Abstract

A micro coaxial cable includes an inner conductor; an insulation layer having foaming cells and formed to surround the inner conductor; an over-foaming preventing layer formed to surround the insulation layer for the purpose of uniform forming of the foaming cells; a metal shield layer formed to surround the over-foaming preventing layer; and a protective coating layer formed to surround the metal shield layer. The over-foaming preventing layer restrains abnormal growth of foaming cells formed in the insulation layer such that the foaming cells are successively adjacently formed with uniform size. Due to the uniformity of foaming, the dielectric constant of the insulation layer is not locally different but uniform as a whole, thereby capable of improving transmission characteristics. In addition, the micro coaxial cable enables to transmit signals even at a high frequency transmission of GHz range, which was impossible in the prior art.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

Other objects and aspects of the present invention will become apparent from the following description of embodiments with reference to the accompanying drawing in which:

FIG. 1 is a perspective view schematically showing a conventional coaxial cable;

FIG. 2 is a side and sectional view showing a micro coaxial cable according to one embodiment of the present invention;

FIG. 3 is a schematic view showing a co-extruder used for making the micro coaxial cable according to the present invention;

FIG. 4 is a photograph showing foaming cells in an insulation layer of the micro coaxial cable according to the present invention;

FIG. 5 is a graph showing a measurement result of a characteristic impedance (Z) of a micro coaxial cable according to the present invention, measured by an impedance analyzer;

FIG. 6 is a photograph showing foaming cells of a conventional micro coaxial cable; and

FIG. 7 is a graph showing a measurement result of a characteristic impedance of a conventional micro coaxial analyzer, measured by an impedance analyzer.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings for better understanding of the present invention. However, the embodiments of the present invention may be modified in various ways, and the present invention should not be interpreted as being limited to the following embodiments. The embodiments of the present invention are provided just for better understanding of the present invention to those having ordinary skill in the art.

A micro coaxial cable according to the present invention includes an over-foaming preventing layer formed to surround an insulation layer, so foaming cells formed in the insulation layer are successively adjacently formed with a uniform size. Due to the uniformity of foaming, a dielectric constant in the insulation layer is uniform as a whole without showing any local difference, thereby giving excellent transmission characteristics.

The micro coaxial cable according to the present invention has no special limitation in its diameter. However, since a micro coaxial cable having a diameter of 1 mm or less shows serious problems such as abnormal growth of foams or unbalance of an outer diameter while forming foaming cells in an insulation layer, the present invention may be more effectively applied to a micro coaxial cable having a diameter of 1 mm or less.

FIG. 2 is a sectional and side view showing a micro coaxial cable according to one embodiment of the present invention.

Referring to FIG. 2, the micro coaxial cable of this embodiment includes an inner conductor 21, an insulation layer 23 formed to surround the inner conductor 21, an over-foaming preventing layer 25 formed to surround the insulation layer 23 in contact with the insulation layer 23, a metal shield layer 27 formed to surround the over-foaming preventing layer 25 in contact with the over-foaming preventing layer 25, and a protective coating layer 24 formed to surround the metal shield layer 27 in contact with the metal shield layer 27.

The inner conductor 21 is composed of one or several conductive wires, and preferably several conductive wires are twisted or stranded at a predetermined pitch to make the inner conductor 21. The conductive wires are preferably made of copper alloy in consideration of electric conductivity and economy. The inner conductor preferably has a diameter of 0.04 to 0.09 mm in consideration of the entire diameter of the micro coaxial cable, and each conductive wire preferably has a diameter of 0.01 to 0.04 mm when several conductive wires are twisted to make the inner conductor.

