Patent Application
20070054810
The present invention relates to a manufacturing method of a MgB2 superconductor having a high critical current density (Jc) and its wire, and a MgB2 superconductor and superconducting wire having a high critical current density (Jc) which are obtained from the method. Compared with a conventional metal-based superconductor in bulk form and its wire, it can be expected that the MgB2 superconductor in bulk form and its wire can be used at higher temperature and lower the cost. Therefore, they can be applied to apparatuses such as a superconducting linear motor car, an MRI medical diagnosis apparatus, a single crystal synthesizing apparatus for semiconductors, superconducting energy storage, a superconducting rotating machine, a superconducting transformer, and a superconducting cable.
Because the superconductor MgB2, which was discovered in Japan in 2001, has the most superior superconducting critical temperature (39 K) among the metal-based superconductors, and it is relatively easy to manufacture the bulk materials and to process the wire, research and development of this superconductor and of forming its wire is undertaken all over the world. A method of manufacturing the bulk materials generally includes pressurizing a mixed powder of Mg powder or MgH2 powder and B powder and then heat-treating (sintering). One of the major methods of forming the wire is a powder-in-tube method wherein a metal tube is filled with Mg (MgH2) powder and B powder. However, Jc characteristics of the bulk form and the wire which are manufactured by the ordinary powder-sintering method and by the powder-in-tube method are not very high. Accordingly, in order to improve the Jc, there have been attempts to add various types of impurities into the mixed powder. Among these additions of impurities, the addition of SiC fine particles having a particle size at the nanometer level is most effective, and much research on this addition is being undertaken (S. X. Dou, et al., Journal of Applied Physics 94 (2003) 1850 (Document 1). However, the price of the SiC fine particles is high and has been an obstacle to putting this technique into practical use.
In view of the circumstance, the present invention has an object to provide a novel method with which MgB2 superconductor and superconducting wire having a sufficiently high Jc of practical level can be provided by a relatively simple method which solves the conventional problems and leads to lowering of costs.
As a means to solve the above-described problems, the present invention provides a method of manufacturing a MgB2 superconductor or a MgB2 superconducting wire, wherein an aromatic hydrocarbon such as benzene is added to the mixed powder of Mg powder or MgH2 powder and B powder which are the raw materials of the superconductor MgB2. The present invention provides a method of manufacturing a MgB2 superconductor, wherein the aromatic hydrocarbon is a compound having a monocyclic or polycyclic carbocyclic ring or heterocyclic ring, the aromatic hydrocarbon is a compound having 4 to 20 carbon atoms, the aromatic hydrocarbon is one or more kinds of benzene, naphthalene, anthracene, perylene, biphenyl, and thiophene, and the aromatic hydrocarbon is added at the ratio of 1 to 40 mol % to MgB2.
Moreover, the present invention provides a method of manufacturing a MgB2 superconducting wire comprising filling and processing a metal tube with a mixture to which an aromatic hydrocarbon is added, and heat-treating the metal tube, wherein the metal tube is an iron tube, and the wire is a multifilament wire having a plurality of MgB2 cores. As a method of mixing powders, ball-mill mixing and mixing in an ordinary mortar are considered, and the heat treatment is considered to be performed in an inert gas atmosphere such as argon or in a vacuum. Moreover, the metal tube is most appropriately an iron tube because it does not react with Mg or B and the price is low.
Furthermore, the present invention provides a MgB2 superconductor or a MgB2 superconducting wire manufactured with any of the methods, wherein Jc in a magnetic field of 10 T at 4.2 K is 5000 A/cm2 or more and Jc in a magnetic field of 12 T at 4.2 K is 2000 A/cm2 or more.
The present invention has the characteristics as described above, and the embodiment is explained below in detail.
According to the present invention, the method of manufacturing a MgB2 superconductor or its wire, as described previously, comprises adding an aromatic hydrocarbon, pressure-compacting, and heat-treating when a mixture of Mg powder or MgH2 powder and B powder as raw materials of a MgB2 superconductor is prepared.
The pressure-compacting is performed with a press using a metal mold and the pressure is preferably 100 to 300 kg/cm2.
