Patent Application
20200263277
The present invention relates to a process for recovering valuable products from ore containing boron and lithium.
The present invention relates more particularly although not exclusively to a process for recovering valuable products from jadarite ore.
The valuable products include any one or more than one of boron-containing, lithium-containing and sodium-containing compounds, by way of example only, boric acid, lithium carbonate, lithium hydroxide, sodium sulfate, and sodium borate.
As noted above, the present invention relates more particularly although not exclusively to a process for recovering valuable products from jadarite ore.
The term “jadarite ore” is understood herein to mean ore containing jadarite mineral.
The Jadar basin in Serbia has a significant resource of a mineral that contains high boron and lithium concentrations. The mineral has been named jadarite after the Jadar Basin region.
The term “jadarite” is understood herein to mean “jadarite mineral”.
The Jadar basin resource also contains several major and minor mineralizations of borates, most notably, NaB (a sodium borate which is predominantly ezcurrite, kernite and tincal), colemanite and searlesite.
The invention applies to all borate and lithium containing minerals that are associated with jadarite, because it is likely that the minerals will be processed with jadarite.
Jadarite is a white, earthy monoclinic silicate mineral having a chemical formula expressed as LiNaB3SiO7(OH) or LiNaSiB3O7(OH) or Na2OLi2O(SiO2)2(B2O3)3H2O.
The invention is concerned with recovering valuable products, including lithium-containing and boron-containing products, from jadarite ore.
The valuable products include, for example, boric acid and lithium carbonate. The valuable products also include, for example, sodium sulfate, lithium hydroxide and sodium borate.
Lithium is used in a vast array of products, most notably, batteries for hybrid and electric cars.
Borates are essential building blocks for heat resistant glass, fibreglass, ceramics, fertilisers, detergents, wood preservatives and many other household and commercial products. They are used in insulation that makes buildings energy-efficient, and to produce TV, computer and smartphone screens.
The above description is not to be taken as an admission of the common general knowledge in USA, Australia or elsewhere.
In broad terms, the invention relates to a process for recovering valuable products from ore containing boron and lithium, such as jadarite ore, that includes an acid digestion step and downstream steps that recover valuable products.
In more detailed, although not exclusive, terms, the invention relates to a process for recovering valuable products from jadarite ore that includes the steps of:
(a) beneficiating a mined or stockpiled jadarite ore and producing a jadarite concentrate,
(b) digesting the concentrate in an acid and taking boron and lithium into solution in a digestion liquor, and,
(c) subsequent steps to separate valuable boron-containing and lithium-containing products from the digestion liquor.
The beneficiation step (a) may include attrition scrubbing mined or stockpiled jadarite ore in an aqueous or other suitable medium under high solids concentration (typically above 50% solids by weight) such that harder minerals like jadarite preferentially slake and attrite softer gangue minerals such as clay, calcite, dolomite, ankerite etc. thereby preferentially reducing the size of the gangue minerals.
The beneficiation step (a) may include a size separation step that separates the gangue minerals degraded during the attrition scrubbing step from jadarite and other harder minerals that remain during the attrition scrubbing step, thereby achieving a grade increase of jadarite in the concentrate.
The digestion step (b) may include digesting the jadarite concentration in sulphuric acid.
The sulphuric acid may be concentrated sulfuric acid.
The subsequent steps (c) may include any suitable series of successive steps to remove valuable products from the digestion liquor.
The selection of the series of steps and the valuable products will depend on a range of factors, including but not limited to requirements for process optimisation.
The valuable products may include any one or more than one of boron-containing, lithium-containing, and sodium-containing products.
The valuable products may include, by way of example only, any of boric acid, lithium carbonate, lithium hydroxide, sodium borate, and sodium sulfate.
The subsequent steps (c) may include precipitating boron-containing and lithium-containing products successively from solution in the digestion liquor.
The subsequent steps (c) may include precipitating or removing non-valuable impurities successively from solution in the digestion liquor.
The subsequent steps (c) may include precipitating boric acid and lithium carbonate successively from solution in the digestion liquor.
The subsequent steps (c) may also include precipitating a sodium-containing product from solution in the digestion liquor.
The subsequent steps (c) may also include precipitating sodium sulfate from solution in the digestion liquor.
The subsequent steps (c) may include precipitating boric acid, lithium carbonate, and sodium sulfate successively from solution in the digestion liquor.
