Modified block copolymer composition

FIELD OF THE INVENTION
The present invention relates to a modified block copolymer composition comprising a thermoplastic polymer and a modified block copolymer.
More particularly, the present invention relates to a resinous modified block copolymer composition excellent in impact resistance, adhesion, paint adhesion, weatherability, resistance to heat aging, transparency and gloss and also to a rubbery or leather-like modified block copolymer composition excellent in heat resistance, abrasion resistance, compression set resistance, adhesion, transparency, oil resistance, weatherability and resistance to heat aging. Each of the abovementioned compositions comprises a thermoplastic polymer and a modified block copolymer comprising a base block copolymer of a monovinyl substituted aromatic hydrocarbon polymer block and an olefin compound polymer block having an ethylenic unsaturation degree not exceeding 20%, the base block copolymer having a molecular unit containing a carboxylic acid group and/or a group derived therefrom grafted thereonto.
DESCRIPTION OF THE PRIOR ART
Recently, thermoplastic resins such as polyamides, thermoplastic polyesters, thermoplastic polyurethanes, polyoxymethylene resins, polycarbonate resins, polysulfone resins, nitrile resins, polyphenylene ether resins and polyarylene sulfide resins have been widely used for mechanical parts and electrical parts for which excellent mechanical characteristics, high heat resistance and good durability are required. Weight reduction of the body of an automobile has been promoted to decrease fuel expenses as one of the energy-saving measures, and thermoplastic resins have attracted attention as light-weight materials for automobile parts which have excellent mechanical characteristics and durability.
However, these thermoplastic resins have some defects and fail to sufficiently satisfy requirements demanded in their application fields.
For example, polyoxymethylene resins and nitrile resins are advantageous in that they have very high tensile strength, flexural strength and flexural modulus, they can provide very tough molded articles and they are excellent in solvent resistance, but these resins are inferior in paint adhesion and they cannot advantageously be used as automotive exterior and interior trims or as exterior decorative materials of household electrical appliances. Polycarbonate resins have a very high mechanical strength and their impact strength is very high, but these resins are defective in that the paint adhesion is relatively poor. Furthermore, polyamides, thermoplastic polyesters, polysulfone resins, polyphenylene ether resins and polyarylene sulfide resins have a good heat resistance and a high mechanical strength, but they are defective in that the impact resistance is poor.
Block copolymers comprising a monovinyl substituted aromatic hydrocarbon and a conjugated diene compound, especially styrene-butadiene block copolymers, are polymeric materials which have recently attracted attentions.
Characteristic properties of these block copolymers differ according to the content of the monovinyl substituted aromatic hydrocarbon. More specifically, a block copolymer having a relatively low content of the monovinyl substituted aromatic hydrocarbon, even though it is unvulcanized, has a good elasticity at room temperature and shows rubbery characteristics. On the other hand, a block copolymer having a relatively high content of the monovinyl substituted aromatic hydrocarbon is excellent in transparency and impact resistance and shows resinous characteristics. Moreover, a block copolymer comprising a monovinyl substituted aromatic hydrocarbon and a conjugated diene compound shows at high temperatures flow characteristics similar to those of a thermoplastic resin, and this block copolymer is advantageous in that the block copolymer can easily be molded by an ordinary extruder or injection molding machine. However, the above-mentioned block copolymers are fatally defective in that the weatherability and resistance to thermal deterioration are poor, and therefore, they have been used only in the fields where such properties are not required. Furthermore, shoes prepared from these block copolymers are inferior to clogs prepared from a vinyl chloride polymer or the like in abrasion resistance and resistance to compression set. Accordingly, improvements of characteristics for overcoming these disadvantages have been desired.
In order to improve the weatherability and resistance to heat aging of the above-mentioned block copolymers, hydrogenating the conjugated diene compound polymer block in the block copolymers have been proposed in Canadian Pat. No. 815,575 and U.S. Pat. No. 3,431,323.
Although the weatherability or resistance to heat aging is improved to some extent according to this method, the hydrogenated block copolymer is defective in that the adhesion to other materials such as other plastics, metals, glass and woven fabrics is drastically degraded. As means for eliminating this defect, U.S. Pat. No. 3,792,124, discloses a method in which an ionically crosslinked product comprising ethylene and an .alpha.,.beta.-ethylenically unsaturated carboxylic acid is incorporated into the hydrogenated block copolymer. However the composition prepared by the method desclosed in U.S. Pat. No. 3,792,124 does not have a satisfactorily improved adhesion to other materials, and the composition is defective in that peeling is readily caused in the bonded surface under high humidity conditions or when immersed in water.
As a means for overcoming these defects of thermoplastic resins or block copolymers, there has been proposed a method in which a thermoplastic resin is mixed with a block copolymer to form a mixed polymer composition. For example, there can be mentioned mixed polymer compositions comprising a styrene-butadiene block copolymer, a styrene-isoprene block copolymer or a block copolymer obtained by partially hydrogenating the above-mentioned copolymer as one component of different polymers for providing a composition having excellent properties and a polar polymer such as a polyamide, polyester or polyurethane as the other component (see U.S. Pat. No. 4,017,558, U.S. Pat. No. 3,975,459, Japanese Patent Application LaidOpen Specification No. 75651/1975, U.S. Pat. No. 4,218,545 and U.S. Pat. No. 4,041,103). However, in these compositions, the block copolymer or hydrogenated block copolymer component is poor in compatibility with the polar polymer and the obtained mixed polymer composition is heterogeneous, and the properties cannot be satisfactorily improved. Moreover, when the mixed polymer composition is laminated with other material such as a metal, the adhesion between the mixed polymer composition and the metal is insufficient and peeling is readily caused.
As is apparent from the foregoing description, although thermoplastic resins and block copolymers comprising a monovinyl substituted aromatic hydrocarbon and a conjugated diene compound have various excellent properties, they cannot be materials sufficiently satisfying requirements demanded in the fields where they are actually used. Moreover, the mixtures of different polymers proposed for overcoming the defects of the thermoplastic resins or block copolymers do not have a satisfactorily improved characteristics. Accordingly, development of a polymer composition having properties required in various fields, for example, in the fields of mechanical parts, electrical parts, automobile parts, construction materials, sheets and films has been strongly desired in the art.
It is therefore a primary object of the present invention to provide a resinous modified block copolymer composition which is excellent in impact resistance, paint adhesion, weatherability, resistance to heat aging, transparency, gloss and adhesion. Another object of the present invention is to provide a rubbery or leather-like modified block copolymer composition which is excellent in heat resistance, abrasion resistance, resistance to compression set, adhesion, weatherability, resistance to heat aging, transparency and oil resistance.
SUMMARY OF THE PRESENT INVENTION
The present inventors have extensively and intensively researched polymer compositions comprising different polymers with a view to improving the compatibility between the different polymers and developing excellent polymer compositions retaining characteristics of the respective polymers. As a result, it has been determined that a modified block copolymer comprising a base block copolymer having a monovinyl substituted aromatic hydrocarbon polymer block and an olefin compound polymer block having an ethylenic unsaturation degree not exceeding 20% and a molecular unit containing a carboxylic acid group and/or a group derived therefrom, which is grafted to the base block copolymer, has a good compatibility with thermoplastic polymers such as polar group-containing polar thermoplastic polymers, polyoxymethylenes, or polycarbonates and that a modified block copolymer composition comprising this modified block copolymer and a thermoplastic polymer is excellent over conventional compositions in mechanical characteristics and has very excellent weatherability and resistance to heat aging. The present invention has been made based on such novel findings.
More specifically, in accordance with the present invention, there is provided a modified block copolymer composition comprising:
(a) at least one thermoplastic polymer selected from the group consisting of polar thermoplastic polymers each containing at least one polar functional group, polyoxymethylenes, polycarbonates, modified polycarbonates, polysulfones, modified polysulfones, nitrile polymers, polyphenylene ethers, modified polyphenylene ethers, polyarylene sulfides and modified polyarylene sulfies; and
(b) at least one modified block copolymer comprising a base block copolymer of at least one monovinyl substituted aromatic hydrocarbon polymer block A and at least one olefin compound polymer block B having an ethylenic unsaturation degree not exceeding 20%, the base block copolymer having at least one molecular unit grafted thereonto, with the at least one molecular unit containing at least one member selected from a carboxylic acid group and groups derived therefrom, the polar thermoplastic polymer excluding the modified block copolymer (b).
The modified block copolymer composition of the present invention is characterized in that a composition having characteristics of a resin (hereinafter often referred to as "resinous composition"), a composition having characteristics of a rubber (hereinafter often referred to as "rubbery composition") and a composition having characteirstics intermediate between characteristics of a resin and characteristics of a rubber (hereinafter often referred to as "leather-like composition") can be optionally selected according to an intended use by appropriately adjusting the ratio between the components (a) and (b) and the content of the monovinyl substituted hydrocarbon in the base block copolymer of the modified block copolymer. When the composition of the present invention is a resinous composition, it is especially excellent in impact resistance, adhesion, paint adhesion, weatherability, resistance to heat aging, transparency and gloss, and when the composition of the present invention is a rubbery or leather-like compositon, it is especially excellent in heat resistance, abrasion resistance, resistance to compression set, adhesion, transparency, oil resistance, weatherability and resistance to heat aging.
In the modified block copolymer composition of the present invention, since the modified block copolymer component (b) contains a reactive carboxylic acid group or a group derived therefrom in the molecule, when the component (a) is a polar thermoplastic polymer containing a polar group reactive with a carboxylic acid group or a group derived therefrom, chemical bonding is caused by mutual reaction of both the components or ionic crosslinkage is formed by both the components through a metal ion or the like, whereby the component (a) is strongly bonded to the component (b). When the component (a) is a polar group-free thermoplastic polymer, both the components show an excellent compatibility with each other because of physical mutual actions. Accordingly, the modified block copolymer composition of the present invention is excellent over conventional mixed different polymer compositons having an insufficient impact resistance due to a poor mutual compatibility in that the modified block copolymer composition of the present invention has excellent mechanical characteristics, and furthermore, the modified block copolymer composition of the present invention has both the characteristics of the component (a) and the characteristics of the component (b) the is practically very valuable. Moreover, since the olefin compound polymer block of the modified block copolymer has an ethylenic unsaturation degree not exceeding 20%, the modified block copolymer composition of the present invention is excellent in weatherability and resistance to heat aging over conventional block copolymers having a high ethylenic unsaturation degree, for example, styrene-butadiene block copolymers.
DETAILED DESCRIPTION OF THE INVENTION
The present invention will now be described in detail.
The component (a) of the modified block copolymer composition of the present invention is at least one thermoplastic polymer selected from the group consisting of polar thermoplastic polymers each containing at least one polar functional group, polyoxymethylenes, polycarbonates, modified polycarbonates, polysulfones, modified polysulfones, nitrile polymers, polyphenylene ethers, modified polyphenylene ethers, polyarylene sulfides and modified polyarylene sulfides, and the component (a) excludes the component (b). As the polar thermoplastic polymer containing at least one polar functional group, any polymer having a functional group capable of chemically linking to or capable of exhibiting a strong physical mutual action with a carboxylic acid group and/or a group derived therefrom present in the modified block copolymer (b) can be used. As preferred examples of the functional group, there can be mentioned an amino group, a hydroxyl group, a thiol group, a carboxyl group, an isocyanate group, an epoxy group and groups derived therefrom, such as a urethane group, an ester group, an amide group, an ammonium salt group and a metal carboxylate group. Thermoplastic polymers conatining at least one functional group selected from the foregoing groups are preferably used as the component (a). These functional groups may be bonded to either the terminals or the side chains of the polymers. As preferred examples of the polar thermoplastic polymer containing such polar functional group, there can be mentioned polyamides, thermoplastic polyesters, thermoplastic polyurethanes, vinyl alcohol polymers, vinyl ester polymers and ionomers. These polar thermoplastic polymers will now be described in detail.
As the polyamide, there can be mentioned a polycondensate of a dicarboxylic acid and a diamine, a polycondensate of an .alpha.-aminocarboxylic acid and a polymer produced by ring-opening polymerization of a cyclic lactam. More specifically, nylon-6, nylon-66, nylon-610, nylon-11, nylon-12, and copolymers thereof, such as nylon-6/nylon-66 and nylon-6/nylon-12 copolymers, are preferred. From the viewpoint of the processability of the composition, it is preferred that the number average molecular weight of the polyamide be 200 to 30,000, especially 200 to 20,000 and that the melting point of the polyamide be 150.degree. to 270.degree. C., especially 150.degree. to 220.degree. C. In the present invention, not only one polyamide but also a mixture of two or more of the polyamides may be used.
