The present disclosure generally relates to the field of transparent substrate repair. More particularly, the present disclosure relates to repairing transparent substrates in situ, for example, without removing transparent substrates from an installed orientation in a position of end use.
Windows are substantially transparent structural components, and are incorporated into stationary structures and mobile structures alike. Vehicles may incorporate windows including, but not limited to, specialized windows (e.g. windshields, etc.) to provide transparent viewing out of vehicles. Many windows and windshields comprise a multi-layer, or laminate structure that imparts desirable characteristics to the transparent structures. Such desirable characteristics include improved strength, durability, resistance to damage or breakage, resistance to shattering, etc.
In use, transparent structures such as windows and windshields may sustain damage or an adverse degradation in their optimum optical transmissivity including, but not limited to rippling, distortion etc. Some of the adverse degradation may include force induced distortion, or rippling causing varying visible degrees of optical distortion. When it becomes necessary to repair windows and windshields that have incurred an unacceptable degree of damage due, for example, to force induced rippling, such repair requires taking the vehicle out of service for an amount of time, and removing and replacing the windows or windshields. This required maintenance for replacing windows and windshields is time consuming and costly. Improved window and windshield maintenance and repair processes that reduce time and expense would be advantageous.
An aspect of the present disclosure is directed to a method comprising contacting a first heat source to a first side of a transparent substrate, with the transparent substrate comprising an amount of distortion, and with the first heat source in communication with a controller; positioning a second heat source at a predetermined distance from a second side of the transparent substrate, with the second heat source in communication with the first or a second controller; activating the first and second heat sources; increasing the surface temperature of the first and second sides of the transparent substrate in situ to a predetermined temperature; maintaining the surface temperature of the first and second sides of the transparent substrate at predetermined temperatures for predetermined durations; and reducing distortion in the transparent substrate in situ.
Another aspect of the present disclosure is directed to, after or coincident with the step of contacting a first heat source to a first side of a transparent substrate, positioning at least one sensor on each of the first and second sides of the transparent substrate, with the heat sensors in communication with one or more controllers. It is therefore contemplated that a single controller may be in communication with both heat sources, or each heat source may be in communication with a separate controller.
A further aspect is directed to, after or coincident with increasing the surface temperature of the first and second sides of the transparent substrate in situ to a predetermined temperature, monitoring the surface temperature of the first and second sides of the transparent substrate.
In another aspect, in the step of contacting a first heat source to a first side of a transparent substrate, the transparent substrate comprises a windshield or a window.
In a further aspect, in the step of contacting a first heat source to a first side of a transparent substrate, the first side of the transparent substrate comprises an exterior surface, and the first heat source comprises a heat blanket.
In yet another aspect, in the step of positioning a second heat source at a predetermined distance from a second side of a transparent substrate, the second side of the transparent substrate comprises an interior surface, and the second heat source comprises at least one heat gun.
In another aspect, in the step of positioning a second heat source at a predetermined distance from a second side of a transparent substrate, the second heat source is in communication with a device for radiating heat.
In still another aspect, in the step of positioning a second heat source at a predetermined distance from a second side of a transparent substrate, the second heat source is positioned proximate to the second side of the transparent substrate.
In another aspect, in the step of positioning heat sensors on the first and second sides of the transparent substrate, said heat sensors comprise at least one thermocouple.
In a further aspect, in the step of maintaining the surface temperature of the first and second sides of the transparent substrate, the first side of the transparent substrate comprises an exterior surface and the temperature is maintained at a temperature ranging from about 160° F. to about 167° F. for a duration ranging from about 150 mins to about 210 mins.
In yet another aspect, in the step of maintaining the surface temperature of the first and second sides of the transparent substrate, the second side of the transparent substrate comprises an interior surface and the temperature is maintained at a temperature ranging from about 160° F. to about 165° F. for a duration ranging from about 150 mins to about 210 mins.
In yet another aspect, in the step of reducing distortion in the transparent substrate in situ, the distortion is reduced in an amount ranging from about 10% to 100%.
In a further aspect, in the step of contacting a first heat source to a first side of a transparent substrate having an amount of distortion, the transparent substrate comprises at least two layers of dissimilar material.
In yet another aspect, in the step of contacting a first heat source to a first side of a transparent substrate having an amount of distortion, the first side of the transparent substrate comprises at least one layer comprising a polymeric thermoset material.
In yet another aspect, in the step of contacting a first heat source to a first side of a transparent substrate having an amount of distortion, the transparent substrate comprises a layer comprising a polyurethane-containing material, a polyvinyl butryal resin-containing material, polyether-containing material and combinations thereof.
In a further aspect, in the step of contacting a first heat source to a first side of a transparent substrate having an amount of distortion, the transparent substrate comprises a layer configured to act as a spall shield.
