Methods of making coated articles by sputtering silver in oxygen inclusive atmosphere

Information

  • Patent Grant
  • 6787005
  • Patent Number
    6,787,005
  • Date Filed
    Monday, September 16, 2002
    22 years ago
  • Date Issued
    Tuesday, September 7, 2004
    20 years ago
Abstract
A sputter coated article is provided with improved mechanical durability (e.g., pre-HT scratch resistance) and/or thermal stability by sputtering at least one Ag inclusive layer in an atmosphere including at least O2 gas. For instance, in certain example embodiments an Ag inclusive target may be sputtered in an atmosphere including a combination of Ar and O2 gas. In certain embodiments, this enables the resulting AgOx infrared (IR) reflecting layer to better adhere to adjacent contact layer(s).
Description




This invention relates to heat treatable low emissivity (low-E) coated articles, and methods of making the same. Such coated articles may be used in the context of vehicle windshields, insulating glass (IG) units, other types of architectural and/or vehicle windows, and other suitable applications.




BACKGROUND AND SUMMARY OF THE INVENTION




Layer coatings provided for solar management purposes are known in the art. Such coatings often seek to reflect significant amounts of infrared (IR) radiation while at the same time enabling a high amount of visible light transmittance. High visible transmittance is often desired, and this need often conflicts with the need for good IR reflection, and it is difficult to obtain both simultaneously. It is also desirable for such coatings to be heat treatable in some instances, so that they may be used in vehicle windows where heat bending is required, tempered architectural or vehicle windows, and/or the like.




WO 02/04375 discloses a low-E coating including the following layers: glass/TiO


x


/Si


x


N


y


/NiCrO


x


/Ag/NiCrO


x


/SnO


x


/Si


x


N


y


/NiCrO


x


/Ag/NiCrO


x


/SnO


x


/Si


x


N


y


. The metallic Ag layers are sputtered in an argon (Ar) gas atmosphere, as is typical in the art. This low-E coating provides for excellent solar performance and is an overall good coating. However, it has been found that this coating is subject to scratching during, for example, pre-final-product processing (e.g., before heat treatment).




In view of the above, it will be apparent to those skilled in the art that there exists a need in the art for a low-E coating that is more mechanically durable and thus less susceptible to scratching and the like, and/or which is more thermally stable (i.e., does not suffer a radical drop in visible transmission upon heat treatment such as tempering).




An object of certain example embodiments of this invention is to provide a more durable coating that is less susceptible to scratching and/or other types of mechanical damage, and/or which has improved thermal stability.




Surprisingly, it has been found that sputtering the Ag inclusive layers of the aforesaid coating in an atmosphere not simply including Ar gas, but also including oxygen gas (O


2


), renders the resulting coating (a) more mechanically durable and less susceptible to scratching, and/or (b) acceptably thermally stable. For example, it has been found that sputtering at least one of the Ag inclusive layers of the aforesaid coating in an atmosphere including a combination of Ar/O


2


gas leads to a more durable without sacrificing thermal stability.




U.S. Pat. No. 5,584,902 discloses a low-E coating system including, from the glass substrate outward, a stack of: Si


3


N


4


/NiCr/Ag/NiCr/Si


3


N


4


. Like most other prior art, the Ag layer of the '902 patent is preferably sputtered in an Ar gas atmosphere (e.g., see col. 16, lines 33-45). However, the '902 Patent does mention at col. 12, lines 59-63, that each of the three metallic layers NiCr/Ag/NiCr may be sputtered optionally in an atmosphere including “a small amount of O


2


(e.g. about 5-10%).” However, this means that all three layers (NiCr, Ag and NiCr) are sputtered in the same atmosphere, and that each atmosphere includes the same amount of oxygen—this is undesirable in many instances. While the '902 coating is heat treatable and low-E in nature, it is characterized by rather high emissivity and/or sheet resistance values which lead to rather low R


solar


(total solar energy reflectance) values around 22-24%. For example, one coating reported in the '902 patent had a sheet resistance (R


s


) of 14.4 ohms/square and a normal emissivity (E


n


) of 0.15 before heat treatment; and a R


s


of 10.5 ohms/square and a E


n


of 0.11 after heat treatment. Moreover, there is no disclosure or suggestion in the '902 Patent that sputtering an Ag target in an atmosphere including oxygen can lead to improved mechanical durability and/or thermal stability.




As explained above, an object of certain embodiments of this invention is to provide a more durable low-E coating that is less susceptible to scratching and/or other types of mechanical damage, and/or which has improved thermal stability. This object may be fulfilled by sputtering at least one Ag inclusive layer in an atmosphere including O


2


gas (e.g., a combination of Ar and O


2


gas may be used). The use of oxygen gas proximate the Ag sputtering target is especially beneficial in this respect when one or more of the immediately adjacent contact layers is/are significantly oxidized (e.g., when one or both of the adjacent contact layers comprises NiCrO


x


).




Another object of certain exemplary embodiments of this invention is to provide a dual silver low-E coating which is heat treatable and is mechanically and/or chemically durable.




Another object of certain exemplary embodiments of this invention is to provide a heat treatable low-E coating having high visible transmittance (e.g., of at least about 65%) combined with a normal emissivity (E


n


) of no greater than 0.08 (more preferably no greater than 0.06) before heat treatment, and/or an E


n


of no greater than 0.07 (more preferably no greater than 0.05) after heat treatment (HT).




Another object of certain exemplary embodiments of this invention is to provide a heat treatable low-E coating having high visible transmittance combined with a sheet resistance (R


s


) of no greater than 10.0 ohms/sq. (more preferably no greater than 8.0 ohms/sq., and most preferably no greater than about 5.0 ohms/sq.) before heat treatment; and/or a R


s


of no greater than 8.0 ohms/sq. (more preferably no greater than 6.0 ohms/sq., and most preferably no greater than about 4.0 ohms/sq.) after heat treatment.