Polymer having a low dielectric constant is extruded and coated on the outer circumference of the inner conductor to form the insulation layer 23 in order to improve transmission characteristics. In order to lower the dielectric constant, fluoric resins are preferred, among which PFA (PerFluoroAlkoxy) is most referred. In addition, in order to further lower the dielectric constant, polymer is foamed such that foaming cells are formed in the insulation layer 23. For this purpose, a gas injection device, a mixing screw and a nozzle are applied to the extruder, and a foaming cell is formed at an outlet of the extruder. When being employed in the micro coaxial cable, the insulation layer preferably has a thickness of 0.03 to 0.09 mm in consideration of electric features, more preferably 0.035 to 0.075 mm. If the insulation layer has a thickness less than 0.03 mm, it is not easy to meet the characteristic impedance having suitable power transmission characteristics. If the insulation layer has a thickness exceeding 0.09 mm, it can be hardly used for a micro coaxial cable. In the present invention, foaming cells formed in the insulation layer are adjacent to each other, differently from the conventional ones, and thus it is possible to give a uniform dielectric constant. The foaming cell preferably has a size of 0.02 to 0.07 mm. A foaming cell having a size less than 0.02 mm can be hardly realized, and a foaming cell having a size exceeding 0.07 mm is restricted due to the thickness of the insulation layer.

The over-foaming preventing layer 25 is formed to surround the insulation layer 23 in contact with the insulation layer 23, and it prevents over-foaming when foaming cells are formed in the insulation layer 23. Thus, the over-foaming preventing layer 25 allows foaming cells to be uniformly formed in the insulation layer, attributes to restraining of formation of abnormal foaming cell, and makes foaming cells be adjacent to each other. The over-foaming preventing layer 25 as mentioned above preferably has a lower melt temperature than the insulation layer 23, in order to induce uniform growth of cells by facilitating cooling of the foams of the insulation layer 23. Thus, the over-foaming preventing layer 25 is preferably made of polyethylene (PE), polypropylene (PP), polyethylene terephthalate (PET), or their mixtures, among which PET having the fastest cooling speed is most preferred. In particular, PET has a processing temperature of about 200° C., similar to fluoric resins, so it is advantageous in aspect of thermal stability in comparison to polyethylene or polypropylene that has a processing temperature of about 100° C. The over-foaming preventing layer preferably has a smaller thickness than the insulation layer, preferably in the range of 0.01 to 0.04 mm.

When the insulation layer 23 and the over-foaming preventing layer 25 are formed, an extruder nozzle conducts co-extrusion or successive double extrusion (or, tandem extrusion) such that the over-foaming preventing layer 25 directly covers the outer circumference of the foamed insulation layer 23. In this way, at the same time as the insulation layer 23 is extruded, the over-foaming preventing layer 25 is extruded on the outer circumference of the insulation layer. The over-foaming preventing layer 25 is instantly cooled after passing through the nozzle in a melt state, and restrains excessive foam growth when gas is foamed in the insulation layer 23, thereby facilitating to make uniform and fine foams. In addition to the above effects, it is possible to improve productivity since a separate cooling line is not required by applying the co-extrusion or tandem extrusion.

FIG. 3 is a schematic view showing an extruder for conducting co-extrusion (namely, a co-extruder), which is used for making the micro coaxial cable according to the present invention. Referring to FIG. 3, the co-extruder includes an insulation layer resin supplier 31 for supplying resin used for forming an insulation layer, a preventing layer resin supplier 33 for supplying resin used for forming an over-foaming preventing layer, and a head 35. As a conductive wire 37 progresses in a wire advancing direction A, the insulation layer 23 is extruded on the outer circumference of the conductive wire, and at the same time the over-foaming preventing layer 25 is extruded on the outer circumference of the insulation layer.

The metal shield layer 27 made of metal mesh, metal filament, helical winding or metal thin film is formed on the outer circumference of the over-foaming preventing layer 25, and the protective coating layer 24 is formed on the outer circumference of the metal shield layer 27 so as to protect the micro coaxial cable. The protect coating layer 24 may be made of any material used for forming the protective coating layer 24 of a conventional coaxial cable, without any limitation.

The micro coaxial cable configured as mentioned above, which includes the over-foaming preventing layer 25 on the outer circumference of the insulation layer 23, allows to form foaming cells with uniform size on the insulation layer 23 and restrain any local difference of dielectric constant caused by broken foams or partially clumping foams, thereby capable of preventing signal deterioration according to a high frequency transmission.

