Patent Application
20050042615
The present invention relates to a microfluidic method of generating in situ a colloid for use in detecting an analyte using for example SER(R)S, as well as a method of detecting an analyte using SER(R)S in a microfluidic system. The invention also relates to microfluidic devices for use in detecting analytes such as by way of SER(R)S signals.
Surface-enhanced resonance Raman scattering(1,2) is an extremely powerful analytical tool which not only yields information about the molecular structure of the analyte in the form of a vibrational spectrum, but also allows sensitivity comparable to that achieved using fluorescence spectroscopy(3-5). Surface enhanced Raman scattering(SERS) involves the adsorption of an analyte on a suitable surface(usually roughened silver or gold) and the recording of the Raman scattering from that surface. The use of molecular resonance enhancement, where the frequency of the excitation source is tuned to be in resonance with an analyte chromophore as well as surface enhancement(SER(R)S), results in a further increase in sensitivity and also enhances the selectivity of the system(6). This enables discrimination of the analyte of interest from any contaminants which may be present in the system. Additionally, as compared to detection using fluorescence, there is much better labelling chemistry and much better results in multiplex detection.
One of the main problems associated with using SERRS as a quantitative analytical technique is the difficulty associated with producing reproducible SERRS substrates. Variations in the morphology of SERRS substrates can give rise to vast variations in the SERRS intensities produced(7). One common SERRS substrate is silver colloid(8-11). This can be easily prepared by reduction of aqueous solutions of silver salts(9, 12, 13). However, as with other substrates, there is still a problem associated with the production of stable, reproducible silver colloids(10, 14). It has also been found that in order to achieve the maximum enhancement from silver colloid the colloid must be aggregated(15-18). This is due to the greatly enhanced electromagnetic field between aggregated colloidal particles compared with that at the surface of a single colloidal particle(19). Aggregation can be induced using a wide range of reagents, however, this is a dynamic process and as different SERRS intensities are accumulated from aggregates of different morphologies(20, 21), it is desirable to be able to control the aggregation process in order to achieve reproducible SERRS signals.
One method of improving the reproducibility of SERRS signals obtained using silver colloid as the SERRS substrate, is to use a macro-flowcell for analysis(22-26). In this type of system the colloid, analyte and aggregating agent are pumped into a cell where they are allowed to mix. The signal is then accumulated from the flowing stream as it passes the laser beam. As the sample solution is continually flowing throughout the signal accumulation time, there is an averaging of the SERRS intensities accumulated from different aggregates and control over the kinetics of aggregate formation. This results in increased analytical precision and good quantitation over several orders of magnitude. This type of system also gives greater control over the rates of addition of reagents and the state of aggregation of the colloid at the point of signal accumulation. Similar systems have also been developed in which the colloid is prepared on-line(27-29). This eliminates the need to prepare stable, reproducible colloid batches.
However, there are a number of potential disadvantages with using macro-flow cell based systems. For example if colloid is prepared in situ, the colloid may only remain stable for a short period of time, typically minutes. This means essentially that the analyte sampling and SERRS detection have to be carried out concurrently. It is not generally possible therefore to take a sample and carry out the SERRS detection at a later time.
Moreover, with macro-flowcell systems a relatively large amount of reagents for carrying out the SERRS analysis is required, leading to impracticalities of field use of such devices. Additionally the sensitivity of SERRS detection using macro-flowcells may not be optimal due to an effective dilution of an analyte with the colloid. Other disadvantages of using a macro-flowcell system include the ability to store chemicals under non-degrading conditions and disposal of waste.
It is an object of the present invention to obviate and/or mitigate at least one of the aforementioned disadvantages.
In a first aspect the present invention provides method of generating in situ a colloid for use in detecting an analyte using SER(R)S, wherein the colloid is generated by contacting a first microfluidic stream of a suitable metal salt with a second microfluidic stream of a reducing agent whereby mixing of said first and second streams substantially occurs at an interface region between said first and second streams and wherein colloid is formed in the interface region.
The colloid so generated in situ, or ex situ (that is not using a micofluidic system, or a separate microfluidic system) may be mixed with an analyte so as to adhere the analyte thereto and thereafter detected by way of SER(R)S. Optionally a further reagent may be bound or otherwise associated with the colloid and the analyte adhered thereto. Typically the analyte is provided by way of a third microfluidic stream arranged to contact the colloid so formed.
