Claims
- 1. A method of producing a product for waterproofing and protecting a surface of solid building material against liquids and chemical and biological corrosion, said method comprising:
a) preparing a first aqueous solution by dissolving calcium oxide in a first quantity of water to which has been added a dissolving agent which increases the quantity of calcium oxide which may be dissolved in said first quantity of water; b) preparing a second aqueous solution by introducing a quantity of sodium silicate into a second quantity of water; and c) mixing the first aqueous solution and the second aqueous solution thereby forming an aqueous product containing silica, calcium, and sodium ions, said aqueous product, when dried, being capable of forming a glass-like waterproof surface film on said building material surface.
- 2. The method according to claim 1 wherein the dissolving agent is saccharose.
- 3. The method according to claim 1 wherein the dissolving agent is glycerine.
- 4. The method according to claim 1 wherein said water is demineralised and including degasifying first quantity of said demineralised water prior to the adding of said dissolving agent thereto.
- 5. The method according to claim 1 wherein said calcium oxide comprises selectively quicklime or calcium hydroxide.
- 6. The method according to claim 5 wherein said quicklime or calcium hydroxide is added in a quantity selected with reference to the quantity of dissolving agent present in said first quantity of water.
- 7. The method according to claim 1 wherein said calcium oxide comprises calcium hydroxide.
- 8. The method according to claim 1 wherein said calcium oxide or calcium hydroxide is dissolved in said first quantity of water at room temperature.
- 9. The method according to claim 8 wherein said calcium hydroxide is added in a quantity selected with reference to the quantity of dissolving agent present in said first quantity of water.
- 10. The method according to claim 1 wherein the quantities of calcium oxide and sodium silicate added to the first and second aqueous solutions respectively are in such quantities that the aqueous product contains a ratio of Ca:Na2 of approximately 0.1:1.0.
- 11. The method according to claim 1 wherein said sodium silicate is in the form of sodium metasilicate pentahydrate or other form of water soluble sodium silicate.
- 12. An aqueous product applicable in a wet state to a surface of a solid building material for waterproofing and impregnating said surface against liquids and chemical and biological corrosion, said aqueous product being capable of being dried after its application to said surface, said aqueous product comprising an aqueous solution containing silica, calcium, and sodium ions, said aqueous product, when dried after its application to said surface forming a glass-like film on said surface.
- 13. The product according to claim 12 wherein said aqueous product contains calcium and sodium in a ratio of Ca:Na2 of approximately 0.1:1.0.
- 14. The product according to claim 12 and including the following components by weight %:
52.5 to 56% water; 24 to 33% saccharose; 1.9 to 2.7% calcium oxide; and 8.6 to 21.3% sodium metasilicate pentahydrate.
- 15. The product according to claim 12 and including the following components by weight %:
55.6 to 68% water; 31 to 36.6% glycerine; 1.1 to 1.31% calcium oxide; and 4.3 to 12.3% sodium metasilicate pentahydrate.
- 16. A method of waterproofing a surface of solid building material comprising:
a) preparing a first aqueous solution by dissolving calcium oxide in a first quantity of water; b) preparing a second aqueous solution by introducing a quantity of sodium silicate into a second quantity of water; and c) coating said surface with said first and second solutions prior to the formation and precipitation of a double silicate.
- 17. The method according to claim 16 including mixing said first and second solutions together shortly prior to the coating of said surface.
- 18. The method according to claim 16 including applying said first and second solutions to said surface sequentially commencing with said second solution.
- 19. The method according to claim 18 including drying the coating formed by said second solution prior to applying said first solution.
- 20. The method according to claim 16 including applying a plurality of coatings of said second solution to said surface followed by applying a plurality of coatings of said first solution over the coatings of said second solution.
- 21. The method according to claim 20 including drying each of said coatings prior to applying another of said coatings.
- 22. The method according to claim 20 wherein the number of coatings of each of said first and second solutions is equal.
Priority Claims (2)
Number |
Date |
Country |
Kind |
PCT/EP98/04914 |
Aug 1998 |
EP |
|
97 122 083.5 |
Dec 1997 |
EP |
|
RELATED APPLICATION
[0001] This application is a continuation-in-part of application Ser. No. 09/284,761 filed Aug. 6, 1998.
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
09284761 |
Apr 2000 |
US |
Child |
09788914 |
Feb 2001 |
US |