Another object of this invention is to fulfill one or more of the above-listed objects.




Generally speaking, certain example embodiments of this invention fulfill one or more of the above-listed objects by providing a method of making a coated article including a coating supported by a glass substrate, the method comprising: sputtering a first dielectric layer so as to be supported by the glass substrate; sputtering a first contact layer on the substrate over the first dielectric layer; sputtering a target comprising Ag in an atmosphere including at least oxygen gas in order to form an infrared (IR) reflecting layer comprising AgO


x


which is located over and contacts the first contact layer; sputtering a second contact layer on the substrate so that the second contact layer is located over and in contact with the IR reflecting layer comprising AgO


x


; and wherein said sputtering of at least one of the contact layers comprises sputtering a target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form a metal oxide contact layer, and wherein more oxygen gas is introduced into an atmosphere used in sputtering the metal oxide contact layer than is introduced into an atmosphere proximate the target comprising Ag used in sputtering the IR reflecting layer comprising AgO


x


. In one example embodiment, oxygen may be fed into the neighboring cathode bay instead of directly into either the contact layer or IR reflecting layer bays; oxygen would thereby enter into the contact layer and/or IR reflecting layer bay(s)s by diffusion.




Certain other example embodiments of this invention fulfill one or more of the above-listed objects by providing a coated article including a coating supported by a glass substrate, the coating comprising: a first dielectric layer supported by the glass substrate; a first contact layer comprising a metal oxide provided on the substrate over the first dielectric layer, wherein a central portion of the first contact layer is at least about 40% oxidized; an IR reflecting layer comprising AgO


x


contacting the first contact layer, wherein the first contact layer is either above or below the IR reflecting layer on the substrate; and at least one dielectric layer provided on the substrate over the IR reflecting layer and the first contact layer.




Certain other example embodiments of this invention fulfill one or more of the above-listed objects by providing a coated article including a coating supported by a glass substrate, the coating comprising: a first dielectric layer supported by the glass substrate; an optional first contact layer comprising a metal oxide provided on the substrate over the first dielectric layer, wherein a portion of the first contact layer is at least about 40% oxidized; an IR reflecting layer comprising AgO


x


contacting the first contact layer or the bottom dielectric layer, an optional contact layer above the IR reflecting layer; and at least one dielectric layer provided on the substrate over the IR reflecting layer contacting directly either the IR reflecting layer or the optional contact layer.




This invention will now be described with respect to certain example embodiments thereof as illustrated in the following drawings, wherein:











IN THE DRAWINGS





FIG. 1

is a side cross sectional view of a coated article according to an example embodiment of this invention.





FIG. 2

is a schematic partial cross sectional view of a laminated vehicle windshield according to an example embodiment of this invention, in which coatings according to any embodiment of this invention may be used.




FIG.


3


(


a


) is cross sectional view of a portion of a coating according to an optional embodiment of this invention illustrating a pair of oxidation graded contact layers (e.g., NiCrO


x


layers) surrounding an IR reflecting layer.




FIG.


3


(


b


) is cross sectional view of a portion of a coating according to another optional embodiment of this invention illustrating an IR reflecting layer surrounded by a pair of contact layers (e.g., NiCrO


x


layers), only one of which is oxidation graded.





FIG. 4

is a schematic and partial cross sectional view illustrating how an optional graded contact layer (e.g., NiCrO


x


layer) is deposited via sputtering in accordance with an example embodiment of this invention.





FIG. 5

is a cross sectional view of the layer stack of a coating according to an Example of the instant invention.





FIG. 6

is a cross sectional view of a coated article according to another embodiment of this invention.











DETAILED DESCRIPTION OF CERTAIN EXAMPLE EMBODIMENTS OF THE INVENTION




Referring now more particularly to the accompanying drawings in which like reference numerals indicate like parts or layers throughout the several views.




Certain embodiments of this invention provide a low-E coating or layer system that may be used in applications such as vehicle windshields, other vehicle windows, skylights, glass doors, IG units, other types of architectural or residential windows, and the like. Coatings according to certain embodiments of this invention preferably have low-E characteristics as well as high visible transmittance, and are heat treatable. Preferably, coatings of certain embodiments herein are mechanically durable before and/or after heat treatment (HT), and HT does not cause a significant jump in sheet resistance (R


s


) and/or haze. As is known in the art, such HT often necessitates heating the coated substrate to temperature(s) of from 560° C. to 800° C. for a sufficient period of time to attain the desired result (e.g., tempering, bending, and/or heat strengthening).




Improved mechanical durability (e.g., pre-HT) is surprisingly achieved according to certain embodiments of this invention by sputtering at least one Ag inclusive layer (


9


and/or


19


) in an atmosphere including at least O


2


gas. For instance, in certain example embodiments an Ag inclusive target may be sputtered in an atmosphere including a combination of Ar (or other inert) and O


2


gas. The result is a layer of or including AgO


x


. The term “AgO


x


” as used herein means that the layer (


9


and/or


19


) including Ag is formed when at least some oxygen is present in a sputtering chamber in which an Ag inclusive target is located so that the resulting layer is (a) at least partially oxidized, and/or (b) of or includes metallic Ag intermixed with oxygen atoms. It has surprisingly been found that the use of the oxygen in the Ag sputtering chamber improves the adhesion between the AgO


x


layer (


9


and/or


19


) and at least one of the immediately adjacent contact layers (


7


,


11


,


17


and/or


21


) (e.g., a contact layer may be of or include NiCrO


x


, or any other suitable material, so long as it contacts the layer including Ag). This benefit of using oxygen in the Ag sputtering chamber has been found to be particularly advantageous when the contact layer(s) (


7


,


11


,


17


and/or


21


) is significantly oxidized; i.e., the central portion of the contact layer(s) is at least partially oxidized, and at least some part of the contact layer is at least about 40% oxidized, more preferably at least about 50% oxidized, and most preferably at least about 60% oxidized. In certain embodiments, visible transmission of the coated article does not decrease upon heat treatment for thermal tempering or the like. In certain embodiments, transmission starts low (e.g., at 60-65%, such as 63%) and then increases upon heating from about 1-10%.