Optionally an aggregating agent or means may also be required for colloid generation where the reducing agent alone is not sufficient for colloid generation. Said aggregating agent may be introduced by way of a further stream, or included in an existing stream which may be combined with said other streams, before, during, or after analyte mixing. Aggregating means may include electrochemical, electric, dielectric or magnetic means designed to aggregate the colloid. Such means could be positioned adjacent or in contact with the microfluidic stream, so as to act thereon.
It is to be appreciated that SER(R)S refers to SERS (surface enhanced Raman scattering) and SERRS (surface enhanced resonance Raman spectroscopy), with SERRS being preferred. This should not however be construed as limiting, as other scattering or wave-resonance detection techniques including Raleigh scattering and surface plasmon resonance could also be employed.
Examples of analytes which may be detected include, nucleic acids, nucleic acid analogues, proteins, peptides, amino acids, enzymes, prions, antibodies, aldehydes, amines, ketones, explosives, drugs of abuse, therapeutic agents, metabolites and environmental pollutants. This is not however exhaustive, as any suitable analyte may be detected. The analyte may be obtained from a sample and the sample may be any suitable preparation in which the target analyte is likely to be found. However, conveniently the sample may be in a fluid, or in solution or transferred to a solution before mixing with the colloid. Thus, for example when detecting explosives or drugs of abuse, a sample of gas, such as air or breath respectively, may be taken and any target analyte absorbed onto a suitable substrate. Thereafter, any target analyte may be removed from the substrate by washing with a suitable solvent.
For effective SERRS analysis, a chromophore of a suitable wavelength to be in resonance with the laser chosen, must be present in the analyte or a chromophore must be created by derivatisation of the analyte before analysis. Moreover in either case effective adsorption to the surface of the colloid particles must be achieved. Thus, the analyte may be reacted with a reagent so as to derivatise the analyte. The reagent which is used to derivatise the analyte, may provide a chromophore, may provide in combination with the analyte, a chromophore and/or render the analyte susceptible to adhering to the SERRS active substrate. Full details of such derivatisation may be found for example in PCT/GB01/01611, to which the skilled reader is directed.
The colloid particles prepared according to the present invention are aggregated in a controlled manner so as to be of a reproducible size and shape and as stable as possible against self-aggregation. Processes for preparing such unaggregated colloids are already known. They involve, for instance, the reduction of a metal salt (eg. silver nitrate) with a reducing agent such as citrate, to form a stable microcrystalline suspension (see P. C. Lee & D. Meisel, J. Phys, Chem. (1982), 86, p3391). This “stock” suspension is then aggregated in situ by contacting with a suitable aggregating agent. Suitable aggregating agents include acids (eg. HNO3 or ascorbic acid), polyamines (eg. polylysine, spermine, spermidine, 1,4-diaminopiperazine, diethylenetriamine, N-(2-aminoethyl)-1,3-propanediamine, triethylenetetramine and tetraethylenepentamine) and inorganic activating ions such as Cl−, I−, Na or Mg2+. Heating may be required in certain circumstances to achieve colloid formation in a desirable timescale. A particularly preferred method of forming the colloid, which may be carried out at room temperature, is to mix a first stream comprising sodium-borohydride with a second stream comprising silver nitrate. To increase control over the process, all equipment used should be scrupulously clean, and reagents should be of a high grade. Unlike colloids prepared using existing techniques, the problem of precipitation does not occur. SER(R)s analysis may therefore be conducted for example 10 minutes to 4 hours after colloid aggregation, such as 15 minutes to 1 hour after aggregation.
The colloid particles are preferably monodisperse in nature and can be of any size so long as they give rise to a SERRS effect—generally they will be about 4-50 nm in diameter, preferably 25-36 nm, though this will depend on the type of metal. Any suitable metal or metal alloy may be used such as silver, copper or gold. Moreover, the particles may be coated on another surface, such as a bead or sphere, in order to, for example, increase the effective size/weight of the particles and thus alter their flow characteristics.
Preferably, the surface comprises metal, such as silver colloid particles, which may be substantially hexagonal in shape and of about 20-36 nm maximum diameter.
Adhering the analyte/derivatised analyte with the colloid will typically be by chemi-sorption of the complex onto the surface of the colloid particles, or by chemical bonding (covalent, chelating, etc.) of the complex with either the surface or a coating on the surface, either directly or through a linking group. The association will usually be via suitable functional groups on the analyte or derivatised analyte, such as charged polar groups (eg. NH3+ or CO2−), attracted to the surface or surface coating (eg. to free amine groups in a polyamine coating). Clearly, the type of association will depend on the nature of the surface and the label in any given case; different functional groups will be attracted to a positively-charged surface, for instance, as to a negatively-charged one.
