Patent Application
20220339746
The present disclosure relates to the formation of cores and, more particularly, to cores with mini-cores bonded thereto.
Certain high-performance turbine vane designs require numerous, very small and fragile cores, which are referred to as mini-cores, on the pressure side of the main body of the core. Currently, however, it is not possible to cast these geometries monolithically with the main body core and therefore the mini-cores are cast separately and subsequently bonded to the main body of the core.
Bonding the mini-cores is typically accomplished by forming a post-in-hole joint in which a hole or recess is formed in the surface of the main body of the core where the mini-core is going to be bonded, paste is metered into the hole or recess and a post of the mini-core is inserted therein. This process presents multiple issues, though. Notably, it can be difficult to meter a correct amount of paste into the hole due to the viscous nature of the paste. As a result, there is frequently too much or not enough paste in the joint. This, in turn, leads to a relatively poor joint interface. In addition, manual cleaning of the bond area can be difficult, labor intensive and variable due to the area being small and inaccessible. As an example of the difficulty in creating the bond properly, it can require a skilled technician over an hour to bond only five mini-cores for a given vane. Moreover, even with this time requirement, joint detail at the base can be variable. An additional issue with the process is that the paste often has to be thickened with filler to prevent shrink in the eventual arrangement. The thickened paste is thus hard to work with and does not flow well. Consequently, slight variances in either the post or hole can cause formation of a relatively bad or unreliable joint.
Accordingly, an improved method of bonding mini-cores to cores is needed.
According to an aspect of the disclosure, a method of bonding a mini-core to a surface of a core is provided. The method includes providing the mini-core with an attachment device that includes a protrusion of a surface of the mini-core, dipping the protrusion into a supply of paste to transfer a fixed quantity of paste to the protrusion and affixing the protrusion to the surface of the core with the fixed amount of paste interposed between the surface and the protrusion.
In accordance with additional or alternative embodiments, the affixing includes pressing the protrusion onto the surface to drive the paste toward forming a fillet at a base of the protrusion.
In accordance with additional or alternative embodiments, the core is a ceramic core for forming an internal cavity of a turbine blade or vane and the surface is a pressure surface of the core.
In accordance with additional or alternative embodiments, the protrusion of each mini-core includes one or more posts, studs or bumpers and a perforated plate section having a side to which the one or more posts, studs or bumpers are attached.
In accordance with additional or alternative embodiments, the dipping includes dipping the one or more posts, studs or bumper into the supply of paste to transfer the fixed amount of paste to each of the one or more posts, studs or bumpers and the affixing includes affixing the one or more posts, studs or bumpers to the surface with the fixed amount of paste interposed between the surface and each of the one or more posts, studs or bumpers.
In accordance with additional or alternative embodiments, the dipping of the one or more posts, studs or bumpers into the supply of paste includes simultaneously dipping the one or more posts, studs or bumpers into the supply of paste and the affixing of the one or more posts, studs or bumpers to the surface includes simultaneously affixing the one or more posts, studs or bumpers to the surface.
In accordance with additional or alternative embodiments, the paste has a viscosity of about 400 to about 1700 centipoise.
In accordance with additional or alternative embodiments, the paste includes about 90% paste and about 10% thinner.
According to another aspect of the disclosure, a method of bonding multiple mini-cores to a surface of a core is provided. The method includes providing each of the mini-cores with one or more posts, studs or bumpers, simultaneously dipping each of the one or more posts, studs or bumpers of one of the mini-cores into a supply of paste to transfer a fixed quantity of paste to each of the one or more posts, studs or bumpers, simultaneously affixing the one or more posts, studs or bumpers to the surface with the fixed amount of paste interposed between the surface and each of the one or more posts, studs or bumpers and repeating the simultaneously dipping and affixing for each of the mini-cores to form a linear array of mini-cores on the surface.
In accordance with additional or alternative embodiments, the simultaneously affixing includes pressing each of the one or more posts, studs or bumpers of each of the mini-cores onto the surface to drive the paste toward forming a fillet at a base of each of the one or more posts, studs or bumpers.
