The present invention relates to glass compositions and, in particular, to glass compositions for forming fibers.
Large scale commercial production of continuous glass fibers (E-glass and C-glass types) comprises melting batch materials consisting primarily of minerals that are crystalline or substantially crystalline in nature. Conversion of these crystalline raw materials to a glassy state requires significant energy to be applied during the melting process. In view of the significant energy investment accompanying crystalline materials, glassy or amorphous minerals have sometimes been used in the production of glass compositions. A glassy or amorphous structure can reduce the amount of energy consumed in the melting process. Glassy minerals such as basalt and obsidian, for example, have been used as significant portions of feedstock for the production of mineral wool.
An associated disadvantage with some glassy minerals, however, is the high iron content of such minerals. Basalt and obsidian both comprise relatively large amounts of iron, thereby making their resulting melts highly energy absorbing. As a result, use of conventional gas fired furnaces is typically impractical for melt processing of these minerals. Electrical melting can be used to process glassy minerals of high iron content, but this is often a constraint in high volume glass fiber production as compared with conventional gas fired furnace technology. Raw materials used in the production of E-glass and C-glass fibers are generally low in iron, thereby permitting the use of large scale gas fired furnaces.
Perlite (and its expanded form pumice) is a mineral that naturally occurs in the glassy form. Perlite has not been extensively used as a raw material in glass production, partially because of its compositional parameters. The major constituents of perlite are SiO2, Al2O3 and alkali oxide (R2O). SiO2 is typically present in perlite in an amount between about 70 and about 75 weight percent. Al2O3 is typically present in perlite in an amount between about 12 and about 15 weight percent. Alkali oxides are typically present in perlite in an amount between about 3 and about 9 weight percent. These parameters conflict with the compositional requirements of several widely used glass compositions, including, for example, those of E-glass and C-glass.
E-glass compositions, for example, are well-suited for forming glass fibers. As a result, the majority of glass fibers used in reinforcement applications, such as polymeric reinforcement applications, are formed from E-glass compositions. E-glass compositions generally limit the amount alkali oxides to no more than 2 percent. The high alkali oxide content of perlite is inconsistent with this limitation and renders perlite largely unsuitable for use in batch compositions for the production of E-glass compositions.
Moreover, C-glass compositions have also been used to form fibers resistant to corrosion in acidic environments. In order to resist acidic corrosion, C-glass compositions comprise a high SiO2 content and a low Al2O3 content (<8 wt. %). The high Al2O3 content of perlite generally precludes use of perlite in batch compositions for the production of C-glass compositions.
In one aspect, the present invention provides glass compositions formed from batch compositions comprising significant amounts of one or more glassy minerals, including perlite and/or pumice. In another aspect, the present invention provides glass fibers formed from glass compositions described herein.
In one embodiment, the present invention provides a glass composition formed from a batch composition comprising at least 10 weight percent of a glassy mineral, at least 5 weight percent of a sodium source, wherein the glassy mineral comprises a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some such embodiments, the batch composition comprises at least 25 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some further such embodiments, the batch composition comprises at least 40 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some embodiments, the glassy mineral comprising a combination of SiO2 and Al2O3 is perlite, pumice or mixtures thereof.
Moreover, in some embodiments, the batch comprises at least 10 weight percent of a sodium source. A sodium source, in some embodiments, comprises sodium carbonate (soda). In some embodiments, the batch comprises at least 10 weight percent of a source of both silicon and aluminum. In some such embodiments, the source of both silicon and aluminum is an aluminum-containing silicate mineral, such kaolinite, dickite, halloysite, nacrite, montmorillonite, or alkali metal aluminosilicates. In some embodiments, the batch comprises at least 10 weight percent of a source of silicon. In some embodiments, the batch comprises at least 10 weight percent of a source of aluminum.
In another embodiment, the present invention provides a glass composition comprising 53-64 weight percent SiO2, 8-12 weight percent Al2O3, 8.5-18 weight percent alkali oxide (R2O) component and a metal oxide (RO) component, wherein the metal oxide component is present in an amount to provide a mass ratio of R2O/RO ranging from about 0.15 to about 1.5. In some such embodiments, the glass composition includes 10-12 weight percent Al2O3.
In some embodiments, a R2O component comprises Na2O, K2O or Li2O or mixtures thereof. In some embodiments, a glass composition of the present invention comprises Na2O in an amount ranging from 6.5 weight percent to about 16 weight percent. A glass composition, in some embodiments, comprises K2O in an amount ranging from 0.5 weight percent to 4 weight percent, and 2 weight percent to 4 weight percent in further embodiments. In some embodiments, a glass composition comprises Li2O in an amount up to 2 weight percent.