The subsequent steps (c) may include a boric acid crystallisation step.
The boric acid crystallisation step may include evaporating the digestion liquor to increase the boric acid concentration to a predetermined concentration. The predetermined concentration may be any suitable concentration. By way of example, the predetermined concentration may be 20-25% boric acid in the digestion liquor on a weight basis.
The boric acid crystallisation step may include nitrogen blanketing and treatment with reducing and chelating agents such as sodium dithionite, oxalic acid, di-sodium ethylene diamine tretraacetic acid and sulfuric acid in the range of 1-10 g/L prior to crystallization to control iron contamination of the boric acid.
The boric acid crystallisation step may include cooling, for example flash cooling, the digestion liquor to precipitate boric acid crystals from the digestion liquor and separating the boric acid crystals from the digestion liquor.
The flash cooling step may be carried out in multiple stages.
The flash cooling step may cool the digestion liquor to ambient or less than ambient temperature. The temperature may be a minimum of 5° C. The temperature may be a maximum of 35° C. Typically, the temperature is in a range of 15-35° C.
The subsequent steps (c) may include precipitating boric acid and sodium sulfate decahydrate (Glauber's salt) in the same precipitation vessel.
The boric acid/sodium sulfate decahydrate mix may be passed directly to a sodium sulfate precipitation step.
The boric acid/sodium sulfate decahydrate precipitation step may include partial separation of the boric acid and sodium sulfate decahydrate, either within the precipitation vessel, or in a downstream separation unit, such as a centrifuge.
A boric acid rich stream produced from the partial separation of the boric acid/sodium sulfate decahydrate mix may be returned to the boric acid crystallisation step.
A sodium sulfate decahydrate-rich stream produced from the partial separation of the boric acid/sodium sulfate decahydrate mix may be passed directly to a sodium sulfate precipitation step.
The subsequent steps (c) may include a lithium carbonate crystallisation step.
The lithium carbonate crystallisation step may include precipitating impurities including any one or more than one of Mg. Al, Fe, Si and other heavy metal hydroxides, gypsum and silica from the digestion liquor and separating the precipitates from the digestion liquor.
The lithium carbonate crystallisation step may include evaporating water to increase the lithium concentration in the digestion liquor.
The impurity precipitation step may include adding any one or more than one of calcium carbonate, calcium hydroxide, sodium carbonate and sodium hydroxide in any suitable proportion to the digestion liquor.
The lithium carbonate crystallisation step may include precipitating calcium from the digestion liquor.
The lithium carbonate crystallisation step may include separating calcium precipitates from the digestion liquor.
The process may include purifying lithium carbonate from the lithium carbonate crystallisation step by dissolution in presence of carbon dioxide, filtration to remove insoluble impurities, ion exchange or solvent extraction to remove dissolved impurities, and re-precipitation of lithium carbonate by heating or steam stripping.
The calcium precipitation step may include adding sodium carbonate and/or carbon dioxide to the digestion liquor.
The lithium carbonate crystallisation step may include a solvent extraction step to strip boron from the digestion liquor.
The lithium carbonate crystallisation step may include precipitating lithium carbonate from the digestion liquor by adding sodium carbonate and carbon dioxide in any suitable proportion to the digestion liquor.
The process may include converting lithium carbonate from the lithium carbonate crystallisation step to lithium hydroxide by reacting lithium carbonate with calcium hydroxide or sodium hydroxide, filtration to remove insoluble contaminants and crystallization of lithium hydroxide by evaporation and cooling.
The lithium hydroxide crystals may be separated from the digestion liquor, washed to remove adhering impurities and dried under a carbon dioxide free environment.
The lithium hydroxide product may be produced is re-dissolved and refined using ion exchange processes to remove deleterious elements, for example, Ca, Na, B, and recrystallizing lithium hydroxide by evaporation and cooling followed by separation from the digestion liquor, washing and drying in a carbon dioxide free atmosphere.
The subsequent steps (c) may include a sodium sulfate crystallisation step.
The sodium sulfate crystallisation step may include adjusting the pH of the digestion liquor to a neutral pH.
The sodium sulfate crystallisation step may include adjusting the pH of the digestion liquor to a pH in a range of 2-10, typically pH 3-7.
The sodium sulfate crystallisation step may include precipitating sodium sulfate crystals by evaporating and/or cooling the digestion liquor.