The polyester which is used in the present invention is a thermoplastic polyester having an ester linkage in the molecule, and a polyester having a structure formed by polycondensation of a dicarboxylic acid with a glycol is preferred. Polyesters of this type are obtained by polycondensing a dicarboxylic acid or a lower ester, acid halide or acid anhydride thereof with a glycol. As the starting aromatic or aliphatic dicarboxylic acid, there are preferably used oxalic acid, malonic acid, succinic acid, glutaric acid, pimelic acid, suberic acid, adipic acid, sebacic acid, azelaic acid, 1,9-nonane-dicarboxylic acid, 1,10-decane-dicarboxylic acid, 1,16-hexadecanedicarboxylic acid, terephthalic acid, isophthalic acid, p,p'-dicarboxydiphenyl, p-carboxyphenoxyacetic acid and 2,6-naphthalene-dicarboxylic acid. Mixtures of two or more of these dicarboxylic acids may also be used. Of the above-mentioned dicarboxylic acids, terephthalic acid and isophthalic acid are particularly preferred. An aliphatic or aromatic glycol (or diol) is used as the other starting material of the polyester. For example, there can be mentioned ethylene glycol, 1,3-propane diol, 1,2-propane diol, 1,4-butane diol, 1,6-hexane diol, 1,4-cyclohexane diol, 1,10-decane diol, neopentyl glycol and p-xylene glycol. These glycols may be used singly or in the form of a mixture of two or more of them. Of these glycols, alkylene glycols having 2 to 10 carbon atoms are preferred, and ethylene glycol and 1,4-butane diol are particularly preferred. Particularly valuable polyesters produced by polycondensation of the dicarboxylic acid with the glycol are polyethylene terephthalate and polybutylene terephthalate, and modified products thereof in which the monomer units are partly substituted with other monomer units.
From the standpoint of processability and mechanical strength of the composition, the number average molecular weight of the polyester is generally 500 to 100,000 and preferably 5,000 to 50,000.
The polymerization method for formation of the polyester used in the present invention is not particularly critical, and the polymerization may be carried out according to customary procedures. For example, there may be mentioned a method in which the above-mentioned acid component, for example, terephthalic acid, isophthalic acid, an aliphatic dicarboxylic acid or an ester thereof is subjected to direct esterification or ester exchange reaction with at least one member selected from the above-mentioned glycols at a time or stepwise and polymerization is then conducted. Catalysts, stabilizers, modifiers and additives customarily used may optionally be added.
Another valuable polyester which may be used in the present invention is a polylactone obtained by ring-opening polymerization of a cyclic lactone such as pivalolactone, .beta.-propiolactone or .epsilon.-caprolactone.
The above-mentioned polyesters have hydroxyl or carboxyl groups at the terminal ends of the molecule, and these terminal functional groups may be rendered unreactive by reaction with a monofunctional alcohol or carboxylic acid. It is preferred that all or part of the terminal ends of the molecule of the polyester have functional groups capable of reacting with the functional groups of the modified block copolymer. The polyester having these functional groups has a remarkably improved compatibility with the modified block copolymer because part of these functional groups is reacted with the modified block copolymer.
In the present invention, the foregoing polyesters may be used alone or in combination thereof.
The thermoplastic polyester referred to in the present invention includes polyesters used as fibers, films or resins, such as polyethylene terephthalate, low crystalline polyesters having a lower melting point, and polyether-ester block copolymers containing hard segments and soft segments in the molecule.
Thermoplastic polyurethanes which are used in the present invention are divided into completely thermoplastic polymers and incompletely thermoplastic polymers according to synthetic conditions, that is, the molar ratio of the NCO group of the diisocyanate relative to the OH group of the starting bifunctional polyol or glycol. More specifically, the polyurethane synthesized in a molar ratio of about 0.95<NCO/OH.ltoreq.1 is a completely thermoplastic polyurethane, and the polyurethane synthesized in a molar ratio of about 1<NCO/OH<1.1 is an incompletely thermoplastic polyurethane. As the thermoplastic polyurethane, there may be mentioned a polyurethane comprising a block of a polyol (polyester or polyether) and a diisocyanate as a soft segment and a block of a diisocyanate and a glycol as a hard segment.
As the starting polyester diol, there may be mentioned poly(1,4-butylene adipate), poly(1,6-hexane adipate) and polycaprolactone, and as the polyether diol, there may be mentioned polyethylene glycol, polypropylene glycol and polyoxytetramethylene glycol. As the glycol, there can be mentioned ethylene glycol, 1,4-butane diol and 1,6-hexane diol. As the diisocyanate, aromatic, alicyclic and aliphatic diisocyanates can be used. For example, there may be used tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, hexamethylene diisocyanate and isophorone diisocyanate.
Besides the foregoing thermoplastic polyurethanes, polyurethanes customarily used as adhesives, foams or paints may be used for the composition of the present invention, so far as they have a sufficient compatibility with the modified block copolymer used as the component (b) in the present invention.
From the standpoint of mechanical characteristics of the composition, it is preferred that the number average molecular weight of the thermoplastic polyurethane be 5,000 to 500,000, particularly 10,000 to 300,000.
In the present invention, homopolymers of vinyl esters and olefin-vinyl ester copolymers, such as polyvinyl acetate, ethylene-vinyl acetate copolymers and propylene-vinyl acetate copolymers, are preferably used as the vinyl ester polymer.
The vinyl alcohol polymers which are used in the present invention include a polymer composed of vinyl alchol units and a copolymer containing vinyl alchol units. The polymer composed of vinyl alchol units is a polymer obtained by partially or completely saponifying a vinyl ester polymer with an aqueous alkali. In the present invention, various polyvinyl alcohols can be used. An olefin-vinyl alcohol copolymer is preferably used as the copolymer containing vinyl alcohol units, and from the standpoint of processability and mechanical characteristics of the composition, an ethylene-vinyl alcohol copolymer is particularly preferred. The ethylene-vinyl alcohol copolymer is synthesized from the corresponding ethylene-vinyl acetate copolymer as the starting substance. An ethylene-vinyl acetate copolymer having a vinyl acetate content of 0.5 to 80 mole % is generally used, and an ethylene-vinyl alcohol copolymer obtained by saponifying 10 to 100 mole % of the vinyl acetate units of this ethylene-vinyl acetate copolymer is generally used.
As the commercially available vinyl alcohol polymer that can be used in the present invention, there may be mentioned EVAL manufactured and sold by Kuraray Co., Ltd., Japan and GL Resin manufactured and sold by Nippon Gosei Kagaku Co., Ltd., Japan.
The ionomer which is used in the present invention is an ionically crosslinked polymer obtained by ionically crosslinking carboxylic acid groups in a substrate copolymer of an .alpha.,.beta.-ethylenically unsaturated carboxylic acid and other monomer with at least one member selected the group consisting of monovalent, divalent and trivalent metal ions.
A copolymer of a non-polar monomer, for example, an olefin such as ethylene, propylene or butene or styrene and an .alpha.,.beta.-ethylenically unsaturated monocarboxylic acid such as acrylic acid or methacrylic acid or an .alpha.,.beta.-ethylenically unsaturated dicarboxylic acid such as maleic acid is generally used as the substrate polymer. An olefin-.alpha.,.beta.-ethylenically unsaturated carboxylic acid copolymer having an olefin content of at least 50 mole % and an .alpha.,.beta.-ethylenically unsaturated carboxylic acid content of 0.2 to 25 mole % is preferred.
The ionomer is prepared by reacting the above-mentioned substrate polymer, for example, an olefin-.alpha.,.beta.-ethylenically unsaturated carboxylic acid copolymer, with a monovalent, divalent or trivalent metal compound according to the process disclosed in Japanese Patent Application Publication No. 6810/1964. The metal compound is added in such an amount that 10 to 100 mole % of the carboxylic acid groups in the copolymer will be neutralized and participate in ionic crosslinkage.
As the olefin-.alpha.,.beta.-ethylenically unsaturated carboxylic acid, there may be mentioned, for example, an ethylene-acrylic acid copolymer, an ethylene-methacrylic acid copolymer, an ethylene-itaconic acid copolymer, an ethylene-maleic acid copolymer, an ethylene-acrylic acid-methacrylic acid copolymer and an ethylene-propylene-methacrylic acid copolymer. Of the above-mentioned copolymers, a copolymer comprising an unsaturated monocarboxylic acid, for example, an ethylene-acrylic acid copolymer or an ethylene-methacrylic acid copolymer, is preferred.
Monovalent, divalent and trivalent ions of metals of the Groups I, II, III, IV-A and VII of the Periodic Table are used as the metal ion for the production of the ionomer. For example, there may be mentioned monovalent ions such as Na.sup.+, Li.sup.+, K.sup.+, Cs.sup.+ and Ag.sup.+, divalent ions such as Mg.sup.2+, Ca.sup.2+, Ba.sup.2+, Zn.sup.2+, Sr.sup.2+, Hg.sup.2+ and Fe.sup.2+, and trivalent ions such as Al.sup.3+, and Fe.sup.3+. These metal ions are reacted with the substrate polymers in the form of hydroxides, alcoholates and low carboxylic acid salts.
The ionomer can also be prepared by saponifying an olefin-.alpha.,.beta.-ethylenically unsaturated carboxylic acid ester copolymer, for example, an ethylene-methyl methacrylate copolymer or an ethylene-methyl acrylate copolymer, with a hydroxide of a monovalent, divalent or trivalent metal or partially neutralizing the resulting saponification product to convert part of the saponification product to a corresponding carboxylic acid. The so-prepared ionomer may be used as the component (a) of the composition of the present invention.
As the commercailly available ionomer which can be used as the component (a) of the composition of the present invention, there may be mentioned "Surlyn" (the trade name of an ionomer manufactured and sold by Du Pont Co., U.S.A.), "Copolene" (the trade name of an ionomer manufactured and sold by Asahi-Dow Co., Ltd., Japan) and "Hi-Milan" (the trade name of an ionomer manufactured and sold by Mitsui Polychemical Co., Ltd., Japan).
The thermoplastic polymers which may be used as the component (a) of the modified block copolymer composition, other than the above-mentioned polar thermoplastic polymers, will now be described in detail.
As the polyoxymethylene which is used in the present invention, there may be mentioned a homopolymer obtained by polymerization of formaldehyde or trioxane or a copolymer comprising the above-mentioned monomer as the main component. The terminal groups of the homopolymer are generally converted to ester or ether groups to improve the heat resistance or chemical resistance. As the copolymer, there may be mentioned a copolymer of formaldehyde or trioxane with an aldehyde, a cyclic ether, a cyclic carbonate, an epoxide, an isocyanate or a vinyl compound.
An aromatic polycarbonate having a structural unit represented by the following general formula: ##STR1## wherein Ar.sup.1 and Ar.sup.1' stand for a phenylene group or a phenylene group substituted with an alkyl group, a substituted alkyl group, an alkoxy group, a halogen atom or a nitro group, and A stands for an alkylene group, an alkylidene group, a cycloalkylene group, a cycloalkylidene group, a sulfur atom, an oxygen atom, a sulfoxide group or a sulfone group, is preferably used as the polycarbonate in the present invention. Poly-4,4'-dioxydiphenyl-2,2'-propane carbonate is particularly preferred.
A thermoplastic polysulfone having a structural unit represented by the following general formula:
--Ar.sup.2 --B--Ar.sup.2 --So.sub.2 -- or --Ar.sup.2' --SO.sub.2 --
wherein Ar.sup.2 and Ar.sup.2' stand for a phenylene group, and B stands for an oxygen atom, a sulfur atom or an aromatic diol residue, is preferred as the polysulfone that is used in the present invention. Poly(ether sulfone) and poly(4,4-bisphenol ether sulfone) are particularly preferred.
Thermoplastic homopolymers and copolymers synthesized by using at least 50% by weight of an .alpha.,.beta.-olefinically unsaturated mononitrile as the constituent monomer are preferably used as the nitrile polymer in the present invention. As the .alpha.,.beta.-olefinically unsaturated mononitrile, there may be mentioned, for example, acrylonitrile, methacrylonitrile and .alpha.-bromoacrylonitrile. A mixture of two or more of these monomers may be used. As the monomer to be copolymrized with the .alpha.,.beta.-olefinically unsaturated mononitrile, there may be mentioned lower .alpha.-olefins such as ethylene, propylene, isobutylene, pentene-1, vinyl chloride and vinylidene chloride; monovinyl substituted aromatic hydrocarbons such as styrene, .alpha.-methylstyrene, vinyltoluene, chlorostyrene and methylstyrene; vinyl esters such as vinyl acetate; lower alkyl esters of .alpha.,.beta.-olefinically unsaturated carboxylic acids such as methyl acrylate and methyl methacrylate; and vinyl ethers such as vinyl methyl ether.
A polyphenylene ether having a structural unit represented by the following general formula: ##STR2## wherein R.sup.1 and R.sup.2 stand for an unsubstituted or substituted alkyl group having 1 to 4 carbon atom or a halogen atom, or a polyphenylene ether graft copolymer obtained for grafting a styrene type compound onto the above polyphenylene ether is preferably used as the polyphenylene ether in the present invention. As the styrene type compound used for the graft modification, there can be mentioned styrene, .alpha.-methylstyrene, methylstyrene, tert-butylstyrene and chlorostyrene. Two or more of these styrene type compounds may be used for the graft polymerization. If desired, other copolymerizable vinyl compounds such as acrylic acid esters, methacrylic acid esters, acrylonitrile and methacrylonitrile may be grafted together with the styrene type compound. Poly(2,6-dimethyl-1,4-phenylene) ether and a styrene-grafted copolymer thereof are particularly preferred as the polyphenylene ether.
Arylene sulfide homopolymers and copolymers having a structural unit represented by the following general formula:
--Ar.sup.3 --S--
wherein Ar.sup.3 stands for a phenylene group or a phenylene group substituted with an alkyl group or a substituted alkyl group, are preferably used as the polyarylene sulfide in the present invention. Polyphenylene sulfide and poly-4,4'-diphenylene sulfide are particularly preferred.