Suitable groups by which the complex may be bound to the active surface include complexing groups such as nitrogen, oxygen, sulphur and phosphorous donors; chelating groups; bridging ligands and polymer forming ligands. Specific details of preferred methods of adhering the derivatised analyte with the SERRS active substrate are described, for example, in WO97/05280.
The method for obtaining the SERRS spectrum, once the derivatised analyte has been adhered to the metal substrate, may be conventional. By way of example, however, the following might apply to the spectroscopic measurements:
Typically, the methods of the invention will be carried out using incident light from a laser, having a frequency in or close to the visible spectrum ie. −380 nm-850 nm, particularly between 400 nm-650 nm (the exact frequency chosen will generally depend on the chromophore used in each case—frequencies in the red area of the visible spectrum tend, on the whole, to give rise to better surface enhancement effects but the fourth power of Raman means that blue is better and many chromophore lie in the green region giving maximum resonace enhancment there. However, it is possible to envisage situations in which other frequencies, for instance in the ultraviolet (ie. 200 nm-400 nm) or the near-infrared ranges (700 nm-1100 nm), might be used. Thus, SERRS detection may be conducted between about 300 nm-1100 nm.
The selection and, if necessary, tuning of an appropriate light source, with an appropriate frequency and power, will be well within the capabilities of one of ordinary skill in the art, particularly on referring to the available SERRS literature. To achieve highly sensitive detection, using SERRS, a coherent light source is needed with a frequency at or close to the absorption maximum for the chromophore (as described above) or that of the surface plasmons. If lower sensitivities are required, the light source need not be coherent or of high intensity and so lamps may be used in combination with a monochromator grating or prism to select an appropriate excitation frequency; here, there is no need to operate at the resonant frequency of the chromophore or the plasmons.
The light can be conducted from the source to the active surface by reflection in mirrors and can be focussed to give a higher light flux by passing through lenses. A suitable apparatus for SERRS analyses is a microscope with signal detection at 180 degrees to the excitation beam. A fluorescence microscope with confocal optics is also appropriate. The use of microscope optics permits the very small channels and/or volumes of a microfluidic device to be analysed.
Several devices are suitable for collecting SERRS signals, including wavelength selective mirrors, holographic optical elements for scattered light detection and fibre-optic waveguides. The intensity of a SERRS signal can be measured for example using a charge coupled device (CCD), a silicon photodiode, CMOS integrated detector, or photomultiplier tubes arranged either singly or in series for cascade amplification of the signal. Photon counting electronics can be used for sensitive detection-. The choice of detector will largely depend on the sensitivity of detection required to carry out a particular assay.
Note that the methods of the invention may involve either obtaining a full SERRS spectrum across a range of wavelengths, or selecting a peak and scanning only at the wavelength of that peak (ie. Raman “imaging”).
Apparatus for obtaining and/or analysing a SERRS spectrum will almost certainly include some form of data processor such as a computer.
Raman signals consist of a series of discrete spectral lines of varying intensity. The frequencies and the relative intensities of the lines are specific to the derivatised analyte being detected and the Raman signal is therefore a “fingerprint” of the derivatised analyte. If a SERRS analyser is being used selectively to detect one analyte out of a mixture then it will be necessary to detect the entire “fingerprint” spectrum for identification purposes. However if the analyser is being used to quantitate the detection of one or several analytes, each of which has a unique spectral line, then it will only be necessary to detect signal intensity at a chosen spectral line frequency or frequencies, or to detect all Raman scattering using a filter to exclude Rayleigh scattering.
Once the SERRS signal has been captured by an appropriate detector, its frequency and intensity data will typically be passed to a computer for analysis. Either the fingerprint Raman spectrum will be compared to reference spectra for identification of the detected Raman active compound or the signal intensity at the measured frequencies will be used to calculate the amount of Raman active compound detected.
A commercial SERRS analyser of use in carrying out the invention would be expected to consist of the following components: a laser light source, the appropriate optics for carrying the light to the SERRS active surface, a stage for mounting the microfluidic device for analysis, optics for receiving the Raman signal, a detector for converting the Raman signal into a series of intensities at certain wavelengths and a data processor for interpreting the wavelength/intensity data and providing an analytical output.
In a further aspect the present invention provides a microfluidic device for use in detecting analytes by way of SER(R)S, the device comprising a substrate having microscale channels formed therein and inlets attached to the channels for introducing a suitable metal salt, a reducing agent, a sample and optionally an aggregating agent, wherein flows within channels for carrying the suitable metal salt and the reducing agent converge so as to allow mixing of the suitable metal salt and the reducing agent and generation of a colloid at an interface between the suitable metal salt flow and the reducing agent flow; and flow within a channel for carrying the sample is arranged to converge with the colloid so produced such that any analyte present in the sample may adhere to the colloid.