The term “mined” ore is understood herein to include, but is not limited to, (a) run-of-mine material and (b) run-of-mine material that has been subjected to at least primary crushing or similar or further size reduction after the material has been mined and prior to being sorted.
The process may be carried out as a continuous series of steps that digest the jadarite concentrate and then process the digestion liquor to precipitate the above-described downstream products.
The invention is not confined to this process and the process may be carried out as a series of discrete process stages.
The invention also provides boric acid made by the process described above.
The invention also provides lithium carbonate made by the process described above.
The invention also provides lithium hydroxide made by the process described above.
The invention also provides sodium sulfate made by the process described above.
The present invention is described further with reference to the accompanying Figures, of which:
It is emphasised that
The skilled person will appreciate that the invention is not limited to the particular selections of process operating conditions and equipment shown in
In particular, the invention is not limited to the particular sequence of precipitating valuable products from digestion liquor formed in the process.
The overall process recovery of the process shown in
With reference to
The flow sheet shown in
(a) comminuting and beneficiating the run-of-mine jadarite ore and producing a jadarite concentrate.
(b) digesting the concentrate in an acid and taking boron, lithium and sodium into solution in a digestion liquor, and
(c) subsequent steps to separate a series of valuable products (intermediate and final), including boron-containing, lithium-containing and sodium-containing products, and impurities from the digestion liquor.
Comminution
The first step in the process is comminution of the run-of-mine ore 101.
As noted above, jadarite is a white, earthy monoclinic silicate mineral having a chemical formula expressed as LiNaB3SiO7(OH) or LiNaSiB3O7(OH) or Na2OLi2O(SiO2)2(B2O3)3H2O.
The jadarite mineralization in the run-of-mine ore exists predominantly as 0.5-2.0 mm nodules interspersed within a clay and dolomitic matrix. The flow sheet is based on, but not limited to, this jadarite mineralization.
It is emphasised that the invention extends to changes to the process operating conditions and equipment of
The run-of-mine jadarite ore 101 is crushed to a top size of 2-5 mm, preferably 2.36 mm size, using multiple stage roll crushing/milling in steps 102/103 and produces firstly a crushed ore 2 and then a crushed/milled ore 3.
This size has been determined to be the most appropriate for the above-described jadarite mineralization based upon liberation studies and response to beneficiation. The invention is not limited to this size.
The choice of roll crushers is to ensure that the fines (−210 micrometres) generation is minimum as the fines are rejected in the beneficiation step.
Beneficiation
Beneficiation includes an attrition scrubbing step 104 in which the crushed/milled run-of-mine ore 3 is attrition scrubbed under natural conditions in a water or other suitable aqueous medium at a high, nominally 50-65% solids concentration.
In the attrition scrubber, softer clays are slaked away and the harder jadarite mineral attrites the softer calcite and dolomite minerals. The beneficiation residence time is dependent on the mineralogy and can be up to 20 minutes to achieve the best balance between concentrate grade, jadarite recovery and carbonate rejection.
The resultant product 4 from the attrition scrubber is screened at 210 micrometres size in classifying step 105. Alternatively, by way of example, hydraulic separation could be used to achieve a similar goal using upward current classifiers or hydrocyclones or similar options.
The oversize stream 6 from the scrubber is the beneficiated product, i.e. a jadarite concentrate 7.
The undersize stream 5 from the scrubber is thickened and centrifuged or pressure filtered (not shown) to a paste consistency for either underground placement or impounding.
The beneficiation step is mineralogy dependent, but typically 80-90% of the jadarite in the run-of-mine ore 101 is in the jadarite concentrate 7.
Other beneficiation techniques can also be applied to produce a higher grade concentrate from the run-of-mine ore 101. If high grade ores such as NaB 106 are present, only comminution steps 107 and 108 may be necessary to produce a NaB concentrate 109.
The jadarite concentrate 7 is processed as received from the classifying step 105 in the digestion step 111.
In one other, although not the only other, embodiment, not shown in the Figure, the jadarite concentrate 7 from the classifying step 105 is wet milled in a closed-circuit ball mill to a nominal −149 micrometres size before being processed in the digestion step 111. The nominal −149 micrometres size was determined to be a suitable cut-off size for digestion of the jadarite mineralization. The resultant ball mill product is further thickened to 65-70% solids in high density thickeners in a thickening step (not shown) and forms the digestion feed.
