Methods of using a submerged combustion melter to produce glass products

Information

  • Patent Grant
  • 9481593
  • Patent Number
    9,481,593
  • Date Filed
    Tuesday, January 27, 2015
    9 years ago
  • Date Issued
    Tuesday, November 1, 2016
    8 years ago
Abstract
A method comprises flowing an oxidant and a fuel into a submerged combustion burner in a glass tank furnace, the glass tank furnace receiving a feed of glass forming material and producing molten glass, the burner and furnace comprising a melting system. The melting system has a variable system vibration and/or oscillation due to the nature of submerged combustion. One method includes predicting a value of at least one property, such as viscosity, of the molten glass using the variable system vibration and/or oscillation.
Description
BACKGROUND INFORMATION

1. Technical Field


The present disclosure relates generally to the field of submerged combustion glass melters and methods of use.


2. Background Art


Submerged combustion melters are known for producing molten glass. The nature of submerged combustion melters and their operation cause a perceptible and measurable vibration and/or oscillation in the system.


It would be an advance in the submerged combustion glass melting art to develop methods of using the vibration and/or oscillation of the submerged combustion melter, either alone or in combination with other system parameters, to predict properties of the molten glass or other material melted within the melter, particularly in situations where melter feeds, fuels, and/or oxidants are changing or expected to change.


SUMMARY

In accordance with the present disclosure, methods of using vibrations and/or oscillations of a submerged combustion melter are described that may allow predicting or tuning of one or more molten or finished glass parameters.


A first aspect of the disclosure is a method, the method comprising:


a) flowing an oxidant and a fuel into a submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass; and


b) predicting a value of at least one property of the molten glass using at least the variable system vibration.


A second aspect of the disclosure is method of producing molten glass using submerged combustion, the method comprising:


a) flowing an oxidant and a fuel into at least one submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass;


b) measuring frequency and/or amplitude of the variable system vibration; and


b) predicting a value of viscosity of the molten glass using at least the measured frequency and/or amplitude of the variable system vibration.


A third aspect of the disclosure is a method of producing molten glass using submerged combustion, the method comprising:


a) flowing an oxidant and a fuel into at least one submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass;


b) measuring frequency and/or amplitude of the variable system vibration;


c) analyzing the frequency and/or amplitude of the variable system vibration using one or more mathematical techniques to identify one or more key frequencies and/or amplitudes; and


b) predicting a value of viscosity of the molten glass using at least the measured frequency and/or amplitude of the variable system vibration.


Certain methods within the disclosure include feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows.


Methods of the disclosure will become more apparent upon review of the brief description of the drawings, the detailed description of the disclosure, and the claims that follow.





BRIEF DESCRIPTION OF THE DRAWINGS

The manner in which the objectives of the disclosure and other desirable characteristics can be obtained is explained in the following description and attached drawings in which:



FIG. 1 is a schematic side-elevation view, partially in cross-section of a submerged combustion melter and method of controlling same and/or predicting a parameter of the melt in accordance with the present disclosure;



FIGS. 2, 3 and 4 are schematic side elevation views, partially in cross-section, of downstream systems and methods that may be controlled using a predicted value of a parameter from the system and method of FIG. 1;



FIGS. 5, 6, 7 and 8 are logic diagrams of four methods in accordance with the present disclosure; and



FIGS. 9A and 9B are prior art schematic representations of vibration that may be useful in understanding aspects of the present disclosure.





It is to be noted, however, that FIGS. 1-4 of the appended drawings are not to scale and illustrate only typical embodiments of this disclosure, and are therefore not to be considered limiting of its scope, for the disclosure may admit to other equally effective embodiments.


DETAILED DESCRIPTION

In the following description, numerous details are set forth to provide an understanding of the disclosed methods and systems for carrying out the methods. However, it will be understood by those skilled in the art that the methods and systems may be practiced without these details and that numerous variations or modifications from the specifically described embodiments may be possible and are deemed within the claims or claimable subject matter in this or subsequent patents. All United States (U.S.) published patent applications and U.S. Patents referenced herein are hereby explicitly incorporated herein by reference. In the event definitions of terms in the referenced patents and applications conflict with how those terms are defined in the present application, the definitions for those terms that are provided in the present application shall be deemed controlling.


The term “fuel”, according to this disclosure, means a combustible composition comprising a major portion of, for example, methane, natural gas, liquefied natural gas, propane, atomized oil or the like (either in gaseous or liquid form). Fuels useful in the disclosure may comprise minor amounts of non-fuels therein, including oxidants, for purposes such as premixing the fuel with the oxidant, or atomizing liquid fuels. As used herein the term “fuel” includes gaseous fuels, liquid fuels, flowable solids, such as powdered carbon or particulate material, waste materials, slurries, and mixtures or other combinations thereof. When the fuel comprises gaseous fuel, the gaseous fuel may be selected from the group consisting of methane, natural gas, liquefied natural gas, propane, carbon monoxide, hydrogen, steam-reformed natural gas, atomized oil or mixtures thereof.


“Oxidant” means air, or compositions comprising the same molar concentration of oxygen as air, while the term “oxygen” means a gas with an oxygen molar concentration of at least 50%. Such oxidants include oxygen-enriched air containing at least 50% vol., oxygen such as “industrially” pure oxygen (99.5%) produced by a cryogenic air separation plant or non-pure oxygen produced by an adsorption process or membrane permeation process (about 90% vol. oxygen or more).


Submerged combustion melters useful in methods and systems of the present disclosure may be comprised of metal, ceramic, ceramic-lined metal, or combination thereof. Suitable metals include stainless steels, for example, but not limited to, 306 and 316 steel, as well as titanium alloys, aluminum alloys, and the like.


In all embodiments of the disclosure the sources of oxidant and fuel may be one or more conduits, pipelines, storage facility, cylinders, or, in embodiments where the oxidant is air, ambient air. Oxygen-enriched oxidants may be supplied from a pipeline, cylinder, storage facility, cryogenic air separation unit, membrane permeation separator, or adsorption unit such as a vacuum swing adsorption unit. Certain burner and melter embodiments may comprise a source of oxidant fluidly connected to the second conduit for routing the oxidant to the primary annulus, wherein the oxidant is selected from the group consisting of air and oxygen-enriched air, and a source of fuel fluidly connected to the second end of the first conduit for routing the fuel to the longitudinal bore of the first conduit.


In certain methods of the disclosure the predicted and/or controlled property of the molten glass may be a physical property selected from the group consisting of boiling point, color, concentration, density, electrical conductivity or impedance, flexibility, flow rate, mass, melting point, pressure, specific heat, resistivity, temperature, tension, velocity, viscosity, and volume.


In certain methods the predicting step may comprise measuring the depth or level of molten glass in the glass tank furnace, and using the measured depth or level in the predicting.


Certain method embodiments may comprise feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows.


Certain method embodiments may comprise using the predicted value of the at least one property of the melt to control the glass tank furnace.


Certain method embodiments may comprise feeding forward the predicted value of the at least one property of the melt to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows and using the predicted value of the at least one property to control the glass tank furnace.