The microfluidic device may be in the form of a Lab-on-a-chip device well known in the art and comprising all the necessary reagents within the chip. Alternatively the reagents can be provided from sources external to the device.
Typically the substrate is formed of glass, such as soda lime glass, for optical quality purposes although other clear materials may be used optically, such as silicon or polymers and the microscale channels have dimensions in the range 1 μm to 500 μm, typically 10 μm-200 μm but most commonly 50 μm. The size is however more dependent on being able to produce the appropriate laminar flow properties which have been observed as particularly beneficial. The inlets for introducing the various reagents are typically in the form of wells or reservoirs for maintaining a suitable quantity of reagent or sample.
Once any analyte has adhered to the colloid, detection of the analyte may be carried out by way of SER(R)S as hereinbefore described. Conveniently a microscope with a suitable lens may be focussed on a channel carrying colloid with adhered analyte.
The reagents and sample are drawn through the channels using suitable means, this may include for example, pumps, syringe drives, electrokinetics and/or electrohydrodynamics (see for example U.S. Pat. No. 6,409,900).
Electroosmotic flow is an electrokinetic phenomenon that can be exploited to manipulate fluids within complex microfluidic manifolds. If silanol groups on the surface of a glass micro channel are deprotonated, positive ions from the bulk solution are attracted and are loosely bound to provide overall charge neutrality. When a high potential is applied across this channel, these loosely bound positive ions are attracted the cathode which through viscous coupling drags the bulk solution resulting in electroosmotic flow. One of the main advantages of EOF is the elimination of moving parts such as valves/switches. In addition, flat flow profiles are present eliminating the parabolic flow profile prevalent in pressure driven systems, i.e. the velocity is same across the whole channel. Typical channel dimensions used for successful EOF are approximately 10-100 μm wide and 5-40 μm deep with channel lengths in the regions of a few centimeters employing electrical field strengths of 100 v-1 kv/cm. Although electrophoretic forces are still present, the EOF is generally greater, allowing negative species such as a negative metal colloid or molecule to be driven towards the cathode.
In the case of colloid formation, aqueous silver salts can be mixed with an appropriate aqueous reducing agent such sodium borohydride to form a colloid stream. Exploiting the laminar flow properties of microfluidics, a stable and reproducible interface is formed between the two reagents at which reactions are dominated by diffusional processes rather than convective or mechanical means associated with macro scale formation. As such colloid size is more reproducible and precise. The use of such planar flow cells is compatible with optical microscopy regimes and is therefore well suited to SERRS detection, eliminating the problems commonly associated with focusing on circular capillaries/tubing In microfluidic systems, low dimensions and fast fluid flow gives low Reynolds numbers and consequently no turbulence. Consequently, as two streams of fluid are brought together, liquid streamlines do not interfere with each other, and the only mixing that occurs is that provided by diffusion between the two streams. The process is known as laminar flow. The consequence of laminar flow and lack of mixing is often seen as a disadvantage for microfluidic systems. However, in the present invention the lack of bulk mixing has been utilised to provide the generation of colloid in a controlled manner.
In the context of detection by SER(R)S analysis, the production of colloidal metal, such as silver in a microfluidic system occurs through the bringing together of two streams of reactants. In such a case, silver nanoparticles are only produced at the interface between these two laminar streamlines, which do not, themselves mix.
The consequences of this are as follows:
Previously, some of the present inventors have demonstrated the integration of microelectrode arrays and/or waveguides or optical fibres in Lab-on-a-Chip devices (30). Using these microfabrication techniques, it is possible to further take advantage of the highly localised colloid particles of the present invention and achieve the following analytical advantages.
One application particularly suited to detection using the method and/or device according to the present invention is the detection of extremely small amounts of DNA for the analysis of single nucleotide polymorphisms (SNPs).
The basic approach makes use of the fact that SERRS can identify different chromophores based on molecular structure. Thus, a label can be generated in situ by the reaction of a SERRS activating agent and a specific tag attached to the molecule of interest. However, the tagged species does not produce any SERRS on its own, and only therefore produces a SERRS signal when in combination with the SERRS activating agent.