In some embodiments, a RO component comprises MgO, CaO, SrO, BaO, or ZnO or mixtures thereof. A RO component, in some embodiments, is present in a glass composition of the present invention in an amount ranging from 7 weight percent to 31 weight percent. In one embodiment, a glass composition comprises MgO in an amount up to about 5 weight percent. A glass composition, in some embodiments, comprises CaO in an amount ranging from 7 weight percent to 26 weight percent. In some embodiments, a glass composition comprises ZnO in an amount up to 3 weight percent. Glass compositions of the present invention, in some embodiments, comprise metal oxides in addition to RO including, but not limited to, ZrO2, TiO2, MnO2 or La2O3 or mixtures thereof.
In another embodiment, the present invention provides a glass composition comprising 56-63 weight percent SiO2, 9-12 weight percent Al2O3, 12-17 weight percent RO (CaO+MgO), 12-14 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass composition comprising 60-64 weight percent SiO2, 9-12 weight percent Al2O3, 7-15 weight percent RO (CaO+MgO), 13-15.5 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass composition comprising 55-63 weight percent SiO2, 9-14 weight percent Al2O3, 11-16.5 weight percent RO (CaO+MgO), 14-17 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In some embodiments, glass compositions of the present invention have an Fe2O3 content of less than 1 weight percent. Glass compositions, in other embodiments, can comprise less than 0.7 weight percent Fe2O3.
Glass compositions, according to some embodiments of the present invention are fiberizable. In some embodiments, glass compositions of the present invention have a forming temperature (TF) ranging from 1120° C. to about 1300° C. As used herein, the term “forming temperature” means the temperature at which the glass composition has a viscosity of 1000 poise (or “log 3 temperature”). In some embodiments, glass compositions of the present invention are fiberizable at the forming temperature.
Moreover, in some embodiments, glass compositions of the present invention have a liquidus temperature (TL) ranging from about 1020° C. to about 1240° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention ranges from about 45° C. to about 165° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention is at least 65° C.
In some embodiments, glass compositions of the present invention have a molten density at the forming temperature ranging from 2.35 g/cm3 to 2.40 g/cm3. In some embodiments, glass composition of the present invention have molten density ranging from 2.36 g/cm3 to 2.38 g/cm3.
Glass compositions of the present invention, in some embodiments, have a molten surface tension at the forming temperature ranging from about 390 E−3 N/m to 400 E−3 N/m.
As provided herein, glass fibers can be formed from some embodiments of the glass compositions of the present invention. In some embodiments, fibers formed from glass compositions of the present invention have a modulus (E) ranging from about 53 GPa to about 65 GPa. Moreover, in some embodiments, fibers formed from glass compositions of the present invention have a specific strength ranging from 1.30-1.35 E5 m.
Fibers formed from glass compositions of the present invention, in some embodiments, also demonstrate acidic and alkaline corrosion resistance. In one embodiment, for example, a fiber formed from a glass composition of the present invention has a weight loss (wt. %) ranging from about 0.55 to about 0.60 when exposed to 1N H2SO4 (pH 0) at 100° C. for one hour. In another embodiment, a fiber formed from a glass composition of the present invention has a weight loss (wt. %) ranging from about 0.25 to 0.30 when exposed to 0.1N NaOH (pH 12) at 100° C. for one hour.
Glass fibers formed from glass compositions of the present invention can be used in various reinforcement applications. In some embodiments, glass fibers of the present invention are used in the reinforcement of polymers including thermoplastics and thermosets. In some embodiments, glass fibers formed from glass compositions of the present invention are used in the reinforcement of building materials including, but not limited to, cement and roofing systems such as shingles.
In another aspect, the present invention provides methods of making glass compositions from batch compositions comprising significant amounts of one or more glassy minerals, including perlite and/or pumice.
In one embodiment, a method of making a glass composition of the present invention comprises providing a batch composition comprising at least 10 weight percent of a glassy mineral and at least 5 weight percent of a sodium source, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent and heating the batch composition to a temperature sufficient to form the glass composition. In some embodiments, the batch comprises at least 10 weight percent of an additional source of both silicon and aluminum. In some embodiments, the batch comprises at least 10 weight percent of an additional source of silicon. In some embodiments, the batch comprises at least 10 weight percent of an additional source of aluminum. In some embodiments, the batch composition is heated to a temperature of about 1400° C. to about 1450° C.
These and other embodiments are presented in greater detail in the detailed description which follows.
Unless indicated to the contrary, the numerical parameters set forth in the following specification are approximations that can vary depending upon the desired properties sought to be obtained by the present invention. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all subranges subsumed therein. For example, a stated range of “1 to 10” should be considered to include any and all subranges between (and inclusive of) the minimum value of 1 and the maximum value of 10; that is, all subranges beginning with a minimum value of 1 or more, e.g. 1 to 6.1, and ending with a maximum value of 10 or less, e.g., 5.5 to 10. Additionally, any reference referred to as being “incorporated herein” is to be understood as being incorporated in its entirety.