It is preferred that the modified polycarbonate, modified polysulfone, modified polyphenylene ether and modified polyarylene sulfide which is used in the present invention be respectively a blend of the above-mentioned polycarbonate, polysulfone, polyphenylene ether and polyarylene sulfide with an alkenyl aromatic hydrocarbon homopolymer and/or an alkenyl aromatic hydrocarbon copolymer as the modifying polymer. As the alkenyl aromatic hydrocarbon homopolymer or alkenyl aromatic hydrocarbon copolymer which is used for the modification, there may be mentioned polymers containing at least 50% by weight of a monovinyl substituted aromatic hydrocarbon, for example, polystyrene, a styrene-.alpha.-methylstyrene copolymer, a butadiene-styrene block copolymer, an impact-resistant rubber-modified styrene polymer, an acrylonitrile-styrene copolymer, a styrene-methacrylic acid ester copolymer, a styrene-maleic anhydride copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylic acid ester-butadiene-styrene copolymer, a methacrylic acid ester-butadiene-styrene copolymer and mixtures of two or more of the foregoing polymers. From the standpoint of modification effect, it is preferred that the content of the modifying polymer in the blend be 10 to 70% by weight, particularly 20 to 50% by weight.
The modified block copolymer which is used as the component (b) of the composition of the present invention is at least one modified block copolymer comprising a block copolymer (hereinafter referred to as "base block copolymer") having at least one monovinyl substituted aromatic hydrocarbon polymer block A and at least one olefin compound polymer block B having an ethylenic unsaturation degree not exceeding 20%, the base block copolymer having at least one molecular unit grafted thereonto, with the at least one molecular unit containing at least one member selected from a carboxylic acid group and a group derived therefrom. The olefin compound polymer block is preferably a polymer block in which at least one olefin compound selected from mono-olefins such as ethylene, propylene, 1-butene and isobutylene, conjugated diolefins such as butadiene, isoprene and 1,3-pentadiene and non-conjugated diolefins such as 1,4-hexadiene, norbornene and norbornene derivatives is homopolymerized or copolymerized, and the ethylenic unsaturation degree of this block does not exceed 20%. The term "ethylenic unsaturation degree" as used herein is intended to mean the percent of the number of the monomer units having an unsaturated bond relative to the number of all the monomer units constituting the olefin compound polymer block. Accordinly, the term "ethylenic unsaturation degree not exceeding 20%" as used herein is intended to mean that the percent of the number of the monomer units having an unsaturated bond relative to the number of all the monomer units constituting the olefin compound polymer block does not exceed 20%. It is preferred that the ethylenic unsaturation degree of the olefin compound polymer block be not more than 15%. If the olefin compound polymer block has an ethylenic unsaturation degree exceeding 20%, the weatherability and resistance to thermal deterioration of the composition are degraded, and no good results can be obtained. Accordingly, if a diolefin such as mentioned above is used as the constituent monomer of the olefin compound polymer block, it is necessary that the ethylenic unsaturation degree should be reduced by hydrogenation or the like to such an extent that the ethylenic unsaturation degree of the olefin compound polymer block does not exceed 20%, preferably not more than 15%. A monovinyl substituted aromatic hydrocarbon may be random-copolymerized to the olefin compound polymer block. As the base block copolymer, there may be mentioned a hydrogenation product of a block copolymer of a monovinyl substituted aromatic hydrocarbon and a conjugated diene compound, and a block copolymer of a monovinyl substituted aromatic hydrocarbon and a mono-olefin. A modified block copolymer which is preferably used in the present invention is one prepared by addition-reacting the above-mentioned base block copolymer with at least one modifier selected from unsaturated carboxylic acids and derivatives thereof. A modified block copolymer which is most preferably used in the present invention is a modified block copolymer obtained by selectively hydrogenating a block copolymer (hereinafter referred to as "precursory block copolymer") comprising at least one monovinyl substituted aromatic hydrocarbon polymer block and at least one polymer block composed mainly of a conjugated diene compound at its conjugated diene compound moiety so that the ethylenic unsaturation degree of the polymer block composed mainly of the conjugated diene compound does not exceed 20%, and addition-reacting the hydrogenated block copolymer with at least one modifier selected from unsaturated carboxylic acids and derivatives thereof. A precursory block copolymer comprising at least two monovinyl substituted aromatic hydrocarbon polymer blocks and at least one polymer block composed mainly of a conjugated diene compound is especially preferred. In the polymer block composed mainly of a conjugated diene compound, it is preferred that the monovinyl substituted aromatic hydrocarbon/conjugated diene compound weight ratio be in the range of from 0/100 to 50/50, particularly from 0/100 to 30/70. In the case where the conjugated diene compound is copolymerized with the monovinyl substituted aromatic hydrocarbon in this polymer block, the distribution of the monovinyl substituted aromatic hydrocarbon may be a random distribution, a tapering distribution (the monomer content increases or decreases along the molecule chain), a partially blocked distribution or any combination thereof. In the precursory block copolymer of the present invention, a portion of a copolymer of the monovinyl substituted aromatic hydrocarbon and the conjugated diene compound having a monovinyl substituted aromatic hydrocarbon content higher than 50% by weight may be present in the transitional portion between the monovinyl substituted aromatic hydrocarbon polymer block and the polymer block composed mainly of the conjugated diene compound. In the present invention, this copolymer portion is included in the polymer block composed mainly of the conjugated diene compound.
In the precursory block copolymer, the monovinyl substituted aromatic hydrocarbon content is 5 to 95% by weight, preferably 10 to 90% by weight, more preferably 15 to 85% by weight. When the monovinyl substituted aromatic hydrocarbon content is not more than 60% by weight, preferably not more than 55% by weight, the precursory block copolymer has characteristics as a thermoplastic elastomer, and when the monovinyl substituted aromatic hydrocarbon content is more than 60%, preferably more than 70%, the precursory block copolymer has characteristics as a resinous polymer.
At least one member selected from styrene, .alpha.-methylstyrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, dimethylstyrene and p-tert-butylstyrene is preferably used as the monovinyl substituted aromatic hydrocarbon constituting the precursory block copolymer, and styrene is particularly preferred. At least one member selected from butadiene, isoprene and 1,3-pentadiene is preferably used as the conjugated diene compound, and butadiene and/or isoprene is particularly preferred. The number average molecular weight of the precursory block copolymer is 20,000 to 500,000, preferably 40,000 to 300,000. It is preferred that the ratio of the weight average molecular weight relative to the number average molecular weight be in the range of from 1.05 to 10. The weight average molecular weight can be measured by the ultra-centrifugal method and the number average molecular weight can be measured by the osmotic pressure method. In the precursory polymer block, it is preferred that the vinyl content of the conjugated diene portion be 10 to 80%. When it is necessary that rubbery elasticity should be given to the modified block copolymer, it is preferred that the vinyl content be 25 to 65%, particularly 35 to 55%. The vinyl content of the precursory block copolymer can be measured by means of a nuclear magnetic resonance apparatus.
When the precursory block copolymer contains at least two monovinyl substituted aromatic hydrocarbon polymer blocks or at least two polymer blocks composed mainly of the conjugated diene, these blocks may have the same structure, or they may be different in monomer content, monomer distribution in the molecule chain, molecular weight of the block and linking manner of the conjugated diene portion.
As the method for preparing the precursory block copolymer, there may be mentioned methods disclosed in British Patent No. 895,980, British Patent No. 1,130,770, U.S. Pat. No. 3,281,383, Japanese Patent Application Publication No. 2423/1973 and U.S. Pat. No. 3,639,517. According to each of these methods, the monovinyl substituted aromatic hydrocarbon is block-copolymerized with the conjugated diene compound in a hydrocarbon solvent using as an anion polymerization initiator an organic lithium compound or the like and if necessary using as a vinyl modifier an ether compound such as diethyl ether or tetrahydrofuran, a tertiary amine such as triethyl amine or N,N,N',N'-tetramethylethylene diamine or a Lewis base such as a phosphine compound, e.g., hexamethylphosphamide, and as a coupling agent a polyfunctional compound such as silicon tetrachloride or epoxidized soy bean oil. A block copolymer having a linear, branched or radial structure can be obtained. In the present invention, a block copolymer prepared according to any of the foregoing polymerization methods can be used. Not only one precursory block copolymer but also a mixture of two or more precursory block copolymers may be used.
The base block copolymer can be obtained by hydrogenating the above-mentioned precursory block copolymer according to a known method, for example, the method disclosed in British Patent No. 1,020,720. It is requisite that at least 80%, preferably at least 85%, of the monomer units having an aliphatic double bond in the polymer block composed mainly of the conjugated diene compound in the precursory block copolymer should be hydrogenated. In other words, it is requisite that the ethylenic unsaturation degree of the olefin compound polymer block B formed by conversion of the polymer block composed mainly of the conjugated diene compound by hydrogenation should not exceed 20%, preferably not exceed 15%. As pointed out hereinbefore, if the ethylenic unsaturation degree of the olefin compound polymer block exceeds 20%, the weatherability or resistance to thermal deterioration of the composition is degraded and good results can not be obtained. From the standpoint of mechanical characteristics, it is preferred that the degree of hydrogenation of the monomer units containing aromatic double bonds derived from the monovinyl substituted aromatic hydrocarbon in the monovinyl substituted aromatic hydrocarbon polymer block and the monovinyl substituted aromatic hydrocarbon copolymerized according to need to the polymer block composed mainly of the conjugated diene compound be not more than 20%. The ethylenic unsaturation degree of the olefin compound polymer block can be measured by instrumental analysis using an infrared spectrophotometer (IR) or a nuclear magnetic resonance apparatus (NMR) or by titration analysis such as iodine titration.
The base block copolymer is then modified by addition reaction with at least one modifier selected from unsaturated carboxylic acids and derivatives thereof, whereby a modified block copolymer to be used in the present invention is obtained. As the unsaturated carboxylic acid or its derivative which is used as the modifier, there may be mentioned, for example, maleic acid, maleic anhydride, maleic acid esters, maleic acid amides, maleic acid imides, fumaric acid, fumaric acid esters, fumaric acid amides, fumaric acid imides, itaconic acid, itaconic anhydride, itaconic acid esters, itaconic acid amides, itaconic acid imides, halogenated maleic acid, halogenated maleic anhydride, halogenated maleic acid esters, halogenated maleic acid amides, halogenated maleic acid imides, cis-4-cyclohexene-1,2-dicarboxylic acid, cis-4-cyclohexene-1,2-dicarboxylic anhydride, cis-4-cyclohexene-1,2-dicarboxylic acid esters, cis-4-cyclohexene-1,2-dicarboxylic acid amides, cis-4-cyclohexene-1,2-dicarboxylic acid imides, endo-cis-bicyclo(2,2,1)-5-heptene-2,3-dicarboxylic acid, endo-cis-bicyclo(2,2,1)-5-heptene-2,3-dicarboxylic anhydride, endo-cis-bicyclo(2,2,1)-5-heptene-2,3-dicarboxylic acid esters, endo-cis-bicyclo(2,2,1)-5-heptene-2,3-dicarboxylic acid amide, endo-cis-bicyclo(2,2,1)-5-heptene-2,3-dicarboxylic acid imide, acrylic acid, acrylic acid esters, acrylic acid amide, methacrylic acid, methacrylic acid esters and methacrylic acid amide. These modifiers may be used alone or in combination thereof. Among these modifiers, unsaturated dicarboxylic acids and derivatives thereof are preferred and maleic anhydride is particularly preferred.
The modified block copolymer is obtained by grafting the above-mentioned modifier onto the base block polymer in a solution state or molten state in the presence or absence of a radical initiator. The method for preparing the modified block copolymer is not particularly critical in the present invention. However, a method providing a modified block copolymer containing an undesirable component such as gel or a modified block copolymer having an extremely high melt viscosity and degrading the processability of the composition is not preferred. For example, there is preferably adopted a method in which the base block copolymer is reacted with the above-mentioned modifier in the presence of a radical initiator in, for example, an extruder.
The amount of the molecular unit containing a carboxylic acid group or a group derived therefrom, which is contained in the modified block copolymer, that is, the amount of the unsaturated carboxylic acid or its derivative grafted onto the base block copolymer, is 0.05 to 30 parts by weight, preferably 0.1 to 20 parts by weight, more preferably 0.3 to 10 parts by weight, per 100 parts by weight of the base block copolymer, as the mean value in the entire modified block copolymer used in the present invention. When this amount of the molecular unit containing a carboxylic acid group or a group derived therefrom is smaller than 0.05 part by weight, no significant modification effect can be obtained over the unmodified block copolymer, and even if this amount exceeds 30 parts by weight, no substantial increase of the modification effect can be attained.
The content of the molecular unit containing a carboxylic acid group or a group derived therefrom in the modified block copolymer can be easily determined by infrared spectrophotometry or titration. In the present invention, the unmodified block copolymer may be contained in the modified block copolymer used as the component (b), so far as the amount of the unsaturated carboxylic acid or its derivative grafted onto the base block copolymer as the mean value in the entire component (b) is in the above-mentioned range.
In the present invention, the modified block copolymer may be an ionically crosslinked modified block copolymer. This ionically crosslinked modified block copolymer is obtained by crosslinking the above-mentioned modified block copolymer through at least one member selected from monovalent, divalent and trivalent metal ions. Namely, the crosslinked modified block copolymer is prepared by reacting the modified block copolymer with at least one crosslinking agent selected from monovalent, divalent and trivalent metal compounds.
In the ionically crosslinked modified block copolymer, the carboxylic acid group and/or the group derived therefrom of the modified block copolymer is ionized by addition of the above-mentioned crosslinking agent. The degree of ionization can be adjusted according to the amount of the crosslinking compound employed, and the degree of ionization can be determined by, for example, an infrared spectrophotometer.
