Microwave dielectric ceramic

Abstract

A dielectric ceramic material consisting essentially of a composition of Formula 1 xATiO3(1−x)NdzRe(1−z)AlO3   (1) doped with 0.005% to 5% of a dopant selected from the group consisting of: cerium oxide, manganese oxide and mixtures thereof; wherein A may be selected from the group consisting of: Ca, Sr, Mg and mixtures thereof; Re may be selected from a group consisting of La, Sm, Pr, Dy, Er, Gd, Y and mixtures thereof; wherein z is from 0.95 to 0.995; and wherein x is a positive number less than 1.

Description

This application claims priority under 35 U.S.C. §119 to the following United Kingdom patent applications: No. 0516421.5, filed Aug. 10, 2005; No. 0518736.4, filed Sep. 14, 2005; and No. 0519804.9, filed Sep. 29, 2005.

This invention relates to a dielectric ceramic material and also to a dielectric resonator comprising the novel ceramic material, the resonator being particularly useful for microwave application.

According to the present invention there is provided a dielectric ceramic material consisting essentially of a composition of Formula 1:xATiO₃+(1−x)Nd_zRe_(1−z)AlO₃  (1)doped with about 0.005 wt % to about 5 wt % of a dopant selected from the group consisting of: cerium oxide, manganese oxide and mixtures thereof;wherein A may be selected from the group consisting of: Ca, Sr, Mg and mixtures thereof;Re may be selected from a group consisting of La, Sm, Pr, Dy, Gd, Y, Er and mixtures thereof;wherein z is from 0.95 to 0.995; andwherein x is a positive number less than 1.

Materials in accordance with this invention find application in microwave base station filters (single and multimode). Preferred materials may be prepared which allow changes to relative permittivity ε_r and TCf values while retaining Q values>10,000 at about 2 GHz suitable for their intended applications.

Preferred materials in accordance with this invention possess high relative permittivity ε_r values in comparison to known materials with equivalent Q values. Particularly preferred materials have ε_r of 42-50, Q>10,000, for example>14,000, at about 2 GHz (e.g., 2.7 GHz) and TCf between −10 to +10 MK⁻¹.

Materials in accordance with this invention possess further advantages in relation to materials disclosed in the prior art, for example U.S. Pat. No. 5,356,844, because the ceramics of this invention have an improved microwave quality factor at ambient and higher operating temperatures.

Preferred materials consist essentially of a composition of Formula 2:xCa_dSr_(1−d)TiO₃+(1−x)Nd_zRe_(1−z)AlO₃  (2)

• • doped with about 0.005% to about 5% of a dopant selected from the group consisting of: cerium oxide, manganese oxide and mixtures thereof;
    • wherein 0.5≦x≦0.9
      • 0.25≦d≦1.0
      • 0.95≦z≦0.995
      • 1≦y≦2
      • Re may be selected from a group consisting of La, Sm, Pr, Dy and mixtures thereof and wherein
      • CeO₂ is added as a dopant in the range about 50 ppm to about 2.5 wt %.
      • MnO_y is added as a dopant in the range about 50 ppm to about 2.5 wt %.

Further preferred materials consist essentially of a composition of Formula 3:xCaTi_1.03O₃+(1−x)Nd_0.95Re_0.05AlO₃  (3)

• • wherein 0.65≦x≦0.72; y and Re are as stated above and wherein
  • CeO₂ is added as a dopant in the range about 50 ppm to about 2.0 wt %.
  • MnO_y is added as a dopant in the range about 50 ppm to about 1.0 wt %.
  • In preferred materials the ratio of Nd:Re is about 19:1.

An additional dopant selected from Fe₂O₃, Nb₂O₅, Ta₂O₅, Ga₂O₃ and mixtures thereof preferably Ga₂O₃ may be present in an amount of about 20 to about 5000 ppm, more preferably about 20 to about 2000 ppm.

The manganese oxide may be provided as the oxide or mixture of oxides or as a carbonate, oxalate or other thermally labile derivative.