Digestion, Solubilization and Pregnant Leach Solution (PLS) Production
The jadarite concentrate 7 (and NaB concentrate 109—if present) from the classifying step 105 is digested with concentrated sulfuric acid 8 (i.e. >95% H2SO4) in the presence of recycled process liquors (stream 9 and mother liquor 11 in
The amount of water 10 that is added is controlled to maintain a 20-25% boric acid concentration, or at 80-90% of saturation dependent on temperature in the slurry 12.
Digestion of the jadarite concentrate 7 occurs in a series of stirred tank reactors which include an internal draft tube, controlled at a temperature of between 50-100° C., preferably 80-95° C. Acid addition is carefully controlled to maintain the pH of the slurry between 1-5, preferably 2.0-3.8. Acid addition is in the high mixing zone in the draft tube to allow rapid dispersion and prevent any local variations in the pH. This technique retards silica dissolution and consequent polymerization which can lead to gelling of the digestion liquors over time.
In another embodiment not shown in
Given the mix behavior over time in the digestion process, a Broadfield mixer-den digestor is one option. Tests by the digestor manufacturer and pilot testing have demonstrated suitability of this type of a machine for the ore. Broadfield digestors are commonly used in the manufacture of single superphosphate where flourapatite ore (phosphate rock) is acidulated with sulfuric acid and the reaction mix undergoes similar physical transformations.
During the reaction of jadarite ore with sulfuric acid, a large amount of CO2 is released from the reaction of acid with the contained dolomite and calcite in the ore. The evolved carbon dioxide tends to create a foam. Along with CO2, some amount of H2S is liberated.
The digestor is operated under a negative pressure where evolved gases are collected and scrubbed for H2S removal using a caustic solution.
The slurry 12 is subjected to a solid/liquid separation step 112 by being filtered in a series of centrifuges, pressure filters and vacuum filters with wash water not shown to yield a PLS 13 and gangue solids 23, which includes calcium sulfate.
The PLS 13 contains boron, lithium, and sodium in solution.
The following sections of the specification describe separating valuable products including boron-containing, lithium-containing and sodium-containing products, from the PLS 13.
Boric Acid (“BA”) Crystallization
The PLS 13 from the solid/liquid separation step 112 is evaporated if needed (not shown in the flow sheet) to a boric acid concentration of 20-25%.
The evaporated stream or the PLS 13 is treated with a combination of sodium dithionite, oxalic acid, di-sodium ethylene diamine tretraacetic acid and concentrated sulfuric acid in the range of 1-10 g/L. (identified as sulfuric acid 14 in the Figure), and then processed in 2-3 stages of flash cooling in step 113 to 25-35° C. or lower temperatures to crystallize boric acid.
The boric acid product slurry 15 is filtered using a counter-current washing circuit comprised of vacuum and horizontal belt filters or pressure filters in step 114.
The moist boric acid crystals 16 containing 4-8% moisture are dried in a rotary dryer or a vibrating fluidized bed dryer at 70° C. in step 115 and form a first marketable product 18. Gentle drying is required to prevent size degradation of the boric acid crystals and proper temperature control is needed to prevent dehydration of the boric acid molecule.
Anti-caking agents may be added to the dried boric acid product 116.
Lime and Calcium Precipitation
The weak liquor stream 19 from the boric acid filtration step 114 is transferred to a lime precipitation step 117.
In this step, the weak liquor stream 19 is contacted with excess lime 20 at ambient temperature to precipitate impurities, including Mg, Al. Fe and other heavy metal hydroxides along with gypsum and silica, with the resultant stream being in the form of a slurry 21. The slurry 21 is separated into solids 22 and limed liquor 24 using a combination of vacuum and pressure filters and centrifuges in a multi-stage counter wash circuit with intermediate re-pulps in step 118.
Nearly 20% and in a number of instances up to 40% of the boron in the weak liquor stream 19 is precipitated as a calcium borate in the liming step 117. The conditions in this step are optimized to prevent lithium losses, minimize boron losses and achieve a near complete removal of the Mg, Al, heavy metal and silica impurities. A short residence time of less than 30 minutes may be sufficient. However, typically, longer residence times of 1 hour are required.
The limed liquor stream 24 is saturated with calcium and is at pH 10.5-12.5, typically pH 10.5-11.5.