FIG. 1

is a side cross sectional view of a coated article according to an embodiment of this invention. The coated article includes substrate


1


(e.g., clear, green, bronze, or blue-green glass substrate from about 1.0 to 10.0 mm thick, more preferably from about 1.8 mm to 4 mm thick), first dielectric anti-reflection layer


3


, second dielectric layer


5


, first lower contact layer


7


(which contacts layer


9


), first AgO


x


conductive infrared (IR) reflecting layer


9


, first upper contact layer


11


(which contacts AgO


x


layer


9


), third dielectric layer


13


(which may be deposited in one or multiple steps in different embodiments of this invention), fourth dielectric layer


15


, second lower contact layer


17


(which contacts layer


19


), second AgO


x


or Ag conductive IR reflecting layer


19


, second upper contact layer


21


(which contacts layer


19


), fifth dielectric layer


23


, and finally sixth protective dielectric layer


25


. The “contact” layers each contact at least one IR reflecting layer


9


or


19


. The aforesaid layers


3


-


25


make up heat treatable low-E (i.e., low emissivity) coating


27


which is provided on glass or plastic substrate


1


.




In certain embodiments of this invention, first dielectric layer


3


may be of or include titanium dioxide (TiO


x


where x is from 1.7 to 2.3, most preferably 2.0), silicon nitride (Si


x


N


y


where x/y may be about 0.75 (i.e., Si


3


N


4


), or alternatively x/y may be from about 0.76 to 1.5 in Si-rich embodiments), silicon dioxide (SiO


x


where x is from 1.7 to 2.3, most preferably about 2.0), niobium oxide (e.g., Nb


2


O


5


), SiZrN, tin oxide, zinc oxide, silicon oxynitride, or any other suitable dielectric material. First dielectric layer


3


functions as an antireflection layer in certain embodiments of this invention.




Second dielectric layer


5


may function to reduce haze in certain embodiments of this invention, and is preferably of or includes silicon nitride (e.g., Si


3


N


4


, or alternatively silicon-rich silicon nitride Si


x


N


y


where x/y is from 0.76 to 1.5, more preferably from 0.85 to 1.2, for haze reduction purposes). When sputtering silicon nitride layer(s) herein, a Si target may be used, or alternative a target including Si admixed with up to 3-20% by weight aluminum and/or stainless steel (e.g. SS#316) may be used, with about this amount of aluminum and/or steel then appearing in the layer(s) so formed. Other materials may also be used for haze reducing layer


5


, including but not limited to SiZrN.




Infrared (IR) reflecting layer


9


and


19


preferably include silver (Ag) as an IR reflecting material. One or both of IR reflecting layers


9


,


19


may be of or include AgO


x


as described above (e.g., formed by sputtering Ag target in an oxygen inclusive atmosphere). When only one of layer


9


and


19


is of or includes AgO


x


, the other IR reflecting layer may be of or include Ag or any other suitable IR reflecting material. These IR reflecting layers


9


,


19


help enable coating


27


to have low-E characteristics.




Contact layers


7


,


11


,


17


, and


21


are of or include nickel (Ni) oxide, or a nickel alloy oxide such as nickel chrome oxide (NiCrO


x


), in certain embodiments of this invention. NiCrO


x


layers


7


,


11


,


17


, and/or


21


may be fully oxidized in certain embodiments of this invention (i.e., fully stochiometric), or may be at least about 75% oxidized in other embodiments of this invention. While NiCrO


x


is a preferred material for layers


7


,


11


,


17


and/or


21


, those skilled in the art will recognized that other materials may instead be used and that one or more of the contact layers may be a metal oxide such as oxides of Ni, oxides of Ni alloys, oxides of Cr, oxides of Cr alloys, NiCrO


x


N


y


, or any other suitable material. Thus, when it is said that a contact layer is a “metal oxide”, this includes oxides of metal alloys such as niCr and also includes layers that may be partially nitrided in addition to oxided. Optionally, one or both contact layers may be removed adjacent one or both IR reflecting layers.




In any event, regardless of what metal(s) is provided in contact layer(s)


7


,


11


,


17


and


21


, the benefit of using oxygen in an Ag sputtering chamber(s) has been found to be particularly advantageous when one or more of the contact layer(s) (


7


,


11


,


17


and/or


21


) located adjacent an AgO


x


layer (


9


or


19


) is significantly oxidized. Thus, at least one contact layer (and preferably two) located adjacent an AgO


x


layer has a central portion that is at least partially oxidized, and at least some part of the contact layer is at least about 40% oxidized, more preferably at least about 50% oxidized, and most preferably at least about 60% oxidized. It is noted that contact layers


7


,


11


,


17


and/or


21


may or may not be continuous in different embodiments of this invention.




When layers


7


,


11


,


17


and/or


21


comprise NiCrO


x


in certain embodiments, the Ni and Cr may be provided in different amounts, such as in the form of nichrome by weight about 0-90% Ni and 10-90% Cr. An exemplary sputtering target for depositing these layers includes not only SS-316 which consists essentially of 10% Ni and 90% other ingredients, mainly Fe and Cr, but Haynes 214 alloy as well.




