The present invention generally relates to fabricating optical integrated circuits that exhibit reduced polarization dependent loss. In particular, the present invention relates to reducing stress within optical integrated circuits as a means to reduce polarization dependent loss.
As optical networks increasingly carry burgeoning Internet traffic, the need for advanced and efficient optical components rises. Optical communication systems permit the transmission of large quantities of information. Improved optical integrated circuits (OICs) are particularly needed. OICs come in many forms such as 1×N optical splitters, optical switches, wavelength division multiplexers (WDMs), demultiplexers, optical add/drop multiplexers (OADMs), and the like. Optical circuits allow branching, coupling, switching, separating, multiplexing and demultiplexing of optical signals without intermediate transformation between optical and electrical media.
Such optical circuits include planar lightwave circuits (PLCs) having optical waveguides on flat substrates, which can be used for routing optical signals from one of a number of input optical fibers to any one of a number of output optical fibers or optical circuitry. PLCs make it possible to achieve higher densities, greater production volume and more diverse functions than are available with fiber components through employment of manufacturing techniques typically associated with the semiconductor industry. For instance, PLCs contain optical paths known as waveguides formed on a silicon wafer substrate using lithographic processing, wherein the waveguides are made from transmissive media including lithium niobate (LiNbO3) or other inorganic crystals, silica, glass, thermo-optic polymers, electro-optic polymers, and semiconductors such as indium phosphide (InP), which have a higher index of refraction than the chip substrate or the outlying cladding layers in order to guide light along the optical path. By using advanced photolithographic and other processes, PLCs are fashioned to integrate multiple components and functionalities into a single optical chip.
One important application of PLCs and OICs generally involves wavelength-division multiplexing (WDM) including dense wavelength-division multiplexing (DWDM). DWDM allows optical signals of different wavelengths, each carrying separate information, to be transmitted via a single optical channel or fiber in an optical network. In order to provide advanced multiplexing and demultiplexing (e.g., DWDM) and other functions in such networks, arrayed-waveguide gratings (AWGs) have been developed in the form of PLCs.
A problem with OICs is polarization dependence of the waveguides, typically caused by waveguide birefringence. Waveguide birefringence is experienced in varying degrees with waveguides fabricated from the above-mentioned materials. For example, where the waveguides are formed by depositing a glass film on a silicon substrate, the difference in thermal expansion coefficient between the glass film and the silicon substrate base causes stress applied on the waveguides in a direction parallel to the surface to be different from that in a perpendicular direction.
Waveguide birefringence results, wherein the refractive index of the waveguides in the direction parallel to the substrate surface becomes different from that in the perpendicular direction. The birefringence, in turn, causes polarization dependence in the waveguides, where the optical path length difference (e.g., between adjacent waveguides) changes depending on the polarizing direction of light. In this situation, shifts occur between the transverse electric (TE) and transverse magnetic (TM) mode peaks, where the shift changes according to polarization. Consequently, the device characteristics change in accordance with the polarized state of the light provided to the device. For instance, the peak coupling in a particular channel or waveguide can vary according to the polarities of the various wavelength components, causing polarization dependent wavelength shift.
The polarization state in an optical network is affected by many parameters including stress on an optical fiber or waveguide. The varying loss associated with changing polarization is called polarization dependent loss. In other words, polarization dependent loss is a measure of component sensitivity to state of polarization. Polarization dependent loss is measured by monitoring the change in insertion loss as the polarization is changed through all of the possible polarization states with a polarization controller. Polarization dependent loss is expressed as the difference between the maximum and minimum insertion loss. The difference in insertion loss for one polarization compared to another is expressed in dB. Polarization dependent loss in optical network components affects a system's performance, especially when there are many components in the system.
OICs may contain one or more couplers. A coupler is a device for coupling optical power between two waveguides. Couplers made of planar waveguides consist of deposited films and other structures that typically have unmatched coefficients of thermal expansion. As a result, stress is present in the device. Stress in coupler waveguides in close proximity can be one or more of anisotropic and asymmetric. For example, the inner edges of coupler waveguides show higher stress compared to the outer edges. The stress is one or more of tensile stress and compressive stress.