It is further noted that, as used in this specification, the singular forms “a,” “an,” and “the” include plural referents unless expressly and unequivocally limited to one referent.
Certain embodiments of the present invention can employ the various thermodynamic and processing advantages offered by glassy minerals to provide glass compositions having desirable properties. In one aspect, the present invention provides glass compositions formed from batch compositions comprising significant amounts of one or more glassy minerals, including perlite and/or pumice. The glass compositions, in some embodiments, can be fiberizable glass compositions. In some embodiments, glass fibers formed from glass compositions of the present invention can demonstrate advantageous properties including, but not limited to, mechanical and corrosion resistant properties equaling or exceeding glass fibers formed from previous compositions, such as E-glass and C-glass compositions.
Various embodiments of the present invention provide glass compositions, including, without limitation, fiberizable glass compositions. In one embodiment, the present invention provides a glass composition formed from a batch composition comprising at least 10 weight percent of a glassy mineral and at least 5 weight percent of a sodium source, wherein the glassy mineral comprises a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some embodiments, the batch composition comprises at least 25 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In another embodiment, the batch composition comprises at least 40 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent.
In some embodiments, a glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent is perlite, pumice or mixtures thereof.
Moreover, in some embodiments, the batch composition comprises at least 10 weight percent of a sodium source. In another embodiment, the batch composition comprises at least 12 weight percent of a sodium source. A suitable sodium source for use in batch compositions of the present invention, in some embodiments, comprises sodium carbonate (soda).
In some embodiments, the batch comprises at least 10 weight percent of an additional source of both silicon and aluminum. In some such embodiments, the source of both silicon and aluminum is an aluminum-containing silicate mineral, such kaolinite, dickite, halloysite, nacrite, montmorillonite, or alkali metal aluminosilicates. In some embodiments, the batch comprises at least 10 weight percent of an additional source of silicon. In some such embodiments, the source of silicon can be a silicon-containing mineral, such as silica. In some embodiments, the batch comprises at least 10 weight percent of an additional source of aluminum. In such embodiments, the source of aluminum can be an aluminum-containing mineral, such as corundum.
In another embodiment, the present invention provides a glass composition comprising 53-64 weight percent SiO2, 8-12 weight percent Al2O3, 8.5-18 weight percent alkali oxide (R2O) component and a metal oxide (RO) component, wherein the metal oxide component is present in an amount to provide a mass ratio of R2O/RO ranging from about 0.15 to about 1.5.
In some embodiments, a R2O component is not limited to a single compound but can comprise several compounds. In some embodiments, a R2O component comprises Na2O, K2O or Li2O or mixtures thereof. Moreover, in some embodiments and without limitation, a R2O component can mean Na2O only, K2O only, Li2O only, a combination of Na2O and K2O, a combination of K2O and Li2O, a combination of Na2O and Li2O, or a combination of Na2O, K2O and Li2O.
In some embodiments, a glass composition of the present invention comprises Na2O in an amount ranging from 6.5 weight percent to about 16 weight percent. In another embodiment, a glass composition comprises Na2O in an amount ranging from 9 weight percent to 13 weight percent. In some embodiments, a glass composition comprises Na2O in an amount ranging from 10 weight percent to 12.5 weight percent.
In some embodiments, a glass composition of the present invention comprises K2O in an amount ranging from 0.5 weight percent to 4 weight percent. A glass composition of the present invention, in some embodiments, comprises K2O in an amount ranging from 2 weight percent to 4 weight percent. In some embodiments, a glass composition comprises K2O in an amount ranging from 2.5 weight percent to 3.5 weight percent.
In some embodiments, a glass composition of the present invention comprises Li2O in an amount up to 2 weight percent. A glass composition, in another embodiment, comprises Li2O in an amount ranging from 0.5 weight percent to 1.5 weight percent.
In some embodiments, a RO component comprises MgO, CaO, SrO, BaO or ZnO or mixtures thereof. In some embodiments, a RO component can comprise MgO only, CaO only, SrO only, BaO only or ZnO only. In some embodiments, a RO component can comprise any combination of two or more metal oxides of MgO, CaO, SrO, BaO and ZnO. A RO component, in some embodiments, is present in a glass composition of the present invention in an amount ranging from 7 weight percent to 31 weight percent.
In one embodiment, a glass composition of the present invention comprises MgO in an amount up to 5 weight percent. A glass composition, in another embodiment, comprises MgO in an amount ranging from 1 weight percent to 4 weight percent. In some embodiments, a glass composition comprises MgO in an amount ranging from 2 weight percent to 3 weight percent.
In some embodiments, a glass composition of the present invention comprises CaO in an amount ranging from 7 weight percent to 26 weight percent. A glass composition, in another embodiment, comprises CaO in an amount ranging from 8 weight percent to 20 weight percent. In some embodiments, a glass composition comprises CaO in an amount ranging from 10 weight percent to 14 weight percent.