In accordance with additional or alternative embodiments, the core is a ceramic core for forming an internal cavity of a turbine blade or vane and the surface is a pressure surface of the core.
In accordance with additional or alternative embodiments, each mini-core includes a perforated plate section having a side to which the corresponding one or more posts, studs or bumpers are attached.
In accordance with additional or alternative embodiments, the paste has a viscosity of about 400 to about 1700 centipoise.
In accordance with additional or alternative embodiments, the paste includes about 90% paste and about 10% thinner.
According to an aspect of the disclosure, a core and mini-core assembly is provided and includes a core including a surface, which is entirely continuous along a single plane, a mini-core including a perforated plate section having a side and one or more posts, studs or bumpers attached to and extending from the side of the plate section and paste by which each of the one or more posts, studs or bumpers is bonded to the surface. The paste includes, at each post, stud or bumper a portion of the paste interposed between the post, stud or bumper and a local section of the surface and a remaining portion of the paste forming a fillet about the post, stud or bumper.
In accordance with additional or alternative embodiments, the fillet includes a substantially uniform radius about the post, stud or bumper.
In accordance with additional or alternative embodiments, the core is a ceramic core for forming an internal cavity of a turbine blade or vane and the surface is a pressure surface of the core.
In accordance with additional or alternative embodiments, the mini-core is provided as multiple mini-cores respectively affixed to the surface in a linear array.
In accordance with additional or alternative embodiments, the paste has a viscosity of about 400 to about 1700 centipoise.
In accordance with additional or alternative embodiments, the paste includes about 90% paste and about 10% thinner.
Additional features and advantages are realized through the techniques of the present disclosure. Other embodiments and aspects of the disclosure are described in detail herein and are considered a part of the claimed technical concept. For a better understanding of the disclosure with the advantages and the features, refer to the description and to the drawings.
For a more complete understanding of this disclosure, reference is now made to the following brief description, taken in connection with the accompanying drawings and detailed description, wherein like reference numerals represent like parts:
In cases in which mini-cores are bonded to cores, the bonding paste is much stronger than the core material and forms a very aggressive bond with the core material. Thus, as will be described below, mini-cores are bonded to a core by surface bonds that are considerably simpler to accomplish than conventional bonds. The mini-core posts, studs or bumpers are dipped onto a surface of a paste in order to transfer a fixed amount of paste volume to the mini-core post, stud or bumper so that the fixed amount of paste can be used thereafter in a joint including the post, stud or bumper and another surface. In some cases, relatively thin paste can be used, as the problem of shrinking in this process does not tend to cause gaps. The paste forms a radius at the post joint.
With reference to
In accordance with embodiments, the paste can be an alumina-based, silica-based or zirconia-based aqueous or non-aqueous paste that can cure at or near room temperature within a time window of about six hours or less, four hours or two hours or less or, in some cases, on the order of minutes or about −10-20 seconds. The paste has a viscosity of about 400 to about 1700 centipoise, or about 700 to about 1200 centipoise, about 800 to about 900 centipoise or about 830 centipoise. In order to achieve a desired viscosity and for ease of use, the paste may include about 5% to about 20% of a thinner, about 8% to about 15% of a thinner, about 9% to about 12% of a thinner or about 10% of a thinner The thinner can be provided as a sodium silicate solution that is blended with the paste to achieve a desired viscosity. In accordance with further embodiments, the paste can be provided as Resbond 989FSTM available from Cotronics Corporation and the thinner can be provided as A2101 fluid available from Cotronics Corporation.