In one embodiment an oligonucleotide may be modified to contain the tag as described above. Oligonucleotides are used in a wide variety of analysis and one specific example is given below. The tag is a small unreactive chemical moiety that does not produce SERRS. i.e. no chromophores in the visible region and no propensity for the metal surface used. To generate a specific SERRS signal a chemical reaction that is specific to the tag (i.e. is not affected by any other chemical group) is used. This desirably has to be fast and occur in aqueous solution. One such reaction is a Diels Alder cycloaddition which actually occurs faster in water than organic solvent. The cycloaddition occurs between a diene and a dienophile. Thus it is possible to use either as the tag moiety. For the sake of brevity further reference will be made to the use of a diene as a tag on an oligonucleotide, but this is not to be construed as limiting. The tag may, for example, be added at the 5′or 3′-terminus or at any position within the oligonucleotide. For example, a furan residue which is a diene may be added to the 5′-terminus of an oligonucleotide and also to the 5-position of a thymidine nucleoside. The thymidine nucleoside can be used to add to any position of the probe oligonucleotide whilst being produced by solid phase synthesis.
A suitable dienophile is benzotriazole maleimide (BTM). The benzotriazole provides excellent surface attachment (see patent WO97/05280) and the maleimide is a dienophile commonly used in Diels Alder cycloadditions.
When the tagged oligonucleotide reacts with the BTM a unique signal is produced. Rather unexpectedly the quality of the signal is better than that of the pure, isolated cycloadduct without the attached oligonucleotide. Without wishing to be bound by theory this improvement is attributed to the presence of the oligonucleotide which confers increased aqueous solubility to the system.
A proposed method of DNA analysis using the method and/or device according to the present invention is as follows:
An object is to allow identification of single base polymorphisms within a gene based on the principle of mini-sequencing. A triphosphate with a diene tag may be produced according to the structures below.
Thus, as the 3′-OH is missing (1) or blocked (2) only one base will be added in a round of enzymatic extension using a specific primer as is common in mini-sequencing. Once added, development takes place by addition of the dienophile to produce a unique SERRS active cycloadduct relating to the base added. In the case of triphosphate (2) the diene will be joined to the sugar via a photocleavable linkage. An example of a class of photocleavable linkers are nitrobenzyl groups and derivatives thereof, see (31). This will allow the diene to be removed to expose the 3′-OH again. This provides a primer that will hybridise as normal and a second round of sequencing can be performed to give the next base in the sequence. This may be done for example by recirculating the mix or by having a series of reaction chambers depending on the number of bases required for sequencing. The fact that the colloid stream remains in the middle of the channel and does not diffuse means that the tag can be removed photo chemically and will react with the developing reagent to give the SERRS active cycloadduct. This will actively move towards the colloidal stream and become adsorbed onto the surface of the colloid and is thus removed from further reaction. The liquid surrounding the colloid stream may then be recirculated and now contains a primer with one extra base added. This will allow the next base in the sequence to be identified by following the same procedure as for the first base.
The increased sensitivity of SERRS in a microflow cell means that this will be possible on DNA isolated directly from the organism without amplification. Advantages are that four compounds are all that's needed for identification of any number of mutations or normal bases. This approach cannot be done by fluorescence as fluorophores at the 3′-OH prevent the enzyme adding the triphosphate and fluorescence wouldn't give a fingerprint of the tag used.
Embodiments of the present invention relate to the ability to selectively code particles. For example it is possible to attach a number of different SER(R)S reactive dyes to the surface of a colloid particle as well as a reagent, such as a protein, peptide or oligonucleotide designed to bind to the analyte to be detected. This can be done either prior to introduction of the particle to the device or in situ in the dvice. By virtue of being able to effectively code the particles based on the particular dyes used, it is possible to detect analyte based on the particular SER(R)S signal generated. Complex mixtures of differently coded particles can be provided and readily identified based on the signal generated.
Also particles which have been functionalised with different dyes can be provided in a single system, whereby only one type of particle can bind to a particular analyte, thereby allowing detection of the analyte. An example of this would be to provide a number of separate oligonucleotides, each oligonucleotide being associated with a differently labeled particle, such that each oligonucleotide is capable of specifically binding to one form of a polymorphic nucleotide sequence, thereby enabling identification of the particular sequence in a sample being tested. Such a process is often referred to as multiplexing.
A final example relates to the ability to use the described method/system to introduce colloid particles into, for example, a biological cell, such as an animal cell. The cell can be introduced to a device so that the cell is immobilized or otherwise retaing the cell so that it is in the flow-path of the colloid. The cell can then be permeabilised by, for example, electroporation, such that colloid can flow into and/or through the cell. The colloid particles can be functionalised by attachment of, for example, an oligonucleotide, protein or peptide, which is designed to bind to a component-within the cell. The exact location and/or presence of the component within the cell can then be detected by way of SER(R)S analysis.