Certain method embodiments may comprise measuring frequency and/or amplitude of the variable system vibration. Certain methods may comprise analyzing the frequency and/or amplitude of the variable system vibration using one or more mathematical techniques to identify one or more key frequencies and/or amplitudes. Certain methods may comprise measuring at least one other system property selected from the group consisting of flow rate of oxidant, flow rate of fuel, flow rate of glass forming material, flow rate of molten glass, glass tank furnace pressure, height or depth of molten glass in the glass tank furnace, and combinations thereof. In certain methods the predicting may comprise using a technique selected from the group consisting of linear regression, non-linear modeling, and neural net modeling.


Certain method and systems embodiments of the disclosure may be controlled by one or more controllers. For example, burner flame temperature may be controlled by monitoring one or more parameters selected from velocity of the fuel, velocity of the primary oxidant, mass flow rate of the fuel, mass flow rate of the primary oxidant, energy content of the fuel, temperature of the fuel as it enters the burner, temperature of the primary oxidant as it enters the burner, temperature of the effluent, pressure of the primary oxidant entering the burner, humidity of the oxidant, burner geometry, combustion ratio, and combinations thereof. Exemplary methods and systems of the disclosure may comprise one or more slave combustion controller which receives one or more input parameters selected from velocity of the fuel, velocity of the primary oxidant, mass flow rate of the fuel, mass flow rate of the primary oxidant, energy content of the fuel, temperature of the fuel as it enters the burner, temperature of the primary oxidant as it enters the burner, pressure of the oxidant entering the burner, humidity of the oxidant, burner geometry, oxidation ratio, temperature of the effluent and combinations thereof, and may employ a control algorithm to control combustion temperature based on one or more of these input parameters. One or more of the slave combustion controllers may feed one or more outputs to one or more master controllers that receive measurements indicative of one or more melter vibrations and/or oscillations, the master controller then predicting a parameter of the melt for feeding forward to another process, or controlling the melter, or both.


Referring now to the figures, FIG. 1 is a side-elevation view, partially in cross-section, of a submerged combustion melter system and method embodiment 1 in accordance with the present disclosure, including a glass tank furnace or melter 10 positioned on a plant floor or other surface 2, including two burners 4 and 6, one or both of which may be of the adjustable burner type described in assignee's co-pending U.S. patent application Ser. No. 13/268,028, filed Oct. 7, 2011, now U.S. Pat. No. 8,875,544, comprising first and second conduits configured to form a primary annulus between the external surface of the first conduit and the internal surface of the second conduit, and an adjustable structure comprising a generally cylindrical central hub adjustable axially in relation to and removably attached to the first end of the first conduit, the hub defining a central passage and one or more non-central through passages. More than or less than two burners may be used, as well as burners of other designs, as long as one submerged burner is present. Metter 10 includes sidewalls 8, a floor 12, a roof 14, an exhaust chute 16, and a glass melt exit 18. A glass-forming material feed bin 20 may be attached to melter sidewall 8 via a conduit 22. One or more burners 4, 6 may be in one or more sidewalls 8, as long as the flame and/or products of combustion 28 emanate below surface 24 of melt 26. Burners 4, 6 may be positioned in a sidewall 8 or floor 12 of submerged combustion melter 10 such that the longitudinal axis of the burners makes an angle to a side panel 8 or floor 12 of melter 10 ranging from about 30 to about 90 degrees. Sidewalls 8, floor 12, and roof 14 are typically composed of ceramic or other refractory material. Other melter designs, having other feed arrangements, burner arrangements, and wall designs, such as disclosed in assignee's co-pending application Ser. No. 12/817,754, filed Jun. 17, 2010, now U.S. Pat. Nos. 8,769,992; 12/888,970, filed Sep. 23, 2010, now U.S. Pat. Nos. 8,650,914; and 13,267,990, 13,268,028, 13/268,098, and 13/268,130 all filed Oct. 7, 2011, and now U.S. Pat. Nos. 8,997,525, 8,875,544, 8,707,740, and 9,021,838, respectively and U.S. Pat. No. 7,273,583, are considered within the present disclosure.


Still referring to FIG. 1, the inventors herein have discovered that submerged combustion melter systems such as illustrated schematically in embodiment 1 of FIG. 1 may exhibit vibration and/or oscillation depending on their configuration, as indicated in FIGS. 1 at 30 and 32. The inventors herein have also discovered that this vibration and/or oscillation may be used for one or more useful purposes, such as controlling (or contributing to the control of) submerged combustion melter 10, and/or controlling or contributing to the control of one or more processes or systems downstream of melter 10. As a non-limiting example, embodiment 1 illustrated schematically in FIG. 1 employs burner controllers 34, 36, which may be programmable logic controllers or other controllers. In this embodiment, controller 34 receives signals (signals, which may be wired or wireless, are indicated by dashed lines) from oxidant flow meter 38 and fuel flow meters 40, 42, while controller 36 receives signals from oxidant flow meter 44 and fuel flow meter 46. Controllers 34 and 36 may send control signals to control valves (not illustrated) controlling flow of fuel (such as natural gas) and oxidant (such as oxygen) to burners 4 and 6. A main or primary, or master controller 48 may receive one or signals indicating vibration and/or oscillation of one or more locations of melter 10. Master controller 48 may also receive various other signals, for example from burner controllers 34, 36; a glass forming material feed flow meter 50; from a molten glass depth or level sensor 52; from a melt temperature sensor 54; and/or from a melt flow rate sensor 56 in a forehearth 58. A predicted value P of the melt may then be computed or estimated mathematically by controller 48 and used for one or more purposes, as noted further herein. It will be understood that many control variations are possible. For example, controller 48 may receive signals directly from flow meters 38, 40, 42, 44, and 46 rather than through burner controllers 34, 36. In the figures, direction of flow of signal is indicated by arrows. Indication of an arrow in one direction does not necessarily mean signals cannot be sent the opposite direction. Double headed arrows, while generally indicating that signals may be sent and received between two components, does not mean that signals are always sent between those components in both directions.


Referring now to FIG. 2, FIG. 2 is a schematic process flow diagram of a prior art air-fuel fiberization system and method embodiment 100 that may benefit from the systems and methods of the invention. Molten glass 101 from forehearth 58 of embodiment 1 may be transported to a heated pot 104. Optionally, glass marbles may be transported to distribution hopper 102 and then into heated pot 104, which then melts the marbles into molten glass. Molten glass 101 and/or marbles may be transported to feed hopper 102 and/or heated pot 104 with a distribution manifold to a plurality of heated pots 104, the feed rate to heated pots 104 being a function of pot temperature and roller 110 rpm. Heated pot 104, sometimes referred to as the marble pot, may typically comprise a metallic cylinder heated with a heating jacket using premixed natural gas burners on its side walls. The bottom of marble pot 104 may be formed from a metal alloy comprising multiple holes ranging from about 0.05 inch to 0.5 inch in diameter, depending on the glass fiber product being made, through which the molten glass is drawn into primary fibers 106 (only one primary fiber is shown). Primary fibers 106 may be pulled and directed by rollers 112 and by fiber guides 113 and 114 through a heat containment shield 108. Shield 108 may extend in space between the bottom of marble pot 104 to the top of the first set of rollers 110, and functions to control the cooling rate of the primary fiber. The objective is to keep the primary fiber as hot as possible without damaging roller pad material in the rollers. In addition to the heat shield, heat sources, such as infrared sources may be placed in the spaces before rollers 110 and 112 or after the rollers.