One or more of contact layers


7


,


11


,


17


, and/or


21


(e.g., of or including NiCrO


x


) may be oxidation graded in certain embodiments of this invention so that the degree of oxidation in the layer(s) changes throughout the thickness of the layer(s). Oxidation grading is optional, and need not be provided in certain embodiments of this invention. When oxidation grading is practiced, one or more of contact layers (


7


,


11


,


17


and/or


21


) may be graded so as to be less oxidized at the contact interface with the immediately adjacent IR reflecting layer (


9


or


19


) than at a portion of the contact layer(s) further or more/most distant from the immediately adjacent IR reflecting layer (a central portion of the contact layer is at least partially oxidized in any event). It is believed that oxidation grading of one or more of contact layer(s)


7


,


11


,


17


and/or


21


may help the low-E coating


27


to achieve the combination of heat treatability and high visible transmission.




FIGS.


3


(


a


) and


3


(


b


) illustrate various types of oxidation grading of the contact layer(s) according to certain example embodiments of this invent on. These figures are for purposes of example only. Further details with respect to oxidation grading of the contact layer(s) may be found in U.S. Ser. No. 09/794,214, filed Feb. 28, 2001 (now U.S. Pat. No. 6,576,349), the entire disclosure of which is hereby incorporated herein by reference.





FIG. 4

illustrates how an oxidation graded contact layer may be deposited on a substrate as part of a coating according to an exemplary embodiment of this invention, using an asymmetric introduction of oxygen gas at a target area. Substrate


1


with part of a layer system thereon proceeds in direction D through the sputter coater. When the substrate


1


is moving in direction D beneath target


51


(within shield


53


), gas is introduced around the target on two sides


57


and


59


thereof. On one side


57


of target


51


, at least oxygen (e.g., O


2


) gas (e.g., oxygen flow of about 30-60 mL/min. at 4.1 kW), and optionally a mixture of oxygen and an inert gas such as argon (Ar), is fed into the coating zone beneath and/or proximate the target. However, on the other side


59


of target


51


, less oxygen gas is used and more of another gas such as Ar is introduced into the coating zone beneath and/or proximate the target. Again, further details with respect to oxidation grading may be found in U.S. Ser. No. 09/794,224 (now U.S. Patent No. 6.576,349). It can also be seen that oxygen gas is used proximate the silver target


60


as discussed herein.




Turning back to

FIG. 1

, third dielectric layer


13


acts as a coupling layer between the two halves of the coating


27


, and is of or includes tin oxide in certain embodiments of this invention. However, other dielectric materials may instead be used for layer


13


, including but not limited to silicon nitride, titanium dioxide, niobium oxide, silicon oxynitride, zinc oxide, or the like. Fourth dielectric layer


15


functions as a haze reducer in certain embodiments of this invention, and is preferably of or includes silicon nitride (e.g., Si


3


N


4


, or alternatively silicon-rich silicon nitride discussed above). However, in alternative embodiments of this invention, other materials (e.g., SiZrN) may instead be used for dielectric layer


15


.




Fifth dielectric layer


23


may be of or include tin oxide in certain embodiments of this invention. However, other dielectric materials may instead be used for layer


23


, including but not limited to silicon nitride, titanium dioxide, niobium oxide, silicon oxynitride, zinc oxide, or the like. Protective overcoat dielectric layer


25


is provided at least for durability purposes, and may be of or include silicon nitride (e.g., Si


3


N


4


) in certain embodiments of this invention. However, other dielectric materials may instead be used for layer


25


, including but not limited to titanium dioxide, silicon oxynitride, tin oxide, zinc oxide, niobium oxide, SiZrN, or the like.




Other layer(s) below or above the illustrated coating


27


may also be provided. Thus, while the layer system or coating


27


is “on” or “supported by” substrate


1


(directly or indirectly), other layer(s) may be provided therebetween. Thus, for example, coating


27


of

FIG. 1

may be considered “on” and “supported by” the substrate


1


even if other layer(s) are provided between layer


3


and substrate


1


. Moreover, certain layers of coating


27


may be removed in certain embodiments, while others may be added in other embodiments of this invention without departing from the overall spirit of certain embodiments of this invention.




Further details regarding the aforesaid layers


3


-


7


,


11


-


17


and


21


-


25


may be found in U.S. Ser. No. 09/794,224, filed Feb. 28, 2001 (now U.S. Patent No. 6,576,349), the entire disclosure of which is hereby incorporated herein y reference (see also WO 02/04375).





FIG. 2

illustrates a laminate (e.g., vehicle windshield) according to an embodiment of this invention, including coating


27


of FIG.


1


. As shown in

FIG. 2

, the laminate (e.g., windshield) includes first glass substrate


1


on which coating


27


is provided, and second glass substrate


31


. PVB (or other polymer inclusive material) layer


33


is provided between the substrates in a known manner, so as to contact coating


27


on one side thereof. In the

FIG. 2

embodiment, coating


27


is provided at/on the second (or #2) surface


37


of the laminate. The first surface


35


is at the exterior of the laminate exposed to the outside of the vehicle, second surface


37


is on the interior or inside of outer substrate


1


third surface


39


is on the inside of the interior substrate


31


, and fourth surface


41


is at the interior of the vehicle. Coatings


27


herein are preferably provided on either the second


37


or third


39


surface(s) of such laminates (the same is also true with regard to IG units).