The stress affects the refractive index of the waveguides through the stress optic coefficients and leads to unwanted rotations of the optical axes in the couplers. The rotation of optical axes facilitates the coupling between polarizations within the same waveguide as well as between different waveguides in close proximity. Such polarization coupling may result in increased polarization dependent loss within the device.
In OICs with a plurality of optical devices, such as a plurality Mach-Zehnder devices, polarization dependent loss bow is exhibited. Polarization dependent loss bow occurs when the end/edge channels of an array exhibit low polarization dependent loss, and polarization dependent loss increases as the middle/central channel is approached. This may be due to excessive etch loading on the end channels during their formation. Although it is generally desirable to reduce polarization dependent loss, an asymmetric occurrence of polarization dependent loss may be undesirable.
OICs contain metal lines, metal heaters, metal interconnects, and other metal films on top of the top cladding. These metal structures are required for the operation of the OICs. However, the metal structures on top of the top cladding often induce stress in the underlying waveguides. When the stress is asymmetric, birefringence is induced undesirably rotating the optical axes.
The following presents a simplified summary of the invention in order to provide a basic understanding of some aspects of the invention. This summary is not an extensive overview of the invention. It is intended to neither identify key or critical elements of the invention nor delineate the scope of the invention. Rather, the sole purpose of this summary is to present some concepts of the invention in a simplified form as a prelude to the more detailed description that is presented hereinafter. The present invention provides OICs and methods for reducing polarization dependent loss in OICs and OICs exhibiting reduced polarization dependent loss. Generally speaking, the present invention provides a number of avenues for reducing and/or more evenly distributing stress within OICs thereby reducing polarization dependent loss.
One aspect of the invention relates to a method of reducing polarization dependent loss in an OIC by providing at least one dummy waveguide structure proximate an operable waveguide or at least one dummy metal structure proximate an operable metal structure to reduce and/or more evenly distribute stress within the OIC.
Another aspect of the invention relates to a method of reducing polarization dependent loss in an OIC by forming an OIC comprising a substrate and at least one waveguide having a first birefringence and a first optical axes; and imposing a mechanical force on the OIC to exert mechanical stress thereby changing at least one of the first birefringence and the first optical axes of the at least one waveguide to a second birefringence and a second optical axes.
Yet another aspect of the invention relates to a method of reducing polarization dependent loss in an OIC by forming a metal heater proximate at least one waveguide using a first set of metal deposition parameters; forming a conductive metal structure contacting the metal heater using a second set of metal deposition parameters; and selecting the first set of metal deposition parameters and the second set of metal deposition parameters to reduce metal stress between the conductive metal structure and the metal heater.
To the accomplishment of the foregoing and related ends, certain illustrative aspects of the invention are described herein in connection with the following description and the annexed drawings. These aspects are indicative, however, of but a few of the various ways in which the principles of the invention may be employed and the present invention is intended to include all such aspects and their equivalents. Other advantages and novel features of the invention will become apparent from the following detailed description of the invention when considered in conjunction with the drawings.
The present invention provides avenues for reducing polarization dependent loss in OICs by tailoring and/or controlling stress. Stress and polarization dependent loss in OICs can be mitigated by positioning dummy waveguide structures proximate operable waveguides functioning as couplers; by positioning dummy waveguide structures proximate operable end waveguide channels; by positioning dummy metal structures proximate operable metal structures; by maximizing the symmetry of metal structures relative to the operable waveguides; by applying mechanical stress to the OIC/waveguides; and/or by controlling the metal deposition conditions to regulate stress between adjacent metal structures.
Since stress on operable waveguides causes birefringence resulting in polarization dependent loss, reducing the stress and/or making the stress uniform upon substantially all portions of a waveguide and/or upon all waveguides in a given OIC, reduces polarization dependent loss in the OICs containing the waveguides.