A fiberization burner 116, which may be an air-fuel or oxy-fuel burner, functions to produce a hot flame at a controlled temperature, velocity, and oxidation state. The glass fiber product to be manufactured is a function of the mass flow rate of the glass, the primary glass fiber diameter, the flame temperature produced by burner 116, the slot size and pressure inside of burner 116, and the product code fiber diameter. Benefits of using oxygen or oxygen-enriched air as an oxidant in fiberization burners may include higher flame temperature fiberization, which may lead to increased fiber tensile strength, longer fibers, and reduce production or elimination of shot, or looser process control to avoid producing shot. Fluctuations in humidity may be reduced, and variation in fiber quality may be reduced.


In accordance with the present disclosure, a controller 140 may receive a signal P from controller 48 controlling melter system and method 1 (FIG. 1). Controller 140 may also receive signals from heated pot 104, pull rollers 110, and/or burner 116, and may send one or more control signals to a valve 142, heated pot 104, pull rollers 110, and/or burner 116.


In the system and method illustrated schematically in FIG. 2, a collection chamber 118 comprising a generally cylindrical chute collects short fibers and entrains air into chamber 118 to rapidly cool the molten fibers. The fiber are then routed to a larger section of chamber 118 where at the far end a fiber pickup drum 120 collects the fibers, where a secondary fiber pickup apparatus 122, such as vacuum ducting or a roller, removes the fibers. Pickup drum 120 is typically a rotating perforated steel cylinder with a filter material suitable for collecting fibers secured to the outer surface of the cylinder, with aide of negative pressure on the inside of drum 120. Combustion gases, any particulates, and excess air (in the prior art process, and in addition excess oxygen in systems and methods of the present disclosure) pass through drum 120 through ducting 124 and flow through a particulate removal device 126, with aide of an exhaust fan 128. A heat exchanger 130 may be used to cool exhaust gases, which exit to atmosphere at 136. In prior art system and methods using air-fuel combustion, cool air 132 is used to cool the exhaust, resulting in warmed air 134 of low grade heat content, largely unusable in heat recovery. However, with the higher temperatures experienced in oxy-fuel combustion if used in fiberization burner 116, this heat may be recovered and used in various ways. In light of the higher fiberization burner flame temperatures involved when using oxy-fuel fiberization burners (from about 2200 to about 3200° F. as opposed to 1900° F. for air-fuel fiberization flame temperatures), opportunities exist also for heat recovery and energy savings, as further explained in assignee's U.S. Pat. No. 7,802,452



FIG. 3 is an illustration of a method and system 200 of making continuous fibers in accordance with the present disclosure. Several different processes may be used to form fibers, depending on the type of fiber. Textile fibers may be formed from molten glass directly from the furnace, or the molten glass may be fed first to a machine that forms glass marbles of about 0.62 inch (1.6 cm) in diameter, as alluded to herein. These marbles allow the glass to be inspected visually for impurities. In both the direct melt and marble melt process, the glass or glass marbles may be fed through electrically heated bushings (also called spinnerets) 202, 204. Bushing may be made of platinum or metal alloy, with anywhere from 200 to 3,000 very fine orifices 206. The molten glass passes through orifices 206 and comes out as fine filaments 208, as indicated schematically in FIG. 3. Multiple fine or primary filaments 208 may be collected into a product filament 210 by a fiber gatherer (in some embodiments binder applicator) 212 and rollers 213, and product filament 210 may be wound on a winder 214. A controller 218 may be used to control production of continuous fibers in embodiment 200 and similar embodiments. Controller 218 may receive a predicted value P from controller 48 of system and method embodiment 1 (FIG. 1), as well as signals representative of temperature of bushings 202, 204, pull rate of rollers 213, rate of winding of winder 214, and/or other parameters.



FIG. 4 illustrates another non-limiting system embodiment 300 in accordance with the present disclosure. In embodiment 300, initial foamy molten glass 304 from one or more submerged combustion melters 10 is discharged into one or more refractory or refractory-lined channels 58 where the bubble size in the molten glass is increased through means of additional air or other gaseous injection through one or more gas injectors 302, four being illustrated in this embodiment, to form a lower density, foamy molten glass through increased bubble size, and to control product density, bubble size, and gases contained within the bubbles. This lower density glass is discharged to a cooling and annealing lehr 306 on a conveyor 308 for thermal treatment into glass 310, and subsequent shaping into final products 314 of various shapes, for example by cutting equipment 312. Lehr 306 may not be necessary in all embodiments. In embodiment 300, a controller 316 may receive a sensed signal indicative of vibration and/or oscillation of melter 10, as well as other signals, such as oxidant and fuel flow rates to burner 4, flow of gas to refractory channel 58, level in melter 10, and so on. Controller 316 may calculate an actual or predicted value of a parameter of foamy melt 304 exiting melter 10, for example density, which value may be used to control the system and method, for example, amount of gas injected into the foamy melt using a valve 318 or other flow controller, burner fuel or oxidant flow rates, and the like.


Flow rates and composition of injected gas will depend upon the desired final foamed glass product density, and the flow rate of molten glass, but generally the flow rate of gas will range from about 0 to about 0.1 scf/lb. (0 to about 6250 cm3/kg) of molten glass product/injector, or from 0 to about 0.03 scf/lb. (0 to about 1875 cm3/kg) of molten glass product/injector. The number of and position of gas injectors 302 may vary, with lower number of injectors generally meaning their diameter would increase to deliver an equivalent amount of gas. Some of the injectors may be floor (bottom) mounted while some may be side-wall mounted, or all may be floor-mounted or all may be side-wall mounted. Gas injectors 302 may be positioned uniformly or non-uniformly. Flow of gas may be pulsed or non-pulsed. The flow rate of molten glass though channel 58 will in turn depend on the dimensions of channel 58, size of melter 10, temperature of the melt, viscosity of the melt, and like parameters, but in general the flow rate of molten glass in channel 58 may range from about 0.5 lb/min to over 5000 lbs/min (from about 0.23 kg/min to over 2300 kg/min), or from about 10 lbs/min to about 500 lbs/min (from about 4.5 kg/min to about 227 kg/min), or from about 100 lbs/min to 300 lbs/min (from about 45 kg/min to about 135 kg/min).


Temperature of the injected gas through gas injectors 302 is not critical, but higher temperature gases may increase the ability of the gas to disperse in the foamy molten glass and cause less heat loss in the system, while cooler gases may require that the melter and possibly the lehr use more energy in the melting and annealing steps. In certain embodiments the injected gas may actually be used to control cooling of the foamy molten glass.