The limed liquor stream 24 is optionally evaporated in step 119 to form a concentrated limed liquor 25.
Optionally, the concentrated limed liquor 25 is treated with a small amount of 30% soda ash solution 26 or carbon dioxide gas (not shown) to precipitate calcium as carbonate and a small amount of lithium (also as a carbonate) in a softening step 120 to ensure near complete removal of calcium in a stream 28.
The precipitated calcium and lithium carbonate solids in 27 are separated by filtration in step 121 to produce a softened liquor 28.
The separated calcium and lithium carbonates are recycled (not shown) to the liming step 117 to recover the precipitated lithium values.
Near complete removal of calcium is very important in this step 120 as the remaining calcium would otherwise contaminate the lithium carbonate product produced downstream in the process.
Solvent Extraction of Boron (not Shown in Figure)
In this optional step, the liquor 28 from the calcium precipitation and separation steps 120 and 121 is transferred to a solvent extraction step.
The solvent extraction step is used to recover any remaining boron as boric acid and to reduce boron content of the raffinate going forward to lithium carbonate crystallization such that the lithium carbonate product has <10 ppm boron impurity.
The solvent extraction step is conducted at ambient temperatures and employs two stages of extraction, two stages of stripping and a wash stage. Crud removal and treatment is included as customary. The extractant is a custom made aromatic chemical which has been industrially demonstrated to have very high selectivity towards boron. The extractant is used in a 1:3 ratio with an aliphatic carrier. Stripping is performed with sulfuric acid. Organic: aqueous ratios of 2-3:1 are used in both the extraction and stripping stages. Extraction and stripping residence times are short (<2 minutes) and phase separation times are of the order of 4-5 minutes with tri-butyl phosphate used as a phase modifier.
The solvent extraction step produces a raffinate containing <100 ppm boron and a strip liquor containing 8 grams per liter of boron.
The solvent has limited selectivity towards lithium and any extracted lithium along with the boron in the strip liquor is recycled back to the digestion and solubilization step.
The raffinate from solvent extraction step is a very clean liquor essentially containing only sodium and lithium sulfates.
Solvent extraction is optional and would be considered if it is important to obtain a high purity.
In this case, liquor 28 from the calcium precipitation and separation step 121 proceeds to lithium carbonate crystallization. Without solvent extraction the lithium carbonate product can be optionally purified.
Lithium Carbonate Crystallization
The softened liquor 28 is processed in a lithium carbonate precipitation step 122 in a reactive forced circulation evaporative crystallizer with mechanical vapor recompression (MVR) with the addition of sodium carbonate solution 29.
Alternatively, the crystallization step can be a rapid precipitation reaction in stirred tank reactors at temperature controlled at 70-100° C., preferably 90-100° C., with addition of sodium carbonate solution 29. Controlled crystallization yields higher purity product.
Due to the inverse solubility of lithium carbonate, low temperature rises have to be maintained in the heat exchangers to provide long wash-out cycles. Meta-stable zone width determinations in the laboratory as well as pilot testing have determined that the heat exchangers should be sized for a temperature rise of 1.5° C.
The crystallized lithium carbonate containing slurry 30 is separated from the mother liquor in a centrifuge separation step 123 with peeler centrifuges in a three-stage counter-current wash circuit with intermediate re-pulps.
The dewatered lithium carbonate cake 37 contains 15-25% moisture which can be directly dried in rotary or flash driers in step 129 (described below)—and form a technical grade marketable product 49.
Purification of Lithium Carbonate
Further purification of lithium carbonate is accomplished by dissolving the dewatered lithium carbonate cake 37 in water while bubbling carbon dioxide 38 in a lithium carbonate digestion step 126.
The solution is then filtered to remove undissolved solids (not shown in Figure). Undesired cationic impurities such as Ca and Mg and anionic impurities such as B are removed sequentially using suitable specific ion exchange resins in step 127. The resin is regenerated using hydrochloric acid 40, sulfuric acid 41 and sodium hydroxide 42.
The purified solution 43 is then heated indirectly or directly with steam 44 to remove carbon dioxide and precipitate high purity lithium carbonate product in slurry 45 in a Battery Grade (BG) lithium carbonate crystallization step 128. The liberated carbon dioxide is captured and used in the dissolution step 126.
