Patent Application
20130095996
Methods of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support are described in this application. The sorbents in the methods described herein can adsorb gases such as carbon dioxide. The carbon dioxide can be adsorbed from the air or from carbon dioxide point sources like off-gases or intentionally produced carbon dioxide, or from their mixtures. The sorbents described herein can be used for gas purification or for gas separation.
U.S. Pat. No. 7,378,561 discusses a method for producing methanol and dimethyl ether using the air as the sole source of materials is disclosed. The method relates to separating water (i.e., the moisture in the air) and carbon dioxide content of atmospheric air for their use in the subsequent production of methanol, dimethyl ether and derived synthetic hydrocarbons as products. The method includes the conversion of carbon dioxide and water under conditions sufficient to produce methanol and/or dimethyl ether. Carbon dioxide is captured on a suitable absorbent, preferentially polyethyleneimine supported on nano-structured fumed silica.
WO2008/021700 discusses regenerative, supported amine sorbents that include an amine or an amine/polyol composition deposited on a nano-structured support such as nanosilica.
JP 61-227821 discusses a method for removing carbon dioxide gas by adsorption via a solid amine adsorbent.
Chen et al., Gel-coated polymeric solid amine for sorption of carbon dioxide from humid air, Journal of Polymer Materials (2002), 19(4), 381-387, discusses adsorption of carbon dioxide using polyethyleneimine.
WO2009/149292 discusses a method for capturing carbon dioxide from an air stream, comprising exposing one or more collection surfaces formed of a solid sorbent material, wherein the solid sorbent material absorbs carbon dioxide from the air stream.
U.S. Patent Application Publication 2008/0289495 provides a system for removing carbon dioxide from an atmosphere to reduce global warming which can increase availability of renewable energy or non-fuel products such as fertilizers and construction materials, comprising: an air extraction system that collects carbon dioxide from the atmosphere through a medium and removes carbon dioxide from the medium; a collection system that isolates the removed carbon dioxide to a location for at least one of sequestration, storage and generation of a renewable carbon fuel or non-fuel products such as fertilizers and construction materials; and one or more energy sources that supply process heat to the air extraction system to remove the carbon dioxide from the medium and which can regenerate it for continued use.
U.S. Patent Application Publication 2007/0149398 provides a carbon dioxide sorption structure, comprising: a high surface area structure that includes a plurality of pores in the high surface area structure, wherein each pore has an inside surface, wherein at least the inside surface of the pore includes hydroxyl groups on the surface; and a hyperbranched polymer covalently bonded to the inside surface of the pore via the oxygen of the hydroxyl group on the inside surface of the pore.
There continues to be an increased need throughout the world to limit release of carbon dioxide.
As evidenced by some of the references discussed hereinabove, it has been difficult to develop high-performing and cost-effective carbon dioxide capture/separation technologies.
Therefore, there still remains a need in the industry to develop technologies that provide high-performing and cost-effective adsorption of carbon dioxide and/or other gases.
According to one embodiment, a method of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support is disclosed. The method comprises: (i) optionally, preparing the substrate coated with the support by pre-treating the substrate with a slurry, wherein the slurry comprises: a. solvent, b. a binder, c. the support, and d. optional dispersant; and (ii) treating the substrate, the support, and/or the substrate coated with the support, with a sorbent; wherein the substrate is (a) a monolithic or honeycomb structure made of ceramic, metal, or plastic; (b) a polyurethane foam, a polypropylene foam, a polyester foam, a metal foam, or a ceramic foam; or (c) woven or non-woven plastic or cellulosic fibers, wherein the support is alumina, silica, silica-alumina, titania, zirconia, carbon, zeolite, metal-organic framework (MOF), or combinations thereof, and wherein the sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof.
According to another embodiment, a method of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support is disclosed. The method comprises: (i) treating the substrate, the support, and/or the substrate coated with the support, with a slurry comprising: a. a solvent, b. a binder, and c. the sorbent; wherein the substrate is (a) a monolithic or honeycomb structure made of ceramic, metal, or plastic; (b) a polyurethane foam, a polypropylene foam, a polyester foam, a metal foam, or a ceramic foam; or (c) woven or non-woven plastic or cellulosic fibers, wherein the support is alumina, silica, silica-alumina, titania, zirconia, carbon, zeolite, metal-organic framework (MOF), or combinations thereof, and wherein the sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof.
In other embodiments, the sorbent coated substrate, the sorbent coated support, and the sorbent coated substrate coated with the support of the above-discussed methods are described.
