Claims
- 1. A method comprising:extruding a microcellular parison suitable for blow molding from an extruder die while varying the thickness of the parison; and blow molding the parison to form a microcellular, blow-molded article.
- 2. A method as in claim 1, comprising providing a single-phase, non-nucleated solution of polymeric material and a blowing agent that is a gas under ambient conditions, nucleating the single-phase solution by subjecting the solution to a high pressure drop rate, and extruding a microcellular parison that is a product of the single-phase solution.
- 3. A method as in claim 1, wherein the article has a void volume of at least about 10%.
- 4. A method as in claim 1, further comprising establishing a stream of a fluid, single-phase non-nucleated solution of a precursor of microcellular material and a blowing agent, continuously nucleating the solution to form a nucleated polymeric fluid, and extruding the microcellular parison from the nucleated polymeric fluid.
- 5. A method as in claim 4, the step of continuously nucleating involving creating sites of nucleation of the blowing agent in the stream by subjecting the stream to conditions of solubility change sufficient to create sites of nucleation in the solution in the absence of an auxiliary nucleating agent.
- 6. A method as in claim 1, further comprising establishing a stream of a fluid, single-phase non-nucleated solution of a precursor of microcellular material and a supercritical fluid blowing agent prior to extruding the microcellular parison.
- 7. A method as in claim 4, involving creating sites of nucleation by subjecting the stream to a pressure drop at a pressure drop rate sufficient to create sites of nucleation.
- 8. A method as in claim 7, involving subjecting the stream to a pressure drop at a pressure drop rate sufficient to create sites of nucleation at a density of at least about 107 sites/cm3.
- 9. A method as in claim 7, involving subjecting the stream to a pressure drop at a pressure drop rate of at least about 0.3 GPa/sec to create sites of nucleation.
- 10. A method as in claim 1, comprising extruding the microcellular parison into ambient conditions from an extruder die while varying the thickness of the parison.
- 11. A method as in claim 1, further comprising establishing the stream of fluid, single-phase non-nucleated solution of a precursor of microcellular material and a blowing agent by introducing, into fluid polymeric material flowing at a rate of at least about 10 lbs./hr, a fluid that is a gas under ambient conditions and, in a period of less than about one minute, creating a single-phase solution of the fluid and the polymer, the fluid present in the solution in an amount of at least about 2% by weight based on the weight of the solution.
- 12. A method as in claim 11, further comprising continuously nucleating the solution by continuously decreasing the pressure within successive, continuous portions of the flowing, single-phase stream at a rate which increases.
- 13. A method as in claim 11, wherein the concentration of the blowing agent in the homogeneous single-phase non-nucleated solution is at least about 5 percent, by weight, of the solution.
- 14. A method as in claim 11, wherein the concentration of the blowing agent in the homogeneous single-phase non-nucleated solution is at least about 7 percent, by weight, of the solution.
- 15. A method as in claim 11, wherein the concentration of the blowing agent in the homogeneous single-phase non-nucleated solution is at least about 10 percent, by weight, of the solution.
- 16. A method as in claim 11, wherein the blowing agent is supercritical carbon dioxide.
- 17. A method comprising:providing an extruded polymeric microcellular foam parison; and subjecting the parison to blow molding conditions.
- 18. A method as in claim 17, the subjecting step comprising applying pressure of at least about 1.5 bar internal of the parison.
- 19. A method as in claim 18, comprising applying pressure of at least about 3 bar internal of the parison.
- 20. A method as in 18, comprising applying pressure of at least about 5 bar internal of the parison.
- 21. A method as in 18, comprising applying pressure of at least 10 bar internal of the parison.
- 22. A method as in claim 17, further comprising forming a blow-molded article that is essentially free of a supporting, non-foam structure, the article being essentially closed cell, having a wall thickness of less than about 0.075 inch.
- 23. A method as in claim 17, comprising continuously extruding the polymeric microcellular foam parison and continuously subjecting the parison to blow molding conditions.
- 24. A method as in claim 17, comprising:providing an extruded polymeric foam parison having a first portion and a second portion spaced from the first portion in the parison machine direction, the first portion and the second portion differing in thickness by a factor of at least about 1.1; and subjecting the parison to blow molding conditions.
- 25. A method as in claim 24, the first portion and the second portion differing in thickness by a factor of at least about 1.3.
- 26. A method as in claim 24, the first portion and the second portion differing in thickness by a factor of at least about 1.5.
- 27. A method as in claim 24, the first portion and the second portion differing in thickness by a factor of at least about 1.7.
- 28. A method as in claim 24, comprising:providing an extruded polymeric foam parison having a first portion and a second portion spaced from the first portion in the parison machine direction, the first portion and the second portion differing in material density by a factor of at least about 1.1; and subjecting the parison to blow molding conditions.
- 29. A method as in claim 24, comprising:providing an extruded parison of polymeric material of melt flow no more than about 0.2 g/10 min; and subjecting the parison to blow molding conditions.