The present invention will now be described by way of example and with reference to the Figures which show:
a shows a schematic diagram of a chip design for use in generating colloid according to the present invention and detecting an analyte using SERRS;
b shows an inset of a detail of a channel in the device as shown in
c shows a schematic diagram of a chip design according to the present invention, utilizing electroosmotic flow to manipulate fluids within the device;
a and b show SER(R)S spectra obtained from 2 and 3 labeled oligonucleotides, respectively.
The fluid channel was fabricated by a standard photolithographic technique. S1818 photoresist (Shipley Europe, Coventry, UK) was spin coated on an acid cleaned 1.5 mm thick soda lime glass (Soda Lime glass, Nanofilm, USA) at 4000 rpm for 30 seconds. The glass was baked on a 90° C. hot plate for 3 minutes, followed by UV exposure through an acetate sheet lithography mask to define the channel pattern for 8 seconds. The photoresist was developed in a mixed solution of 1 part of Microposit Developer Concentrate (Shipley Europe) and 1 part of RO water for 35 seconds and dried with nitrogen. The substrate was then baked on a 90° C. hot plate for 15 minutes to ensure all the solvent had been evaporated and to harden the photoresist. Finally, the glass was wet etched in a mixed solution of 1 part of hydrofluoric acid and 4 parts of RO water for 15 minutes, resulting in 30 μm deep and 250 μm wide channel. After the etching procedure, the glass was ultrasonicated in acetone to remove the photoresist.
To seal the channels a cover plate was fabricated. Holes, for the inlet and outlet reservoirs, were aligned with the etched substrate and drilled using a 1.5 mm diamond engraving bit (RS, Corby, Northants, UK). The etched substrate and cover plate were then prepared for bonding. Successful bonding relies on ultra clean surfaces which was carried out by cleaning the glass in a piranha solution (H2SO4:H2O2=1:7) for at least 10 minutes, followed by a ultrasonication in acetone for 5 minutes. They were then rinsed in RO water and thoroughly dried with nitrogen. The etched substrate was then aligned with the access holes in the cover plate and placed in a steel clamp (Engineering Workshop, University of Glasgow) between two pieces of macor plates (RS, Corby, Northants, UK). The clamp was then placed in a furnace set at 60 C which was ramped over 60 minutes to 500 C and held for 1 hour. The temperature was then ramped up to 570 C and held for a further 5 hours. Finally, the furnace was taken down to 60 C and allowed to cool down overnight. The thermal bonding strategy resulted in permanent bond between the etched substrate and cover plate.
A diagram of the flow system used is shown in
b is a diagram of a flow system designed to use elctroosmotic flow. Devices for colloid formation were fabricated from soda lime glass microscope slides. These devices were fabricated using standard photolithographic methods followed by hydrofluidic acid etching and thermal bonding of a blank glass coverplate. C dimension were 60 μm wide, 10 μm deep with a variety of lengths. The channel layout and mode of operation is shown
Sodium borohydride (99%), silver nitrate (99.9999%) and sodium hydroxide (97%) were purchased from Aldrich (Dorset, England). An aqueous solution of silver nitrate (2.6×10−3 M) and a solution of sodium borohydride (1.1×10−3 M) in sodium hydroxide solution (0.1 M), were introduced into inlets 3 and 5 respectively using a micropipette. The azo dye solution, which was prepared in methanol, was introduced into inlet 7. The chosen analyte was an azo dye, 5-(2-methyl-3,5-dinitro-phenylazo)quinolin-8-ol, synthesised as part of a program to detect trinitrotoluene (TNT) by derivatisation methods. It was analysed by nmr and C,H and N analysis and found to be pure (C was within 0.4%). The structure of the dye is shown in
The solutions were pulled through the system under vacuum using a syringe attached to outlet 15. Spectra were accumulated by focussing the laser on the colloid stream using a ×10 objective lens. Accumulation times were 10 s. In the experiments involving pre-mixing of the dye solution with the borohydride solution, a mixture of 1:1 sodium borohydride and dye solution (1×10−6 M) was introduced into inlet 5, silver nitrate was introduced into inlet 3 and distilled water was introduced into inlet 7. The solutions were then pulled through the system using a syringe and spectra were accumulated using a Renishaw Mark I system 2000(Gloucs. England) with a Spectra Physics 361C 15 mW argon ion laser working at 514 nm, as the excitation source.
