This application is based on and claims the benefit of priority from the prior Japanese Patent Application No. 2004-376014 filed on Dec. 27, 2004 and No. 2005-155135 filed on May 27, 2005, the entire contents of which are incorporated herein by reference.
The present invention relates to a microlens array sheet having a plurality of semispheroid microlenses cut from a spheroid material or semispherical microlenses cut from a spherical material, and a method of producing such a microlens array sheet. Particularly, this invention relates to a microlens array sheet useful for screens, for example, in rear-projection televisions, and a method of producing such a microlens array sheet.
Displays are classified into a direct-view type for direct-viewing images displayed on a cell assembly and a projection type for viewing images projected onto a screen by front or rear projection. The latter can be manufactured in a large type at low cost and are gradually popular, especially, in North America and Chaina.
A rear-projection display is a projection type. This type of display mostly employs a lenticular lens array sheet for its screen. The lenticular lens array sheet is, usually, produced by extrusion or injection molding, or press roll with a photocurable resin.
However, the lenticular lens array sheet has a problem in that it gives a wider angle of field only either a horizontal or vertical direction.
In order to solve such a problem, Japanese Un-examined Patent Publication No. 2001-305315 proposes a screen equipped with a light-shielding layer having a microlens array sheet with a lens function.
The microlens array sheet has microlens aligned on a flat base, as concave and convex sections of the base. A screen equipped with such a microlens array sheet is applicable to displays and expected to be popular in the near future.
Japanese Un-examined Patent Publication No. 2001-305315 discloses a microlens array sheet. Formed on a surface of a lens substrate is a plurality of microlens. Formed on the other surface of the substrate is a light-shielding layer having a circular or square light-emitting section.
The Un-examined Patent Publication gives one requirement (Sr≧2t×tanΘ+R) to the microlens array sheet, in which “Sr” is the size of the microlens, “t” is the thickness of the lens substrate, “Θ”, eqaul to sin−1 (1/n), is the maximum incident angle, “n” is a refractive index of the lens substrate, and “R” is the diameter of the light-emitting section.
However, a microlens array sheet designed according to the expression shown above sometimes causes optical vignetting, a phenomenon in which transmissivity (the amount of an outgoing beam/the amount of an incoming beam) is decreased when a part of an incoming beam incident along a correct optical path is blocked due to spherical aberration. This is because the above expression does not include a focal point of each microlens.
According to the expression, the maximum incident angle “Θ” depends the refractive index “n” of the lens substrate. Thus, an outgoing beam emitted from the light-emitting section originated from an incoming beam having the maximum incident angle “Θ” sometimes causes optical vignetting to other incoming beams.
Wider apertures for the light-shielding layer to avoid optical vignetting decreases a ratio of the area of black on the light-shielding layer to the total area of a light diffusion plate, thus causing lower contrast for projected images.
There is thus a demand for a microlens array sheet and a production method thereof that achieve both restriction of optical vignetting and enhancement of contrast inconsistent with each other.
A purpose of the present invention is to provide a high-performance microlens array sheet that exhibits high light transmissivity to offer high contrast images and a method of producing such a microlens array sheet.
The present invention provides a microlens array sheet comprising: a light-shielding base having a first surface and a second surface opposite to the first surface; and a microlens array attached to the first surface of the light-shielding base, the array having a plurality of microlens, wherein the light-shielding base has a plurality of apertures that correspond to the microlenses, each aperture having a conical trapezoid-like shape in which a size of each aperture on the first surface side is larger than another size of each aperture on the second surface side.
Moreover, the present invention provides a microlens array sheet comprising: a transparent base having a first surface and a second surface opposite to the first surface; a microlens array attached to the first surface of the transparent base, the array having a plurality of microlens, a light-shielding layer, having a third surface and a fourth surface opposite to the third surface, provided on the second surface of the transparent base, the light-shielding layer having a plurality of apertures that correspond to the microlenses, each aperture having a conical trapezoid-like shape in which a size of each aperture on the third surface side is larger than another size of each aperture on the fourth surface side.