In some embodiments, a glass composition comprises ZnO in an amount up to 3 weight percent.
Glass compositions of the present invention, in some embodiments, comprise metal oxides in addition to RO including, but not limited to ZrO2, TiO2, MnO2 or La2O3 or mixtures thereof. In some embodiments, a glass composition can comprise ZrO2 in an amount up to 3 weight percent, TiO2 in an amount up to 3 weight percent, MnO2 in an amount up to 3 weight percent and/or La2O3 in an amount up to 3 weight percent.
In another embodiment, the present invention provides a glass composition comprising 56-63 weight percent SiO2, 9-12 weight percent Al2O3, 12-17 weight percent RO (CaO+MgO), 12-14 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass composition comprising 60-64 weight percent SiO2, 9-12 weight percent Al2O3, 7-15 weight percent RO (CaO+MgO), 13-15.5 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass composition comprising 55-63 weight percent SiO2, 9-14 weight percent Al2O3, 11-16.5 weight percent RO (CaO+MgO), 14-17 weight percent R2O (Na2O+K2O), 0-2 weight percent
Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In some embodiments, glass compositions of the present invention have an Fe2O3 content of less than 1 weight percent. Glass compositions, in other embodiments, can comprise less than 0.7 weight percent Fe2O3.
Glass compositions of the present invention, in some embodiments, have a forming temperature (TF)ranging from about 1120° C. to about 1300° C. In another embodiment, glass compositions of the present invention have a forming temperature ranging from about 1150° C. to about 1250° C. In some embodiments, glass compositions have a forming temperature ranging from about 1200° C. to about 1225° C.
Glass compositions of the present invention, in some embodiments, have a liquidus temperature ranging from about 1020° C. to about 1240° C. In another embodiment, glass compositions of the present invention have a liquidus temperature ranging from about 1070° C. to about 1200° C. In some embodiments, glass compositions of the present invention have a liquidus temperature ranging from about 1110° C. to about 1140° C.
In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention ranges from about 45° C. to about 165° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention is at least 65° C.
In some embodiments, glass compositions of the present invention have a molten density at the forming temperature ranging from 2.35 g/cm3 to 2.40 g/cm3. In some embodiments, glass compositions of the present invention have molten density ranging from 2.36 g/cm3 to 2.38 g/cm3. As discussed further herein, in some embodiments, molten densities of some glass compositions of the present invention are 5% to 7% lower than the molten densities of some E-glass compositions. As a result, glass fibers formed from some glass compositions of the present invention are lighter per unit volume in comparison to some E-glass fibers. Lighter glass fibers can be advantageous in many applications, particularly material reinforcement applications, such as polymeric reinforcement applications, where weight savings are often highly desirable. Moreover, as a result of lower densities, glass fibers formed from some glass compositions of the present invention can have larger diameters in comparison to some E-glass fibers of the same weight, thereby providing enhanced mechanical properties.
Additionally, glass compositions of the present invention, in some embodiments, have a molten surface tension at the forming temperature ranging from about 390 E−3 N/m to 400 E−3 N/m.
As provided herein, glass compositions of the present invention can be produced from batch compositions comprising a significant amount of one or more glassy minerals, including perlite and/or pumice. In being produced from batch compositions comprising a significant amount of glassy minerals, glass compositions of the present invention can realize sizable energy savings in some embodiments. As discussed further herein, in some embodiments, production of a melt of a glass composition of the present invention requires up to 33% less energy in comparison to that required to produce a melt of some E-glass compositions.
Glass compositions of the present invention can be produced by several methods. In one embodiment, a method of producing a glass composition comprises providing a batch composition comprising at least 10 weight percent of a glassy mineral and at least 5 weight percent of a sodium source, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent and heating the batch composition to a temperature sufficient to form a melt of the glass composition. In some embodiments, the batch composition is heated to a temperature of about 1400° C. to about 1450° C. In some embodiments, the batch comprises at least 10 weight percent of an additional source of both silicon and aluminum. In some such embodiments, the source of both silicon and aluminum is an aluminum-containing silicate mineral, such kaolinite, dickite, halloysite, nacrite, montmorillonite, or alkali metal aluminosilicates. In some embodiments, the batch comprises at least 10 weight percent of an additional source of silicon. In some embodiments, the batch comprises at least 10 weight percent of an additional source of aluminum.
In some embodiments, the batch composition comprises at least 25 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In another embodiment, the batch composition comprises at least 40 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent.
In some embodiments, a glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent is perlite, pumice or mixtures thereof. Perlite and/or pumice used in the production of glass compositions of the present invention, in some embodiments, is provided in particulate or powder form. In some embodiments, additional energy savings can be realized by using perlite and/or pumice compositions having fine particle size as opposed to coarser particle sizes.
