Abstract

There is disclosed an MnMgCuZn ferrite material which contains ranges of 46.5 to 50.4 mol % of iron oxide, 10.5 to 22.0 mol % of magnesium oxide, 22.5 to 25.0 mol % of zinc oxide, 6.0 to 16.0 mol % of copper oxide, and 0.1 to 3.5 mol % of manganese oxide. Advantages of an MnMgCuZn ferrite material that resistivity is relatively high and material cost is low are utilized to realize a superior MnMgCuZn ferrite material which is much smaller in magnetic loss than conventional materials of the same series and which has a sufficient saturated magnetic flux density.

Description

BACKGROUND OF THE INVENTION

The present invention relates to an MnMgCuZn ferrite material, particularly to an MnMgCuZn ferrite material which has a low magnetic loss and a sufficient saturated magnetic flux density and which can be used in a deflection yoke core or a transformer for a high speed scanning cathode-ray tube, particularly a high-definition high-speed scanning cathode-ray tube.

For example, an MnMgZn ferrite material (Japanese Patent Application Laid-open No. 65499/1973) is heretofore used in a deflection yoke core for a high speed scanning cathode-ray tube (hereinafter referred to as CRT). Since the MnMgZn ferrite material is relatively high in resistivity and low in material cost, it has been broadly used as a ferrite material for the deflection yoke core not only domestically but also internationally.

In a method of manufacturing the deflection yoke core, in the same manner as a general ferrite core, materials are mixed, calcined, ground, kneaded together with an appropriate binder, granulated, and press-molded in a predetermined shape using a metallic mold, and the molded material is sintered. When the conventional MnMgZn ferrite material is used, sintering is performed at a temperature of 1250° C. or higher.

Furthermore, recently, CRT display has progressed in raising definition and increasing screen size, while household television has progressed in increasing speed and enlarging angle. Additionally, for the increased definition and speed, a horizontal frequency has become very high. As a result, a ferrite core for use in a deflection yoke is requested to reduce a magnetic loss. Moreover, for the enlarged screen and angle, the ferrite core for use in the deflection yoke needs to have a high saturated magnetic flux density.

On the other hand, in order to prevent thermal runaway at an operation temperature, it is desirable in the deflection yoke core that a temperature coefficient of magnetic loss in the vicinity of 100° C. be negative. In a technique for making negative the temperature coefficient of magnetic loss, a ferrite having a high Curie point is used, and the Curie point necessary for the deflection yoke is about 140° C. or higher.

To suppress ringing phenomenon, the deflection yoke core needs to have a high resistivity. In the ringing phenomenon, an electrostatic capacity is generated between coils or between coil and core, and vertical streaks appear on screen by modulated currents. In order to suppress the ringing phenomenon, the necessary resistivity of the ferrite core is set to 10 6 Ωcm or more (Japanese Patent Publication No. 75714/1993).

In the aforementioned circumstances, it is disclosed in Japanese Patent Publication No. 66254/1991, 75714/1993 and Journal of the Magnetics Society of Japan 21,915-918(1997) that when copper oxide is applied in the range of 5 mol % or less (in terms of CuO) to the conventional MnMgZn ferrite material, the magnetic loss is reduced. In order to further increase the saturated magnetic flux density and Curie point, however, the content of copper oxide needs to be increased. In an MnMgCuZn ferrite material containing more than 5 mol % of copper oxide in terms of CuO, there is a problem that when calcining is performed at a temperature of 1250° C. or higher, abnormal grain growth and Cu segregation are caused in a crystal structure, and electromagnetic properties are remarkably deteriorated.

Moreover, it is proposed that the magnetic loss is reduced by remarkably increasing the content of manganese oxide (9 to 15 mol % in terms of MnO, 4.5 to 7.5 mol % in terms of Mn 2 O 3 ) in the MnMgCuZn ferrite material (Japanese Patent Application Laid-open No. 25114/1998). When the content of manganese oxide is increased in the MnMgCuZn ferrite material, however, the saturated magnetic flux density at the operation temperature of the deflection yoke (around 100° C.) becomes remarkably low, which disadvantageously reduces the allowable amount of electric currents passed through a deflection yoke coil. Furthermore, since the Curie point is lowered, a problem occurs that the thermal runaway is caused in the operation of the deflection yoke at 100° C. or higher.