The OICs of the present invention contain at least one waveguide. The OICs may be or contain AWGs, wavelength splitters, taps, couplers, Mach Zehnders, variable optical attenuators (VOAs), and integrated devices containing two or more thereof. The OICs are made, at least in part, with materials such as silica, monocrystalline silicon, InP, thermo-optic polymers, electro-optic polymers, LiNbO3, silicon oxynitride, silicate glasses, and the like. Examples of silicate glasses include phosphosilicate glass (PSG), fluorosilicate glass (FSG), borophosphosilicate glass (BPSG), germanium borophosphosilicate glass (GBPSG), germanium, germanium phosphosilicate, and germanium posophosphosilicate.
The OICs are typically made by forming a bottom cladding layer on a substrate; depositing and patterning a core layer thereover forming at least one waveguide; forming a top cladding layer over the waveguides; and forming heaters and other metal structures over the top cladding layer.
In one embodiment, the present invention involves reducing polarization dependent loss in an OIC by providing at least one dummy waveguide structure proximate an operable waveguide to reduce stress within the optical integrated circuit. The dummy or inoperable waveguide structure, which is made of the same or similar material as the operable waveguides, may have shape a shape similar to an operable waveguide, or it may have a random shape. In this connection, the dummy waveguide structure may have a cross-sectional area approximately equal (typically about 2 μm or more and about 10 μm or less in diameter) to operable waveguides, or the dummy waveguide structure may have a square, rectangular, circular, oval, or other geometric structure.
While not wishing to be bound by any theory, it is believed that the dummy waveguide structure contributes to symmetric stress distribution on the operable waveguides within an OIC. Alternatively or additionally, it is believed that forming the dummy waveguide structure at the time of forming the operable waveguides contributes to more even distribution of the etch loading of end/edge channels, thereby reducing polarization dependent loss bow across an OIC.
Referring to
Referring to
Dummy waveguide structures 14 are in the shape of operable waveguides, but they do not mimic the same layout as the operable waveguides 12, although they may be positioned in such a manner (not shown). Dummy waveguide structures 14 may or may not be near the coupling regions of operable waveguides 12.
Dummy waveguides 14 may be positioned on one side of operable waveguides 12, or on both sides as shown in
Referring to
Dummy waveguide structures 24 are positioned near at least a portion of the operable waveguides 22 (within about 500 μm or less of the operable waveguides 22). By positioning the dummy waveguide structures 24 near the coupling region of the operable waveguides 22, stress on the operable waveguides in the coupling region is mitigated.
Referring to
Dummy waveguide structures 26 are positioned near at least a portion of the operable waveguides 22 (within about 500 μm or less of the operable waveguides 22). By positioning the dummy waveguide structures 26 near the coupling region of the operable waveguides 22, stress on the operable waveguides in the coupling region is mitigated.
Referring to
Dummy waveguide structures 28 are positioned near at least a portion of the operable waveguides 22 (within about 500 μm or less of the operable waveguides 22). By positioning the dummy waveguide structures 28 near the coupling region of the operable waveguides 22, stress on the operable waveguides in the coupling region is mitigated.
Referring to
Dummy waveguide structures 30 are positioned near at least a portion of the operable waveguides 22 (within about 500 μm or less of the operable waveguides 22). By positioning the dummy waveguide structures 30 near the coupling region of the operable waveguides 22, stress on the operable waveguides in the coupling region is mitigated.
The dummy waveguide structures in
The dummy waveguide structures are made of the same or similar material as the operable waveguides. It can be advantageous to provide dummy waveguide structures with the same material as the operable waveguides in order to match or make similar the coefficient of expansion and other physical properties. Generally speaking, the coefficient of expansion and other physical properties of the operable waveguides and the dummy waveguide structures are within about 20% of each other.