Turning back to

FIG. 1

, while various thicknesses may be used consistent with one or more of the objects discussed herein, exemplary preferred thicknesses and example materials for the respective layers on the glass substrate


1


in the

FIG. 1

embodiment are as follows:












TABLE 1











(Example Materials/Thicknesses;

FIG. 1

Embodiment)















Preferred




More







Layer




Range (Å)




Preferred (Å)




Example



















TiO


x


(layer 3)




0-400









40-200









 80 Å






Si


x


N


y


(layer 5)




0-400









50-250









165 Å






NiCrO


x


(layer 7)




5-100









10-50









 26 Å






AgO


x


(layer 9)




50-250









80-120









103 Å






NiCrO


x


(layer 11)




5-100









10-50









 26 Å






SnO


2


(layer 13)




0-800









450-800









550 Å






Si


x


N


y


(layer 15)




0-800









50-250









165 Å






NiCrO


x


(layer 17)




5-100









10-50









 26 Å






Ag (layer 19)




50-250









80-150









130 Å






NiCrO


x


(layer 21)




5-100









10-50









 26 Å






SnO


2


(layer 23)




0-500









50-250









100 Å






Si


3


N


4


(layer 25)




0-500









100-300









205 Å















FIG. 6

illustrates a low-E heat treatable coating


27


according to another embodiment of this invention. The

FIG. 6

coating


27


is the same as the

FIG. 1

coating described above, except that either (i) dielectric layer


3


is removed, or (ii) layers


3


and


5


are replaced with a single silicon nitride layer


40


. Silicon nitride layer


40


may be of or include Si


3


N


4


in certain embodiments of this invention. In other embodiments, silicon nitride layer


40


may be of or include Si


x


N


y


where x/y may be from about 0.65 to 0.80, or alternatively from about 0.76 to 1.5 in silicon rich embodiments. In another embodiment of the particular

FIG. 6

embodiment, layer


40


may be of or include SiZrN. Nitride layer


40


is advantageous because if functions to reduce haze, and is preferably from about 10 to 500 Å thick, more preferably from about 200-400 Å thick. As with all embodiments herein, Si-rich silicon nitride has improved performance in reducing haze compared to Si


3


N


4


.




In certain exemplary embodiments of this invention, coating/layer systems


27


have the following low-E characteristics before/after heat treatment (HT) when in monolithic form, as set forth in Table 2:












TABLE 2











Monolithic Before/After Heat Treatment (HT)
















More




Most






Characteristic




General




Preferred




Preferred









R


s


(ohms/sq.)(before HT):




<=10.0 




<=8.0




<=5.0






R


s


(ohms/sq.)(after HT):




<=8.0




<=6.0




<=4.0






E


n


(before HT):




 <=0.08




 <=0.06




n/a






E


n


(after HT):




 <=0.07




 <=0.05




n/a






T


vis


(pre and post-HT):




  >=60% 




  >=70% 




  >=75% 






Haze (after HT):




 <=0.40




 <=0.30




 <=0.28














As can be seen above, in certain embodiments of this invention where coated articles are used monolithically, they have a high visible transmittance both before and after HT.




Coatings


27


according to certain exemplary embodiments of this invention (e.g.,

FIGS. 1-6

) have the following color/transmission/reflection/haze characteristics when on a clear soda lime silica glass substrate (e.g., 2-4 mm thick) in laminated or IG unit form with another similar clear soda lime silica glass substrate (e.g., in laminated form of a vehicle windshield with PVB or index oil between the two substrates as shown in

FIG. 2

, or in conventional IG unit form) as set forth in Table 3. In Table 3 below, R


g


Y is visible reflection from the exterior of the vehicle/building as shown in

FIG. 2

, and R


f


Y is visible reflection from the other side of the laminate such as from the vehicle/building interior in

FIG. 2

, and the a*, b* values under these respective reflection parameters also correspond to glass (g) side and film (f) side, respectively.












TABLE 3











Color/Transmission After HT; Laminated or IG Unit Form















Characteristic




General




More Preferred











T


vis


(Ill. A, 2 deg.):




  >=60% 




  >=70% 







T


vis


(Ill. C, 2 deg.):




  >=60% 




  >=70% 







R


g


Y (Ill. A, C; 2 deg.):




  <=13% 




  <=11% 







a*


g


(Ill. C; 2°):




−3.0 to +5.0




−2.0 to +2.0







b*


g


(Ill. C; 2°):




−10.0 to +10.0




−8.0 to −2.0







R


f


Y (Ill. A, C; 2 deg.):




  <=14% 




  <=12% 







a*


f


(Ill. C; 2°):




−5.0 to +5.0




−2.0 to 2.0  







b*


f


(Ill. C; 2°):




−10.0 to 10.0  




−5.0 to 5.0  







R


solar


:




  >=26% 




  >=28% 







Haze:




<=0.4




<=0.3







T


solar


:




  <=50% 




  <=48% 







T


ultraviolet






 <=0.45




 <=0.36







SHGC:




 <=0.50




 <=0.40















EXAMPLE




The following coating was made in accordance with an example embodiment of this invention (e.g., see FIG.