In yet other embodiments, the sorbent coatings of the above-discussed methods are described.
In the embodiments described in this disclosure, the sorbents in the methods described herein can adsorb gases such as carbon dioxide.
According to an embodiment, an alumina support comprising a sorbent coating is disclosed, wherein the sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof, and wherein the alumina support has a surface area of about 150 m2/g to 250 m2/g and a pore volume of about 0.7 cc/g to 1.5 cc/g.
The terms “about” or “approximately” when used herein and associated with a numeric value refer to that numeric value plus or minus 10%, preferably plus or minus 5%, more preferably plus or minus 2%, most preferably plus or minus 1%.
According to one embodiment, a method of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support is disclosed. The method comprises:
(i) optionally, preparing the substrate coated with the support by pre-treating the substrate with a slurry, wherein the slurry comprises: a. solvent, b. a binder, c. the support, and d. optional dispersant; and
(ii) treating the substrate, the support, and/or the substrate coated with the support, with a sorbent.
The dispersants can be anionic, cationic, or non-ionic selected from the group consisting of polyacrylates, alkoxylates, carboxylates, phosphate esters, polyether polymers, sulfonates, sulfosuccinates, stearates, laureates, amines, amides, imidazolines, sodium dodecylbenzene sulfonate, sodium dioctyl sulfosuccinate, polyoxypropylene-polyoxyethylene polymer, alkyl phenyl ethoxylates, and mixtures thereof. Preferred dispersants include polyacrylic acid polymers and polyethers.
The substrate is (a) a monolithic or honeycomb structure made of ceramic, metal, or plastic; (b) a polyurethane foam, a polypropylene foam, a polyester foam, a metal foam, or a ceramic foam; or (c) woven or non-woven plastic or cellulosic fibers that are either natural or manufactured.
The support is alumina, silica, silica-alumina, titania, zirconia, carbon, zeolite, metal-organic framework (MOF), or combinations thereof.
The support may contain promoters such as lanthanum, ceria, or barium to stabilize the support and/or enhance the effectiveness of the sorbent.
The sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof.
The “sorbent” as referred to herein includes one sorbent or a mixture of sorbents alone or coated on the substrate, the support, and/or the substrate coated with the support.
The sorbent coating on the substrate, the support, and/or the substrate coated with the support can be used to adsorb carbon dioxide from the air or from carbon dioxide point sources like off-gases or intentionally produced carbon dioxide, or from their mixtures. The carbon dioxide obtained in this manner can be used for further storing and/or in several applications such as enhanced oil recovery, carbonation of beverages, for food processing/cooling/freezing, as reactant in the production of chemicals, as feedstock for algae, or as a fire extinguishing medium.
The sorbent coating on the substrate, the support, and/or the substrate coated with the support can also be used for gas purification or for gas separation. For example, the sorbent can be used in natural gas purification and/or breathing air purification, such as submarine air purification, air treatment in air conditioning devices, or hospital air purification. The sorbent can adsorb carbon dioxide to purify natural gas, ambient air, flue gas, or other impure gas mixtures containing carbon dioxide.
Burning of methane produces carbon dioxide which is an example of intentionally produced carbon dioxide.
According to an embodiment,
Step (i) of the above double-dip method can further comprise:
a. coating the substrate with the slurry;
b. removing excess solvent from the coated substrate; and
c. calcining the binder and the support onto the substrate.
The calcining can occur at a temperature range of 200° C. to 550° C., preferably a temperature of 425° to 475° C., and more preferable at a temperature of 450° C.
The binder in step (i) of the double-dip method can be alumina sol, aluminum oxide hydroxide, silica sol, titania sol, zirconium acetate, silicone, or combinations thereof.
The slurry containing support and/or binder can be milled to have a D50 particle size ranging from 1 μm to 10 μm and more preferably a D50 particle size ranging from 3 μm to 6 μm.
The double-dip method can further comprise:
(iii) after step (ii), drying the treated substrate to remove excess amounts of the sorbent and to remove excess solvent to obtain a sorbent coated substrate, a sorbent coated support, and/or a sorbent coated substrate coated with a support.
The drying in step (iii) can occur in air at a temperature range of 30° C. to 70° C., more preferably at a temperature range of 40° C. to 60° C., and most preferably at a temperature 50° C. Alternatively the drying can occur in an oxygen-free environment at a temperature up to 110° C.
As provided hereinabove, the slurry comprises: a. solvent, b. a binder, and c. the support, and d. optional dispersant. The binder is typically added in an amount of about 0 to 10 wt % based on the total weight of the support, more preferably in an amount of about 3 to 7 wt % based on the total weight of the support, and even more preferably in an amount of about 6.5 wt % based on the total weight of the support.