Pressure of the injected gases is also not critical, except that the pressure at the tip of the gas injectors need be higher than the local pressure of the foamy molten glass in channel 58. Too high gas injection pressures may cause unnecessary and undesired “belching” of the foamy molten glass, while too low gas injection pressure may cause the gas to be held up by the foamy molten glass, or not enter the foamy molten glass in channel 58. In worse cases the foamy molten glass might enter the gas injectors, which is undesired.


Gas injectors 302 may simply be open-ended pipes protruding through the bottom, the sides, or both of channel 58, or may be specifically designed injectors, such as pipe-in-pipe designs having water-cooled injection tubes, nozzles, and the like. The injectors themselves may be straight, angled, or curved conduits, and they may inject gas perpendicular to the bottom or sidewalls of channel 58, or may inject gas at an angle to the bottom and/or sidewalls.


Channel 58 and gas injectors 302 may be made from stainless steel, ceramic material (for example zirconia and the like), or other heat-resistant material, and combinations thereof (for example ceramic inserts in stainless steel tubes). Channel 58 may have any lateral shape, such rectangular, oval, round, and the like. Depth of channel 58 may vary, but exemplary embodiments may have a depth that is commensurate with melter 10 depth, and such that the foamy molten glass will be able to move onto conveyor 308 and into lehr 306.



FIGS. 5, 6, 7, and 8 are logic diagrams of four method embodiments in accordance with the present disclosure. The method of embodiment 500 of FIG. 5 comprises flowing an oxidant and a fuel into a submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass, box 502; and predicting a value of at least one property of the molten glass using at least the variable system vibration, box 504.


Another method of this disclosure is presented in the logic diagram of FIG. 6 as embodiment 600. Embodiment 600 is a method of producing molten glass, and comprises the steps of flowing an oxidant and a fuel into at least one submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass, box 602. Method embodiment 600 then comprises measuring frequency and/or amplitude of the variable system vibration, box 604, then predicting a value of viscosity of the molten glass using at least the measured frequency and/or amplitude of the variable system vibration, box 606.


Yet another method of this disclosure is presented in the logic diagram of FIG. 7 as embodiment 700. Embodiment 700 is a method of producing molten glass, and comprises the steps of flowing an oxidant and a fuel into at least one submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass, box 702. Method embodiment 700 then comprises measuring frequency and/or amplitude of the variable system vibration, box 704, then analyzing the frequency and/or amplitude of the variable system vibration using one or more mathematical techniques to identify one or more key frequencies and/or amplitudes, box 706. Method 700 then comprises predicting a value of viscosity of the molten glass using at least the measured frequency and/or amplitude of the variable system vibration, box 708.


Another method of this disclosure is presented in the logic diagram of FIG. 8 as embodiment 800. Embodiment 800 is a method of producing molten glass, and comprises the steps of flowing an oxidant and a fuel into a submerged combustion burner in a glass tank furnace, the glass tank furnace also receiving a feed of glass forming material, the burner and furnace comprising a melting system, the melting system having a variable system vibration, the melting system producing molten glass, box 802, then predicting a value of at least one property of the molten glass using at least the variable system vibration, box 804. Method embodiment 800 includes feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter for making glass objects, box 806. The process or component downstream of the glass tank melter may be selected from the group consisting of a continuous glass fiber production system, a staple fiber attenuation system, a system for producing shaped glass objects, or other downstream component, system or method. In certain embodiments the system for producing shaped glass objects may comprise a system for producing foamed glass objects.


In operation of burners of the disclosure, in exemplary embodiments oxidant may be fed to the primary annulus, and a fuel to the longitudinal bore of the first conduit. An inorganic glass-forming material is charged to the melter. The mass flow rate of the inorganic material, for example glass, is a function of the composition of the feed material, desired composition, viscosity, and temperature of the molten glass, the flame temperature of the burner(s), the burner geometry, for example burner exit, nozzle exit, and non-central passages sizes, the pressure in the mixing region of the burner, and other parameters. The process operating conditions are generally not independent values but have some degree of interaction. Oxygen-enhanced oxidant/fuel melting is markedly different than the traditional air-fuel melting processes. The general principle is to operate combustion in the mixing region of the burner in a manner that replaces some of the air with a separate source of oxygen. The overall combustion ratio may not change. The process of combining fuel and oxygen-enriched oxidant will, in most embodiments, primarily occur in the mixing region, after the gases have passed over a flame arrestor safety device. Varying the oxygen content of the oxidant can control the flame temperature of the combustion gases.


The total quantities of fuel and oxidant used by submerged combustion burners useful in methods and systems of the present disclosure may be such that the flow of oxygen may range from about 0.9 to about 1.2 of the theoretical stoichiometric flow of oxygen necessary to obtain the complete combustion of the fuel flow. Another expression of this statement is that the combustion ratio may range from about 0.9 to about 1.2.


The velocity of the fuel in the burners of various method and system embodiments of the present disclosure depends on the burner geometry used, but generally is at least about 15 meters/second (m/s). The upper limit of fuel velocity depends primarily on the desired penetration of flame and/or combustion products into the glass melt and the geometry of the burner and melter; if the fuel velocity is too low, the flame temperature may be too low, providing inadequate temperature in the melter, which is not desired, and if the fuel flow is too high, flame and/or combustion products might impinge on a melter wall or roof, or cause carryover of melt into the exhaust, or be wasted, which is also not desired. Similarly, oxidant velocity should be monitored so that flame and/or combustion products do not impinge on a melter wall or roof, or cause carryover of melt into the exhaust, or be wasted. Oxidant velocities depend on fuel flow rate and fuel velocity, but in general should not exceed about 200 ft/sec at 400 scfh flow rate.


Additionally, burners useful in methods and system embodiments of this disclosure may also be provided with stabilization of the flame with an auxiliary injection of fuel and/or oxidant gases. For example, a portion of the oxidant may be premixed with fuel as a primary oxidant, usually air, in addition to a secondary oxidant injection.


Conduits, submerged combustion melter, luers, forehearths, channels, burners and the like useful in methods of the present disclosure may be comprised of metal, ceramic, ceramic-lined metal, or combination thereof. Suitable metals include stainless steels, for example, but not limited to, 306, 316, as well as titanium alloys, aluminum alloys, and the like. High-strength materials like C-110 and C-125 metallurgies that are NACE qualified may be employed. (As used herein, “NACE” refers to the corrosion prevention organization formerly known as the National Association of Corrosion Engineers, now operating under the name NACE International, Houston, Tex.) Use of high strength steel and other high strength materials may significantly reduce the wall thickness required, reducing weight for example of burners and melter walls. Threaded connections may eliminate the need for 3rd party forgings and expensive welding processes—considerably improving system delivery time and overall cost. It will be understood, however, that the use of 3rd party forgings and welding is not ruled out for certain burners useful in the methods described herein, and may actually be preferable in certain situations.


If ceramic materials are used, suitable materials may include fused zirconia (ZrO2), fused cast AZS (alumina-zirconia-silica), rebonded AZS, or fused cast alumina (Al2O3). The choice of a particular material is dictated among other parameters by the chemistry, pressure, and temperature of fuel and oxidant used and type of glass melt to be produced.


The skilled artisan, having knowledge of the particular application, pressures, temperatures, vibrations, and available materials, will be able design the most cost effective, safe, and operable system components for each particular application without undue experimentation.