SUMMARY OF THE INVENTION

In consideration of the problems, an object of the present invention is to utilize advantages of an MnMgCuZn ferrite material that resistivity is relatively high and material cost is low and to provide a superior MnMgCuZn ferrite material which is much smaller in magnetic loss than conventional materials of the same series and which has a sufficient saturated magnetic flux density.

Specifically, the present invention provides an MnMgCuZn ferrite material which is in a composition range of 46.5 to 50.4 mol % of iron oxide, 10.5 to 22.0 mol % of magnesium oxide, 22.5 to 25.0 mol % of zinc oxide, 6.0 to 16.0 mol % of copper oxide, and 0.1 to 3.5 mol % of manganese oxide.

The MnMgCuZn ferrite material of the present invention is largely lower in magnetic loss, higher in saturated magnetic flux density, and higher in resistivity and Curie point as compared with the conventional MnMgCuZn ferrite material, and useful as a deflection yoke core or a transformer for a CRT, particularly a high-definition CRT. Moreover, sintering can be performed at a relatively low temperature of 1200° C. or less, e.g., about 1000 to 1150° C., and manufacture cost can be lower as compared with the conventional MnMgCuZn ferrite material.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Preferred embodiments of the present invention will be described hereinafter.

An MnMgCuZn ferrite material of the present invention mainly contains 46.5 to 50.4 mol %, preferably 47.4 to 49.5 mol % of iron oxide in terms of Fe 2 O 3 ; 10.5 to 22.0 mol %, preferably 15.4 to 21.0 mol % of magnesium oxide in terms of MgO; 22.5 to 25.0 mol % of zinc oxide in terms of ZnO; 6.0 to 16.0 mol %, preferably 8.0 to 11.0 mol % of copper oxide in terms of CuO; and 0.1 to 3.5 mo i%, preferably 0.2 to 2.0 mol % of manganese oxide in terms of Mn 2 O 3 .

In a composition region outside the aforementioned ranges, for example, when the MnMgCuZn ferrite material is used in a deflection yoke, the magnetic loss is large, and the saturated magnetic flux density, resistivity and Curie point are insufficiently low.

Specifically, for example, if the content of iron oxide is less than 46.5 mol %, the saturated magnetic flux density and Curie point are lowered. If the content of iron oxide exceeds 50.4 mol %, the resistivity is lowered. Moreover, when the content of zinc oxide is less than 22.5 mol %, and sintering is performed at a relatively low calcining temperature in the range of 1000 to 1150° C., the magnetic loss is slightly increased. On the other hand, if the content of zinc oxide exceeds 25.0 mol %, the saturated magnetic flux density and Curie point are lowered. When the content of copper oxide is less than 6.0 mol %, the sintering cannot be performed at the relatively low calcining temperature in the range of 1000 to 1150° C., the magnetic loss is increased, and the saturated magnetic flux density and Curie point are lowered. When the content of copper oxide exceeds 16.0 mol %, the magnetic loss is increased, and the resistivity is lowered. Furthermore, the manganese oxide effectively reduces magnetic anisotropy, promotes grain growth, enhances initial permeability, and reduces hysteresis loss. However, when the content of manganese oxide exceeds 3.5 mol %, the saturated magnetic flux density, Curie point, and resistivity are lowered. Additionally, the magnesium oxide fulfills a supplementary role of maintaining the proportion of the other components.

In addition to the main components, the MnMgCuZn ferrite material of the present invention may contain as secondary components at least one of CaO, NiO, SiO 2 , GeO 2 , ZrO 2 , MoO 3 , WO 3 , Bi 2 O 3 , In 2 O 3 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , V 2 O 5 , and the like in the proportion of 1 wt % or less. For such sub component, when the content is increased, the magnetic loss of the MnMgCuZn ferrite material is lowered down to a minimum value (while maintaining the Curie point, saturated magnetic flux density, and resistivity). Thereafter, as the content is increased, the magnetic loss turns to be increased. For example, the material preferably contains, in terms of concentration, 1800 ppm or less of WO 3 , 2900 ppm or less of Nb 2 O 5 , 2350 ppm or less of V 2 O 5 , 2400 ppm or less of Ta 2 O 5 , 6100 ppm or less of GeO 2 , and 6100 ppm or less of ZrO 2 . When these ranges are exceeded, the magnetic loss becomes larger than the magnetic loss at the applied amount of 0 ppm. Moreover, when the MnMgCuZn ferrite material contains two or more types of the sub components, the content of each component can appropriately be set in such a manner that the magnetic loss is decreased to a desirable value.