In some embodiments, the total solids (support+binder) amount is typically about 15 to 50 wt % based on the total slurry weight. In some embodiments, a surfactant or mixtures of surfactants can be added to help disperse the support (e.g., alumina) in the slurry. The surfactant or mixtures of surfactants can be added in an amount of up to about 10 wt % based on the total weight of the support.
In some embodiments, the sorbent (e.g., PEI) is typically added in an amount of about 25 to 100 wt % based on the total weight of the support and more preferably in an amount of about 40 to 70 wt % based on the total weight of the support.
The amount of PEI that results in the coating as a percentage of the total coating weight (PEI+alumina) is about 20% to 50% with a more preferred range of 30 to 40%. The coating is the total amount of non-solvent material applied to the substrate that remains after drying. For the final part, this includes the support and sorbent and/or binder.
A two-coat coating process includes the following steps. Make first slurry by blending ingredients into a solvent. Typical ingredients are listed below. The total wt % solids in the slurry are typically 20 wt % to 50 wt %. The slurry is applied to the substrate by various methods such as dip-coating or spraying. The coated substrate is dried either partially or wholly to remove excess moisture. The part is then calcined to activate binder. In the case of a honeycomb substrate the amount of coating that is on the part is typically 0.5 g/in3 to 2.0 g/in3 and preferably 1.0 to 1.7 g/in3.
The second coating formulation is made by mixing organic sorbent into solvent (for example PEI in water). The formulation may also contain a dispersant to aid in wetting the support surface. The total wt % solids in the slurry are typically 20 wt % to 50 wt %. This formulation is applied to the substrate by various methods such as dip-coating or spraying. The coated substrate is dried either partially or wholly to remove excess moisture. Typically at least 50 wt % of the solvent is removed by drying. Drying is done under conditions so as to not degrade the organic performance as a CO2 sorbent (low temperature and/or low oxygen content).
According to another embodiment, a method of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support is disclosed. The method comprises:
(i) treating the substrate, the support, and/or the substrate coated with the support, with a slurry comprising: a. a solvent, b. a binder, and c. the sorbent; wherein the substrate is (a) a monolithic or honeycomb structure made of ceramic, metal, or plastic; (b) a polyurethane foam, a polypropylene foam, a polyester foam, a metal foam, or a ceramic foam; or (c) woven or non-woven plastic or cellulosic fibers.
As provided hereinabove, the support is alumina, silica, silica-alumina, titania, zirconia, carbon, zeolite, metal-organic framework (MOF), or combinations thereof.
The supports may contain promoters such as lanthanum, ceria, or barium to stabilize the support and/or enhance the effectiveness of the sorbent.
As further provided hereinabove, the sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof.
The single-dip method can further comprise:
(ii) after step (i), drying the slurry treated substrate, support, and/or substrate coated with the support; and then
(iii) removing excess sorbent and solvent at a temperature so as to prevent degradation of the binder or the sorbent to obtain a sorbent coated substrate, a sorbent coated support, and/or a sorbent coated substrate coated with a support.
The drying in step (ii) of the single-dip method can occur at a temperature range of from 50° C. to 150° C., more preferably, at a temperature range of from 70° C. to 110° C.
The binder in step (i) can be selected from the group consisting of polyethylene, polypropylene, polyolefin copolymers, polyisoprene, polybutadiene, polybutadiene copolymers, chlorinated rubber, nitrile rubber, polychloroprene, ethylene-propylene-diene elastomers, polystyrene, polyacrylate, polymethacrylate, polyacrylonitrile, poly(vinyl esters), poly(vinyl halides), polyamides, cellulosic polymers, polyimides, acrylics, vinyl acrylics and styrene acrylics, polyvinyl alcohol, thermoplastic polyesters, thermosetting polyesters, poly(phenylene oxide), poly(phenylene sulfide), fluorinated polymers such as poly(tetrafluoroethylene)polyvinylidene fluoride, poly(vinylfluoride) and chloro/fluoro copolymers such as ethylene chlorotrifluoro-ethylene copolymer, polyamide, phenolic resins and epoxy resins, polyurethane, silicone polymers, and combinations thereof.
The binder can be added in an amount of about 6 to 25 wt % based on the weight of the support, more preferably in an amount of about 8 to 16 wt % based on the weight of the support, and even more preferably in an amount of about 10 to 14 wt % based on the weight of the support.