One or more control strategies may be employed, as long as the strategy includes measurement of melter system vibration and/or oscillation and those measurements (or values derived from those measurements) are used in predicting a melt property and/or controlling the melter system and/or controlling a downstream component or process. A combustion process control scheme may be employed, for example in conjunction with burner controllers 34, 36. A master controller may be employed, such as controller 48, but the disclosure is not so limited, as any combination of controllers could be used. Programmable logic controllers (PLCs) may be used.


Control strategies may be selected from proportional-integral (PI), proportional-integral-derivative (PID) (including any known or reasonably foreseeable variations of these), and may compute a residual equal to a difference between a measured value and a set point to produce an output to one or more control elements. The controller may compute the residual continuously or non-continuously. Other possible implementations of the disclosure are those wherein the controller comprises more specialized control strategies, such as strategies selected from feed forward, cascade control, internal feedback loops, model predictive control, neural networks, and Kalman filtering techniques.


Measurement of vibration is a well-developed science in its own right and requires little explanation to the skilled vibration sensor artisan. A good summary is provided by Furman, B. J., “Vibration Measurement”, San Jose State University, Department of Mechanical and Aerospace Engineering, pp. 1-14, 22 Nov. 2005, incorporated herein by reference. Furman described vibration as interchange between potential and kinetic energy in bodies with finite stiffness and mass that arises from time dependent energy input, and gives examples, including fluid flow. Without being limited to any particular theory, the inventors herein theorize that the oxidant and/or fuel fluid flows through submerged combustion burners, and the flames and combustion products emanating from those burners, contribute to the vibration and/or oscillation observed in submerged combustion glass tank furnaces. Basic parameters of vibration study, such as amplitude, amplitude peak level, peak-to-peak amplitude, root-mean-square (RMS) amplitude level, and average (rectified) amplitude, are given schematically in FIG. 9A for a sinusoidal vibration, and in FIG. 9B for a more typical industrial vibration, from Furman.


Furman also summarizes vibration measurement transducers that may be useful in methods and systems of the present disclosure, for example, displacement-based sensors, velocity-based sensors, and acceleration-based sensors. Other sensors may be used. Examples of displacement-based sensors include linear variable differential transformer (LVDT) sensors, Eddy current sensors, capacitive sensors, and Hall sensors. Examples of velocity-based sensors include geophones and laser Doppler vibrometers. Examples of acceleration-based vibration sensors, perhaps more commonly referred to simply as accelerometers, include piezoelectric accelerometers, microelectromechanical systems (MEMS) accelerometers, and thermal accelerometers.


Sensors may be provided for burner controllers for the following parameters, which are merely exemplary examples: Vfuel, velocity of fuel entering burner; VPO, velocity of primary oxidant entering burner; VSO, velocity of secondary oxidant entering burner; Mfuel, mass flow rate of fuel entering burner; MPO, mass flow rate of primary oxidant entering burner; Tfuel, temperature of fuel entering burner; TPO, temperature of primary oxidant entering burner; PPO, pressure of primary oxidant entering burner; HPO, humidity of primary oxidant. Outputs may be provided for the following parameters, which are merely exemplary: Vfuel, velocity of fuel entering burner; VPO, velocity of primary oxidant entering burner; Mfuel, mass flow rate of fuel entering burner; MSO, mass flow rate of secondary oxidant entering burner; Tfuel, temperature of fuel entering burner; TPO, temperature of primary oxidant entering burner; PSO, pressure of secondary oxidant entering burner; MEFF (or MHTF), mass flow rate of hot effluent (or heat transfer fluid). Other parameters may be included as inputs, such as burner geometry, melter geometry, combustion ratio, melt viscosity, and the like.


Mathematical treatment of vibration and/or oscillation data, or any data collected as described herein, is straightforward. Transforms, such as Fourier and Inverse Fourier transforms, Laplace and Inverse Laplace transforms, Z-transforms and inverse Z-transforms, are known and explained in various textbooks and on the Internet. For example, see MathWorks.com. Any one or more of these mathematical treatments may be used to identify key frequencies, amplitudes, and the like.


An example of an equation that might be analyzed and used for predicting melt viscosity is Equation (1):

η=f(T, h, ω, u, P, R)  (1)


where: η=melt viscosity, T=melt temperature, h=depth of glass in the melter, ω=frequency of vibration and/or oscillation of the melter, u=amplitude of vibration and/or oscillation of the melter, P=pressure in the melter, and R=melt flow rate from the melter. Non-limiting examples of other equations might be Equations 2-6:

η=f(T, ω, u, P, R, Vfuel,VPO, Mfuel, MPO)  (2)
η=f(T, h, ω, P, R, Vfuel, VPO, Mfuel, MPO)  (3)
η=f(T, h, ω, u, P, R, melter geometry)  (4)
Θ=f(T, h, ω, u, P, R, burner geometry)  (5)
ρ=f(T, ω, u, P, R)  (6)

where ρ is density of the melt. More than one equation may be employed, depending on the specific situation.


The term “control”, used as a transitive verb, means to verify or regulate by comparing with a standard or desired value. Control may be closed loop, feedback, feed-forward, cascade, model predictive, adaptive, heuristic and combinations thereof. The term “controller” means a device at least capable of accepting input from sensors and meters in real time or near—real time, and sending commands directly to burner control elements, and/or to local devices associated with burner control elements able to accept commands. A controller may also be capable of accepting input from human operators; accessing databases, such as relational databases; sending data to and accessing data in databases, data warehouses or data marts; and sending information to and accepting input from a display device readable by a human. A controller may also interface with or have integrated therewith one or more software application modules, and may supervise interaction between databases and one or more software application modules.


The phrase “PID controller” means a controller using proportional, integral, and derivative features. In some cases the derivative mode may not be used or its influence reduced significantly so that the controller may be deemed a PI controller. It will also be recognized by those of skill in the control art that there are existing variations of PI and PID controllers, depending on how the discretization is performed. These known and foreseeable variations of PI, PID and other controllers are considered within the disclosure.


The controller may utilize Model Predictive Control (MPC). MPC is an advanced multivariable control method for use in multiple input/multiple output (MIMO) systems. MPC computes a sequence of manipulated variable adjustments in order to optimise the future behavior of the process in question. At each control time k, MPC solves a dynamic optimization problem using a model of the controlled system, so as to optimize future behavior (at time k+1, k+2 . . . k+n) over a prediction horizon n. This is again performed at time k+1, k+2 . . . . MPC may use any derived objective function, such as Quadratic Performance Objective, and the like, including weighting functions of manipulated variables and measurements. Dynamics of the process and/or system to be controlled are described in an explicit model of the process and/or system, which may be obtained for example by mathematical modeling, or estimated from test data of the real process and/or system. Some techniques to determine some of the dynamics of the system and/or process to be controlled include step response models, impulse response models, and other linear or non-linear models. Often an accurate model is not necessary. Input and output constraints may be included in the problem formulation so that future constraint violations are anticipated and prevented, such as hard constraints, soft constraints, set point constraints, funnel constraints, return on capital constraints, and the like. It may be difficult to explicitly state stability of an MPC control scheme, and in certain embodiments of the present disclosure it may be necessary to use nonlinear MPC. In so-called advanced control of various systems, PID control may be used on strong mono-variable loops with few or nonproblematic interactions, while one or more networks of MPC might be used, or other multivariable control structures, for strong interconnected loops. Furthermore, computing time considerations may be a limiting factor. Some embodiments may employ nonlinear MPC.