FIG. 4 is a photograph showing foaming cells of the insulation layer 23 of the micro coaxial cable according to the present invention, and FIG. 5 is a graph showing a measurement result of a characteristic impedance (Z) of the micro coaxial cable according to the present invention, measured by an impedance analyzer. Seeding FIG. 4, it would be understood that foaming cells are formed successively with uniform size. Also, from FIG. 5, it would be understood that the characteristic impedance is substantially kept uniformly between the upper and lower limits.

FIG. 6 is a photograph showing foaming cells in a conventional micro coaxial cable, namely a coaxial cable having no over-foaming preventing layer, and FIG. 7 is a graph showing a measurement result of a characteristic impedance of a conventional micro coaxial cable, measured by an impedance analyzer. Seeing FIG. 6, it would be understood that foaming cells have irregular sizes and are not formed adjacently but formed sparsely. Seeing FIG. 7, it would be understood that a dielectric constant locally varies due to irregular sizes of the foams in length and radial directions, and thus a characteristic impedance varies in a length direction, approximating to the upper and lower limits of the standard in a severe region, so its characteristic is unstable.

APPLICABILITY TO THE INDUSTRY

The micro coaxial cable according to the present invention includes the over-foaming preventing layer formed to surround the insulation layer, thereby restraining abnormal growth of foaming cells formed in the insulation layer such that the foaming cells are successively adjacently formed with uniform size. Thus, due to the uniformity of foaming, the dielectric constant of the insulation layer is not locally different but uniform as a whole, thereby capable of improving transmission characteristics.

In addition, the micro coaxial cable of the present invention enables to transmit signals even at a high frequency transmission of GHz range, which was impossible in the prior art. Also, the micro coaxial cable of the present invention ensures excellent transmission characteristics due to the uniformity of dielectric constant in the insulation layer even when it is made into a very small size with a diameter of 1 mm or less, furthermore in an ultra small size of so far as 0.21 mm or less. Thus, the micro coaxial cable of the present invention may be made into a very small size, and it may also allow medical instruments such as an endoscope to have a very small size, which may relieve the pain of a patient during medical examination and treatment.

Claims

1. A micro coaxial cable, comprising: an inner conductor;an insulation layer having foaming cells and formed to surround the inner conductor;an over-foaming preventing layer formed to surround the insulation layer for the purpose of uniform forming of the foaming cells;a metal shield layer formed to surround the over-foaming preventing layer; anda protective coating layer formed to surround the metal shield layer.

2. The micro coaxial cable according to claim 1, wherein the micro coaxial cable has a diameter of 1 mm or less.

3. The micro coaxial cable according to claim 2, wherein the insulation layer has a thickness of 0.03 to 0.09 mm.

4. The micro coaxial cable according to claim 2, wherein the foaming cells provided in the insulation layer have a size of 0.02 to 0.07 mm.

5. The micro coaxial cable according to claim 2, wherein the over-foaming preventing layer has a thickness of 0.01 to 0.04 mm.

6. The micro coaxial cable according to claim 1, wherein the over-foaming preventing layer has a smaller thickness than the insulation layer.

7. The micro coaxial cable according to claim 1 or 2, wherein the over-foaming preventing layer has a lower melt temperature than the insulation layer.

8. The micro coaxial cable according to claim 1 or 2, wherein the insulation layer is made of fluoric resin.

9. The micro coaxial cable according to claim 8, wherein the fluoric resin is PFA (PerFluoroAlkoxy).

10. The micro coaxial cable according to claim 1 or 2, wherein the over-foaming preventing layer is made of one or more polymer resin selected from the group consisting of polyethylene, polypropylene and polyethylene terephthalate.

11. The micro coaxial cable according to claim 1 or 2, wherein the insulation layer and the over-foaming preventing layer are formed using co-extrusion or tandem extrusion.