The Ca, Nd, Al, Ti site occupancies may all be varied by +/−10%. In this specification MnO_y refers to the material after firing. Most Mn salts may be used to achieve the final MnO_y.

The electrical properties for these ceramics can be summarised as follows:ε_r42−48

• • Q (2 GHz)>10,000
  • TCf (variable through composition)−10 to +10 MK⁻¹.

Compositions of the present invention may be manufactured by mixing the appropriate oxides, carbonates or oxalates or mixtures thereof in the above mentioned proportions, pulverising the mixture using a wet or dry method, calcining the mixture at a temperature of 1100° C. to 1400° C. for 1 to 16 hours, shaping the calcined mixture into an optional form and sintering the shaped body at a temperature of 1400° C. to 1700° C.

Percentages and other amounts referred to in this specification are by weight unless indicated otherwise.

The invention is further described by means of example but not in any limitative sense:

Experimental Procedure

All initial starting powders were of purity>99%. The raw materials were weighed in the appropriate quantities to form the compositions required. Deionised water or propan-2-ol was added to the weighed batches which were subsequently ball milled with magnesia stabilised zirconia milling media for 16 hours. Alternatively, the materials were attrition milled for 2 hours with yttria stabilised zirconia media. Subsequently, the raw material batches were dried at 80° C. and sieved through a 250 μm nylon mesh. The dried powder was calcined at temperatures in the interval 1100° C. to 1400° C. for 1 to 16 hours. The as-calcined powders were re-milled with 2 wt % PEG binder (MW 10000) for 8 hours, dried and sieved. Standard test samples of 9 g weight were uniaxially pressed in a 20 mm hardened stainless steel die using a pressure of˜150 MPa. Sintering of the pellets was performed between 1350 and 1600° C. for 1 to 48 hours under either an air or oxygen atmosphere. All samples were of density>95% theoretical density using the Archimedes water immersion technique.

The electrical properties were tested on the sintered components. Microwave dielectric properties were measured in reflection using the TE016 mode in a cubic silver plated cavity. TCf measurements were made in the interval +80° C. to −20° C. with the values of 60, 20 and −10° C. being used to calculate TCf. Er measurements were made using the parallel plate transmission technique of Hakki and Coleman.

EXAMPLE 1

Data mixtures of CaTiO₃ (CT) and Nd_0.95Sm_0.05AlO₃ (NSA); i.e a ratio of Nd to Sm of 19:1—aiming for a TCf between +6 and −6 MK⁻¹ were as shown in Table 1.

TABLE 1
Material	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.700 CT + 0.300 NSA	4.79	2.67	46.8	15300	40700	5.6
0.695 CT + 0.305 NSA	4.78	2.69	46.0	15300	41000	3.3
0.690 CT + 0.310 NSA	4.81	2.70	46.7	15300	41200	0.8
0.685 CT + 0.315 NSA	4.80	2.72	44.9	15300	41400	−1.5
0.680 CT + 0.320 NSA	4.83	2.74	45.3	15100	41400	−4.0

EXAMPLE 2

Variation in electrical properties as a function of Nd to auxiliary rare earth ratio: Properties of undoped CTNReA (0.700 CaTi_1.03O₃+0.300 Nd_0.9Re_0.1AlO₃) ceramics where the ratio of Nd to Re is equal to 9:1 are shown in Table 2.

TABLE 2
	Density/
Material	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
100% Nd2O3	4.77	2.67	46.6	15500	41400	6.0
Substitution of alternative rare earth for Nd in a ratio 10:1
CeO2	4.76	2.65	46.9	14700	39000	7.9
Sm2O3	4.77	2.68	46.6	15600	41600	6.1
Pr6O11	4.76	2.66	47.0	15500	41200	8.3
Dy2O3	4.78	2.68	46.4	14000	37400	6.8
Y2O3	4.71	2.68	46.2	14100	37700	5.3

EXAMPLE 3

Properties of undoped CTNReA (0.700 CaTi_1.03O₃+0.300 Nd_0.95Re_0.05AlO₃) ceramics where the ratio of Nd to Re is equal to 19:1 are shown in Table 3.