The crosslinking agent is added in such an amount that a carboxylic acid group and/or a group derived therefrom, which is contained in the modified block copolymer, is partially or completely ionized. The ionization reaction is advanced substantially quantitatively, but in some case, in order to obtain the desirable degree of ionization, it is necessary to add the crosslinking agent in excess of the stoichiometrical amount. In order to obtain the ionically crosslinked modified block copolymer effectively, it is preferred that the ratio of the mole number of the metal compound relative to the total mole number of the carboxylic acid group and the group derived therefrom, contained in the modified block copolymer be in the range of from 0.1 to 3.0.
At least one member selected from compounds of metals of the Groups I, II and III of the Periodic Table is preferably used as the crosslinking agent to be added to the modified block copolymer for formation of the ionically crosslinked modified block copolymer. More specifically at least one member selected from lithium compounds, sodium compounds, potassium compounds, magnesium compounds, calcium compounds, zinc compounds and aluminum compounds is preferably used. It is preferred that these compounds are hydroxides, alcoholates or carboxylic acid salts.
As the method for obtaining the ionically crosslinked modified block copolymer, there may be mentioned a method in which the crosslinking agent is added to the melt of the modified block copolymer, a method in which the modified block copolymer is dissolved in an appropriate solvent, for example, an organic solvent such as toluene, benzene or tetrahydroruran and the crosslinking agent is added to the solution to effect the crosslinking reaction, and a method in which the crosslinking agent is added to a latex of the modified block copolymer. Any of these methods can be used for formation of the ionically crosslinked modified block copolymer to be used in the present invention.
The ionically crosslinked modified block copolymer which is used in the present invention is thermoplastic, and a composition obtained by mixing this modified block copolymer with the component (a) is processable at high temperatures, and the ionic crosslinkage is a reversible crosslinkage. These characteristic properties are not possessed by block copolymers obtained through irreversible crosslinkage such as sulfur crosslinkage, peroxide crosslinkage or irradiation crosslinkage.
The composition of the present invention includes an ionically crosslinked composition obtained by adding the crosslinkage agent to a mixture of the thermoplastic polymer as the component (a) and the modified block copolymer as the component (b) which is molten or dissolved in an appropriate solution, to effect the crosslinking reaction.
From the standpoint of mechanical characteristics of the composition, it is preferred that the monovinyl substituted aromatic hydrocarbon content of the base block copolymer of the component (b) of the modified block copolymer composition of the present invention be 5 to 95% by weight. When the modified block copolymer as the component (b) is required to have a rubbery elasticity, it is preferred that the monovinyl substituted aromatic hydrocarbon content of the base block copolymer be 5 to 60% by weight. On the other hand, when the modified block copolymer as the component (b) is required to have resinous characteristics, it is preferred that the monovinyl substituted aromatic hydrocarbon content of the base block copolymer be over 60% by weight up to 95% inclusive by weight. As pointed out hereinbefore, the modified block copolymer composition of the present invention can be a resinous composition, a rubbery composition or a leather-like composition according to the ratio of the thermoplastic polymer as the component (a) relative to the modified block copolymer as the component (b) and the monovinyl substituted aromatic hydrocarbon content of the base block copolymer of the modified block copolymer as the component (b). In the case where a resinous composition is obtained, when the monovinyl substituted aromatic hydrocarbon content of the base block copolymer is over 60% by weight up to 95% inclusive by weight, preferably 65 to 90% by weight, the component (a)/component (b) weight ratio is adjusted in the range of from 90/10 to 5/95, preferably from 85/15 to 10/90, more preferably from 80/20 to 15/85, and when the monovinyl substituted aromatic hydrocarbon content of the base block copolymer is 5 to 60% by weight, preferably 10 to 55% by weight, more preferably 15 to 50% by weight, the component (a)/component (b) weight ratio is adjusted in the range of from over 50/50 up to 98/2 inclusive, preferably from 60/40 to 95/5, more preferably from 70/30 to 90/10. When the amount of the component (b) is too small and below the above range, no substantial effect of improving the impact resistance or paint adhesion can be attained, and when the amount of the component (b) is too large, the rigidity is degraded. In the case where a rubbery or leather-like composition is prepared, when the monovinyl substituted aromatic hydrocarbon content of the base block copolymer is 5 to 60% by weight, preferably 10 to 55% by weight, more preferably 15 to 55% by weight, the component (a)/component (b) weight ratio is adjusted in the range of from 2/98 to 50/50, preferably 5/95 to 40/60, more preferably from 10/90 to 30/70. When the amount of the component (a) is too small and below the above range, no substantial improvement of the composition as a rubbery or leather-like composition can be attained. When the amount of the component (a) is too large, the rubbery or leather-like characteristics are lost and the composition becomes resinous.
Reinforcers, fillers, antioxidants, ultraviolet absorbers, coloring agents, pigments, lubricants, flame retardants, foaming agents and other additives may be added to the modified block copolymer composition of the present invention. Specific examples of the additives which can be added to the composition of the present invention are described in "Handbook of Additive Chemicals to Rubbers and Plastics" published by Rubber Digest Co., Ltd, Japan in 1974.
For example, a composition obtained by adding 5 to 150 parts by weight, preferably 10 to 100 parts by weight, of a glass fiber to 100 parts by weight of the resinous modified block copolymer composition of the present invention is an excellent molding material having improved rigidity, heat resistance and mechanical strength. Glass fibers having a diameter of 2 to 20.mu. and a length of 50 to 20,000.mu., customarily incorporated into resins, are preferably used.
When the rubbery or leather-like modified block copolymer composition of the present invention is used as a material for a shoe sole or an industrial article, a finely divided solid such as calcium carbonate, clay, silica or titanium dioxide may be added as a filler or pigment, and a hardness adjusting agent, for example, a resin such as polystyrene or polyolefin and a moldability adjusting agent, for example, a process oil such as a paraffin oil or a naphthene oil may be added according to need. An Example of the amounts of these additive added to the modified block copolymer composition are as follows:
Rubbery or leather-like composition of the present invention: 100 parts by weight
Resin: 30 to 100 parts by weight
Process oil: 50 to 100 parts by weight
Finely divided filler: 20 to 200 parts by weight
The modified block copolymer composition of the present invention may be formed by mixing the components (a) and (b) by means of a mixing device appropriately selected according to the mixing ratio of the components (a) and (b) from various mixing devices such as a single screw extruder, a multiple screw extruder, a mixing roll, a Banbury mixer and a kneader. It is preferred that the mixing be carried out in the molten state. Moreover, the composition of the present invention can be formed according to a method in which the respective components are dissolved in an organic solvent such as toluene, benzene or tetrahydrofuran and the solvent is removed from the resulting mixture by heating.
The modified block copolymer composition of the present invention can be easily molded into various, practically valuable products such as sheets, foams, films and injection molded, blow molded, pressure formed and rotary molded articles having various shapes according to optional known molding methods such as extrusion molding, injection molding, blow molding and rotary molding methods.
The so-obtained molded articles formed of the modified block copolymer of the present invention may be painted or plated according to need. Any of known paints such as acrylic resin paints, vinyl-modified acrylic resin paints, alkyd resin paints, polyurethane resin paints, epoxy resin paints, phenolic resin paints, melamine resin paints and urea resin paints may be used for painting these molded articles.
A metallic feel can be imparted to the molded articles by a plating treatment. Any of the known plating methods such as chemical plating and electrical plating methods may be adopted. In case of the resinous modified block copolymer composition of the present invention comprising the ionically crosslinked modified block copolymer as the compoennt (b), when the incorporated amount of the component (a) is relatively large, the component (b) is dispersed in the component (a) in the peculiar form different from the circular or oval form observed in conventional different polymer mixtures, and therefore, when a molded article of this composition is chemically etched and then plated, a high anchor effect can be attained and a plated molded article having a high plate adhesion can be obtained.
PREFERRED EMBODIMENTS OF THE INVENTION
The present invention will now be described in more detail with reference to the following Examples.
In the Examples, the number average molecular weights of polymers were determined according to the osmotic pressure method and the weight average molecular weights were determined according to the ultra-centrifugal method. Furthermore, the melt index values referred to in the Examples are those determined according to the method of ASTM D-1238.
(1) Preparation of Unmodified Block Copolymers
Unmodified block copolymers shown in Table 1 were prepared by subjecting butadiene and styrene to anionic block copolymerization in n-hexane or cyclohexane as a solvent by using n-butyl lithium as a polymerization catalyst and tetrahydrofuran as a vinyl content adjusting agent. For example, an unmodified block copolymer A-1 was prepared by performing polymerization according to the following procedures. To an n-hexane solution containing 13 parts by weight of butadiene (butadiene concentration, 20% by weight) were added 0.1 part by weight of n-butyl lithium and 5 parts by weight of tetrahydrofuran, and polymerization was carried out at about 60.degree. C. for 1 hour. After substantial completion of the polymerization of butadiene, an n-hexane solution containing 20 parts by weight of styrene (styrene concentration, 20% by weight) was added to the resulting reaction mixture and polymerization was carried out at about 60.degree. C. for 1 hour. After substantial completion of the polymerization of styrene, an n-hexane solution containing 47 parts by weight of butadiene (butadiene concentration, 20% by weight) was added to the resulting reaction mixture and polymerization was carried out at about 60.degree. C. for 1 hour. After substantial completion of the polymerization of butadiene, an n-hexane solution containing 20 parts by weight of styrene (styrene concentration, 20% by weight) was added to the resulting reaction mixture and polymerization was carried out at about 60.degree. C. for 1 hour to obtain the unmodified block copolymer A-1.
When unmodified block copolymers A-4 and A-5 were prepared, silicon tetrachloride was used as a coupling agent.
2,6-Di-tert-butyl-4-methylphenol (hereinafter often referred to as "BHT") was added as a stabilizer to each of the unmodified block copolymers shown in Table 1.
TABLE 1__________________________________________________________________________Unmodified Vinyl Content*.sup.2 Number Aver-Block Polymer Styrene Content (%) in Buta- age Molecu-Copolymer Structure % by weight) diene Block lar Weight__________________________________________________________________________A-1 B--S--E--S 40 42 64,000A-2 55,000A-3 S--B--S 30 38 75,000A-4 Si(B--S).sub.4 30 48 164,000A-5 Si(B--S).sub.4 70 53 105,000A-6 S--B'--S 80 36 120,000__________________________________________________________________________ Note: *.sup.1 B stands for a butadiene polymer block, B'stands for a butadienestyrene random compolymer block, and S stands for a styrene polymer block. *.sup.2 The vinyl content was measured using a nuclear magnetic resonance apparatus.
(2) Preparation of Hydrogenated Block Copolymers
The unmodified block copolymer shown in Table 1 was put in an n-hexane/cyclohexane mixed solvent or a cyclohexane solvent, and hydrogenation was carried out at 50.degree. C. under a hydrogen pressure of 7 Kg/cm.sup.2 for 5 hours using cobalt naphthenate and triethyl aluminum as catalysts, whereby there was obtained a selectively hydrogenated block copolymer in which about 90% of double bonds of the butadiene block were hydrogenated but benzene rings of the styrene block were scarcely hydrogenated. The metals of the catalyst residue were removed by washing with an aqueous solution of hydrochloric acid and methanol.
The hydrogenated block copolymers obtained by thus hydrogenating the unmodified block copolymers A-1 through A-6 shown in Table 1 are designated as hydrogenated block copolymers B-1 through B-6, respectively.
(3) Preparation of Modified Hydrogenated Block Copolymers
To 100 parts by weight of the so-obtained hydrogenated block copolymer was added 1 to 5 parts by weight of maleic anhydride so that a desired amount of maleic anhydride was added to the hydrogenated block copolymer, and 0.1 part by weight of Perhexa 25B [the trade name of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane manufactured and sold by Nippon Yushi K.K., Japan] was added to the mixture, and the mixture was homogeneously blended and supplied to a single screw extruder having a diameter of 20 mm [length/diameter ratio (hereinafter often referred to as "L/D")=24]. The maleinization reaction was carried out at a cylinder temperature of 250.degree. C. to prepare a modified copolymer. Unreacted maleic anhydride was removed from the modified hydrogenated block copolymer by heating under reduced pressure, and BHT was added as a stabilizer in an amount of 0.5 part by weight per 100 parts by weight of the modified copolymer. Thus, modified hydrogenated block copolymers shown in Table 2 were prepared. The analysis values of the obtained modified hydrogenated block copolymer are shown in Table 2. The modified hydrogenated block copolymers obtained by hydrogenating and modifying the unmodified block copolymers A-1, A-2, A-4, A-5 and A-6 shown in Table 1 are designated as modified hydrogenated block copolymers C-1, C-2, C-5, C-6 and C-7, respectively. The modified hydrogenated block copolymers obtained by hydrogenating the unmodified block copolymer A-3 and modifying the hydrogenated block copolymer so that the amounts of maleic anhydride grafted onto the hydrogenated block copolymer were 1.2% by weight and 0.7% by weight are designated as modified hydrogenated block copolymers C-3 and C-4, respectively.