5


); this example being provided for purposes of example but without limitation. The coating/layer system


27


shown in

FIG. 5

is considered on a clear 3.3 mm thick large soda lime silica float glass substrate


1


. A Leybold Terra-G seven-chamber sputter coating apparatus was used to sputter the coatings


27


onto the substrates


1


. There was a total of 27 cathodes used. Cathode numbering utilizes the first digit to refer to the coater chamber, and the second digit to refer to the cathode position in that chamber. For example, cathode #


32


was the second cathode (second digit) in the third (first digit) sputter chamber. Thus, it can be seen for example that the cathodes used for sputtering the Ag inclusive layers (i.e., cathodes


31


,


32


and


62


,


63


) are in different sputtering chambers than the cathodes used for sputtering the NiCrO


x


contact layers (i.e., cathodes


25


,


33


,


61


and


64


). Below, “*” means Al content of approximately 10%. The line speed was about 4.99 meters per minute, and the coater/process setup is set forth in Table 4. All gas flows (e.g., oxygen, argon, nitrogen) are presented in units of sccm. Volts refers to cathode volts, and amps (A) refers to cathode amps. Pressure is measured in hecta pascals. Trim gas refers to individually adjusted gas flows along the cathode length to make corrections regarding layer thickness or stoichiometry uniformity, and the flow units are in terms of sccm. The NiCr targets were approximately 80/20 NiCr. The pressure for each sputter chamber was from 3.7 to 7 E-3 hPa.












TABLE 4











Coater Setup/Processes for Example


















Cathode




Target




Volts (V)




Power (kW)




Ar (sccm)




O


2


(sccm)




N


2


(sccm)




Trim Gas





















#11




Ti




552




12.9




350




11




0




29.7 O


2








#12




Ti




549




40.8




350




11




0




29.8 O


2








#13




Ti




534




0.6




350




11




0




29.8 O


2








#14




Ti




263




39.2




350




11




0




29.8 O


2








#15




Ti




25




0




350




0




0




0






#23




Si*




658




71.7




250




0




299




 124 N


2








#25




NiCr




507




18




250




193




0




0






#31




Ag




n/a




n/a




250




0




0




0






#32




Ag




n/a




n/a




225




30




0




0






#33




NiCr




479




13.5




250




72




0




0






#35




Sn




10.3




0




225




72




0




0






#41




Sn




479.5




33.8




200




389




75




 159 O


2








#42




Sn




480




33.2




200




360




75




 166 O


2








#43




Sn




494




30.5




200




360




75




 166 O


2








#44




Sn




472




33.9




200




360




75




 166 O


2








#45




Sn




477




31.1




200




360




75




 166 O


2








#51




Sn




243




40.6




200




389




75




 166 O


2








#52




Sn




2.1




0




200




0




75




0






#54




Si*




651




56




250




0




280




 124 N


2








#61




NiCr




507




18




250




128




0




0






#62




Ag




n/a




n/a




275




0




0




0






#63




Ag




473




8




300




0




0




0






#64




NiCr




499




13.4




250




59




0




0






#71




Sn




505.6




42




200




555




62




 195 O


2








#73




Si*




488




61




250




0




500




 220 N


2








#74




Si*




498




61




250




0




500




 220 N


2








#75




Si*




497




61




250




0




500




 220 N


2
















In view of the coater set-up set forth above, it can be seen that the lower IR reflecting layer


9


was sputtered in an atmosphere including oxygen, but that the upper IR reflecting layer


19


(see cathode #s


62


-


63


) was sputtered in a purely Ar atmosphere. Thus, lower IR reflecting layer


9


(see cathode #s


31


-


32


) was of or included AgO


x


while the upper IR reflecting layer


19


was metallic Ag. In other example embodiments of this invention, both layers


9


,


19


(or alternatively just upper IR reflecting layer


19


) may be of or include AgO


x


. The coating from the Example above was characterized by solar/optical/thickness characteristics as set forth in Tables 1-3 above.




With respect to the lower IR reflecting layer


9


where both oxygen and argon gas is used in sputtering the Ag target, it can be seen that more oxygen gas may be introduced into the respective atmospheres proximate the targets used in sputtering the first and second contact layers (


7


,


11


) (or in an intermediate unused bay/chamber) than is introduced into the atmosphere proximate the target comprising Ag used in sputtering the IR reflecting layer comprising AgO


x


(


9


). In the Example above, 30 sccm of oxygen gas is introduced into the atmosphere proximate one of the Ag targets, while 193 sccm and 72 sccm of oxygen are introduced into the respective atmospheres used for sputtering the adjacent metal oxide contact layers


7


and


11


, respectively. Thus, the respective contact layers


7


and


11


may be oxidized to a greater extent than is IR reflecting layer


9


. The relative oxidation of a layer is complex function of the sputtering process parameters. We could therefore have situations where the relative oxidation of the contact layers versus the adjacent IR reflecting layer may not be directly correlated to the relative oxygen gas flows in the respective bays. The scope of the invention is not limited to the relative oxidation levels between the contact (or dielectric) layers and the IR reflecting layers, unless recited in the claims.




In certain embodiments of this invention, the ratio of (a) oxygen gas introduced into the atmosphere proximate the Ag inclusive target for sputtering the IR reflecting layer, to (b) oxygen gas introduced into the atmosphere proximate a target for sputtering an adjacent contact layer, is from about 1:1.3 to 1:10, more preferably from about 1:1.5 to 1:8, and most preferably from about 1:2 to 1:5. In different embodiments of this invention, from about 10-250 sccm of oxygen gas may be introduced into the atmosphere proximate the Ag inclusive target, more preferably from about 20-100 sccm, and most preferably from about 20-60 sccm (e.g., regardless of the relative oxygen flow in neighboring cathode bays or the oxidation levels of the adjacent layers in the stack). Additionally, the oxygen for the contact layer(s) and/or the adjacent IR reflecting layer may be supplied in total or in part from adjacent bays. In this manner, we would rely on diffusion in the coater to supply oxygen to the contact layer(s) and/or the IR reflecting layer(s).




After being made, the coated article of the aforesaid Example was heat treated (HT) in order to temper the same. Surprisingly, it was found that high visible transmission (at least about 65%, more preferably at least about 70%, and most preferably at least about 75%) was able to be maintained for longer periods of HT when the oxygen was provided in the Ag target atmosphere for at least one of the Ag inclusive layers. The tempered coated article may then be used either monolithically, or in combination with another substrate, in various window applications.