TABLE 3
	Density/
Material	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
100% Nd2O3	4.77	2.67	46.6	15500	41400	6.0
Substitution of alternative rare earth for Nd in a ratio 19:1
La2O3	4.74	2.66	46.9	15300	40700	6.6
Sm2O3	4.75	2.67	46.6	15300	40600	6.1
Pr6O11	4.75	2.66	46.9	15300	40700	6.9

EXAMPLE 4

Properties of doped CTNReA (0.690 CaTi_1.03O₃+0.310 [Nd,Sm]AlO₃+0.5 wt % CeO₂) ceramics where the ratio of Nd to Sm is greater than 19:1 are shown in Table 4.

TABLE 4
Nd:Sm	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
99:1	4.80	2.70	45.3	15800	42600	−0.6
49:1	4.79	2.71	45.4	15800	42800	−0.6
32:1	4.80	2.70	45.4	15700	42400	−0.2
24:1	4.80	2.71	45.3	15900	43000	−1.0
19:1	4.80	2.73	45.4	15500	42100	−0.5

EXAMPLE 5

Properties of undoped CTNReA (0.700 CaTi_1.03O₃+0.300 Nd_0.05Re_0.95AlO₃) ceramics where the ratio of Nd to Re is equal to 1:19 are shown in Table 5.

TABLE 5
	Density/
Material	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
100% Nd2O3	4.77	2.67	46.6	15500	41400	6.0
Substitution of alternative rare earth for Nd in a ratio 1:19
La2O3	4.65	2.57	49.9	14000	35850	22.0
Sm2O3	4.81	2.69	45.7	15200	40900	7.9
Pr6O11	4.68	2.60	48.8	14300	37200	24.9

EXAMPLE 6

Properties of undoped CTNPrA (0.660 CaTi_1.03O₃+0.340 [Nd,Pr]AlO₃) ceramics where the ratio of Nd to Pr is varied for zero TCf are shown in Table 6.

TABLE 6
Nd:Pr	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
1:19.0	4.84	2.76	44.0	14500	39800	1.1
1:18.0	4.80	2.73	44.8	14100	38500	6.6
1:17.0	4.76	2.70	45.7	13900	37400	13.0
1:16.0	4.72	2.66	46.8	13400	35700	20.0
1:15.5	4.70	2.65	47.5	12900	34200	25.5

EXAMPLE 7

Single doping of zero TCf material where Nd:Sm is 19:1.

Base material: 0.690 CaTi_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃

The data for MnO₂ doping are shown in Table 7(a)

TABLE 7(a)
	Density/
wt % MnO2	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.000	4.79	2.70	45.7	15300	41200	0.8
0.005	4.78	2.71	45.7	15300	41500	1.0
0.010	4.78	2.70	45.7	15400	41500	0.9
0.050	4.78	2.70	45.7	15000	40400	0.9
0.100	4.78	2.70	45.7	15000	40400	1.0
0.250	4.78	2.70	45.7	14200	38400	0.9

The data for CeO₂ doping are shown in Table 7(b)

TABLE 7(b)
	Density/
wt % CeO2	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.000	4.79	2.70	45.7	15300	41200	0.8
0.005	4.79	2.70	45.7	15600	42200	0.8
0.010	4.80	2.71	45.4	15600	42200	0.8
0.050	4.81	2.70	45.5	15700	42400	0.7
0.100	4.80	2.71	45.4	15600	42400	0.4
0.200	4.79	2.70	45.3	15700	42400	0.1
0.500	4.81	2.71	45.2	15700	42500	−0.7

The data for Co-doping with CeO₂ & MnO₂ are shown in Table 7(c)

TABLE 7(c)
wt % CeO2 &	Density/
% MnO2	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.00 & 0.00	4.79	2.70	45.7	15300	41200	0.8
0.01 & 0.01	4.78	2.70	45.5	15300	41200	0.8
0.03 & 0.03	4.78	2.70	45.5	15200	41100	0.8
0.05 & 0.05	4.78	2.70	45.6	15200	40900	0.8
0.01 & 0.05	4.78	2.69	45.5	15300	41300	0.8
0.05 & 0.01	4.78	2.70	45.6	15100	40700	1.0

EXAMPLE 8

Single doping of zero TCf material where Nd:Sm or Nd:Pr is 1:19.