Although it is not required, each mini-core can include one or more attachment devices and a perforated plate section having a side to which the one or more attachment devices are attached and from which the one or more attachment devices extend. In these or other cases, the dipping of operation 102 includes dipping the one or more attachment devices into the supply of paste to transfer the fixed amount of paste to each of the one or more attachment devices and the affixing of operation 103 includes affixing the one or more attachment devices to the surface with the fixed amount of paste interposed between the surface and each of the one or more attachment devices. In further detail, the dipping of the one or more attachment devices into the supply of paste can include simultaneously dipping the one or more attachment devices into the supply of paste and the affixing of the one or more posts to the surface can include simultaneously affixing the one or more attachment devices to the surface.
With reference to
Also as above, in accordance with embodiments, the paste can be an alumina-based, silica-based or zirconia-based aqueous or non-aqueous paste that can cure at or near room temperature within a time window of about six hours or less, four hours or two hours or less or, in some cases, on the order of minutes or about −10-20 seconds. The paste has a viscosity of about 400 to about 1700 centipoise, or about 700 to about 1200 centipoise, about 800 to about 900 centipoise or about 830 centipoise. In order to achieve a desired viscosity and for ease of use, the paste may include about 5% to about 20% of a thinner, about 8% to about 15% of a thinner, about 9% to about 12% of a thinner or about 10% of a thinner The thinner can be provided as a sodium silicate solution that is blended with the paste to achieve a desired viscosity. In accordance with further embodiments, the paste can be provided as Resbond 989FSTM available from
Cotronics Corporation and the thinner can be provided as A2101 fluid available from Cotronics Corporation.
Although it is not required, each mini-core can include a perforated plate section having a side to which the corresponding one or more posts, studs or bumpers are attached and from which the corresponding one or more posts, studs or bumpers extend.
With reference to
With reference to
In accordance with embodiments, the paste 420 can be an alumina-based, silica-based or zirconia-based aqueous or non-aqueous paste that can cure at or near room temperature within a time window of about six hours or less, four hours or two hours or less or, in some cases, on the order of minutes or about −10-20 seconds. The paste 420 has a viscosity of about 400 to about 1700 centipoise, or about 700 to about 1200 centipoise, about 800 to about 900 centipoise or about 830 centipoise. In order to achieve a desired viscosity and for ease of use, the paste 420 may include about 5% to about 20% of a thinner, about 8% to about 15% of a thinner, about 9% to about 12% of a thinner or about 10% of a thinner The thinner can be provided as a sodium silicate solution that is blended with the paste 420 to achieve a desired viscosity. In accordance with further embodiments, the paste 420 can be provided as Resbond 989FSTM available from Cotronics Corporation and the thinner can be provided as A2101 fluid available from Cotronics Corporation.
When the paste 420 provides for the bonding, the paste 420 includes, at each post, stud or bumper 412, a portion of the paste 420 interposed between the post, stud or bumper 412 and a local section of the surface 402 and a remaining portion of the paste forming a fillet 421 (see
As further shown in
Technical effects and benefits of the present disclosure are the provision of surface bonding technique that allows a faster, easier method of bonding mini cores to surfaces of cores, and produces a better quality radius at the foot of the post of the mini core. Dipping the post ends just to surface contact the paste volume automatically transfers a fixed amount of paste to the joint so no precision dispensing is required. The surface bonding technique also accommodates slight core variance, is easy to automate and requires no manual post finishing touch up. A skilled technician can be able to manually make high quality bonds using this approach in about 2 minutes.
The corresponding structures, materials, acts, and equivalents of all means or step plus function elements in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the present disclosure has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the technical concepts in the form disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the disclosure. The embodiments were chosen and described in order to best explain the principles of the disclosure and the practical application, and to enable others of ordinary skill in the art to understand the disclosure for various embodiments with various modifications as are suited to the particular use contemplated.
While the preferred embodiments to the disclosure have been described, it will be understood that those skilled in the art, both now and in the future, may make various improvements and enhancements which fall within the scope of the claims which follow. These claims should be construed to maintain the proper protection for the disclosure first described.
This application is a division of U.S. application Ser. No. 17/237,655, filed Apr. 22, 2021, the contents of which are hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17237655 | Apr 2021 | US |
| Child | 17738531 | US |