The specific shape or pattern of the dummy waveguide structures may vary, as several specific different examples are shown in
In another embodiment, the present invention involves reducing polarization dependent loss in an OIC by providing at least one dummy metal structure proximate an operable metal structure to reduce stress within the optical integrated circuit. Alternatively, dummy metal structures are provided on an OIC so that a generally symmetrical metal layout (relative to the entire OIC or relative to one or all waveguides) may be obtained. By positioning at least one dummy metal structure near an operable metal structure, the stress associated with different coefficients of expansion (or other physical properties) between metal, the waveguides, and cladding material are mitigated and/or more evenly distributed throughout the OIC.
Referring to
In this embodiment, the metal heater 42 is typically made of a resistive or refractory metal, such as chromium, nickel, tantalum, titanium, tungsten, titanium-tungsten, vanadium, and mixtures and alloys thereof. Also in this embodiment, the metal contact 44 and metal interconnect 46 are typically made of a conductive metals, such as aluminum, copper, silver, gold, and mixtures and alloys thereof. Thus, the dummy metal structure 48 may be made of resistive metals, refractory metals, and/or conductive metals.
Dummy metal structures 48 are in the shape of operable metal structures, the metal interconnects 46 in particular in this embodiment, but they do not mimic the same layout as all the operable metal structures, although they may be positioned in such a manner (not shown). Dummy metal structures 48 may have any shape that reduces stress within the OIC. Dummy metal structures 48 may or may not be near the coupling regions of an OIC. Dummy metal structures 48 may be positioned on one side of an operable metal structure, or on both sides.
Often, metal heaters are positioned directly over a waveguide, Mach Zehnder, coupler, or the like in a layer above the waveguides. Dummy metal structures near operative metal heaters are positioned to impart some symmetry to the overall metal layout on an OIC. As a result, stress due to different coefficients of expansion between metal structures (both operable and dummy) and other OIC materials is more evenly distributed within the OIC and/or about one or more waveguides in the OIC.
The dummy metal structures may be made in the substantially same manner as the operable metal structures. After a top clad layer is formed over one or more waveguides, a metal layer containing one or more suitable metals to function as a heater, interconnect, contact, conductor, and the like is formed thereover. The metal layer is patterned, typically using lithographic techniques. Patterning the metal layer provides operable metal structures as well as the dummy metal structures (typically not connected to other metal structures). When formed in this manner, the dummy metal structures have the same or substantially the same thickness as the operable metal structures.
The dummy metal structures are made of the same or similar material as the operable metal structures. It can be advantageous to provide dummy metal structures with the same material as the operable metal structures in order to match or make similar the coefficient of expansion and other physical properties. Generally speaking, the coefficient of expansion and other physical properties of the operable metal structures and the dummy metal structures are within about 20% of each other.
In the event two or more different types of metals are patterned on the OIC in two different sets of deposition/patterning steps, the dummy metal structures may be formed with one or more of the first set of metal structures, the second set of metal structures, the third set of metal structures and so on.
The specific shape or pattern of the dummy metal structures may vary from that shown in
In yet another embodiment, the present invention involves reducing polarization dependent loss in an OIC by imposing a mechanical force on the OIC to exert mechanical stress thereby changing at least one of the birefringence and optical axes of the waveguide(s) in the OIC.
In a first aspect, the mechanical force is imposed by bending the optical integrated circuit. Referring to
The stress is imposed by securing or holding the OIC with any suitable device and applying a force to the OIC at the location where held or at a different location(s) using another device. For example, the OIC 50 may be held at point 64, and forces may be applied along arrows 51 and 60 to impose mechanical stress on the waveguides. Numerous combinations of holding positions and force positions may be employed, and such can be determined by one skilled in the art.
A suitable force is applied to sufficiently bend the OIC so that at least one of the birefringence and optical axes of waveguide(s) in the OIC are changed to reduce polarization dependent loss. The force applied depends on the size of the OIC, the materials that make up the OIC particularly including the waveguide material, the thickness of the substrate, and the like.