The dissolution step is preferably conducted cold and under pressure. The precipitation or carbon dioxide stripping is preferably conducted at high temperatures.
The hot slurry 45 is separated from the mother liquor in peeler centrifuges in a three-stage counter-current wash circuit with intermediate repulps to produce a wet lithium carbonate cake 47 in step 144. The separated mother liquor 46 is recycled to the lithium carbonate digestion step 126 as stream 39. The wet cake is dried in rotary or flash driers in step 129—and forms a second marketable product 49.
The product 49 can be micrometre-sized in an air-swept pulverizer 130 to produce another size classification of the marketable product 50.
Acidulation and Sodium Sulfate Crystallization
The liquor 31 after the lithium carbonate crystallization and solid-liquid separation steps 122 and 123 is acidified in an acidification step (not shown) with sulphuric acid to a pH of 2-3.5 to drive off all dissolved carbon dioxide. Subsequently, the pH is adjusted back to 4.5-9.0, typically 4.5-7.0.
The neutralized liquor is evaporated in a sodium sulfate crystallization step 124 with MVR to produce a slurry containing sodium sulfate crystals 32.
The sodium sulfate crystals 32 are dewatered in pusher centrifuges to 3-4% moisture in step 125. The moist sodium sulfate crystals 34 are dried in rotary dryers in step 132 and form a third marketable product 36.
The mother liquor 33 from the sodium sulfate crystallization and solid-liquid separation steps 124 and 125 is recycled to the ore digestion step 111. A portion of this stream 33 is bled for impurities control and can be recovered after concentration and rejection of impurities in an SSU unit (not shown).
Conversion of Lithium Carbonate to Lithium Hydroxide
Lithium hydroxide is another marketable product that can be produced from this process.
In order to produce lithium hydroxide, wet lithium carbonate cake 37 or dry products 47 or 49 are slurried and reacted with calcium hydroxide 51 in a stirred tank reactor in the lithium hydroxide conversion step 134.
The reacted slurry 52 is filtered in step 135 to produce a lithium hydroxide solution 54.
The lithium hydroxide solution 54 is cooled and evaporated in the lithium hydroxide crystallization step 136 to yield lithium hydroxide crystal containing slurry 55 which are separated from the mother liquor by a suitable solid liquid separation technique in step 137.
The wet lithium hydroxide cake 57 can then dried under a carbon dioxide free atmosphere in step 142 to produce the final product.
The wet lithium hydroxide cake 57 can be further refined by re-dissolution with water 59 in step 138. Dissolved impurities are removed from the resultant slurry 58 using ion exchange in step 139 to produce a refined lithium hydroxide solution 62. The ion exchange resin is regenerated using hydrochloric acid 60 and sulfuric acid 61.
The refined lithium hydroxide solution 62 is cooled and evaporated in the BA (battery grade) lithium hydroxide crystallization step 140 to produce high purity lithium hydroxide crystals containing slurry 63.
This slurry 63 is separated from the mother liquor in centrifuges, step 141, to generate a wet battery grade lithium hydroxide 65 which is dried under a carbon dioxide free atmosphere in step 142 to produce the final battery grade lithium hydroxide product 66.
The mother liquor 64 from separation of battery grade lithium hydroxide crystals 65 is recycled as stream 56 to the first lithium hydroxide crystallization step 136 and used in regeneration of ion exchange resins in step 139.
Glauber's Salt (Sodium Sulfate Decahydrate Crystallization) (not Shown in the Figure)
In another embodiment (not shown), sodium sulfate can be produced in different areas of the process. An advantage of Glauber's salt production is the removal of excess water from the process in form of the water of hydration associated with Glauber's salt. The areas where Glauber's salt production can occur are:
Test Work
The applicant has carried out extensive test work in relation to the invention. The test work includes three pilot plant campaigns that investigated the steps in the process of the invention.
The following description provides details of a sub-set of the third pilot plant test work.
The key findings of the third pilot plant campaign are as follows:
Beneficiation
The purpose of the beneficiation pilot plant test work was to test the effectiveness of the attrition scrubbing step 104 to produce a beneficiated concentrate on actual samples of jadarite ore.