A single-coat coating process includes the following steps. Make slurry by blending ingredients into a solvent. Typical ingredients are listed below. The total wt % solids in the slurry are typically 20 wt % to 50 wt %. The slurry is applied to the substrate by various methods such as dip-coating or spraying. The coated substrate is dried either partially or wholly to remove excess moisture and to activate binder. Drying is done under conditions so as to not degrade the organic performance as a CO2 sorbent (low temperature and/or low oxygen content). In the case of a honeycomb substrate the amount of coating that is on the part is typically 1.0 g/in3 to 4.0 g/in3 and preferably 2.0 to 3.4 g/in3.
The ceramic substrate in the double-dip and/or the single-dip method(s) can be selected from the group consisting of cordierite, alumina, cordierite-α alumina, silicon nitride, zircon mullite, spodumene, alumina-silica magnesia, zircon silicate, sillimanite, magnesium silicates, zircon, petalite, aluminosilicates, and combinations thereof.
More preferably, the ceramic substrate can be cordierite, alumina, or a combination thereof.
The metal substrate in the double-dip and/or the single-dip method(s) can be aluminum, titanium, stainless steel, a Fe—Cr alloy, or a Cr—Al—Fe alloy in the form of a sheet, mesh, foil, flakes, powder, wire, rod, or combinations thereof.
More preferably, the metal substrate can be aluminum, stainless steel, Cr—Al—Fe alloy, or combinations thereof in the form of a sheet, mesh, or foil.
The plastic substrate in the double-dip and/or the single-dip method(s) can be a polymer and/or copolymer of polyolefin(s), polyester(s), polyurethane(s), polycarbonate(s), polyetheretherketone(s), polyphenylene oxide(s), polyether sulfone(s), melamine(s), polyamide(s), polyacrylates, polystyrenes, polyacrylonitriles, polyimides, polyfurfural alcohol, phenol furfuryl alcohol, melamine formaldehydes, resorcinol formaldehydes, cresol formaldehyde, phenol formaldehyde, polyvinyl alcohol dialdehyde, polycyanurates, polyacrylamides, various epoxies, agar, and agarose, or combinations thereof.
More preferably, the plastic substrate can be a polymer and/or copolymer of polyolefin, polyester, polyurethane, melamine, polypropylene, or polyamide.
The monolithic structure (substrate) can be made of cellulosic fibers (i.e., paper).
The substrate can be made of a ceramic pellet or a carbon pellet.
The examples herein were made on ceramic honeycombs. However, the choice of the particular substrate can be determined by the unique properties of each and their resultant impact on the commercial design of the system. For example, in applications where reducing the weight of the system is critical, or where the pressure drop through the honeycomb is critical, the metallic and cellulosic fiber honeycombs can offer advantages compared to ceramic honeycombs. In applications where heat transfer is critical, the metallic honeycombs can offer advantages compared to the ceramic. In applications where multiple sorbents may be required, the ceramic honeycombs can offer advantages over the other honeycombs.
The polyolefin can be ethylene vinyl acetate, ethylene methyl acrylate, polyethylene, polypropylene, ethylene-propylene rubber, ethylene-propylene-diene rubbers, poly(1-butene), polystyrene, poly(2-butene), poly(1-pentene), poly(2-pentene), poly(3-methyl-1-pentene), poly(4-methyl-1-pentene), 1,2 poly-1,3-butadiene, 1,4-poly-1,3-butadiene, polyisoprene, polychloroprene, poly(vinyl acetate), poly(vinylidene chloride), poly(vinylidene fluoride), poly(tetrafluoroethylene) or a mixture thereof.
The polyester can be polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polyethylene naphthalate (PEN), copolymers of PET, copolymers of PBT and copolymers of PEN.
The monolithic structure in the double-dip and/or the single-dip method(s) can have channels having about 50 to about 900 cells per square inch.
The channels can be square, triangular, or sinusoidal in cross-section.
The channels can be straight, zig-zag, skewed, or herringbone in shape.
The channels can have walls that are perforated or louvered.
The ceramic or plastic monolithic structure in the double-dip and/or the single-dip method(s) can be made by extrusion.
The metal or plastic monolithic structure in the double-dip and/or the single-dip method(s) can be made by layering corrugated metal foil or corrugated plastic sheets.
The solvent in the double-dip and/or the single-dip method(s) can be selected from the group consisting of water, methanol, ethanol, toluene, isopropanol, 2-methoxyethyl ether, and mixtures thereof.