In one embodiment, the force applied to sufficiently bend the OIC is about 100 MPa or more. In another embodiment, the force applied to sufficiently bend the OIC is about 150 MPa or more.
In a second aspect, the optical integrated circuit is adjacent a riser, and the mechanical force is imposed by providing a riser with a first thermal expansion coefficient and the OIC substrate has a second thermal expansion coefficient. The difference in thermal expansion coefficients imposes mechanical stress upon the OIC, which causes changes in at least one of the birefringence and optical axes of waveguide(s) in the OIC. The intentional mismatch of thermal expansion coefficients is thus an efficient manner to impose mechanical stress on an OIC. Additionally or alternatively, an adhesive that is optionally employed between the riser and OIC substrate can be selected based upon its thermal expansion coefficient, or mismatch thereof relative to the OIC.
Referring to
In a third aspect, the mechanical force is imposed by depositing metal on top of the OIC. The metal has a first thermal expansion coefficient and the OIC has a second thermal expansion coefficient. The difference in thermal expansion coefficients imposes mechanical stress upon the OIC, which causes changes in at least one of the birefringence and optical axes of waveguide(s) in the OIC.
Referring to
The metal structure(s) 84 may be made in the substantially same manner as other metal structures in the OIC. After forming the OIC, a metal layer is formed thereover. The metal layer is then optionally patterned, typically using lithographic techniques.
The metal structure(s) 84 may have any shape and thickness that imposes a mechanical force on the OIC. The specific shape or pattern of the metal structure 84 may and will vary from that shown in
In a fourth aspect, the optical integrated circuit comprises silicon dioxide on its backside, and the mechanical force is imposed by removing a portion of the silicon dioxide. Generally speaking, OICs are fabricated on silicon or silica substrates, mainly due to the balance in maximizing both cost and performance considerations. In this aspect of the invention, the OIC substrate is thinned, on the backside, to impose a mechanical force on the waveguides (compared to the OIC without the thinned substrate) causing changes in at least one of the birefringence and optical axes of waveguides.
The different materials that make up an OIC each have different thermal expansion coefficients. The waveguides have a first thermal expansion coefficient and the OIC substrate (unthinned) has a second thermal expansion coefficient. Thinning the backside of the OIC substrate provides the OIC substrate with a third thermal expansion coefficient, which imposes a mechanical force on the waveguides compared to the unthinned OIC substrate. The amount of thinning is that which is suitable to provide the OIC substrate with a different thermal expansion coefficient (different from the unthinned OIC substrate), and which imposes a mechanical force on the waveguides to cause changes in at least one of the birefringence and optical axes. It is not necessary to uniformly thin the backside of the OIC substrate.
In one embodiment, about 1 μm or more and about 10,000 μm or less in thickness is removed from the backside of the OIC substrate. In another embodiment, about 10 μm or more and about 5,000 μm or less in thickness is removed from the backside of the OIC substrate. The OIC substrate may be thinned in any suitable manner including liquid etching, plasma etching, chemical mechanical polishing, and precision grinding.
In still yet another embodiment, the present invention involves reducing polarization dependent loss in an OIC by selecting metal deposition parameters of a metal heater and metal deposition parameters a conductive metal structure contacting the metal heater to reduce metal stress where the conductive metal structure contacts the metal heater. When two metal layers or structures are formed adjacent each other, the difference in thermal expansion coefficients can vary depending on the manner in which the metal structures are formed. In particular, varying the deposition parameters of a metal structure leads to differences in the thermal expansion coefficients of subsequently formed metal structures.
Referring to
In OIC fabrication, metal structures are formed, in part, by initially depositing a metal (or metals, or alloys) on the target substrate by electroplating, evaporation, chemical vapor deposition (CVD), physical vapor deposition (PVD) or sputtering. Parameters that can be varied in these deposition processes include one or more of pressure, temperature, power, atmosphere composition, time, concentration of metals (when forming an alloy layer), and the like. Selection of specific values of each of the applicable parameters depends upon the identity of the metal(s) being deposited, the desired thickness, and the identity of metal(s) that may be subsequently deposited adjacent thereto.