Certain terms are prevalently used in the glass coating art, particularly when defining the properties and solar management characteristics of coated glass. Such terms are used herein in accordance with their well known meaning. For example, see the meanings of these terms as set forth in 09/794,224 now U.S. Patent No. 6,576,349 incorporated herein by reference (see also WO 02/04375)




Once given the above disclosure many other features, modifications and improvements will become apparent to the skilled artisan. For example, and without limitation, the use of oxygen in sputtering an Ag inclusive layer may be used with or without oxidation graded contact layer(s) and/or Si-rich silicon nitride layer(s), and may be used with single silver layer stacks, as well as the illustrated dual (or more) silver layer stacks. Furthermore, the dielectric materials listed above for the dielectric layers are provided for purposes of example and the instant invention is not so limited unless such materials are recited in the claims. Moreover, the term “sputtering” as used herein includes any and all forms of sputtering including but not limited to magnetron sputtering, ion-assisted sputtering, etc. Such other features, modifications and improvements are therefore considered to be a part of this invention, the scope of which is to be determined by the following claims:



Claims
  • 1. A method of making a coated article including a coating supported by a glass substrate, the method comprising:sputtering a first dielectric layer on the glass substrate; sputtering a target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form a first contact layer comprising a metal oxide on the substrate over the first dielectric layer; sputtering a target comprising Ag in an atmosphere including at least oxygen gas in order to form an infrared (IR) reflecting layer comprising AgOx which is located over and contacts the first contact layer; sputtering a target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form a second contact layer comprising a metal oxide on the substrate so that the second contact layer is located over and in contact with the IR reflecting layer comprising AgOx; wherein more oxygen gas is introduced into each of the respective atmospheres proximate the targets used in sputtering the first and second contact layer than is introduced into the atmosphere proximate the target comprising Ag used in sputtering the IR reflecting layer comprising AgOx; and heat treating the glass substrate with the coating thereon in order to thermally temper the same, and wherein visible transmission of the coated article does not decrease as a result of said heat treating.
  • 2. The method of claim 1, wherein a ratio of (a) oxygen gas introduced into the atmosphere proximate the target comprising Ag for sputtering the IR reflecting layer, to (b) oxygen gas introduced into the atmosphere proximate one of the targets for sputtering a corresponding one of the contact layers, is from about 1:1.3 to 1:10; so that more oxygen is present proximate the target used in sputtering the contact layer than is present proximate the target comprising Ag used in sputtering the IR reflecting layer.
  • 3. The method of claim 2, wherein the ratio is from about 1:1.5 to 1:8.
  • 4. The method of claim 2, wherein the ratio is from about 1:2 to 1:5.
  • 5. The method of claim 1, wherein from about 20-100 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag, and wherein at least one of the contact layers comprises NiCrOx.
  • 6. The method of claim 1, wherein from about 20-60 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag.
  • 7. The method of claim 1, wherein both the oxygen gas and argon gas are introduced into the atmosphere proximate the target comprising Ag, and wherein more argon gas than oxygen gas is introduced into the atmosphere proximate the target comprising Ag.
  • 8. The method of claim 1, wherein at least one of the contact layers comprises NiCrOx and is oxidation graded so that a first portion of said one contact layer close to said infrared (IR) reflecting layer is less oxidized than a second portion of said one contact layer that is further from said infrared (IR) reflecting layer and is located in a central portion of said one contact layer.
  • 9. The method of claim 1, wherein the coated article comprises from the glass substrate outwardly:the first dielectric layer; the first contact layer which comprises NiCrOx; the IR reflecting layer comprising AgOx; the second contact layer which comprises NiCrOx; at least one additional dielectric layer; a third layer comprising NiCrOx; a second IR reflecting layer; a fourth layer comprising NiCrOx; and at least one additional dielectric layer.
  • 10. The method of claim 1, wherein the coated article as a visible transmittance of at least about 65%, and a sheet resistance (Re) of no greater than 8.0 ohms/sq.
  • 11. The method of claim 1, wherein at least one of the contact layers comprises NiCrOx.
  • 12. The method of claim 1, wherein another dielectric layer is located between the first dielectric layer and the first contact layer.
  • 13. The method of claim 12, wherein said another dielectric layer comprises silicon nitride, and the first dielectric layer comprises an oxide of titanium.
  • 14. A method of making a coated article including a coating supported by a glass substrate, the method comprising:sputtering a first dielectric layer so as to be supported by the glass substrate; sputtering a first contact layer on the substrate over the first dielectric layer; sputtering a target comprising Ag in an atmosphere including at least oxygen gas in order to form an infrared (IR) reflecting layer comprising AgOx which is located over and contacts the first contact layer; sputtering a second contact layer on the substrate so that the second contact layer is located over and in contact with the IR reflecting layer comprising AgOx; wherein said sputtering of at least one of the contact layers comprises sputtering a target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form a metal oxide contact layer; heat treating the substrate with the coating thereon for tempering, and wherein visible transmission of the coated article does not decrease due to the heat treating; wherein more oxygen gas is provided in an atmosphere used in sputtering the metal oxide contact layer than is provided in an atmosphere proximate target comprising Ag used in sputtering the IR reflecting layer comprising AgOx; and wherein visible transmission of the coated article increased upon said heat treating.
  • 15. The method of claim 14, wherein the first and second contact layers each comprise an oxide of NiCr.
  • 16. The method of claim 14, wherein a ratio of (a) oxygen as introduced into the atmosphere proximate the target comprising Ag for sputtering the IR reflecting layer, to (b) oxygen gas introduced into the atmosphere proximate one of the targets for sputtering a corresponding one of the contact layers, is from about 1:1.3 to 1:10; so that more oxygen is present proximate the target used in sputtering the contact layer than is present proximate the target comprising Ag used in sputtering the IR reflecting layer.
  • 17. The method of claim 16, wherein the ratio is from about 1:1.5 to 1:8.
  • 18. The method of claim 14, wherein from about 20-100 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag, and wherein at least one of the contact layers comprises an oxide of NiCr.
  • 19. The method of claim 14, wherein from about 20-60 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag.
  • 20. A method of making a coated article including a coating supported by a glass substrate, the method comprising:sputtering a first dielectric layer so as to be supported by at least the glass substrate; sputtering a first contact layer on the substrate over the first dielectric layer; sputtering a target comprising Ag in an atmosphere including at least oxygen gas in order to form an infrared (IR) reflecting layer comprising AgOx which is located over and contacts the first contact layer; sputtering a second contact layer on the substrate so that the second contact layer is located over and in contact with the JR reflecting layer comprising AgOx; wherein said sputtering of at least one of the contact layers comprises sputtering a target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form a metal oxide contact layer, wherein more oxygen gas is provided in an atmosphere used in sputtering the metal oxide contact layer than is provided in an atmosphere proximate the target comprising Ag used in sputtering the IR reflecting layer comprising AgOx.
  • 21. The method of claim 20, wherein the first and second contact layers each comprise an oxide of NiCr.
  • 22. The method of claim 20, wherein a ratio of (a) oxygen as introduced into the atmosphere proximate the target comprising Ag for sputtering the IR reflecting layer, to (b) oxygen gas introduced into the atmosphere proximate one of the targets for sputtering a corresponding one of the contact layers, is from about 1:1.3 to 1:10; so that more oxygen is present proximate the target used in sputtering the contact layer than is present proximate the target comprising Ag used in sputtering the IR reflecting layer.
  • 23. The method of claim 22, wherein the ratio is from about 1:1.5 to 1:8.
  • 24. The method of claim 20, wherein from about 20-100 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag, and wherein at least one of the contact layers comprises an oxide of NiCr.
  • 25. The method of claim 20, wherein from about 20-60 sccm of oxygen gas is introduced into the atmosphere proximate the target comprising Ag.
Parent Case Info

