Microwave dielectric composition and method for preparing the same

Information

  • Patent Grant
  • 6028021
  • Patent Number
    6,028,021
  • Date Filed
    Tuesday, June 30, 1998
    26 years ago
  • Date Issued
    Tuesday, February 22, 2000
    24 years ago
Abstract
A microwave dielectric composition superior in all dielectric constant, product of resonant frequency by quality coefficient and temperature-dependent coefficient of resonant frequency, can be prepared by mixing a main oxide formulation consisting of lead oxide, calcium oxide, zirconium oxide and tin oxide with manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O), calcining the mixture at a temperature of about 1,000 to 1,200.degree. C., pulverizing and molding the mixture, and sintering the molded body at a temperature of about 1,200 to 1,550.degree. C. in an oxygen atmosphere. It is 100 or greater in dielectric constant, 4,000 or greater in the product of resonant frequency by quality coefficient and .+-.3 mmp/.degree. C. or less in temperature-dependent coefficient of resonant frequency.
Description

BACKGROUND OF THE INVENTION
1. Field of the invention
The present invention relates to a microwave dielectric composition and a preparing method therefor. More particularly, the present invention relates to a microwave dielectric composition superior in all dielectric constant, product of resonant frequency by quality coefficient and temperature-dependent coefficient of resonant frequency. Also, the present invention is concerned with a method for preparing such a microwave dielectric composition.
2. Description of the Prior Art
Today, various microwave dielectric compositions are used in high frequency integrated circuits or dielectric resonators. In addition, the exploitation for ever higher frequency in high frequency band has been continuous. Together with the availability of high frequency, the tendency toward simpleness, thinness, shortness and smallness in electromagnetic appliances, has made the demand for the microwave dielectric composition which is more improved in dielectric constant and quality coefficient.
To meet the demand, J. Kato et al. developed a microwave dielectric composition comprising lead oxide (PbO), calcium oxide (CaO) and zirconium oxide (ZrO.sub.2) through an oxide mixing technique, as reported in Jpn. J. Appl. Phsy. 30(9B) 2343(1991) and 32(9B) 4356(1993). The compositions are found to be superior in individual dielectric constant, temperature coefficient of resonant frequency and the product of quality coefficient by resonant frequency but not in all of the properties. Accordingly, the compositions of J. Kato et al. are not suitable for use in microwave dielectric appliances, in practice.
SUMMARY OF THE INVENTION
It is, therefore, an object of the present invention to overcome the above problems encountered in prior arts and to provide a microwave dielectric composition superior in all dielectric constant, product of resonant frequency by quality coefficient and temperature-dependent coefficient of resonant frequency.
It is another object of the present invention to provide a method for preparing such a micrwave dielectric composition.
In accordance with an aspect of the present invention, there is provided a microwave dielectric composition comprising the oxides of lead (Pb), calcium (Ca), zirconium (Zr) and tin (Sn) in combination of an oxide of manganese (Mn).
In accordance with another aspect of the present invention, there is provided a method for preparing a microwave dielectric composition, in which a main oxide formulation consisting of lead oxide, calcium oxide, zirconium oxide and tin oxide is mixed with manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O), calcined at a temperature of approximately 1,000 to 1,200.degree. C., pulverized and molded, and sintered at a temperature of approximately 1,200 to 1,550.degree. C. in an oxygen atmosphere.
DETAILED DESCRIPTION OF THE INVENTION
The microwave dielectric composition of the present invention is based on (Pb.sub.1-x Ca.sub.x)(Zr.sub.1-y Sn.sub.y)O.sub.3 wherein x and y each represent a mole fraction, in combination with water-soluble manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O). In more detail, manganese oxide (MnO) is added in the form of hydrous manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O at an amount less than 3% by weight on the basis of 100 parts by weight of the main composition comprising lead oxide (PbO), calcium oxide (CaO), zirconium oxide (ZrO.sub.2) and tin oxide (SnO.sub.2) when reduced into the weight of the oxides.