Such specific values can be determined by one skilled in the art, especially in view of stress formulae. The stress formula takes into account the stresses associated with depositing specific metals under specific conditions. These stresses are known to those skilled in the art, or can be readily determined by those skilled in the art. The combined metal stress can be calculated using Formula (I):
wherein σom is the combined overall metal stress, σm1, is the metal stress of the first metal(s) deposited (such as the heater), σm2 is the metal stress of the second metal(s) deposited (such as the interconnect), tm1 is the thickness of the first metal(s) deposited, and tm2 is the thickness of the second metal(s) deposited. And the overall OIC or wafer stress can be calculated using Formula (II):
wherein σow is the effective overall OIC or wafer stress, σTC is the stress of the top clad layer, tTC is the thickness of the top clad layer, and tom is the average thickness of the metal layers.
In one embodiment, the present invention enables reducing polarization dependent loss in an OIC by about 0.05 dB or more. In another embodiment, the present invention enables reducing polarization dependent loss in an OIC by about 0.1 dB or more. In another embodiment, the present invention enables reducing polarization dependent loss in an OIC by about 0.15 dB or more.
In one embodiment, the present invention enables reducing polarization dependent loss by about 5% or more in an OIC. In another embodiment, the present invention enables reducing polarization dependent loss by about 10% or more in an OIC. In yet another embodiment, the present invention enables reducing polarization dependent loss by about 20% or more in an OIC.
Although the invention has been shown and described with respect to certain illustrated implementations, it will be appreciated that equivalent alterations and modifications will occur to others skilled in the art upon the reading and understanding of this specification and the annexed drawings. In particular regard to the various functions performed by the above described components (assemblies, devices, circuits, systems, etc.), the terms (including a reference to a “means”) used to describe such components are intended to correspond, unless otherwise indicated, to any component which performs the specified function of the described component (e.g., that is functionally equivalent), even though not structurally equivalent to the disclosed structure, which performs the function in the herein illustrated exemplary aspects of the invention. In this regard, it will also be recognized that the invention includes a system as well as a computer-readable medium having computer-executable instructions for performing the acts and/or events of the various methods of the invention.
In addition, while a particular feature of the invention may have been disclosed with respect to only one of several implementations, such feature may be combined with one or more other features of the other implementations as may be desired and advantageous for any given or particular application. As used in this application, the term “component” is intended to refer to a computer-related entity, either hardware, a combination of hardware and software, software, or software in execution. For example, a component may be, but is not limited to, a process running on a processor, a processor, an object, an executable, a thread of execution, a program, and a computer. Furthermore, to the extent that the terms “includes”, “including”, “with”, “has”, “having”, and variants thereof are used in either the detailed description or the claims, these terms are intended to be inclusive in a manner similar to the term “comprising.”
This application is a Division of and claims the benefit of priority to co-pending U.S. patent application Ser. No. 11/351,031, filed on Feb. 9, 2006, the entire contents of which are incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
6222974 | Nagata | Apr 2001 | B1 |
6240221 | Thompson | May 2001 | B1 |
6243517 | Deacon | Jun 2001 | B1 |
6278168 | Day | Aug 2001 | B1 |
6885795 | Hsu et al. | Apr 2005 | B1 |
7003198 | Doerr | Feb 2006 | B2 |
20040146247 | Tsai et al. | Jul 2004 | A1 |
20050013576 | Chhabra et al. | Jan 2005 | A1 |
20050213887 | Balakrishnan et al. | Sep 2005 | A1 |
20060126989 | Glebov | Jun 2006 | A1 |
Number | Date | Country | |
---|---|---|---|
20080279497 A1 | Nov 2008 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11351031 | Feb 2006 | US |
Child | 12181905 | US |