TABLE 2______________________________________ Amount of Maleic Anhydride*.sup.3 Tolune-Modified Polymer Grafted onto InsolubleHydrogenated before Hydrogenated ComponentBlock Hydro- Block Copolymer ContentCopolymer genation (% by weight) (% by weight)______________________________________C-1 A-1 1.4 0.04C-2 A-2 1.8 0.04C-3 A-3 1.2 0.04C-4 0.7 0.05C-5 A-4 2.3 0.05C-6 A-5 1.2 0.02C-7 A-6 0.5 0.01______________________________________ Note: *.sup.3 The amount of maleic anhydride grafted onto the hydrogenated bloc copolymer was measured by the neutralization titration method using sodiu methylate.
(4) Preparation of Modified Unhydrogenated Block Copolymers
Modified unhydrogenated block copolymers D-1, D-2, and D-3 were prepared by grafting maleic anhydride onto the unmodified block copolymers A-2, A-3 and A-5 according to the following procedures.
To 100 parts by weight of the unmodified block copolymer was added 2 to 5 parts by weight of maleic anhydride so that a desired amount of maleic anhydride was grafted onto the unmodified block copolymer, and 0.3 part by weight of BHT and 0.2 part by weight of phenothiazine were added to the mixture. The mixture was homogeneously blended using a mixer.
The mixture was supplied to a single extruder having a diameter of 20 mm (L/D=24) and the maleinization reaction was carried out at a cylinder temperature of 250.degree. C. to prepare a modified copolymer. Unreacted maleic anhydride was removed from the obtained modified copolymer by drying under reduced pressure. Then, 0.5 part by weight of BHT was added to 100 parts by weight of the modified copolymer. Thus, modified unhydrogenated block copolymers shown in Table 3 were prepared. The analysis values of the obtained modified unhydrogenated polymers are shown in Table 3.
TABLE 3______________________________________ Amount of Maleic Anhydride GraftedModified onto UnmodifiedUnhydrogenated Polymer before Block CopolymerBlock Copolymer Modification (% by weight)______________________________________D-1 A-2 1.8D-2 A-3 0.7D-3 A-5 1.2______________________________________
(5) Preparation of Ionically Crosslinked Modified Block Copolymer
Ionically crosslinked modified block copolymers E-1 through E-4 were obtained according to a recipe shown in Table 4. When the ionic crosslinking was carried out in a solvent, the solvent was removed by heating after the crosslinking reaction. By the infrared spectrum, it was confirmed that the acid anhydride groups in the samples E-1 through E-4 were ionized.
TABLE 4__________________________________________________________________________ Ionically Crosslinked Modified Block CopolymerConditions E-1 E-2 E-3 E-4__________________________________________________________________________Ionic Crosslinking ReactionModified Hydrogenated C-2 C-5 C-6 C-7Block CopolymerCrosslinking Kind CH.sub.3 ONa Mg(OH).sub.2 Al(OH).sub.3 KOHagent Amount (parts 0.5 0.7 0.5 0.1 by weight)*.sup.4 Crosslinking 0.5 0.5 0.5 0.25 Agent/Acid Anhydride Molar RatioCrosslinking in toluene in molten in molten in moltenReaction Method solution, state, mix- state, Bra- state, Bra- 20 wt. % ing roll, bender bender polymer 160.degree. C., 15 Plasto- Plasto- concentra- minutes graph, 200.degree. C., graph, tion, room 5 minutes 200.degree. C., 5 temperature, minutes 1 hour__________________________________________________________________________ Note: *.sup.4 The amount added per 100 parts by weight of the modified hydrogenated block copolymer.

EXAMPLES 1 AND 2 AND COMPARATIVE EXAMPLES 1 AND 2
A resinous composition was obtained by mixing 80 parts by weight of nylon 6 (number average molecular weight: 18,000) as the polar thermoplastic polymer with 20 parts by weight of the modified hydrogenated block copolymer C-1 shown in Table 2 by means of a screw type extruder having a diameter of 30 mm (twin, L/D=28).
Another resinous composition was obtained in the same manner as described above except that the modified block copolymer C-2 was used instead of the modified hydrogenated block copolymer C-1.
For comparison, a comparative resinous composition was obtained in the same manner as described above except that the unmodified block copolymer A-1 shown in Table 1 was used instead of the modified hydrogenated block copolymer C-1 or C-2.
Another comparative resinous composition was obtained in the same manner as described above except that the unmodified block copolymer A-3 was used instead of the modified hydrogenated copolymer C-1 or C-2 or the unmodified block copolymer A-1.
Test pieces were prepared of the so-obtained resinous compositions by injection molding, and the physical properties of the test pieces were measured. The obtained results are shown in Table 5.
As will be readily understood from the results shown in Table 5, the compositions of the present invention are excellent in compatibility and have a highly improved impact resistance over the comparative compositions.
TABLE 5______________________________________ Com- Com- parative parative Example Example Example Example 1 2 1 2______________________________________Composition(% by weight)Modified hydro- 20 -- -- --genated blockcopolymer C-1Modified hydro- -- 20 -- --genated blockcopolymer C-3Unmodified block -- -- 20 --copolymer A-1Unmodified block -- -- -- 20copolymer A-3Nylon 6 80 80 80 80Physical propertiesIzod impact 21.0 18.5 6.0 5.4strength (Kg .multidot. cm/cm,notched)*.sup.5Tensile strength 610 590 450 430(yield point)Kg/cm.sup.2)*.sup.6Elongation (%)*6 115 110 60 56Transparency 13.2 14.5 56.0 58.5(Haze) (%)*.sup.7______________________________________ Note: *.sup.5 The Izod impact strength was measured according to ASTM D256. *.sup.6 The tensile strength and elongation were measured according to ASTM D638. *.sup.7 The transparency was measured according to JIS K6714.
EXAMPLE 3 AND COMPARATIVE EXAMPLE 3
A rubbery composition was obtained by kneading 30 parts by weight of nylon 6 (number average molecular weight: 18,000) as a polar thermoplastic polymer with 70 parts by weight of the modified hydrogenated block copolymer C-1 shown in Table 2 for 10 minutes by means of a Brabender Plastograph. Test pieces were prepared of the obtained composition by compression molding, and the physical properties were determined.
For comparison, a comparative rubbery composition was obtained in the same manner as described above except that the unmodified block copolymer A-1 shown in Table 1 was used instead of the modified hydrogenated block copolymer C-1, and test pieces were prepared of the composition and the physical properties were determined.
The obtained results are shown in Table 6.
As will be readily understood from the results shown in Table 6, the composition of the present invention comprising the modified hydrogenated block copolymer and nylon 6 is highly improved in compatibility over the comparative composition, as is proved by the values of the transparency. Moreover, the composition of the present invention has high tensile strength and modulus and is improved in heat resistance represented by the tensile strength at a high temperature. Furthermore, the composition of the present invention is characterized by a highly improved weatherability.
TABLE 6______________________________________ Comparative Example 3 Example 3______________________________________Composition (parts by weight)Modified hydrogenated block 70 --copolymer C-1Unmodified block copolymer A-1 -- 70Nylon 6 30 30Physical properties25.degree. C. Hardness *8 94 93 Tensile strength *8 195 78 (breaking point) (Kg/cm.sup.2) 300% Modulus *8 (Kg/cm.sup.2) 175 70 Elongation *8 400 33050.degree. C. Tensile strength *8 100 30 (breaking point) (Kg/cm.sup.2)70.degree. C. Tensile strength *8 70 12 (breaking point) (Kg/cm.sup.2)Oil resistance *9 (volume in- 23 45crease ratio) (%) (oil JIS No.3, 23.degree. C., 22 hours)Transparency (Haze) (%) 15 65Weatherability (%) *10 (strength 96 34retention after 100 hours'exposure in weatherometer)______________________________________ Note:- *8 The hardness, tensile strength, 300% modulus and elongation were measured according to JIS K6301. *9 The oil resistance (volume increase ratio) was measured according to JIS K6310. *10 The weatherability was evaluated based in the elongation retention, that is, the ratio of the elongation of the test piece after 100 hours' exposure in the weatherometer (XWWR available from Atlas Co., U.S.A.; light irradiation only) to the elongation of the test piece before the exposure, and was calculated according to the following Elongation retention (%) (weatherability) ##STR3##
EXAMPLES 4 AND 5 AND COMPARATIVE EXAMPLES 4 AND 5
Resinous compositions were prepared in the same manner as in Examples 1 and 2 and Comparative Examples 1 and 2 except that nylon 66 (number average molecular weight: 20,000) was used instead of nylon 6. In the same manner as in Examples 1 and 2 and Comparative Examples 1 and 2, test pieces were prepared of the obtained compositions and the physical properties were determined. The obtained results are shown in Table 7.
TABLE 7______________________________________ Com- Com- parative parative Example Example Example Example 4 5 4 5______________________________________Composition(parts by weight)Modified hydro- 20 -- -- --genated blockcopolymer C-1Modified hydro- -- 20 -- --genated blockcopolymer C-3Unmodified block -- -- 20 --copolymer A-3Unmodified block -- -- -- 20copolymer A-3Nylon 66 80 80 80 80Physical propertiesIzod impact 28 24 7.6 7.0strength*.sup.5 Kg .multidot. cm/cm,notched)Tensile strength*.sup.6 660 630 475 460(yield point)(Kg/cm.sup.2)Elongation*.sup.6 (%) 54 51 45 47Transparency*.sup.7 14.8 15.2 58.0 61.5(Haze) (%)______________________________________ Note: *.sup.5,*.sup.6,*.sup.7 See the Note under Table 5.
EXAMPLES 6 AND 7 AND COMPARATIVE EXAMPLES 6 AND 7
A resinous composition was obtained by mixing 80 parts by weight of PBT 1041 (the trade name for polybutylene terephthalate manufactured and sold by Toray Industries Inc., Japan) as a polar thermoplastic polymer with 20 parts by weight of the modified hydrogenated block copolymer C-1 shown in Table 2 by means of a screw type extruder having a diameter of 30 mm (twin, L/D=28).
Another resinous composition was obtained in the same manner as described above except that the modified hydrogenated block copolymer C-3 was used instead of the modified hydrogenated block copolymer C-1.
For comparison, a comparative resinous composition was obtained in the same manner as described above except that the unmodified block copolymer A-1 shown in Table 1 was used instead of the modified hydrogenated block copolymer C-1 or C-3.
Another comparative resinous composition was obtained in the same manner as described above except that the unmodified block copolymer A-3 was used instead of the modified hydrogenated block copolymer C-1 or C-3 or the unmodified block copolymer A-1.
Test pieces were prepared of the so-obtained compositions by injection molding, and the physical properties thereof were measured. The obtained results are shown in Table 8.
TABLE 8______________________________________ Com- Com- parative parative Example Example Example Example 6 7 6 7______________________________________Composition(parts by weight)Modified hydro- 20 -- -- --genated blockcopolymer C-1Modified hydro- -- 20 -- --genated blockcopolymer C-3Unmodified block -- -- 20 --copolymer A-1Unmodified block -- -- -- 20copolymer A-3Polybutylene 80 80 80 80terephthalatePhysical propertiesIzod impact 5.2 5.6 2.4 2.3strength*.sup.5(Kg .multidot. cm/cm,notched)Tensile strength*.sup.6 514 532 505 500(yield point)(Kg/cm.sup.2)Elongation*.sup.6 (%) 36 30 28 25Heat distortion 150 152 152 150temperature*.sup. 11(.degree. C.) (under loadof 4.64 Kg/cm.sup.2)______________________________________ Note: *.sup.11 The heat distortion temperature was measured according to ASTM D648. *.sup.5 and *.sup.6 See the Note under Table 5.
EXAMPLE 8 AND COMPARATIVE EXAMPLE 8
A polyester prepared from ethylene glycol (diol component), terephthalic acid (dicarboxylic acid component) and isophthalic acid (dicarboxylic acid component) and having a softening point of 195.degree. C. and an intrinsic viscosity of 0.75 (as measured at 35.degree. C. in o-chlorophenol) was used as a polar thermoplastic polymer.
A rubbery composition was obtained by mixing 20 parts by weight of the above-mentioned polyester as a polar thermoplastic polymer with 80 parts by weight of the modified hydrogenated block copolymer C-1 shown in Table 2 by using a screw type extruder having a diameter of 30 mm (twin, L/D=28).
For comparison, a comparative rubbery composition was prepared in the same manner as described above except that the unmodified block copolymer A-1 shown in Table 1 was used instead of the modified hydrogenated block copolymer C-1.
Test pieces were prepared of the so-obtained compositions by compression molding, and the physical properties thereof were determined. The obtained results are shown in Table 9. ##STR4##
As will be readily understood from the results shown in Table 9, the composition of Example 8 comprising the modified hydrogenated block copolymer and the polyester is excellent over the composition of Comparative Example 8 comprising the unmodified block copolymer and the polyester in mechanical properties such as the tensile strength and 300% modulus, the oil resistance and the heat resistance represented by the tensile strength retention at 50.degree. C., and the composition of the present invention is a very valuable material.
EXAMPLES 9 THROUGH 11 AND COMPARATIVE EXAMPLES 9 AND 10
A resinous composition was obtained by mixing and kneading EVAL EP-E [the trade name for an ethylene-vinyl alcohol copolymer, obtained by saponifying an ethylene-vinyl acetate copolymer, manufactured and sold by Kuraray Co., Ltd., Japan] with the modified hydrogenated block copolymer C-1 shown in Table 2 at a mixing ratio shown in Table 10 by means of a mixing roller.
Another resinous composition was obtained by mixing and kneading 75 parts by weight of EVAL EP-E with 25 parts by weight of the modified hydrogenated block copolymer C-3 by means of a mixing roller.
