The invention relates to polymeric materials that are used to conduct electrical signals, and relates in particular to conductive adhesives that are used with medical monitoring sensors that are placed directly on a patient, such as an electro-cardiogram (EKG) sensor.
Electrically conductive pressure-sensitive adhesives for use in biomedical applications are disclosed, for example, in U.S. Pat. No. 4,848,353. Since such conductive materials typically depend on the presence of water, however, the material must be maintained in a sealed environment until being used. See also, U.S. Pat. No. 5,143,071, which discloses non-stringy adhesive gels for that are hydrophilic.
Such substances must be isolated from the environment prior to use (e.g., in sealed packages), and may function improperly if allowed to lose water from the conductive material. These limitations adversely affect both the cost of sensors that use such conductive adhesives as well as the amount of use that any particular sensor may enjoy.
There is a need therefore, for a material that may be used to conduct electricity yet is not susceptible to variations in the water vapor content of the environment in which it is used.
The invention provides an alternating current responsive composite. The composite includes a polymeric material and a polar material that is substantially dispersed within the polymeric material. The polar material is responsive to the presence of an alternating current. In various embodiments, the polar material includes an organic salt and the polymeric material includes a pressure sensitive acrylic adhesive.
The following description may be further understood with reference to the accompanying drawings in which:
The drawings are shown for illustrative purposes and are not to scale.
It has been discovered that a polar material (such as an organo salt) may be dispersed within a polymeric material of sufficient concentration that the resulting composite may be responsive to the presence of an alternating current yet not be sensitive to water gain or loss from ambient temperature or humidity conditions. For example, as shown in
A suitable combination of polar material and polymeric material may be identified by the following procedure. First, a polar material is combined with the polymeric material in about five different concentrations (typically between about 5% to about 45% by weight). Then the adhesive-salt composite is drawn onto a release liner (of about 1.5 mil), and permitted to dry and cure. The surface of the composite is then inspected after a short period of time. If the salt has crystallized out or bloomed to the surface, then the combination of components is not compatible. If, on the other hand, the composite is clear, it is subject to the next level of compatibility testing. The samples should then be subjected an exposure test in which the samples are exposed to 100 F with 95% relative humidity for 3 days. The samples are then again inspected to determine whether the polar material has migrated toward either surface. If there has been no migration of the polar material and the composite is clear, then the dielectric constant for the composite is determined and the composite is tested for use as a medical monitoring material. The dielectric constant, for example, may be at least 50 for signals at 200 Hz.
In accordance with an embodiment of the invention, the polymeric material may include an acrylic pressure sensitive adhesive such as the V-95 acrylic pressure sensitive adhesive sold by FLEXcon Corporation of Spencer, Mass. The polar material may include a quaternary ammonium organo salt such as the CHEMAX AS-3106 sold by Chemax Corporation of Beaumont, Tex. The percentage by weight of the polar material in the composite may for example, range from about 5% to about 65%, and preferably ranges from about 10% to about 35%.
As shown in
In further embodiments, the composite 10 may be used in a wide variety of other uses, including for example, other diagnostic sensors, as well as applications in fuel cell technology, battery technology, electro luminescence, or any other application in which an electrical current and/or signal is carried through an electrolyte that has at it's source a dependence on water. Composites of the invention are insensitive to the presence or absence of water vapor, and therefore, do not require high levels of maintenance of certain levels of water in packaging and during use. It has been discovered that the shortcomings of having an electrolyte dependent on the presence of water vapor are avoided by using for example organo-salts (quaternary ammonium salts, organo-sulfates, fluoroboarates, and other salt like materials having some organic functionality). The organic functionality facilitates the salt's organic compatibility with the polymeric material. Organic compatibility may not be required when a polymer has compatibility with a purely inorganic salt, e.g., Cesium Iodide. An objective is to provide a polar material such as salt that is at least substantially uniformly dispersed throughout the polymeric material. The water insensitive electrolytic may then respond to an ascending/collapsing electric field via a capacitive coupling. In view of the relatively high volume direct current resistance of this type of doped polymer, the sensitivity is towards alternating current (AC) rather than direct current (DC). The composite, therefore, may even be more effective at detecting an AC signal than carrying an electrical current.
As discussed above with reference to
Another variation of these monitoring pads is to provide a polymeric material that has sufficient adhesive qualities to be used itself as the adhesive without requiring the adhesive foam carrier 20. As shown in
Composites of certain embodiments of the invention have also been tested at varying humidity and over extended periods of time and found to exhibit an insignificant amount of change in performance. Such composites have also been found to provide a recovery time after inducing an overloading current of within 5-10 seconds after the overloading condition was ceased. Although both the hydro-gel and composites of the invention act as a parallel capacitor/resistor, the hydro-gel has a DC resistance of about 500 ohms while a doped adhesive of the invention has a DC resistance of about 100K ohms or higher. The hydro-gel has a capacitance in both high (˜10 kHz) and low (˜200 Hz) frequency ranges in the microfarad range. The doped adhesive of an embodiment of the invention has a more pronounced capacitance that vanes with frequency effect from about 230 Pico-farads at 10 kHz to about 1 microfarad at 200 Hz. The dielectric constant K must, therefore, be changing with frequency. In fact, at 10 kHz it is discovered that K is about 10, and at 200 Hz, K is about 10,000 or above. When the K is lower the resistance increases, which requires that the pad impedance and matching impedance of the monitoring equipment must be increased.
In other embodiments, the polymeric material may include various polymeric materials such as acrylic adhesives that may be distinguished by the relative composition of their monomers and by their molecular weights. For example, acrylic adhesives such as the DURO-TAK 80-1074 acrylic adhesive, the DURO-TAK 80-136A acrylic adhesive, or the DURO-TAK 87-2852 acrylic adhesive each of which sold by National Starch and Chemical Co. of Bridgewater, N.J. may be used as the polymeric material. In certain embodiments, the polar material may include organo-sulfonium, organic ester salts, organo-metallic materials, organo-borates, phosphates and phosphites etc. In particular, the polar material may include a quaternium 18 & isopropyl alcohol (such as the ARQUAD 2HT-75 product), dicocodimoium chloride & isopropyl alcohol (such as the ARQUAD 2C-75 product), stearyl octyldimonium methosulfate (such as the ARQUAD HTL8-MS product) each of which is sold by Akzo Nobel Surface Chemistry LLC of Chicago, Ill., or PEG-5 cocomonium chloride (such as the ETHOQUAD C/25 product sold by Brenntag N.V. of Deerlijk, Belgium). Suitable further specific combinations of polymeric materials and salts are provided in the following table using the above product names.
Composites of the invention may be employed in a wide variety of applications involving the coupling of alternating current electrical activity from one location to another, such as other applications involving the monitoring of electrical activity, or the active application of electrical activity, or even the grounding of undesired electrical activity in, for example, conductive housings.
Those skilled in the art will appreciate that numerous modifications and variations may be made to the above disclosed embodiments without departing from the spirit and scope of the invention.
The present application claims priority to U.S. Provisional Patent Application Ser. No. 60/371,306 filed Apr. 10, 2002.
| Number | Date | Country | |
|---|---|---|---|
| 60371306 | Apr 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10410988 | Apr 2003 | US |
| Child | 12123773 | US |