Furthermore, the present invention provides a method of producing a microlens array sheet comprising the steps of: preparing a light-shielding base having a first surface and a second surface opposite to the first surface; attaching a microlens array having a plurality of microlens on the first surface of the light-shielding base so that a focal point of each microlens is located in the vicinity of the second surface of the light-shielding base, thus producing a microlens array base structure; and emitting a laser beam to the microlens array base structure so that the beam is focused onto the focal point of each microlens in a direction orthogonal to the light-shielding base, thus removing a part of the light-shielding base to form an aperture that correspond to each microlens, the aperture having a conical trapezoid-like shape in which a size of the aperture on the first surface side is larger than another size of the aperture on the second surface side.
Still, furthermore, the present invention provides a method of producing a microlens array sheet comprising the steps of: preparing a transparent base having a first surface and a second surface opposite to the first surface; attaching a microlens array having a plurality of microlens on the first surface of the transparent base; forming a light-shielding layer, having a third surface and a fourth surface opposite to the third surface, on the second surface of the transparent base so that the third surface faces the second surface; arranging the microlens so that a focal point of each microlens is located in the vicinity of the fourth surface of the light-shielding layer, thus producing a microlens array base structure; and emitting a laser beam to the microlens array base structure so that the beam is focused onto the focal point of each microlens in a direction orthogonal to the light-shielding layer, thus removing a part of the light-shielding layer to form an aperture that correspond to each microlens, the aperture having a conical trapezoid-like shape in which a size of the aperture on the third surface side is larger than another size of the aperture on the fourth surface side.
Preferred embodiments of a microlens sheet and a production method for such a microlens sheet according to the present invention will be disclosed with reference to the attached drawings.
The same reference signs or numerals are given to the same or analogous elements throughout figures. The figures are not drawn in scale and exaggerated particularly in the thickness direction for easier understanding.
A microlens sheet which is produced by a first embodiment of a production method disclosed below is equipped with a microlens array and a light-shielding layer provided on both sides of a transparent base.
The production method, as the first embodiment, includes formation of a microlens array on a transparent base (a first process), formation of a light-shielding layer on the transparent base (a second process), and self-alignment formation of apertures to the light-shielding layer (a third process).
(First Process)
The first process (formation of a microlens array on a transparent base) will be disclosed with reference to
Prepared first is a metal mold 2 having a plurality of concave and semisphere-like shape sections 1 each with 50 μm in radius “r1”, aligned at a pitch “L1” of 100 μm, by closest packing or injection, as shown in
Injected into the semisphere-like shape sections 1 is a UV (ultraviolet)-curable resin 3 that exhibits about 180 mPa·s in viscosity and 90% or higher in light transmissivity when cured. Employed as the resin 3 in this embodiment is TB3087B made by Three Bond. Co., Ltd.
The amount of the UV-curable resin 3 to be injected is adjusted so that the level “A” of the resin 3 is higher, by a height “t1”, than the level “B” of the opening of each semisphere-like shape section 1 of the metal mold 2. Although disclosed layer, the thickness of a transparent layer which is formed in the later stage is adjusted with the height “t1” of the resin 3 and also pressure in radiation of UV rays.
Although, the metal mold 2 has more semisphere-like shape sections 1 in actual application, it is shown in
Next, as shown in
The transparent base 4 is then peeled off or removed from the metal mold 2, as shown in
Obtained in this process is a microlens array base structure 8 formed on the transparent base 4, as having a microlens array 7 via a transparent layer 5, both made of the UV-cured resin 3. The microlens array 7 has a plurality of closest-packed, convex and semisphere-like shape microlenses 6 each with 50 μm in radius “r1”, aligned at a pitch “L1” of 100 μm. The height “t1” of the resin 3 and also the pressure in radiation of UV rays are adjusted to give a thickness “t3” of 5 μm to the transparent layer 5. The resin 3 exhibits 1.51 in refractive index “n1” after UV-cured.
Illustrated in
The succeeding processes will be disclosed as applied to the microlens array base structure 8 having the semisphere-like shape microlenses 6 each having a circular-like bottom arranged in a honeycomb pattern. However, the same processes can also be applied to the microlens array base structure 8a shown in
(Second Process)
The second process (formation of a light-shielding layer on the transparent base) will be disclosed with reference to
A UV-curable resin (that becomes an adhesive layer 9), the same as the resin 3 used in the first process, is applied onto a surface of the microlens array base structure 8, which is opposite to the surface with the microlens array 7 formed thereon. In this process, the resin is applied at a thickness which can be ignored in the total thickness in the structure.