Base material: 0.690 CaTi_1.03O₃+0.310 Nc_0.05Sm_0.95AlO₃

TABLE 8(a)
	Density/
wt % CeO2	g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.0	4.86	2.73	44.6	15400	42100	2.8
0.1	4.86	2.74	44.6	15300	41700	2.8
0.2	4.85	2.74	44.4	15400	42100	2.3
0.5	4.86	2.75	44.3	15500	42400	1.5

Base material: 0.660 CaTi_1.03O₃+0.340 Nd_0.05Pr_0.95AlO₃

TABLE 8(b)
wt %
CeO2	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.0	4.84	2.76	44.0	14500	39800	1.1
0.1	4.82	2.76	43.9	14400	39800	0.6
0.5	4.83	2.76	43.7	14500	40000	0.7

EXAMPLE 9

Additional doping trials:

(a) Fe₂O₃

Fe₂O₃ was added as an excess to the composition 0.690 CaTi_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃.

TABLE 9(a)
wt %
Fe2O3	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.000	4.79	2.70	45.7	15300	41200	0.8
0.005	4.77	2.69	45.7	15500	41700	1.2
0.010	4.77	2.69	45.7	15500	41700	1.3
0.050	4.77	2.69	45.7	15300	41100	1.5
0.100	4.78	2.69	45.7	15100	40500	1.6
0.500	4.77	2.69	45.8	13400	36200	2.3

(b) SrO

SrO was added as a substitution for Ca in the composition 0.690 (Ca,Sr)Ti_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃+0.2 wt % excess CeO₂.

TABLE 9(b)
mol % SrO	Density/g cm−3	f/GHz	εr	Q	Qf/GHz
0.0	4.79	2.70	45.7	15300	41200
1.0	4.77	2.69	45.9	14900	40200
2.0	4.79	2.69	45.9	15100	40500
5.0	4.82	2.70	46.1	14500	39200
10.0	4.86	2.68	46.7	14100	37800
20.0	4.93	2.67	47.6	12700	34000

(c) Nb₂O₅

Nb₂O₅ was added an excess to the composition 0.690 CaTi_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃

+0.2 wt % excess CeO₂.

TABLE 9(c)
wt %
Nb2O5	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.0	4.79	2.70	45.7	15300	41200	0.8
0.1	4.77	2.70	45.7	15600	42100	1.2
0.2	4.77	2.70	45.7	15600	42000	1.3
0.5	4.77	2.70	45.9	15300	41200	1.5

(d) Ta₂O₅

Ta₂O₅ was added an excess to the composition 0.690 CaTi_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃

+0.2 wt % excess CeO₂.

TABLE 9(d)
wt %
Ta2O5	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.0	4.79	2.70	45.7	15300	41200	0.8
0.1	4.78	2.71	45.6	15600	42300	1.0
0.2	4.78	2.69	45.7	15600	41900	1.2
0.5	4.78	2.70	45.7	15700	42500	1.1

(e) Ga₂O₃

Ga₂O₃ was added as both an excess and a substitute for Ti in the composition 0.690 CaTi_1.03O₃+0.310 Nc_0.95Sm_0.05AlO₃+0.2 wt % excess CeO₂.

TABLE 9(e)
	Density/					TCf/
% Ga2O3	g cm−3	f/GHz	εr	Q	Qf/GHz	MK−1
0.000	4.79	2.70	45.7	15300	41200	0.8
0.005 on Ti site	4.77	2.70	45.4	16100	43500	−0.1
0.010 on Ti site	4.77	2.70	45.1	16200	43800	−0.8
0.100 wt % excess	4.77	2.70	45.6	15900	42700	1.0
0.200 wt % excess	4.77	2.69	45.7	15900	42700	1.1
0.500 wt % excess	4.77	2.69	45.6	15700	42200	1.5

EXAMPLE 10

Influence of cation stoichiometry upon electrical properties:

(a) Ca

The composition range examined was 0.690 Ca_zTi_1.03O₃+0.310 Nd_0.95Sm_0.05AlO₃+0.2 wt % excess CeO₂, where z varied between 0.95 and 1.05.