Moreover, in some embodiments, batch compositions of the present invention comprise at least 10 weight percent of a sodium source. In some embodiments, batch compositions comprise at least 12 weight percent of a sodium source. A suitable sodium source for use in batch compositions of the present invention, in some embodiments, comprises sodium carbonate (soda).
In some embodiments, batch compositions used to produce glass compositions of the present invention further comprise other minerals including, but not limited to, limestone, dolomite or mixtures thereof. In one embodiment, for example, a batch composition further comprises up to 17 weight percent limestone. In another embodiment, a batch composition further comprises up to 13 weight percent dolomite.
As provided herein, glass fibers can be formed from any of the glass compositions of the present invention. Glass fibers according to the various embodiments of the present invention can be formed using any process known in the art for forming glass fibers, and more desirably, any process known in the art for forming essentially continuous glass fibers. For example, although not limiting herein, the glass fibers according to non-limiting embodiments of the present invention can be formed using direct-melt or indirect-melt fiber forming methods. These methods are well known in the art and further discussion thereof is not believed to be necessary in view of the present disclosure. See, e.g., K. L. Loewenstein, The Manufacturing Technology of Continuous Glass Fibers, 3rd Ed., Elsevier, N.Y., 1993 at pages 47-48 and 117-234.
In one embodiment, the present invention provides a glass fiber comprising a glass composition formed from a batch composition comprising at least 10 weight percent of a glassy mineral and at least 5 weight percent of a sodium source, wherein the glassy mineral comprises a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some embodiments, the batch composition comprises at least 25 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In another embodiment, the batch composition comprises at least 40 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some embodiments, the batch composition comprises at least 10 weight percent of a source of both silicon and aluminum. In some embodiments, the batch comprises at least 10 weight percent of a source of silicon. In some embodiments, the batch comprises at least 10 weight percent of a source of aluminum.
In another embodiment, the present invention provides a glass fiber comprising 53-64 weight percent SiO2, 8-12 weight percent Al2O3, 8.5-18 weight percent alkali oxide (R2O) component and a metal oxide (RO) component, wherein the metal oxide component is present in an amount to provide a mass ratio of R2O/RO ranging from about 0.15 to about 1.5. In some such embodiments, the glass composition includes 10-12 weight percent Al2O3.
In another embodiment, the present invention provides a glass fiber comprising 56-63 weight percent SiO2, 9-12 weight percent Al2O3, 12-17 weight percent RO (CaO +
MgO), 12-14 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass fiber comprising 60-64 weight percent SiO2, 9-12 weight percent Al2O3, 7-15 weight percent RO (CaO +
MgO), 13-15.5 weight percent R2O (Na2O+K2O)), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a glass fiber comprising 55-63 weight percent SiO2, 9-14 weight percent Al2O3, 11-16.5 weight percent RO (CaO+MgO), 14-17 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In some embodiments, fibers formed from glass compositions of the present invention have a modulus (E) ranging from about 53.0 GPa to about 65.0 GPa. In another embodiment, fibers formed form glass compositions of the present invention have a modulus (E) ranging from about 56 GPa to about 62 GPa. Moreover, in some embodiments, fibers formed from glass compositions of the present invention have a specific strength ranging from 1.30-1.35 E5 m.
Fibers formed from glass compositions of the present invention, in some embodiments, also demonstrate acidic and alkaline corrosion resistance. In one embodiment, for example, a glass fiber formed from a glass composition of the present invention has a weight loss (wt. %) ranging from 0.55 to 0.60 when exposed to 1N H2SO4 (pH 0) at 100° C. for one hour. In another embodiment, a glass fiber formed from a glass composition of the present invention has a weight loss (wt. %) ranging from 0.60 to 1.70 when exposed to 1N H2SO4 (pH 0) at 100° C. for one hour.
In another embodiment, a fiber formed from a glass composition of the present invention has a weight loss (wt. %) ranging from about 0.25 to about 0.30 when exposed to 0.1N NaOH (pH 12) at 100° C. for one hour. A fiber formed from a glass composition of the present invention, in some embodiments, has a weight loss (wt. %) ranging from 0.35 to 0.85 when exposed to 0.1N NaOH (pH 12) at 100° C. for one hour.
Although not limiting herein, glass fibers according to some embodiments of the present invention can be useful in structural reinforcement applications. In some embodiments, glass fibers of the present invention are used in the reinforcement of polymers including thermoplastics and thermosets. In some embodiments, glass fibers formed from glass compositions of the present invention are used in the reinforcement of building materials including, but not limited to, cement and roofing systems such as shingles.
In one embodiment, the present invention provides a polymeric composite comprising a polymeric material and at least one glass fiber in the polymeric material, the at least one glass fiber comprising a glass composition a formed from a batch composition comprising at least 10 weight percent of a glassy mineral and at least 5 weight percent of a sodium source, wherein the glassy mineral comprises a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In some embodiments, the batch composition comprises at least 25 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent. In another embodiment, the batch composition comprises at least 40 weight percent of a glassy mineral, the glassy mineral comprising a combination of SiO2 and Al2O3 in an amount of at least 80 weight percent.