A feed forward algorithm, if used, will in the most general sense be task specific, meaning that it will be specially designed to the task it is designed to solve. This specific design might be difficult to design, but a lot is gained by using a more general algorithm, such as a first or second order filter with a given gain and time constants.


Although only a few exemplary embodiments of this disclosure have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel teachings and advantages of this disclosure. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims. In the claims, no clauses are intended to be in the means-plus-function format allowed by 35 U.S.C. §112, paragraph 6 unless “means for” is explicitly recited together with an associated function. “Means for” clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents, but also equivalent structures.

Claims
  • 1. A method including feeding glass forming material into a melter, flowing an oxidant and a fuel into a submerged combustion burner positioned in the melter, the burner and melter defining a submerged combustion glass melting system producing molten glass, at least the melter having a variable vibration, the method comprising: a) measuring frequency and/or amplitude of the variable vibration of the melter;b) measuring oxidant flow rate, fuel flow rate, and glass forming material flow rate to the submerged combustion burner, and molten glass flow rate from the melter; andc) predicting a value of density of the molten glass using at least the measured frequency and/or amplitude of the variable vibration of the melter and the measured oxidant, fuel, glass forming material, and molten glass flow rates.
  • 2. The method of claim 1 comprising measuring the depth or level of molten glass in the glass tank furnace, and using the measured depth or level in the predicting.
  • 3. The method of claim 1 comprising feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows.
  • 4. The method of claim 1 comprising using the predicted value of the at least one property to control the glass tank furnace.
  • 5. The method of claim 1 comprising feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows and using the predicted value of the at least one property to control the glass tank furnace.
  • 6. The method of claim 1 wherein the predicting comprises using a technique selected from the group consisting of linear regression, non-linear modeling, and neural net modeling.
  • 7. A method of producing molten glass using submerged combustion, including feeding glass forming material into a melter, flowing an oxidant and a fuel into a submerged combustion burner positioned in the melter, the burner and melter defining a submerged combustion glass melting system producing molten glass, at least the melter having a variable vibration, the method comprising: a) measuring frequency and/or amplitude of the variable vibration of the melter;b) measuring oxidant flow rate, fuel flow rate, and glass forming material flow rate to the submerged combustion burner, and molten glass flow rate from the melter;c) predicting a value of viscosity of the molten glass using at least the measured frequency and/or amplitude of the variable vibration of the melter and the measured oxidant, fuel, glass forming material, and molten glass flow rates; andd) predicting a value of density of the molten glass using at least the predicted value of viscosity.
  • 8. The method of claim 7 comprising measuring the depth or level of molten glass in the glass tank furnace, and using the measured depth or level in the predicting.
  • 9. The method of claim 7 comprising feeding forward the predicted value of the at least one property to a controller controlling a process or component downstream of the glass tank melter into which at least a portion of the molten glass flows.
  • 10. The method of claim 7 comprising using the predicted value of the at least one property to control the glass tank furnace.
  • 11. The method of claim 7 comprising measuring at least one other system property selected from the group consisting of glass tank furnace pressure, height or depth of molten glass in the glass tank furnace, and combinations thereof.
  • 12. A method of making glass objects using submerged combustion, including feeding glass forming material into a melter, flowing an oxidant and a fuel into a submerged combustion burner positioned in the melter, the burner and melter defining a submerged combustion glass melting system producing molten glass, at least the melter having a variable vibration, the method comprising the steps of: a) measuring frequency and/or amplitude of the variable vibration of the melter;b) measuring oxidant flow rate, fuel flow rate, and glass forming material flow rate to the submerged combustion burner, and molten glass flow rate from the melter; andc) predicting a value of density of the molten glass using at least the measured frequency and/or amplitude of the variable vibration of the melter and the measured oxidant, fuel, glass forming material, and molten glass flow rates; andd) feeding forward the predicted value of the density to a controller controlling a process or component downstream of the melter for making glass objects.
  • 13. The method of claim 12 wherein the process or component downstream of the glass tank melter is selected from the group consisting of a continuous glass fiber production system, a staple fiber attenuation system, and a system for producing shaped glass objects.
  • 14. The method of claim 13 wherein the system for producing shaped glass objects comprises a system for producing foamed glass objects.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a division of U.S. application Ser. No. 13/268,065 filed Oct. 7, 2011, now issued Pat. No. 8,973,400. This application is related to assignee's United States non-provisional U.S. application Ser. No. 12/817,754, filed Jun. 17, 2010, now issued U.S. Pat. No. 8,769,992, issued Jul. 8, 2014; Ser. No. 12/888,970, filed Sep. 23, 2010, now issued U.S. Pat. No. 8,650,914, issued Feb. 18, 2014; Ser. No. 13/267,990, filed Oct. 7, 2011; and Ser. No. 13/268,028, filed Oct. 7, 2011, now issued U.S. Pat. No. 8,875,544, issued Nov. 4, 2014, all of which are incorporated herein by reference.