TABLE 10(a)
z Ca	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.95	4.78	2.67	46.8	14000	37400	6.8
0.97	4.78	2.68	46.4	14500	38800	4.4
0.99	4.78	2.69	46.0	15100	40700	1.9
1.00	4.79	2.70	45.7	15300	41200	0.8
1.01	4.77	2.71	45.2	15600	42100	−0.7
1.03	4.61	2.76	42.5	12600	34700	−2.0
1.05	4.74	2.74	44.2	14700	40300	−4.7

(b) Ti

The composition range examined was 0.690 CaTi_zO₃+0.310 Nd_0.95Sm_0.05AlO₃+0.2 wt %

excess CeO₂, where z varied between 0.98 and 1.08.

TABLE 10(b)
z Ti	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.98	4.76	2.78	43.0	14400	40000	−9.7
1.00	4.69	2.78	42.9	12400	34300	−5.3
1.02	4.78	2.72	45.1	15500	42200	−1.5
1.03	4.79	2.70	45.7	15300	41200	0.8
1.04	4.78	2.70	46.2	15100	40600	2.9
1.06	4.78	2.66	47.0	14500	38400	7.6
1.08	4.79	2.64	48.0	13900	36500	12.2

(c) Al

The composition examined was 0.690 CaTi_1.03O₃+0.310 Nd_0.95Sm_0.05Al_zO₃+0.2 wt % excess CeO₂, where z varied between 0.95 and 1.05.

TABLE 10(c)
z Al	Density/g cm−3	f/GHz	εr	Q	Qf/GHz	TCf/MK−1
0.95	4.46	NR	—	—	—	—
0.97	4.78	2.70	45.7	15400	41500	0.4
0.99	4.78	2.70	45.6	15600	41900	0.4
1.00	4.79	2.70	45.7	15300	41200	0.8
1.01	4.78	2.70	45.6	15400	41600	0.7
1.03	4.78	2.70	45.6	15400	41400	1.1
1.05	4.78	2.71	45.5	15100	40800	1.4
NR—no resonance detected

EXAMPLE 11

1 and 2 GHz parts:

Commercial size resonators were developed from the following composition:0.69CaTi_1.03O₃+0.31Nd_0.95Sm_0.05AlO₃+0.2 wt % excess CeO₂.   Comp A

The electrical response of ceramics prepared from the above composition A were evaluated against an undoped material of composition:0.69CaTi_1.03O₃+0.31NdAlO₃  Comp B

The measured Q-values were as follows:

	TABLE 11
	Freq/GHz	Comp A	Comp B	% Differential
	1.0	34600	33000	4.6
	2.0	21000	20300	3.3
	2.7	16000	15600	2.5

EXAMPLE 12

Dopant and influence on Q-value at elevated temperatures:

• • Composition: Comparison of Q-value at ambient and elevated temperature for compositions A and B (0.69 CaTi_1.03O₃+0.31 Nd_0.95Sm_0.05AlO₃)

TABLE 12
Temperature/″ C.	Q-value of Comp A	Q-value of Comp B
22	16000	15600
80	13900	13500
120	12800	12400
150	12000	11600

Although the foregoing invention has been described in some detail for purposes of clarity of understanding, it will be apparent that certain changes and modifications may be practiced within the scope of the appended claims. It should be noted that there are many alternative ways of implementing the compositions of the present invention. Accordingly, the present embodiments are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details given herein, but may be modified within the scope and equivalents of the appended claims.

The entire disclosures of all references cited herein are incorporated by reference for all purposes.