The MnMgCuZn ferrite material of the present invention can be manufactured by sintering the ferrite material in the atmospheric air at a temperature of 1000 to 1200° C. in such a manner that the composition of the main components after sintering falls in the aforementioned range. As compared with the conventional material of the same series, the MnMgCuZn ferrite material of the present invention has a smaller magnetic loss (400 kW/m 3 or less on the condition that 100 mT of sine-wave alternating magnetic field with a frequency of 100 kHz is applied in 100° C.), a higher saturated magnetic flux density (180 mT or more at 100° C.), a higher Curie point (140° C. or more), and a higher resistivity (10 6 Ωcm or more). Additionally, the material can be sintered at a relatively low temperature (1000 to 1150° C.), and is useful as a deflection yoke core or a transformer for a CRT, particularly a high-definition CRT.

The present invention will next be described in more detail by illustrating examples.

First, each component was weighed so as to have a composition after sintering within following ranges, and wet-mixed in a ball mill of iron steel for 15 hours.

iron oxide (Fe 2 O 3 ): 46.5 to 50.4 mol %

magnesium oxide (MgO): 10.5 to 22.0 mol %

zinc oxide (ZnO): 22.5 to 25.0 mol %

copper oxide (CuO): 6.0 to 16.0 mol %

manganese oxide (Mn 2 O 3 ): 0.1 to 3.5 mol %

Subsequently, the mixed powder was tentatively calcined in the atmospheric air at 900° C. for two hours, and then wet-ground in the ball mill of iron steel for 15 hours. Applied to the resulting MnMgCuZn ferrite powder was 10 wt % of aqueous polyvinyl alcohol to perform granulation. The material was molded in a toroidal shape under a pressure of 1 ton/cm 2 . The molded material was sintered in the atmospheric air at a predetermined temperature in the range of 1000 to 1200° C. for three hours to obtain MnMgCuZn ferrite materials (Examples 1 to 12).

The composition, sintering temperature and retention time of each of the MnMgCuZn ferrite materials (Examples 1 to 12) are shown in Table 1.

Moreover, for each of the MnMgCuZn ferrite materials (Examples 1 to 12), the magnetic loss on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz was applied at 100° C., the saturated magnetic flux density in 100° C., the resistivity at a room temperature, and Curie point were measured. Results are shown in Table 1.

For comparison, MnMgCuZn ferrite materials with the compositions after sintering being deviated from the aforementioned range (Comparative Examples 1 to 7) were prepared in the same manner as the MnMgCuZn ferrite materials (Examples 1 to 12). Additionally, the composition, sintering temperature and retention time of each of the MnMgCuZn ferrite materials (Comparative Examples 1 to 7) were set as shown in Table 2. Moreover, for each of the MnMgCuZn ferrite materials (Comparative Examples 1 to 7), the magnetic loss on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz was applied at 100° C., the saturated magnetic flux density in 100° C., the resistivity at the room temperature, and Curie point were measured. Results are shown in Table 2.

Furthermore, for comparison, MnMgCuZn ferrite materials with the compositions after sintering being deviated from the aforementioned range (MnMgCuZn ferrite materials included in the invention according to Japanese Patent Publication No. 66254/1991 and Japanese Patent Application Laid-open No. 25114/1998) were prepared. Additionally, in the same manner as the examples 1 to 12, the MnMgCuZn ferrite materials were molded into toroidal shapes. Thereafter, the molded materials were sintered in the atmospheric air at 1250° C. for two hours to form MnMgCuZn ferrite materials (Comparative Examples 8, 9). Additionally, the compositions of the MnMgCuZn ferrite materials (Comparative Examples 8, 9) were set as shown in Table 2. Moreover, for each of the MnMgCuZn ferrite materials (Comparative Examples 8, 9), the magnetic loss on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz was applied at 100° C., the saturated magnetic flux density in 100° C., the resistivity at the room temperature, and Curie point were measured. Results are shown in Table 2.