US Referenced Citations (281)
Number Name Date Kind
1716433 Ellis Jun 1929 A
2174533 See et al. Oct 1939 A
2118479 McCaskey Jan 1940 A
2269459 Kleist Jan 1942 A
2432942 See et al. Dec 1947 A
2679749 Poole Jun 1954 A
2718096 Henry et al. Sep 1955 A
2773545 Petersen Dec 1956 A
2781756 Kobe Feb 1957 A
2867972 Louis et al. Jan 1959 A
2878644 Fenn Mar 1959 A
2890166 Heinze Jun 1959 A
2902029 Hill Sep 1959 A
2981250 Stewart Apr 1961 A
3020165 Davis Feb 1962 A
3056283 Tiede Oct 1962 A
3073683 Switzer et al. Jan 1963 A
3084392 Labino Apr 1963 A
3088812 Bitterlich et al. May 1963 A
3104947 Switzer et al. Sep 1963 A
3129087 Hagy Apr 1964 A
3160578 Saxton et al. Dec 1964 A
3165452 Williams Jan 1965 A
3170781 Keefer Feb 1965 A
3174820 See et al. Mar 1965 A
3215189 Bauer Nov 1965 A
3224855 Plumat Dec 1965 A
3237929 Plumat et al. Mar 1966 A
3239325 Roberson et al. Mar 1966 A
3241548 See et al. Mar 1966 A
3248205 Dolf et al. Apr 1966 A
3260587 Dolf et al. Jul 1966 A
3268313 Burgman et al. Aug 1966 A
3285834 Guerrieri et al. Nov 1966 A
3325298 Brown Jun 1967 A
3380463 Trethewey Apr 1968 A
3402025 Garrett et al. Sep 1968 A
3407805 Bougard Oct 1968 A
3407862 Mustian, Jr. Oct 1968 A
3421873 Burgman et al. Jan 1969 A
3432399 Schutt Mar 1969 A
3445214 Oremesher May 1969 A
3498779 Hathaway Mar 1970 A
3510393 Burgman et al. May 1970 A
3525674 Barnebey Aug 1970 A
3533770 Adier et al. Oct 1970 A
3592623 Shepherd Jul 1971 A
3606825 Johnson Sep 1971 A
3617234 Hawkins et al. Nov 1971 A
3627504 Johnson et al. Dec 1971 A
3692017 Glachant et al. Sep 1972 A
3717139 Guillet et al. Feb 1973 A
3738792 Feng Jun 1973 A
3746527 Knavish et al. Jul 1973 A
3747588 Booth Jul 1973 A
3754879 Phaneuf Aug 1973 A
3756800 Phaneuf Sep 1973 A
3763915 Perry et al. Oct 1973 A
3764287 Brocious Oct 1973 A
3771988 Starr Nov 1973 A
3818893 Kataoka et al. Jun 1974 A
3835909 Douglas et al. Sep 1974 A
3840002 Douglas et al. Oct 1974 A
3885945 Rees et al. May 1975 A
3907585 Francel et al. Sep 1975 A
3913560 Lazarre et al. Oct 1975 A
3951635 Rough Apr 1976 A
3976464 Wardlaw Aug 1976 A
4001001 Knavish et al. Jan 1977 A
4004903 Daman et al. Jan 1977 A
4083711 Jensen Apr 1978 A
4110098 Mattmuller Aug 1978 A
4153438 Stream May 1979 A
4185982 Schwenninger Jan 1980 A
4203761 Rose May 1980 A
4226564 Takahashi et al. Oct 1980 A
4238226 Sanzenbacher et al. Dec 1980 A
4249927 Fakuzaki et al. Feb 1981 A
4270740 Sanzenbacher et al. Jun 1981 A
4282023 Hammel et al. Aug 1981 A
4303435 Sleighter Dec 1981 A
4316734 Spinosa et al. Feb 1982 A
4323718 Buhring et al. Apr 1982 A
4349376 Dunn et al. Sep 1982 A
4406683 Demarest Sep 1983 A
4413882 Bailey et al. Nov 1983 A
4488537 Laurent Dec 1984 A
4539034 Hanneken Sep 1985 A
4542106 Sproull Sep 1985 A
4545800 Won et al. Oct 1985 A
4626199 Bounini Dec 1986 A
4632687 Kunkle et al. Dec 1986 A
4634461 Demarest, Jr. et al. Jan 1987 A
4657586 Masterson et al. Apr 1987 A
4735642 Jensen et al. Apr 1988 A
4738938 Kunkle et al. Apr 1988 A
4758259 Jensen Jul 1988 A
4814387 Donat Mar 1989 A
4816056 Tsai et al. Mar 1989 A
4877436 Sheinkop Oct 1989 A
4882736 Pieper Nov 1989 A
4919700 Pecoraro et al. Apr 1990 A
4927886 Backderf et al. May 1990 A
4953376 Merlone Sep 1990 A
5032230 Shepherd Jul 1991 A
5052874 Johanson Oct 1991 A
5062789 Gitman Nov 1991 A
5097802 Clawson Mar 1992 A
5168109 Backderf et al. Dec 1992 A
5169424 Grinnen et al. Dec 1992 A
5199866 Joshi et al. Apr 1993 A
5204082 Schendel Apr 1993 A
5299929 Yap Apr 1994 A
5360171 Yap Nov 1994 A
5374595 Dumbaugh et al. Dec 1994 A
5405082 Brown et al. Apr 1995 A
5449286 Snyder et al. Sep 1995 A
5483548 Coble Jan 1996 A
5490775 Joshi et al. Feb 1996 A
5545031 Joshi et al. Aug 1996 A
5575637 Slavejkov et al. Nov 1996 A
5595703 Swaelens et al. Jan 1997 A
5606965 Panz et al. Mar 1997 A
5613994 Muniz et al. Mar 1997 A
5615668 Panz et al. Apr 1997 A
5636623 Panz et al. Jun 1997 A
5672827 Jursich Sep 1997 A
5713668 Lunghofer et al. Feb 1998 A
5718741 Hull et al. Feb 1998 A
5736476 Warzke et al. Apr 1998 A
5743723 Iatrides et al. Apr 1998 A
5765964 Calcote et al. Jun 1998 A
5814121 Travis Sep 1998 A
5829962 Drasek et al. Nov 1998 A
5833447 Bodelin et al. Nov 1998 A
5849058 Takeshita et al. Dec 1998 A
5863195 Feldermann Jan 1999 A
5944864 Hull et al. Aug 1999 A
5954498 Joshi et al. Sep 1999 A
5975886 Philippe Nov 1999 A
5979191 Jian Nov 1999 A
5984667 Philippe et al. Nov 1999 A
5993203 Koppang Nov 1999 A
6029910 Joshi et al. Feb 2000 A
6039787 Edlinger Mar 2000 A
6045353 VonDrasek et al. Apr 2000 A
6068468 Philippe et al. May 2000 A
6071116 Philippe et al. Jun 2000 A
6074197 Philippe Jun 2000 A
6077072 Marin et al. Jun 2000 A
6085551 Pieper et al. Jul 2000 A
6109062 Richards Aug 2000 A
6113389 Joshi et al. Sep 2000 A
6116896 Joshi et al. Sep 2000 A
6120889 Turner et al. Sep 2000 A
6123542 Joshi et al. Sep 2000 A
6126438 Joshi et al. Oct 2000 A
6154481 Sorg et al. Nov 2000 A
6156285 Adams et al. Dec 2000 A
6171100 Joshi et al. Jan 2001 B1
6183848 Turner et al. Feb 2001 B1
6210151 Joshi et al. Apr 2001 B1
6210703 Novich Apr 2001 B1
6237369 LeBlanc et al. May 2001 B1
6241514 Joshi et al. Jun 2001 B1
6244197 Coble Jun 2001 B1
6244857 VonDrasek et al. Jun 2001 B1
6247315 Marin et al. Jun 2001 B1
6250136 Igreja Jun 2001 B1
6250916 Philippe et al. Jun 2001 B1
6274164 Novich Aug 2001 B1
6276924 Joshi et al. Aug 2001 B1
6276928 Joshi et al. Aug 2001 B1
6293277 Panz et al. Sep 2001 B1
6314760 Chenoweth Nov 2001 B1