Claims

1. A dielectric ceramic material consisting essentially of a composition of formula 1: xATiO3+(1−x)NdzRe(1−z)AlO3  (1)

2. A dielectric ceramic material as claimed in claim 1 with a composition of formula 2: xCadSr(1−d)TiO3+(1−x)NdzRe(1−z)AlO3  (2)

3. A dielectric ceramic material as claimed in claim 1 with a composition of formula 3: xCaTi1.03O3+(1−x)Nd0.95Re0.05AlO3  (3)wherein 0.60≦x≦0.72 and y are as stated above and Re is Sm or Pr and whereinCeO2 is added as a dopant in the range about 50 ppm to about 2.5 wt %, andMnOy is added as a dopant in the range about 50 ppm to about 2.5 wt %.

4. A dielectric ceramic material as claimed in claim 3, wherein 0.65≦x≦0.72, Re is Smand CeO2 is added as an excess dopant in an amount of 0.2 wt %.

5. A dielectric ceramic material as claimed in claim 1 with a composition of formula 4: xCaTi1.03O3+(1−x)Nd0.05Re0.95AlO3  (4)wherein 0.60≦x≦0.72 and y are as stated above and Re is Sm or Pr and whereinCeO2 is added as a dopant in the range about 50 ppm to about 2.5 wt %, andMnOy is added as a dopant in the range about 50 ppm to about 2.5 wt %.

6. A dielectric ceramic material as claimed in claim 5, wherein 0.60≦x≦0.72, Re is Smand CeO2 is added as an excess dopant in an amount of from 0.01 wt % to 1.0 wt %.

7. A dielectric ceramic material as claimed in claim 5, wherein 0.60≦x≦0.72: Re is Prand CeO2 is added as an excess dopant in an amount of from 0.01 wt % to 1.0 wt %.

8. A dielectric ceramic material as claimed in claim 3 wherein Sr, Mg or a mixture thereof are substituted for Ca in an amount of 0 to 20 mol % and wherein 0.85≦x≦1.0.

9. A dielectric ceramic material as claimed in claim 1, further comprising an additional dopant in an amount of 20 to 5000 ppm, wherein the additional dopant is selected from the group consisting of: Fe2O3, Nb2O5, Ta2O5, Ga2O3 and mixtures thereof.

10. A dielectric ceramic material as claimed in any preceding claim 2, including further comprising an additional dopant in an amount of 20 to 5000 ppm, wherein the additional dopant is selected from the group consisting of: Fe2O3, Nb2O5, Ta2O5, Ga2O3 and mixture thereof.

11. A dielectric ceramic material as claimed in any preceding claim 3, including further comprising an additional dopant in an amount of 20 to 5000 ppm, wherein the additional dopant is selected from the group consisting of: Fe2O3, Nb2O5, Ta2O5, Ga2O3 and mixture thereof.

12. A dielectric ceramic material as claimed in claim 9, wherein the additional dopant is Ga2O3.

13. A dielectric ceramic material as claimed in claim 12, wherein the amount of Ga2O3 is from 20 to 2000 ppm.

14. A dielectric ceramic material as claimed in claim 3, wherein the cation site occupancy of Ca, Ti, Nd and Al is varied by ±10%.

15. A dielectric ceramic material as claimed in claim 1, wherein the material has electrical properties summarised as follows: εr42−48Q (2 GHz)>10,000TCf (variable through composition)−10 to +10 MK−1.

16. A dielectric ceramic material as claimed in claim 1, wherein the material has electrical properties summarised as follows: εr42−48Q (2.7 GHz)>14,000TCf (variable through composition)−10 to +10 MK−1.

17. A dielectric resonator comprising a dielectric ceramic material as claimed in claim 1.

18. A dielectric resonator as claimed in claim 17 with a composition of formula 2.

19. A dielectric resonator as claimed in claim 17 with a composition of formula 3.

20. A dialectic resonator as claimed in claim 17, wherein the dielectric ceramic material has electrical properties summarised as follows: εr42−48Q (2 GHz)>10,000TCf (variable through composition)−10 to +10 MK−1.