A comparative resinous composition was obtained by mixing and kneading 75 parts by weight of EVAL EP-E with 25 parts by weight of the unmodified block copolymer A-1 shown in Table 1 by means of a mixing roll.
Another comparative resinous composition was obtained in the same manner as described above except that the unmodified block copolymer A-3 shown in Table 1 was used instead of the unmodified block copolymer A-1.
Test pieces were prepared of the so-obtained compositions by compression molding, and the physical properties thereof were determined. The obtained results are shown in Table 10. Furthermore, the adhesion of each composition to high density polyethylene was determined. The obtained results are also shown in Table 10.
TABLE 10__________________________________________________________________________ Comparative Comparative Example 9 Example 10 Example 11 Example 9 Example 10__________________________________________________________________________Composition (parts by weight)Modified hydrogenated 25 10 -- -- --block copolymer C-1Modified hydrogenated -- -- 25 -- --block copolymer C-3Unmodified block -- -- -- 25 --copolymer A-1Unmodified block -- -- -- -- 25copolymer A-3EVAL EP-E 75 90 75 75 75Physical propertiesMelt index (200.degree. C., 5 Kg 5.1 9.6 6.8 24.8 25.6load) (g/10 min)Izod impact strength*.sup.5 82.5 12.0 11.1 3.4 3.6(Kg .multidot. cm/cm, notched)Tensile strength*.sup.6 (yield 330 420 382 340 356point) (Kg/cm.sup.2)Tensile strength*.sup.8 270 318 306 314 320(breaking point) (Kg/cm.sup.2)Elongation (%)*.sup.8 58 75 63 24 21Adhesion to high density 3.0 1.6 2.1 0.3 0.2polyethylene*.sup.12 (T-peel-ing strength) (Kg/25 mm)__________________________________________________________________________ Note: *.sup.5 and *.sup.6 See the Note under Table 5. *.sup.8 See the Note under Table 6. *.sup.12 The adhesion to high density polyethylene was determined according to JIS K6854.
As will be readily understood from the results shown in Table 10, the composition of Example 9 comprising the modified hydrogenated block copolymer has a tensile strength (yield point) substantially comparable to that of the composition of Comparative Example 9 comprising the corresponding unmodified block copolymer, but the notched Izod impact strength of the composition of Example 9 is extremely improved over that of the comparative composition.
When the samples of the compositions of Example 9 and Comparative Example 9 were observed by a phase contrast microscope, it was found that in the sample of Example 9, the modified block copolymer is uniformly dispersed in the form of particles having a size of about 0.5 to about 2.mu. in the matrix of the ethylene-vinyl alcohol copolymer, wherease in the sample of Comparative Example 9, unmodified block copolymer particles having a size of about 5 to about 10.mu. or larger are dispersed. Accordingly, it has been confirmed that there is a distinct difference of the compatibility between the two samples.
Furthermore, it has been confirmed that the composition of the present invention has an improved adhesion to polyethylene.
EXAMPLES 12 AND 13 AND COMPARATIVE EXAMPLES 11 AND 12
Each composition shown in Table 11 was prepared by using a mixing roller. Test pieces were prepared of the obtained composition by compression molding. The physical properties thereof were determined. The obtained results are shown in Table 11.
TABLE 11______________________________________ Com- Com- parative parative Example Example Example Example 12 13 11 12______________________________________Composition(parts by weight)Modified hydro- 75 90 -- --genated blockcopolymer C-1Unmodified block -- -- 75 90copolymer A-1EVAL EP-E 25 10 25 10Physical propertiesMelt index (200.degree. C., 5.7 2.8 17.0 13.55 Kg load)(g/10 min)Hardness*.sup.8 89 87 87 87300% modulus*.sup.8 86 82 44 31(Kg/cm.sup.2)Tensile strength*.sup.8 196 205 178 190(breaking point)(Kg/cm.sup.2)Oil resistance*.sup.30 23 48 53 54(weight increase(%) (oil JIS No.3, 24 hours'dipping)Adhesion to high 7.4 6.2 1.6 1.7density poly-ethylene*.sup.12(T-peelingstrength)(Kg/25 mm)______________________________________ Note: *.sup.8 See the Note under Table 6. *.sup.12 See the Note under Table 10. *.sup.30 The oil resistance was determined according to JIS K6310.
As will be readily understood from the results shown in Table 11, the modulus of the composition of the present invention is highly improved and the oil resistance is remarkably improved by addition of a small amount of the ethylene-vinyl alcohol copolymer. Moreover, the adhesion to polyethylene is improved with respect to the composition of the present invention.
EXAMPLES 14 THROUGH 16 AND COMPARATIVE EXAMPLES 13 THROUGH 15
Compositions of the present invention and comparative compositions were obtained by mixing Paraplene P-22 SM (the trade name for a thermoplastic polyurethane manufactured and sold by Nippon Polyurethane Co., Ltd., Japan) as a polar thermoplastic polymer according to the recipe shown in Table 12 by means of a Brabender Plastograph.
Each of the obtained compositions was press-bonded at 180.degree. C. to a polyvinyl chloride sheet or a high density polyethylene sheet and the peeling strength was measured according to JIS K-6854. The obtained results are shown in Table 12.
TABLE 12__________________________________________________________________________ Example Example Example Comparative Comparative Comparative 14 15 16 Example 13 Example 14 Example 15__________________________________________________________________________Composition Modified hydrogenated 10 60 90 -- -- --(parts by block copolymer C-1weight) Unmodified block -- -- -- 10 60 90 copolymer A-1Polyurethane (Para- 90 40 10 90 40 10 plene P-22 SM)Adhesion to polyvinyl 9.2 8.9 6.0 8.0 2.8 0.9chloride (90.degree. peeling strength)(Kg/25 mm)Adhesion to polyethylene 8.3 12.1 13.0 1.2 2.0 3.7(180.degree. peeling strength)(Kg/25 mm)__________________________________________________________________________
As will be readily understood from the results shown in Table 12, the composition of the present invention has excellent adhesion characteristics to polyvinyl chloride and polyethylene sheets within a broad mixing ratio. In contrast, the adhesiveness of the comparative composition is inferior to that of the corresponding composition of the present invention.
EXAMPLES 17 AND 18
A mixture obtained by impregnating 100 parts by weight of the hydrogenated block copolymer B-1 used for formation of the modified hydrogenated block copolymer C-1 shown in Table 2 (obtained by hydrogenating the unmodified block copolymer A-1 shown in Table 1) with 2.5 parts by weight of acrylic acid was homogeneously mixed with 0.1 part by weight of Perhexa 25B [the trade name of 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane available from Nippon Yushi K.K., Japan]. The obtained mixture was supplied into a screw type extruder having a diameter of 20 mm (single, L/D=24) and the reaction was carried out at a cylinder temperature of 210.degree. C. to modify the hydrogenated block copolymer B-1. Unreacted acrylic acid was removed from the obtained modified hydrogenated block copolymer by heating under reduced pressure. Then, BHT was added as a stabilizer in an amount of 0.5 part by weight per 100 parts by weight of the obtained polymer. The so-obtained modified hydrogenated block copolymer is designated as "F- 1".
A modified hydrogenated block copolymer was prepared in the same manner as described above except that the hydrogenated block copolymer B-3 used for formation of the modified hydrogenated block copolymer C-3 (obtained by hydrogenating the unmodified block copolymer A-3 shown in Table 1) was used instead of the hydrogenated block copolymer B-1. The obtained modified hydrogenated block copolymer is designated as "F-2".
The analysis values of the so-obtained modified hydrogenated block copolymers are shown in Table 13.
TABLE 13__________________________________________________________________________Modified Amount (% by weight)hydrogenated of acrylic acid grafted Melt index Toluene-insolubleblock Polymer before onto hydrogenated (200.degree. C., components contentcopolymer hydrogenation block copolymer 5 Kg load) (% by weight)__________________________________________________________________________F-1 A-1 2.05 1.1 0.05F-2 A-3 1.87 0.9 0.05__________________________________________________________________________
The amount of grafted onto the hydrogenated block copolymer was measured by the neutralizing titration method using sodium methylate.
A resinous composition was obtained in the same manner as described in Examples 4 and 5 except that F-1 was used as the modified hydrogenated block copolymer.
Another resinous composition was obtained in the same manner as described above except that F-2 was used as the modified hydrogenated block copolymer.
In the same manner as described in Examples 4 and 5, test pieces were prepared of the so-obtained compositions, and the physical properties thereof were measured. The obtained results are shown in Table 14.
TABLE 14______________________________________ Example 17 Example 18______________________________________Composition (parts by weight)Modified hydrogenated block 20 --copolymer F-1Modified hydrogenated block -- 20copolymer F-2Nylon 66 80 80Physical propertiesIzod impact strength*.sup.5 32 29(Kg .multidot. cm/cm, notched)Tensile strength*.sup.6 670 650(yield point) (Kg/cm.sup.2)Elongation*.sup.6 (%) 50 50Transparency*.sup.7 (Haze) (%) 17.3 19.1______________________________________ Note: *.sup.5,*.sup.6 and *.sup.7 See the Note under Table 5.
As will readily be understood from the results shown in Table 14, the compositions of the present invention comprising modified hydrogenated block copolymers have improved impact strengths as compared with the compositions of Comparative Examples 4 and 5 (see Table 7).
EXAMPLES 19 AND 20 AMD COMPARATIVE EXAMPLES 16 THROUGH 21
Compositions were prepared by mixing block copolymers shown in Table 15 with the same nylon 66 as used in Examples 4 and 5 or the same EVAL EP-E as used in Examples 9 through 11, and the Izod impact strength was measured and the weatherability test and the heat aging resistance test were carried out.
It was confirmed that the compositions of the present invention are excellent in impact resistance, weatherability and resistance to heat aging.
TABLE 15__________________________________________________________________________ Comparative Comparative Example Example Example Example 19 16 17 18 20 19 20 21__________________________________________________________________________Composition (parts by weight)Block Copolymer Kind C-3 A-3 B-3 D-2 C-2 A-2 B-2 D-1 Amount 20 25Thermoplastic Kind nylon 66 EVAL EP-EResin Amount 80 75Izod Impact Strength *5 24 7.0 8.1 22 85 3.4 3.9 82(Kg .multidot. cm/cm, Notched)Weatherability *3 (%) 72 42 71 45 83 54 80 59Heat aging 80 51 78 55 77 48 75 51Resistance *14 (%)__________________________________________________________________________ Note:- *5 See the Note under Table 5. *13 Before and after 500 hours' exposure (light irradiation only) in a weatherometer (XWWR available from Atlas Co., U.S.A.), the Izod impact strength (unnotched) of the test pieces was measured, and the weatherability was evaluated based on the Izod impact strength retention after the exposure in the weatherometer, which was calculated according t the following formula: Izod impact strength retention (weatherability (%) ##STR5## *14 Before and after standing in air at 100.degree. C. for one month, the Izod impact strength (unnotched) of the test pieces was measured, and the resistance to thermal deterioration was evaluated based on the Izod impac strength retention, which was calculated according to the following formula: Izod impact strength retention (heat aging resistance) (%) =- ##STR6##
EXAMPLE 21 AND COMPARATIVE EXAMPLE 22
A modified hydrogenated block copolymer C-1' having maleic anhydride grafted onto the hydrogenated block copolymer in an amount of 4.1% by weight was prepared in the same manner as adopted for the production of the modified hydrogenated block copolymer C-1 except that 7 parts by weight of maleic anhydride was incorporated into 100 parts by weight of the hydrogenated block copolymer B-1 (obtained by hydrogenating the unmodified block copolymer A-1 shown in Table 1).
A modified ethylene-propylene copolymer rubber G-1 was prepared in the same manner as described above except that JSR EP57P (the trade name of an ethylene-propylene copolymer rubber manufactured and sold by Nippon Gosei Gomu K.K., Japan) was used instead of the hydrogenated block copolymer B-1. The amount of maleic anhydride grafted was 3.0% by weight.
A resinous composition was obtained by mixing 20 parts by weight of the so-obtained modified hydrogenated block copolymer C-1' with 80 parts by weight of the same nylon-66 as used in Examples 4 and 5 by means of a screw type extruder having a diameter of 30 mm (twin, L/D=28).
A comparative resinous composition was obtained in the same manner as described above except that the modified ethylene-propylene copolymer rubber G-1 as prepared above was used instead of the modified hydrogenated block copolymer C-1'.
Test pieces were prepared of the obtained compositions by injection molding, and the physical properties thereof were determined. Futhermore, test pieces having a thickness of 0.5 mm were prepared of the compositions, and the transparency was measured. The obtained results are shown in Table 16. From the results shown in Table 16, it is apparent that the composition of the present invention is excellent in transparency and impact resistance.
TABLE 16______________________________________ Example Comparative 21 Example 22______________________________________Composition (parts by weight)Modified hydrogenated 20 --block copolymer C-1'Modified ethylene-propylene -- 20copolymer rubber G-1Nylon 66 80 80Physical PropertiesIzod impact strength*.sup.5 75 68(Kg .multidot. cm/cm, notched)Tensile strength*.sup.6 630 635(yield point) (Kg/cm.sup.2)Elongation (%)*.sup.6 35 30Transparency (Haze) (%).sup.*7 23.1 38.5______________________________________ Note: *.sup.5, *.sup.6 and *.sup.7 See the Note under Table 5.