6314896 Marin et al. Nov 2001 B1
6338337 Panz et al. Jan 2002 B1
6344747 Lunghofer et al. Feb 2002 B1
6357264 Richards Mar 2002 B1
6386271 Kawamoto et al. May 2002 B1
6418755 Chenoweth Jul 2002 B2
6422041 Simpson et al. Jul 2002 B1
6454562 Joshi et al. Sep 2002 B1
6460376 Jeanvoine et al. Oct 2002 B1
6536651 Ezumi et al. Mar 2003 B2
6558606 Kulkarni et al. May 2003 B1
6660106 Babel et al. Dec 2003 B1
6694791 Johnson et al. Feb 2004 B1
6701617 Li et al. Mar 2004 B2
6705118 Simpson et al. Mar 2004 B2
6708527 Ibarlucea et al. Mar 2004 B1
6711942 Getman et al. Mar 2004 B2
6715319 Barrow et al. Apr 2004 B2
6722161 LeBlanc Apr 2004 B2
6736129 Sjith May 2004 B1
6739152 Jeanvoine et al. May 2004 B2
6796147 Borysowicz et al. Sep 2004 B2
6797351 Kulkarni et al. Sep 2004 B2
6854290 Hayes et al. Feb 2005 B2
6857999 Jeanvoine Feb 2005 B2
6883349 Jeanvoine Apr 2005 B1
6918256 Gutmark et al. Jul 2005 B2
7027467 Baev et al. Apr 2006 B2
7116888 Aitken et al. Oct 2006 B1
7134300 Hayes et al. Nov 2006 B2
7168395 Engdahl Jan 2007 B2
7231788 Karetta et al. Jun 2007 B2
7273583 Rue et al. Sep 2007 B2
7330634 Aitken et al. Feb 2008 B2
7383698 Ichinose et al. Jun 2008 B2
7392668 Adams et al. Jul 2008 B2
7428827 Maugendre et al. Sep 2008 B2
7441686 Odajima et al. Oct 2008 B2
7448231 Jeanvoine et al. Nov 2008 B2
7454925 DeAngelis et al. Nov 2008 B2
7509819 Baker et al. Mar 2009 B2
7565819 Jeanvoine et al. Jul 2009 B2
7578988 Jacques et al. Aug 2009 B2
7581948 Borders et al. Sep 2009 B2
7622677 Barberree et al. Nov 2009 B2
7624595 Jeanvoine et al. Dec 2009 B2
7748592 Koga et al. Jul 2010 B2
7767606 McGinnis et al. Aug 2010 B2
7778290 Sacks et al. Aug 2010 B2
7781562 Crawford et al. Aug 2010 B2
7802452 Borders et al. Sep 2010 B2
7832365 Hannum et al. Nov 2010 B2
7845314 Smith Dec 2010 B2
7855267 Crawford et al. Dec 2010 B2
20020086077 Noller et al. Jul 2002 A1
20020152770 Becher et al. Oct 2002 A1
20020162358 Jeanvoine et al. Nov 2002 A1
20020166343 LeBlanc Nov 2002 A1
20040168474 Jeanvoine et al. Sep 2004 A1
20040224833 Jeanvoine et al. Nov 2004 A1
20050039491 Maugendre et al. Feb 2005 A1
20050103323 Engdahl May 2005 A1
20060000239 Jeanvoine et al. Jan 2006 A1
20060101859 Takagi et al. May 2006 A1
20060174655 Kobayashi et al. Aug 2006 A1
20060233512 Aitken et al. Oct 2006 A1
20060257097 Aitken et al. Nov 2006 A1
20060287482 Crawford et al. Dec 2006 A1
20060293494 Crawford et al. Dec 2006 A1
20060293495 Crawford et al. Dec 2006 A1
20070106054 Crawford et al. May 2007 A1
20070122332 Jacques et al. May 2007 A1
20070130994 Boratav et al. Jun 2007 A1
20070137259 Borders et al. Jun 2007 A1
20070212546 Jeanvoine et al. Sep 2007 A1
20070220922 Bauer et al. Sep 2007 A1
20080035078 Li Feb 2008 A1
20080227615 McGinnis et al. Sep 2008 A1
20080256981 Jacques et al. Oct 2008 A1
20080276652 Bauer et al. Nov 2008 A1
20080293857 Crawford et al. Nov 2008 A1
20090042709 Jeanvoine et al. Feb 2009 A1
20090044568 Lewis Feb 2009 A1
20090176639 Jacques et al. Jul 2009 A1
20090220899 Spangelo et al. Sep 2009 A1
20100064732 Jeanvoine et al. Mar 2010 A1
20100087574 Crawford et al. Apr 2010 A1
20100089383 Cowles Apr 2010 A1
20100120979 Crawford et al. May 2010 A1
20100143601 Hawtof et al. Jun 2010 A1
20100162757 Brodie Jul 2010 A1
20100227971 Crawford et al. Sep 2010 A1
20100236323 D'Angelico et al. Sep 2010 A1
20100242543 Ritter et al. Sep 2010 A1
20100300153 Zhang et al. Dec 2010 A1
20100304314 Rouchy et al. Dec 2010 A1
20100307196 Richardson Dec 2010 A1
20100319404 Borders et al. Dec 2010 A1
20100326137 Rouchy et al. Dec 2010 A1
20110054091 Crawford et al. Mar 2011 A1
20110061642 Rouchy et al. Mar 2011 A1
20110088432 Purnode et al. Apr 2011 A1
20110107670 Galley et al. May 2011 A1
20110236846 Rue et al. Sep 2011 A1
20120216567 Boughton et al. Aug 2012 A1
20120216576 Boughton et al. Aug 2012 A1
Foreign Referenced Citations (20)
Number Date Country
196 19 919 Aug 1997 DE
100 29 983 Sep 2003 DE
10 2005 033330 Aug 2006 DE
0 181 248 Oct 1989 EP
1 337 789 Dec 2004 EP
1 990 321 Nov 2008 EP
2 133 315 Dec 2009 EP
1 986 966 Apr 2010 EP
1 667 934 Feb 2011 EP
2 740 860 Sep 1997 FR
191301772 Jan 1914 GB
191407633 Jan 1914 GB
164073 May 1921 GB
1208172 Jul 1989 IT
114827 Jul 1999 RO
9855411 Dec 1998 WO
2008103291 Aug 2008 WO
2009091558 Jul 2009 WO
2010011701 Jan 2010 WO
2010045196 Apr 2010 WO
Non-Patent Literature Citations (7)
Entry
“Glass Technologies—The Legacy of a Successful Public-Private Partnership”, 2007, U.S. Department of Energy, pp. 1-32.
“Glass Melting Technology—A Technical and Economic Assessment,” 2004, U.S. Department of Energy, pp. 1-292.
Rue, “Energy-Efficient Glass Melting—The Next Generation Melter”, Gas Technology Institute, Project No. 20621 Final Report (2008).
“Glass Industry of the Future”, United States Department of Energy, report 02-GA50113-03, pp. 1-17, Sep. 30, 2008.
Olabin, V.M. et al, “Submerged Combustion Furnace for Glass Melts,” Ceramic Engineering and Science Proceedings, Jan. 1, 1996, pp. 84-92, vol. 17—No. 2, American Ceramic Society Inc., US.
Furman, BJ, ME 120 Experimental Methods Vibration Measurement, San Jose University Department of Mechanical and Aerospace Engineering.
Mert et al., “A new method to determine viscosity of liquids using vibration principles,” Springer-Verlag 2003.
Related Publications (1)
Number Date Country
20150135775 A1 May 2015 US
Divisions (1)
Number Date Country
Parent 13268065 Oct 2011 US
Child 14606234 US