Images
Images of the flow system were obtained using a white light microscope (Olympus) with a colour CCD camera (Polnex). Images were collected using a ×5 microscope objective. The bromocresol purple solution (pH 9.0) was obtained from Micronics Inc.
Results and Discussion
Flow Characteristics
Introduction of silver nitrate and sodium borohydride solution into inlets 3 and 5 resulted in the formation of a thin line of colloid within the flow system channels. The colloid line could be followed through the system using a white light microscope in either transmission or reflection mode. An image of the point of colloid formation within the channel is shown in
In order to try to promote mixing within the channels pillars 20 were introduced into the flow system. This is illustrated schematically in
To illustrate the relative rates of mixing and diffusion of the colloidal particles and dye molecules within the flow system a solution of indicator, bromocresol purple (pH 9.0) was introduced into inlet 7. When this solution mixed with the sodium borohydride solution, which is in 0.1 N sodium hydroxide solution, the pH change caused the indicator colour to change from orange to purple. It was therefore possible to monitor the diffusion of the indicator molecules within the cell by recording the colour change. Again images were taken using the white light microscope, this time in transmission mode. Silver nitrate, sodium borohydride and bromocresol blue solutions were introduced into inlet 3,5 and 7 respectively and these solutions were pulled through the system using a syringe. The flow was then stopped and the solutions were allowed to diffuse within the channels. An image was taken while the solutions were flowing and at intervals over a period of approximately two seconds after the flow had stopped. These images are shown in
In order to show whether there is any colloid diffusion within the channels while the flow is stopped, silver nitrate, sodium borohydride and distilled water were introduced into inlets 3,5 and 7 respectively and these solutions were sucked through the flow system once. Images were then taken at the point of colloid formation, immediately after colloid formation and at various time intervals over a 70-minute period. The images taken immediately after colloid formation and after 70 minutes are shown in
SERRS spectra of a dye 5-(2-methyl-3,5-dinitro-phenylazo)quinolin-8-ol, were accumulated using this system by introducing silver nitrate, sodium borohydride and dye solution into inlets 3,5,7 respectively. In order to determine the sampling point from which the maximum signal intensity could be achieved, spectra were accumulated from various points throughout the system. Generally speaking the intensities of the spectra accumulated decreased after the point of colloid generation. This may be due to rapid colloid formation within the first half of system and a lack of diffusion of the colloidal particles throughout the remainder of the system. The higher concentration of silver in these parts of the system gives rise to an increase in the amount of silver surface available for dye attachment, therefore leading to an increase in signal intensity in these areas.
As it was found that there was an increase in the signal intensity towards the start of the chip, it was thought that premixing of the dye with either the sodium borohydride or silver nitrate solutions may lead to an increase in the signal intensity, as the dye would be present at the point in the system where the colloid is formed. In all cases when the dye was premixed with silver nitrate this resulted in no colloid formation. This was due to the dye complexing with the silver prior to mixing with sodium borohydride solution, therefore preventing colloid formation. Spectra were accumulated throughout the system by introducing silver nitrate into inlet 3 and a mixture of sodium borohydride and dye solution into inlet 5. The accumulation of spectra from the different points was randomised in order to eliminate any potential effects of the time of signal accumulation. As expected the most intense signals were accumulated from close to the point of colloid formation. There was however no significant difference between the signal intensities achieved from the point of colloid formation after premixing of the dye with sodium borohydride solution and-those accumulated later in the system after introducing the dye through inlet 7.
The absence of any diffusion of the colloid line once the flow has stopped makes this system suitable for analysis using a stopped flow system. This would enable accumulation of the SERRS signal over an extended period of time therefore decreasing the detection limits achievable using this system. In order to assess the potential for signal accumulation over an extended period of time, SERRS spectra of the dye were accumulated every minute for one hour from the same point in the system. A plot of the signal intensity against time is shown in
In order to determine the detection limit of the dye using this system, dye solutions of concentrations ranging from 10−6 M to 10−9 M were introduced into the system through inlet 3. The colloid was formed in the system as described above and 10 μL of each of the dye solutions was introduced into the system, resulting in dye concentrations ranging from 10 pico moles to 10 femto moles. The spectra were accumulated by focussing the laser on the colloid stream at the point where the dye solution met the colloid. The spectra accumulated are shown in
A sample of DNA 50 is introduced into the system 52 and thereafter allowed to mix with appropriate primers, tagged triphosphates and DNA polymerase 54. The triphosphates are tagged with a suitable diene as described earlier. Each triphosphate ie. ATP, CTP, GTP or TTP is tagged with a different diene, so that upon SERRS detection a signal corresponding to each particular diene is generated which may be equated with a particular nucleotide triphosphate. Extension of the primer by addition of a tagged triphosphate is achieved by passing the mixture comprising the sample of DNA 50, the primers, tagged triphosphates and DNA polymerase 54 over a Peltier block 56, the temperature of which is controlled to first denature the DNA and thereafter allow annealing of the primer and primer extension by enzymic addition of a tagged triphosphate. The tagged extended primer is then reacted with the SERRS developing reagent 58 such as benzotriazole maleimide. Thereafter the tagged diene and SERRS developing agent 58 are cleaved by use of UV light, leaving the extended primer ready for further reaction/extension before reacting with colloid 58 formed from AgNO3 and NaBH4 and the particular diene/SERRS developing agent detected by Raman spectroscopy. In this manner the identify of the added nucleotide triphosphate may be determined. The extended primer may be recycled for further reaction/extension and the waste removed.