This application claims the benefit of Provisional Application No. 60/407,687, filed Sep. 4, 2002, the entire content of which is hereby incorporated herein by reference.

US Referenced Citations (25)
Number Name Date Kind
3843405 Bourg Oct 1974 A
4413877 Suzuki et al. Nov 1983 A
4799745 Meyer et al. Jan 1989 A
4898789 Finley Feb 1990 A
5201926 Szczyrbowski et al. Apr 1993 A
5229194 Lingle et al. Jul 1993 A
5332888 Tausch et al. Jul 1994 A
5344718 Hartig et al. Sep 1994 A
5514476 Hartig et al. May 1996 A
5557462 Hartig et al. Sep 1996 A
5563734 Wolfe et al. Oct 1996 A
5584902 Hartig et al. Dec 1996 A
5770321 Hartig et al. Jun 1998 A
5800933 Hartig et al. Sep 1998 A
5834103 Bond et al. Nov 1998 A
5942338 Arbab et al. Aug 1999 A
6014872 Hartig et al. Jan 2000 A
6524688 Eby et al. Feb 2003 B1
6576349 Lingle et al. Jun 2003 B2
6602608 Stachowiak Aug 2003 B2
6623846 Laird Sep 2003 B2
20010041252 Laird Nov 2001 A1
20020031674 Laird Mar 2002 A1
20020068167 Veerasamy Jun 2002 A1
20030049464 Glenn et al. Mar 2003 A1
Foreign Referenced Citations (4)
Number Date Country
195 33 053 Apr 1997 DE
WO 9964362 Dec 1999 WO
WO 0166483 Sep 2001 WO
WO 0204375 Jan 2002 WO
Non-Patent Literature Citations (11)
Entry
US 4,960,645, 10/1990, Lingle et al. (withdrawn)
XP-002202187 “The Role of Neutral Oxygen Radicals in the Oxidation of Ag Films”, Schmidt et al., Thin Solid Films 281-282 (1996), pp. 105-107.
“Adhesion of Silver Films to Ion-Bombarded Zirconia”, ERCK, vol. 47, 8, pp. 640-644.
“Ion Beam Mixing of Silver-Magnesium Oxide Multilayers”, Fuchs et al., Thin Solid Films 165 (1988) pp. 347-358.
“Ion Assisted Deposition of Silver” Thin Films, Lee et al., Thin Solid Films 359 (2000) pp. 95-97.
“Swift Heavy Ion-Induced Modification of Metallic” Thin Films and Multilayers, GUPTA, Vacuum 58 (2000) pp. 16-32.
“Roughness Modification of Surfaces Treated by a Pulsed Dielectric Barrier Discharge”, Dumitrascu et al., Apr. 5, 2002, pp. 127-134.
“MeV Heavy Ion-Induced Adhesion of Thin Silver Film to Tantalum”, QIU et al., 1991, pp. 367-372.
Proceedings Coating Technology Symposium, Maui, Feb. 3-6, 1987 Airco, Ross et al.
XP-002267135, “Method Manufacture Laminate Component Display Device Interposed Oxide Film Silver Group Material Substrate Silver System Film Contain Silver Group Material”, Jun. 17, 2003.
International Search Report dated Jan. 29, 2004.
Provisional Applications (1)
Number Date Country
60/407687 Sep 2002 US