Prepared in this process is a light-absorptive light-shielding layer 10 having a thickness “t4” of 50 μm made of, for example, a PET film including light-absorptive carbon black at a high percentage.
The light-shielding layer 10 is attached to the microlens array base structure 8 via the adhesive layer 9, with a laminator (not shown). The base structure 8 is then irradiated with non-collimated UV rays via the microlens array 7 so that the UV-curable resin is cured which causes the light-shielding layer 10 to be bonded to the base structure 8 via the adhesive layer 9.
Produced in this process is a microlens array and light-shielding layer base structure 11 having the total thickness “t5” of about 150 μm.
When a microlens-array sheet made of the microlens array and light-shielding layer base structure 11 is used in a rear-projection display, a light beam to be projected as an image is incident to the structure 11 via the microlens array 7 and then emitted therefrom via the light-shielding layer 10. This surface 14 of the layer 10 via which the light beam is emitted is referred to as a beam-outgoing surface in the following disclosure.
Through the first and second processes in the first embodiment, the microlens array 7 is formed first on one side of the transparent base 4 and then the light-shielding layer 10 on the other side of the base 4. However, the order of processes can be reversed in a way that the light-shielding layer 10 is formed first on one side of the base 4 and then the array 7 on the other side.
(Third Process)
The third process (self-alignment formation of apertures to the light-shielding layer) will be disclosed with reference to
As shown in
A much higher power for the laser beam 12 could damage the microlenses 6 by melting, sublimation or ablation (which will be discussed layer). The diameter of a laser spot of the beam 12 is thus adjusted so that minute self-aligned apertures 13 can be formed in the light-shielding layer 10, with no damages to the microlenses 6. There are the optimum requirements for the laser-spot adjustments, which will be discussed layer.
The laser beam 12 adjusted under the optimum requirements is incident to the light-shielding layer 10 via the microlens array 7, the transparent layer 5, and the transparent base 4. It removes a part of the layer 10 by melting, sublimation or ablation to form a plurality of self-aligned apertures 13, thus a microlense array sheet 15 (the first embodiment) being produced, as shown in
Although discussed later in detail, the total thickness “”t5” of the microlense array sheet 15 is adjusted so that a focal point “FP” of each microlense 6 is located in the vicinity of the beam-outgoing surface 14 of the light-shielding layer 10, as shown in
The term “ablation” is defined as explosive removal of a solid matter, such as, an organic or inorganic substance and a metal, with plasma emission and sonic boom. It happens due to evaporation caused by absorption heat generated when the solid matter is irradiated with a powerful laser beam.
Disclosed below in detail is a laser-processing method for the self-aligned apertures 13, with reference to
The laser beam 12 is adjusted so that a laser spot 16 has a radius “r2” larger than a radius “r1” of each microlens 6, as illustrated in
Discussed next is the shape of the self-aligned apertures 13 versus the scanning pitch “L” (one laser-processing requirement) of the laser beam 12.
Different self-aligned apertures 13 were formed according to the following four scanning-pitch requirements and observed under a transmission optical microscope and a laser microscope:
(A) scanning pitch: La=50 μm
(B) scanning pitch: Lb=40 μm
(C) scanning pitch: Lc=20 μm, and
(D) scanning pitch: Ld=10 μm
Each scanning pitch was achieved at a constant scanning speed of 10 m/s and a constant radius “r2” of 50 μm or larger for the laser spot 16. The diameter of 2×r2 (≧100 μm) of the spot 16 was much larger than each scanning pitch “L” (≦50 μm), for almost uniform laser intensity distribution over the microlens array 7. The radius “r1” of each microlens 6 was 50 μm under each laser-processing (scanning-pitch) requirement.
The sectional shape of each of the self-aligned apertures 13a and 13b formed under the laser-processing requirements (A) and (B), respectively, shown in
The sectional shape of the self-aligned apertures 13c formed under the laser-processing requirement (C) and shown in
The sectional shape of the self-aligned apertures 13d formed under the laser-processing requirement (D) and shown in
Discussed next with respect to
The microlens array and light-shielding layer base structure 11 is irradiated with the laser beam 12 such that the beam 12 is incident via the microlens array 7 in a direction orthogonal to the beam-outgoing surface 14 of the light-shielding layer 10.