	TABLE 1
	CALCINING	FERRITE MATERIAL PROPERTIES
	FERRITE	CONDITIONS	SATURATED
	MATERIAL COMPOSITION	CALCINING	RETENTION	MAGNETIC	MAGNETIC	RESIS-	CURIE
	(mol %)	TEMPERATURE	TIME	FLUX DENSITY	LOSS	TIVITY	POINT
SAMPLE	Fe 2 O 3	MgO	CuO	ZnO	Mn 2 O 3	(° C.)	(HOURS)	(mT)	(kW/m 3 )	(Ω · cm)	(° C.)
EXAMPLE 1	49.3	16.1	9.9	24.5	0.2	1020	3	181	394	10 9	143
EXAMPLE 2	49.5	21.0	6.0	23.3	0.2	1020	3	181	381	10 10	142
EXAMPLE 3	49.5	19.0	8.0	23.3	0.2	1020	3	198	382	10 10	148
EXAMPLE 4	49.6	19.1	8.0	23.0	0.2	1040	3	203	369	10 9	155
EXAMPLE 5	49.5	19.5	8.0	22.8	0.2	1020	3	209	386	10 10	157
EXAMPLE 6	49.5	21.5	8.0	22.5	0.2	1020	3	209	397	10 10	160
EXAMPLE 7	48.4	15.6	11.0	24.0	1.0	1020	3	193	372	10 9	146
EXAMPLE 8	47.4	15.6	11.0	24.0	2.0	1020	3	181	321	10 8	144
EXAMPLE 9	47.8	16.5	10.0	23.7	2.0	1080	3	186	328	10 8	143
EXAMPLE 10	48.2	16.1	10.0	23.7	2.0	1100	3	191	339	10 7	146
EXAMPLE 11	48.9	15.4	10.0	23.7	2.0	1120	3	194	378	10 6	156
EXAMPLE 12	46.7	11.1	15.6	23.7	2.9	1100	3	215	398	10 7	163

	TABLE 2
	CALCINING	FERRITE MATERIAL PROPERTIES
	FERRITE	CONDITIONS	SATURATED
	MATERIAL COMPOSITION	CALCINING	RETENTION	MAGNETIC	MAGNETIC	RESIS-	CURIE
	(mol %)	TEMPERATURE	TIME	FLUX DENSITY	LOSS	TIVITY	POINT
SAMPLE	Fe 2 O 3	MgO	CuO	ZnO	Mn 2 O 3	(° C.)	(HOURS)	(mT)	(kW/m 3 )	(Ω · cm)	(° C.)
COMPARA-	49.5	22.8	4.2	23.3	0.2	1100	3	163	394	10 10	135
TIVE
EXAMPLE 1
COMPARA-	49.4	20.2	8.0	22.2	0.2	1020	3	210	415	10 10	163
TIVE
EXAMPLE 2
COMPARA-	50.5	18.3	8.0	23.0	0.2	1160	3	199	379	10 4	150
TIVE
EXAMPLE 3
COMPARA-	49.4	14.3	10.6	25.5	0.2	1020	3	178	470	10 8	134
TIVE
EXAMPLE 4
COMPARA-	49.5	9.7	14.6	26.0	0.2	1020	3	184	506	10 7	137
TIVE
EXAMPLE 5
COMPARA-	49.5	5.8	17.5	27.0	0.2	1020	3	169	597	10 6	133
TIVE
EXAMPLE 6
COMPARA-	49.5	15.6	11.0	24.1	3.8	1020	3	149	332	10 7	132
TIVE
EXAMPLE 7
COMPARA-	48.2	27.8	1.4	20.0	2.6	1250	2	179	512	10 7	158
TIVE
EXAMPLE 8
COMPARA-	43.7	29.8	1.8	19.1	5.6	1250	2	150	402	10 7	139
TIVE
EXAMPLE 9

As shown in Table 1, it has been confirmed that in each of the MnMgCuZn ferrite materials of the present invention (Examples 1 to 12), the magnetic loss is 400 kW/m 3 or less on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz is applied in 100° C., the saturated magnetic flux density is 180 mT or more in 100° C., Curie point is 140° C. or higher, and the resistivity is 10 6 Ωcm in or more. It is especially clear that different from the conventional MnMgCuZn ferrite materials shown in Table 2 (Comparative Examples 8, 9), in the MnMgCuZn ferrite materials of the present invention (Examples 1 to 12), the magnetic loss is largely reduced, and the saturated magnetic flux density is largely enhanced.