It is preferred that x is between 0.15 and 0.40. For example, if x is below 0.1, the resulting microwave dielectric composition has a low product of quality coefficient by resonant frequency. On the other hand, if x exceeds 0.40, the microwave dielectric composition is improved in the product of quality coefficient by resonant frequency, but poor in dielectric constant.
As for y, it is preferable to be between 0.15 and 0.50. For example, if y is below 0.15, the resulting microwave dielectric composition has a temperature-dependent coefficient of resonant frequency less than -10 mmp/.degree. C. On the other hand, if y is over 0.5, the temperature-dependent coefficient of resonant frequency increases to +10 mmp/.degree. C. or greater.
The amount of the additive element MnO is very important to the properties of the microwave dielectric composition. For example, when the additive element is present at an amount exceeding the allowable range, the resulting microwave dielectric composition is deteriorated in sintering property and quality coefficient.
In accordance with the present invention, the precise adjustment of the additive element can be possible by taking advantage of hydrous manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O).
When a composition comprising 0.65 mol of lead oxide (PbO), 0.35 mol of calcium oxide (CaO), 0.79 mol of zirconium oxide (ZrO.sub.2), 0.21 mol of tin oxide (SnO.sub.2), and 0.5% by weight of hydrous mianganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O), is sintered at a temperature of 1,350.degree. C., a superior microwave dielectric composition can be obtained which is 130 or greater in dielectric constant at 5 GHz, 500 in the product of quality coefficient by resonant frequency, and 1 mmp/.degree. C. in temperature-dependent coefficient of resonant frequency.





A better understanding of the present invention may be obtained in light of the following examples which are set forth to illustrate, but are not to be construed to limit, the present invention.
EXAMPLES 1 TO 8 & COMPARATIVE EXAMPLES 1 TO 4
Main compositions consisting of lead oxide (PbO), calcium oxide (CaO), zirconium oxide (ZrO.sub.2) and tin oxide (SnO.sub.2), each being 99% or higher in purity, and manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O) were weighed as indicated in the following Table 1. Thereafter, they were mixed by using a nylon jar and zirconium oxide balls for 2 hours in a planetary mill. At that moment, distilled water was used as a dispersing medium. The slurries thus obtained were dried before calcination at a temperature of approximately 1,000 to 1,200.degree. C. according to their compositions and then, pulverized into powders with appropriate sizes.
The powders were molded to specimens with a diameter of 8.0 mm and a thickness of 3.5 mm by dry-pressing under 1 MPa.
In an oxygen atmosphere, the specimens were sintered at a temperature of approximately, 1,200 to 1,550.degree. C. Unless the specimens were sintered in an oxygen atmosphere, their quality coefficients were poor.
The additive water-soluble manganous nitrate (Mn(NO.sub.3).sub.2.4H.sub.2 O) was advantageous in that it can be homogeneously diffused throughout the powders during the calcination or sintering.
TABLE 1__________________________________________________________________________Properties of Microwave Dielectric Compositions Main Comp. Dielec. (mol) Addi. Sinter Const Examp. Pb.sub.1-x Ca.sub.x Zr.sub.1-y Sn.sub.y)O.sub.3 MnO* Temp. at 5 GHz .tau..sub.fNos. x y (wt %) (.degree. C.) (K) Qxf (ppm/.degree. C.)__________________________________________________________________________1 0.29 0.30 1.0 1300 120 4500 3 2 0.31 0.25 2.0 1350 110 4200 2 3 0.33 0.32 1.5 1320 105 4700 -1 4 0.30 0.40 2.0 1280 103 5500 0 5 0.30 0.35 1.3 1300 125 5200 4 6 0.25 0.40 1.0 1200 110 8000 -2.5 7 0.35 0.21 0.5 1350 130 5300 1 8 0.18 0.42 0.1 1400 140 5200 1C.1 0.10 0.10 . 1300 unable to be sinteredC.2 0.20 0.30 . 1320 120 2500 4 C.3 0.30 0.60 . 1100 80 3000 20 C.4 0.50 0.30 0.1 1400 70 2400 80__________________________________________________________________________ *added in the form of manganous nitrate (Mn(NO.sub.3.4H.sub.2 O)
After being polished to have a smooth surface, the sintered specimens were measured for dielectric constant, quality coefficient and temperature-dependent coefficient of resonant frequency in an open cavity manner.