In still another aspect, in the step of positioning a second heat source at a predetermined distance from a second side of the transparent substrate, the second side of the transparent substrate comprises at least one layer comprising glass.
Another aspect is directed to an object comprising a transparent substrate having distortion that is removed according to a method comprising contacting a first heat source to a first side of a transparent substrate, with the transparent substrate comprising an amount of distortion, with the transparent substrate positioned in place as a component in a larger structural assembly, and with the first heat source in communication with a controller; positioning a second heat source at a predetermined distance from a second side of the transparent substrate, with the second heat source in communication with the first or second controller; positioning at least one sensor each on the first and second sides of the transparent substrate, with the heat sensors in communication with the controller; activating the first and second heat sources; increasing the surface temperature of the first and second sides of the transparent substrate to heat the first and second sides of the transparent substrate in situ to a predetermined temperature; monitoring the surface temperature of the first and second sides of the transparent substrate; maintaining the surface temperature of the first and second sides of the transparent substrate at predetermined temperatures for predetermined durations; and reducing distortion in the transparent substrate in situ.
In a further aspect, the object is a stationary structure.
In another aspect, the object is a vehicle.
In yet another aspect, the vehicle is selected from group consisting of: a manned aircraft, an unmanned aircraft, a manned spacecraft, an unmanned spacecraft, a manned rotorcraft, an unmanned rotorcraft, a manned terrestrial vehicle, an unmanned terrestrial vehicle, a manned waterborne surface vehicle, an unmanned water borne surface vehicle, a manned waterborne sub-surface vehicle, an unmanned waterborne sub-surface vehicle, and combinations thereof.
Having thus described variations of the disclosure in general terms, reference will now be made to the accompanying drawings, which are not necessarily drawn to scale, and wherein:
a are perspective views of an aspect of the present disclosure showing a heat source and its position proximate to the interior surface and exterior surface of an aircraft windshield;
The presently disclosed subject matter now will be described more fully hereinafter with reference to the accompanying Drawings (i.e. FIGs.), in which some, but not all aspects of the presently disclosed subject matter are shown. Like numbers refer to like elements throughout. The presently disclosed subject matter may comprise many different forms and should not be construed as limited to the aspects set forth herein; rather, many aspects are provided so that this disclosure will satisfy applicable legal requirements. Indeed, many modifications and other alternatives of the presently disclosed subject matter set forth herein will come to mind to one skilled in the art, to which the presently disclosed subject matter pertains having the benefit of the teachings presented in the foregoing descriptions and the associated Drawings. Therefore, it is to be understood that the presently disclosed subject matter is not to be limited to the specific aspects disclosed and that modifications and other aspects are intended to be included within the scope of the appended claims.
Aspects of the present disclosure are directed to methods, systems and apparatuses for reducing or substantially eliminating distortion from a transparent substrate while the transparent substrate remain in position, in situ, integrated into a larger structure. Transparent substrates include, but are not limited to windows, windshields, etc. The term “substantially eliminating” refers to the elimination of more than about 90% of distortion from a transparent substrate. The term “transparent” refers to the percentage of light that passes through an object having a transmissivity value ranging from about 0% to about 100%.
According to aspects of the present disclosure, heat is a applied in situ to interior and exterior sides of an installed transparent substrate in a predetermined and controlled heating regimen, and for a predetermined duration, to restore a transparent substrate to an original degree of optical clarity and transmissivity by reducing or substantially eliminating visible distortion from the transparent substrate. Visible distortion includes, without limitation, the conditions known as rippling, including rippling that may be force induced. By reducing or substantially eliminating distortion from the transparent substrate in situ, the transparent substrate is substantially returned to its original shape and/or dimension. Importantly, the restoration of the transparent substrate through the removal or substantial elimination of distortion is conducted in situ. That is, the treatment performed on the transparent substrate is conducted while the transparent substrate is in its installed position as a part of a larger structure, device or object, etc., including, without limitation, stationary objects such as buildings, etc., and mobile objects, such as vehicles, including, without limitation, manned and unmanned aircraft, spacecraft, terrestrial vehicles and surface and sub surface marine vehicles, etc.
While aspects of the present application disclose the use of a heat blanket in combination with an aluminum heat distributor, it is understood that any heat source may be used that can be controlled to deliver a substantially controllable amount of heat that can be monitored to maintain a temperature of from about 160° F. to about 167° F. to the exterior surface of a transparent substrate. Such heat sources include, but are not limited to, at least one heat lamp, at least one heat gun, an infrared heater, etc., and combinations thereof. Similarly, while aspects of the present application disclose the use of heat guns oriented into a heat box assembly, it is understood that any heat source may be used that can be controlled to deliver a substantially controllable amount of heat that can be monitored to maintain a temperature of from about 160° F. to about 167° F. to the interior surface of a transparent substrate. Such heat sources include, but are not limited to at least one heat lamp, at least one heat gun, an infrared heater, etc., and combinations thereof.