The test work evaluated attrition scrubbing of jadarite ore samples for a range of attrition scrubbing times. Feed material for the scrubbing tests was prepared from −31.5 mm ore samples. 25 kg was jaw crushed at a 12.5 mm close side setting (CSS) and screened at 4 mm. The oversize was then jaw crushed at 6 mm CSS and screened at 4 mm. The oversize was then roll crushed at 3 mm nominal gap to 100% passing 4 mm. The samples were then wet screened at 212 microns. The wet screen undersize was sub-sampled for assay. Test charges were prepared from the oversize by rotary splitting. 1 kg attrition scrubs were performed on these samples at 65% solids for various times, 3, 6, 9 and 15 minutes. Products were collected, weighed and prepared for assay.
The text work established that the above attrition scrubbing test procedures were effective in terms of producing concentrates that had high concentrations of boron-containing and lithium-containing compounds.
Digestion, Solubilization and Pregnant Leach Solution (PLS) Production
Pilot plant test work was carried out on samples of jadarite concentrates to assess digestion performance and filtration of the digestor output.
Digestion Performance
Pilot plant test work found that lithium extraction in digestion with concentrated sulfuric acid was consistently 96 to 97% and boron extraction was around 96%.
Small amounts of coarse un-leached white nodules of jadarite in digestion residue were observed. Extended leaching of these un-leached jadarite nodules showed that additional lithium and boron could be extracted.
In the test work, digestion acid consumption averaged 357 kg/t.
In the test work, residue primary filtration, a hot pre-wash of the filter before primary filtration, and a hot filter feed pump (achieved via a pump submerged in a 90° C. hot water bath) ensured that the boric acid concentration did not drop over the course of filtration so that the feed solution to boric acid crystallisation was at a target concentration. This is shown in
Digestion Filtration
In the pilot plant test work, a coarse removal screen was used to remove material >1 mm.
Primary filtration rates1 were at around 59 kg dry solids/m2/h (
Primary cake solids were typically 54 to 58% solids (TDS corrected).
Final filtration rates (i.e. after a third re-pulp stage) were typically 175 kg dry solids/m2/h.
Final cake solids were very consistent at 61 to 63% solids in the test work.
Boric Acid (“BA”) Crystallization Pilot plant test work was carried out on precipitating boric acid from samples of pregnant leach liquor in a crystalliser.
In one series of tests, the purity of the boric acid product was 100.3% B(OH)3 by titration2. 2 The boric acid titration has an associated error, and for high purity boric acid this means that values over 100% can be reported. This is accepted in industry, and some product specifications are over 100%.
The crystal size of the boric acid product was finer than a commercially available boric acid product—see
Concentrations of boron out of the crystalliser were consistently close to predicted levels, as shown in
In the test work, filtration of the boric acid slurry via vacuum pan filtration resulted in a final cake with 81 to 84% solids.
Liming Filtration
Pilot plant test work was carried out to determine the efficiency of liming to remove magnesium and other impurities. It was found that liming achieved target magnesium removal, and boron losses were consistent with expectations. Soluble losses less than 1.5% were regularly achieved.
In one series of tests, primary filtration rates for liming cake were 93 kg dry solids/m2/h. Primary liming cakes typically contained 40 to 55% solids (TDS adjusted). Final liming cake (i.e. after fourth re-pulp) filtered at 138 kg dry solids/m2/h, and had a final solids of 55 to 65%. This is in line with the expected commercial filter performance of 53.6% solids.
Acidulation and Sodium Sulfate Crystallization
Pilot plant test work was carried out on precipitating sodium sulfate from samples of pregnant leach liquor.
In one series of tests, the sodium sulfate purity was 99.8%.
Impurity specifications for calcium, magnesium and chloride were all comfortably met, as shown in
The crystals that were produced (
The pilot plant test work described briefly above and the whole of the test work carried out by the applicant indicates that the process of the invention is an effective process.
Many modifications may be made to the embodiments of the present invention described above without departing from the spirit and scope of the invention.
By way of example, whilst the embodiments are described above in the context of jadarite ore, it can readily be appreciated that the invention is not so limited in scope and extends generally to recovering valuable products from ore containing lithium and more particularly to recovering valuable products from ore containing boron and lithium.
By way of further example, whilst the embodiments are described above in the context of particular types of crushers, centrifuges and other equipment, it can readily be appreciated that the invention is not so limited in scope and extends generally to equipment that can operate with the described functionality.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017904543 | Nov 2017 | AU | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US18/59952 | 11/9/2018 | WO | 00 |