According to an embodiment, an alumina support comprising a sorbent coating is disclosed. As discussed hereinabove, the sorbent adsorbs carbon dioxide and the sorbent is selected from the group consisting of amines; monoethanolamine; diethanolamine; polyethylenimine (PEI); aminopropyltrimethoxysilane; polyethyleneimine-trimethoxysilane; amide or amine containing polymers including nylon, polyurethane, polyvinylamine, or melamine; and combinations thereof. In some preferred embodiments, the sorbent is polyethylenimine (PEI).
The alumina support has a surface area of about 150 m2/g to 250 m2/g and a pore volume of about 0.7 cc/g to 1.5 cc/g. In some preferred embodiments, the alumina support has a surface area of about 170 m2/g to 180 m2/g and a pore volume of about 0.9 cc/g to 1.2 cc/g. In even more preferred embodiments, the alumina support has a surface area of about 175 m2/g and a pore volume of about 1.1 cc/g.
It will now be apparent to those skilled in the art that this specification describes new, useful, and nonobvious methods of applying a sorbent coating on a substrate, a support, and/or a substrate coated with a support are described in this application. It will also be apparent to those skilled in the art that numerous modifications, variations, substitutes, and equivalents exist for various aspects of the invention that have been described in the detailed description above. Accordingly, it is expressly intended that all such modifications, variations, substitutions, and equivalents that fall within the spirit and scope of the invention, as defined by the appended claims, be embraced thereby.
A slurry was made by mixing 45.22 g of alumina with 4.52 g of aluminum oxide hydroxide and 169.48 g of water. This slurry was coated onto honeycomb made of cordierite such that 1.15 g/in3 of alumina coating was applied. This alumina coated honeycomb was then impregnated with polyethylenimine (PEI) by immersing in an aqueous solution having 20% PEI. The so prepared core was tested for CO2 adsorption capacity (described hereinbelow in Example 3—Adsorption Test) and found to adsorb 4.20 mmol CO2/g of PEI.
Flow 400 ppm CO2 in air with 1% water through adsorbent coated honeycomb at 35° C. at a velocity of 2.5 msec until sample is saturated with CO2. Desorb the CO2 by flowing nitrogen with 1% water at 110° C. through the core. Adsorb CO2 again at the same conditions as previous adsorption.
Prior to conducting the adsorption measurement, each sample undergoes a treatment of exposing the sample to a flow of 400 ppm CO2 in air with 1% water at a velocity of 2.5 msec and at a temperature of 35° C. until the sample is saturated with CO2. The sample is sorbent impregnated onto a support coated onto a substrate: for example PEI on alumina coated onto a ceramic honeycomb. The sample is then purged of CO2 by flowing nitrogen with 1% water through the sample at 2.5 msec and a temperature of 110° C. until no more CO2 is released. Then the adsorption measurement is conducted by flowing 400 ppm CO2 in air with 1% water at a velocity of 2.5 msec and at a temperature of 35° C. through the sample until it is saturated with CO2.
Samples were made by the double-dip coating method. The first coat was made by applying a water based slurry having the composition listed below to ceramic honeycomb. Each sample was made using a different alumina (alumina A thru K) having different properties of surface area and pore structure.
First Coating Composition:
This was calcined to adhere the coating. The weight of this first coat is approximately 1.2 g/in3 of honeycomb.
Polyethylenimine was applied as a second dip from an aqueous solution resulting in an organic fraction of the total coating of 26% to 39% (see table). (organic fraction is (PEI weight divided by (alumina plus binder weight) the dispersant is not counted because it is removed by the calcining step).
These samples are prepared in the same method as example 3 (double-dip with same bill-of-materials) with the exception that the amount of PEI applied was varied between the samples The organic fraction of each of the samples is given in the table.
This coating weight includes both the alumina and polyethylenimine (PEI) weight As can be seen in
A sample was prepared by the method of Example 3 provided hereinabove having a total coating loading of 2.1 g/in3 with 29% of the coating as PEI. This sample was evaluated for CO2 adsorption capacity by flowing gas containing 4000 ppm of CO2, 12% oxygen, 1% water, and balance nitrogen at a flow of 2.5 msec until saturated with CO2. The sample was found to adsorb 3.88 mmol of CO2 per gram of PEI.
The present invention has been described by way of the foregoing exemplary embodiments to which it is not limited. Variations and modifications will occur to those skilled in the art that do not depart from the scope of the invention as recited in the claims appended thereto.
This application claims priority to U.S. Provisional Patent Application No. 61/543,999, filed on Oct. 6, 2011, which is hereby incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61543999 | Oct 2011 | US |