On the other hand, as shown in Table 2, the MnMgCuZn ferrite materials deviated from the composition range of the present invention (Comparative Examples 1 to 7) correspond to any one of the results that the magnetic loss exceeds 400 kW/m 3 on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz is applied in 100° C., the saturated magnetic flux density is less than 180 mT in 100° C., Curie point is lower than 140° C. and that the resistivity is less than 10 6 Ωcm. Furthermore, it is apparent that when these materials are used in the deflection yoke cores especially for high-definition CRTs, problems are caused.

Subsequently, 24 types of MnMgCuZn ferrite materials (7A-1 to 4, 7B-1 to 4, 7C-1 to 4, 7D-1 to 4, 7E-1 to 4, 7F- 1 to 4) were prepared on the same conditions as in Example 7, except that WO 3 , Nb 2 O 5 , V 2 O 5 , Ta 2 O 5 , GeO 2 and ZrO 2 were applied in applied amounts shown in Table 3. For these MnMgCuZn ferrite materials and Example 7, the magnetic loss on the condition that 100 mT of sine-wave alternating magnetic field with the frequency of 100 kHz was applied at 100° C., the saturated magnetic flux density in 100° C., the resistivity at the room temperature, and Curie point were measured, and results are shown in Table 3.

	TABLE 3
	CALCINING	FERRITE MATERIAL PROPERTIES
	ADDITIVES	CONDITIONS	SATURATED
		APPLIED	CALCINING	RETENTION	MAGNETIC	MAGNETIC		CURIE
		AMOUNT	TEMPERATURE	TIME	FLUX DENSITY	LOSS	RESISTIVITY	POINT
SAMPLE	TYPE	(ppm)	(° C.)	(HOURS)	(mT)	(kW/m 3 )	(Ω · cm)	(° C.)
EXAMPLE 7	—	0	1020	3	193	372	10 9	146
7A-1	WO 3	200	1020	3	191	362	10 9	148
7A-2		1000	1020	3	189	307	10 9	147
7A-3		1700	1020	3	192	370	10 9	149
7A-4		2000	1020	3	190	493	10 9	146
7B-1	Nb 2 O 5	200	1020	3	193	365	10 9	144
7B-2		1200	1020	3	195	328	10 9	145
7B-3		2700	1020	3	191	366	10 9	143
7B-4		3000	1020	3	188	415	10 8	142
7C-1	V 2 O 5	200	1020	3	189	366	10 9	143
7C-2		2000	1020	3	192	319	10 9	145
7C-3		2300	1020	3	195	372	10 9	147
7C-4		2500	1020	3	190	413	10 9	145
7D-1	Ta 2 O 5	200	1020	3	189	360	10 9	148
7D-2		2000	1020	3	185	344	10 9	147
7D-3		2200	1020	3	190	361	10 9	146
7D-4		2500	1020	3	190	420	10 8	147
7E-1	GeO 2	200	1020	3	196	368	10 9	148
7E-2		1800	1020	3	193	313	10 9	146
7E-3		6000	1020	3	199	364	10 8	149
7E-4		6200	1020	3	200	452	10 8	148
7F-1	ZrO 2	200	1020	3	198	370	10 9	146
7F-2		2200	1020	3	201	324	10 9	145
7F-3		6000	1020	3	201	371	10 8	147
7F-4		6200	1020	3	197	431	10 8	144

As shown in Table 3, in Examples 7A-1 to 3 containing WO 3 in a concentration range of 1800 ppm or less, Examples 7B-1 to 3 containing Nb 2 O 5 in a concentration range of 2900 ppm or less, Examples 7C-1 to 3 containing V 2 O 5 in a concentration range of 2350 ppm or less, Examples 7D-1 to 3 containing Ta 2 O 5 in a concentration range of 2400 ppm or less, Examples 7E-1 to 3 containing GeO 2 in a concentration range of 6100 ppm or less, and Examples 7F-1 to 3 containing ZrO 2 in a concentration range of 6100 ppm or less, the magnetic loss of each example is as low as or lower than the magnetic loss of Example 7. It has also been confirmed that each of these MnMgCuZn ferrite materials maintains Curie point, saturated magnetic flux density, and resistivity at the same levels as those in Example 7.