From the data of Table 1, it is apparent that the microwave dielectric composition of the present invention is 100 or greater in dielectric constant, 4,000 or greater in the product of resonant frequency by quality coefficient and .+-.3 mmp/.degree. C. or less in temperature-dependent coefficient of resonant frequency.
As described hereinbefore, the microwave dielectric composition prepared according to the present invention is superior in all dielectric constant, product of resonant frequency by quality coefficient and temperature-dependent coefficient of resonant frequency on the account that the water-soluble additive manganous nitrate (Mn(NO.sub.3).4H.sub.2 O) can be precisely added.
Other features, advantages and embodiments of the invention disclosed herein will be readily apparent to those exercising ordinary skill after reading the foregoing disclosures. In this regard, while specific embodiments of the invention have been described in considerable detail, variations and modifications of these embodiments can be effected without departing from the spirit and scope of the invention as described and claimed.
Claims
  • 1. A microwave dielectric composition consisting essentially of the main composition of lead oxide (PbO), calcium oxide (CaO), zirconium oxide (ZrO.sub.2) and tin oxide (SnO.sub.2), expressed by the formula (Pb.sub.1-x Ca.sub.x)(Zr.sub.1-y Sn.sub.y)O.sub.3, wherein x and y each represent a mole fraction under the condition of 0.15<x<0.40 mol. and 0.15<y<0.50 mol, and oxide of manganese as an additive wherein the amount of additive is less than 3% by weight on the basis of 100 parts by weight of a main composition.
  • 2. A microwave dielectric composition, comprising the oxides of lead (Pb), calcium (Ca), zirconium (Zr), and tin (Sn), wherein said oxides are represented by the following formula:
  • (Pb.sub.1-x)Ca.sub.x)(Zr.sub.1-y Sn.sub.y)O.sub.3
  • wherein x and y each represent a mole fraction under the condition of 0.15<x<0.40 mol. and 0.15<y<0.50 mol, in combination with an oxide of manganese (Mn).
  • 3. A method for preparing a microwave dielectric composition, in which a main oxide formulation of lead oxide, calcium oxide, zirconium oxide and tin oxide expressed by the formula (Pb.sub.1-x Ca.sub.x)(Zr.sub.1-y Sn.sub.y)O.sub.3, wherein x and y each represent a mole fraction under the condition of 0.15<x<0.40 mol. and 0.15<y<0.50, is mixed with manganous nitrate(Mn(NO.sub.3).sub.2.4H.sub.2 O), calcined at a temperature of approximately 1,000 to 1,200.degree. C., pulverized and molded, and sintered at a temperature of approximately 1,200 to 1,550.degree. C. in an oxygen atmosphere.
Priority Claims (1)
Number Date Country Kind
97-30876 Jul 1997 KRX
US Referenced Citations (4)
Number Name Date Kind
4550088 Park et al. Oct 1985
4992398 Huang et al. Feb 1991
5219809 Kato et al. Jun 1993
5756412 Lee et al. May 1998
Non-Patent Literature Citations (2)
Entry
Kato et al., "Dielectric Properties of Lead Alkaline-Earth Zirconate at Microwave Frequencies," Japanese Journal of Applied Physics, vol. 30, No. 9B (1991), pp. 2343-2346 No Month.
Kato et al., "Crystal Structure Refinement of (Pb.sub.1- .sub.x Ca.sub.x) ZrO.sub.3 by the Rietvelt Method," Japanese Journal of Applied Physics, vol. 32, No. 9B (1993), pp. 4356-4359 No Month.