In another embodiment, the present invention provides a polymeric composite comprising a polymeric material and at least one glass fiber in the polymeric material, the at least one glass fiber comprising 53-64 weight percent SiO2, 8-12 weight percent Al2O3, 8.5-18 weight percent alkali oxide (R2O) component and a metal oxide (RO) component, wherein the metal oxide component is present in an amount to provide a mass ratio of R2O/RO ranging from about 0.15 to about 1.5. In some such embodiments, the glass composition includes 10-12 weight percent Al2O3.
In another embodiment, the present invention provides a polymeric composite comprising a polymeric material and at least one glass fiber in the polymeric material, the at least one glass fiber comprising 56-63 weight percent SiO2, 9-12 weight percent Al2O3, 12-17 weight percent RO (CaO+MgO), 12-14 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a polymeric composite comprising a polymeric material and at least one glass fiber in the polymeric material, the at least one glass fiber comprising 60-64 weight percent SiO2, 9-12 weight percent Al2O3, 7-15 weight percent RO (CaO+MgO), 13-15.5 weight percent R2O (Na2O+K2O)), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
In another embodiment, the present invention provides a polymeric composite comprising a polymeric material and at least one glass fiber in the polymeric material, the at least one glass fiber comprising 55-63 weight percent SiO2, 9-14 weight percent Al2O3, 11-16.5 weight percent RO (CaO+MgO), 14-17 weight percent R2O (Na2O+K2O), 0-2 weight percent Li2O, 0-3 weight percent ZnO, 0-3 weight percent ZrO2, 0-3 weight percent MnO2 and 0-3 weight percent La2O3.
Polymeric composites according to the various embodiments of the present invention can be made by any method known in the art for making polymeric composites.
For example, in one embodiment, polymeric composites according to the present invention can be made by impregnating woven fabrics or non-woven fabrics or mats of glass fibers with a polymeric material and then curing the polymeric material. In another embodiment, continuous glass fibers and/or chopped glass fibers comprising glass compositions of the present invention can be disposed in the polymeric material. Depending on the identity of the polymeric material, the polymeric material can be cured subsequent to receiving the continuous or chopped glass fibers.
Various non-limiting embodiments of the present invention will now be illustrated in the following, non-limiting examples. Examples 1 through 6 of glass compositions of the present invention provided in Table I were prepared by providing mixtures of ingredients covering 65-72 weight percent perlite, 0-22 weight percent dolomite, 6-35 weight percent limestone and 0-8 weight percent soda. The specific amounts of perlite, dolomite, limestone and/or soda used to produce Examples 1 through 6 were determined by reference to the compositional parameters of each mineral in relation to the desired compositional parameters of each glass composition. Mixtures of the minerals were subsequently heated to a temperature of about 1400° C. to obtain molten glass compositions. The molten glass compositions were cooled to provide glass compositions of Examples 1 through 6.
Examples 7 through 13 of glass compositions of the present invention provided in Table II were prepared by providing mixtures of ingredients covering 69-71 weight percent perlite, 6-20 weight percent limestone and 7-10 weight percent soda. The specific amounts of perlite, limestone and soda used to produce Examples 7 through 13 were determined by reference to the compositional parameters of each mineral in relation to the desired compositional parameters of each glass composition. Mixtures of the minerals were subsequently heated to a temperature of about 1400° C. to obtain molten glass compositions. The molten glass compositions were cooled to provide glass compositions of Examples 7 through 13.
Examples 14 through 19 of glass compositions of the present invention provided in Table III were prepared by providing mixtures of ingredients covering 69-72 weight percent perlite, 0-13 weight percent dolomite, 3-17 weight percent limestone and 7-10 weight percent soda. The specific amounts of perlite, limestone, soda and/or dolomite used to produce Examples 14 through 19 were determined by reference to the compositional parameters of each mineral in relation to the desired compositional parameters of each glass composition. Mixtures of the minerals were subsequently heated to a temperature of about 1400° C. to obtain molten glass compositions. The molten glass compositions were cooled to provide glass compositions of Examples 14 through 19.
#1 wt % Li2O replaced 1 wt % Na2O; Sb2O3 used in refining removed
Examples 20 through 37 of glass compositions of the invention provided in Table IV were prepared by providing mixtures of ingredients covering 68-73 weight percent perlite, 0-13 weight percent dolomite, 4-16 weight percent limestone and 12-17 weight percent soda. The specific amounts of perlite, limestone, soda and/or dolomite used to produce Examples 20 through 37 were determined by reference to the compositional parameters of each mineral in relation to the desired compositional parameters of each glass composition. Mixtures of the minerals were subsequently heated to a temperature of about 1400° C. to obtain molten glass compositions. The molten glass compositions were cooled to provide glass compositions of Examples 20 through 37.