For the above-described powder as raw materials, powder having the same purity and particle size as the conventional method can be mixed in the range of Mg or MgH2/B=0.5/2 to 1.5/2 molar ratio. More preferably, the molar ratio is in the range of about 0.8/2 to 1.2/2.
For the particle size, an average particle size of Mg or MgH2 and B is considered to be preferably about in the range of 10 to 50 μm and 0.2 to 1 μm respectively. For the mixing, specifically, a proper amount of the aromatic hydrocarbon is added to the mixture of Mg powder or MgH2 powder and B powder, and the mixture is mixed thoroughly using a ball mill or other means. After the mixture is pressure-compacted, it is heat-treated and the bulk form is obtained. In the case of the wire, a metal tube such as an iron tube is filled with the mixture to which the aromatic hydrocarbon is added, is processed to a tape or a wire with a pressure roll or other means, and is heat-treated.
The aromatic hydrocarbon may be considered to be various types of compound having a monocyclic or polycyclic carbocyclic ring or heterocyclic ring. Although the number of carbon atoms in the compound is not limited, it is considered to be suitably in the range of 4 to 20 in general.
The aromatic hydrocarbon may have various types of functional groups as long as the operation and effect of the invention are not inhibited. Considering the availability, handling, price, etc., the selection of the aromatic hydrocarbon can be made properly. Representative examples include carbocyclic aromatic hydrocarbons such as benzene, naphthalene, anthracene, perylene, biphenyl, toluene, and xylene, and heterocyclic aromatic hydrocarbons such as thiophene.
It is more preferable to add these aromatic hydrocarbons at a ratio of 1 to 40 mol % to MgB2 in theory or in an experimental production amount. In this range, for example, the MgB2 superconductor or its wire which has a high Jc at 4.2 K of 5000 A/cm2 or more in a magnetic field of 10 T (tesla) and 2000 A/cm2 or more in a magnetic field of 12 T (tesla), is realized more reliably.
For the mixing, pressure-compacting, and heat treatment, the same conditions as the conventional conditions may be adopted. The same applies to the conditions of forming a wire.
Accordingly, Examples are shown below and the invention is explained in more detail. Of course, the invention is not limited to Examples below.
MgH2 powder available on the market and B powder available on the market were mixed at a molar ratio of 1:2. Then 10 mol % of benzene to MgB2 was added, and the mixture was placed in a ball-mill pot manufactured by WC and subjected to ball milling for about an hour. An iron tube of 6 mm outer diameter and 4 mm inner diameter was filled with the mixed powder obtained in this manner, and processed into a tape of 5 mm width and 0.5 mm thickness by being processed with a groove roll and rolled with a flat roll. Moreover, a tape to which benzene was not added was manufactured with the same method for comparison. A heat treatment was performed on these wires for an hour at 600° C. in an argon atmosphere using a tube-like furnace. A flow chart of manufacturing the wire is shown in
According to Document 1, a part of the B atoms in MgB2 was substituted by C atoms when SiC was added, MgB2−xCx was produced, and as a result of this, the Jc characteristics were improved. Considering this report, the reason why the Jc characteristics were improved in the present experiment is presumed to be that a part of the B atoms in MgB2 was substituted by a carbon atom when benzene was added, and MgB2−xCx was produced.
In place of benzene in Example 1, 10 mol % of naphthalene was added and a tape was manufactured with the same method. The Jc-B characteristics of the tape at 4.2 K are shown in
In place of benzene in Example 1, 10 mol % of thiophene was added and a tape was manufactured with the same method. The Jc-B characteristics of the tape at 4.2 K are shown in
In place of MgH2 powder in Example 1, Mg powder available on the market was used. The molar ratio of Mg to B was set to be 1:2 and a MgB2 superconducting tape was manufactured with the same method. The Jc-B characteristics of the tape at 4.2 K were measured, and almost the same Jc-B characteristics were obtained as those of the tape for which MgH2 was used. The effect of adding benzene was also observed clearly in the case of using Mg powder in place of MgH2 powder.
According to the present invention described above, a MgB2 superconductor having higher superconducting critical current density (Jc) or its wire can be provided with a simple and lower cost method for practical use.