As illustrated in
The thermal energy source 17e causes removal of a part of the light-shielding layer 10, by melting, sublimation or ablation, in the vicinity of the focal point “FP” (almost on the beam-outgoing surface 14 of the layer 10), which spreads towards the microlens array 7. The narrower the laser scanning pitch “L”, the larger the thermal energy, and hence, the wider the thermal energy source 17a to 17d along the laser path, from
This is a possible reason why the self-aligned apertures 13d were formed as a “reverse” conical trapezoid in its section at the scanning pitch “Ld” of 10 μm under the laser-processing (scanning-pitch) requirement (D).
The thermal energy given by the laser beam 12 increases under the laser-processing (scanning-pitch) requirements in the order from (A) to (D), with the wider thermal energy sources from 17a to 17d, as shown from
Moreover, the inventors of the present invention have confirmed that self-aligned apertures of almost an elliptic conical trapezoid in its sectional shape can be formed when semispherical microlenses cut from a spheroid material are used.
Accordingly, it is possible to form self-aligned apertures having a sectional shape that corresponds to a specific portion of each microlens that exhibits beam-converging effects.
Discussed next is the light transmission factor (in a visible-light range under consideration of relative visibility), the contrast of projected images, and the laser processability versus the sectional shape of self-aligned apertures.
Four samples in the table shown in
The table in
In the first embodiment, the laser processing requirement (D) with the scanning pitch “Ld” of 10 μm gives the self-aligned apertures 13d having the reverse conical trapezoid, such as, shown in
Discussed next with reference to the table in
In the same way as discussed above, a CO2 laser was adjusted to achieve an optimum scanning pitch “L” so that self-aligned apeertures had the reverse conical trapezoid in their sectional shapes, such as, shown in
The eight samples had the same shape and material as those shown in
Shown in the table in
The table in
Moreover, the inventors of the present invention have devoted themselves to examine the results discussed above and found a proportional relationship between the optimum thickness of the light-shielding layer 10 and the radius “r1” of each micorlens 6.
In detail, the radius “r1” of each micorlens 6 is, for example, 50 μm, in the first embodiment. Under the proportional relationship, the ranges from 1 to 75 μm and 2 to 50 μm for the thickness “t4” of the light-shielding layer 10 can be expressed as from 1 to 1.5×r1 μm and 2 to r1 μm, respectively.
Illustrated in
The light-shielding layer 10 with the thin thickness “t4a” in
In contrast, the light-shielding layer 10 with the thick thickness “t4b” in
Therefore, a preferable range for the thickness “t4” of the light-shielding layer 10, when the radius “r1” of each micorlens 6 is 50 μm (the first embodiment), is from 1 to 75 μm, or from 1 to 1.5×r1 μm, more preferably, from 2 to 50 μm, or from 2 to r1 μm.
Disclosed next, with reference to
A microlens sheet produced by the second embodiment of a production method is equipped with a microlens array provided on a light-absorptive light-shielding base.
The production method, as the second embodiment, includes formation of a microlens array on a light-absorptive light-shielding base (a first process) and self-alignment formation of apertures to the base (a second process).
(First Process)
The first process (formation of a microlens array on a light-absorptive light-shielding base) will be disclosed with reference to
Prepared first is a glass mold 22 having a plurality of concave and semisphere-like shape sections 21 each with 25 μm in radius “r21”, aligned at a pitch “L21” of 50 μm, by closest packing or injection, as shown in
Injected into the semisphere-like shape sections 21 is a UV-curable resin 23 that exhibits about 180 mpa·s in viscosity and 90% or higher in light transmissivity when cured. Employed as the resin 23 in this embodiment is TB3087B made by Three Bond. Co., Ltd.
Not only glass, the mold 22 may be made of any material , such as, plastic, that is transparent to UV rays.
The concave and semisphere-like shape sections 21 may be formed in the glass mold 22 by microblasting, wet etching, etc.