The glass composition of Example 38 provided in Table V was prepared in accordance with the glass composition of Example 12 above, except 1 wt % Li2O was used to replace 1 wt % Na2O and any Sb2O3 used during refining was removed. The glass composition of Example 39 in Table V was prepared in accordance with the glass composition of Example 12 above, except ZnO was used to replace 1 wt % Na2O and 1 wt % CaO and any Sb2O3 used during refining was removed.
Examples 40 through 71 of glass compositions of the present invention provided in Table VI were prepared in accordance with the glass composition of Example 12 above, except the glass compositions were designed to include various combinations of Li2O, La2O3, MnO2, TiO2, ZnO and ZrO2. Various amounts of Li2CO3, La2O3, MnO2, TiO2, ZnO and ZrO2 were incorporated into the batch composition of Example 12 to produce Examples 39-70. Moreover, each of the glass compositions of Examples 39-70 also included 0.09 wt % SO3, 0.27-0.28 wt % F and 0.53-0.55 wt % Fe2O3.
Examples 72 through 74 of glass compositions of the present invention provided in Table VII may be prepared by providing mixtures of ingredients covering 11-41 weight percent perlite, 0-55 weight percent dolomite, 12-17 weight percent limestone, 0-30 weight percent alkali aluminosilicate mineral, 34-56 weight percent silica, 0-19 weight percent clay (kaolinite), and 1-3 weight percent rouge. The specific amounts of perlite, dolomite, alkali aluminosilicate mineral, silica, clay and/or rouge used to produce Examples 72 through 74 were determined by reference to the compositional parameters of each mineral in relation to the desired compositional parameters of each glass composition. Mixtures of the minerals are heated to a temperature of about 1400° C. to obtain molten glass compositions. The molten glass compositions are cooled to provide glass compositions of Examples 72 through 74.
The melt properties of several glass compositions of Examples 1 through 71 were investigated. Investigation of the melt properties of glass compositions of the present invention assisted in the determination of how various compositional parameters affect processing considerations including forming temperatures (TF) and liquidus (TL) temperatures of the glass compositions.
The measurement of melt viscosity for determining forming temperatures of various glass compositions of the present invention was done by the counter-balance method over the viscosity range of 102-105 Poise. The apparatus used to execute the method was calibrated using NIST standard glass.
The apparatus (1) for measuring melt viscosity comprised a platinum ball (2) with a diameter of 16 mm. The platinum ball (2) was hung on a thin platinum wire (6) with the help of a special bracket/holder (11) attached to the right scale of the analytical balance. Initially, the first the end of the platinum wire (6) was attached to the bracket/holder at point A. After warming the furnace (9), the platinum ball was placed in the sample melt inside the crucible (3) and the first end of the wire was attached to the bracket/holder at point B to locate the platinum ball (2) in the center of the melt. The distance between the platinum ball (2) and the walls of the crucible (3) was 13-15 mm. If the distance were smaller, it would affect the precision of the measurement.
The movement of the platinum ball (3) in the melt was performed by changing the weight of the rider. The speed of the movement of the ball in the melt was defined in relative numbers of the balance indicator shift that was observed on the balance scale. When the balance indicator moved 100 points to both sides from zero position, the ball in the melt shifted 1.7 mm from the central position up and down. The sensitivity of the balance was 10 mg per 100 points. A Pt/PtRh thermocouple was placed in the furnace next to the crucible (3) and provided automatic temperature control of the furnace. The hot end of another thermocouple (5) was inside the crucible (10) filled with Al2O3 powder. This thermocouple was connected with the potentiometer to control the furnace temperature at the set point. The temperature control had a precision ±1.5° C.
During the testing, the platinum ball (2) moved from a marked upper position in the melt to a lower marked position under its gravity, the time of which was recorded using a stopwatch with the precision within 0.1 second. The time of the balance scale shift to 20-60 scale divisions was measured depending on the viscosity of the melt. The speed of the platinum ball (2) movement (per scale division/seconds) was taken as an average value of six measurements.
Using the velocity (V)-weight (G) data, a plot of V-G was constructed for each glass composition under investigation, all of which showed straight lines passing through the point of origin of the V-G coordinates. The slope k of each line was correlated with melt viscosity in a form of:
log η=a*log (tgk)+b
where a (1.09) and b (0.87) were constants determined from cell calibration using a NIST standard glass (710A). The relative error in defining viscosity was within 3% over the viscosity range, 2.5<log η<3.5, and within 4-6% over the range, log η<2.5 and log η>3.5.
The measurement of glass composition liquidus temperature (TL) was conducted in a tube type gradient furnace with maximum temperature 1250° C. The furnace chamber had a dimension of 480 mm in length and 50 mm in diameter. The geometry and dimension of the furnace were close to those recommended by the ASTM C829-81.