Aspects of the present disclosure describe a second heat source for heating the second side, or interior surface of the transparent substrate that contemplates a heat box that is proximate to, but not in direct contact with, the second side. As such, a necessary gap exists between the second heat source assembly and the second side of the transparent substrate. However, it is understood that further heat sources are contemplated that could be in direct contact with, or proximate to but not in direct contact with, the second side of the transparent substrate, so long as the contact did not interfere with the distortion removal, or otherwise adversely affect the properties of the transparent substrate (e.g. providing a temperature to the second side that exceeded the glass transition temperature, or the melting point of materials incorporated into the transparent substrate, or materials that are positioned adjacent to the transparent substrate including, but not limited to, moldings, fasteners, fittings, etc.
In addition, while aspects of the present application disclose the use of thermocouples to sense and monitor a surface temperature, it is understood that any means for measuring and relaying information regarding a temperature, and/or controlling or regulating a temperature can be used, including, without limitation, a non-contact infrared thermometer, a non-reversible temperature label, a wireless temperature monitoring device, etc., and combinations thereof.
Further, it is understood that the thermocouples and heat sources disclosed herein can be coupled appropriately with, or otherwise be in communication with, necessary controllers and software, hardware, computers and computer programs, etc. to run such software, hardware and controllers, etc. In addition, the assemblies and systems for removing and/or substantially eliminating distortion from transparent substrates in situ may further be controlled to run remotely, and/or automatically, or may be operated manually, as desired.
According to an aspect of the present disclosure, the following protocol was conducted. The inner surface of an aircraft window with distortion was heated to a temperature of 155 to 160° F. for two (2) hours without any window removal or window re-working (in other words the window was heated in situ). The inner and outer surface of the window were cleaned using MS-260 glass cleaner (Miller-Stephenson Chem. Co., Inc., Danbury, Conn.). Scratches or defects other than the distortion were noted. The experimental set-up for the exterior of the window comprised the following steps. Both sides of an aluminum heat distributor were cleaned with MS-260 cleaner, and the heat distributor was placed directly on the outside surface of the window. The heat distributor was secured using Teflon tape (Nitto, Lakewood, N.J.), ensuring that even spacing was maintained between the window nib seal and the heat distributor. Four (4) thermocouples (FLUKE, Everett, Wash.) were placed in contact with and onto the aluminum heat distributor at predetermined locations. Thermocouple wire (AirTech Int'l. Chino, Calif.) ends were in direct contact with the heat distributor, and thermocouple wires were plugged into the heat distributor controller. A breather cloth was placed around the periphery of the heat distributor and secured to the aircraft and the heat distributor using Teflon tape. A composite heat blanket (HeatCon, Seattle, Wash.) was placed onto the heat distributor, while insuring that the heat blanket did not contact the aircraft skin. The heat blanket controller (BriskHeat, Columbus, Ohio) was set to a temperature of 167° F. The breather cloth was placed over the entire composite heat blanket as a heat insulator.
The following steps for the interior of the window set-up were conducted as follows. A heat insulation box frame was positioned in the aircraft cabin insuring that the frame did not contact the inside (i.e. interior) surface of the window. The heat insulation box comprised a supporting frame, with the heat insulation box maintained at a distance from the interior surface of the window of about 0.2″. The heat box was attached to the heat box frame and secured using Teflon tape. A support pedestal was positioned to engage the floor of the cabin at a location beneath the heat box, and extended upward to contact the bottom of the heat box, for the purpose of supporting the heat box. Heat guns (Steinel, Germany) were positioned onto a heat gun pedestal made from a modified light stand (Fostoria), with the nozzle ends of the heat guns positioned to extend into the heat insulation box through holes in the heat insulation box. The holes in the heat box were dimensioned appropriately to accommodate entry of the nozzle ends of the heat guns into the heat box a desired and predetermined distance.
Power was then supplied to the composite heat blanket. A heat ramp rate for the composite heat blanket of about 7° F./minute was set and observed until the thermocouples attached to the composite heat blanket registered a temperature of 167° F. Power was then supplied to the heat guns to maintain an observed temperature on the thermocouple (FLUKE, Everett, Wash.) of 165° F.=/−2° F. Four (4) thermocouples (not shown) were placed in each corner of the heat box and positioned within about 1″ of, but were not in contact with, the interior surface of the interior of the window. Heat levels on the heat guns and on the thermal blanket were maintained for 2.5 hours. Power to the heat blanket and the heat guns was turned off, and the window was allowed to cool to ambient temperature. The above-outlined equipment was removed from the exterior and interior of the window, and the previously observed distortion in the window was absent, as the distortion had been removed.