The amount of the UV-curable resin 23 to be injected is adjusted so that the level “C” of the resin 23 is higher, by a height “t21”, than the level “D” of the opening of each semisphere-like shape section 21 of the glass mold 22. Although disclosed layer, the thickness of a transparent layer which is formed in the later stage is adjusted with the height “t21” of the resin 23 and also pressure in radiation of UV rays.
Although, the glass mold 22 has more semisphere-like shape sections 21 in actual application, it is shown in
Next, as shown in
The light-shielding base 24 is then peeled off or removed from the glass mold 22, as shown in
Obtained in this process is a microlens array base structure 28 formed on the light-shielding base 24, as having a microlens array 27 via a transparent layer 25, both made of the UV-cured resin 23. The microlens array 27 has a plurality of closest-packed, convex and semisphere-like shape microlenses 26 each with 25 μm in radius “r21”, aligned at a pitch “L21” of 50 μm. The height “t21” of the resin 23 and also the pressure in radiation of UV rays are adjusted to give a thickness “t23” of 5 μm to the transparent layer 25. The resin 23 exhibits 1.51 in refractive index “n1” after UV-cured. The total thickness “t24” of the microlens array base structure 28 is about 75 μm.
When a microlens-array sheet made of the microlens array base structure 28 is used in a rear-projection display, a light beam to be projected as an image is incident to the structure 28 via the microlens array 27 and then emitted from a surface of the light-shielding base 24, on the opposite side of the base 24 with respect to the array 27. This surface 34 (shown in
Illustrated in
The succeeding processes will be disclosed as applied to the microlens array base structure 28 having the closest-packed semisphere-like shape microlenses 26 each having a circular-like bottom arranged in a honeycomb pattern. However, the same processes can also be applied to other microlens array base structures, such as, shown in
(Second Process)
The second process (self-alignment formation of apertures to the light-absorptive light-shielding base) will be disclosed with reference to
As shown in
A much higher power for the laser beam 32 could damage the microlenses 26 by melting, sublimation or ablation, like discussed in the first embodiment. The diameter of a laser spot of the beam 32 is thus adjusted so that minute self-aligned apertures 33 can be formed in the light-shielding base 24, with no damages to the microlenses 26. There are the optimum requirements for the laser-spot adjustments, which will be discussed layer.
The laser beam 32 adjusted under the optimum requirements is incident to the light-shielding base 24 via the microlens array 27 and the transparent layer 25. It removes a part of the base 24 by melting, sublimation or ablation to form a plurality of self-aligned apertures 33, thus a microlense array sheet 35 (the second embodiment) being produced, as shown in
Although discussed later in detail, the total thickness “t24” of the microlense array sheet 35 is adjusted so that a focal point “FP” of each microlense 26 is located in the vicinity of the beam-outgoing surface 34 of the light-shielding base 24, as shown in
A laser-processing method for the self-aligned apertures 33 is the same as that for the counterparts 13 explained with reference to
Discussed next is the shape of the self-aligned apertures 33 versus the scanning pitch “L” (one laser-processing requirement) of the laser beam 32.
Different self-aligned apertures 33 were formed according to the following four scanning-pitch requirements and observed under a transmission optical microscope and a laser microscope:
(E) scanning pitch: Le=25 μm
(F) scanning pitch: Lf=20 μm
(G) scanning pitch: Lg=20 μm, and
(H) scanning pitch: Lh=5 μm
As illustrated in
The sectional shape of each of the self-aligned apertures 33a and 33b formed under the laser-processing requirements (E) and (F), respectively, shown in
The sectional shape of the self-aligned apertures 33c formed under the laser-processing requirement (G) and shown in
The sectional shape of the self-aligned apertures 33d formed under the laser-processing requirement (H) and shown in
The reason why the self-aligned apertures in the light-shielding base 24 exhibit different sectional shapes depending on the laser-processing requirements is the same as that discussed with reference to
The inventors of the present invention have also confirmed in the second embodiment that self-aligned apertures of almost an elliptic conical trapezoid in its sectional shape can be formed when semispherical microlenses cut from a spheroid material are used.
Accordingly, it is possible to form self-aligned apertures having a sectional shape that corresponds to a specific portion of each microlens that exhibits beam-converging effects.