EXAMPLES 22 THROUGH 27 AND COMPARATIVE EXAMPLES 23 THROUGH 26
Compositions comprising Surlyn A-1706 (the trade name of a partially metal-crosslinked ethylene-acrylic acid copolymer available from Du Pont Co., U.S.A.) as the component (a) were prepared by mixing according to the recipe shown in Table 17 by means of rollers. The physical properties of the test pieces prepared from these compositions by compression molding are shown in Table 17.
As will be readily understood from the results shown in Table 17, the composition of the present invention is improved over the comparative compositions in tensile strength and oil resistance. Incidentally, in Examples 22 through 27, it was confirmed by an infrared spectrophotometer that the acid anhydride groups in the modified block copolymer participated in the ionic crosslinking.
Then, the adhesion of each composition to an aluminum plate was examined. It was found that the compositions of the present invention are excellent over the comparative compositions in adhesive properties. The compositions of the present invention have a good adhesion even after immersion in water, and this is a great characteristic not possessed by the comparative compositions.
TABLE 17__________________________________________________________________________ Comparative Example Example No. No. 22 23 24 25 26 27 23 24 25 26__________________________________________________________________________CompositionComponent (a) Amount (% 30 20 10 30 20 10 30 20 10 -- by weight)Component (b) Amount (% 70 80 90 70 80 90 70 80 90 100 by weight)Physical Properties300% Modulus*.sup.8 (Kg/cm.sup.2) 64 57 55 70 65 60 51 45 44 35Tensile strength*.sup.8 205 187 243 230 213 255 153 167 210 180(breaking point) (Kg/cm.sup.2)Oil resistande*.sup.28 (weight 13 18 30 10 15 25 42 51 72 60increase) (%)Adhesion to Before Im- 21.0 17.3 28.5 23.6 19.5 33.1 1.8 1.3 0.9 0.5aluminium mersion inplate*.sup.31 (peel- Watering strength) After Im- 6.3 5.2 8.4 7.1 5.7 9.8 0.2 0.2 0.1 0.1(Kg/25 mm) mersion in Water__________________________________________________________________________ Note: *.sup.8 See the Note under Table 6. *.sup.28 See the Note under Table 11. *.sup.31 The adhesion was measured under the following conditions according to the following method. Measurement method: JIS K6854 Bonding conditions: temperature of 200.degree. C., compression pressure o 20 Kg/cm.sup.2 Immersion conditions: room temperature (about 20.degree. C.), 24 hours, i water
EXAMPLES 28 THROUGH 33 AND COMPARATIVE EXAMPLES 27 THROUGH 30
Compositions comprising Copolene QD-400 (the trade name of a partially metal-crosslinked ethylene-acrylic acid copolymer manufactured and sold by Asahi Down Co., Japan) as the component (a) were obtained by mixing according to the recipe shown in Table 18 by means of mixing rolls. The physical properties of the test pieces prepared of the obtained compositions by compression molding are shown in Table 18. Then, the adhesion of each composition to nylon (undrawn sheet of nylon 6) was examined. The obtained results are shown in Table 18.
From the results shown in Table 18, it is apparent that the compositions of the present invention are excellent over the comparative compositions in tensile strength and adhesiveness.
TABLE 18__________________________________________________________________________ Comparative Example No. Example No. 28 29 30 31 32 33 27 28 29__________________________________________________________________________CompositionComponent (a) Amount (% 80 70 60 80 70 60 80 70 60 by weight)Component (b) Kind C-5 C-6 C-2 E-2 E-3 E-1 A-4 A-5 A-2 Amount (% 20 30 40 20 30 40 20 30 40 by weight)Physical PropertiesTensile Strength*.sup.6 (yield 270 250 220 285 265 235 245 230 200point) (Kg/cm.sup.2)Adhesion to Before Im- 5.1 3.7 7.0 6.5 4.6 9.4 1.2 1.0 1.1nylon sheet*.sup.32 mersion in(peeling strength) Water(Kg/25 mm) After Im- 3.4 2.8 5.4 4.7 3.1 6.2 0.2 0.1 0.1 mersion in Water__________________________________________________________________________ Note: *.sup. 6 See the Note under Table 5. *.sup.32 The adhesion was measured under the following conditions according to the following method. Measurement method: JIS K6854 Bonding conditions: temperature of 200.degree. C., compression pressure o 20 Kg/cm.sup.2 Immersion conditions: room temperature (about 20.degree. C.), 24 hours, i water
EXAMPLES 34 THROUGH 43 AND COMPARATIVE EXAMPLES 30 THROUGH 41
Compositions comprising a thermoplastic polymer and a block copolymer, as shown in Table 19, were prepared. More specifically, 100 parts by weight of a thermoplastic polymer was sufficiently mixed with 10 parts by weight of a block copolymer by a Henschel mixer, and the mixture was pelletized by a screw type extruder having a diameter of 40 mm (single, L/D=28). A flat plate having a size of 120 mm.times.120 mm.times.3 mm was prepared from the pelletized composition by injection molding. The obtained flat plate was degreased with methyl alcohol, spray-coated with Acryca B160 (the trade name of an acrylic resin paint available from Kawakami Toryo K.K., Japan), and naturally dried. In case of the composition comprising a polyoxymethylene or nitrile resin as the thermoplastic polymer, the plate was, instead of being degreased with methyl alcohol, immersed in a 0.1N hydrochloric acid solution for 30 seconds and spray-washed with water.
Each resulting plate was subjected to the paint adhesion test. The obtained results are shown in Table 19. As is apparent from the results shown in Table 19, the compositions of the present invention are excellent in paint adhesion.
TABLE 19______________________________________ Kind of Kind of Block Thermoplastic Paint Ad- Copolymer Polymer*.sup.15 hesion*.sup.19______________________________________Example 34 modified hydro- PO .circle. genated block copolymer C-2Example 35 modified hydro- PC .circleincircle. genated block copolymer C-2Example 36 modified hydro- PS .circleincircle. genated block copolymer C-2Example 37 modified hydro- NR .circle. genated block copolymer C-2Example 38 modified hydro- PPE .circleincircle. genated block copolymer C-2Example 39 modified hydro- GPPE .circleincircle. genated block copolymer C-2Example 40 modified hydro- PPS .circleincircle. genated block copolymer C-2Example 41 modified hydro- PC + PET*.sup.16 .circle. genated block copolymer C-2Example 42 modified hydro- PS + PA*.sup.17 .circle. genated block copolymer C-2Example 43 modified hydro- PO + TPET*.sup.18 .circle. genated block copolymer C-2Comparative unmodified block PO XExample 30 copolymer A-2Comparative unmodified block PC .DELTA.Example 31 copolymer A-2Comparative unmodified block PS .DELTA.Example 32 copolymer A-2Comparative unmodified block NR XExample 33 copolymer A-2Comparative unmodified block PPE .circle.Example 34 copolymer A-2Comparative unmodified block PPS .DELTA.Example 35 copolymer A-2Comparative hydrogenated block PO XExample 36 copolymer B-2Comparative hygrogenated block PC .DELTA.Example 37 copolymer B-2Comparative hydrogenated block PS .DELTA.Example 38 copolymer B-2Comparative hydrogenated block NR XExample 39 copolymer B-2Comparative hydrogenated block PPE .circle.Example 40 copolymer B-2Comparative hydrogenated block PPS .DELTA.Example 41 copolymer B-2______________________________________Note:*.sup.15 The thermoplastic polymers used are as follows (PS,PPE and PPS are products of companies in U.S.A. and otherresins are products of Japanese companies):Abbrevi-ation Thermoplastic Polymer Maker Trade namePC polycarbonate Teijin Kasei Panlite L-1225PS polysulfone ICI Polyether Sulfone 200PPPE polyphenylene ether General Noryl 701 ElectricGPPE styrene-grafted Asahi-Dow Xylon 500H polyphenylene etherPPS polyphenylene sulfide Phillips Ryton R-6 PetroleumPBT polybutylene Toray PBT 1041 terephthalateTPET thermoplastic Toyobo Pelprene polyester P150BPA polyamide Toray Amilan CM-1017ABS acrylonitrile-butadi- Asahi-Dow Stylac 181 ene styrene copolymerHIPS impact-resistant Asahi-Dow Styron 492 rubber modified polystyrenePO: polyoxymethylene (polyoxymethylene diacetate havinga melt index of about 10 g/10 min as measured at210.degree. C. under a load of 2.16 kg was used)NR: nitrile resin [acrylonitrile/styrene (90/10)copolymer having a melt index of about 1 g/10 minas measured at 190.degree. C. under a load of 12.5 kg was used]*.sup.16 A mixture of PC/PET (2/1 weight ratio) was used as thethermoplastic polymer.*.sup.17 A mixture of PS/PA (2/1 weight ratio) was used as thethermoplastic polymer.*.sup.18 A mixture of PO/TPET (4/1 weight ratio) was used asthermoplastic polymer.*.sup.19 Eleven cut lines having an interval of 1 mm were formedwith a knife on the coated surface of the flat plate inboth the longitudinal direction and the lateral directionto form 100 cut squares. A pressure sensitive adhesive cellophanetape was applied to the coated surface and the tape waspeeled off in the vertical direction. The adhesivenesswas evaluated based on the number of cut squares peeledtogether with the tape..circleincircle.: up to 10 of peeled squares .circle. : 11 to 20 of peeled squares.DELTA.: 21 to 40 of peeled squaresX: 41 or more of peeled squares
EXAMPLES 44 THROUGH 47 AND COMPARATIVE EXAMPLES 42 THROUGH 53
Compositions comprising a thermoplastic polymer and a block copolymer, shown in Table 20, were prepared in the following manner. Namely, 100 parts by weight of a thermoplastic polymer was mixed with 50 parts by weight of a block copolymer by a screw type extruder having a diameter of 40 mm (single L/D=28) and the mixture was pelletized. Test pieces were prepared of the pelletized composition by injection molding. The Izod impact strength and gloss thereof were measured and the weatherability and heat aging tests were carried out. The obtained results are shown in Table 20. In Table 20, there are also shown the values of the gloss measured for the test pieces of the composition comprising the ionic crosslinking product E-3 of the modified block copolymer C-6, which was used as a block copolymer. From the results shown in Table 20, it is seen that the compositions of the present invention are excellent in weatherability and heat aging resistance as expressed in strength retention.
TABLE 20__________________________________________________________________________ Izod impact Heat Thermo- Strength *5 Weather- AgingBlock plastic (Kg .multidot. cm/cm, Gloss *20 ability *21 Resistance *14Copolymer Polymer notched (%) (%) (%)__________________________________________________________________________Example 44 modified hy- PC 38.6 70 (75) 73 78 drogenated block copoly- mer C-6Example 45 modified hy- PS 10.4 61 (68) 76 80 drogenated block copoly- mer C-6Example 46 modified hy- GPPE 29.5 71 (77) 74 87 drogenated block copoly- mer C-6Example 47 modified hy- PPS 4.6 62 (70) 79 85 drogenated block copoly- mer C-6Comparative unmodified PC 29.1 63 31 45Example 42 block copoly- mer A-5Comparative unmodified PS 6.3 55 34 47Example 43 block copoly- mer A-5Comparative unmodified GPPE 24.2 66 36 55Example 44 block copoly- mer A-5Comparative unmodified PPS 2.5 57 40 54Example 45 block copoly- mer A-5Comparative hydrogenated PC 30.0 64 72 76Example 46 block copoly- mer B-5Comparative hydrogenated PS 6.9 54 74 79Example 47 block copoly- mer B-5Comparative hydrogenated GPPE 25.0 67 74 87Example 48 block copoly- mer B-5Comparative hydrogenated PPS 2.8 55 79 85Example 49 block copoly- mer B-5Comparative modified unhy- PC 34.5 70 32 47Example 50 drogenated block copoly- mer D-3Comparative modified unhy- PS 8.5 60 34 47Example 51 drogenated block copoly- mer D-3Comparative modified unhy- GPPE 27.0 71 38 56Example 52 drogenated block copoly- mer D-3Comparative modified unhy- PPS 3.5 60 41 54Example 53 drogenated block copoly- mer D-3__________________________________________________________________________ Note:- *5 See the Note under Table 5 *14 See the Note under Table 15. *20 The gloss was measured according to the method of JIS Z8741. Each parenthesized value in Table 20 is the value of gloss measured with respcet to the composition comprising the ionic crosslinking product E3 o the modified hydrogenated block copolymer C6 instead of the copolymer C6. *21 After and before 1000 hours' exposure (light irradiation only) in a weatherometer (XWWR manufactured and sold by Atlas Co., U.S.A.), the Izod impact strength (unnotched) of test pieces was measured, and the Izod impact retention after the exposure in the weatherometer was calculated according to the following formula: Izod impact strength retention (weatherability) (%) =- ##STR7##
EXAMPLES 48 THROUGH 51 AND COMPARATIVE EXAMPLES 54 THROUGH 57
Compositions of the present invention and comparative compositions were prepared according to the recipes shown in Table 21 by using a screw type extruder having a diameter of 40 mm (single, L/D=28). Test pieces were prepared of the obtained compositions by injection molding, and the Izod impact strength thereof was measured. The obtained results are shown in Table 21. From the results shown in Table 21, it is seen that the composition of the present invention is excellent in impact resistance. Incidentally, polystyrene having a weight average molecular weight of about 220,000 was used in Example 50 and Comparative Example 56.