Aspects of the present disclosure are directed to reducing or substantially removing distortion from a transparent substrate in situ. Transparent substrates include, without limitation, windows and windshields. Contemplated transparent substrates include those made from a single material, as well as those comprising multiple materials, including those comprising layers or laminates. Of particular interest are transparent substrates comprising layers of glass and non-glass, and also transparent substrates comprising no glass. Aspects of the present disclosure include tailoring the distortion-eliminating (i.e. substantially eliminating), or distortion-reducing procedures disclosed herein to meet the demands and limitations of the transparent substrates themselves. That is, by altering the temperatures applied to the two sides of the transparent substrates, as well as the duration, the procedures disclosed herein work effectively to reduce or substantially eliminate distortion from transparent substrates by tailoring the procedures set forth herein to take into account transparent substrate composition, thickness, amount of distortion, presence of laminates or layers, etc.
Aspects of the present disclosure are directed to reducing or substantially eliminating the distortion of transparent substrates, including, without limitation, windows and windshields. For the purposes of the present disclosure, the terms “windshield” and “window” are used interchangeably, and therefore are deemed to have equivalent meaning. Such windows are typically multi-layered, optically transparent structures comprising non-glass layer(s) sandwiched between glass layers. Typical non-glass layers include, without limitation, thermoset and thermoplastic polymers such as polyurethane, polyvinyl butyral-containing resins, polyether-containing films, etc., and combinations thereof.
Non-glass layers often act as so-called “anti-spalling layers; layers that serve to inhibit the release of shattered glass from the transparent structure (e.g. windows and windshields, etc.) While bound to no particular theory, it is believed that this polymeric material that acts as an anti-spalling layer contributes to the force induced distortion that occurs in transparent structures comprising such anti-spalling layers. It is believed that thermoset polymeric materials contained in the transparent windshield structures become stressed due to pressure and/or temperatures that approach or exceed the material's glass transition temperature, leading to distortion of the transparent structure. Such thermoset materials used in the manufacture of windows and windshields are often processed at temperatures approaching or exceeding about 220° F. However, when such materials are exposed to temperatures of about 140° F., noticeable distortion can occur. Such distortion has been referred to as force induced distortion.
Previously, such force induced distortion in transparent structures in aircraft or other vehicles ordinarily resulted in the need to replace such structures from the vehicles. According to aspects of the present disclosure, it is now possible to reduce or substantially eliminate distortion from transparent structures by applying sustained heat at predetermined levels for prescribed durations to both sides of the transparent structures (and to a level that is below the material's glass transition temperature and/or melting point, but above the temperatures at which the distortion was induced). Again, while being bound by no particular theory, it is believe that by observing the spirit of the protocols set forth herein, the materials in the transparent structure “relax” and re-orient their structure to a non-distorted and desirable orientation. Thermoset and, more commonly, thermoplastic components, when subjected to elevated temperatures, can re-orient their structure when in contact with a foreign object to accommodate the shape and form of the object. As set forth herein, and according to aspects of the present disclosure, the desirable re-orientation is achieved by elevating the temperature of both sides of the window above the temperature at which the force-induced distortion was induced.
Such force induced distortion in transparent substrates is visible to the naked eye, and is also known as “rippling”. Distortion can be optically sensed through the use of optical sensors and interferometers. According to aspects of the present disclosure, the processes and protocols reduce distortion to any degree required to return the previously distorted transparent substrate to optimum performance, without removing the substrate from its installed state (e.g. from a building, an aircraft or other vehicle, etc.). That is, the processes described herein can reduce distortion from a 10% to 100% for a transparent substrate, while treating the substrate in situ.
The variations and alternatives of the present disclosure relate to the manufacture and use of components and parts such as, for example, composite component parts of any dimension, including the manufacture and use of components and parts in the fabrication of larger parts and structures. Such devices include, but are not limited to, transparent components and parts designed to be positioned on the exterior or interior of stationary objects including, without limitation, general construction objects, buildings, etc. Further objects include, without limitation, atmospheric and aerospace vehicles and other objects, and structures designed for use in space or other upper-atmosphere environments such as, for example, manned or unmanned vehicles and objects. Contemplated objects include, but are not limited to vehicles such as, for example, manned and unmanned aircraft, spacecraft, rotorcraft, satellites, rockets, missiles, terrestrial vehicles, non-terrestrial vehicles, and even surface and sub-surface water-borne vehicles and objects.
When introducing elements of the present disclosure or exemplary aspects thereof, the articles “a,” “an,” “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising,” “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements. Although this disclosure has been described with respect to specific aspects, the details of these aspects are not to be construed as limitations. While the preferred variations and alternatives of the present disclosure have been illustrated and described, it will be appreciated that various changes and substitutions can be made therein without departing from the spirit and scope of the disclosure.
Aspects of this disclosure were made with Government support under N00019-C-12-0112 awarded by Department of Defense. The government has certain rights in this invention.