Discussed next, like in the first embodiment, is the light transmission factor (in a visible-light range under consideration of relative visibility), the contrast of projected images, and the laser processability versus the sectional shape of self-aligned apertures.
Four samples in the table shown in
The table in
In the second embodiment, the laser processing requirement (H) with the scanning pitch “Lh” of 5 μm gives the self-aligned apertures 33d having the reverse conical trapezoid, such as, shown in
Throughout the embodiments, the order of processes and the structures can be modified within the scope of the claims.
Microlenses applicable in the present invention are, for example, a spherical (including spheroid) micorlens, an aspherical microlens, and a cluster microlens having a larger lens with a smaller lens formed therein. One requirement for such microlenses applicable in the present invention is that they have a curvature and a focal point is located in the vicinity of a beam-outgoing surface of a light-shielding layer or base attached to them.
It is preferable for a light-shielding layer tightly attached to a microlens array via a transparent base, like the first embodiment, to exhibit a light-shielding and -absorbing capability to a laser-beam wavelength to be used and a visible-light range.
A light-shielding base, like used in the second embodiment, is usually made of a resin composition with a pigment, such as, carbon black and titanium black, or a black dye, dispersed or dissolved therein. It is also preferable for such a light-shielding base to exhibit a light-shielding and -absorbing capability to a laser-beam wavelength to be used and a visible-light range.
One requirement for the micorlens array sheet according to the present invention lies in the total thickness. The total thickness is defined as a distance from the lens summit to the beam-outgoing surface of the light-shielding layer via the transparent base (first embodiment) or to the beam-outgoing surface of the light-shielding base (second embodiment). The requirement is that the total thickness has to be adjusted so that a focal point of each micorlens is located in the vicinity of the beam-outgoing surface of the light-shielding layer or base.
In detail, for a microlens having a radius of “R” and made of a transparent resin material that exhibts 1.5 in refractive index “n1”, a focal length “f” is 3×R which is given by the following expression:
f=n1R/(n1−n0)=1.5R/0.5=3×R
wherein “n0” is the refractive index of air that is about 1.0.
The focal point of each micorlens has to be located in the vicinity of the beam-outgoing surface of the light-shielding layer or base, in this invention. It is, thus, required that the total thickness of the micorlens sheet is adjusted at about 3×R, or almost equal to the focal length of each micorlens.
Moreover, the thickness “t2” of the transparent base 4 in the first embodiment may be thinner as illustrated in
The laser beams 12 and 32, in the first and second embodiments, respectively, are preferably adjusted to have r≧R and L≦R for the radius “r” of the laser spot and the laser scanning pitch “L”, respectively, with respect to the radius “R” of each micorlens.
Several modifications to the first and second embodiments will be disclosed with reference to
Illustrated in
Illustrated in
Illustrated in
Illustrated in
Throughout
The transparent reinforcing base 37 may include a diffusing material for a wider angle of field when the modifications are used as a screen. Suitable materials for the transparent reinforcing base 37 are PMMA (polymethyl methacrylate), a copolymer of PMMA and styrene at a ratio of 6:4, etc.
The first and second embodiments employ a closest-packed microlens structure. Not only that, the present invention achieves advantages similar to these embodiments when microlenses are arranged with a given space. Moreover, the present invention achieves similar advantages when microlenses are arranged regularly or irregularly.
As disclosed in detail, the microlens array sheet according to the present invention is provided with a plurality of apertures on the light-shielding base or layer, each aperture having a (reverse) conical trapezoid-like shape in which the size of each aperture on the microlense array side is larger than that on the opposite side, thus exhibiting high light transmissivity to offer high contrast images.
Number | Date | Country | Kind |
---|---|---|---|
2004-376014 | Dec 2004 | JP | national |
2005-155135 | May 2005 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
6473238 | Daniell | Oct 2002 | B1 |
6594079 | Trott et al. | Jul 2003 | B1 |
Number | Date | Country |
---|---|---|
10-128563 | May 1998 | JP |
11-084105 | Mar 1999 | JP |
2001-305315 | Oct 2001 | JP |
2002-182309 | Jun 2002 | JP |
2002-287256 | Oct 2002 | JP |
Number | Date | Country | |
---|---|---|---|
20060139758 A1 | Jun 2006 | US |