TABLE 21__________________________________________________________________________ Example No. Comparative Example No. 48 49 50 51 54 55 56 57__________________________________________________________________________Block Co- Kind Modified hydrogenated unmodified blockpolymer block copolymer C-5 copolymer A-4 Amount (% 10 20 20 10 10 20 20 10 by weight)Thermoplastic First Kind PC PS GPPE PPS PC PS GPPE PPSpolymer*.sup.15 Component Amount (% 70 60 65 70 70 60 65 70 by weight) Second Kind ABS HIPS poly- HIPS ABS HIPS poly- HIPS Component styrene styrene Amount (% 20 20 15 20 20 20 15 20 by weight)Izod Impact 46.1 19.0 35.3 16.5 35.2 13.4 29.6 10.7Strength*.sup.5 (Kg .multidot. cm/cm/ notched)__________________________________________________________________________ Note: *.sup.5 See the Note under Table 5. *.sup.15 See the Note under Table 19.
EXAMPLES 52 AND 53 AND COMPARATIVE EXAMPLES 58 AND 59
The unmodified block copolymer A-5 was hydrogenated according to the same method as adopted for production of the hydrogenated block copolymers B-1 through B-6 to obtain two hydrogenated block copolymers having hydrogenation degrees of about 86% and about 60%, respectively. The hydrogenated block copolymers were modified according to the same method as adopted for production of the modified hydrogenated block copolymer C-6 to obtain modified hydrogenated block copolymers C-6' and C-6" having a hydrogenation degree different from that of C-6. Compositions comprising the modified hydrogenated block copolymer C-6, the obtained modified hydrogenated block copolymer C-6' or C-6" or the modified unhydrogenated block copolymer D-3 were obtained according to the recipe shown in Table 22 by using a screw type extruder having a diameter of 40 mm (single, L/D=28). Test pieces were prepared of the obtained compositions by injection molding, and the weatherability and heat aging tests were carried out. The obtained results are shown in Table 22.
From the results shown in Table 22, it is seen that when a modified block copolymer prepared from a block copolymer having a hydrogenation degree lower than 80% (an ethylenic unsaturation degree exceeding 20%) is used, the weatherability and resistance to heat aging are degraded.
TABLE 22______________________________________ Comparative Example Example 52 53 58 59______________________________________Unhydrogenated polymer A-5used for formation ofmodified block copolymerHydrogenation degree (%) 90 86 60 0Amount (% by weight) of 1.2 1.3 1.3 1.2maleic anhydride graftedonto the block copolymerComposition modified block C-6 C-6' C-6" D-3(parts by copolymerweight) amount 50 50 50 50 thermoplastic PC PC PC PC polymer*.sup.15 amount 100 100 100 100Weatherability*.sup.21 (%) 73 70 53 32Heat aging 78 71 55 47resistance*.sup.14 (%)______________________________________ Note: *.sup.15 See the Note under Table 19. *.sup.21 See the Note under Table 20. *.sup.14 See the Note under Table 15.
EXAMPLES 54 AND 55
Compositions of the present invention containing a glass fiber were prepared according to the recipe shown in Table 23 by using a screw type extruder having a diameter of 30 mm (twin, L/D=28). Test pieces were prepared of the obtained compositions by injection molding, and the Izod impact strength was measured. The obtained results are shown in Table 23.
TABLE 23______________________________________ Example 54 Example 55______________________________________Composition (parts by weight)modified hydrogenated block 30 --copolymer C-6modified hydrogenated block -- 10copolymer C-4thermoplastic polymer PS*.sup.15 40 --thermoplastic polymer PPE*.sup.15 -- 70glass fiber*.sup.22 30 20Physical PropertyIzod impact strength*.sup.5 12.5 23.1(Kg .multidot. cm/cm, notched)______________________________________ Note: *.sup.5 See the Note under Table 5. *.sup.15 See the Note under Table 19. *.sup.22 CS 99A401 (the trade name of a glass fiber manufactured and sold by Nittobo Co., Japan) was used.
EXAMPLES 56 THROUGH 63 AND COMPARATIVE EXAMPLES 60 THROUGH 66
Compositions of the present invention and comparative compositions comprising a block copolymer and a thermoplastic polymer, shown in Table 24, were prepared according to the recipe shown below by using a screw type extruder having a diameter of 30 mm (twin, L/D=28) for kneading.
______________________________________ AmountComposition Recipe (parts by weight)______________________________________modified hydrogenated block copolymer 100C-2 or unmodified block copolymer A-2thermoplastic polymer*.sup.23 50Shellflex 311 (the trade name of a 50naphthene type process oil manufac-tured and sold by Sankyo YukaCo., Ltd., Japan)titanium oxide 1stabilizer*.sup.24 0.7______________________________________ Note: *.sup.23 A powdery product having a particle size of about 50 mesh, which was obtained by freezepulverizing the pelletized thermoplastic polymer, was used. *.sup.24 2,2'-Methylene-bis(4-methyl-6-tert-butylphenol) was used as the stabilizer.
Test pieces of the obtained compositions were prepared by molding, and the tensile strength, abrasion resistance and compression permanent strain thereof were determined. The obtained results are shown in Table 24.
From the results shown in Table 24, it is seen that the composition of the present invention is excellent over the comparative composition comprising an unmodified block copolymer in tensile strength, abrasion resistance and resistance to compression permanent strain.
According to the method described in the Note *10 under Table 6, the weatherability test was carried out. It was found that the test pieces of the compositions of Examples 56 through 63, after the weatherability test, substantially retained the characteristics and rubbery elasticity, while with respect to the test pieces of the compositions of Comparative Examples 62 through 68, the elongation retention at the tensile test was lower than 30% and the rubbery elasticity was lost, showing considerable deterioration.
TABLE 24__________________________________________________________________________ Abrasion Compression Permanent Thermo- Tensile*.sup.8 Resis- Strain (%)*.sup.26 Block Co- plastic Strength tance*.sup.25 *.sup.27 *.sup.27 polymer polymer (Kg/cm.sup.2) (index) 20.degree. C. 60.degree. C. 20.degree. C. 60.degree. C.__________________________________________________________________________Example 56 modified by- PO 128 135 20 33 12 22 drogenated block co- polymer C-2Example 57 modified hy- PC 140 150 18 30 10 20 drogenated block co- polymer C-2Example 58 modified hy- PS 133 145 17 25 10 12 drogenated block co- polymer C-2Example 59 modified hy- NR 125 130 21 32 11 21 drogenated block co- polymer C-2Example 60 modified hy- PPE 140 160 17 27 12 20 drogenated block co- polymer C-2Example 61 modified hy- PPS 137 145 18 26 10 16 drogenated block co- polymer C-2Example 62 modified hy- PC + PBT*.sup.28 131 130 19 32 11 21 drogenated block co- polymer C-2Example 63 modified hy- PS + PA*.sup.28 128 130 20 35 13 20Comparative unmodified PO 93 80 36 58 -- --Example 60 block co- polymer A-2Comparative unmodified PC 102 100 30 53 -- --Example 61 block co- polymer A-2Comparative unmodified PS 97 90 34 47 -- --Example 62 block co- polymer A-2Comparative unmodified NR 90 70 28 51 -- --Example 63 block co- polymer A-2Comparative unmodified PPE 100 100 32 54 -- --Example 64 block co- polymer A-2Comparative unmodified PPS 98 90 34 51 -- --Example 65 block co- polymer A-2Comparative unmodified poly- 120 100 27 63 -- --Example 66 block co- styrene polymer A-2__________________________________________________________________________ Note: *.sup.25 The abrasion resistance was determined according to the method o ASTM D2228, and there is shown a relative value calculated based on tne supposition that the abrasion of the composition of Comparative Example 6 comprising polystyrene as t he thermoplastic polymer was 100. A larger value indicates a better abrasion resistance. *.sup.26 The measurement was carried out at a compression ratio of 2.5% for a compression time cf 22 hours according to JIS K6301. *.sup.27 At the step of extrusion kneading, 0.5 part by weight of zinc stearate was further added per 100 parts by weight of the sample C2, and the compression permanent strain of the resulting composition comprising the ionic crosslinking product o f the modified block copolymer was measured. *.sup.28 A mixture of PC/PBT (mixing weight ratio = 2/1) and a mixture of PS/PA (mixing weight ratio = 2/1) were used as the thermoplastic polymer.
EXAMPLES 64 AND 65 AND COMPARATIVE EXAMPLE 67
Compositions comprising Surlyn A-1706 (the trade name of a partially metal-crosslinked ethylene-acrylic acid copolymer available from Du Pont Co., U.S.A.) as the component (a) were prepared according to the recipe shown in Table 25 by using mixing rolls. Test pieces of the obtained compositions were prepared by compression molding and the Izod impact strength thereof was measured to obtain results shown in Table 25, from which it is seen that the compositions of the present invention have an excellent Izod impact strength.
TABLE 25______________________________________ Example Example Comparative 64 65 Example 67______________________________________Compositioncomponent (a) amount (% 20 20 20 by weight)component (b) kind C-7 E-4 B-6 amount (% 80 80 80 by weight)Izod Impact Strength*.sup.5 6.5 8.7 4.2Kg .multidot. cm/cm, notched)______________________________________ Note: *.sup.5 See the Note under Table 5.
EXAMPLES 66 THROUGH 68 AND COMPARATIVE EXAMPLES 68 THROUGH 72
Compositions comprising a modified block copolymer and Evaflex 150 (the trade name of an ethylene-vinyl acetate copolymer available from Mitsui Polychemical Co., Ltd., Japan), as shown in Table 26, were prepared by using a screw type extruder having a diameter of 40 mm (single, L/D=28), and these compositions were tested with respect to the adhesiveness to an aluminum plate. The obtained results are shown in Table 26.
The modified hydrogenated block copolymer C-8 shown in Table 26 was prepared in the following manner.
A block copolymer of the S-B-S type having a styrene content of 20% by weight, a number average molecular weight of about 100,000 and a vinyl content in the butadiene block of about 35% was hydrogenated to obtain a hydrogenated block copolymer B-7 (having a hydrogenation degree of about 90%). The obtained copolymer B-7 was modified with maleic anhydride to obtain a modified hydrogenated block copolymer C-8 (the amount of maleic anhydride grafted onto the hydrogenated block copolymer was 0.25% by weight).
TABLE 26__________________________________________________________________________ Example No. Comparative Example No. 66 67 68 68 69 70 71 72__________________________________________________________________________CompositionComponent (a) Amount (% 40 70 20 40 70 20 100 --Evaflex 150 by weight)Component (b) Kind C-1 C-1 C-8 B-1 B-1 B-7 -- B-1 Amount (% 60 30 80 60 30 80 -- 100 by weight)Adhesion to Before Im- 13.2 6.5 3.5 1.5 1.1 1.7 1.0 2.0aluminium*.sup.31 mersion in(peeling Waterstrength) After Im- 3.1 1.8 1.9 0.3 0.2 0.4 0.1 0.5(Kg/25 mm) mersion in Water__________________________________________________________________________ Note: *.sup.31 See the Note under Table 17.
EXAMPLE 69
The hydrogenated block copolymer B-1 was supplied into a screw type extruder having a diameter of 30 mm (twin, L/D=28), and simultaneously, 0.1 part by weight of Perhexa 25B [the trade name of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane available from Nippon Yushi K.K., Japan] and 35 parts by weight of maleic anhydride, per 100 parts by weight of the hydrogenated block copolymer B-1, were supplied through the side supply inlet provided on the cylinder portion of the extruder. The maleinization reaction was carried out at a cylinder temperature of 250.degree. C. The obtained block copolymer (C-9) was treated and analyzed in the same manner as described hereinbefore. It was found that the amount of maleic anhydride grafted onto the hydrogenated block copolymer was 18.5% by weight.
Compositions were prepared in the same manner as described in Examples 34 through 47 except that the copolymer C-9 was used as the modified hydrogenated block copolymer, and the physical properties of the compositions were examined. It was found that this composition is excellent in paint adhesion, impact resistance, gloss, weatherability and resistance to heat aging as well as the compositions obtained in Examples 34 through 47.
Probability of Utilization in Industry
As will be apparent from the foregoing description, since the modified block copolymer composition of the present invention is a composition comprising a thermoplastic polymer and a modified block copolymer having a very good compatibility with each other, the composition of the present invention is very homogeneous and is excellent over the conventional mixtures of different polymers in mechanical characteristics, and furthermore, the composition of the present invention has an excellent weatherability and heat aging resistance. Accordingly, it is expected that the composition of the present invention will be effectively used in various fields. As specific uses now considered, there can be mentioned materials for machine parts, automobile parts, electrical parts, toys, industrial parts, belts, hoses, shoes, medical appliances, shock-absorbing rubber articles, daily necessaries, miscellaneous goods, construction articles, sheets, films, blow-molded articles, solution-type adhesives, hot melt adhesives, tackifiers and adhesive layers of laminated articles.
The invention being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the present invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.

Number	Date	Country	Kind
56-125882	Aug 1981	JPX
56-131650	Aug 1981	JPX

Number	Name	Date
3792124	Davison et al.	Feb 1974
3845163	Murch	Oct 1974
3972961	Hammer et al.	Aug 1976
4017557	Hammer et al.	Apr 1977
4041103	Davison et al.	Aug 1977
4218545	Serini et al.	Aug 1980
4292414	Saito et al.	Sep 1981
4427828	Hergenrother et al.	Jan 1984

Number	Date	Country
50-85695	Jul 1975	JPX
55-38803	Mar 1980	JPX
998439	Jul 1965	GBX

Modified block copolymer composition

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)