Table VIII summarizes measured liquidus temperature (TL) and reference temperature of forming (TF) defined by melt viscosity of 1000 Poise for glass compositions of Examples 1-22. Glass compositions of Examples 1-6 demonstrated liquidus temperatures greater than 1240° C., the upper limit of the gradient temperature furnace setting. As a result, no viscosity measurements were made for these compositions for a determination of forming temperature. Moreover, several glass compositions displayed desirable melt properties by having lower liquidus and forming temperatures while maintaining a difference in liquidus temperature and forming temperature of at least 65° C. Examples 18, 20 and 21 each provided a forming temperature under 1222° C. while maintaining a difference in liquidus and forming temperature of at least 75° C.
Table IX summarizes measured liquidus temperature (TL) and the forming (TF) temperature for glass compositions of Examples 40 through 71 as a function of weight percent of Li2O in the glass compositions. As provided in Table IX, Li2O plays a significant role in lowering the liquidus and forming temperatures of glass compositions of the present invention with minimum reductions in forming and liquidus temperatures being 30° C. and 43° C. respectively.
Additionally, glass compositions of the present invention formed from batch compositions comprising perlite and/or pumice, in some embodiments, require less energy for converting the batch composition to a glass melt composition.
Fibers formed from glass compositions of the present invention were made in a laboratory using a single tip bushing set up. To compare with commercial glass fiber corrosion resistance under the same testing conditions, AR-, C-, ECR- and E-glass fibers were also made using the same method using cullet.
Glass fiber resistance to corrosion was evaluated in terms of the relative sample percent weight loss after leaching test. Testing was administered by boiling a fiber strand at 100° C. for one hour in sulfuric acid or sodium hydroxide solutions under various pH conditions. All of the tests were performed by keeping ratio of solution volume to the sample mass or volume (5,000 m2) constant. 50 ml of the solution and of 1.375 gram (filament diameter −22 μm) were used for each test. Triplicate samples were tested to determine average sample weight losses. The results of the acid and alkaline corrosion resistance testing are provided in Table X.
1 The average determined from three individual tests and standard deviation is not greater than 0.1%.
2C-glass (wt %): 66 SiO2, 5.5 Al2O3, 10.4 CaO, 3.6 MgO, 0.3 Fe2O3, 0.2 K2O, 12.5 Na2O, 0.5F and 0.2 SO3.
3AR-glass (wt %): 57 SiO2, 3.2 Al2O3, 15 ZrO2, 4.2 CaO, 0.1 MgO, 0.1 Fe2O3, 0.1 K2O, 12 Na2O, 0.5 F and 0.23 SO3.
Tensile strengths of fibers formed from the glass composition of Example 37 of the present invention were measured by drawing 10-um diameter fibers from single tip bushing in laboratory. The fibers were subsequently tested by applying tensile force to the fibers from both ends within the same day of fiber forming.
Fiber sonic tensile modulus was measured by drawing 30-um diameter fibers comprising the glass composition of Example 37 of the present invention from a single tip bushing in laboratory. The fibers were subsequently tested by applying dead weight from both ends to measure velocity of sound traveling inside the fiber. Fiber density was also measured. The elastic modulus was calculated using E=ρC2 where E, ρ, and C are modulus, density, and sound velocity, respectively. Fibers of two sets were formed at two different temperatures, the first set at 1000 Poise melt viscosity (Low T Forming) and the second set at 50° C. higher than the first set. (High T Forming) Table XI summarizes the statistical analysis of the fiber modulus with an average of about 56.8 GPa and 61.5 GPa for low and high forming temperature cases, respectively.
Desirable characteristics, which can be exhibited by embodiments of the present invention, can include, but are not limited to, the provision of new glass compositions that utilize glassy minerals; the provision of new glass compositions that utilize perlite; the provision of batch compositions requiring less energy to form melts of glass compositions; the provision of new glass compositions demonstrating significant differences in liquidus and forming temperatures; the provision of glass fibers having reduced weights without a concomitant reduction in mechanical properties; and the provision of glass fibers demonstrating desirable acid and alkaline corrosion resistance properties.
It is to be understood that the present description illustrates aspects of the invention relevant to a clear understanding of the invention. Certain aspects of the invention that would be apparent to those of ordinary skill in the art and that, therefore, would not facilitate a better understanding of the invention have not been presented in order to simplify the present description. Although the present invention has been described in connection with certain embodiments, the present invention is not limited to the particular embodiments disclosed, but is intended to cover modifications that are within the spirit and scope of the invention, as defined by the appended claims.
The present application is a continuation-in-part application of U.S. patent application Ser. No. 12/534,490, filed Aug. 3, 2009, which is incorporated by reference as though fully set forth herein.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13365590 | Feb 2012 | US |
| Child | 15408946 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12534490 | Aug 2009 | US |
| Child | 13365590 | US |