Claims

1. An MnMgCuZn ferrite material comprising main components consisting of an iron oxide, and a magnesium oxide, a zinc oxide, a copper oxide, and a manganese oxide,the ferrite material comprising 46.5 to 50.4 mol % of the iron oxide, 10.5 to 22.0 mol % of the magnesium oxide, 22.5 to 25.0 mol % of the zinc oxide, 6.0 to 16.0 mol % of the copper oxide, and 0.1 to 3.5 mol % of the manganese oxide, and further comprising 200 ppm to 1% of at least one secondary component selected from the group consisting of ZrO2, WO3, Ta2O5, Nb2O5, V2O5, and GeO2.

2. The MnMgCuZn ferrite material according to claim 1, wherein the concentration ranges for the secondary components are 1800 ppm to 200 ppm of WO3, 2900 ppm to 200 ppm of Nb2O5, 2350 ppm to 200 ppm of V2O5, 2400 ppm to 200 ppm of Ta2O5, 6100 ppm to 200 ppm of GeO2, and 6100 ppm to 200 ppm of ZrO2.

3. The MnMgCuZn ferrite material according to claim 1, wherein sintering is performed in atmospheric air at a temperature in the range of 1000 to 1200° C.

4. The MnMgCuZn ferrite material according to claim 1, wherein a magnetic loss is 400 kW/m3 or less when 100 mT of sine-wave alternating magnetic field with a frequency of 100 kHz is applied at 100° C.

5. The MnMgCuZn ferrite material according to claim 1, wherein a saturated magnetic flux density at 100° C. is 180 mT or more.

6. The MnMgCuZn ferrite material according to claim 1, wherein Curie point is 140° C. or more.

7. The MnMgCuZn ferrite material according to claim 1, wherein resistivity is 106 Ωcm or more.

8. A deflection yoke core comprising the MnMgCuZn ferrite material of claim 1.

9. A deflection yoke core comprising the MnMgCuZn ferrite material of claim 2.

10. A transformer for a high speed scanning cathode-ray tube comprising the MnMgCuZn ferrite material of claim 1.

11. A transformer for a high speed scanning cathode-ray tube comprising the MnMgCuZn ferrite material of claim 2.

12. A process for preparing the MnMgCuZn ferrite material of claim 1 comprising:mixing metal oxides comprising an iron oxide, a magnesium oxide, a zinc oxide, a copper oxide and a manganese oxide, and at least one secondary component selected from the group consisting of ZrO2, WO3, TA2O5, Nb2O5 and GeO2; calcining said mixed metal oxides in air, thereby forming a MnMgCuZn ferrite.

13. A process for preparing the deflection yoke core of claim 8 comprising:mixing metal oxides comprising an iron oxide, a magnesium oxide, a zinc oxide, a copper oxide and a manganese oxide, and at least one secondary component selected from the group consisting of ZrO2, WO3, TA2O5, Nb2O5 and GeO2; calcining said mixed metal oxides in air; grinding said calcined mixed metal oxides, thereby forming a MnMgCuZn ferrite powder; kneading said MnMgCuZn ferrite powder with a binder; granulating said MnMgCuZn ferrite powder; molding said granulating MnMgCuZn ferrite powder; and sintering said molded MnMgCuZn ferrite powder.

14. A process for preparing the transformer for a high speed scanning cathode-ray tube of claim 10 comprising:mixing metal oxides comprising an iron oxide, a magnesium oxide, a zinc oxide, a copper oxide and a manganese oxide, and at least one secondary component selected from the group consisting of ZrO2, WO3, TA2O5, Nb2O5 and GeO2; calcining said mixed metal oxides in air; grinding said calcined mixed metal oxides, thereby forming a MnMgCuZn ferrite powder; kneading said MnMgCuZn ferrite powder with a binder; granulating said MnMgCuZn ferrite powder; molding said granulating MnMgCuZn ferrite powder; and sintering said molded MnMgCuZn ferrite powder.