Philips EM420 operated at 100 kV.
1.c Results and Discussion
1.c.(i) Thermogravimetric Analysis
When heated in the presence of oxygen gas, carbon materials undergo oxidation, forming the gases CO or CO2. Any material remaining after all of the carbon has been consumed is the initial metal catalyst in oxide form.
For the data in
For both sets of procedures, the samples underwent a final anneal at 750° C. under flowing forming gas consisting of nitrogen plus hydrogen. In comparing the TGA curves after the first step of purification for each method,
Yields were measured corresponding to the present purification process and the conventional process examined. The SWNT content remaining in the sample at the end of the present purification process involving potassium intercalation/exfoliation is about 18 wt. % whereas the total yield of carbon nanotubes for the more established purification process combining refluxing in nitric acid, refluxing in H2O2 and wet oxidations in air is less than a few weight percent.
1.c(ii) Micro Raman Spectroscopy
The spectrum from as-received AP Carbolex material (plot (a) in
1.c(iii) X-Ray Diffraction
1.c(iv) TEM Images of Sample After Purification
1.d Conclusion
The present methods are effective for purifying carbon single-wall nanotubes synthesized by the arc-discharge process. The processing step of potassium intercalation and subsequent reacting with EtOH exfoliates the graphite impurities, and exfoliates the graphitic shells around the metal catalyst particles. After intercalation, the metal catalyst particles are more susceptible to removal by subsequent wet oxidation treatments coupled with HCl reflux steps. It is demonstrated that purification methods using this intercalation step decreases the catalyst content to levels that are obtained by a conventional purification process, however, using fewer purification steps. Evidence for the efficacy of this potassium intercalation step was provided by TGA measurements and TEM observations. Raman spectroscopy indicated that the structural integrity of the nanotubes was not compromised by the various stages of purification. XRD showed good crystallinity of the material after purification.
The present invention provides versatile methods for purifying a range of carbon materials in samples generated by catalytic synthesis techniques. The ability of methods of the present invention using potassium intercalation to purify carbon materials other than carbon nanotubes was experimentally verified by purifying samples containing carbon nanofibers generated by catalytic synthesis. The synthesis and characteristics of theses fibers has been reviewed by K. P. De Jong and J. W. Geus in Catalysis reviews-Science and Engineering, 42 (2000) pp 481-510. X-ray diffraction (XRD) is used to characterize the composition of the starting carbon fiber-containing sample and the composition of the sample after important processing steps of the present methods. The experimental results provided in this example illustrate that the present methods provide an effective, nondestructive pathway for purifying samples containing carbon nanofibers. Similar to the experimental results obtained for SWNTs (See e.g., Example 1), potassium intercalation followed by reacting in ethanol was observed to be particularly useful for enhancing the removal of residual metal catalyst particles by dissolution in an acid solution.
Carbon fiber materials subject to purification were vapor grown via catalytic growth techniques and, therefore, had a significant impurity comprising residual cobalt-iron catalyst particles having a composition of about 50 percent iron by mass and about 50 percent cobalt by mass. (see for example: M. Audier et al. in J. Crystal Growth 55(1981) 549-556) The starting carbon fiber-containing sample was first evacuated and heated to 300° C. to remove any trace of moisture and O2. Using an argon-filled glove box, samples were then loaded into a two-bulb reactor of the type used to synthesize graphitic potassium intercalation compounds. The carbon material and the potassium metal intercalant are put into each bulb of a glass reactor, evacuated, and then placed into a two-zone furnace. The potassium zone temperature was maintained at 250° C., whereas the nanotube zone temperature was adjusted to higher temperature to minimize the possibility that potassium metal might condense on the sample. Intercalation of the carbon fiber-containing sample proceeded under these conditions for two days. After intercalation, the potassium-doped nanotubes were reacted with ethanol to initiate exfoliation. The sample was then refluxed in concentrated hydrochloric acid for 24 hours. The materials were then subjected to a low temperature oxidation (350° C. during 24 hours) under a flow of wet air, and again refluxed with HCl for 24 hours to further remove exposed catalyst particles. A final wet air oxidation at 450° C. with a shortened oxidation time of 2.5 hours was subsequently performed, followed by another treatment with concentrated HCl for 24 hours. As a final step, the sample was annealed in nitrogen-hydrogen forming gas at 750° C. for 2 hours to repair any damage to the carbon fibers and improve crystallinity.
2.a X-Ray Diffraction Results
The experimental results provided in this example demonstrate the applicability of the present methods for purifying carbon fibers materials generated by catalytic synthesis. The processing step of potassium intercalation and subsequent reacting with ethanol exfoliates carbonaceous impurities that form shells around residual metal catalyst particles. After intercalation, the residual metal catalyst particles are more susceptible to removal by subsequent wet oxidation treatments coupled with HCl reflux steps. XRD patterns obtained before, during and after sample processing, indicate the present methods provide an effective pathway for removing metal catalyst impurities and that the present methods provide a source of purified carbon fibers exhibiting good crystallinity.
2.b TEM Images of Sample Before and After Purification
This application claims priority under 35 U.S.C. 119(e) to U.S. provisional Patent Application 60/553,930 filed Mar. 17, 2004, which is hereby incorporated by reference in its entirety to the extent not inconsistent with the disclosure herein.
This invention was made, at least in part, with United States governmental support awarded by Department of Energy Grant DE-FC36-01GO11090. The United States Government has certain rights in this invention.