Here it is shown that a labelled oligonucleotide can be detected with three other dyes in a suspension of nanoparticles indicating the ability to provide a coded nanoparticle for identification of a particular sequence in a mixture of DNA fragments.
The oligonucleotide examined contained a basic priming sequence of 5′ GTG CTG CAG GTG TAA ACT TGT ACC AG 3′. The visible chromophore used was the fluorophore 2,5,2′,4′,5′,7′-hexachloro-6-carboxyfluorescein (HEX), which was attached at the 5′ terminus. HEX is negatively charged and therefore repels the negatively charged metal surface. Surface attachment was achieved by the incorporation of positively charged modified nucloebases at the 5′-terminus next to the HEX label. The three dyes used were azos containing the benzotriazole group for surface attachment.
All spectra were acquired in a Renishaw 2000 Raman Microprobe with a charge-coupled device (CCD) spectrometer. The excitation was provided by a Spectra-Physics Model 2020 argon-ion laser with a wavelength of 514.5 nm and 2 mW of power at the source. Samples were analysed in a plastic microtitre plate using a ×50 objective. The acquisition time for all spectra was 10 s and the grating was centred at 1350cm−1.
20 μl of Rhodamine labelled oligonucleotide (17 mer), 20 μl of Hex labelled oligonucleotide and 10 μl of 0.067M spermine were premixed and added as a continuous flow into a microflow cell, as described in example 1. The cell was designed to enable the colloid to be produced in situ and the colloid and oligonucleotide stream was mixed. The Raman spectrum was collected shortly after the point of mixing in the cell for 5 seconds. The time between mixing and measurement was 20 seconds.
Extension of this approach to three oligonucleotides is shown in
Motivation was to produce low resistance access to intracellular space in order to produce a reversible pore within the cell and to introduce SERRS particles. This has been achieved using both micron and submicron sized particles (sensor beads) enabling sensing to occur within the intracellular space.
Microelectrodes for electroporation were produced using standard photolithographic methods. Geometries were created to give a uniform fied across the cell or cells. Metal multilayers of Ti/Pd/Au (10/10/1000 nm) were deposited against a photopaterned resist layer on a glass substrate and the geometry was realized by lift-off. A fluidic overlayer was defined in moulded PDMA and was sealed against the glass substrate. Dry etching of the glass prior to sealing gave a good fluidic seal, preventing leakage. The area for cell electroporation was prefunctionalised by either adsorption or attachment of an attachment motif or by polylysine 5 mg/ml dried onto the surface. This functionalisation promoted cell adhesion, when introduced using a drawn micropipette, between the microelectrode geometries. The cell used was a rabbit cardiomyocyte prepared according to standard techniques.
Colloid was formed in the chip, as previously described under pressure driven flow, using two pumps, and the colloid flowed towards and round the cell. Two pairs of microelectrodes were used, one pair to electropermealise the cell, the second to monitor changes in local conductivity, such that it was possible to know that the cell compartment was accessed. The former pair of electrodes delivered a voltage pulse train of >200 mV for dielectric membrane breakdown. For example, ultrashort pulses (5 milliseconds) with 5-10 V DC enables reversible electropermeabilisation. Low voltage-pulses can be continually applied to a second orthogonal pair of electrodes to monitor the conductance of the cell, and hence the extent of permeabilisation. Groups of colloidal particles were viewed to have entered the cell, by visual observation of the cell under an inverted microscope.
In,the preferred format, Au particles were used as they were found to be less toxic.
References
Journal of the Chemical Society-Dalton Transactions 1996, 791-799.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0136319.3 | Nov 2001 | GB | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/GB02/05025 | 11/4/2002 | WO |