- 30. A method comprising:providing a polymeric microcellular foam parison; and without heating the parison subjecting the parison to blow molding conditions.
- 31. A method as in claim 30, wherein the parison is an extruded polymeric microcellular foam parison.
- 32. A method as in claim 17, further comprising conveying polymeric material in a downstream direction in an extruder.
- 33. A method as in claim 32, further comprising introducing a blowing agent into the polymeric material in the extruder to form a mixture of blowing agent and polymeric material.
- 34. A method as in claim 33, wherein the blowing agent is a physical blowing agent.
- 35. A method as in claim 34, wherein the blowing agent comprises carbon dioxide or nitrogen.
- 36. A method as in claim 33, wherein the blowing agent is introduced through multiple orifices into the polymeric material in the extruder.
- 37. A method as in claim 33, further comprising mixing the mixture of blowing agent and polymeric material to form a single-phase solution.
- 38. A method as in claim 37, further comprising extruding the single-phase solution to form the extruded polymeric microcellular foam parison.
- 39. A method as in claim 38, further comprising nucleating the single-phase solution in a nucleating pathway while extruding the single-phase solution.
- 40. A method as in claim 39, comprising nucleating the single-phase solution at a pressure drop rate of at least about 0.1 GPa/sec.
- 41. A method as in claim 32, wherein the polymeric material has a melt flow of no more than about 0.2 g/10 minute.
- 42. A method as in claim 17, comprising subjecting the parison to blow molding conditions to form a microcellular, blow-molded article.
- 43. A method as in claim 42, wherein the microcellular, blow-molded article has an average cell size of less than about 50 microns.
- 44. A method as in claim 42, wherein the microcellular, blow-molded article has a maximum cell size of about 100 microns.
- 45. A method as in claim 42, wherein the microcellular, blow-molded article is a bottle.
- 46. A method as in claim 42, wherein walls of the microcellular, blow-molded article are formed entirely of microcellular material.
- 47. A method as in claim 42, wherein the microcellular, blow-molded article includes sections having different void volumes.
- 48. A method as in claim 42, wherein the microcellular, blow-molded article includes sections having different thicknesses.
- 49. A method as in claim 42, wherein the microcellular, blow-molded article has a wall thickness of less than about 0.100 inch.
- 50. A method as in claim 42, wherein the microcellular, blow-molded article has a void volume of at least about 10%.
- 51. A method as in claim 42, wherein the microcellular, blow-molded article has a void volume of at least about 30%.
- 52. A method as in claim 42, wherein the microcellular, blow-molded article has a void volume of at least about 50%.
- 53. A method as in claim 42, wherein the microcellular, blow-molded article is essentially closed-cell.
- 54. A method as in claim 42, wherein the microcellular, blow-molded article includes at least about 1% by weight nucleating agent.
RELATED APPLICATIONS
This application is a divisional of U.S. patent application Ser. No. 09/241,352, filed Feb. 2, 1999 now abandoned, which is a continuation-in-part of PCT application serial no. PCT/US98/27118, filed Dec. 18, 1998, which is a continuation-in-part of U.S. patent application Ser. No. 60/107,754 filed Nov. 10, 1998 and a continuation-in-part of U.S. patent application Ser. No. 60/068,173 filed Dec. 19, 1997.
US Referenced Citations (48)
Foreign Referenced Citations (10)
Number |
Date |
Country |
0707935 |
Apr 1996 |
EP |
0799853 |
Oct 1997 |
EP |
0818292 |
Jan 1998 |
EP |
1 456 171 |
Nov 1976 |
GB |
WO 8900918 |
Feb 1989 |
WO |
WO 9007546 |
Jul 1990 |
WO |
WO 9524440 |
Sep 1995 |
WO |
WO 9728050 |
Aug 1997 |
WO |
WO 9808667 |
Mar 1998 |
WO |
WO 9831521 |
Jul 1998 |
WO |
Non-Patent Literature Citations (3)
Entry |
D.F. Baldwin et al., “A processing system for the extrusion of microcellular polymer sheets: shaping and cell growth Control”, Cellular and Microcellular Materials, Nov. 1994, MD-vol. 53, pp. 95-107 (ASME 1994). |
C. Park et al., “Effect of the pressure drop rate on cell nucleation in continuous processing of microcellular polymers” Polymer Engineering and Science, Mar. 1995, vol. 35, No. 5, pp. 432-440. |
C. Park et al., “Filamentary extrusion of microcellular poylmers using a rapid decompressive element”, Polymer Engineering & Science, Jan. 1996, vol. 36, No. 1, pp. 34-48, XP000583331, see page 42, column 2 —p. 46. |
Provisional Applications (2)
|
Number |
Date |
Country |
|
60/107754 |
Nov 1998 |
US |
|
60/068173 |
Dec 1997 |
US |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
PCT/US98/27118 |
Dec 1998 |
US |
Child |
09/241352 |
|
US |